Materials providing broadband light antireflection have applications as highly transparent window coatings, military camouflage, and coatings for efficiently coupling light into solar cells and out of light-emitting diodes. In this work, densely packed silicon nanotextures with feature sizes smaller than 50 nm enhance the broadband antireflection compared with that predicted by their geometry alone. A significant fraction of the nanotexture volume comprises a surface layer whose optical properties differ substantially from those of the bulk, providing the key to improved performance. The nanotexture reflectivity is quantitatively well-modelled after accounting for both its profile and changes in refractive index at the surface. We employ block copolymer self-assembly for precise and tunable nanotexture design in the range of ~10–70 nm across macroscopic solar cell areas. Implementing this efficient antireflection approach in crystalline silicon solar cells significantly betters the performance gain compared with an optimized, planar antireflection coating.
Proper design of an antireflection coating involves managing the refractive index mismatch at the abrupt optical interface1. The most straightforward approach places a single layer of intermediate optical index at the interface to create destructive interference in the reflected light, providing full antireflection at a single wavelength, λ=4ni·t, with material thickness (t) and refractive index , where nS and nA are the refractive indices of the substrate and air, respectively. Increasing broadband coverage, for application in transparent window coatings2,3,4,5, military camouflage6 or solar cells7,8,9,10,11,12,13,14,15, is possible using thin-film multilayer schemes16. An alternative to thin-film-coating strategies instead patterns the interface at subwavelength dimensions, creating an effective medium between the substrate and air, with ni changing gradually from nA to nS10,11,17. Such structures, often called moth eyes because of their biomimicry, provide broadband antireflection over a wide range of incident light angles when subwavelength textures are taller than t~0.4·λ and spaced closer than ℓ~λ/2ns12,14,18,19,20.
In this work, we enhance the broadband antireflection properties of a nanofabricated moth eye structure through simultaneous control of both the geometry and optical properties, by designing nanotextures sufficiently small to take advantage of a beneficial material surface layer only a few nm thick.
We leverage block copolymer self-assembly and plasma etching to fabricate highly regular surface nanotextures, with precise control over the texture’s lateral feature size in the range of 10–70 nm, vertical profile and feature density. Self-assembly based nanofabrication provides a scalable approach to creating deeply subwavelength moth eye structures (schematics in Fig. 1a). We pattern surface nanotextures on polished (100) silicon by first self-assembling a cylindrical phase polystyrene-block-poly(methyl methacrylate) (PS-b-PMMA) block copolymer thin film (Mw=99 kg mol−1, PS:PMMA ~7:3) by spin-coating and thermal annealing. Appropriate surface pretreatment facilitates perpendicular orientation of uniformly sized 25-nm-diameter PMMA cylindrical microdomains within a PS matrix, locally hexagonally arranged with a separation ℓ=52±6 nm21. We systematically vary ℓ in the nanotexture from 40±3 to 67±13 nm using block copolymers with total molecular weight ranging between 67 and 177 kg mol−1. Exposing assembled copolymer films to three sequential cycles of tri(methyl aluminium) and water vapour selectively loads PMMA microdomains with alumina by sequential infiltration synthesis (Fig. 1b; Supplementary Fig. 1)22.
The self-assembled alumina pattern provides a rugged template for creating surface nanotextures using plasma etching. We anisotropically etch the underlying silicon by inductively coupled plasma-reactive ion etching using a gas chemistry of hydrogen bromide, chlorine and oxygen, which produces a sidewall angle of >80° (Fig. 1c,d). The gas mixture and etch parameters control the nanotexture profile, with t increasing with etch time and taller nanotextures tapering to smaller sizes at their tops (Fig. 1c,d). Block copolymer self-assembly provides a scalable method for producing these controlled nanotextures over arbitrarily large areas, evidenced by its successful prior integration into 300-mm-diameter semiconductor wafer-processing facilities23. Previous investigations have used different block copolymer phases5,24 and micelles25 with larger length scales (>100 nm) as templates for nanotextures imparting antireflection to glass and silicon surfaces, which are too large to observe the enhancements described here.
The average reflectance of the nanotextured silicon surface decreases with increasing feature height (t) in the λ range of 400 nm to 1 μ, from 35% on a flat surface to <1% for tapered nanotextures with t=230 nm and ℓ=52 nm (Fig. 1e). The nanotextured surface is significantly less reflective than antireflection methods employed in commercial silicon solar cells, including flat silicon coated with an 80-nm-thick silicon nitride layer (Fig. 1e, green open circles) and chemically etched, inverted pyramid coatings (Fig. 1e, green inverted triangles, simulated using OPAL 2 (ref. 26)). This latter scheme requires sacrificing ~10 μ of silicon at the device top surface, which may have consequences for thin-film devices. In practice, all types of silicon solar cells are bonded to a protective glass or plastic top coating. In principle, block copolymer antireflection schemes can be applied to glass surfaces as well. The tapered vertical profile gradually changes ni from air (nA=1) to silicon (nS=5.6 at 400 nm; nS=3.6 at 1 μm). Shallower nanotextures preferentially decrease the reflectance at shorter λ (Fig. 1e, blue colour), consistent with the requirement of t/λ>0.4 for full antireflection in a moth eye structure. Taller nanotextures extend the antireflection to longer λ (Fig. 1e, red colour). We estimate neff(z) for hexagonal arrangements of cones with subwavelength dimensions that taper to a point at their top (z=0) and join at their base (z=t) using the effective medium approximation (EMA) (q=0, Supplementary Methods), valid for λ>π·ℓ~200 nm, by calculating the fractional areal coverage of silicon [fS(z)] and air [fA(z)] versus depth (z): and fA(z)=[1−fS(z)]. Neglecting light absorption in air and silicon:
with A and S are the frequency-dependent dielectric constants of air and silicon, respectively.
The surface nanotexture provides broadband antireflection over a wide range of incident light angles. The reflectance of a flat silicon surface (at 650 nm) versus incident angle is markedly different for s- and p-polarized light, while a nanotextured silicon surface with t=230 nm and ℓ=52 nm displays similar, reduced reflectance for both polarizations (Fig. 1f). The texture’s deeply subwavelength lateral separation (ℓ) eliminates diffraction effects (that is, ℓ<λ/2n for λ>400 nm), such that the average reflectance (R≡(spol+ppol)/2) remains <4% for angles as high as 60° from normal. The nanotexture provides omnidirectional antireflection across a broad λ-range. For example, at a 45° incident angle the average reflectance of s- and p-polarized light between 400 nm<λ<1 μm is <1%, more than 10 × smaller than that of flat silicon (Fig. 1g).
Reflectance dependence on nanotexture dimensions
Nanotextures made from self-assembled block copolymer templates with different ℓ have qualitatively similar vertical profiles and, when sufficiently tall, also provide high antireflection across a broad range of λ. A powerful characteristic of block copolymers as patterning materials is their lateral size tunability. For example, a cylindrical phase PS-b-PMMA with Mw=67 kg mol−1 generates surface textures with ℓ=40±3 nm (Fig. 2a), while Mw=132 and 177 kg mol−1 produce structures with ℓ=60±8 and 67±13 nm, respectively (Fig. 2b; Supplementary Fig. 2). Increasing the copolymer Mw broadens the distributions of nearest neighbour separations (ℓ) (Supplementary Fig. 3) and decreases the degree of hexagonal ordering (Supplementary Fig. 4), because of slower self-assembly kinetics. However, neither of these affects the general results of our experiments because of the deeply subwavelength dimensions of our structures (ℓ≪λ).
Textures with smaller feature sizes outperform the geometric model of equation (1), needing <50% of the minimum height t~0.4 × λ~400 nm to achieve average broadband reflectance of <1%. The required nanotexture height decreases linearly with ℓ (Fig. 2c; Fig. 2d, red triangles), shrinking to only ~165 nm for ℓ=40 nm. The largest textures we measured (ℓ=67 nm) require a height of t=440 nm (Fig. 2d, red triangles), similar to the value of 430 nm for <1% average reflectance calculated using the transfer matrix method (Fig. 2d, grey line; Supplementary Methods) and consistent with the taller heights of other silicon moth eye structures with larger lateral dimensions12,14,27. Calculations of the reflectance of a silicon nanotexture with an hourglass profile and alumina cap (Fig. 2d, inset) also fail to capture the measured trend with decreasing ℓ (Fig. 2d, open circles). Reflectance values calculated using the actual nanotexture refractive index profile measured by spectroscopic ellipsometry (SE) (for ℓ=52 nm) more accurately reproduce the measured data at smaller ℓ (Fig. 2d, open triangles). Because the refractive index profile contains both shape- and material-dependent properties, we conclude that the measured reflectance results from combined effects of the geometry and modifications to the silicon surface optical properties (Supplementary Fig. 9)28.
The chlorine, bromine and oxygen etch chemistries we use to generate the nanotextures are known to modify the silicon within ~5–10 nm of the surface28,29, including redeposition of silicon oxychloride30,31, creating a surface layer with substantially different optical properties32 and providing an additional mechanism for grading ni between air and silicon. In nanotextures with larger dimensions, this surface layer is an inconsequential fraction of the total volume. However, because our nanotextures have lateral feature sizes on the scale of 10 nm, even material modifications within a few nm of the surface comprise a significant volume fraction, and can thus substantially alter ni of the entire structure.
We visualize changes in the nanotexture surface by comparing cross-sectional scanning electron microscope images before (Fig. 3a) and after (Fig. 3b) treating with a dilute (50:1) hydrofluoric acid:water mixture (buffered with NH4F), which removes surface oxides. In addition to stripping the alumina caps, the etch narrows the texture radius by several nm, consistent with removal of a silicon oxide layer that has been previously observed during studies of similar etch chemistries (Supplementary Fig. 5)30,31. These results are consistent with transmission electron microscopy images showing the etched silicon nanotextures coated with an amorphous material (Supplementary Fig. 6). X-ray photoelectron spectra of the nanotexture’s Si 2p and O 1s core levels display higher binding-energy peaks (Supplementary Methods; Supplementary Fig. 7), consistent with those of a material previously identified as a porous, anodic silicon oxide33. SE measurements of the complex refractive index profile (n+ik) of nanotextures with ℓ=52 nm and increasing t show the effect of such a modification, most easily observed at the nanotexture base, where ni increases abruptly from ~2 to the bulk silicon value (ns=3.7) (Fig. 3c). In a two-dimensional close-packed arrangement of nanotextures composed of silicon alone, we would expect a ni reduced only slightly from that of silicon at the base (ni~3.5; equation (1) with z=t). Transfer matrix reflectance calculations of silicon nanotextures (ℓ=52 nm) using optical constants obtained from SE measurements accurately describe the measured data for all nanotexture heights (Fig. 3d), capturing both the reflectance magnitude and optical resonance positions. These simulations provide a significantly improved description compared with similar calculations using bulk silicon optical constants (Supplementary Fig. 9).
Applying the block copolymer-based surface nanotexture to a crystalline silicon solar cell improves the power conversion efficiency under AM1.5G illumination from 8.7 to 13.1% (Fig. 4a). The broadband antireflection improves the photocurrent (Jsc) from 22 to 33 mA cm−2, a substantial increase of 50% that agrees well with the integrated (from 400 to 1,000 nm) 50% increase in solar power transmitted to the device (Supplementary Methods; Supplementary Fig. 16). The photocurrent is significantly improved over that of similar planar devices coated instead with an optimized 80-nm-thick silicon nitride antireflection coating (Fig. 4a, green open circles). The surface nanotexture allows the device to maintain nearly 100% of the Jsc at normal incidence, even at oblique light angles 60° from normal (Fig. 4b). The performance of all three devices is limited by charge recombination, which manifests in the device dark current (J0) and diode ideality factor (ndiode), and reduces the device open-circuit voltage (Voc). The silicon nitride antireflection coating slightly reduces both J0 (to 10−3 mA cm−2) and ndiode (to ~1.8) compared with both planar and nanotextured devices (where J0~3 × 10−3 mA cm−2 and ndiode~2), which improves the device fill factor from 70 to 71%. Our future studies will target understanding the passivation effects of the nanotextured interface and integration with higher-performance devices.
Our nanostructured samples included surface textures made from PS-b-PMMA block copolymers (Polymer Source Inc.) with molecular weights of MW=67 kg mol−1 (PS:PMMA 46:21, polydispersity PD=1.09), 99 kg mol−1 (PS:PMMA 64:35, PD=1.09), 132 kg mol−1 (PS:PMMA 96.5:35.5, PD=1.11) and 177 kg mol−1 (PS:PMMA 131:46, PD=1.10). We mixed solutions of all polymers in toluene at concentrations of 1% by weight. Block copolymer films were spin cast from solution onto silicon wafers at rates of 3K r.p.m. (67 K polymer), 2K r.p.m. (99 K polymer) and 1.6K r.p.m. (132 and 177 K polymers) and then annealed at <1 Torr at a temperature of 205 °C for 12 h. Prior to spin coating the block copolymer, we coated with a PS-r-PMMA random copolymer brush (MW≃11 kg mol−1, PS:PMMA 52:48) by spin casting (0.4 wt % in toluene, 600 r.p.m.), thermally annealing for 4 h and rinsing with toluene. We converted self-assembled PS-b-PMMA templates to aluminium oxide nanostructures by infiltration of the PMMA domains using three sequential exposures to tri-methyl aluminium and water vapour (for 300 s each at >5 Torr and 85 °C) in a commercial atomic layer deposition system (Cambridge Nanotech Savannah S100). We removed all remaining organic materials by oxygen plasma (20 W rf power, 100 mTorr O2, 2 min) using a March Plasma CS1701 etcher.
We generate nanotextures in silicon having a conical profile by inductively coupled plasma-reactive ion etching using an Oxford Instrument Plasma Lab 100 with a 50:50:10 ratio of HBr, Cl2 and O2 gas (10 mTorr, 60 W rf power, 250 W inductive plasma power) at room temperature. We measure a vertical silicon etch rate of ~2 nm s−1 and a slower lateral etch rate of 0.07 nm s−1. The process includes a 10-s breakthrough using BCl3 and Cl2 (20:5 standard cubic centimetre per minute, 10 mTorr, 100 W rf power, 800 W inductive plasma power). Samples were characterized by scanning electron microscopy (Hitachi S4800) operating at 20 kV.
We fabricated silicon solar cells from Czochralski p-type (100) single-side-polished silicon wafers (550 μm thick, boron doped, 8 Ω cm). We used 4-cm2 samples and are limited in our laboratory to 100-mm-diameter substrates. We formed the device p–n junction by diffusing phosphorous dopants from a solid source (ACCUSPIN, Honeywell P-8545) by first spin-coating at 3K r.p.m. for 30 s, baking on a hotplate at 150 °C (1 min) and annealing at 1,050 °C (20 s) in Ar using rapid thermal annealing processing. We removed the phosphosilicate glass from the substrate top surface using 10:1 buffered hydrofluoric acid (10 m). We formed the device back-contact by thermal evaporation of aluminium (100 nm) and annealing at 600 °C (1 m). The front-side contact was made with a photolithography-defined grid pattern and metal deposition of titanium (70 nm) and silver (100 nm). The total device area including front-side grid contacts is (0.5 cm)2. We deposited silicon nitride antireflection layers (80 nm) onto control devices by plasma-enhanced chemical vapour deposition prior to front- and back-contact metallization. We also formed surface nanotextures by the block copolymer process after p–n junction diffusion but prior to front- and back-contact metallization.
Ultraviolet–visible light spectroscopy and spectroscopic ellipsometry
We performed hemispherical reflectance measurements using a PerkinElmer Lambda 950 spectrophotometer equipped with an integrating sphere detector. The samples were placed at an 8° angle relative to the incident beam direction. Specular reflectivity for varying angle of incidence was measured using a supercontinuum laser at different wavelengths and angle of incidence ranging from 10° to 85°. We crosschecked these data with measurements using a Woollam Ellipsometer for angles of incidence >45°.
We performed spectroscopic ellipsometry measurements using a J. A. Woollam Variable Angle Spectroscopic Ellipsometer M-2000, based on the diode array rotating compensator ellipsometer technology. We made measurements in three distinct spots on each sample in the wavelength range of 210–1,700 nm and at angles varying between 45° and 75° in divisions of 7.5°. We analysed ellipsometric data by simultaneously fitting identical models from each of the three spots, which were defined with coupled complex refractive indices, using the WVASE32 software (version 3.770, J. A. Woollam Co.). We determined the best fit for the optical constants by minimizing the mean square error between the measured and the modelled curves using the Levenberg–Marquardt multivariate regressions algorithm.
We described the silicon material using a Drude model with critical-point-parabolic-band oscillators at 3.34 and 4.31 eV. Nanotextured silicon films were modelled using a graded EMA of optical constants of silicon and air/void, where the volume fraction of air/void versus depth is geometrically calculated. In this model, the optical constants determined from bare silicon were allowed to vary to give modified silicon optical constants. We divided the EMA layer into 40 slices and the modified silicon optical constants were held constant within each slice. More details can be found in the Supplementary Methods.
X-ray photoelectron spectroscopy
X-ray photoelectron spectroscopy measurements were performed in an ultrahigh vacuum system equipped with a SPECS Phoibos 100 hemispherical analyzer and a dual-anode X-ray source. All measurements were carried out with non-monochromatized Al Ka excitation. The measured data are fit with a Gaussian–Lorentzian product analysis (60% Lorentzian) carried out using CasaXPS software ( www.casaxps.com).
We computationally model the light reflection, transmission and absorption spectra by the different nanostructured surfaces using the transfer matrix method. For these calculations, we use the software package http://sjbyrnes.com/fresnel-solver.nb with some modifications. More details are provided in the Supplementary Methods.
Solar cell measurement
We measure the current–voltage characteristics of our silicon solar cells in the dark and under simulated AM1.5G illumination (calibrated using a certified silicon reference cell) at normal incidence using an HP4156B Semiconductor Parameter Analyzer. We perform the single-wavelength angular current–voltage measurements using a Thorlabs HNL150L EC, He Ne Laser at 632.8 nm. We mounted the sample on a Thorlabs CR1-Z7-motorized rotation stage and rotated in steps of 5°. The angular reflection measurements under oblique light incidence are carried out using a Fianium WL-Micro supercontinuum laser. The polarization of the incident light is selected using a Thorlabs broadband-polarizing beamsplitter cube and is adjusted using a half-wave plate. The incident/reflected light is detected using a Thorlabs PM100A power meter with a SV120VC silicon photo-detector.
How to cite this article: Rahman, A. et al. Sub-50-nm self-assembled nanotextures for enhanced broadband antireflection in silicon solar cells. Nat. Commun. 6:5963 doi: 10.1038/ncomms6963 (2015).
Chattopadhyay, S. et al. Anti-reflecting and photonic nanostructures. Mater. Sci. Eng. R 69, 1–35 (2010).
Park, K.-C. et al. Nanotextured silica surfaces with robust superhydrophobicity and omnidirectional broadband supertransmissivity. ACS Nano 6, 3789–3799 (2012).
Gombert, A. et al. Subwavelength-structured antireflective surfaces on glass. Thin Solid Films 351, 73–78 (1999).
Xi, J.-Q. et al. Optical thin-film materials with low refractive index for broadband elimination of fresnel reflection. Nat. Photon. 1, 176–179 (2007).
Paivanranta, B. et al. Nanofabrication of broad-band antireflective surfaces using self-assembly of block copolymers. ACS Nano 5, 1860–1864 (2011).
Phan, L. et al. Reconfigurable infrared camouflage coatings from a cephalopod protein. Adv. Mater. 25, 5621–5625 (2013).
Zhu, J., Hsu, C.-M., Yu, Z., Fan, S. & Cui, Y. Nanodome solar cells with efficient light management and self-cleaning. Nano Lett. 10, 1979–1984 (2009).
Yu, P. et al. Towards high-efficiency multi-junction solar cells with biologically inspired nanosurfaces. Prog. Photovolt. Res. Appl. 22, 300–307 (2012).
Wang, K. X., Yu, Z., Liu, V., Cui, Y. & Fan, S. Absorption enhancement in ultrathin crystalline silicon solar cells with antireflection and light-trapping nanocone gratings. Nano Lett. 12, 1616–1619 (2012).
Koynov, S., Brandt, M. S. & Stutzmann, M. Black nonreflecting silicon surfaces for solar cells. Appl. Phys. Lett. 88, 203107–203109 (2006).
Branz, H. M. et al. Nanostructured black silicon and the optical reflectance of graded-density surfaces. Appl. Phys. Lett. 94, 231121–231123 (2009).
Huang, Y.-F. et al. Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures. Nat. Nano 2, 770–774 (2007).
Oh, J., Yuan, H.-C. & Branz, H. M. An 18.2%-efficient black-silicon solar cell achieved through control of carrier recombination in nanostructures. Nat. Nano 7, 743–748 (2012).
Sai, H., Kanamori, Y., Arafune, K., Ohshita, Y. & Yamaguchi, M. Light trapping effect of submicron surface textures in crystalline Si solar cells. Prog. Photovolt. Res. Appl. 15, 415–423 (2007).
Wang, W., Wu, S., Reinhardt, K., Lu, Y. & Chen, S. Broadband light absorption enhancement in thin-film silicon solar cells. Nano Lett. 10, 2012–2018 (2010).
Dobrowolski, J., Poitras, D., Ma, P., Vakil, H. & Acree, M. Toward perfect antireflection coatings: numerical investigation. Appl. Opt. 41, 3075–3083 (2002).
Yuan, H.-C. et al. Efficient black silicon solar cell with a density-graded nanoporous surface: optical properties, performance limitations, and design rules. Appl. Phys. Lett. 95, 123501–123503 (2009).
Wilson, S. & Hutley, M. The optical properties of ‘moth eye’ antireflection surfaces. J. Mod. Opt. 29, 993–1009 (1982).
Clapham, P. B. & Hutley, M. C. Reduction of lens reflexion by the "moth eye" principle. Nature 244, 281–282 (1973).
Parker, A. R. & Townley, H. E. Biomimetics of photonic nanostructures. Nat. Nano 2, 347–353 (2007).
Thurn-Albrecht, T. et al. Nanoscopic templates from oriented block copolymer films. Adv. Mater. 12, 787–791 (2000).
Peng, Q., Tseng, Y.-C., Darling, S. B. & Elam, J. W. Nanoscopic patterned materials with tunable dimensions via atomic layer deposition on block copolymers. Adv. Mater. 22, 5129–5133 (2010).
Black, C. T. et al. Polymer self assembly in semiconductor microelectronics. IBM J. Res. Dev. 51, 605–633 (2007).
Zhang, X. et al. Silicon patterning using self-assembled PS-b-PAA diblock copolymer masks for black silicon fabrication via plasma etching. Plasma Processes Polym. 9, 968–974 (2012).
Lohmuller, T., Helgert, M., Sundermann, M., Brunner, R. & Spatz, J. P. Biomimetic interfaces for high-performance optics in the deep-UV light range. Nano Lett. 8, 1429–1433 (2008).
McIntosh, K. R. & Baker-Finch, S. C. OPAL 2: Rapid Optical Simulation Of Silicon Solar Cells. (Photovoltaic Specialists Conference (PVSC)), 2012 38th IEEE, 000265–000271 (Austin, TX, USA, 2012).
Sun, C.-H., Jiang, P. & Jiang, B. Broadband moth-eye antireflection coatings on silicon. Appl. Phys. Lett. 92, 061112–061113 (2008).
Blayo, N. et al. Comparison of advanced plasma sources for etching applications. IV. Plasma induced damage in a helicon and a multipole electron cyclotron resonance source. J. Vac. Sci. Technol. B 12, 1340–1350 (1994).
Awadelkarim, O. et al. Creation of deep gap states in Si during Cl2 or HBr plasma etch exposures. J. Vac. Sci. Technol. A 11, 1332–1336 (1993).
Kogelschatz, M., Cunge, G. & Sadeghi, N. Analysis of the chemical composition and deposition mechanism of the SiOx:SiCly layer on the plasma chamber walls during silicon gate etching. J. Vac. Sci. Technol. A 22, 624–635 (2004).
Ullal, S. J., Singh, H., Vahedi, V. & Aydil, E. S. Deposition of silicon oxychloride films on chamber walls during Cl2/O2 plasma etching of si. J. Vac. Sci. Technol., A 20, 499–506 (2002).
Wu, C. et al. Near-unity below-band-gap absorption by microstructured silicon. Appl. Phys. Lett. 78, 1850–1852 (2001).
Montero, I., Galan, L., De La Cal, E., Albella, J. & Pivin, J. Incorporation of oh radicals in anodic silicon oxide films studied by secondary-ion mass spectroscopy, X-ray photoelectron spectroscopy and IR analysis. Thin Solid Films 193, 325–332 (1990).
This research is supported by the US Department of Energy, Basic Energy Sciences at the Center for Functional Nanomaterials (A.R., H.X., X.T., P.S. and C.B.) and the Sustainable Energy Technologies Department (A.A. and M.E.) under Contract No. DE-AC02-98CH10886. We thank Drs Eric Stach and Nanditha Dissanayake for helpful discussions.
The authors declare no competing financial interests.
About this article
Cite this article
Rahman, A., Ashraf, A., Xin, H. et al. Sub-50-nm self-assembled nanotextures for enhanced broadband antireflection in silicon solar cells. Nat Commun 6, 5963 (2015). https://doi.org/10.1038/ncomms6963
This article is cited by
Nature Communications (2022)
Journal of Bionic Engineering (2019)
Review of Recent Advances in Applications of Vapor-Phase Material Infiltration Based on Atomic Layer Deposition