Figure 1: SEM images of the morphologies of Li metal after plating on Cu substrates in different electrolytes. | Nature Communications

Figure 1: SEM images of the morphologies of Li metal after plating on Cu substrates in different electrolytes.

From: High rate and stable cycling of lithium metal anode

Figure 1

(a,b) 1 M LiPF6-PC. (c,d) 4 M LiFSI-DME. The current density was 1.0 mA cm−2 and the deposition time was 1.5 h. The diameter of the Cu substrate shown in the insert of (a,c) was 2 cm. Scale bar, 10 μm.