Understanding the nature of charge carriers at the LaAlO3/SrTiO3 interface is one of the major open issues in the full comprehension of the charge confinement phenomenon in oxide heterostructures. Here, we investigate thermopower to study the electronic structure in LaAlO3/SrTiO3 at low temperature as a function of gate field. In particular, under large negative gate voltage, corresponding to the strongly depleted charge density regime, thermopower displays high negative values of the order of 104–105μVK−1, oscillating at regular intervals as a function of the gate voltage. The huge thermopower magnitude can be attributed to the phonon-drag contribution, while the oscillations map the progressive depletion and the Fermi level descent across a dense array of localized states lying at the bottom of the Ti 3d conduction band. This study provides direct evidence of a localized Anderson tail in the two-dimensional electron liquid at the LaAlO3/SrTiO3 interface.
The electronic properties of the two-dimensional (2D) electron system found at the LaAlO3/SrTiO3 (LAO/STO) interface1, characterized by Hall-measured sheet carrier densities n2D~2–8 × 1013 cm−2 and a thickness of a few nm, are deeply affected by the electronic confinement, which leads to an anisotropic spatial extension of Ti 3d conduction bands and to a sub-band structure of the t2g levels. This geometry favours the spontaneous charge localization within dxy levels spatially very confined (≅2 nm) on the SrTiO3 (STO) side of the interface. This electronic confinement and breaking of inversion symmetry is also at the origin of a strong Rashba spin-orbit coupling2.
When the electronic density is large enough, Ti 3dxz−dyz sub-bands with a larger spatial extension are progressively filled with consequences on magnetotransport and possibly on superconductivity3,4. Less well understood is the nature of the low-density regime on the verge of localization, a key aspect for field-effect applications. Experiments have shown that a sharp transition to a highly resistive state occurs at a critical density of 0.5–1.5 × 1013 cm−2 (ref. 5). Considerations based on the polarization catastrophe model6 suggest that a large portion of the electron charge present at the interface may actually be trapped in localized levels located in energy somewhere below the band mobility edge. The presence of electrons localized by impurities, disorder or polaronic behaviour, has been reported in a number of works7,8,9,10. So far, however, only indirect evidences of these localized states were furnished, based on features in optical and transport properties.
Field-effect is unquestionably the most powerful approach to study the fundamental properties of oxide heterostructures at varying charge density. Under gate voltage, the phase diagram can be cleanly and reversibly explored without the complications inherent to chemical doping, which may easily result in additional effects blurring the intrinsic behaviour of these systems. For the LAO/STO system, field-effect has been extensively used to reveal tunable superconductivity11,12, strong Rashba spin-orbit2,3, enhanced capacitance and negative compressibility13, and magnetic effects14,15,16,17. Several works5,13,18,19 in particular have emphasized the correlated/localized nature of the electron carriers at large negative gate voltage, corresponding to a strongly charge-depleted regime characterized by sheet resistance of the order MΩ or higher, and densities lower than n2D~1013 cm−2.
Among transport measurements, the most direct probe of the electronic properties of a metal is certainly furnished by thermopower (or Seebeck coefficient, S). In contrast with magnetoresistivity (that is, Shubnikov de Haas) measurements20,21, which require high-mobility samples and strong magnetic fields, S can be equally well measured at low and high temperature and for the whole range of Hall-measurable charge densities. Specifically, S is the sum of two terms, the diffusive Seebeck (Sd), which is the potential drop generated by electrons diffused by a thermal gradient, and the phonon-drag Seebeck (Sg), that is, the additional electron current generated by the coupling of electrons with diffused phonons. Sd, related to the energy derivative of the conductivity22, is much less crucially dependent on the scattering regime than conductivity or mobility, and represents a very sensitive probe of the electronic density of states (DOS) of the system. On the other hand, Sg is directly related to the electron-phonon coupling (EPC), and may be used as a probe for a quantitative evaluation of the momentum relaxation rate of the electrons due to EPC23.
Note that very large values of the Seebeck coefficient have been measured in titanium oxides, even in the shape of three-dimensional samples (see, for example, refs 24, 25). More recently, Ohta and co-workers26,27,28 have studied the enhancement of the Seebeck effect driven by charge confinement in titanate heterostructures, both in the diffusion and drag regimes.
In this work, we perform Seebeck measurements under field effect, focusing on the depletion regime. We find that S assumes huge negative values and oscillates while the Fermi level is progressively lowered. We consider this behaviour as an evidence of charge localization below the bottom of the conduction band.
Transport and thermopower measurements
Transport and thermopower under applied gate voltage of several LAO/STO samples are measured. As all the samples show similar results, only one of them will be presented in the following (the others are described in the Supplementary Note 1 and shown in Supplementary Fig. 1). Seebeck effect is measured in a home-made cryostat, from 4.2 K to room temperature, using an ac technique29, in the configuration sketched in Fig. 1a. Hall effect and resistivity data are measured in a Quantum Design Physical Properties Measurement System (PPMS), from 2 K to room temperature and in magnetic field up to 9 T. Both dc and ac techniques are used. In particular, in the depletion regime, the ac lock-in technique is preferable, in that it allows very low currents (~10 nA) to be applied and thus pinch-off problems to be avoided.
In Fig. 1b, the Seebeck coefficient measured at 4.2 K as a function of the gate voltage Vg is displayed, for two different thermal cycles. S is negative at any voltage, indicating electron-like carriers. For positive Vg (see inset), which scans the charge accumulation regime, S shows the magnitude (~100 μV K−1) typically seen in STO bulk or heterostructures30,31,32 and varies by no more than 60% across the whole positive range, exhibiting a non-monotonic behaviour. In this accumulation regime, the measured magnitude of S first displays a very small increment up to Vg~20 V, and then it decreases regularly at larger Vg; assuming diffusive regime, the lowering of S is simply a consequence of the Fermi energy increase occurring along with the progressive charge accumulation. If one looks now at the negative Vg region, after a featureless gate voltage interval of ~7 V, something really astonishing happens: S progressively bursts to high values of the order of ~104 μV K−1 (it changes from S=−80 μV K−1 at Vg=−5 V to −26,000 μV K−1, that is more than two orders of magnitude, for a Vg variation of only 10 V). Furthermore, S dramatically oscillates with Vg. These oscillations are regularly distributed, and roughly occur at voltage intervals of 0.6 V. Above a maximum limit of Vg~ −15 V, no thermoelectric voltage signal can be detected experimentally anymore, the sample entering a highly insulating state. We may argue, however, that in principle the exponential rise of S to even greater negative values and the associated oscillations could be continued up to the ideal limit of complete charge depletion (in the Supplementary Note 1, a sample with S reaching ~−105 μV K−1 is shown as well). It is interesting to note that slight shifts of the S curves are observed after different cycles of temperature and Vg, as explained in the Methods and Supplementary Note 1 sections, however, the oscillating and diverging behaviour is always present. In particular, oscillating and diverging S curves are systematically observed at low negative Vg values after a forming protocol of Vg cycle at low temperature. The protocol is to apply at low temperature first the highest positive voltage Vmax to be used and then to sweep the voltage between Vmax and Vmin. This procedure allows reproducible measurements to be obtained.
In Fig. 2a,b, the characterization of electric and thermoelectric properties as a function of T (at Vg=0) and Vg (at T=4.2 K) is reported, respectively. From the measurement of longitudinal and Hall resistances, sheet carrier density n2D (which as usual we identify with the inverse Hall resistance assuming the Hall factor equal to unity and single band description) and Hall mobility μ are extracted. As a function of T and at zero gate voltage, the sample shows features typical of standard LAO/STO interfaces30: S exhibits a phonon-drag peak at low temperature and is linear above 50 K, as expected in the diffusive regime. Rsheet decreases with decreasing T, as expected for phonon-limited metallic behaviour, and saturates at a residual value of 700 Ω. The sheet carrier density n2D extracted from the inverse Hall constant varies, depending on the samples, in the range 3–8 × 1013 cm−2 as is common for LAO/STO samples. A slight RH downturn at low temperature has also been observed in other similar samples33 and may be interpreted in terms of charge delocalization related to the increased screening at low temperature, where the dielectric permittivity is very large. Mobility has a low-T value around 380 cm2 V−1 s−1 and decreases approximately as T−2 at high T, as expected from scattering by optical phonons. The same properties measured at fixed T=4.2 K and varying Vg (Fig. 2b) depict an accumulation-depletion scenario, with Rsheet and n2D being decreasing and increasing functions of Vg, respectively. Rsheet shows a sharp change in slope at Vg=0, that is at the border of accumulation and depletion regions, similar to what was reported in previous field-effect measurements at low T12,18, and reaches values of the order of 104–105 Ω for Vg<−40 V corresponding to a maximally depleted sheet density n2D~8 × 1012 cm−2. Below this threshold, Rsheet cannot be measured any longer since a sharp metal-insulator transition occurs. Consistently, we find the Hall mobility to decrease with negative Vg up to the lowest measurable value, in agreement with the literature19.
From the measurements two essential concepts emerge: (i) on the positive side of the gate field, transport properties are compatible with ordinary 2D electron gas (2DEG) behaviour in the charge accumulation regime; a switch towards negative gate values drags the system towards a highly depleted regime characterized by a sharp rise of resistivity and decrease of mobility, prefiguring a transition from metallic to localized charge transport behaviour; (ii) At low T this progressive depletion is indicated by rapidly diverging and dramatically oscillating Seebeck coefficient. In the absence of any magnetic field, this huge oscillating thermopower has no exact precedent in the literature, to our knowledge. In a small number of works a large field effect enhancement of the Seebeck coefficient is reported. The closest analogies with our result are probably the diverging thermopower and electrical resistivity measured in Silicon 2DEG34, occurring near the metal-insulator transition and attributed to Anderson localization, and the oscillating thermopower as a function of the carrier concentration found in GaAs/AlGaAs 2DEGs35 and in single-layer MoS2 (ref. 36), attributed, respectively, to electron-localization phenomena and variable range hopping mechanism. In both cases, however, the measured S coefficients (~103 μV K−1 for Si and ~102 μV K−1 for GaAs 2DEG) remain well below our values, and in both papers the dominant thermoelectric contribution is attributed to electron diffusion. Although we agree that electron localization must be the appropriate electronic structure landscape for this phenomenon, our standing point is that the measured thermopower is incompatible with electron diffusion, and must be primarily due to phonon drag, which is known to dominate over diffusion in certain ranges of temperature and densities where the EPC is strong.
Evidence of large EPC in STO bulk and STO-based heterostructures related to electron localization has been reported in several works7,8,37,38. EPC can ignite large phonon drag according to the following expression for Sg in the j direction (the detailed formulation39,40,41 is reported in the Supplementary Notes 4–7):
where σj is the electron conductivity, Vj a velocity factor, Γn k ,n k′ the electron-phonon scattering matrix, τep the phonon relaxation time due to EPC, whereas τph sums up all the other relevant relaxation mechanisms (for example, phonon–phonon, phonon–boundary, phonon–impurity scatterings), and the sum is over all the relevant phonon vectors (q) and modes, as well as electronic bands (n) and wavevectors (k). In standard metallic (accumulation) regime, Sg is only relevant in the narrow T interval (typically around T~θD/5, θD is the Debye temperature) where T is large enough to activate a substantial number of phonons, but not so large as to make phonon–phonon scattering (τph−1~T3) dominant over EPC, as for τph−1>>τep−1 Sg quickly vanishes.
This scenario is dramatically altered in case of strong depletion. First, electron localization largely suppresses conductivity, thus favouring large Sg, according to equation (1); at variance, Sd has a much weaker dependence on σj (see Supplementary equation (32) and the related discussion in the Supplementary Note 6), and cannot be amplified as much by a decrease of conductivity. Second, EPC may become very large in the so-called ‘dirty limit’, that is for electron diffusion lengths L much shorter than phonon wavelengths (qL≪1)23,35. In particular, this condition holds for narrow two-dimensional electron systems41 in the confined direction (for example, z), as strong EPC occurs for any qz≪1/t (t being the electron liquid thickness), thus any phonon wavevector contributes, eventually up to the Debye frequency. In other words, in the limit t→0 EPC may be large since even very short-wavelength acoustic phonons can couple to electrons. A further burst to EPC may come from the polar character of the system, which can lead to a large coupling between electrons and the electric field associated with acoustic phonons of very-long wavelength. The peculiar characteristics of two-dimensional electron liquid (2DEL) in LAO/STO under large negative gate voltage are thus highly favourable to the occurrence of strong EPC.
As a quantitative assessment of our analysis, we calculate the Seebeck coefficient and resistivity for a multiband effective-mass model (details are given in the Supplementary Notes 4–8). The model includes a single delocalized conduction band of t2g dxy symmetry, which is sufficient to describe the low-density regime n2D <1013 cm−2 according to first-principles calculations4. Below the conduction band bottom (CBB), we insert (see Fig. 3a–c) a series of low-density, low-mobility polaronic states (for brevity called ‘localized’ hereafter), with the intent of mimicking a disorder-induced Anderson tail, consistent with the scenario proposed in previous works7,8,10. Our model is also consistent with a scenario dominated by Mott localization, often invoked to explain other correlation phenomena observed in this system (see for example, capacitance enhancement described in ref. 13), as electrons can localize on Ti3+ sites at very low charge density, eventually helped by structural deformations (that is, polarons), even in the absence of disorder. As the measured Seebeck coefficient shows 12 oscillations in the range between −7 and −14 V, and the Hall measurement indicates in this voltage range a modulation of the carrier density of n2D~6 × 1011 cm−2, in the model we include 12 localized states, whose integrated DOS amounts to n2D~6 × 1011 cm−2. The basic characteristics of these states (energies, effective masses, bandwidth) are set to qualitatively reproduce the measured Seebeck in terms of oscillation frequency and amplitudes, as well as the Seebeck absolute value. The model is finalized to reproduce the following scenario: at zero voltage, the lowest conduction band is occupied by a mobile carrier density (n2D~1.2 × 1013 cm−2) similar to that usually found in LAO/STO. Then, it is assumed that the substantial effect of a negative Vg is the progressive charge depletion, thus the progressive lowering of EF, so that mapping S(EF) is equivalent to mapping S(Vg) (additional details are given in the Supplementary Note 8).
In Fig. 3, the calculated S(EF) and ρ(EF) reproduce qualitatively the most important features observed at varying Vg. In the experiment, negative Vg causes mild changes in Rsheet and S up to a certain threshold, which we can dub ‘regular behaviour’. In our interpretation, this threshold corresponds to the point where EF reaches the CBB edge (zero energy in the Figure 3d–f). For EF≤ECBB, a dramatic upturn begins: EF enters the region of localized states, ρ rises to Ωcm values and Sg (negligibly small in accumulation) quickly bursts up to 105 μV K−1 in magnitude. During the EF descent through the series of increasingly localized states, Sg oscillates in correspondence with the crossing (depletion) of each state. Sd also oscillates in correspondence with localized states, but with several fundamental differences from Sg: (i) the magnitude of Sd (~102 μV K−1) is in the usual range for LAO/STO (or even bulk SrTiO3) at low T, whereas Sg is 3–4 orders of magnitude larger; (ii) Sg increases rapidly in magnitude with the lowering of EF, as a consequence of the 1/σ dependence, whereas the oscillation-averaged Sd changes very smoothly with EF; (iii) the amplitude of Sd oscillations is comparable with the averaged Sd value itself. Points (ii) and (iii) make Sd incompatible with the monotonic descent observed in the experiment. These aspects (discussed in detail in the Supplementary Note 8) are derived from the fundamental characteristics of Sd, not from the specific approximation used in the model, thus they represent sound arguments to rule out diffusive Seebeck as the main contribution to the values measured in the strongly depleted regime. We remark that other forms of transport typical of localized carriers (variable-range hopping and thermal activated hopping) were considered as a possible source of the observed oscillations, but they were found incompatible with either the huge oscillating Seebeck or the resistivity values.
Notice that in the simulation ρ also shows oscillations, which are not observed experimentally. A non-oscillating behaviour of Rsheet(Vg) in the presence of oscillations in S(Vg) has been previously noticed in 2DEGs (GaAs/AlGaAs42,43 and MoS2 (ref. 36)). We believe that this is a consequence of the different nature of the two measurements (open- versus closed-circuit for S and R, respectively) and the non-ohmic behaviour of resistivity in the strongly depleted regime5 (a more extended discussion can be found in the Supplementary Note 2).
In conclusion, we measure field-effect transport and thermoelectric properties of the 2DEL at the LAO/STO interface in a wide range of gate field values. Seebeck measurement is an exceptionally sensitive tool for the exploration of highly confined carriers in oxide heterostructures, as it displays a clear signal even for electronic states characterized by extremely low charge density and mobility, and capable to resolve electronic structures in the lower than meV range at very low temperature. In this respect, thermopower seems to be a far more effective probe than any photoemission techniques nowadays available (see Supplementary Note 3).
At low-T, for negative gate voltage larger in magnitude than a given threshold, the measured thermopower displays a diverging, oscillating behaviour with negative values that are unprecedented in the literature. With the help of model results, we interpret this finding as being due to the regime change from normal metal to localized electron behaviour, corresponding to the EF descent below the conduction band, and across a series of lower lying localized electronic states, characterized by large resistivity, large EPC, and in turn huge measurable phonon drag.
This huge-Seebeck transient phase can be considered incipient of the insulating regime: it lives in a narrow charge density interval between the band-like metallic density (n2D≥1013 cm−2) and the insulating phase (n2D≤8–9 × 1012 cm−2), so that only a handful of these states (recognizable by the number of S oscillations) are visible. If the polarization catastrophe scenario is correct, we expect that a further lowering of EF would bring us right into the insulating phase where a large quantity of localized charge (n2D~1014 cm−2) is present. We argue that this charge is associated to diverging S values and conductivity too low to be detected by any possible means. Thus, the thermopower oscillations measured in this work are a strong, direct signature of the presence of localized states in the LAO/STO system.
Sample preparation and measurement setup
The samples are prepared as described in detail in the ref. 44. Pulsed laser deposition is used to grow an epitaxial layer of LaAlO3 (4–10 unit cells thick) on a (001)-oriented TiO2-terminated SrTiO3 substrate. The substrate temperature is about 800 °C and the oxygen pressure 10−4 Torr. The laser fluence is estimated at 0.6 J cm−2. Reflection high-energy electron diffraction intensity oscillations and patterns show layer-by-layer growth and good crystalline quality. The growth rate is around 60 laser shots per unit cell. After deposition, the oxygen pressure is raised to 200 mbar and the sample is kept at 500 °C for 1 h before being cooled down to room temperature. X-ray diffraction patterns confirm that the LaAlO3 layers are epitaxial and crystalline while atomic force microscope images show atomically flat terraces on the LaAlO3 surface, with terrace-edge heights corresponding to one layer of LaAlO3. Other details about sample preparation are found in refs 45, 46, 47.
The samples measured in this work behave in a very similar way, so that data on only one of them are presented. One sample is patterned in the shape of a Hall bar (channel width 1.5 mm) for better definition of geometrical factors and is used as a reference to confirm the exact relationship between measured properties. The measurement configuration sketched in Fig. 1a shows that the a.c. heat flows along the 010 direction (the longer side) of the 10 × 5 mm2 crystal. The typical power fed to the ac heater is ~1 mW. The voltage contact separation, equal to thermocouple separation, is 1.5–3 mm. The back gate electrode is a 3 × 5 mm2 gold pad evaporated on the backside of the 0.5-mm-thick substrate. The leakage current to the gate electrode is always monitored to be below 10 nA during the S measurements.
The Seebeck coefficient is measured in a home-made cryostat, from 4.2 K to room temperature, using an ac technique29. The period of the sinusoidal power supplied to the sample is 150 s and the applied thermal gradient is around 0.3 K across a distance of ~2 mm. Hall effect and resistivity data are measured in a Quantum Design PPMS system, from 2 K to room temperature and in magnetic field up to 9 T. Both dc and ac techniques are used. In particular, in the depletion regime, the ac lock-in technique is preferable, in that it allows very low currents (~10 nA) to be applied and pinch-off problems to be avoided.
The electrical and thermoelectrical responses to field effect of all the samples exhibit the general features presented in this work, in particular the divergent and oscillating S in the depletion regime. Nevertheless, some specific details (threshold voltage for the occurrence of the depletion regime, as well as exact magnitude of S) may vary from sample to sample and from thermal cycle to thermal cycle. We believe that this behaviour originates from the fact that the electrostatic landscape around the 2D electron liquid may change significantly, because of empty and filled traps within the SrTiO3 substrate. This may affect the screening of the gate electric field and thus may be the primary source of changing threshold voltage and details of experimental curves. On the other hand, reproducible S(Vg) curves are obtained after a forming protocol of Vg cycle at low temperature33, carried out by applying, at low temperature, first the highest positive voltage Vmax (usually ~200 V) to be used and then sweeping the voltage between Vmax and Vmin. This procedure allows reproducible measurements to be obtained, even sweeping Vg back and forth, as long as the sample is maintained at low temperature. The stability and reproducibility of Seebeck measurements after the forming protocol is also checked by measuring Seebeck signal for hours at fixed temperature and gate voltage, which yields constant curves.
In any case, considering all the different sets of measurements, it is clear that all the measurements present the same striking common features, that is evenly spaced oscillations as a function of gate voltage and diverging Seebeck coefficient in the tens of mV K−1 range in the depletion regime, which support the general character of our results and their interpretation.
We point out that there is a clear discrepancy between, on the one hand, the low T limit values in electrical and thermo-electrical transport curves as shown in Fig. 2a and, on the other hand, the zero gate voltage values of thermo-electrical and electrical transport properties as shown in Figs 1b and 2b, respectively. Indeed, the S value at the lowest temperature in Fig. 2a is around −240 μV K−1 slightly different from the Vg=0 value of Fig. 1b. Similarly, the n2D(Vg=0) value in Fig. 2b is much smaller than the low temperature value displayed in the third panel of Fig. 2a. This is due to the fact that the electron state at the interface setup by the forming protocol is stable only at the lowest temperatures. Data in Fig. 1b and Fig. 2b are measured after the forming protocol, whereas in Fig. 2a, data are measured before the forming protocol.
Diffusive thermopower and electric resistivity are calculated through the Boltzmann equation in the relaxation time approximation48. The electronic structure is simulated using a variant of the multi-band effective mass modelling previously employed to describe STO/LAO30, and the electronic relaxation time is modelled in terms of common energy-dependent analytic formulae (the Brooks-Herring formula for impurity scattering and the deformation potential approach for acoustic phonon scattering). Phonon-drag formulation is based on the coupled Boltzmann equations for electrons and phonons, in relaxation time approximation40,41. As the low-temperature limit is required, only the electron-acoustic phonon scattering is included in the phonon drag. Acoustic phonons are modelled according to the deformation potential approach, plus a piezoelectric scattering to account for the polar character of STO. The theoretical model is built to reproduce n-doped STO bulk, even with the presence of localized states below the conduction band (see Supplementary Figs 2 and 3). LAO/STO quantum well DOS is modelled with 12 equally spaced localized levels lying below the CBB. In Supplementary Fig. 4, the individual contributions of each electronic state to phonon drag, diffusive Seebeck and conductivity are shown, whereas main features of each level in terms of effective mass and electronic bandwidth are reported in Supplementary Table 1. Finally, the electron-phonon scattering rate at different doping level is reported in Supplementary Fig. 5. The formulation is displayed in full detail in the Supplementary Note 4.
How to cite this article: Pallecchi, I. et al. Giant oscillating thermopower at oxide interfaces. Nat. Commun. 6:6678 doi: 10.1038/ncomms7678 (2015).
Ohtomo, A. & Hwang, H. Y. A high-mobility electron gas at the LaAlO3/SrTiO3 heterointerface. Nature 427, 423–426 (2004) .
Caviglia, A. D. et al. Tunable Rashba spin-orbit interaction at oxide interfaces. Phys. Rev. Lett. 104, 126803 (2010) .
Fête, A., Gariglio, S., Caviglia, A. D., Triscone, J.-M. & Gabay, M. Rashba induced magnetoconductance oscillations in the LaAlO3-SrTiO3 heterostructure. Phys. Rev. B 86, 201105(R) (2012) .
Delugas, P. et al. Spontaneous 2-dimensional carrier confinement at the n-type SrTiO3/LaAlO3 interface. Phys. Rev. Lett. 106, 166807 (2011) .
Liao, Y. C., Kopp, T., Richter, C., Rosch, A. & Mannhart, J. Metal-insulator transition of the LaAlO3-SrTiO3 interface electron system. Phys. Rev. B 83, 075402 (2011) .
Okamoto, S. & Millis, A. J. Electronic reconstruction at an interface between a Mott insulator and a band insulator. Nature 428, 630–633 (2004) .
Fix, T., Schoofs, F., MacManus-Driscoll, J. L. & Blamire, M. G. Charge confinement and doping at LaAlO3/SrTiO3 interfaces. Phys. Rev. Lett. 103, 166802 (2009) .
Zhou, K.-J. et al. Localized and delocalized Ti 3d carriers in LaAlO3/SrTiO3 superlattices revealed by resonant inelastic X-ray scattering. Phys. Rev. B 83, 201402 (2011) .
Huang, Z. et al. Conducting channel at the LaAlO3/SrTiO3 interface. Phys. Rev. B 88, 161107 (2013) .
Yamada, Y., Sato, H. K., Hikita, Y., Hwang, H. Y. & Kanemitsu, Y. Measurement of the femtosecond optical absorption of LaAlO3/SrTiO3 heterostructures: evidence for an extremely slow electron relaxation at the interface. Phys. Rev. Lett. 111, 047403 (2013) .
Reyren, N. et al. Superconducting interfaces between insulating oxides. Science 317, 1196–1199 (2007) .
Caviglia, A. D. et al. Electric field control of the LaAlO3/SrTiO3 interface ground state. Nature 456, 624–627 (2008) .
Li, L. et al. Very large capacitance enhancement in a two-dimensional electron system. Science 332, 825–828 (2011) .
Brinkman, A. et al. Magnetic effects at the interface between non-magnetic oxides. Nature Mat 6, 493–496 (2007) .
Li, L., Richter, C., Mannhart, J. & Ashoori, R. C. Coexistence of magnetic order and two-dimensional superconductivity at LaAlO3/SrTiO3 interfaces. Nat. Phys. 7, 762–766 (2011) .
Dikin, D. A. et al. Coexistence of superconductivity and ferromagnetism in two dimensions. Phys. Rev. Lett. 107, 056802 (2011) .
Bert, J. A. et al. Direct imaging of the coexistence of ferromagnetism and superconductivity at the LaAlO3/SrTiO3 interface. Nat. Phys. 7, 767–771 (2011) .
Rössle, M. et al. Electric-field-induced polar order and localization of the confined electrons in LaAlO3/SrTiO3 heterostructures. Phys. Rev. Lett. 110, 136805 (2013) .
Bell, C. et al. Dominant mobility modulation by the electric field effect at the LaAlO3/SrTiO3 interface. Phys. Rev. Lett. 103, 226802 (2009) .
Caviglia, A. D. et al. Two-dimensional quantum oscillations of the conductance at LaAlO3/SrTiO3 interfaces. Phys. Rev. Lett. 105, 236802 (2010) .
Ben Shalom, M., Ron, A., Palevski, A. & Dagan, Y. Shubnikov–De Haas oscillations in SrTiO3/LaAlO3 interface. Phys. Rev. Lett. 105, 206401 (2010) .
Mott, N. F. Conduction in Non-Crystalline Materials 53Clarendon (1987) .
Fletcher, R., Tsaousidou, M., Coleridge, P. T., Feng, Y. & Wasilewski, Z. R. Electron-phonon coupling and phonon drag thermopower of a very low mobility 2DEG. Physica E 12, 478–481 (2002) .
Frederikse, H. P. R., Thurber, W. R. & Hosler, W. R. Electronic transport in strontium titanate. Phys. Rev. 134, A442–A445 (1964) .
Thurber, W. R. & Mante, A. J. H. Thermal conductivity and thermoelectric power of rutile (TiO2). Phys. Rev 139, A1655–A1665 (1965) .
Ohta, H. Two‐dimensional thermoelectric Seebeck coefficient of SrTiO3‐based superlattices. Phys. Status Solidi B 245, 2363–2368 (2008) .
Ohta, H. et al. Giant thermoelectric Seebeck coefficient of a two-dimensional electron gas in SrTiO3 . Nat. Mater 6, 129–134 (2007) .
Ohta, H. et al. Field-modulated thermopower in SrTiO3-based field-effect transistors with amorphous 12CaO·7Al2O3 glass gate insulator. Appl. Phys. Lett. 95, 113505 (2009) .
Calzona, V., Cimberle, M. R., Ferdeghini, C., Putti, M. & Siri, A. S. Fully automated apparatus for thermal diffusivity measurements on HTSC in high magnetic field. Rev. Sci. Instrum 64, 766–773 (1993) .
Filippetti, A. et al. Thermopower in oxide heterostructures: the importance of being multiple-band conductors. Phys. Rev. B 86, 195301 (2012) .
Delugas, P. et al. Doping-induced dimensional crossover and thermopower burst in Nb-doped SrTiO3 superlattices. Phys. Rev. B 88, 045310 (2013) .
Pallecchi, I. et al. Seebeck effect in the conducting LaAlO3/SrTiO3 interface. Phys. Rev. B 81, 085414 (2010) .
Ariando, et al. Electronic phase separation at the LaAlO3 /SrTiO3 interface. Nat. Comm 2, 188–194 (2011) .
Fletcher, R., Pudalov, V. M., Radcliffe, A. D. B. & Possanzini, C. Critical behaviour of thermopower and conductivity at the metal-insulator transition in high-mobility Si-MOSFETs. Semicond. Sci. Technol. 16, 386–393 (2001) .
Goswami, S. et al. Highly enhanced thermopower in two-dimensional electron systems at millikelvin temperatures. Phys. Rev. Lett. 103, 026602 (2009) .
Wu, J. et al. Large thermoelectricity via variable range hopping in chemical vapor deposition grown single-layer MoS2 . Nano Lett. 14, 2730–2734 (2014) .
Bidault, O., Maglione, M., Actis, M., Kchikech, M. & Salce, B. Polaronic relaxation in perovskites. Phys. Rev. B 52, 4191–4197 (1995) .
Devreese, J. T., Klimin, S. N., van Mechelen, J. L. M. & van der Marel, D. Many-body large polaron optical conductivity in SrTi1−xNbxO3 . Phys. Rev. B 81, 125119 (2010) .
Bailyn, M. Transport in metals: effect of the nonequilibrium phonons. Phys. Rev 112, 1587–1598 (1958) .
Cantrell, D. G. & Butcher, P. N. A calculation of the phonon-drag contribution to the thermopower of quasi-2D electrons coupled to 3D phonons. I. General theory. J. Phys. C Solid State Phys. 20, 1985–1992 (1987) .
Cantrell, D. G. & Butcher, P. N. A calculation of the phonon-drag contribution to the thermopower of quasi-2D electrons coupled to 3D phonons. II. Applications. J. Phys. C Solid State Phys. 20, 1993–2003 (1987) .
Narayan, V. et al. Density-dependent thermopower oscillations in mesoscopic two-dimensional electron gases. New J. Phys. 16, 085009 (2014) .
Narayan, V. et al. Evidence of novel quasiparticles in a strongly interacting two-dimensional electron system: giant thermopower and metallic behaviour. J. Low Temp. Phys. 171, 626–631 (2013) .
Cancellieri, C. et al. Influence of the growth conditions on the LaAlO3/SrTiO3 interface electronic properties. Europhys. Lett. 91, 17004 (2010) .
Gariglio, S., Reyren, N., Caviglia, A. D. & Triscone, J.-M. Superconductivity at the LaAlO3/SrTiO3 interface. J. Phys. Cond. Matter 21, 164213 (2009) .
Cancellieri, C. et al. Electrostriction at LaAlO3/SrTiO3 interface. Phys. Rev. Lett. 107, 056120 (2011) .
Salluzzo, M. et al. Structural and electronic reconstructions at the LaAlO3/SrTiO3 interface. Adv. Mater. 25, 2333–2338 (2013) .
Ridley, B. K. Quantum Processes in Semiconductors 2nd edn Clarendon (1988) .
We acknowledge fruitful discussions with C. Aruta, A. Braggio, R. Buzio, C. Cancellieri, A. Gerbi, P. Orgiani and M. Salluzzo. This work was supported by: Italian MIUR through projects FIRB RBAP115AYN ‘Oxides at the nanoscale, multifunctionality and applications’ and PRIN 2010NR4MXA ‘OXIDE’, Università di Genova, Swiss National Science Foundation through the National Center of Competence in Research, Materials with Novel Electronic Properties, ‘MaNEP’, the ‘Thermoelectric oxides TEO’ project and Division II and the European Research Council under the European Union’s Seventh Framework Programme (FP7/2007–2013)/ERC Grant Agreement No. 319286 (Q-MAC).
P.D. acknowledges financial support by CompuNet, Italian Institute of Technology (IIT) under ‘Platform Computation’. V.F. acknowledges support by CAR of Università di Cagliari. P.D, A.F. and V.F. acknowledge financial support by Fondazione Banco di Sardegna Projects, and computational support by CINECA (Casalecchio di Reno, Italy) and CRS4 (Pula, Italy).
The authors declare no competing financial interests.
About this article
Cite this article
Pallecchi, I., Telesio, F., Li, D. et al. Giant oscillating thermopower at oxide interfaces. Nat Commun 6, 6678 (2015). https://doi.org/10.1038/ncomms7678
This article is cited by
Frontiers of Physics (2019)
Journal of Electronic Materials (2019)
Scientific Reports (2016)
Hidden lattice instabilities as origin of the conductive interface between insulating LaAlO3 and SrTiO3
Nature Communications (2016)
Nature Communications (2016)