Solution self-assembly of block copolymers into inverse bicontinuous cubic mesophases is a promising new approach for creating porous polymer films and monoliths with highly organized bicontinuous mesoporous networks. Here we report the direct self-assembly of block copolymers with branched hydrophilic blocks into large monoliths consisting of the inverse bicontinuous cubic structures of the block copolymer bilayer. We suggest a facile and scalable method of solution self-assembly by diffusion of water to the block copolymer solution, which results in the unperturbed formation of mesoporous monoliths with large-pore (>25 nm diameter) networks weaved in crystalline lattices. The surface functional groups of the internal large-pore networks are freely accessible for large guest molecules such as protein complexes of which the molecular weight exceeded 100 kDa. The internal double-diamond (Pn3m) networks of large pores within the mesoporous monoliths could be replicated to self-supporting three-dimensional skeletal structures of crystalline titania and mesoporous silica.
Similar content being viewed by others
Porous polymer films and monoliths with internal bicontinuous nanoporous networks are increasingly important materials for applications such as desalination of water, ultrafiltration, chromatography, drug delivery, catalysis and nanotemplating1,2,3,4,5,6,7. In addition, polymer films and monoliths that have a three-dimensional (3D) crystalline array of internal nanoporous networks can serve as soft templates for creating mesoporous semiconductor crystals for highly efficient optical and optoelectronic materials and multifunctional hybrid materials8,9,10,11,12. In spite of recent advances in synthesizing porous polymers with internal bicontinuous porous networks13,14,15,16,17,18,19,20, microphase separation of block copolymers (BCPs) in bulk, followed by a selective removal of the labile polymer domains, remains a dominant method to create a cubic crystalline array of bicontinuous nanopores in polymer films and monoliths21,22. This method relies on the slow motion of BCPs in bulk, which might impede rapid synthesis of large monoliths with highly organized bicontinuous arrays of pores such as bicontinuous cubic structures23. Although solution self-assembly of BCPs has been widely used to create nanostructures with the desired morphology and functions24,25, this method generally yielded low-dimensional nanostructures, and, thus, has rarely been adopted as a method for the creation of highly ordered 3D periodic porous polymers.
Peinemann, Abetz, and others14,26,27,28,29,30,31 reported the synthesis of 3D porous polymers by non-solvent-induced phase separation of BCPs, which gives an integral asymmetric membrane with a highly ordered thin layer on top of a non-ordered sponge-like layer. Recently, Wiesner and co-workers13,17 developed SIM2PLE (spinodal-decomposition-induced macro- and mesophases separation plus extraction by rinsing) method based on the phase separation of BCPs and spinodal decomposition between BCPs and oligomeric additives, rendering the resulting structures to be hierarchically porous polymer monoliths composed of ordered mesopores and randomly distributed macropores. Still, however, direct self-assembly of BCPs in solution into the dense inverse bicontinuous cubic (IBC) structures of the BCP bilayer in the form of films and monoliths has remained a challenge.
Solution self-assembly of BCPs has shown the formation of inverse mesophases, which resulted in the formation of colloidal nano- and microparticles having internal bicontinuous pore networks32,33,34,35,36,37. The direct self-assembly of BCPs into IBC structures consisting of the BCP bilayers is an emerging method to create highly regular bicontinuous porous polymers without any aid of post processes to generate internal pore networks and surface functional groups36,37. We recently showed that the dendritic-linear BCPs composed of a dendritic block with peripheral hydrophilic poly(ethylene glycol) (PEG) chains and a glassy polystyrene (PS) hydrophobic block (Fig. 1a) preferentially self-assemble into inverse bicontinuous mesophases, in which the constituting BCP bilayers form the IBC structure, a 3D-flexed periodic structures of the membrane having zero mean curvature32,36. This self-assembly results in the formation of microscaled colloidal particles having internal non-interpenetrating networks of water channels weaved in a cubic crystalline order. The internal structures of the resulting colloidal particles (polymer cubosomes) consist of the IBC structure of the BCP bilayers, and show crystalline lattices over the long range including primitive cubic (P surface), double-diamond (D surface) and gyroid (G surface) symmetries. Peinemann and co-workers37 also reported the formation of polymer cubosomes having internal P surface by self-assembly of poly(acrylic acid)-b-PS in dilute solution, which exhibited high sorption capabilities for proteins. This new synthetic strategy based on direct self-assembly of BCPs in solution could be greatly beneficial to the creation of porous polymers with 3D-ordered porous networks. However, the solution self-assembly of BCPs has rendered the resulting porous polymers to be colloidal particles rather than films and monoliths.
We report here the direct solution self-assembly of amphiphilic dendritic-linear BCPs into mesoporous monoliths entirely composed of triply periodic IBC structures of the BCP bilayer. Utilizing the preferential self-assembly of dendritic-linear BCPs into inverse mesophases in solution36, we devise a simple and scalable method for the preparation of large mesoporous monoliths by self-assembly of the BCPs into the IBC structures, which is driven by the diffusion of a poor solvent (water) into the BCP solution under controlled humidity. This method allows the unperturbed growth of the porous monolith with an internal 3D cubic crystalline array of networks of large water channels (>25 nm) of a double-diamond lattice (Pn3m) with the desired surface functional groups. The internal network of the water channels may be used as a platform to accommodate guest molecules such as protein complexes, and the monolith is also demonstrated as a scaffold for the synthesis of 3D skeletal nanostructures of inorganic oxides with hierarchical porous networks.
Solvent diffusion–evaporation-mediated self-assembly of BCPs
In the routine practice for the self-assembly of dendritic-linear BCPs such as 1217 and 2213 (Fig. 1a) in dilute solution (cosolvent method), water, a poor solvent for the hydrophobic PS block, is gradually introduced to the BCP solution dissolved in dioxane, a common solvent for both of the polymer blocks. The addition of water destabilizes the PS blocks and consequently results in the aggregation of these PS blocks to form the core of the bilayer membrane, which has a corona composed of the PEG domain. This process inevitably requires physical agitation of the solution to ensure a homogeneous mixing of the two solvents, which renders the resulting self-assembled structures to be colloidal polymer cubosomes with microscaled sizes36. Therefore, the inverse bicontinuous structures formed in solution by self-assembly of BCPs remained colloidal particles rather than macroscopic objects such as films and monoliths.
To avoid this formation of colloidal particles in solution, we devised a method to introduce water into the dioxane solution of the BCP without physical agitation or perturbation. We imagined that, under saturated humidity (relative humidity=100%), water vapour in the atmosphere would diffuse into the dioxane solution of 1217 cast on a stationary substrate, with dioxane evaporating into the atmosphere. When the critical water content within the dioxane solution is reached (~15 vol%), the self-assembly of 1217 would be initiated from the air–solution interface where the water content is presumably highest. We assumed that the formation of the IBC phases of the BCP would proceed downwards from the interface caused by diffusion of water. This method would ensure unperturbed growth of the monolith consisting of the IBC structure of the BCP because of the fast kinetics of self-assembly of 1217 in solution.
We tested our method, namely ‘solvent diffusion–evaporation-mediated self-assembly’ (SDEMS; Fig. 1b), by placing a dioxane solution (12 wt%) of 1217 cast on a glass substrate (0.5 mm wet film thickness) in a sealed humidity chamber (relative humidity=100%, 23 °C). After 1 h, the glass substrate was removed from the chamber and immersed into water to quench the assembly process by vitrification of the PS blocks. After removing dioxane by solvent exchange in water, we obtained the opaque monolithic film of 1217. Observed on scanning electron microscopy (SEM), this monolithic film revealed that the internal IBC structures consisting of the bilayer of 1217 resided under the top layer (~10 μm thick) without any defined mesostructures (Supplementary Fig. 1). When the same dioxane solution of 1217 was placed in the same chamber filled with dry N2, we did not observe any formation of the IBC structures of the BCP. Instead, a transparent film without any mesoscaled internal structure was observed after solvent evaporation. We also observed the formation of polymer cubosomes instead of monoliths when the dilute dioxane solution of 1217 (0.5–3 wt%) was used for the SDEMS (Supplementary Fig. 2). This observation indicated that the formation of the inverse bicontinuous mesophase of 1217 was the result of the self-assembly of the BCP in solution rather than the microphase separation of the BCP in bulk during the solvent evaporation.
As the rate of dioxane evaporation under saturated humidity during the SDEMS process is directly related to the rate of the increase of water content, we expected that the kinetics of self-assembly of BCPs could be controlled by reducing the rate of dioxane evaporation. To prevent a premature quenching of the self-assembly of the BCP by a rapid increase of the water content, resulting in the formation of a featureless bulk of the BCP at the air–solution interface, we presaturated the humidity chamber with a mixture of water and dioxane (1:1 v/v) with an expectation that the dioxane vapour in the atmosphere would reduce the vapour pressure of the solvent, and thus slow down the rate of evaporation of the organic solvent.
Under these conditions, a dioxane solution of 2213 (12 wt%) was cast on a glass disk (2.5 cm diameter, 0.3 mm wet film height), and the coated disk was placed in a humidity chamber presaturated with a dioxane/water mixture (1:1 v/v) at 23 °C. After 1 h, the resulting disk was removed from the humidity chamber and immersed in excess water to remove residual dioxane, which yielded an opaque monolithic film on the substrate (Fig. 2a inset). SEM images of the resulting monolith showed that the top layer of the monolith consisted of a perforated BCP bilayer, which exhibited an array of nanopores (~10 nm diameter) over the entire top surface (8.5 × 109 pores per cm2 obtained by image analysis; Fig. 2a). Below the top perforated bilayer, a highly crystalline inverse bicontinuous structure of polymer bilayers was observed over the entire thickness of the monolith (40 μm; Fig. 2b–e). We also observed that the disordered domains and macroscopic defects gradually appeared within the monolith of 2213 as the thickness of the monolith increased (Fig. 2b). We attributed this increased disorders within the monolith to the fact that the motion of polymer chains might be kinetically limited by the concentration gradient of water as the self-assembly progressed from the air–solution interface to the substrate by diffusion of water from the interface.
SEM images of the fractured monolith of 2213 revealed the IBC crystalline structures of the BCP bilayers. These structures were assigned to a double-diamond lattice (D surface, Pn3m symmetry, lattice constant (a)=51.7 nm) by synchrotron small angle X-ray scattering (SAXS) (Fig. 2f). Under the identical condition, 1217, an isomeric analogue to 2213 that differs only in the structure of the benzyl ether dendritic block (Fig. 1a), self-assembled to form a monolith exhibiting similar morphology to the monolith of 2213 (Supplementary Fig. 3). The internal structure of the monolithic film of 1217 was assigned to a primitive cubic lattice (P surface, Im3m symmetry, a=82.4 nm) coexisting with a double-diamond lattice (D surface, Pn3m symmetry, a=64.1 nm) by SAXS and SEM (Supplementary Fig. 4). We, therefore, used the monolith of 2213 for further structural characterization and our studies owing to the homogeneity of the internal crystalline lattice. The D surface structure also has been proposed to provide materials with interesting functions such as full bandgap photonic crystals and multifunctional hybrid materials such as a highly electrically conductive but poorly thermally conductive materials11,12.
The formation of the internal IBC structure of the bilayer of 2213 was traced using time-interval quenching of the self-assembled structure by immersion of the monolith in liquid N2, followed by a rapid exchange of the solvent by immersing the frozen structure in water. The rapid cooling of the self-assembled structure of 2213 with liquid N2 ensured that the BCP chains were in the glassy state, resulting in a minimal rearrangement of BCP chains while removing dioxane from the monolith. The quenched samples at each time interval were examined by SAXS and SEM. The results showed a gradual growth of the D surface of the BCP bilayer within the monolith over 1 h. (Fig. 2f and Supplementary Fig. 5). From the SAXS results of the monolith of 2213 prepared by SDEMS, we observed a weak peak appearing at low q region, which might result from the presence of disordered single continuous phases (Fig. 2f)38. Residual solvent molecules localized in the PS-rich domain would plasticize the PS blocks constituting the bilayer, and, therefore, could develop a pressure for the local grains of Pn3m symmetry to be rearranged to a single-diamond phase with some disorder39.
As expected from the materials composed of glassy PS polymer blocks, the monoliths of dendritic-linear BCPs maintained the structural integrity at room temperature upon drying the solvents. The N2 adsorption–desorption isotherms at 77 K revealed that the monolith of 2213 exhibited a large surface area (73 m2 g−1) and pore volume (0.45 cm3 g−1) determined by Brunauer–Emmett–Teller (BET) analysis. The Barrett, Joyner and Halenda (BJH) analysis revealed the pore size distribution at 32 nm, which coincided with the observed pore dimension by SEM studies (Fig. 2g).
The size and the thickness of the monolith were scalable as the BCP solution could be cast on a substrate of any size, and the thickness of the resulting monolithic film was proportional to the wet thickness of the polymer solution cast on a substrate. Using the SDEMS method, we were able to prepare a monolith of dendritic-linear BCPs with a thickness of 400 μm on a 25 cm2 glass slide (Supplementary Fig. 6).
Surface functionalization of the mesoporous monoliths
The bicontinuous cubic networks of large pores embedded within the IBC structure of the BCP bilayers could allow these porous polymer monoliths to be used as platforms for applications such as protein separation, biochemical transformation and nanotemplating36,37. To demonstrate the accessibility and usability of the internal networks of the water channels within the polymer monoliths, we introduced surface amino groups throughout the BCP bilayer by the co-assembly of 2213 and NH2–PEG45–PS210, a linear BCP with an α-amino group at the hydrophilic PEG block under the SDEMS condition (2213/NH2–PEG45–PS210 93:7 w/w in dioxane)36. The resulting surface-functionalized porous monolith exhibited the identical structural characteristics to the monolith of 2213, and showed an internal D surface structure (Pn3m) by SAXS and SEM (a=63.2 nm; Supplementary Fig. 7).
The surface amino groups of the monolith were converted to biotins to anchor streptavidin homo-tetramer labelled with fluorescein (54 kDa, Sigma) using the strong non-covalent interaction between biotin and streptavidin. On confocal laser scanning microscopy (CLSM), the resulting monolith showed a strong green fluorescence over the entire area (~1 cm2) and thickness (~40 μm), which indicated that the fluorescein-labelled streptavidin was successfully bound to the surface biotin within the water channel networks. This streptavidin-bound monolith was immersed in a solution of the biotin-mCherry fluorescent protein (35 kDa; ref. 40), which yielded the monolith clearly showing cherry-coloured fluorescence owing to the binding of biotin-mCherry to the remaining binding sites of the surface-bound streptavidin (Fig. 3a). The axial intensity profile of fluorescence revealed the coexistence of streptavidin and biotin-mCherry fluorescent protein along the optical axis, which indicated the sequential binding of both proteins on the internal surface of the mesoporous networks within the monolith. The gradual decrease of fluorescence intensity along the depth of the monolith was derived from photobleaching during the measurement (Fig. 3c). This result demonstrated that the easy access of large guest molecules such as proteins and their complexes could easily access the internal networks of the large water channels of the polymer monolith.
Templated synthesis of skeletal inorganic structures
These internal large-pore networks of the BCP monolith could be translated into the 3D self-supporting skeletal networks of functional organic and inorganic materials, which have structural symmetry inherited from the IBC structure comprising the BCP monolith (Fig. 4). Therefore, we introduced liquid precursors of inorganic oxides such as titanium (IV) isopropoxide (Ti(OiPr)4) into the D surface monolith of 2213 (thickness 40 μm, 1 cm2 area). Following the acid-catalysed crosslinking of Ti(OiPr)4 to form TiO2, the resulting white monolith was sintered at 500 °C under ambient condition for 3 h to remove the BCP template (Fig. 4; refs 41, 42). The SEM and transmission electron microscopy (TEM) images of the resulting TiO2 monolith (Fig. 5a–c and Supplementary Fig. 8) showed that the monolith consisted of a skeletal replica of the water channel networks residing in the polymer monolith. SAXS analysis of the skeletal TiO2 monolith revealed a diffraction pattern of the single-diamond phase (Fd3m symmetry) (Supplementary Fig. 9 and ref. 38. Thermal treatment during calcination possibly affects structural constraints and causes a rearrangement of Pn3m to Fd3m owing to the increased mobility of polymer chains during calcination at the temperature well above glass transition temperature (Tg) of PS block (Figs 4 and 5; ref. 39).
The energy-dispersive X-ray spectroscopy mapping on TEM confirmed that the resulting 3D skeletal structures consisted of TiO2 (S-TiO2) (Fig. 5c). The mean diameter of the constituting TiO2 skeletons was determined to 15.5 nm by porosimetry, which was in line with the SEM and TEM images. We further revealed the characteristics of S-TiO2 at the atomic scale by X-ray diffraction, which showed a pattern of the crystalline phase of TiO2 in an anatase form. High-resolution TEM images of the skeletons of S-TiO2 clearly showed a well-defined lattice space (0.38 nm) of the typical (100) crystalline plane of anatase TiO2 (Fig. 5d).
We investigated the photocatalytic activity of S-TiO2 by monitoring the change in optical absorbance of methylene blue, which can be found as a water contaminant from dyeing processes43. Upon irradiation of a 3-ml methylene blue solution in the presence of S-TiO2 (3 mg), the photodegradation of methylene blue was complete after 14 min, while the commercial TiO2 nanoparticles (Sigma, <25 nm particle size) under the same experimental condition took nearly 80 min (Fig. 5e). The kinetics of the photodegradation reaction was plotted to a pseudo-first-order rate law using ln(C0/C)=kt, where k is the apparent rate constant and t is the irradiation time44. The average reaction rate constant of k for S-TiO2 was 0.2764, min−1, which was 6.4 times that of the reference anatase TiO2 nanoparticles (k=0.0434, min−1). BET analyses revealed that the surface area (80 m2 g−1) of S-TiO2 is greater than that of TiO2 nanopowder (35 m2 g−1; Supplementary Fig. 10). These results clearly indicated that the 3D skeletal nanostructure of S-TiO2 provided an advantage to photodegradation of dyes arising from the large surface area and high accessibility to the catalytically active crystal planes.
We could also realize the novel example of 3D hierarchically ordered structures with multiscale pores (Figs 4 and 6a–c). By infiltrating the monolith of 2213 with tetraethylorthosilicate (Si(OEt)4) in the presence of cetyltrimethylammonium bromide (CTAB), the skeletal mesoporous silica could be synthesized within the large channels of the porous polymer monolith45. After the crosslinking of Si(OEt)4 and the calcination of the polymer template, we obtained the hierarchically mesoporous skeletal SiO2 replica (mS-SiO2), of which the constituting silica skeletons (~18 nm in diameter) possessed the hexagonally ordered nanochannels (a=3.58 nm, pore diameter~1.4 nm determined by SAXS) parallel to the long axis of the skeleton (Fig. 6f,h). SAXS results of the resulting mS-SiO2 showed that the symmetry breaking from Pn3m to Fd3m occurred upon heating during calcination. SEM and TEM analyses revealed the random shifting of two non-intersecting skeletal networks by showing various projections of Fd3m in a similar manner to the report by Ho and co-workers39 (Fig. 6b–f and Supplementary Fig. 11).
The hierarchically porous structure of mS-SiO2 was also confirmed by N2 adsorption–desorption isotherms (Fig. 6i). The BET analysis of the isotherms showed an increased pore volume (1.38 cm3 g−1) and surface area (953.7 m2 g−1), which was threefold and 13-fold greater than the values of the mesoporous monolith scaffold, respectively. BJH analysis of N2 adsorption–desorption isotherms of mS-SiO2 showed a broad pore distribution in a range of 6–20 nm, exhibiting the mean pore diameter of 5.9 nm (Supplementary Fig. 12). The average diameter of hexagonally ordered smaller mesopores residing in the silica skeletons was estimated to be ~1.5 nm by the Horvath–Kawazoe model analysis (Supplementary Fig. 12). This unique hierarchically porous structure could be beneficial for applications where large surface area and high accessibility to the structure are required simultaneously46.
Solution self-assembly of amphiphilic BCPs into IBC mesophases is an emerging strategy to synthesize highly ordered mesoporous polymers with reticulated mesoscale porous networks without postsynthetic processes for pore generation. This direct self-assembly of BCPs in solution generated highly ordered triply periodic porous structures with the desired surface functional groups, which rendered these porous polymers potentially useful for separation, catalysis and nanotemplating. Our method (SDEMS) to induce self-assembly of BCPs in solution without physical agitation is based on the diffusion of a poor solvent for the PS block (water) into a solution in a common solvent to both polymer blocks. The diffusion of water at the air–solution interface gradually deteriorates the solvent quality towards the PS block, which propels the dendritic-linear BCPs to form bilayers in solution. In appearance, our method shares some resemblance to evaporation-induced self-assembly for the synthesis of mesoporous silica films47. Evaporation-induced self-assembly increases the surfactant concentration above the critical micelle concentration by gradually evaporating a common solvent, which allows the resulting mesoporous structures to be a form of films and monoliths. In our case, the diffusion of a poor solvent into the BCP solution is a key step to induce self-assembly because of the low critical micelle concentration values of BCPs. The rate of evaporation of a common solvent has to be suppressed to prevent a premature kinetic quenching of self-assembly of BCPs. Non-solvent-induced phase separation method by Peinemann, Abetz, and others14,26,27,28,29,30,31 involves a quick phase separation of BCPs at the air–solution interface caused by evaporation of solvents, which was followed by a rapid solvent exchange with non-solvent within a phase-separated domain. SIM2PLE method by Wiesner and co-workers13,17 is based on the phase separation of BCPs under solvent swollen conditions also rendered the resulting structures to be hierarchically porous polymer monoliths. Our method ensures that the self-assembly retain the characteristics of solution self-assembly, but only without physical agitation. The results and the demonstrations shown here substantiate that the highly ordered internal large-pore networks residing within the polymer monolith consisting of the IBC of the BCP bilayer could be valuable platforms for advanced separations and nanotemplating. We also point out that the results reported here suggest a new way to create highly ordered IBCs of BCP bilayers in a large scale by exploiting from the simple and fast solution self-assembly of BCPs in solution into inverse mesophases.
General methods and materials
Nuclear magnetic resonance spectra were recorded on a Varian VNMRS 600 spectrometer with CDCl3 as a solvent. Molecular weights of BCPs were measured on an Agilent 1260 Infinity GPC system equipped with a PL gel 5 μm mixed D column (Polymer Laboratories) and differential refractive index detectors. Tetrahydrofuran (THF) was used as an eluent with a flow rate of 1 ml min−1. A PS standard (Polymer Laboratories) was used for calibration. TEM was performed on a JEOL JEM-2100 and JEM-2100F microscope at an acceleration voltage of 200 kV. Sample specimens were prepared by placing a drop of the solution on a carbon-coated Cu grid (200 mesh, Electron Microscopy Sciences). After 30 min, remaining solution on a grid was removed with a filter paper, and the grid was air-dried for 18 h. SEM images were obtained on a FEI Nova NanoSEM 230 microscope and Hitachi S-4800 FE SEM at an acceleration voltage of 10 kV. The sample was placed on a conductive carbon layer and coated with Pt with a thickness of 3 nm by using a K575X Sputter Coater. CLSM was performed on a FluoView 1000 Confocal Microscope (Olympus). The Porous structures of the samples were analysed by a nitrogen adsorption experiment at 77 K using a BEL BELSORP-Max system. The surface areas and pore size distributions of the samples were calculated by using the BET equation and the BJH method, respectively. Small-angle X-ray scattering data were obtained on the SAXS beam line (PLS-II 9A) at Pohang acceleration laboratory (Pohang, Korea). Powder X-ray diffraction pattern was obtained on a D/MAZX 2500V/PC of Rigaku (Japan), the sample was ground before the measurement.
Synthesis of BCPs
All BCPs were synthesized and characterized by the literature procedures reported earlier (Supplementary Figs 13 and 14; refs 36, 48). The characterization of resulting BCPs are summarized in Supplementary Table 1 in Supplementary Information.
SDEMS of BCPs
In a typical procedure, 2213 (20 mg) was dissolved in 1,4-dioxane (180 mg) in a 15-ml vial, and the resulting solution was kept at room temperature for 1 h before the use. A sealed humidity chamber was prepared by mixing 35 ml of 1,4-dioxane and 35 ml of water in a 100-ml vial, and then a cylindrical column to put a glass substrate was carefully added. A desired amount of the solution of 2213 was carefully cast on the glass slide, which was rapidly placed on the column in the humidity chamber. The humidity chamber was then sealed for 1 h. After completing SDEMS, the glass slide covered with the monolith of 2213 was immersed into excess water to quench the assembly process by vitrification of the PS block. The opaque monolithic film was then obtained after removing 1,4-dioxane by solvent exchange in water.
Surface functionalization of the mesoporous monolith of 2213/NH2–PEG45–PS210
The solution of 2123/NH2–PEG45–PS210 (93:7 w/w in 1,4-dioxane) was applied under SDEMS condition. The monolith was then reacted with excess amount of NHS–PEG4–biotin (1,020 eq., Thermo Scientific) for 48 h, followed by washing with methanol and PBS (pH 7.4) several times. The monolith was incubated with excess amount of streptavidin homo-tetramer having fluorescein dye (54 kDa, Sigma) in PBS (pH 7.4) for 26 h. The excess streptavidin was removed by washing with PBS (pH 7.4). The streptavidin-bound monolith was immersed in a PBS solution of the biotin-mCherry fluorescent protein (35 kDa), followed by washing with PBS (pH 7.4).
Synthesis of S-TiO2 and mS-SiO2
The monolith of 2213 (thickness 40 μm, 1 cm2 area) was impregnated with titanium (IV) isopropoxide, and then the acid-catalysed crosslinking of Ti(OiPr)4 was allowed to form TiO2 under HCl vapour for 2 h. The resulting white monolith was sintered at 500 °C under air condition for 3 h. Polymeric silica sol was prepared by refluxing TEOS, ethanol, water and HCl (molar ratios: 1:3:1:5 × 10−5) at 80 °C for 1 h. Subsequently, CTAB solution (molar ratios, CTAB:EtOH:HCl=0.1:17:0.00395) was added to the silica sol. The monolith of 2213 (thickness 40 μm, 1 cm2 area) was soaked with the fresh sol, and aged at 40 °C for 1 h. The impregnated monolith was calcined under air condition at 520 °C for 4 h.
Typical procedure for photodegradation reaction
TiO2 powder (3.0 mg) was suspended in aqueous solution (3 ml) of methylene blue (0.01 g/l) in a quartz cuvette. Before ultraviolet irradiation, the suspension was stirred in dark for 30 min to ensure the adsorption–desorption equilibrium of methylene blue onto the TiO2 surfaces. The suspension was then irradiated under ultraviolet light (λ=254 nm, 30 W). A portion of the reaction mixture was picked up from the mixture, centrifuged and analysed by ultraviolet-visible absorption spectroscopy. The kinetics of the degradation reaction was evaluated using the equation ln(C0/C)=kt, where k is the rate constant and t is the irradiation time.
How to cite this article: Park, C. et al. Mesoporous monoliths of inverse bicontinuous cubic phases of block copolymer bilayers. Nat. Commun. 6:6392 doi: 10.1038/ncomms7392 (2015).
Wu, D. et al. Design and preparation of porous polymers. Chem. Rev. 112, 3959–4015 (2012) .
Jackson, E. A. & Hillmyer, M. A. Nanoporous membranes derived from block copolymers: from drug delivery to water filtration. ACS Nano 4, 3548–3553 (2010) .
Querelle, S. E., Jackson, E. A., Cussler, E. L. & Hillmyer, M. A. Ultrafiltration membranes with a thin poly(styrene)-b-poly(isoprene) selective layer. ACS Appl. Mater. Interfaces 5, 5044–5050 (2013) .
Svec, F. Porous polymer monoliths: amazingly wide variety of techniques enabling their preparation. J. Chromatogr. A 1217, 902–924 (2010) .
Shannon, M. A. et al. Science and technology for water purification in the coming decades. Nature 452, 301–310 (2008) .
Tokarev, I. & Minko, S. Multiresponsive, hierarchically structured membranes: new, challenging, biomimetic materials for biosensors, controlled release, biochemical gates, and nanoreactors. Adv. Mater. 21, 241–247 (2009) .
Lee, H.-C., Hsueh, H.-Y., Jeng, U. & Ho, R.-M. Functionalized nanoporous gyriod SiO2 with double-stimuli-responsive properties as environment-selective delivery systems. Macromolecules 47, 3041–3051 (2014) .
Crossland, E. J. W. et al. A bicontinuous double gyroid hybrid solar cell. Nano Lett. 9, 2807–2812 (2009) .
Crossland, E. J. W. et al. Mesoporous TiO2 single crystals delivering enhanced mobility and optoelectronic device performance. Nature 495, 215–219 (2013) .
Lee, M. M. et al. Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science 338, 643–647 (2012) .
Torquato, S., Hyun, S. & Donev, A. Multifunctional composites: optimizing microstructures for simultaneous transport of heat and electricity. Phys. Rev. Lett. 89, 266601 (2002) .
Martín-Moreno, L., Gracía-Vidal, F. J. & Somoza, A. M. Self-assembled triply periodic minimal surfaces as molds for photonic band gap materials. Phys. Rev. Lett. 83, 73–75 (1999) .
Dorin, R. M., Sai, H. & Wiesner, U. Hierarchically porous materials from block copolymers. Chem. Mater. 26, 339–347 (2014) .
Peinemann, K.-V., Abetz, V. & Simon, P. F. W. Asymmetric superstructure formed in a block copolymer via phase separation. Nat. Mater. 6, 992–996 (2007) .
Phillip, W. A. et al. Tuning structure and properties of graded triblock terpolymer-based mesoporous and hybrid films. Nano Lett. 11, 2892–2900 (2011) .
Seo, M. & Hillmyer, M. A. Reticulated nanoporous polymers by controlled polymerization-induced microphase separation. Science 336, 1422–1425 (2012) .
Sai, H. et al. Hierarchical porous polymer scaffolds from block copolymers. Science 341, 530–534 (2013) .
Samitsu, S. et al. Flash freezing route to mesoporous polymer nanofibre networks. Nat. Commun. 4, 2653 (2013) .
Zhou, N., Bates, F. S. & Lodge, T. P. Mesoporous membrane templated by a polymeric bicontinuous microemulsion. Nano Lett. 6, 2354–2357 (2006) .
Wan, Y., Shi, Y. & Zhao, D. Supramolecular aggregates as templates: ordered mesoporous polymers and carbons. Chem. Mater. 20, 932–945 (2008) .
Zalusky, A. S., Olayo-Valles, R., Taylor, C. J. & Hillmyer, M. A. Mesoporous polystyrene monoliths. J. Am. Chem. Soc. 123, 1519–1520 (2001) .
Olson, D. A., Chen, L. & Hillmyer, M. A. Templating nanoporous polymers with ordered block copolymers. Chem. Mater. 20, 869–890 (2008) .
Li, L. et al. Gyroid nanoporous membranes with tunable permeability. ACS Nano 5, 7754–7766 (2011) .
Mai, Y. & Eisenberg, A. Self-assembly of block copolymers. Chem. Soc. Rev. 41, 5969–5985 (2012) .
Schacher, F. H., Rupar, P. A. & Manners, I. Functional block copolymers: nanostructured materials with emerging applications. Angew. Chem. Int. Ed. 51, 7898–7921 (2012) .
Jung, A., Rangou, S., Abetz, C., Filiz, V. & Abetz, V. Structure formation of integral asymmetric composite membranes of polystyrene-block-poly(2-vinylpyridine) on a nonwoven. Macromol. Mater. Eng. 297, 790–798 (2012) .
Hahn, J. et al. Structure formation of integral-asymmetric membranes of polystyrene-block-poly(ethylene oxide). Polym. Sci. Part B Polym. Phys. 51, 281–290 (2013) .
Phillip, W. A. et al. Tuning structure and properties of graded triblock terpolymer-based mesoporous and hybrid films. Nano Lett. 11, 2892–2900 (2011) .
Dorin, R. M. et al. Solution small-angle X-ray scattering as a screening and predictive tool in the fabrication of asymmetric block copolymer membranes. ACS Macro Lett. 1, 614–617 (2012) .
Marques, D. S. et al. Self-assembly in casting solutions of block copolymer membranes. Soft Matter 9, 5557–5564 (2013) .
Qiu, X. et al. Selective separation of similarly sized proteins with tunable nanoporous block copolymer membranes. ACS Nano 7, 768–776 (2012) .
Mackay, A. L. Periodic minimal surfaces. Physica 131B, 300–305 (1985) .
Zhang, L. et al. Mesosized crystal-like structure of hexagonally packed hollow hoops by solution self-assembly of diblock copolymers. Phys. Rev. Lett. 79, 5034–5037 (1997) .
Hales, K., Chen, Z., Wooley, K. L. & Pochan, D. J. Nanoparticles with tunable internal structure from triblock copolymers of PAA-b-PMA-b-PS. Nano Lett. 8, 2023–2026 (2008) .
McKenzie, B. E. et al. Temperature-responsive nanospheres with bicontinuous internal structures from a semicrystalline amphiphilic block copolymer. J. Am. Chem. Soc. 132, 10256–10259 (2010) .
La, Y. et al. Colloidal inverse bicontinuous cubic membranes of block copolymers with tunable surface functional groups. Nat. Chem. 6, 534–541 (2014) .
Yu, H., Qiu, X., Nunes, S. P. & Peinemann, K.-V. Biomimetic block copolymer particles with gated nanopores and ultrahigh protein sorption capacity. Nat. Commun. 5, 4110 (2014) .
Yaghmur, A., Laggner, P., Zhang, S. & Rappolt, M. Tuning curvature and stability of monoolein bilayers by designer lipid-like peptide surfactants. PLoS ONE 5, e479 (2007) .
Han-Yu Hsueh, H.-Y. et al. Shifting networks to achieve subgroup symmetry properties. Adv. Mater. 26, 3225–3229 (2014) .
Shaner, N. C. et al. Improved monomeric red, orange and yellow fluorescent proteins derived from Discosoma sp. red fluorescent protein. Nat. Biotechnol. 22, 1567–1572 (2004) .
Li, W., Wu, Z., Wang, J., Elzatahry, A. A. & Zhao, D. A perspective on mesoporous TiO2 materials. Chem. Mater. 26, 287–298 (2014) .
Gajjela, S. R., Ananthanarayanan, K., Yap, C., Grätzel, M. & Balaya, P. Synthesis of mesoporous titanium dioxide by soft template based approach: characterization and application in dye-sensitized solar cells. Energy Environ. Sci. 3, 838–845 (2010) .
Chen, X., Liu, L., Yu, P. Y. & Mao, S. S. Increasing solar absorption for photocatalysis with black hydrogenated titanium dioxide nanocrystals. Science 331, 746–750 (2011) .
Wang, X. H. et al. Wavelength-Sensitive Photocatalytic degradation of methyl orange in aqueous suspension over iron(III)-doped TiO2 nanopowders under UV and visible light irradiation. J. Phys. Chem. B. 110, 6804 (2006) .
Lu, Y. et al. Continuous formation of supported cubic and hexagonal mesoporous films by sol-gel dip-coating. Nature 389, 364–368 (1997) .
Na, K. et al. Directing zeolite structures into hierarchically nanoporous architectures. Science 333, 328–332 (2011) .
Brinker, C. J., Lu, Y., Sellinger, A. & Fan, H. Evaporation-induced self-assembly: nanostructures made easy. Adv. Mater. 11, 579–585 (1999) .
Jeong, M. G., van Hest, J. C. M. & Kim, K. T. Self-assembly of dendritic-linear block copolymers with fixed molecular weight and block ratio. Chem. Commun. 48, 3590–3592 (2012) .
This research was supported by National Research Foundation (NRF) of Korea (NRF-2013R1A1A013075) and UNIST (UMI future challenge grant). C.P. acknowledges NRF for the research fellowship (2013R1A1A2063049). K.T.K also thanks to KIST-UNIST-Ulsan Center (KUUC) for financial support (2V03280). We thank UNIST Central Research Facilities (UCRF) and UNIST-OLYMPUS Biomed Imaging Center (UOBC) for microscopy facilities. K.T.K. thanks Professor Xiaosong Wang for valuable discussions and comments on this work.
The authors declare no competing financial interests.
About this article
Cite this article
Park, C., La, Y., An, T. et al. Mesoporous monoliths of inverse bicontinuous cubic phases of block copolymer bilayers. Nat Commun 6, 6392 (2015). https://doi.org/10.1038/ncomms7392
This article is cited by
Polymer Journal (2020)
Science China Materials (2020)
Nature Communications (2019)
Templated synthesis of cubic crystalline single networks having large open-space lattices by polymer cubosomes
Nature Communications (2018)