Abstract
Helical nanostructures have attracted continuous attention, not only as media for chiral recognition and synthesis, but also as motifs for studying intriguing physical phenomena that never occur in centrosymmetric systems. To improve the quality of signals from these phenomena, which is a key issue for their further exploration, the most straightforward is the macroscopic orientation of helices. Here as a versatile scaffold to rationally construct this hardly accessible structure, we report a polymer framework with helical pores that unidirectionally orient over a large area (∼10 cm2). The framework, prepared by crosslinking a supramolecular liquid crystal preorganized in a magnetic field, is chemically robust, functionalized with carboxyl groups and capable of incorporating various basic or cationic guest molecules. When a nonlinear optical chromophore is incorporated in the framework, the resultant complex displays a markedly efficient nonlinear optical output, owing to the coherence of signals ensured by the macroscopically oriented helical structure.
Similar content being viewed by others
Introduction
When appropriately functionalized molecules are arranged in one-handed helices, they often display intriguing physical phenomena that never occur in centrosymmetric structures, as represented by second harmonic generation (SHG)1,2,3,4 and piezoelectricity5,6,7,8. These helices would also give a clue to pursue unexplored predictions, including molecular solenoid effects9,10. To explore these phenomena further, a key issue is to improve the quality of their output signals. For this purpose, the most straightforward approach is to orient the helices macroscopically so that mutual cancellation of signals is prevented3,4,5,6,8. Although such hierarchical structures, realizing one-handed helicity and macroscopic orientation at the same time, are rarely obtained, their rational formation would become possible by using a framework with macroscopically oriented helical pores11,12,13,14,15,16,17. If this framework serves as a scaffold for arraying various molecules in a macroscopically oriented helical structure by simple host–guest complexation, it should facilitate the exploration of the aforementioned phenomena. However, such a framework has not been developed so far. Even in the case of achiral pores, their macroscopic orientation remains a general challenge18,19,20,21,22. For the present purpose, individual pores must be helical and capable of precisely positioning the incorporated molecules, which makes this challenge even greater.
With the aim of developing such frameworks, we focused on an advanced version of molecularly imprinted polymers23 prepared by the crosslinking of liquid crystals (LCs), which have been pioneered by Gin et al.24 and are now regarded as a new class of solid-state hosts25,26,27,28,29,30,31,32. When a multicomponent LC composed of a polymerizable frame unit and a non-polymerizable template unit (for example, Fig. 1, i) is in situ crosslinked, the frame units are converted into a polymer framework, while the template units are noncovalently captured in the polymer framework and therefore are exchangeable with other molecules. Owing to the well-controlled structure, thus obtained polymer frameworks exhibit unique functions in conversion24, binding25,26,27,28,29,30 and transport31,32 of guest molecules. As we recently demonstrated, chiral pores are rationally constructed by using chiral template units27,28. Although previous polymer frameworks were mostly prepared from randomly oriented LCs except for a few examples31,32, we noted that LCs are dynamic and potentially orientable macroscopically by application of an external stimulus, such as a force or a field31,32,33,34,35,36,37,38,39,40. Among these stimuli, the use of a magnetic field has the advantages of being capable of application in a non-destructive and non-contact manner20,32,33,34.
Here we report an unprecedented type of polymer framework with macroscopically oriented helical pores, prepared by in situ crosslinking of a supramolecular LC preorganized in a magnetic field. This achievement results from our unexpected finding that a chiral liquid crystalline salt we recently developed27,28 meets all requirements as the precursor of such framework, that is, multicomponent nature, polymerizability24,25,26,27,28,29,30,31,32, orientability18,19,20,21,22,31,32,33,34,35,36,37,38,39,40 and helicity with controlled handedness11,12,13,14,15,16,17. Before this work, these features have been achieved separately, but never simultaneously. The resultant polymer framework serves as a versatile scaffold for arraying various molecules in a macroscopically oriented helical structure, thereby offering useful motifs for the exploration of the physical phenomena particular to noncentrosymmetric systems.
Results
Synthesis of the macroscopically oriented polymer framework
The polymer framework is prepared with a supramolecular columnar LC material recently reported by our group (Fig. 1, i)27,28. This consists of a polymerizable carboxylic acid that contains three flexible chains (frame, F)24 and an enantiopure amine (template, T). On mixing in equimolar amounts, these components form a salt (F·T) that exhibits a stable columnar LC mesophase. In attempt to form a macroscopically oriented structure for the LC salt F·T, we began with well-established methods, such as thermal annealing and drop casting. When F·T was slowly cooled from an isotropic molten state at 130 to 20 °C, small, randomly oriented LC domains (∼10 μm) were formed, as confirmed by polarized optical microscopy (POM; Fig. 2a). On the other hand, drop casting of its dichloromethane solution on a glass substrate produced relatively large LC domains, with a size of the order of millimetres and a characteristic crosshatched texture (Fig. 2b). Needless to say, these domains had no orientational regularity at the macroscopic level.
Interestingly, however, the application of a strong magnetic field during the drop-casting process resulted in perfectly controlled orientation of the LC domains over an ∼10-cm2-size scale (Fig. 1, ii). For example, F·T (24.9 mg, 25 μmol) in dichloromethane (500 μl) was cast on a glass substrate (2.5 × 7.5 cm) and slowly concentrated to dryness over 2 h at 20 °C in the presence of a 10-T magnetic field oriented parallel to the substrate plane. As shown in Fig. 2c, the resultant LC film exhibited rhombic patterns of multiple LC domains that aligned along the applied magnetic field to form a continuous two-dimensional (2D) array. Over the entire region of the material, these domains were oriented in the same direction (Supplementary Fig. 1). Because of the high viscosity of LC salt F·T after perfect drying, the macroscopically oriented film did not undergo structural relaxation, even when the applied magnetic field was turned off. This sluggish relaxation suggests that the present magnetic orientation took place in an intermediate state during the solvent evaporation, where residual solvent lowered the viscosity. In contrast, when a 10-T magnetic field was directed perpendicular to the substrate plane, essentially no effect was brought on the orientation of the LC domains (Fig. 2d). These observations indicate that only the horizontal (in-plane) component of the magnetic field vector contributes to this magnetic orientation, as discussed below.
For covalent fixation of the magnetically oriented structure, the LC film of F·T was then subjected to in situ crosslinking polymerization (Fig. 1, iii). To polymerize the acryloyl groups in F, we chose a γ-ray irradiation method41 that can be operated without a radical initiator and is a promising method for preserving an organized structure, as we recently disclosed28. Otherwise, doping with a radical initiator, even in a small amount (for example, 1 wt% of 2-hydroxy-2-methyl-1-propiophen-1-one), markedly weakened the structural order of the LC film. On irradiating the LC film with γ-ray (6.25 kGy h−1) at 20 °C for 16 h, crosslinking polymerization proceeded quantitatively to convert the viscous fluidic F·T into an insoluble and non-meltable solid (Supplementary Figs 2 and 3) consisting of the salt of polymerized F (poly-F) and T (denoted hereafter as poly-F·T). This polymer film was flexible and freestanding, so that it was easily peeled off from the glass substrate (Fig. 3a).
Structural analysis of the framework
Having obtained the macroscopically oriented polymer framework in hand, we investigated its structure at various scales from a macroscopic through the mesoscopic to the molecular. As observed in POM (Fig. 3b) or even by the naked eye (Fig. 3a), the crosshatched texture was extended over the entire region of the polymer film, suggesting that the crosslinking and the peel-off processes had no effect on the macroscopic orientation. When the polymer film was rotated in an in-plane manner, its POM showed a contrast every 45°, giving a dark image when the light-polarization angle with respect to the applied magnetic field was 0° or 90° (Supplementary Fig. 4). The polarized infrared absorption of the film also showed an apparent dependency on the polarization angle, in that the peaks at 1,369 cm−1 (–CO2−) and 3,221 cm−1 (–N+H3) became maximal at the polarization angle of 0° and 90°, respectively (Fig. 3c). From these observations, it is obvious that columnar aggregates of F and T, which are afforded by salt-pair formation between the –CO2H and –NH2 groups, lie along the glass surface and are oriented perpendicular or parallel to the applied magnetic field.
To examine the structure of the polymer framework in more detail, we performed an X-ray diffraction analysis with a synchrotron radiation source. As shown in Fig. 4 (top), the polymer film was exposed to a beam of X-rays from the directions perpendicular (through view) and in-plane (edge and end views) to the film surface to obtain three-dimensional (3D) structural information42. In the in-plane exposure, the X-ray beam was directed parallel (edge view) or perpendicular (end view) to the direction of the magnetic field applied during the preparation of the LC film. In the wide-angle region of the 2D X-ray diffraction images, two types of diffractions characteristic of columnar LCs were observed: a diffuse halo (d-spacing, 4.4 Å) due to the loose packing of the aliphatic chains (Fig. 4a–c, i) and a pair of obscure spots (d-spacing, 3.6 Å) attributable to the stacking of the π-conjugated systems (Fig. 4a,b, ii). Because the diffractions from the π-stacking appeared only in the equatorial region of the through and edge views, the π-conjugated systems in F·T are probably stacked in the direction perpendicular to the magnetic field.
To our surprise, a number of sharp spots appeared at regular intervals in the small-angle region (Fig. 4a–c, iii), unlike usual polymer materials. The end view (Fig. 4c) exhibited a pattern of sixfold symmetry, indicating that the columnar objects (diameter, 31.5 Å) are packed in a hexagonal manner (Supplementary Fig. 5c). The patterns in the through (Fig. 4a) and edge views (Fig. 4b) correspond to rectangular lattices, suggesting that the columnar objects have a regular periodicity (distance, 42.6 Å) along the column axis (Supplementary Fig. 5a,b), most likely originating from the helical pitch43,44. All the reflections could be unambiguously indexed (Fig. 4a–c, iii) by assuming the presence of a 3D hexagonal columnar lattice (a=31.5 Å and c=42.6 Å). Transmission electron microscopy (TEM) images and the Fourier transform also suggested the hexagonal packing of columnar objects (Supplementary Fig. 7).
The 2D X-ray diffraction images, measured for a relatively large film specimen (3 × 3 mm, ∼20 μm thick) to evaluate its macroscopic structural order, were affected by the angular fluctuation because of the flexible, polydomain nature of the film, as exemplified by the radially broaden spots in Fig. 4c. In addition, the presence of amorphous regions was suggested by a broad scattering at q=∼0.04 Å−1, where the crystallinity degree of the film was estimated to 82% (Supplementary Fig. 5). Such amorphous regions would be non-negligible particularly at domain boundaries. To remove the effects of polydomain nature, a monodomain clump trimmed from the film was used instead, where much narrower spots were observed (Supplementary Figs 8 and 9). The crystallinity degree was also estimated to be notably higher (92%; Supplementary Fig. 10) but not perfect, probably because of the dynamic nature of the precursor LC and disordering during the in situ polymerization.
Using the data of the monodomain clump, the space group of poly-F·T was deduced as follows (Supplementary Methods). After determining the lattice parameters, all indexed reflections were integrated. By calculating the internal residual factor from the reflection intensity and considering symmetry, the Laue group was determined to be 6/mmm. Taking account of the systematic extinction rule (Supplementary Fig. 8b), the space group was deduced to be P6122 or its enantiomorph P6522, which contain right- and left-handed sixfold screw axes, respectively. These space groups also have a twofold screw axis that is perpendicular to the sixfold one, indicating that the whole system is intrinsically apolar and that the sixfold helix forms an antiparallel duplex with another homochiral helix. By assuming that the density of poly-F·T is ∼1.0 g cm−3, we estimated the Z-value of the lattice to be 24, indicating the presence of two crystallographically independent pairs of F·T. In relation to this, the c axis lattice parameter (42.6 Å) is exactly 12 times as large as the observed π-stacking distance (3.6 Å), indicating that one helical pitch consists of 12 stacking units. Taking account of all the parameters thus obtained, we proposed the structural model shown in Fig. 5, where two salt pairs of F and T aggregate to form a bow-tie-shaped unit (Fig. 5c). These stack helically with one another (stacking distance, 3.6 Å; rotation angle, 30°) to form a sixfold helix (Fig. 5b). The helical columns lie along the substrate plane and are oriented perpendicular to the applied magnetic field (Fig. 5a).
For further insight into the assembled structure of F·T, thermal behaviour of an analogous salt F·T′ (T′, C2-stereoinverted analogue of T) was investigated (Supplementary Fig. 11). As we previously reported, conformational preferences of T and T′ are quite different from each other, where T tends to adopt a more flatten conformation (=larger dihedral angle θ in Supplementary Fig. 11a) due to the steric hindrance between the phenyl and methyl groups45. Such a flatten conformation would facilitate the stacking of the salt pairs of F and T, as suggested by the diffraction due to π-stacking (Fig. 4a,b ii). Indeed, the analogous salt F·T′ cannot form an assembled structure, exhibiting only an isotropic phase (Supplementary Fig. 11b). The X-ray crystal structure of another analogous salt F′·T (F′, analogue of F lacking long alkyl chains) is in consistent with the above hypothesis (Supplementary Fig. 12 and Supplementary Data 1). Thus, the salt pairs of F′ and T, adopting a flatten shape, self-assemble via π-stacking and hydrogen-bonding interactions. In the crystal structure of F′·T, the salt pairs assemble into a one-dimensional (1D) array with lateral offsets of the π-conjugated systems, while in the LC structure of F·T, the salt pairs assemble in a helical array, most likely because of the steric hindrance of the long alkyl chains in F.
The structural model in Fig. 5 accords with the general tendency of π-conjugated systems to orient parallel to an applied magnetic field, and explains the mechanism underlying the present magnetic orientation. Given that an applied magnetic field orients the π-conjugated systems in individual molecules of F and T parallel to the field, it would generate a torque that orients their columnar aggregates perpendicular to the magnetic field. Simultaneously, the columns are induced to lie along the surface of the film, most likely because of the interaction of the columns’ aliphatic side chains with the air interface during the drop-casting process. When the magnetic field is applied along the substrate plane, the magnetic and surface effects cooperate to produce a unidirectional orientation34. This hypothesis is consistent with the observation that a magnetic field applied perpendicular to the substrate plane had no effect on the structural ordering (Fig. 2d), where both the magnetic and surface effects only defined the columns to orient within the substrate plane and did not restrict their in-plane rotation. We also confirmed that the present magnetic orientation had no effect on the microstructure of the polymer framework; as shown by its 1D SAXS profiles, a film of poly-F·T with a randomly oriented structure, prepared in the absence of magnet, had the same lattice as that of a magnetically structured film (Supplementary Fig. 6).
Use of the framework as a solid-state host
By immersing a film of poly-F·T in acidified ethanol at 20 °C for 10 h, T can be quantitatively desorbed from the framework of poly-F (Fig. 1, iv), owing to the lack of covalent interactions between T and poly-F (Supplementary Fig. 13 and Supplementary Table 2). The resultant film, which consisted exclusively of guest-free polymer framework (poly-F· vacant), showed infrared absorption characteristic of a free carboxyl acid (–CO2H), while the absorption associated with the carboxylate ion (–CO2−) disappeared (Supplementary Fig. 15b). Through the desorption of T, the macroscopic orientation of the polymer framework was well preserved (Supplementary Fig. 16b). However, the hexagonal columns shrunk in diameter from 31.5 to 30.0 Å (Supplementary Fig. 17c) and lost the periodicity of helical pitch (Supplementary Fig. 17a,b), revealing the flexible nature of the polymer framework27.
Because poly-F· vacant contains hollow pores featuring many –CO2H groups, the guest-free film readily incorporates various basic or cationic guest molecules G1–G7 (Fig. 1, v). For example, when a film of poly-F·vacant was immersed at 20 °C for 8 h in a methanolic solution of an amine bearing a p-nitroaniline moiety (G1)46, the film adsorbed ∼0.9 equivalents of G1 with respect to the –CO2H group content of the film (Supplementary Fig. 14 and Supplementary Table 2). The resultant yellow film (Fig. 3d) retained its macroscopic orientation, as confirmed by POM (Fig. 3e). Changes in infrared absorption indicate that this guest binding is driven by salt-pair formation (Supplementary Fig. 15c). Amine G2 bearing a fluorescent moiety and amine G3 bearing a stabilized radical as well as alkali metal ions (G4–G7) were also incorporated as guests in the polymer framework through salt-pair formation with retention of the macroscopic orientation (Supplementary Figs 15 and 16).
As a representative example of a guest-exchanged film, that of poly-F·G1 was investigated in more detail. In polarized infrared spectroscopy, its absorption at 1,369 cm−1 (–CO2−) and 1,540 cm−1 (–NO2) was clearly dependent on the light-polarization angle (Fig. 3f), indicating that the molecular units of F and G1 are anisotropically positioned in the macroscopically oriented helical pores. After incorporation of G1, the polymer framework retained its hexagonal columnar packing, and, moreover, recovered the periodicity of helical pitch. In fact, the 2D X-ray diffraction patterns of poly-F·G1 (Supplementary Fig. 18) were quite similar to those of poly-F·T (Fig. 4) for all three views. In addition, lattice parameters of poly-F·G1 (column diameter=31.4 Å, helical pitch=42.8 Å) were essentially identical to those of poly-F·T (column diameter=31.5 Å, helical pitch=42.6 Å), despite the different molecular shapes of G1 and T. Such consistency in lattice parameters suggests that a fundamental skeleton of the helical pores might be preserved in poly-F even after the helical pitch disordering because of the desorption of T (Supplementary Fig. 17). It is probable that molecules of G1 filled the spaces originally occupied by T molecules, thereby reducing the structural strain in the polymer framework and recovering the helical pitch27. From these observations, we also deduced that the molecules of G1 in the polymer framework were present in a helical arrangement, as in the case of T. In this case, a chiral structure emerged from achiral components (F and G1) because of the chiral template effect of T (ref. 47).
Owing to their push–pull-substituted aromatic systems, p-nitroaniline derivatives such as G1 are known to exhibit the second-order nonlinear optical (NLO) properties, when they are arrayed in a noncentrosymmetric (=polar, chiral or both) arrangement46,48. Because the molecules of G1 confined in poly-F are likely to align in helical arrays, as described above, they potentially show second-order NLO properties1,2,3,4. Although there have been reported several host systems that induce the NLO output of chromophore guests, most of them contain the contribution of polar structures46,49. Contrary to them, our polymer framework with a chiral and apolar space group (P6122 or P6522) would afford NLO output genuinely because of chirality, which is suitable for pursuing nonlinear phenomena in chiral architectures. Furthermore, the macroscopic orientation of poly-F would be expected to have positive effects on the NLO output because the NLO signals generated from the ordered structure should be less prone to mutual cancellation and therefore coherent.
To confirm this possibility, we measured the SHG of the film of poly-F·G1 (Fig. 6a and Supplementary Fig. 19). We used circularly polarized light (CPL) with right- or left-handedness as a fundamental beam, so that we could determine, independently of any effect of birefringence, whether the origin of the SHG was the chiral arrangement induced by the polymer framework or whether it arose from coincidental polar ordering50. To detect the SHG circular dichroism clearly, the incident angle was set to 45°, and the s- and p-polarized contents of the SHG output were separately monitored (Methods)50. When right-handed CPL (wavelength, 800 nm) was irradiated to a 5-μm-thick film of poly-F·G1 with a magnetically oriented structure (Fig. 6a, red), strong SHG output was observed for both of the s- and p-polarized contents (Fig. 6b, red). On switching the handedness of the CPL from right to left (Fig. 6a, blue), the intensity of the SHG reduced by half (Fig. 6b, blue), proving that the SHG observed here is because of the chiral arrangement of G1. As we had conjectured, the macroscopic orientation of the framework had a significant effect on the SHG output. Indeed, the SHG intensity of the film with magnetically oriented structure (Fig. 6b) was seven times greater than that of an analogous 5-μm-thick film with a randomly oriented structure (Fig. 6c).
Discussion
Although many types of ordered porous materials, such as zeolites, porous silicates and metal–organic frameworks, have been developed so far, our new polymer framework (poly-F), prepared by in situ crosslinking of a chiral supramolecular LC salt (F·T) preorganized in a magnetic field (Fig. 1), is the first porous material that realizes helicity with controlled handedness11,12,13,14,15,16,17 and macroscopic orientation18,19,20,21,22,31,32,33,34,35,36,37,38,39,40 at the same time. Our framework, capable of incorporating various basic or cationic guest molecules and restricting their positions, is expected to serve as a ‘universal’ scaffold for arraying molecules into a helical and macroscopically oriented structure. The resulting arrangement of the guest molecules might be suitable for inducing molecular events to proceed in a directionally controlled and mutually correlated manner, as exemplified by the SHG of a NLO chromophore (G1) demonstrated in this work. Further potential applications of our framework include CPL-emitting devices, piezoelectric materials, chiral magnets, anisotropic ion-conductive materials or membranes for chiral separation.
Methods
General
POM was performed on a Nikon model Eclipse LV100POL optical polarizing microscope equipped with a Mettler Toledo model FP90 Central Processor connected with a model FP 82HT hot stage. 60Co γ-ray irradiation was carried out in the Takasaki Advanced Radiation Research Institute of Japan Atomic Energy Agency. Film thicknesses were measured using a Mitutoyo model MDQ-30M micrometer. HPLC analysis was performed on a JASCO model PU-980 intelligent HPLC pump equipped with a model UV-970 intelligent ultraviolet–vis detector. Elemental analysis was performed on a Yanaco CHN CORDER MT-6 elemental analyser. 1H NMR spectra were measured on a JEOL model NM-Excalibur 500 spectrometer operated at 500 MHz. Infrared spectra were measured on a JASCO model FT/IR-4100 Fourier transform infrared spectrometer with a model ATR PRO450-S-attenuated total reflection equipment. X-ray crystallographic study was carried out using a Rigaku AFC-8 diffractometer with graphite monochromated Mo Kα radiation at 300 K.
Materials
3,4,5-Tris(11-acryloyloxyundecyloxy)benzoic acid (F)24, (1R,2R)-pseudonorephedrine (T′)51, 3,5-dimethoxybenzoic acid (F′)52, N-(2-aminoethyl)-p-nitroaniline (G1)46 and N-(7-nitrobenz-2-oxa-1,3-diazol-4-yl)aminoethylamine (G2)53 were prepared according to literature methods. Water was obtained from a Millipore model Milli-Q integral water purification system. (1R,2S)-Norephedrine (T) was purchased from TCI and purified by distillation. Other reagents were used as received from Kanto (CH2Cl2, EtOH, MeOH and HClO4 (60% aqueous solution)), Sigma-Aldrich (Cs2CO3 (G7)), TCI (4-amino-2,2,6,6-tetramethylpiperidine-1-oxyl (G3)) and Wako (HCO2H, hexane, Li2CO3 (G4), K2CO3 (G6) and Na2CO3 (G5)).
Synthesis of a film of poly-F·T with magnetically oriented structure
A solution of salt F·T (24.9 mg, 25 μmol) in CH2Cl2 (500 μl) was cast on a glass substrate (2.5 × 7.5 cm). The glass substrate was placed inside a pair of loosely closed Petri dishes that were immediately inserted into the bore of a superconducting magnet with its 10-T field oriented parallel to the substrate plane. The cast solution of F·T was carefully and slowly concentrated to dryness over 2 h at 20 °C. The resultant material was further dried under reduced pressure (∼1 mm Hg) at 20 °C overnight to remove residual volatiles to give an LC film of F·T with a magnetically oriented structure. To achieve in situ polymerization of the acryloyl groups in F, the LC film on the glass substrate was placed in a glass tube equipped with a three-way cock. The glass tube was evacuated by means of a rotary oil pump (∼1 mm Hg) at 20 °C for 1 h and was purged with argon. The film in the glass tube was then exposed to 60Co γ-ray (6.25 kGy h−1) at 20 °C for 16 h so that the LC film was converted into a film of poly-F·T with a magnetically oriented structure. The film was immersed in CH2Cl2 at 20 °C for a few minutes and then detached from the glass substrate. By using a micrometre gauge, the thickness of the film was estimated to be 10–15 μm. The thickness of the film could be tuned by adjusting the concentration of the F·T solution and the drop-casting area in the LC film-preparation process. Thicknesses of film samples used for the measurements are summarized in Supplementary Table 1.
Synthesis of a film of poly-F·T with randomly oriented structure
Salt F·T was sandwiched between two glass plates and warmed to 130 °C so that the salt turned into an isotropic melt. It was then allowed to cool to 20 °C at 5.0 °C min−1 and then left to stand at 20 °C overnight to give an LC film with a randomly oriented structure. For in situ polymerization of the acryloyl groups in F, the LC film sandwiched between the two glass plates was subjected to 60Co γ-ray irradiation, as described above, to give a film of poly-F·T with a randomly oriented structure.
Desorption of T from a film of poly-F·T
A film of poly-F·T (20.1 mg, containing 20.2 μmol of T and the –CO2H groups) was immersed in a 7.5 M solution of HCO2H in EtOH (50 ml) at 20 °C for 10 h. The resultant mixture was separated into the film and the supernatant. The film was then washed with EtOH (5 ml) and dried under reduced pressure (∼1 mm Hg) to give a film of poly-F·vacant. For the quantification of desorbed T, the supernatant and the washings were combined and concentrated to dryness, dissolved in a pH 2.0 aqueous solution of HClO4 (4.00 ml) containing L-tyrosine (3.0 mM) as an internal standard, and subjected to HPLC. The concentration of T was calculated from the data of authentic solutions of T (Supplementary Fig. 13). Column, Daicel CROWNPAK CR (+) (4.6 × 153 mm); eluent, pH 2.0 aqueous HClO4; temperature, 20 °C; flow rate, 0.60 ml min−1; injection volume, 5.0 μl; detection, UV absorption at 200 nm; elution time, 8.9 (L-tyrosine) and 13.3 min (T).
Adsorption of G1–G7 by films of poly-F·vacant
A film of poly-F·vacant (10.0 mg, containing 11.8 μmol of the –CO2H groups) was immersed in a 2.5 mM solution of G1 in MeOH (5 ml) at 20 °C for 8 h. From the resultant mixture, the film was separated, washed with MeOH (2.5 ml) and dried under reduced pressure (∼1 mm Hg) to afford a film of poly-F·G1. For the quantification of the uptake of G1, the film of poly-F·G1 was immersed in a 7.5-M solution of HCO2H in EtOH (25 ml) at 20 °C for 10 h. From the resultant mixture, the supernatant was separated, while the film was washed with EtOH (2.5 ml). The supernatant and the washings were combined and concentrated to dryness, dissolved in a pH 2.0 aqueous solution of HClO4 (2.00 ml) containing L-tyrosine (3.0 mM) as an internal standard and subjected to HPLC analysis. The concentration of G1 was calculated from the data of authentic solutions of G1 (Supplementary Fig. 14). Column, Daicel CROWNPAK CR (+) (4.6 × 153 mm); eluent, pH 2.0 aqueous HClO4; temperature, 20 °C; flow rate, 1.00 ml min−1; injection volume, 5.0 μl; detection, ultraviolet absorption at 228 nm; elution time, 5.4 (L-tyrosine) and 39.3 min (G1).
The other amino guests (G2 and G3) were adsorbed by similar procedures. Alkali metal ion guests (G4–G7) were adsorbed from a mixture of MeOH and water (90:10, v/v) at 70 °C for 8 h.
Synchrotron 2D X-ray diffraction measurement at SPring-8 BL45XU
2D X-ray diffraction measurement of the polydomain films and powders of poly-F·T and poly-F·G1 was carried out at BL45XU in SPring-8 (Hyogo, Japan)54. Diffraction data were collected using a Rigaku imaging plate area detector model R-AXIS IV++. The incident X-ray beam (1.00 Å wavelength) was monochromated by a diamond (1 1 1) double-crystal monochromator. The sample-to-detector distance was 0.40 m. Scattering vector q and position of an incident X-ray beam on the detector were calibrated using several orders of layer reflections from silver behenate (d=58.380 Å). Film samples were mounted on nylon fibres (ϕ=0.2 mm) and exposed at 20 °C to an X-ray beam for 30 (edge and end views) or 300 s (through view). Powder samples were placed into 1.5-mm-ϕ glass capillaries and exposed at 20 °C to an X-ray beam for 50 s.
Synchrotron 2D X-ray diffraction measurement at SPring-8 BL26B2
2D X-ray diffraction measurement for the determination of the space group of poly-F·T was carried out at BL26B2 in SPring-8 (ref. 55). Diffraction data were collected using a MarMosaic225 detector. The incident X-ray beam (1.0000 Å wavelength) was monochromated by a Si (1 1 1) double-crystal monochromator. The sample-to-detector distance was 500 mm. A monodomain clump (0.7 × 0.6 × 0.2 mm) trimmed from a film of poly-F·T was held on a MicroMounts (MiTeGen) that was attached to a brass pin (Supplementary Fig. 8a), mounted on a goniometer head, and exposed to an X-ray beam at 27 °C. A total of 18 frames of data were collected with an oscillation range of 10° and an exposure time of 10 s for each frame (Supplementary Fig. 8b). The total oscillation angle was 180°.
TEM measurement
TEM measurement was performed on a JEOL model JEM-2100F/SP operated at 200-kV accelerating voltage. Films of poly-F·T were embedded in EPON812 (TAAB Laboratories Equipment) and sectioned at 20 °C with a diamond knife mounted on a Leica Ultracut UCT ultramicrotome. The resultant sections (∼60 nm thick) were floated on water, retrieved on TEM grids, stained in vapour of a 0.5% aqueous solution of RuO4 (TAAB Laboratories Equipment) at 20 °C for 10 min and subjected to TEM observation.
SHG circular dichroism measurement
SHG circular dichroism measurement50 was performed with planar freestanding films of poly-F·G1. For simplicity, films thinner than the coherent length (5 μm thick) were used. As the fundamental beam, right- and left-handed CPLs were created by using 800-nm light of a titanium:sapphire laser (averaged power, 200 mW; duration, 200 fs; repetition, 80 MHz). The laser beam was successively passed through a polarizer and a quarter-wave plate, where the rotation angle of the quarter-wave plate with respect to the polarizer was set to be 45° or 225° for the right-handed CPL and 135° or 315° for the left-handed CPL. Thus, created CPL was guided into a sample with 45° incidence. In the case of film with a magnetically oriented structure, the film was set so that the direction of the magnetic field that was applied during the LC film-formation process was perpendicular to the incident plane, that is, the helical axes of the columnar objects were parallel to the incident plane. SHG signals were detected in the transmission direction by a Hamamatsu model H7421-40 cooled photomultiplier tube after successively passing through an infrared-cut filter, an analyser (s or p), and a 400-nm band pass filter. The signals were recorded by a photon-counting system C8855-01 for a window width of 1 s. For optical scheme, see Supplementary Fig. 19.
Additional information
Accession codes: The X-ray crystallographic coordinates for structures reported in this study have been deposited at the Cambridge Crystallographic Data Centre (CCDC), under deposition number 1056043. These data can be obtained free of charge from The Cambridge Crystallographic Data Centre via www.ccdc.cam.ac.uk/data_request/cif.
How to cite this article: Li, C. et al. Macroscopic ordering of helical pores for arraying guest molecules noncentrosymmetrically. Nat. Commun. 6:8418 doi: 10.1038/ncomms9418 (2015).
Change history
26 October 2015
A correction has been published and is appended to both the HTML and PDF versions of this paper. The error has not been fixed in the paper.
References
Evans, O. R. & Lin, W. Crystal engineering of NLO materials based on metal–organic coordination networks. Acc. Chem. Res. 35, 511–522 (2002).
Verbiest, T. & Persoons, A. In Materials-Chirality: Vol. 24 of Topics in Stereochemistry eds Green M. M., Nolte R. J. M., Meijer E. W. Chapter 9, Wiley (2003).
Verbiest, T. et al. Strong enhancement of nonlinear optical properties through supramolecular chirality. Science 282, 913–915 (1998).
Gonella, G. et al. Control of the orientational order and nonlinear optical response of the “push-pull” chromophore RuPZn via specific incorporation into densely packed monolayer ensembles of an amphiphilic 4-helix bundle peptide: second harmonic generation at high chromophore densities. J. Am. Chem. Soc. 132, 9693–9700 (2010).
Eckert, T., Finkelmann, H., Keck, M., Lehmann, W. & Kremer, F. Piezoelectricity of mechanically oriented SC*-elastomers. Macromol. Rapid Commun. 17, 767–773 (1996).
Jaworek, T., Neher, D., Wegner, G., Wieringa, R. H. & Schouten, A. J. Electromechanical properties of an ultrathin layer of directionally aligned helical polypeptides. Science 279, 57–60 (1998).
Haussuhl, S., Bohaty, L. & Becker, P. Piezoelectric and elastic properties of the nonlinear optical material bismuth triborate, BiB3O6 . Appl. Phys. A 82, 495–502 (2006).
Lee, B. Y. et al. Virus-based piezoelectric energy generation. Nat. Nanotechnol. 7, 351–356 (2012).
Tagami, K., Tsukada, M., Wada, Y., Iwasaki, T. & Nishide, H. Electronic transport of benzothiophene-based chiral molecular solenoids studied by theoretical simulations. J. Chem. Phys. 119, 7491–7497 (2003).
Goh, M., Matsushita, S. & Akagi, K. From helical polyacetylene to helical graphite: synthesis in the chiral nematic liquid crystal field and morphology-retaining carbonization. Chem. Soc. Rev. 39, 2466–2476 (2010).
Miyata, M., Tohnai, N. & Hisaki, I. Crystalline host–guest assemblies of steroidal and related molecules: diversity, hierarchy, and supramolecular chirality. Acc. Chem. Res. 40, 694–702 (2007).
Che, S. et al. Synthesis and characterization of chiral mesoporous silica. Nature 429, 281–284 (2004).
Yu, J. & Xu, R. Chiral zeolitic materials: structural insights and synthetic challenges. J. Mater. Chem. 18, 4021–4030 (2008).
Bradshaw, D., Claridge, J. B., Cussen, E. J., Prior, T. J. & Rosseinsky, M. J. Design, chirality, and flexibility in nanoporous molecule-based materials. Acc. Chem. Res. 38, 273–282 (2005).
Percec, V. et al. Principles of self-assembly of helical pores from dendritic dipeptides. Proc. Natl Acad. Sci. USA 103, 2518–2523 (2006).
Miyagawa, T., Yamamoto, M., Muraki, R., Onouchi, H. & Yashima, E. Supramolecular helical assembly of an achiral cyanine dye in an induced helical amphiphilic poly(phenylacetylene) interior in water. J. Am. Chem. Soc. 129, 3676–3682 (2007).
Gan, Q. et al. Helix-rod host-guest complexes with shuttling rates much faster than disassembly. Science 331, 1172–1175 (2011).
Feng, S. & Bein, T. Growth of oriented molecular sieve crystals on organophosphonate films. Nature 368, 834–836 (1994).
Lee, J. S., Lee, Y.-J., Tae, E. L., Park, Y. S. & Yoon, K. B. Synthesis of zeolite as ordered multicrystal arrays. Science 301, 818–821 (2003).
Tolbert, S. H., Firouzi, A., Stucky, G. D. & Chmelka, B. F. Magnetic field alignment of ordered silicate-surfactant composites and mesoporous silica. Science 278, 264–268 (1997).
Melosh, N. A., Davidson, P., Feng, P., Pine, D. J. & Chmelka, B. F. Macroscopic shear alignment of bulk transparent mesostructured silica. J. Am. Chem. Soc. 123, 1240–1241 (2001).
Miyata, H. et al. Remarkable birefringence in a TiO2–SiO2 composite film with an aligned mesoporous structure. J. Am. Chem. Soc. 133, 13539–13544 (2011).
Wulff, G. Enzyme-like catalysis by molecularly imprinted polymers. Chem. Rev. 102, 1–27 (2002).
Smith, R. C., Fischer, W. M. & Gin, D. L. Ordered poly(p-phenylenevinylene) matrix nanocomposites via lyotropic liquid-crystalline monomers. J. Am. Chem. Soc. 119, 4092–4093 (1997).
Lee, H.-K. et al. Synthesis of a nanoporous polymer with hexagonal channels from supramolecular discotic liquid crystals. Angew. Chem. Int. Ed. 40, 2669–2671 (2001).
Courty, S., Tajbakhsh, A. R. & Terentjev, E. M. Stereo-selective swelling of imprinted cholesteric networks. Phys. Rev. Lett. 91, 085503 (2003).
Ishida, Y., Amano, S., Iwahashi, N. & Saigo, K. Switching of structural order in a cross-linked polymer triggered by the desorption/adsorption of guest molecules. J. Am. Chem. Soc. 128, 13068–13069 (2006).
Amano, S., Ishida, Y. & Saigo, K. Solid-state hosts by the template polymerization of columnar liquid crystals: locked supramolecular architectures around chiral 2-amino alcohols. Chem. Eur. J. 13, 5186–5196 (2007).
Broer, D. J., Bastiaansen, C. M. W., Debije, M. G. & Schenning, A. P. H. J. Functional organic materials based on polymerized liquid-crystal monomers: supramolecular hydrogen-bonded systems. Angew. Chem. Int. Ed. 51, 7102–7109 (2012).
van Kuringen, H. P. C., Eikelboom, G. M., Shishmanova, I. K., Broer, D. J. & Schenning, A. P. H. J. Responsive nanoporous smectic liquid crystal polymer networks as efficient and selective adsorbents. Adv. Funct. Mater. 24, 5045–5051 (2014).
Yoshio, M. et al. One-dimensional ion-conductive polymer films: alignment and fixation of ionic channels formed by self-organization of polymerizable columnar liquid crystals. J. Am. Chem. Soc. 128, 5570–5577 (2006).
Feng, X. et al. Scalable fabrication of polymer membranes with vertically aligned 1 nm pores by magnetic field directed self-assembly. ACS Nano 8, 11977–11986 (2014).
Shklyarevskiy, I. O. et al. High anisotropy of the field-effect transistor mobility in magnetically aligned discotic liquid-crystalline semiconductors. J. Am. Chem. Soc. 127, 16233–16237 (2005).
Kim, H.-S. et al. Uniaxially oriented, highly ordered, large area columnar superstructures of discotic supramolecules using magnetic field and surface interactions. Adv. Mater. 20, 1105–1109 (2008).
Van Winkle, D. H. & Clark, N. A. Freely suspended strands of tilted columnar liquid-crystal phases: one-dimensional nematics with orientational jumps. Phys. Rev. Lett. 48, 1407–1410 (1982).
Mas-Torrent, M., den Boer, D., Durkut, M., Hadley, P. & Schenning, A. P. H. J. Field effect transistors based on poly(3-hexylthiophene) at different length scales. Nanotechnology 15, S265–S269 (2004).
Gibbons, W. M., Shannon, P. J., Sun, S. T. & Swetlin, B. J. Surface-mediated alignment of nematic liquid crystals with polarized laser light. Nature 351, 49–50 (1991).
van de Craats, A. M. et al. Meso-epitaxial solution-growth of self-organizing discotic liquid-crystalline semiconductors. Adv. Mater. 15, 495–499 (2003).
Liu, C.-Y. & Bard, A. J. In-situ regrowth and purification by zone melting of organic single-crystal thin films yielding significantly enhanced optoelectronic properties. Chem. Mater. 12, 2352–2362 (2000).
Tracz, A. et al. Uniaxial alignment of the columnar super-structure of a hexa (alkyl) hexa-peri-hexabenzocoronene on untreated glass by simple solution processing. J. Am. Chem. Soc. 125, 1682–1683 (2003).
Hohn, W. & Tieke, B. γ-ray polymerization of mesogenic diacrylates in the crystalline, liquid crystalline and liquid state – a kinetic study. Macromol. Chem. Phys. 197, 821–831 (1996).
Wang, M.-D., Nakanishi, E. & Hibi, S. Effect of molecular weight on rolled high density polyethylene: 1. Structure, morphology and anisotropic mechanical behavior. Polymer 34, 2783–2791 (1993).
Pisula, W., Feng, X. & Müllen, K. Tuning the columnar organization of discotic polycyclic aromatic hydrocarbons. Adv. Mater. 22, 3634–3649 (2010).
Percec, V. et al. Self-assembly of dendronized Perylene bisimides into complex helical columns. J. Am. Chem. Soc. 133, 12197–12219 (2011).
Ishida, Y. et al. Tunable chiral reaction media based on two-component liquid crystals: regio-, diastereo-, and enantiocontrolled photodimerization of anthracenecarboxylic acids. J. Am. Chem. Soc. 132, 17435–17446 (2010).
Prakash, M. J. & Radhakrishnan, T. P. Second harmonic generation from a homologous series of molecular crystals: impact of supramolecular interactions. Chem. Mater. 18, 2943–2949 (2006).
Choi, S. S., Morris, S. M., Huck, W. T. S. & Coles, H. J. Simultaneous red–green–blue reflection and wavelength tuning from an achiral liquid crystal and a polymer template. Adv. Mater. 22, 53–56 (2010).
Verbiest, T., Houbrechts, S., Kauranen, M., Clays, K. & Persoons, A. Second-order nonlinear optical materials: recent advances in chromophore design. J. Mater. Chem. 7, 2175–2189 (1997).
Caro, J., Marlow, F. & Wübbenhorst, M. Chromophore–zeolite composites: the organizing role of molecular sieves. Adv. Mater. 6, 413–416 (1994).
Araoka, F. et al. Twist-grain-boundary structure in the B4 phase of a bent-core molecular system identified by second harmonic generation circular dichroism measurement. Phys. Rev. Lett. 94, 137801 (2005).
Groeper, J. A., Hitchcock, S. R. & Ferrence, G. M. A scalable and expedient method of preparing diastereomerically and enantiomerically enriched pseudonorephedrine from norephedrine. Tetrahedron 17, 2884–2889 (2006).
Song, Y. M. et al. Synthesis of novel azo-resveratrol, azo-oxyresveratrol and their derivatives as potent tyrosinase inhibitors. Bioorg. Med. Chem. Lett. 22, 7451–7455 (2012).
Cotté, A., Bader, B., Kuhlmann, J. & Waldmann, H. Synthesis of the N-terminal lipohexapeptide of human GαO-protein and fluorescent-labeled analogues for biological studies. Chem. Eur. J. 5, 922–936 (1999).
Fujisawa, T. et al. Small-angle X-ray scattering station at the SPring-8 RIKEN beamline. J. Appl. Crystallogr. 33, 797–800 (2000).
Ueno, G. et al. RIKEN structural genomics beamlines at the SPring-8; high throughput protein crystallography with automated beamline operation. J. Struct. Funct. Genomics 7, 15–22 (2006).
Acknowledgements
C.L. thanks the Japanese Government Scholarship (MEXT, Japan) and the RIKEN Junior Research Associate Fellowship. This work was supported by ImPACT Program of Council for Science, Technology and Innovation (Cabinet Office, Government of Japan) and JSPS Grant-in-Aid for Scientific Research (B), Grant Number 15H03820. The synchrotron X-ray diffraction experiments were performed at BL45XU and BL26B1 in SPring-8 with the approval of RIKEN SPring-8 Center (proposal 20140073). We thank T. Tose for the synthesis of F, M. Takata, T. Hikima and G. Ueno for their support in the X-ray diffraction measurements at SPring-8, T. Kikitsu and D. Inoue for the transmission electron microscopy measurement and S. Amano and K. Saigo for the X-ray crystallographic study.
Author information
Authors and Affiliations
Contributions
Y.I. conceived the project; C.L., J.C. and Y.I. designed, performed and analysed experiments; C.L., J.C. and K.Y. synthesized compounds; D.H. and Y.I. measured and analysed the X-ray diffraction data; F.A. and H.T. measured the SHG; T.A. and Y.I. co-wrote the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-19, Supplementary Table 1-2, Supplementary Methods and Supplementary References (PDF 16618 kb)
Supplementary Data 1
Supplementary Data 1 (CIF 1622 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Li, C., Cho, J., Yamada, K. et al. Macroscopic ordering of helical pores for arraying guest molecules noncentrosymmetrically. Nat Commun 6, 8418 (2015). https://doi.org/10.1038/ncomms9418
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms9418