Growing concerns about global warming and increasing demands for energy have prompted the search for renewable energy sources and the development of improved energy storage options to replace fossil fuel technologies1,2,3,4,5,6,7. In many of the innovative approaches for addressing these challenges, photoelectrolyzing or electrolyzing water to produce oxygen and hydrogen gases is a highly scalable method for storing chemical fuels derived from renewable sources8,9,10. Therefore, the development of abundant, robust and efficient catalysts for photoelectrochemical/electrochemical production of oxygen are crucial for the long-term viability of our community.

In recent years, various materials including simple oxides11,12,13,14,15, combinations of transition metal oxides16,17,18,19,20, phosphates21,22, oxyhydroxide23,24, perovskites10,25 and nanocomposite materials26,27,28,29 have been used to induce an oxygen evolution reaction (OER) in alkaline environment. Despite the interesting catalytic behaviours of existing materials, an inexpensive and reliable electrocatalyst that does not develop defects to hinder charge transfer across the electrolyte/catalyst interface has yet to be achieved. Recent reports of highly economic and efficient electrochemical catalysts have significantly advanced this technology14, however the largest challenge concerning the reliability of the catalyst remains yet unconquered. A major reason for the slow progress of reliable catalysts in the OER is that the electrocatalyst bears most of the charge carriers during the harsh oxidization process because the OER normally occurs under a high anodic potential. A highly stable electrocatalyst has to transfer charge carriers effectively to the OER electrocatalyst/electrolyte interface yet retain a sufficient amount of oxidized species during anodization. To shed light on such complex surface reactions, we need a tool that allows in situ observation of the active phase of metal centres under anodization and a novel strategy to protect electrocatalysts under such harsh conditions in order to achieve reliable catalysts for OER.

The oxygen evolution activity of electrocatalysts depends strongly on corresponding surface structures and the adsorption energies of intermediates on metal oxide surfaces30,31. Generally speaking, surface structure can affect the activity of electrocatalysts and surface states can be further altered by introducing foreign elements, which leads to considerable decreases in overpotential and therefore increases in activity during the OER. In practical conditions, the reactions of OER are only involved within a several nanometre region of the catalyst surface, and in situ studies within this limited region are essential and extremely challenging. Recently, in situ Raman spectroscopy has been conducted to achieve this goal to reveal the intermediates through surface binding of OER reactants11. Moreover, Zhang et al.32 identified the surface bonding formation and relevant intermediates through time-resolved rapid-scan Fourier transform infrared spectroscopy, in which a surface superoxide species was revealed in a fast reaction cycle of OER. However, for designing efficient OER catalysts, in situ study for structure and crystallinity at the atomic level of the metal centres in the catalyst surface are vital and have yet to be achieved. The development of tools to study and investigate the surface of catalysts could provide a powerful means to elucidate fundamental processes in OER catalyst and eventually lead to a novel design principle.

Herein, we investigate single-crystal Co3O4 nanocubes with underlaying of uniform cobalt oxide (CoO) layers as OER electrocatalysts. The strategy is to incorporate a surface layer well adapted to the active phases of the catalytic metal centres to enhance the stability of the electrocatalysts. Furthermore, we develop an in situ grazing-angle X-ray diffraction method to track the atomic-scale structural changes on the surface of the electrode during OER in liquid conditions. This powerful technique reveals that the CoO layer can reversibly adapt to the harsh conditions of OER through reversible structural transformations, which results in a highly robust electrocatalyst. In addition, we choose Co3O4 because of its abundance, low cost, low electrical resistance, thermodynamic stability and moderate overpotential in neutral and alkaline conditions33. Using single-crystal nanocubes as OER electrocatalysts provide strong mechanical strength, minimal structural disorder and defect-free substrates. The structural defects in materials normally turn into trap states that play a dominant role in limiting carrier transportation, and effective carrier transportation within the substance determines the overall efficiency of the devices34,35. Accordingly, the low trap density of the single-crystal defect-free nanostructure enhances its carrier dynamics and thereby improve the electronic properties of the materials. The CoO layer on the surface of the Co3O4 nanocubes forms a reversible adaption junction, enabling a facile structural transformation18 for chemical reactions (for example, OER) and the formation of active phase without breaking the scaffold of the electrocatalysts (for example, Co3O4 nanocubes) to further reduce the overpotential.


Structural characterization of Co3O4–CoO core–shell nanocube

The pristine Co3O4 nanocubes prepared by using a surfactant-free method, in which Co3O4 nanocubes was formed through a reaction of cobalt hydroxides and dissolved oxygen in an aqueous medium. Sequentially a thin (1 nm) CoO film was prepared on the single-crystal Co3O4 nanocube surface by using reducing agent (sodium borohydride) with an accurate control of CoO covering to form a Co3O4–CoO core–shell nanocube, with the average size of the Co3O4@CoO single-crystal cubes (SCs) <50 nm (Fig. 1a). A high-resolution transmission electron microscope (HRTEM) was employed to characterize the nanostructure of the core–shell cubes (Fig. 1b; Supplementary Fig. 1) and the selected area electron diffraction of the individual nanocube was characteristic of the single-crystal structure. A set of spots were indexed to the Co3O4 spinel structure along the [001] zone axis, and the boundary planes of the nanocube were {100}, {010} and {001} (Fig. 1c). A thin, bright layer with a thickness of 1 nm was located on the surface of the Co3O4, indicating that CoO uniformly covered the entire surface of the Co3O4 nanocube. Corresponding spatial distributions of the compositional elements within the individual nanocube were obtained using a scanning transmission electron microscope–energy-dispersive X-ray line scan through the entire nanocube (indicated in Fig. 1d), revealing that the core–shell nanocube comprised Co and O, and the compositional profiles were symmetrical because of the uniform covering of cobalt oxide. The atomic lattice fringes identified in the HRTEM image was shown in Fig. 1e. It indicated that the nanocube was single crystalline, which was consistent with the result from selected area electron diffraction image. The lattice fringe of a representative nanocube with a d-spacing of 2.8 Å could be assigned to the (220) plane of spinel Co3O4 (JCPDS file nos. 43–1003, a=8.084 Å; Supplementary Fig. 2). It was worth noting that the bright outer layer exhibited a clear lattice fringe with a d-spacing of 2.1 Å, corresponding to the (200) plane of CoO (JCPDS file nos. 78–0431, a=4.2667 Å). To further characterize the thin cobalt oxide layer, electron energy-loss spectroscopy (EELS), a powerful technique for local structural analysis featuring nanometre spatial resolution, was performed. The L3/L2 line ratio for the Co-L edge served as a fingerprint for the Co valence state36, and a 3.2 L3/L2 line ratio for the Co EELS peaks was recorded at the middle of the core–shell nanocube as shown in Fig. 1f. This ratio was consistent with the value regarding Co3O4 (II+III; upper part of Fig. 1f). In the outermost region (lower part), the L3/L2 line ratio for the Co peaks was 4.5, which is close to the expected value for CoO (II). Consequently, a single-crystal Co3O4 nanocube with CoO (1 nm) uniformly covering the surface was characterized, in which nanocube catalysts exposed the energetically preferred (001) surfaces of OER to electrolyte32.

Figure 1: Structural characterization of the Co3O4@CoO single-crystal nanocubes.
figure 1

(a,b) A typical transmission electron micrograph. Scale bar, 200 nm (a); 10 nm (b). (c) Selected area electron diffraction pattern of an individual Co3O4@CoO single-crystal nanocube. (d) The corresponding elemental line scan from the Co and O of an individual Co3O4@CoO single-crystal nanocube. (e) HRTEM image of a Co3O4@CoO single-crystal nanocube. The dark area is the Co3O4 and the light area is the CoO. (f) Corresponding electron energy-loss spectrum of a Co3O4@CoO SC nanocube. The upper spectrum was recorded at the dark area of e and the lower spectrum was recorded at the light region of e.

In situ X-ray spectroscopy studies in liquid environment

Since the catalytic performance is strongly dependent on the relevant surface state of electrocatalysts, it would be highly desirable if surface reactive structures could be monitored in liquid condition. In gas evolution situation, obtaining stable signals and monitoring the surface state of catalysts in liquid environment is an extremely difficult task. To achieve this aim, we customized a reaction cell and utilized the synchrotron radiation light source owing to the extremely high intensity and flux of the light source. An in situ grazing-angle X-ray diffraction approach in liquid environment can be achieved to determine the atomic structure of the catalysts surface in ambient condition (Fig. 2a), especially for gas evolution situation (high potential region). Figure 2b depicts the current density as a function of applied voltage, and are colour coded together with diffracted intensities recorded using 12 keV of synchrotron light. At the early stage (before O2 evolution), main reflexes were attributed to the fluorine-doped tin oxide substrate and the spinel-type Co3O4 phases. No CoO phase was observed, indicating that the CoO layer was too thin to diffract the light source (a few atomic layers). At a higher voltage, accompanying the formation of β-CoOOH (JCPDS file no. 14-0673) on the surface of electrode, the electrodes began oxygen gas evolution in both alkaline and neutral conditions. This suggested that the CoO layer was converted into more active phase with increasing applied potential. When the applied voltage was further increased, a new phase, α-CoOOH (JCPDS file no. 26-0480) was observed. Both alkaline and neutral conditions demonstrated a similar phenomenon that OER was strongly correlative with the formation of metal oxyhydroxide. This was direct evidence for the formation of metal oxyhydroxide during higher oxygen gas evolution (30 mA cm−2) in an in situ liquid environment. Notably, the CoO layer functioned as an adapting junction between electrolyte and catalyst to ease off the strain in the nanocrystal substrates when the active phases were formed. As shown in Fig. 2c, when applied potential was cycled between +2.0 and +0.1 V (versus RHE; Reversible Hydrogen Electrode), the in situ X-ray diffraction approach showed that this junction layer could alter its structure reversibly between metal oxyhydroxide and amorphous phases. This observation revealed that this skin junction could reversibly adapt to the environment (applied potential) and condition change during catalyzing reaction, consequently protecting the underlay catalyst (for example, Co3O4) anodizing from applied bias. Moreover, we performed in situ X-ray absorption in a liquid environment in low throughput current (below +1.7 V versus RHE) by using the setup shown in Supplementary Fig. 3, and the extended X-ray absorption fine structure spectra of Co3O4@CoO SCs were depicted in Fig. 2d. We attributed the first peak at 1.5 Å and the second and third peaks at 2.5 and 3.1 Å, respectively, to the single scattering paths of the closest oxygen (that is, Co–O) and the second/third neighbouring cobalt metals (that is, Co–Co) surrounding the absorbing Co atoms. The Co–O distance (1.5 Å) was typical for a Co3O4 normal spinel-type structure, and the first Co–Co distance (2.5 Å) was typical for a Co (III)–Co bond with octahedrally coordinated Co atoms in a normal spinel structure. The second distance of 3.1 Å was attributed to Co (II)–Co bonds with tetrahedrally coordinated Co atoms. These results were consistent with the results determined for the spinel structure of Co3O4. Notably, a new peak was observed at 3.8 Å when a higher potential of +1.7 V (versus RHE) was applied to a Co3O4@CoO SC electrode. The peak was attributed to the formation of cobalt oxyhydroxide phase on the surface of the Co3O4 SC thus led to a new scattering path of Co–O from the cobalt oxyhydroxide phase, which was consistent with the results from X-ray photoelectron spectroscopy (Fig. 2e) and further confirmed the observation in our X-ray diffraction experiments. It was noted that the CoOOH layer formed from Co3O4 nanocubes without covering of CoO skin was characteristic of rough nature. Unlike Co3O4 nanocubes, the CoOOH layer formed from Co3O4 nanocubes with covering of CoO skin exhibited a continuous and uniform surface. This observation can be attributed to the presence of CoO skin layer, while directly anodizing of Co ions on Co3O4 nanocubes surface resulted in a remarkably rough layer (Supplementary Fig. 4). Using the voltage-dependent in situ X-ray diffraction/absorption approach, we concluded that a strong correlation exists between O2 gas evolution and the active metal centres with oxyhydroxide phase. More importantly, this junction layer can reversibly adapt its structure to accommodate harsh condition/environment without breaking the underlying scaffold.

Figure 2: In situ investigation of cobalt oxide SC catalysts during a water oxidation reaction in a liquid environment.
figure 2

(a) Schematic representation of the in situ grazing-angle X-ray diffraction apparatus applied to a liquid electrochemical cell. (b) Contour plots of in situ grazing-angle X-ray diffraction signals of a Co3O4@CoO SC in an aqueous solution containing 0.5 M KOH (pH=13.6) and 0.5 M Na2SO4 (pH=6.5). The images show the diffraction intensity (colour coded) as a function of voltage, and data collection was performed at the NSRRC synchrotron facility by using 12 keV of energy. The lower curves show the measured current density in both cases. (c) Contour plots of in situ grazing-angle X-ray diffraction signals of a Co3O4@CoO SC in an alkaline aqueous solution under switching of voltage (between 2.0 and 0.1 V versus RHE), and data collection was performed at the synchrotron facility by using 10 keV of energy to achieve better position distinguishability. (d) Voltage-dependence Fourier transform extended X-ray absorption fine structure spectra of a Co3O4@CoO SC in an alkaline aqueous solution containing 0.5 M KOH (pH=13.6) and in an in situ liquid cell. (e) XPS Co 2p and O 1s core-level spectra of the Co3O4@CoO SCs before and after oxygen evolution reaction.

Electrochemical performance

We evaluated the electrochemical activity of the Co3O4@CoO SCs during the OER in alkaline and neutral conditions while IrO2 (Supplementary Fig. 5) and RuO2 (Supplementary Fig. 6) catalysts were also tested as references (Fig. 3a). The ohmic potential drop loss caused by the solution resistance was corrected. Noted that the loading amount of the Co3O4@CoO SCs was optimized to attain the optimal conditions (25 μg cm−2; Fig. 3b), in which the catalysts layer could provide a wide range of transparency in the visible region (Fig. 3c). This could allow the development of an electrocatalytic system without inner-filter effects that led to the absorption of an excessive amount of incident light and hindered charge transfer across the semiconductor/electrolyte interface37. Both RuO2 and IrO2 catalysts exhibited slightly lower onset potentials (1.56 V versus RHE@ 5 mA cm−2 and 1.61 V versus RHE@ 5 mA cm−2) as compared with that of Co3O4@CoO SCs, presumably because of the intrinsic nature of RuO2 and IrO2 catalysts18,19,38. Furthermore, the Co3O4@CoO SC could be operated in a neutral environment as well, except the OER onset potential observed shifted towards a higher voltage. This was attributed to the formation of more active phase on the surface of the Co3O4@CoO SC in the alkaline condition and was consistent with theoretical and experimental Pourbaix diagrams31,33. It was noted that the thickness of the CoO layer should be tuned to achieve optimal condition since the usage of a larger amount of reductant led to some undesired reactions on Co3O4 SC instead of further increasing thickness of CoO layer and resulted in a negative effect in their electrochemical performance (Fig. 3d).

Figure 3: Electrochemical characterization of Co3O4@CoO single-crystal nanocubes.
figure 3

(a) OER polarization curves of Co3O4@CoO single-crystal nanocubes in alkaline (0.5 M KOH; pH 13.6) and neutral (0.5 M Na2SO4; pH 6.5) conditions, commercial RuO2 catalysts (0.5 M KOH; pH 13.6), and IrO2 catalysts (0.5 M KOH; pH 13.6); the voltage was corrected according to iR loss from solution resistance. All measurements were performed using an identical catalyst amount (25 μg cm−2) and rotating disk electrode (RDE) voltammetry upon a glassy carbon (GC) disk. (b) Voltage (versus RHE@ 5 mA cm−2) as a function of the catalyst loading amount (μg cm−2), indicating that applying the optimized loading amount (25 μg cm−2) facilitated achieving the optimal overpotential value for the OER. The error bars are defined as s.d. (c) Transmission spectrum of a Co3O4@CoO SC electrode at a loading amount of 25 μg cm−2. Inset: digital photographs of a Co3O4@CoO SC electrode. (d) Polarization curves for the OER of Co3O4@CoO single-crystal nanocubes prepared using various reductant (NaBH4) concentrations in O2-saturated KOH (0.5 M; pH 13.6) and at a 10 mV s−1 scan rate. (e) Steady-state Tafel (overpotential versus log current) measurements of Co3O4@CoO single-crystal nanocubes in alkaline and neutral conditions, commercial RuO2 catalysts (0.5 M KOH; pH 13.6), and IrO2 catalysts (0.5 M KOH; pH 13.6). All measurements were performed using RDE voltammetry upon a GC disk in desired electrolyte. Each data point represents the average of ten individual electrode samples where the error bars are defined as s.d. (f) Comparison of the O2 gas evolution and the charge throughout the circuit (line) in various current densities where the error bar are defined as s.d., indicating that the Faradaic efficiency of water oxidation was close to 100% with no substantial loss.

The steady-state Tafel measurements of Co3O4@CoO SC, IrO2 and RuO2 were shown in Fig. 3e and Table 1. The overpotential (η) comparison of various electrocatalysts to reach a current density of 10 mA cm−2 was promising because this value was the approximate current density necessary for 10% efficient solar-to-fuel conversion19,39. The Co3O4@CoO SC in alkaline condition yielded a current density of 10 mA cm−2 at a low overpotential of 0.430 V, which was similar to the η requirement for IrO2 (0.411 V) and RuO2 (0.358 V) identified both in the present study and relevant literatures18,19. The Tafel slopes of Co3O4@CoO SC were unable to achieve the lowest value that compared with those of other 3d-transition metal oxide systems18,19,20,26. We remarked that a low electrocatalyst loading amount (25 μg cm−2) was employed here, so that the catalysts can potentially be used in a photoelectrochemical system. Because of the low loading of electrocatalysts, the mass activity and the turnover frequency (TOF) calculated using these data achieved a mass activity of 234.0 A g−1 at η=0.4 V, which is equivalent to a TOF of 0.0487, s−1; this value is higher than that of other cobalt-based oxide systems to which high loading amounts were applied (approximately mg cm−2), despite that these values were determined in slightly dissimilar conditions and were not directly comparable11,18,40,41. Comparing the quantities of gases produced and the amount of charge that passed through the circuit revealed that the Co3O4@CoO SCs exhibited nearly 100% charge-to-chemical Faradic efficiency during 10 h in various current densities, indicating that these electrocatalysts could enable efficient carrier transportation without noticeable energy loss (Fig. 3f).

Table 1 Comparison of catalyst activity in the OER* .

Stability studies of single-crystal electrocatalysts

Prolonged testing of the optimized Co3O4@CoO SCs at a current density of 8 mA cm−2 was performed to maintain a constant current density for longer than 1,000 h (>40 days; Fig. 4a and Supplementary Movie 1) without noticeable decay in the current or detaching from the substrate (measured using SEM; Supplementary Figs 7,8 and 9). In contrast, the Co3O4 SCs was unable to achieve a stable current output, showing a remarkable decrease by 55% after 1,000 h of operation. This result suggested that the reliability of the Co3O4@CoO SC catalyst was superior to all previously reported systems; even after 1,000 h of operation, gas bubbles still emanated from the electrode surface (Supplementary Movie 1). To further test the long-term stability, we subjected it to a continual potential cycling between 1.0 and 2.0 V (versus RHE) and used the IrO2 and RuO2 catalysts as controls in O2-saturated 0.5 M KOH while all measurements were performed using rotating disk electrode (RDE) voltammetry upon a glassy carbon (GC) disk in the desired electrolyte. The conditions in the test were severe upon OER, because the potential was alternately applied, and the structure of the catalyst could be damaged by the continual valence cycling. Nevertheless, after 3,000 cycles of measurement, the Co3O4@CoO SCs exhibited no significant decay in its activity, unlike the IrO2 and RuO2 catalysts, which exhibited rapid decay in performance and decreased to a negligible level (3.1 and 2.6 mA cm−2 for IrO2 and RuO2 at 1.68V versus RHE , respectively) at the 3,000th scan (Fig. 4b). The bare Co3O4 SCs could only retain 54% of the initial current density after 6,000 scans (at 1.78V versus RHE) while the activity of Co3O4@CoO SCs did not show noticeable decay. Our results suggested that incorporation of a reversible adapting layer covering nanocrystal electrocatalyst could become an effective design strategy for improving the reliability of electrocatalysts. The spinel type is the most stable phase in Co-based system18,31, and it is able to transform into active oxyhydroxide phase as well. Unlike spinel-type Co3O4, a rock salt CoO layer is kinetically more facile to achieve the structural transformation into active oxyhydroxide phase in surface metal centres. This was indicative that the linear sweep voltammetry curve of the Co3O4@CoO SCs electrode exhibited a considerably lower OER onset potential and higher current density compared with those of the bare Co3O4 SC electrode (Fig. 3d).

Figure 4: Stability test.
figure 4

(a) Current versus time data on a Co3O4@CoO SC electrode and Co3O4 SC electrode in 0.5 M KOH (pH=13.6) for 1,000 h (>40 days) at a constant potential of 1.85 V (versus RHE), in which no significant current throughput decay was observed as compared to Co3O4 SC electrode. (b) OER polarization curves of Co3O4@CoO SC, Co3O4 SC, IrO2, and RuO2 catalysts subjected to continual potential cycling between 1.0 and 2.0 V (versus RHE) in O2-saturated KOH (0.5 M) for 3,000 (and 6,000) cycle measurements; the Co3O4@CoO SC retained activity, unlike the IrO2 and RuO2 control catalysts, which failed to achieve the initial current density. All measurements were performed using rotating disk electrode (RDE) voltammetry upon a glassy carbon (GC) disk in desired electrolyte. (c) Schematic representation of structural transformation within single-crystal and amorphous/polycrystal electrocatalysts, indicating that the formation of more active/oxidized phases may generate structural stress and/or voids and weaken the stability of materials. The CoO layer that eliminated the substantial volume change during the OER provided excellent protection for the Co3O4 nanocubes.


Clearly, the employment of rock salt CoO layer can mediate the interface of electrolyte/electrocatalysts and play multiple roles for efficiently catalyzing the oxidation of water. First, the surface CoO layer is kinetically facile to reach the active oxyhydroxide phase in active metal centres and serve as the active skin for OER. Active metal centres with oxyhydroxide phases are formed in situ with lower overpotential to facilitate efficient oxygen evolution reactions. Second, the CoO film provided an excellent protection to Co3O4 single-crystal nanocubes, because the volume change from Co anodization can be buffered by the CoO layer to avoid mechanical damage to the underlay Co3O4 scaffolds. The Co3O4 nanocubes (22 Å3 per Co) need to undergo a drastic volume change in order to transform into the active metal oxyhydroxides. However, the phase transformations from Co3O4 to β-CoOOH (30 Å3 per Co) and/or α-CoOOH (29 Å3 per Co) caused drastic volume expansions of approximately 36 and 32%, respectively. Therefore, the surface CoO layer can effectively buffer the harsh structural variations without damaging the Co3O4 scaffold. Third, single-crystal Co3O4 nanocubes are characteristically defect free in nature, and thus they avoid self-oxidizing and offer a robust scaffold without energetic losses. In contrast, in the case of amorphous/polycrystal, the formation of more active/oxidized phases are launched from grain boundaries and/or the structural defects, which invariably generates structural stress and/or voids. On the contrary, the volume expansion/contraction did not harm the scaffold (Co3O4) of electrocatalyst owing to the presence of the CoO layer (Fig. 4c). This strategy significantly improves the reliability of an electrocatalyst through the employment of a reversible adapting junction, and should be generalized and is potentially applicable to various electrocatalysis systems. The main guidelines are that this junction should be able to produce the catalytic metal centre with active phase, withstand the volume change from reaction and mediate the interface of catalyst/electrolyte.

In conclusion, the developed single-crystal Co3O4 nanocube catalysts with reversible adapting CoO skin layers are reliable, composed of common earth materials, environmental friendly and can be used as efficient water oxidation catalysts that can be incorporated into electrochemical/photoelectrochemical systems. An in situ X-ray diffraction method was used to identify a strong correlation between the O2 gas evolution and the formation of active metal centres with a metal oxyhydroxide phase through skin layer in liquid condition, and further revealed that this skin layer could remarkably protect underlay electrocatalysts through reversible transformation to active phases. Thus, reversible adapting CoO skin layers and single-crystal Co3O4 nanocubes play complementary roles to achieve an active and robust electrocatalyst, and lead to retaining a stable current for >1,000 h without exhibiting noticeable decay. These results provided significant progress towards the understanding of the phase of active metal centres on the electrocatalysts, and the advance of the reliability of OER electrocatalysts. This in situ X-ray technique provides a powerful tool to the investigation of the phase of surface active metal centre in electrocatalysis and potentially can be applied in probing other catalysis systems. In practical application, solar water splitting or artificial photosynthesis device can be achieved through integration of a reliable catalytic system with photovoltaic solar cell, which captures light energy to generate sufficient driving force for H2/O2 generation. For instance, Luo et al.42 recently demonstrated a perovskite tandem solar cell with incorporation of metal layered double hydroxide catalyst to realize a solar-to-hydrogen efficiency of 12.3% for water photolysis. The remarks described here can serve as a new strategy to design robust electrocatalysts for artificial photosynthesis/water photolysis that allows for the conversion of sunlight into O2 and chemical fuels, where low catalyst loading is essential for the photoelectrochemical system. Although a cobalt-based material was used as a platform to examine the single-crystal electrocatalysts in this study, the performance of the single Co compounds can be greatly optimized by further incorporating other functional materials. Our strategy here provided a fundamentally design of promising electrocatalysts and should become an accepted technique for electrochemical/photoelectrochemical systems.



Sodium borohydrate (NaBH4) and sodium nitrate (NaNO3) were purchased from Acros Organics. Cobalt nitrate hexahydrate, potassium hydroxide and sodium sulfate were obtained from Sigma-Aldrich. Sodium hydroxide was purchased from Fluka. All chemicals were used without further purification. The water used throughout this investigation was reagent-grade water produced using an ELGA ultrapure-water purification system (18.2 MΩ cm).

Preparation of single-crystal Co3O4@CoO nanocubes

To synthesize the Co3O4 nanocubes, NaNO3 (45.0 g) was dissolved in an aqueous solution of 0.3 M NaOH (100 ml) in a 3-necked round bottom flask at 100 °C and stirred vigorously while the temperature was maintained for 5 min. After the mixture was stirred for 5 min, an aqueous solution containing 1.0 M Co(NO3)2 (20 ml) was quickly added to the flask and heated to 115 °C in purified air (50 ml min−1). The colour of the precipitate slowly changed from purple to brown and finally to black after being heated for 12 h. The resulting black colloid (Co3O4 single-crystal nanocubes) was centrifuged at 7,000 r.p.m. and then washed several times with HCl (1.0 M) and deionized water. To prepare the thin CoO layer on the surface of the as-prepared Co3O4 single-crystal nanocubes, 300 μl of the Co3O4 nanocube colloid (0.19 g l−1) was reacted with a desired concentration (1.50–40.5 mM) of a NaBH4 aqueous solution (20 ml) during magnetic stirring at room temperature. After 20 min, the solid product was washed several times, separated from the solution through centrifugation and then dried.


The morphology of the specimens was studied by employing TEM using a JEOL JEM-2100F microscope that was operated at 200 kV, a Hitachi H-7650 that was operated at 120 kV, and a JEOL JSM-7600F field emission scanning electron microscope. The specimens were obtained by placing several drops of the colloidal solution onto a Formvar-covered copper grid and evaporating them in air at room temperature. The chemical composition analysis of the single-crystal nanocubes was performed using an energy-dispersive X-ray analysis (EDX) line scan and EELS in a JEOL JEM-2100F FE-TEM that was equipped with an energy-dispersive spectroscopy probe. The loading amounts were determined using an inductively coupled plasma-mass spectrometer (Agilent 7700 e). The crystallographic structures of the nanocubes were analysed by employing X-ray powder diffraction by using an X’Pert Pro diffractometer with Cu Kα radiation (λ=1.5418 Å). Real-time oxygen gas evolution was measured by a Gas chromatography (Agilent 7890B) with thermal conductivity detector. The absorption spectra of the Co3O4 electrodes were measured using a UV–visible/near-infrared Spectrophotometer V670 (JASCO International Co., Ltd) with an integrating sphere. X-ray absorption measurements of the synthesized samples were performed using synchrotron radiation at room temperature with a handmade reaction cell that was designed for this in situ measurement. Measurements were performed at the Co K-edge (7,709 eV) by using the sample, which was maintained at room temperature, and the 01C1 beamline at the National Synchrotron Radiation Research Center (NSRRC), Taiwan designed for these experiments. X-ray absorption data were analysed according to standard procedures, including pre-edge and post-edge background subtraction, normalization with respect to edge height, and Fourier transformation. X-ray diffraction measurements were conducted using a handmade reaction cell that was designed for this in situ measurement; all spectra were collected using the 01C2 beamline at the NSRRC, which had a radiation light source of 12 keV. It was worth noting that closer examination of the catalysts by using X-ray absorption approach was difficult, because gas bubbles were quickly generated from the increasing applied potential, and thus smooth oscillation cannot be achieved through absorption manner.

In situ grazing-angle X-ray diffraction studies

The grazing incident X-ray diffraction of thin film samples were performed at the BL01C2 beamline of the NSRRC in Taiwan, in which the ring of NSRRC was operated at energy 1.5 GeV with a typical current 360 mA. Two pairs of slits and one collimator were set up in experimental hutch to provide a collimated beam with dimensions of typical 0.5 × 0.5 mm (H × V) at the sample position. An incident angle about 0.2° was employed in present study, in which the X-ray irradiation can pass through several thousand Angstroms upon surface of sample. This geometry allows us to significantly enhance the X-ray scattering intensity from the surface of sample. The grazing-angle was optimized to probe the interior of the sample surface and achieved the best S/N ratio for maximizing scattering signal from electrode surface. In present study, the wavelength of the incident X-rays was 1.033210 Å (12 keV) delivered from the 5 T Superconducting Wavelength Shifter and a Si (111) triangular crystal monochromator, which allowed to achieve an optimized condition for distinguishing scattering rings. The diffraction pattern was recorded with a Mar345 imaging plate detector which was located 320 mm behind the sample, while the pixel size of image was 100 m with typical exposure duration of 1 min. To achieve a correct condition, the diffraction angles were calibrated according to Bragg positions of CeO2 (SRM 674b) standards in desired geometry, and then a program of GSAS II was employed to obtain corresponding one-dimensional powder diffraction profile with cake-type integration. In terms of liquid cell, a kapton polyimide film (DuPont) with a thickness of 0.06 mm served as X-ray window in liquid cell which was mode of Teflon line and the thickness of electrolyte below 1 mm was preciously controlled to suppress the interference from liquid electrode.

Electrochemical studies

To achieve fair comparison among all samples and well control the geometric area/impedance loss, all measurements were performed at room temperature by using RDE voltammetry upon a GC disk at 1,600 r.p.m., in which rotating disk working electrode made of glassy carbon (GC electrode, 5 mm in diameter, PINE:AFE3T050GC PINE, area: 0.196 cm2) connected to a CHI-704E bipotentiostat (CHI Instruments). Uniformly dispersed electrocatalyst slurry was obtained via an ultrasonic dispersal of electrocatalysts in deionized water. In the case of working electrodes of glassy carbon, the GC electrode was initially polished using 0.05 μm alumina powder, and then 15 μl of the electrocatalyst slurry was placed on the working electrode, which was dried in air at 40 °C. Finally, the catalyst-loaded GC electrode was covered with 20 μl of a 1% Nafion solution diluted using isopropyl alcohol and dried in a nitrogen atmosphere. Before the electrochemical measurement, the electrolyte was degassed by bubbling oxygen for at least 30 min to achieve a saturation condition of oxygen gas. In terms of in situ experiments, electrodes were prepared by incorporating as-synthesized nanocubes within a well-defined area (2 × 1 cm2) onto a fluorine-doped tin oxide-coated glass (CP-Solar, Tec 7) since GC disk is unable to utilize in such experiments, which was washed using acetone, isopropanol and deionized water before use; the nanocube film electrodes were subsequently annealed at 175 °C for 4 h. Electrochemical experiments were performed in a typical three-electrode system controlled using a CHI-704E or CHI-405A potentiostat (CHI Instruments). Linear sweep voltammetry was performed at a scan rate of 100 mV s−1. All potentials were referenced to an Hg/HgO reference electrode or Ag/AgCl reference electrode, and Pt was used as the counter electrode in all measurements, in which the electrolyte was either a 0.5 M Na2SO4 (pH 6.5) solution or a 0.5 M KOH (pH 13.6) solution. All potentials were adjusted to compensate for the ohmic potential drop losses (Ru) that arose from the solution resistance and calibrated with respect to RHE.

A long-term amperometric it curve was performed using a sampling interval of 1 s, and each run time was 86,400 s (24 h). Regarding the 1,000-h O2 evolution, the number of repetitive runs was 42 to ensure that measurement was conducted for 1,000 h. The volume of the electrolyte was kept constant to maintain a constant immersed-area of electrodes.

The values of mass activity (A g−1) were calculated using the following equation:

where M is the electrocatalyst loading amount (25 μg cm−2) and J is the measured current density (mA cm−2).

The values of TOF were calculated by assuming that every metal atom was involved in the catalysis (lower limits):

where J is the current density (A cm−2), F is Faraday’s constant (96485.3 C mol−1) and n is moles of electrocatalysts (mol cm−2).

Additional information

How to cite this article: Tung, C.-W. et al. Reversible adapting layer produces robust single-crystal electrocatalyst for oxygen evolution. Nat. Commun. 6:8106 doi: 10.1038/ncomms9106 (2015).