Current methods of chemical vapour deposition (CVD) of graphene on copper are complicated by multiple processing steps and by high temperatures required in both preparing the copper and inducing subsequent film growth. Here we demonstrate a plasma-enhanced CVD chemistry that enables the entire process to take place in a single step, at reduced temperatures (<420 °C), and in a matter of minutes. Growth on copper foils is found to nucleate from arrays of well-aligned domains, and the ensuing films possess sub-nanometre smoothness, excellent crystalline quality, low strain, few defects and room-temperature electrical mobility up to (6.0±1.0) × 104 cm2 V−1 s−1, better than that of large, single-crystalline graphene derived from thermal CVD growth. These results indicate that elevated temperatures and crystalline substrates are not necessary for synthesizing high-quality graphene.
Much progress has been made in growing large-area graphene by means of thermal chemical vapour deposition (CVD) based on catalytic dehydrogenation of carbon precursors on copper1,2,3,4. However, in many instances it is desirable to avoid multiple steps2 and high temperatures (~1,000 °C) employed in thermal-CVD growth. In particular, the conditions for the critical removal of the native copper oxide and the subsequent film growth are dissimilar enough to necessitate separate process steps. Moreover, high processing temperatures restrict the types of devices and processes where CVD can be applied and can also result in film irregularities that compromise the graphene quality itself4. Thermally derived strain and topological defects, for example, can induce giant pseudo-magnetic fields and charging effects5,6,7,8, giving rise to localization and scattering of Dirac fermions7,8 and diminishing the electrical properties.
A variant of thermal CVD, called plasma-enhanced CVD (PECVD), has been widely used for depositing many allotropes of carbon, most notably diamond films. The plasma can provide a rich chemical environment, including a mixture of radicals, molecules and ions from a simple hydrogen-hydrocarbon feedstock9, allowing for lower deposition temperatures10 and faster growth than thermal CVD. The ability of the plasma to support multiple reactive species concurrently is a key advantage. However, the quality of PECVD-grown graphene to date has not been significantly better than that of thermal CVD10,11,12.
Here we demonstrate a PECVD process that encompasses both the preparation of the copper and growth of graphene in a single step. The addition of cyano radicals, which are known to etch copper at room temperature13, to a hydrogen-methane plasma is found to produce a chemistry whereby the native oxide is removed, the copper is smoothly etched, and growth of well-aligned graphene ensues. Etching of the copper substrate is found to be self-limiting, allowing etching and growth steps to proceed in tandem under the same chemistry. The entire process occurs in a matter of minutes without active heating, and the resulting graphene films exhibit high electrical mobility and few structural defects. Our results indicate that elevated temperatures, crystalline growth substrates, and long process times are not necessary for synthesizing high-quality graphene.
Description and characterization of process
The PECVD growth process is schematically illustrated in Fig. 1a–c and further described in Methods and Supplementary Fig. 1. Copper was directly exposed to a low-pressure, microwave hydrogen plasma containing trace amounts of cyano radicals, methane and nitrogen (Supplementary Fig. 2 and Supplementary Fig. 3), as detailed in Supplementary Note 1. Removal of the native oxide and smoothing of the copper typically occurred within 2 min of igniting the plasma (Fig. 1a). Nucleation of graphene ensued on both sides of the substrate (Fig. 1b). With continued exposure to the plasma, disordered graphite and monolayer graphene covered the top and bottom sides, respectively (Fig. 1c). Copper deposits were found on both the process tube and the sample holder after successful growth runs (Fig. 1d), whereas runs with little copper etching did not produce optimal films. Optical microscopy showed that the top surface of the sample was always randomly pitted after growth (Fig. 1e), whereas that on the bottom surface was smooth (Fig. 1f). Scanning tunnelling microscopy (STM) measurements of the surface topography of graphene on the bottom side of Cu revealed sub-nanometre flatness for samples grown on Cu foils and single crystalline Cu (100) and Cu (111) (Fig. 1g–i and Supplementary Fig. 5a–c). Nitrogen incorporation into the graphene, as measured by X-ray photoemission spectroscopy, Supplementary Fig. 4a,b, was found to be below the detection limit14 of 0.1 at.%.
We found that the occurrence of PECVD-graphene growth was largely insensitive to the gas temperature of the plasma. The maximum gas temperature of the plasma determined by a thermocouple sheathed in boron nitride was found to be 160 °C (425 °C) for 10 W (40 W) plasma power, which decayed by more than 120 °C (250 °C) within ~1 cm from the centre of the plasma. The maximum temperature of the copper substrate Ts was measured using the melting points of known solids on top of a copper substrate subjected to the plasma. We found that at 40 W plasma power, lead melted whereas zinc did not, indicating that the maximum Cu substrate temperature was within the range of 327.5 °C<Ts<419.5 °C. Further, we were able to fabricate more than 300 high-quality large-area graphene samples by PECVD within 5–20 min in a single-step by using plasma power varying between 10 and 40 W. The typical substrate size was (8 × 13) mm2. Although the plasma produced by the Evenson cavity was not uniform in intensity over the length of the sample, graphene was found to cover the entire substrate and exhibited consistent quality over the entire film on the bottom side, indicating that the growth was not temperature sensitive and could occur over a range of temperatures. We expect that the sample size should be scalable in a larger cavity under the same growth conditions. The localized nature of the plasma source also allowed multiple samples to be prepared individually in the same process tube without changing conditions or breaking vacuum by simply translating the Evenson cavity.
Nucleation and growth
The time evolution in the Raman spectra of PECVD-graphene on copper foils during growth is shown in Fig. 1j,k. Spectra from the top side (Fig. 1j) featured the D-band, an indicator of edges or disorder in graphene and graphite; the G-band, a feature common to both graphene and graphite; and the 2D-band, a feature that can be used to distinguish graphene from graphite15. The D-band was prominent throughout, whereas the 2D-band decreased and disappeared with time, indicating the formation of disordered graphite, which is consistent with optical images of the top side (Fig. 1e). In contrast, spectra from the bottom side (Fig. 1k) showed that the D-band decreased and eventually vanished with increasing growth time, whereas the relative intensities of 2D and G-bands indicate the formation of monolayer graphene15,16,17,18, as described in Methods and Supplementary Fig. 6a,b. This behaviour is consistent with growth and eventual coalescence of graphene domains wherein the D-band associated with the edge states of the domains diminished19. A comparison of the graphene from the top and bottom sides indicate that increased mass flux and direct plasma exposure adversely affected the film quality, and hereafter we focus our studies on PECVD-graphene grown on the bottom side of Cu.
Scanning electron microscopy (SEM) images taken shortly after the onset of graphene growth on copper foil (Fig. 2a–d) revealed dense, linear arrays of hexagonal graphene domains that extended across the copper grains. With increasing growth time, the well-aligned graphene domains coalesced seamlessly into a monolayer graphene with few defects. Shown in Fig. 2e,f are the 2D/G and D/G intensity ratio maps of a (100 × 100) μm2 area of an as-deposited graphene sample on Cu, respectively. The average 2D/G intensity ratio (I2D/IG) is ~2 and only 5% of the mapped area show any measurable D-band. Histograms of the (I2D/IG) and (ID/IG) maps are provided in Supplementary Fig. 6a,b, respectively.
Although the number of graphene layers may be determined from the full-width half-maximum (FWHM) of the 2D-band20, the absolute value of the FWHM can be affected by the underlying substrate21. To avoid such complications, Raman maps of PECVD-graphene transferred from Cu to Si/SiO2 are provided in Supplementary Fig. 7a–d and detailed in Methods and Supplementary Note 2. The average value of the FWHM of the 2D-band, which was fit to a single Lorentzian, was 28.8 cm−1, and the average ratio (I2D/IG)=2.7, both consistent with the figure of merit for monolayer graphene15,16,17,18,20.
High-resolution (~1 nm) atomic force microscopy and SEM studies over multiple (100 × 100) μm2 areas of an annealed monolayer graphene sample22, which was transferred to single crystalline sapphire with a polymer-free technique23, indicated no discernible grain boundaries. With an increase of growth time, small adlayers began to develop on top of the first layer in an aligned manner, as exemplified by the SEM images in Fig. 2h–j. These findings, which are supported by Fig. 1k, indicate that the growth of PECVD-graphene on copper foils proceeded by nucleation and growth of well-aligned domains24,25 that eventually coalesced into a large single crystalline sheet, and the subsequent growth of the second layer with increasing time followed a similar mechanism (Fig. 2h–j).
Strain and structural ordering
where m (=G, 2D) refers to the specific Raman mode. Using the parameter , the strain distribution over an area of (100 × 100) μm2 is exemplified in Fig. 2g, showing consistently low strain characteristics, with an average strain ~0.07% for m=2D.
Overall, a general trend of downshifted G-band and 2D-band15 was found for all PECVD-graphene relative to thermal CVD-grown graphene on the same substrate, as exemplified in Supplementary Fig. 8a–c for comparison of PECVD- and as-grown thermal CVD-graphene on substrates of Cu foil, Cu (100) and Cu (111). The consistent frequency downshifts for all PECVD-graphene indicate reduction in the averaged biaxial strain. Further, the absence of the D-band in most spectra suggests that the samples were largely free of disorder/edges on the macroscopic scale, which is further corroborated by detailed spatial mapping of the Raman spectra over an area of (100 × 100) μm2 in Fig. 2e,f.
The PECVD-graphene exhibited a well-ordered honeycomb atomic lattice, which is unique to monolayer graphene, as evidenced by the STM images of samples on Cu foil (Fig. 3a–c), Cu (100) (Fig. 3e–g) and Cu (111) (Fig. 3i–k). The long-range structural ordering was further corroborated by the sharp Fourier transformation (FT) of STM topographies, as exemplified in Fig. 3d,h,l. The FT spectra demonstrated dominantly hexagonal lattices for all PECVD-graphene. Samples grown on Cu single crystals further exhibited Moiré patterns, as manifested by the second set of smaller Bragg diffraction peaks. Simulations (see Methods) indicated the Moiré pattern (a parallelogram) in the FT of Fig. 3h for graphene on Cu (100), was the result of a square lattice at approximately an angle ~(12±2)° relative to the honeycomb lattice (Supplementary Fig. 9a), whereas the Moiré pattern (a smaller hexagon) in the FT of Fig. 3l suggested that the Cu (111) hexagonal lattice was at ~6±2° relative to the graphene lattice (Supplementary Fig. 9b). These STM measurement over multiple samples and multiple areas per sample confirm the predominance of monolayer graphene and the absence of discernible bilayer graphene in our PECVD-grown samples.
The STM topography was further employed to analyse strain at the microscopic scale. For a local two-dimensional displacement field , where r and r0 denote the actual position of a carbon atom and its equilibrium position in ideal graphene, respectively27, the compression/dilation strain is given by (∂ux/∂x)+(∂uy/∂y)≡uxx+uyy, which is proportional to the biaxial strain5,7,8. Using the topographies shown in Fig. 3a–c, we obtained the spatial strain maps for PECVD-graphene on Cu foil, Cu (100) and Cu (111) substrates over successively decreasing areas in Fig. 4a,b,e,f,i,j, respectively. The corresponding strain histograms are given in Fig. 4c,g,k. The PECVD-graphene exhibited low and relatively homogeneous strain distributions. Further comparison with the macroscopic strain obtained from a collection of Raman spectra taken on different areas of multiple PECVD-graphene samples are summarized by the strain histograms in Fig. 4d,h,l. There is overall consistency between microscopic STM studies and macroscopic Raman spectroscopic studies, revealing low strain for all PECVD-graphene.
The electrical mobility (μ) of PECVD-graphene was determined by studying back-gated field-effect-transistor devices28,29. Graphene samples were first transferred to hexagonal boron nitride (BN) thin films on 300 nm SiO2/Si substrates using a polymer-free method23, and then lithographically processed into a geometry shown in Fig. 5a,b. The sheet resistance of graphene as a function of the back-gate voltage (V) and the corresponding conductivity (σ) versus sheet carrier density (ns) were measured at 300 K, as exemplified in Fig. 5c,d. The electrical mobility μ was obtained from the derivative of the Drude formula28 near the charge neutrality point:
where C denotes the capacitance of the device. The electrical mobility obtained from nine different devices was found to range from (3.0±0.5) × 104 to (6.0±1.0) × 104 cm2 V−1 s−1 for electrons, as summarized in Table 1, and from (1.2±0.2) × 104 to (3.5±0.5) × 104 cm2 V−1 s−1 for holes, where the errors represented variations in determining the (dσ/dV) slope due to the discreteness of voltage readings. These values are comparable to those obtained on large, single crystalline thermal CVD-grown graphene on BN, the latter yielded μ=4 × 104 to 6 × 104 cm2 V−1 s−1 at 1.7 K and ~1.5 × 104 to 3 × 104 cm2 V−1 s−1 at 300 K (ref. 2).
It is worth commenting on the accuracy of mobility values obtained by the two-terminal configuration depicted in Fig. 5a,b. The contact resistance between electrode and graphene was determined by the Transmission Line Model method and was found to be typically ~10 Ω for all devices. In contrast, the sheet resistance of graphene was typically more than 1 kΩ near the charge neutrality point, which was about two orders of magnitude larger than the contact resistance. Therefore, the contact resistance would not affect the accuracy of the mobility significantly. Additional measurements by patterning some of the PECVD-graphene into the four-point configuration revealed that the differences in mobility thus determined was less than 2–3% from those obtained by means of the two-point method.
Experience with diamond PECVD lends understanding to the observed nucleation and growth of aligned graphene domains presented here. In the case of diamond growth, it is known to involve a competition between growth by carbon radicals (most notably methyl radicals) and etching of amorphous or disordered carbon by atomic hydrogen. The process conditions used in our experiments are similar to those of microwave CVD growth of diamond thin films. Therefore, it is not unreasonable to expect that our PECVD growth of graphene also proceeds in a competitive manner30. Further, diamond is known to nucleate preferentially via surface defects31,32, and the aligned domains in our work were found to be commensurate with the inherent machine marks on the as-received copper foils. Although the copper surface is smoothed during the PECVD process, remnants of the defects are likely because the process temperature is low. For comparison, aligned nucleation was not observed on single-crystal copper, which contains no marks. For thermal CVD growth of large, single-crystal graphene2, it is preferable to have smooth, defect-free substrates and restricted nucleation. Therefore, multiple steps to prepare the substrates before thermal CVD growth and post annealing after the growth to optimize the sample are necessary2. In contrast, graphene with equivalent or even better mobility can be achieved by the one-step PECVD process described in this work. This PECVD process is also scalable11, occurs at CMOS compatible temperatures, and avoids complications with multiple steps and post-processing. Overall, our findings of the guided PECVD growth process not only shed new light on the growth kinetics of graphene but also open up a new pathway to large-scale, excellent quality and fast graphene fabrication. In particular, this one-step PECVD process potentially allows graphene to be used as-deposited, making it amenable for integration with complementary materials and technology.
The experimental setup is summarized in Supplementary Fig. 1, which consists of plasma, vacuum and gas delivery systems. The plasma system (Opthos Instruments Inc.) consists of an Evenson cavity and a power supply (MPG-4), which provides an exciting frequency of 2,450 MHz. The Evenson cavity mates with a quartz tube of inner and outer diameters of 10 and 12.5 mm, respectively. The vacuum system is comprised of a mechanical roughing pump, two capacitance manometers, a pressure control valve and a measurement control system. There is a fore-line trap between the vacuum pump and the MKS 153 control valve. The gas delivery system consists of mass flow controllers (MFCs) for H2, CH4 and Ar. A bakeable variable leak valve is placed before the methane MFC, and there is a leak valve for N2. A gas purifier was placed before the variable leak valve on the methane line. Quarter-turn, shut-off valves are placed directly after each of the MFCs. The system pressure and gas flows are monitored and controlled through the controller via a LabView interface. A residual gas analyzer (RGA) is used to monitor the exhaust gas.
Detailed PECVD growth procedure and information
The copper substrates were placed on a quartz flat inside of quartz tube. A typical substrate size was (8 × 13) mm2. The tube was evacuated to 25–30 mTorr. A 2–5 standard-cubic-centimeters-per-minute (s.c.c.m.) flow of room temperature hydrogen gas with 0.4% methane and a comparable amount of nitrogen gas was added and the pressure was controlled at 500 mTorr.
The addition of methane to the gas flow was controlled by a precision leak valve, and a typical concentration, as measured by gas chromatography, was 0.4%. The initially low vacuum conditions (~25 mTorr) provided sufficient partial pressures of nitrogen (atmospheric) for the PECVD process. (We note that a leak valve for including purified nitrogen was added to the setup to study the effects of increased nitrogen partial pressures.) Typical partial pressures measured by RGA are as follows:
N2 (Mass 28): 6.9 × 10−8 Torr
CH4 (Mass 16): 1.5 × 10−7 Torr
O2 (Mass 32): 5.4 × 10−9 Torr
H2O (Mass 18): 1.2 × 10−6 Torr
CO2 (Mass 44): 2.3 × 10−8 Torr
From these values, we estimate that the concentration of nitrogen in the gas flow is typically on the same order as that of methane.
The PECVD process was found to be highly sensitive to the relative amounts of methane and nitrogen. Excessive methane mixtures resulted in no etching, whereas excessive nitrogen mixtures would result in excessive etching of the copper. Slight adjustments to the methane concentration could be made via either optical emission spectroscopy or RGA.
A low-power (ranging from 10 to 40 W) cold hydrogen plasma was formed over the copper substrate using an Evenson cavity. Exposure of copper substrates to the plasma enabled continuing etching and cleansing of the copper surface during the graphene growth process. The gas temperature inside the plasma was measured using a thermocouple sheathed in boron nitride. The thermocouple was placed in the plasma above the sample and could be translated along the tube. The peak gas temperature measured in plasma treatment was 160 °C at 10 W and 425 °C at 40 W, and the gas temperature profile decreased rapidly (by 120 °C at 10 W and 425 °C at 40 W within 1 cm) from the peak value. The maximum temperature of the copper substrate Ts was measured using the melting point of known solids, lead and zinc, and found to be within the range of 327.5 °C<Ts<419.5 °C at 40 W. Typically after 5–20 min of direct exposure to the plasma, a large-area monolayer graphene formed on the backside of copper substrates, whereas the front side of the substrates was coated with disordered graphite. Upon the completion of graphene growth, the plasma was extinguished, and the gas flows were stopped. The process tube was then evacuated and back filled with Ar, and the substrate with graphene coating was subsequently removed. Copper deposition was visible on the inside of the tube and on the sample holder as the result of plasma etching of the copper substrates.
Analysis of monolayer graphene using Raman spectroscopy
The Raman maps shown in Fig. 2e,f of the manuscript for PECVD-graphene on Cu were collected with Renishaw InVia @ 532 nm, and the spectra were taken at 2 μm per pixel steps over an area of (100 × 100) μm2 for a total of 2,601 spectra. Similarly, the Raman maps in Supplementary Fig. 7a,b for PECVD-graphene transferred to SiO2 were taken at 2 μm per pixel steps over an area of (160 × 150) μm2. Each spectrum was smoothed and the broad background from the copper fluorescence was removed, and the peak locations and intensities for the D, G and 2D features were extracted. The relative intensities of the 2D and G-band and those of the D and G-band are presented in Fig. 2e,f, and histograms of the ratio values and the FWHM linewidth of the 2D band of our PECVD-grown graphene on Cu and commercial thermal CVD-grown graphene on Cu are shown in Supplementary Fig. 6a–e. The predominant (ID/IG)~0 value of the graphene sample shown in Supplementary Fig. 6a indicates negligible defects, whereas the histogram of the 2D/G intensity ratio (I2D/IG) shown in Supplementary Fig. 6b reveals that the average of the (I2D/IG) value is ~2, which agrees with the figure of merit (I2D/IG)>1 for monolayer graphene15,16,17,18.
This notion of predominantly monolayer graphene described in this work is further corroborated by detailed studies of a PECVD-graphene sample transferred from Cu to a SiO2 substrate, which prevents the complication of slow oxidation of the Cu substrate that could result in the 2D linewidth broadening with time due to the influence of the substrate (see Supplementary Note 2). As shown in Supplementary Fig. 7a–d, a large spatial map over an area of (160 × 150) μm2 revealed a mean FWHM value=28.8 cm−1 for the 2D-band and a mean value (I2D/IG)=2.7, both are consistent with predominantly monolayer graphene if we use either the criterion of 2D-band FWHM<30 cm−1 as the figure of merit for monolayer graphene on SiO2 (ref. 20) or the criterion (I2D/IG)>1 for monolayer graphene on various substrates15,16,17,18.
Simulations of the Moiré patterns and the corresponding FT were made by means of Matlab. We generated the triangular and cube lattices by using cosine square function and the hexagonal lattice by displacement of two triangular lattice functions. The lattice constant for the ideal 2D honeycomb structure of graphene is 0.2461, nm and that for the ideal Cu FCC lattice is 0.3615, nm, which has a corresponding lattice constant for the triangular lattice in the 111 direction and the square lattice in the 100 direction.
To simulate realistic STM imaging of the Moiré pattern for a given relative angle θ between the top graphene layer and the underlying Cu lattice, we assume the resulted topological function G(x,y) has the following form:
where 0<r≤1, GC(x,y) is the graphene honeycomb lattice function and GCu(x,y,θ) is the copper layer function which could be either the triangular lattice for Cu (111) or the cubic lattice for Cu (100). Both functions are normalized with maximum 1 and minimum 0. We use the exponent in equation (3) to simulate the rapid decay of the tunnelling current contribution from the copper atom directly under a carbon atom in the top graphene layer, where k is a parameter that controls the decay rate and was chosen to be 2–4. Even for exposed copper atoms without any carbon atom directly positioning above, the signal from copper is expected to be attenuated by a ratio r due to a larger distance from the STM tip to the copper layer. The above expression ensures that contributions from copper atoms directly under carbon atoms are much reduced due to deflection of tunnelling electrons, whereas those from exposed copper atoms are only attenuated by a coefficient r.
The matching between simulations and the Fourier transform (FT) of graphene on Cu (100) lattice data is judged by the angle of inner parallelism. At θ=(12±2)°, the angle of the inner parallelism appear to match the experimental result in Fig. 3h, as shown in by the real space Moiré pattern (left panel) and the corresponding FT (right panel) in Supplementary Fig. 9a.
In contrast, the matching between simulations and the FT of graphene on Cu (111) data is based on the size of inner hexagon relative to that of the outer hexagon for the graphene lattice. In fact, there are actually two inner hexagons according to the simulations, as exemplified in the FT of the Moiré pattern in Supplementary Fig. 9b for θ=(6±2)°. However, empirically only the larger inner hexagon is visible (Fig. 3l). We attribute this discrepancy to the intense DC signal from the zone centre of the FT spectra, which overwhelms the signal of the smaller inner hexagon and so becomes invisible upon our removal of the DC signal.
How to cite this article: Boyd, D. A. et al. Single-step deposition of high-mobility graphene at reduced temperatures. Nat. Commun. 6:6620 doi: 10.1038/ncomms7620 (2015).
Li, X. et al. Large-area synthesis of high-quality and uniform graphene films on copper foils. Science 324, 1312 (2009) .
Hao, Y. et al. The role of surface oxygen in the growth of large single-crystal graphene on copper. Science 342, 720 (2013) .
Yan, Z. et al. Toward the synthesis of wafer-scale single-crystal graphene on copper foils. ACS Nano 6, 9110 (2012) .
Mun, J. H. & Cho, B. J. Synthesis of monolayer graphene having a negligible amount of wrinkles by stress relaxation. Nano Lett. 13, 2496 (2013) .
Guinea, F., Katsnelson, M. I. & Geim, A. K. Energy gaps and a zero-field quantum Hall effect in graphene by strain engineering. Nat. Phys. 6, 30 (2010) .
Levy, N. et al. Strain-induced pseudo magnetic fields greater than 300 Tesla in graphene nanobubbles. Science 329, 544 (2010) .
Yeh, N.-C. et al. Strain-induced pseudo-magnetic fields and charging effects in CVD-grown graphene. Surf. Sci. 605, 1649 (2011) .
Yeh, N.-C. et al. Scanning tunneling spectroscopic studies of Dirac fermions in graphene and topological insulators. EPJ Web. Conf. 23, 00021 (2012) .
Goodwin, D. G. & Butler, J. E. Handbook of Industrial Diamonds and Diamond Films Marcel Dekker, Inc. (1997) .
Kalita, G. et al. Low temperature growth of graphene film by microwave assisted surface wave plasma CVD for transparent electrode application. RSC Adv 2, 2815 (2012) .
Yamada, T., Ishihara, M. & Hasegawa, M. Large area coating of graphene at low temperature using a roll-to-roll microwave plasma chemical vapor deposition. Thin Solid Films 532, 89 (2013) .
Nandamuri, G., Roumimov, S. & Solanki, R. Remote plasma assisted growth of graphene films. Appl. Phys. Lett. 96, 154101 (2010) .
Kuboi, N. & Fukusawa, M. Plasma treatment method, plasma treatment apparatus, and semiconductor device manufacturing method. US patent 20130017672 A1 (2013) .
Shard, A. G. Detection limits in XPS for more than 6000 binary systems using Al and Mg Kα X-rays. Surf. Interface Anal. 46, 175 (2014) .
Ferrari, A. C. et al. Raman spectrum of graphene and graphene layers. Phys. Rev. Lett. 97, 187401 (2006) .
Wu, W. et al. Control of thickness uniformity and grain size in graphene films for transparent conductive electrodes. Nanotechnology 23, 035603 (2012) .
Dimiev, A. et al. Layer-by-layer removal of graphene for device patterning. Science 331, 1168 (2011) .
Zhou, H. et al. Chemical vapour deposition growth of large single crystals of monolayer and bilayer graphene. Nat. Commun. 4, 2096 Article number: 3096 .
Celebi, K. et al. Observations of early stage graphene growth on copper. Electrochem. Solid-State Lett 15, K1 (2012) .
Lee, S. et al. Wafer scale homogeneous bilayer graphene films by chemical vapor deposition. Nano Lett. 10, 4702 (2010) .
Yin, X. et al. Evolution of the Raman spectrum of graphene grown on copper upon oxidation of the substrate. Nano Res. 1–10 (2014)) doi:10.1007/s12274-014-0521-0.
Nemes-Incze, P. et al. Revealing the grain structure of graphene grown by chemical vapor deposition. Appl. Phys. Lett. 99, 023104 (2011) .
Lin, W.-H. et al. A direct and polymer-free method for transferring graphene grown by chemical vapor deposition to any substrate. ACS Nano 8, 1784–1791 (2014) .
Murdock, A. T. et al. Controlling the orientation, edge geometry, and thickness of chemical vapor deposition graphene. ACS Nano 7, 1351 (2013) .
Lee, J.-H. et al. Wafer-scale growth of single-crystal monolayer graphene on reusable hydrogen-terminated germanium. Science 344, 286 (2014) .
Ferralis, N., Maboudian, R. & Carraro, C. Evidence of structural strain in epitaxial graphene layers on 6H-SiC(0001). Phys. Rev. Lett. 101, 156801 (2008) .
Teague, M. L. et al. Evidence for strain-induced local conductance modulations in single-layer graphene on SiO2 . Nano Lett. 9, 2542 (2009) .
Gannett, W. et al. Boron nitride substrates for high mobility chemical vapor deposited graphene. Appl. Phys. Lett. 98, 242105 (2011) .
Dean, C. R. et al. Boron nitride substrates for high-quality graphene electronics. Nat. Nanotechnol 5, 722 (2010) .
Mankelevich, Yu. A. & May, P. W. New insights into the mechanism of CVD diamond growth: Single crystal diamond in MW PECVD reactors. Diam. Relat. Mater. 17, 1021 (2008) .
Liu, H. & Dandy, D. S. Diamond Chemical Vapor Deposition: Nucleation and Early Growth Stages Elsevier (1996) .
Jiang, N. et al. Interfacial analysis of CVD diamond on copper substrates. Diam. Relat. Mater 6, 743 (1997) .
This work at Caltech was supported by National Science Foundation under the Institute of Quantum Information and Matter, and by Moore and Kavli Foundations through the Kavli Nanoscience Institute. The work in Taiwan was supported by the National Science Council under contracts 100-2911-I-002-514 and 101-2628-M-002-004. We thank Professor George Rossman for the use of his Raman spectrometer. D.A.B. specially thanks late Professor David G. Goodwin for his friendship and mentorship.
The authors declare no competing financial interests.
About this article
Cite this article
Boyd, D., Lin, WH., Hsu, CC. et al. Single-step deposition of high-mobility graphene at reduced temperatures. Nat Commun 6, 6620 (2015). https://doi.org/10.1038/ncomms7620
Accounts of Chemical Research (2021)
Single-Step Direct Growth of Graphene on Cu Ink toward Flexible Hybrid Electronic Applications by Plasma-Enhanced Chemical Vapor Deposition
ACS Applied Materials & Interfaces (2021)
Heater‐Free and Substrate‐Independent Growth of Vertically Standing Graphene Using A High‐Flux Plasma‐Enhanced Chemical Vapor Deposition
Advanced Materials Interfaces (2020)
Philosophical Transactions of the Royal Society A: Mathematical, Physical and Engineering Sciences (2020)
Journal of Physics: Condensed Matter (2020)