Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

# Electrocatalytic reduction of carbon dioxide to carbon monoxide and methane at an immobilized cobalt protoporphyrin

## Abstract

The electrochemical conversion of carbon dioxide and water into useful products is a major challenge in facilitating a closed carbon cycle. Here we report a cobalt protoporphyrin immobilized on a pyrolytic graphite electrode that reduces carbon dioxide in an aqueous acidic solution at relatively low overpotential (0.5 V), with an efficiency and selectivity comparable to the best porphyrin-based electrocatalyst in the literature. While carbon monoxide is the main reduction product, we also observe methane as by-product. The results of our detailed pH-dependent studies are explained consistently by a mechanism in which carbon dioxide is activated by the cobalt protoporphyrin through the stabilization of a radical intermediate, which acts as Brønsted base. The basic character of this intermediate explains how the carbon dioxide reduction circumvents a concerted proton–electron transfer mechanism, in contrast to hydrogen evolution. Our results and their mechanistic interpretations suggest strategies for designing improved catalysts.

## Introduction

The efficient electrochemical reduction of carbon dioxide to a fuel with a high-energy density would be a major step forward in the introduction of a CO2 neutral energy cycle, as it would allow for the direct low-temperature conversion of photo-generated electrical current to stored chemical energy, in a manner very similar to the way nature stores solar energy. Plants fix CO2 from the atmosphere by photosynthesis in an enzymatic complex called Rubisco, which selectively binds CO2 and inserts it into existing carbon chains by reductive carboxylation. The high-energy electrons necessary for this process are photo-generated by photosystem II.

Synthetic catalysts for the electrocatalytic reduction of CO2, which could facilitate such an artificial CO2 neutral redox cycle, have been studied for many decades1,2,3,4. A main challenge in electrochemical CO2 reduction is to develop catalysts that are capable of reducing CO2 beyond the two-electron products carbon monoxide (CO), formic acid (HCOOH), and oxalate (C2O42−). Unfortunately, the formation of reduction products requiring four or more electrons is invariably associated with considerable overpotentials due to the multiple intermediates involved in the reaction mechanisms5 (although more reduced products often have higher stability and correspondingly more positive equilibrium potentials). Metallic copper is unique in producing significant amounts of high-energy multi-electron transfer products such as methane, ethylene and ethanol3,6,7. Molecular catalysts that are capable of reducing CO2 to a product different from one of the above-mentioned two-electron products are much less common and typically involve a strong interaction with the working electrode8. A second important challenge in CO2 electrocatalysis concerns the suppression of the concomitant evolution of hydrogen, which is a dominant side reaction for CO2 reduction from aqueous electrolytes. Strategies for suppressing hydrogen evolution typically involve working with high(er) CO2 to proton ratios, such as high CO2 pressures or solvents with a higher CO2 solubility.

Recent fundamental and theoretical work has reconsidered porphyrin-based molecular catalysts for electrochemical CO2 reduction. Tripkovic et al.9 have performed extensive density functional theory calculations of metal-functionalized porphyrin-like graphene surfaces, and predicted the potential formation of methane and methanol from CO2. Costentin et al.10 considered ligand modifications of iron-based porphyrins and found that local proton sources built into the porphyrin ring give rise to high activity and good Faradaic efficiency (FE) for the reduction of CO2 to CO in a mixed DMF–water solvent. In fact, it has been known since the early 1980s that cobalt (Co)-based macrocyclic complexes, either in solution or adsorbed onto carbon electrodes, act as effective electrocatalysts for CO2 reduction, producing CO, HCOOH, methanol and methane, although at relatively high overpotential and with varying selectivity11,12,13,14,15.

Herein, we report on the electrochemical reduction of CO2 to CO and methane, as well as smaller amounts of HCOOH and methanol, on a simple Co protoporphyrin molecular catalyst immobilized onto a pyrolytic graphite (PG) electrode in a purely aqueous electrolyte solution. Previous similar work using immobilized Co porphyrins or Co phthalocyanines has shown the capability of Co-based catalysts to achieve a high FE towards CO, which is highly sensitive to pH and potential16,17,18. Our work confirms that immobilized Co-based porphyrins are good CO2 reduction electrocatalysts capable of producing multi-electron products such as methane and methanol. More significantly, our work underscores the important role of pH in steering the catalytic activity and selectivity towards CO and CH4, especially in the very narrow pH=1–3 range in the absence of coordinating anions. This high sensitivity to pH is explained by a mechanism highlighting the important role of the initial electron transfer in activating CO2 electrochemically. We also demonstrate how such a mechanism for CO2 reduction manifests experimentally and how this property can be exploited to suppress concomitant hydrogen evolution. Furthermore, we show that the overpotential and corresponding turnover frequency (TOF) for CO2 reduction of our catalyst compare favourably to the best molecular porphyrin-based catalyst in the literature10. Therefore, we believe that these insights may have significant implications for the design of new and improved molecular catalyst electrodes and for the formulation of optimized process conditions for efficient electrochemical CO2 reduction to CO as well as to products reduced to a more significant degree.

## Results

### Voltammetry and online electrochemical mass spectrometry

The Co protoporphyrin-coated PG (CoPP-PG) electrode was prepared following a procedure described earlier19 and was detailed in the Methods section. In situ electrochemical scanning tunnelling microscopy and atomic force microscopy images of iron and zinc protoporphyrins on basal plane graphite electrodes by Tao et al.20 suggest that these molecules form monolayer films on the electrode with the molecules lying flat. The blank cyclic voltammograms of the PG electrode, the CoPP-PG electrode in 0.1 M HClO4 and the voltammetry of the dissolved CoPP in the same electrolyte are compared in Supplementary Fig. 1. The voltammetry in Supplementary Fig. 1 shows the reversible redox peak of the Co3+/Co2+ transition at 0.8–0.85 V versus reversible hydrogen electrode (RHE), from which the coverage of the Co-PP on the PG electrode can be determined to be ca. 4 × 10−10 mol cm−2, which is in good agreement with previous experiments of protoporphyrins on PG19,21. No further redox transition of the CoPP is observed at more negative potential, with the onset of hydrogen evolution being at ca. −0.5 VRHE. However, we note that we have previously observed a Co2+/Co+ transition at ca. −0.6 V versus NHE for CoPP immobilized in a DDAB (didodecyl dimethylammonium bromide) film on PG19. The observation of this peak in the DDAB films may be related to the higher hydrophobicity of DDAB. The Co2+/Co+ redox transition has previously been associated with the onset of electrocatalytic hydrogen evolution on Co porphyrins22.

Figure 1 shows the voltammetry at 1 mV s−1 of the CoPP-PG electrode in unbuffered 0.1 M perchlorate solution of pH=1–3, saturated with CO2, together with the mass signals corresponding to H2 (m/z=2), CH4 (m/z=15, corresponding to the CH3 fragment) and CO (m/z=28) as measured simultaneously using online electrochemical mass spectrometry (OLEMS)23. The OLEMS experiment samples the gases formed at the electrode surface by a tip covered with a hydrophobic membrane placed at a distance of ca. 10 μm from the surface. This technique can follow gas production online during cyclic voltammetry (CV). Calibration of our experiment is cumbersome as the signals depend on parameters that are not easy to control (tip distance and tip porosity). Quantitative measurements were therefore performed using long-term electrolysis combined with gas chromatography (to be discussed later). Depending on the quality of the gas-sensing tip used in the OLEMS experiment shown in Fig. 1, m/z=31 was also measured, corresponding to the formation of methanol (Supplementary Fig. 2). Using high-performance liquid chromatography (HPLC), we could also detect HCOOH as one of the products (Supplementary Fig. 3), although both HCOOH and methanol appear to be minority products under these conditions. This confirms, for the first time in a single study, that all four products, CO, HCOOH, CH3OH and CH4 can be formed from CO2 reduction on a Co-based porphyrin. Figure 1a,d,g measured at pH=1 shows that the reduction current is accompanied by the simultaneous formation of H2 and CH4. The m/z=28 signal in Fig. 1 was not corrected for the CO2 fragmentation, and therefore the CO signal combines CO production from CO2 electroreduction with CO formation from CO2 fragmentation in the mass spectrometer (MS). This explains why the CO signal decreases for more negative potentials at which the CO2 reduction rate is higher, as a result of the lower local CO2 concentration near the electrode surface. However, at pH=2 and 3, an increase in the CO signal with more negative potential is observed, simultaneously with the CH4 production, suggesting that CO is an intermediate in the reaction (as also suggested by the fact that CO may be reduced to CH4 on CoPP-PG; Fig. 4 below). Most significantly, at pH=3, CO and CH4 production is observed at less-negative potentials than H2 evolution, showing that the CO2 reduction has a different pH dependence from the hydrogen evolution reaction. We chose to restrict ourselves to pH≤3 in perchlorate solution in order to avoid the interference of buffering anions such as bicarbonate or phosphate (see below) with the CO2 reduction process.

We have performed a number of experiments to convince ourselves that the Co-PP is indeed the active catalytic centre turning over dissolved CO2. On the unmodified PG electrode and on a PG electrode modified with Co-free protoporphyrin, H2 evolution was observed, but no CO2 reduction (Supplementary Figs 5 and 6). A PG electrode onto which a small amount of Co was electrodeposited was also tested for CO2 reduction, but showed no activity (Supplementary Fig. 7). Finally, the reduction of isotopically labelled 13CO2 in deuterated water yielded m/z=19 (corresponding to 13CD3) as reduction product (Supplementary Fig. 8), which irrefutably proves the reduction of dissolved CO2 into methane. These combined results show that the immobilized Co protoporphyrin is responsible for the production of CO and methane from CO2 electroreduction.

As mentioned, the most important conclusion from Fig. 1 is the remarkable role of the pH. Initially, we performed the CO2 reduction experiments at pH=2 and 3 in buffered phosphate solution, also yielding methane as a product but with a pH dependence that was not straightforward to understand. Therefore, we decided to remove the buffering phosphate anions, as they are suspected to interfere with the reactivity by coordinating to the catalytic centre24 or interacting with the catalytic intermediates. In non-adsorbing perchlorate solution, the role of the proton concentration can be better understood by comparing the voltammetry of the CoPP-PG in the absence of CO2 at pH=1–3, as shown in Fig. 2. At pH=1, there is only a single catalytic reduction wave in the potential window studied, corresponding to the reduction of H+ to H2. The voltammetry at pH=2 and 3 shows two waves, one at less-negative potential that is proportional to the H+ concentration and corresponds to H+ reduction, and one starting at −1.1 V that corresponds to H2O reduction. This is also reflected in the H2 formation profiles observed in the mass signals in Fig. 1. We must also take into account here that because of the relatively low proton concentration at pH=3, the direct proton reduction quickly runs into diffusion limitations, and further H2 evolution can only take place at more negative potentials by direct water reduction, which does not suffer from such diffusion limitations. By comparing the results in Figs 1 and 2, we conclude that H2 evolution dominates over CO2 reduction in the presence of a high concentration of protons in solution, whereas the opposite is the case for pH=3. The activation of CO2 is apparently less sensitive to the presence of protons, implying that water molecules are just as powerful in hydrogenating the activated CO2. This remarkable pH dependence is somewhat similar to observations made by Noda et al.25 during CO2 reduction on a gold electrode. The important new finding here is that this small pH shift is the key in favouring CO2 reduction over H2 evolution, also on our molecular catalyst, especially in the absence of buffering anions. This is also evidenced by the FE measurements summarized in Fig. 3, to be discussed next. A mechanistic explanation for this pH sensitivity will be given in the Discussion section.

The FE for the simultaneous CO2 and water reduction to hydrogen, CO and methane was determined separately with long-term electrolysis experiments, using a gas chromatography setup coupled to an electrochemical cell, as detailed elsewhere26,27. Figure 3 shows results for CO and CH4 at pH=1 and 3 for different potentials. The remaining current is used to form H2. The quantitative data and error bars are summarized and further explained in Supplementary Table 1. HCOOH was also observed as a minority product at pH=1 using HPLC, but was not observed at pH=3 (Supplementary Fig. 3). As mentioned above, methanol was observed as a product using OLEMS (Supplementary Fig. 2), but it remained below the detection limit during the gas chromatography (GC) measurements. At pH=1, the FE to CO and methane is low, on the order of a per cent, and the dominant product is H2, and therefore for pH=1, we show results at only a single potential in Fig. 3. Note, however, that at pH=1, more methane is produced than CO. At pH=3, a dramatic change in selectivity is observed, with now CO being a majority product, especially at less cathodic potentials, for which the FE to CO is 40%. This high selectivity is maintained for at least 1 h during the long-term electrolysis experiment at fixed potential (Supplementary Fig. 9), testifying to the good stability of the catalyst. The stability and integrity of the CoPP-PG electrode was also confirmed by pre- and post-electrolysis analysis using X-ray Photoelectron Spectroscopy (XPS), Raman and nuclear magnetic resonance (Supplementary Figs 10–12). Raman spectroscopy showed no significant change in the spectral features of the CoPP-PG surface; XPS showed no change in Co oxidation state after 1 h of electrolysis; and nuclear magnetic resonance showed no decomposition products in solution that could be related to CoPP. Figure 3 also illustrates that less methane is produced at pH=3 as compared with pH=1. We ascribe this lower methane production to the slower reduction of CO to CH4 at pH=3 compared with pH=1 (see next paragraph). The efficiency towards CO can be further boosted by performing the experiment at higher CO2 pressure. Figure 3 illustrates this for a CO2 pressure of 10 atm, which leads to a FE of 60% at pH=3 at a potential of −0.6 V. Note that at pH=1, both the efficiency towards CO and CH4 increases to a few % when the reduction is carried out at increased CO2 pressure. We emphasize that OLEMS and GC experiments exhibited good consistency and reproducibility. The error bars shown in Fig. 3 were based on single long-term electrolysis experiments sampled every 6 min.

### Reduction of other compounds

To determine the involvement of potential intermediates, we also studied the reduction of HCOOH, CO and formaldehyde (HCHO), by combined voltammetry-OLEMS. HCOOH was not reduced at either pH=1 or 3 (Supplementary Fig. 13), and is therefore an end product, not an intermediate. Figure 4 shows the voltammetry and associated OLEMS mass signals on the CoPP-PG electrode for CO reduction at pH=1 and 3, and for HCHO reduction at pH=1. Remarkably, CO is clearly reduced to methane at pH=1, simultaneous with H2 evolution, but the CO reduction activity is much lower compared with hydrogen evolution at pH=3, with an insignificant amount of CH4 detected. This observation is consistent with the results in Fig. 3, showing that methane production from CO2 is lower at pH=3. HCHO is reduced to methane at pH=1 and 3 (Fig. 4 only shows pH=1). Interestingly, HCHO is not reduced to significant amounts of methanol, whereas methanol is the product of HCHO reduction on copper electrodes6. Figure 4 suggests that CO and HCHO, or their catalyst-bound derivatives, are intermediates in the reaction mechanism from CO2 to CH4, but HCOOH is not. It also shows that the reduction of CO exhibits a different pH dependence compared with CO2 reduction, explaining why the selectivity of CO2 towards CO increases with higher pH, but the selectivity towards CH4 decreases with higher pH.

## Discussion

The results presented above give unique new insights into the mechanism of CO2 electroreduction on immobilized Co protoporphyrins, and the observed pH dependence reveals the important role of the initial electron transfer to CO2 in the overall mechanism as explained below, and as illustrated in our suggested mechanistic scheme in Fig. 5. At pH=1, the dominant reaction is hydrogen evolution:

At pH=3, the main origin of hydrogen evolution is direct water reduction:

with reaction 1 generating a smaller amount of H2 at less-negative potential due to diffusion limitations (Fig. 2). This observation is very similar to recent experiments on platinum electrodes28. The observation that CO2 reduction to CO becomes much more dominant at higher pH, must mean that CO2 activation does not sensitively depend on the presence of protons, and hence must involve an intermediate that can easily react with water at any pH. Such an intermediate is most likely a negatively charged Brønsted base, and the most obvious candidate for this intermediate is a CO2 radical anion25,29,30 bound to the Co complex ‘M’:

which subsequently reacts with water to a metal-bound carboxyhydroxyl intermediate:

The formation of the CO2·− radical anion normally has a very negative redox potential3,8, but may be shifted to less-negative potential by the stabilization provided by the coordination of CO2·− to the catalyst. The carboxyhydroxyl intermediate then generates CO:

with the CO subsequently dissociating from the complex. Owing to the presence of the negatively charged intermediate in reaction 4, the pH dependence of this pathway is different from that of the mechanism for reactions 1 and 2, in which no such intermediate is assumed. For reactions 1 and 2, we assume:

and

which involve concerted proton-coupled electron transfer at every step31,32. Reaction 4 is different from the reaction suggested by the Density Functional Theory (DFT) calculations of Leung et al.29,30 because we specify that the proton donor may be water, rather than H+, owing to the basic character of the CO2 radical anion intermediate. Note that in this mechanism, the reaction rate for CO2 reduction itself does not depend on pH, only its relative rate with respect to the hydrogen evolution. Another way of formulating our mechanism is by stating that in the potential window of interest, CO2 reduction is approximately zeroth order in proton concentration, while hydrogen evolution is first order in proton concentration.

The further reduction of CO must be slower than its generation, explaining the relatively low overall FE of CO2 reduction to methane. To explain the pH dependence of CO reduction and methane selectivity from CO2, we must assume that CO is reduced to methane without the involvement of negatively charged intermediates. Our experiments also show that an intermediate or by-product of CO reduction to methane is HCHO. Our suggested overall mechanism is summarized in Fig. 5.

The above mechanism, which we believe explains our observations consistently, has important implications for future catalyst design. The onset potential for CO2 reduction is determined by reaction 3, that is, by the stabilization of the CO2 radical anion coordinated to the complex. As noted above, the onset potential appears to be related to the Co2+/Co+ redox transition on the basis of CV19 and also on the previous observation that the Co+ state is the active state for proton reduction22. Nielsen and Leung have also concluded, based on literature data and their own DFT calculations, that CO2 binds to the Co+ state of the porphyrin29,30. Therefore, we assume that Co+ state of the CoPP is the catalytically active state. The closer the Co2+/Co+ redox potential lies to the overall equilibrium potential, the lower is the overpotential for CO2 reduction. Reaction 3 is therefore the potential-determining step33,34. The key point is that the formation of this intermediate is decoupled from proton transfer, as otherwise we cannot explain the observed pH dependence, an important feature not included in the recent DFT calculations of Tripkovic et al.9. Therefore, future calculations must take into account the existence of such intermediates, and should aim at enhancing the stability of the intermediate in reaction 3. Moreover, in order to have a higher overall efficiency towards methane, the rate of the reduction of CO to methane must be enhanced. Presumably, the rate of this reaction can be tuned by the binding of CO to the complex. This will also require further experiments and calculations aimed at screening various catalyst alternatives. We also believe that our mechanism provides a possible rationale for tuning the H2/CO ratio from electrochemical CO2 reduction, as was recently reported for a Ru-based molecular catalyst in aqueous solution35.

A final word on the overpotential and the TOFs of our catalyst in comparison with previous work on molecular catalysts for CO2 electroreduction to CO. From our experiment, we calculate TOFs through the formula: (FE for CO production) × (current density/2F)/(number of Co-PP per cm2), where F=Faraday constant. In Fig. 3, the average current densities measured over 1 h at potentials of −0.6 and −0.8 V versus RHE, corresponding to overpotentials of ca. 0.5 and 0.7 V, were 0.08 and 0.16 mA cm−2 (at atmospheric pressure), respectively. This corresponds to TOFs of ca. 0.2 and 0.8 s−1. Costentin et al.10 have recently reported on the enhanced activity of a modified Fe tetraphenylporphyrin for CO2 reduction to CO in a mixed DMF–water solvent. In their experiment, the porphyrin was in solution. Their measured current densities and corresponding effective CO2 turnover rates are very similar to ours, namely, 0.3 mA cm−2 (see Supplementary Fig. 5 in their paper) at a similar overpotential of ca. 0.5 V. Note that this comparison does not take into account that the solubility of CO2 is considerably higher in DMF–water mixtures than in water36, thereby leading to correspondingly higher turnover rates in the DMF–water mixture. From a mathematical model for their reactive system including mass transport of the catalyst to the electrode surface, they report a catalytic TOF of ca. 3,000 s−1. This is a TOF of a homogeneous catalyst corrected for the slow mass transport in their system, and can therefore not be compared directly with the ‘effective’ TOF of our heterogeneous catalyst. However, from the similar real current densities at a similar overpotential, we believe that we can safely state that our immobilized catalyst system has a similar efficiency.

Summarizing, we have shown that a Co protoporphyrin immobilized on a PG electrode can reduce CO2 to CO and even to the 6- and 8-electron products methanol and methane, in a purely aqueous electrolyte phase, with a moderate overpotential of ca. 0.5 V. The efficiency of our catalyst (that is, effective rate at given overpotential) compares favourably with best porphyrin-based catalyst reported in the literature10. For optimal FE, that is, low concomitant H2 production, the proton concentration needs to be suitably tuned to the CO2 concentration. The pH-dependent activity and selectivity are explained by a mechanism in which the initial step of CO2 reduction leads to a catalyst-bound CO2·− radical anion. This intermediate has a strong Brønsted-base character and can abstract a proton from water, thereby leading to an overall reactivity of the CO2 reduction whose pH dependence is substantially different from the competing H2 evolution. Lowering the potential for the formation of this catalyst-bound CO2·− radical anion is therefore the key to making a better catalyst with a lower overpotential, and a suitable adjustment of pH will contribute significantly to a high FE of such a catalyst. The further reduction of CO to methane and methanol is slow owing to the weak binding of CO to the catalyst, and owing to the fact that CO reduction prefers a more acidic environment. These new insights into the mechanism of CO2 reduction on immobilized molecular catalysts in aqueous solution provide important design rules for future catalyst improvement.

## Methods

### Electrochemistry and chemicals

The experiments were performed on home-made PG electrodes (Carbone-Lorraine; diameter, 5 mm). Before each experiment, the electrodes were polished using P500 and P1000 SiC sandpaper consecutively, and were ultrasonicated in ultrapure water (Milli-Q gradient A10 system, 18.2 MΩ cm) for 1 min and dried in a flow originating from compressed air. The electrodes were subsequently immersed in the Co protoporphyrin (Frontier Scientific) solution (0.5 mM in borate buffer) for 5 min to immobilize the protoporphyrin on the surface and rinsed with ultrapure water before the experiments. A one-compartment electrochemical cell was used, with a platinum flag as counter electrode and a RHE as a reference, to which all potentials in this work are referred. The reference electrode was separated from the working electrode compartment through a Luggin capillary. An Ivium potentiostat/galvanostat (IviumStat) was used for the electrochemical measurements. Solutions were prepared from HClO4 (Merck, 70%), NaClO4 (Sigma-Aldrich, ≥98.0%), NaOH (Sigma-Aldrich, 99.998%), borate (Sigma-Aldrich) and ultrapure water. Argon (Hoekloos, purity grade 6.0) was purged though the solutions for 30 min before the experiment to remove dissolved oxygen. The reported current densities refer to the geometric surface area.

### Online electrochemical mass spectrometry

The volatile products of the CO2 electrochemical reduction were detected using online electrochemical mass spectroscopy (OLEMS) with an evolution mass spectrometer system (European Spectrometry systems Ltd)23. A porous Teflon tip (inner diameter, 0.5 mm) with a pore size of 10–14 μm was positioned close (10 μm) to the centre of the electrode. Before the experiments, the tip was dipped into a 0.2-M K2Cr2O7 in 2 M H2SO4 solution for 15 min and rinsed with ultrapure water thoroughly. The gas products were collected through a polyether ether ketone (PEEK) capillary into the mass spectrometer. A 2,400-V secondary electron multiplier (SEM) voltage was applied for all the fragments except for hydrogen (m/z=2) which is 1,500 V. The OLEMS measurement was conducted while CV was scanning from 0 to −1.5 V and back at a scan rate of 1 mV s−1.

### Gas chromatography

The quantitative measurements of the gas products were carried out using GC26,27. At atmospheric pressure, CO2 was continuously purged through a two-compartment flow cell with a volume of 12 ml for each compartment at a rate of 5 ml min−1 for 30 min to saturate the electrolyte. The flow rate declined to 2 ml min−1 while a constant potential was applied for 1 h. The reference electrode used here is a Ag/AgCl electrode. The experiments at high CO2 pressure (P=10 atm) were conducted in a stainless-steel autoclave using a Pt mesh as a counter electrode, and a home-made Ag/AgCl in 3 M KCl as a reference electrode. All potentials were scaled to RHE after the experiments for both atmospheric and high pressure, with E(versus Ag/AgCl)=E(versus RHE)−0.197 V−pH × 0.059. CO2 was continuously purged through the autoclave before and during the electrolysis with a flow rate of 50 ml min−1. The reactor effluent was sampled via GC once every 6 min. CO, CO2, H2 and hydrocarbons were simultaneously separated using two series columns in series (a ShinCarbon 2 m micropacked column and a Rtx-1 column). The quantitative analysis of the gas products was performed using a thermal conductivity detector (H2 and CO) and flame ionization detector (hydrocarbons).

### Online HPLC

HPLC (Prominence HPLC, Shimadzu) was used to detect liquid products produced during electrochemical reduction of CO2 using a method described in previous work37. Samples were collected using a Teflon tip (inner diameter: 0.38 mm) positioned 10 μm from the centre of the electrode surface (diameter: 1 cm). The sample volume collected was 60 μl stored in a 96-well microtitre plate (270 μl per well, Screening Device b.v.) using an automatic fraction collector (FRC-10A, Shimadzu). The flow rate of the sample collection was adjusted to 60 μl min−1 with a Shimadzu pump (LC-20AT). A linear sweep voltammogram was recorded while the sample was collecting at a scan rate of 1 mV s−1 from 0 to −1.5 V versus RHE. The microtitre plate with collected samples was then placed in an auto-sampler (SIL-20A) holder and 30 μl of sample was injected into an Aminex HPX 87-H (Bio-Rad) column. The eluent was diluted sulfuric acid (5 mM) with a flow rate of 0.6 ml min−1. The temperature of column was maintained at 85 °C using a column oven (CTO-20A) and the separated compounds were detected with a refractive index detector (RID-10A).

How to cite this article: Shen, J. et al. Electrocatalytic reduction of carbon dioxide to carbon monoxide and methane at an immobilized cobalt protoporphyrin. Nat. Commun. 6:8177 doi: 10.1038/ncomms9177 (2015).

## References

1. 1

Costentin, C., Robert, M. & Saveant, J.-M. Catalysis of the electrochemical reduction of carbon dioxide. Chem. Soc. Rev. 42, 2423–2436 (2013).

2. 2

Qiao, J., Liu, Y., Hong, F. & Zhang, J. A review of catalysts for the electroreduction of carbon dioxide to produce low-carbon fuels. Chem. Soc. Rev. 43, 631–675 (2014).

3. 3

Hori, Y. in Modern Aspects of Electrochemistry Vol. 42, (eds Vayenas C. G., White R. E., Gambao-Aldaco M. E. 89–189Springer, New York (2008).

4. 4

Finn, C., Schnittger, S., Yellowlees, L. J. & Love, J. B. Molecular approaches to the electrochemical reduction of carbon dioxide. Chem. Commun. 48, 1392–1399 (2012).

5. 5

Koper, M. T. M. Thermodynamic theory of multi-electron transfer reactions: implications for electrocatalysis. J. Electroanal. Chem. 660, 254–260 (2011).

6. 6

Schouten, K. J. P., Kwon, Y., van der Ham, C. J. M., Qin, Z. & Koper, M. T. M. A new mechanism for the selectivity to C1 and C2 species in the electrochemical reduction of carbon dioxide on copper electrodes. Chem. Sci. 2, 1902–1909 (2011).

7. 7

Li, C. W., Ciston, J. & Kanan, M. W. Electroreduction of carbon monoxide to liquid fuel on oxide-derived nanocrystalline copper. Nature 508, 504–507 (2014).

8. 8

Savéant, J.-M. Molecular catalysis of electrochemical reactions. mechanistic aspects. Chem. Rev. 108, 2348–2378 (2008).

9. 9

Tripkovic, V. et al. Electrochemical CO2 and CO reduction on metal-functionalized porphyrin-like graphene. J. Phys. Chem. C 117, 9187–9195 (2013).

10. 10

Costentin, C., Drouet, S., Robert, M. & Savéant, J.-M. A local proton source enhances CO2 electroreduction to CO by a molecular Fe catalyst. Science 338, 90–94 (2012).

11. 11

Fisher, B. J. & Eisenberg, R. Electrocatalytic reduction of carbon dioxide by using macrocycles of nickel and cobalt. J. Am. Chem. Soc. 102, 7361–7363 (1980).

12. 12

Kapusta, S. & Hackerman, N. Carbon dioxide reduction at a metal phthalocyanine catalyzed carbon electrode. J. Electrochem. Soc. 131, 1511–1514 (1984).

13. 13

Furuya, N. & Matsui, K. Electroreduction of carbon dioxide on gas-diffusion electrodes modified by metal phthalocyanines. J. Electroanal. Chem. Interfacial Electrochem. 271, 181–191 (1989).

14. 14

Sonoyama, N., Kirii, M. & Sakata, T. Electrochemical reduction of CO2 at metal-porphyrin supported gas diffusion electrodes under high pressure CO2. Electrochem. Commun. 1, 213–216 (1999).

15. 15

Magdesieva, T. V., Yamamoto, T., Tryk, D. A. & Fujishima, A. Electrochemical Reduction of CO2 with transition metal phthalocyanine and porphyrin complexes supported on activated carbon fibers. J. Electrochem. Soc. 149, D89–D95 (2002).

16. 16

Atoguchi, T., Aramata, A., Kazusaka, A. & Enyo, M. Cobalt(II)-tetraphenylporphyrin-pyridine complex fixed on a glassy carbon electrode and its prominent catalytic activity for reduction of carbon dioxide. Chem. Commun. 3, 156–157 (1991).

17. 17

Yoshida, T. et al. Selective electroacatalysis for CO2 reduction in the aqueous phase using cobalt phthalocyanine/poly-4-vinylpyridine modified electrodes. J. Electroanal. Chem. 385, 209–225 (1995).

18. 18

Tanaka, H. & Aramata, A. Aminopyridyl cation radical method for bridging between metal complex and glassy carbon: cobalt(II) tetraphenylporphyrin bonded on glassy carbon for enhancement of CO2 electroreduction. J. Electroanal. Chem. 437, 29–35 (1997).

19. 19

de Groot, M. T. & Koper, M. T. M. Redox transitions of chromium, manganese, iron, cobalt and nickel protoporphyrins in aqueous solution. Phys. Chem. Chem. Phys. 10, 1023–1031 (2008).

20. 20

Tao, N. J., Cardenas, G., Cunha, F. & Shi, Z. In situ STM and AFM study of protoporphyrin and iron(III) and zinc(II) protoporphyrins adsorbed on graphite in aqueous solutions. Langmuir 11, 4445–4448 (1995).

21. 21

de Groot, M. T., Merkx, M., Wonders, A. H. & Koper, M. T. M. Electrochemical reduction of NO by hemin adsorbed at pyrolitic graphite. J. Am. Chem. Soc. 127, 7579–7586 (2005).

22. 22

Kellett, R. M. & Spiro, T. G. Cobalt porphyrin electrode films as hydrogen catalysts. Inorg. Chem. 24, 2378–2382 (1985).

23. 23

Wonders, A. H., Housmans, T. H. M., Rosca, V. & Koper, M. T. M. On-line mass spectrometry system for measurements at single-crystal electrodes in hanging meniscus configuration. J. Appl. Electrochem. 36, 1215–1221 (2006).

24. 24

Diaz-Morales, O., Hersbach, T. J. P., Hetterscheid, D. G. H., Reek, J. N. H. & Koper, M. T. M. Electrochemical and spectroelectrochemical characterization of an iridium-based molecular catalyst for water splitting: turnover frequencies, stability, and electrolyte effects. J. Am. Chem. Soc. 136, 10432–10439 (2014).

25. 25

Noda, H., Ikeda, S., Yamamoto, A., Einaga, H. & Ito, K. Kinetica of electrochemical redcution of carbon-dioxide on a gole electrode in phosphate buffer solutions. Bull. Chem. Soc. Jpn 68, 1889–1895 (1995).

26. 26

Kas, R. et al. Electrochemical CO2 reduction on Cu2O-derived copper nanoparticles: controlling the catalytic selectivity of hydrocarbons. Phys. Chem. Chem. Phys. 16, 12194–12201 (2014).

27. 27

Kas, R., Kortlever, R., Yılmaz, H., Koper, M. T. M. & Mul, G. Manipulating the hydrocarbon selectivity of copper nanoparticles in CO2 electroreduction by process conditions. ChemElectroChem. 2, 354–358 (2015).

28. 28

Strmcnik, D. et al. Improving the hydrogen oxidation reaction rate by promotion of hydroxyl adsorption. Nat. Chem. 5, 300–306 (2013).

29. 29

Leung, K., Nielsen, I. M. B., Sai, N., Medforth, C. & Shelnutt, J. A. Cobalt−porphyrin catalyzed electrochemical reduction of carbon dioxide in water. 2. mechanism from first principles. J. Phys. Chem. A 114, 10174–10184 (2010).

30. 30

Nielsen, I. M. B. & Leung, K. Cobalt−porphyrin catalyzed electrochemical reduction of carbon dioxide in water. 1. a density functional study of intermediates. J. Phys. Chem. A 114, 10166–10173 (2010).

31. 31

Koper, M. T. M. Theory of the transition from sequential to concerted electrochemical proton-electron transfer. Phys. Chem. Chem. Phys. 15, 1399–1407 (2013).

32. 32

Koper, M. T. M. Theory of multiple proton-electron transfer reactions and its implications for electrocatalysis. Chem. Sci. 4, 2710–2723 (2013).

33. 33

Nørskov, J. K. et al. Origin of the overpotential for oxygen reduction at a fuel-cell cathode. J. Phys. Chem. B 108, 17886–17892 (2004).

34. 34

Koper, M. M. Analysis of electrocatalytic reaction schemes: distinction between rate-determining and potential-determining steps. J. Solid State Electrochem. 17, 339–344 (2013).

35. 35

Kang, P., Chen, Z., Nayak, A., Zhang, S. & Meyer, T. J. Single catalyst electrocatalytic reduction of CO2 in water to H2+CO syngas mixtures with water oxidation to O2. Energ. Environ. Sci. 7, 4007–4012 (2014).

36. 36

Jödecke, M., Pérez-Salado Kamps, Á. & Maurer, G. An experimental investigation of the solubility of CO2 in (N,N-dimethylmethanamide+water). J. Chem. Eng. Data 57, 1249–1266 (2012).

37. 37

Kwon, Y. & Koper, M. T. M. Combining voltammetry with HPLC: application to electro-oxidation of glycerol. Anal. Chem. 82, 5420–5424 (2010).

## Acknowledgements

J.S. acknowledges the award of a grant of the Chinese Scholarship Council. This work was financed in part by NanoNextNL, a micro and nanotechnology consortium of the Government of the Netherlands and 130 partners, by the BioSolar Cells open innovation consortium, supported by the Dutch Ministry of Economic Affairs, Agriculture and Innovation, and by The Netherlands Organization for Scientific Research (NWO).

## Author information

Authors

### Contributions

J.S. performed all the electrochemistry, OLEMS, GC and HPLC experiments. R. Kortlever assisted in the HPLC, OLEMS and GC experiments. R. Kas assisted in the GC and XPS measurements. Y.Y.B. assisted in the HPLC and OLEMS experiments, specifically those detecting methanol. O.D.-M., and I.L.-Y. assisted in the electrochemistry experiments. Y.K. assisted in the HPLC experiments and K.J.P.S. assisted in the OLEMS experiments. G.M. provided access to the GC and XPS measurements. J.S. and M.T.M.K. interpreted data and co-wrote the manuscript; and all authors commented on the manuscript. M.T.M.K. conceived the idea.

### Corresponding author

Correspondence to Marc T. M. Koper.

## Ethics declarations

### Competing interests

The authors declare no competing financial interests.

## Supplementary information

### Supplementary Information

Supplementary Figures 1-14, Supplementary Table 1 and Supplementary References (PDF 1179 kb)

## Rights and permissions

Reprints and Permissions

Shen, J., Kortlever, R., Kas, R. et al. Electrocatalytic reduction of carbon dioxide to carbon monoxide and methane at an immobilized cobalt protoporphyrin. Nat Commun 6, 8177 (2015). https://doi.org/10.1038/ncomms9177

• Accepted:

• Published:

• DOI: https://doi.org/10.1038/ncomms9177

• ### The boosting of electrocatalytic CO2-to-CO transformation by using the carbon nanotubes-supported PCN-222(Fe) nanoparticles composite

• Lin-Wei Xu
• She-Liang Qian
• Zong-Wei Li

Journal of Materials Science (2022)

• ### Effects of Topological Defect on the Energy Spectra and Thermo-magnetic Properties of $$CO$$ Diatomic Molecule

• C. O. Edet
• A. N. Ikot

Journal of Low Temperature Physics (2021)

• ### Two-dimensional transition metal phthalocyanine sheet as a promising electrocatalyst for nitric oxide reduction: a first principle study

• Shiqiang Liu
• Yawei Liu
• Tao Yuan

Environmental Science and Pollution Research (2021)

• ### Electron-withdrawing functional ligand promotes CO2 reduction catalysis in single atom catalyst

• Xinyi Ren
• Song Liu
• Bin Liu

Science China Chemistry (2020)

• ### Reticular chemistry in electrochemical carbon dioxide reduction

• Yanfang Wang
• Yuexiang Li
• Zhouguang Lu

Science China Materials (2020)