The lithium-sulphur battery relies on the reversible conversion between sulphur and Li2S and is highly appealing for energy storage owing to its low cost and high energy density. Porous carbons are typically used as sulfur hosts, but they do not adsorb the hydrophilic polysulphide intermediates or adhere well to Li2S, resulting in pronounced capacity fading. Here we report a different strategy based on an inherently polar, high surface area metallic oxide cathode host and show that it mitigates polysulphide dissolution by forming an excellent interface with Li2S. Complementary physical and electrochemical probes demonstrate strong polysulphide/Li2S binding with this ‘sulphiphilic’ host and provide experimental evidence for surface-mediated redox chemistry. In a lithium-sulphur cell, Ti4O7/S cathodes provide a discharge capacity of 1,070 mAh g−1 at intermediate rates and a doubling in capacity retention with respect to a typical conductive carbon electrode, at practical sulphur mass fractions up to 70 wt%. Stable cycling performance is demonstrated at high rates over 500 cycles.
Rechargeable batteries with high energy density and long-lasting cycle performance are highly sought-after for electric vehicles and large-scale electrochemical energy-storage systems. However, current Li-ion batteries using electrodes based on Li+-ion insertion chemistry cannot satisfy this demand in terms of specific energy1,2. Elemental sulphur—abundant and nontoxic—has become one of the most promising positive electrode active materials because of its high theoretical specific capacity (1,675 mAh g−1), based on a redox reaction that reversibly interconverts sulphur and Li2S via intermediate lithium polysulphides (LiPSs, that is, Li2Sn with n=4–8)3,4,5. Li-S cells generally experience low sulphur utilization and poor long-term cycling mainly because of three factors: poor conductivity of sulphur and its discharge products, a large volumetric expansion upon the formation of Li2S, and the dissolution of LiPS intermediates in liquid electrolytes, which triggers a polysulphide-shuttle process3,4,5. The latter results in low Coulombic efficiency unless the lithium electrode is passivated. The role of additives in protecting the lithium surface has been thoroughly elucidated6, re-inspiring the development of ‘catholyte’-type cells, where the LiPS is completely solubilized. These benefit from tailored cathode architecture designs, such as those based on woven carbon nanotubes7.
In the opposite tactic where polysulphide dissolution is constrained to increase volumetric energy density, a variety of approaches have been explored. These include solid-state electrolytes8,9,10 that show much promise for future development in conjunction with an ionically conductive sulphur cathode11. More effort, to date, has been devoted to the cathode side in order to physically confine the LiPSs within the pores or layers of carbonaceous materials that include mesoporous carbon12, hollow porous carbon spheres13,14, graphene15,16, conductive polymer nanotubes17 and carbon interlayers18. However, over long-term cycling, the hydrophilic LiPSs diffuse out from the hydrophobic pores. This is suspected to be because carbon, being non-polar in nature, does not bind favourably to the polar and ionic sulphides. A more targeted approach is to utilize chemical interactions between oxygen-containing functional groups and the LiPS species on the interface. First employed for polyethylene glycol grafted on mesoporous carbon12, more recent studies have demonstrated binding of LiPSs using graphene oxides19,20 or carbon materials decorated with an amphiphilic polymer21. However, the functional oxygen-containing groups either lower the overall electronic conductivity or are not permanently bound. Metal oxides, such as SiO2 (ref. 22), TiO2 (refs 23, 24) and Al2O3 (ref. 25) have also been utilized as both adsorbents, and coatings, to hinder the diffusion of LiPSs. Among these, polysulphide reservoirs rely on an insulating mesoporous oxide that traps the LiPS species without directly enabling their reduction22,23. Nonetheless, insulating oxides ultimately impede electron transport and Li+-ion pathways, thus leading to lower sulphur utilization and rate capability. Seminal work on metal-organic frameworks has shown that these effectively encapsulate LiPSs26, and a recent study has elucidated the role of their Lewis acid metal centres in polysulphide adsorption27. Although this confirms the importance of chemical interactions in hindering the migration of soluble polysulphides, the intrinsically low electrical conductivity nonetheless results in a relatively low specific discharge capacity of ~650 mAh g−1. Addressing these limitations is a key point to obtain better electrochemical properties.
Here, instead of relying solely on porosity to physically confine sulphides, we present a different approach based on a two-in-one strategy: creation of a bifunctional sulphur host material that combines inherent metallic conductivity with the ability to chemically bind LiPSs on the surface and facilitate reduction to Li2S. A high surface area Magnéli phase (Ti4O7) fulfills these roles and realizes excellent cycle performance and high-rate capability. While exhibiting bulk metallic conductivity as high as 2 × 103 S cm−1 at 298 K28, Ti4O7 also contains polar O-Ti-O units that have a high affinity for LiPSs. The presence of strong metal oxide-polysulphide interactions are demonstrated using X-ray photoelectron spectroscopy (XPS), X-ray absorption near-edge structure (XANES) and LiPS adsorption studies. Moreover, by comparison with hydrophobic carbonaceous materials, Li2S wetting with the Ti4O7 support is enhanced. This approach to cathode design results in low capacity fade rates for composites containing up to 70 wt% sulphur, even without special binders or surfactants.
Ti4O7 is a member of the TinO2n−1 Magnéli phases, substoichiometric compositions of metallic titanium oxides that form a homologous series between the end members TiO2 and Ti2O3. Their structures are characterized by two-dimensional shear plane slabs of Ti-O octahedra. Ti4O7 has been utilized as a Pt catalyst support for fuel cells because of its high electronic conductivity (about threefold greater than graphite)29; however, its utilization in an ultrahigh surface area modification, which is essential for optimal sulphide interaction, has not yet been reported for energy-storage applications. We synthesized this material by a simple polymer-mediated route (see Methods for details) that relies on the crosslinking of titanium ethoxide with polyethylene glycol followed by carbothermal reduction to crystallize the desired oxygen-deficient titanium oxide. The X-ray diffraction pattern (Fig. 1a) indicates that Ti4O7 is the primary crystalline phase; elemental microanalysis indicates the inclusion of 15.4 wt% residual amorphous carbon. The latter is important both to maintain a high surface area and to serve as a hydrophobic component for binding sulphur. High-resolution transmission electron microscopy (TEM) images (Fig. 1b) combined with bright/dark field imaging (Supplementary Fig. 1a,b) reveal that the material primarily comprises ~8–20 nm Ti4O7 crystals that are loosely bound with interspersed carbon. This gives rise to a bulk four-point probe electronic conductivity on pressed pellet of 3.2±0.1 S cm−1, which is naturally lower vis a vis the single crystal material but more than sufficient for excellent electron transport within the electrode. The resultant material exhibits a very high surface area of 290 m2 g−1 (see N2 adsorption/desorption measurements, Supplementary Fig. 2a), which is a factor of 100 times higher than conventional Ti4O7 (ref. 30). This is essential for interfacial interaction with LiPSs upon cycling as will be demonstrated below. The isotherm measurement also shows the presence of micro and mesopores (Supplementary Fig. 2b) that provide both surface area and additional spatial confinement.
The Ti4O7 was impregnated with 60–70 wt% sulphur by melt-diffusion at 155 °C, determined by thermogravimetric analysis (Supplementary Fig. 2c). In addition to intrusion into the pores, sulphur forms a conformal coating on the reduced oxide, as shown using scanning electron microscopy (SEM, Supplementary Fig. 1c). Energy-dispersive X-ray elemental mapping confirmed a uniform distribution of sulphur over the Magnéli oxide surface (Supplementary Fig. 3). To demonstrate the advantages of conductive oxide materials as a sulphur host versus carbonaceous materials, VULCAN XC72 carbon (denoted as VC) with a similar surface area of 260 m2 g−1 was used as a comparison.
The interaction between Ti4O7 and polysulphides
The interaction of different sulphur host materials (Ti4O7, VC and graphite) with LiPSs was probed using a combination of XPS and visual discrimination, taking Li2S4 as the representative polysulphide. The latter was prepared using previously reported methods31. An equivalent amount of target host material (based on surface area) was first added to a solution of Li2S4 in tetrahydrofuran. The superior intrinsic capability of Ti4O7 to adsorb Li2S4 was clearly obvious, as shown in Fig. 2b,c. Addition of Ti4O7 rendered the Li2S4 solution light yellow immediately upon contact and almost completely colourless after it was stirred for 1 h—indicating strong adsorption—whereas the graphite or VC solutions remained intense yellow-gold, indicative of no interaction.
The spectrum of Li2S4 materials were analysed using XPS after centrifugation and drying and the S 2p spectra are shown in Fig. 2d–f. Only the 2p3/2 component of the 2p3/2/2p1/2 doublet is quoted, following convention. The spectrum of Li2S4 (Fig. 2d) shows a 1:1 ratio of two 2p3/2 contributions at 161.6 and 163.1 eV, as expected for the terminal () and bridging sulphur (), respectively (Supplementary Table 1). The assignment is based on comparison with values reported for copper polysulphides32 and the similarity of the spectrum to that of other polysulphides we synthesized (Supplementary Fig. 4a,b). The assignment is in accord with the proposed chain-like structure of LiPSs where ab initio calculations show that the negative charge is localized at the termini.33 The spectrum of Li2S4 bound to Ti4O7 is very different: it exhibits two higher binding energy contributions at 164.3 and 164.8 eV (Fig. 2e), representing a +2.7 and +1.7 eV shift for and , respectively. A similar binding energy (164.3 eV) has been attributed to interaction of elemental sulphur with oxygen groups33. Although the precise nature of the binding of the sulphide with the metallic oxide is not yet elucidated, data clearly indicate that interaction of both the terminal and bridging sulphur in the LiPS with Ti4O7 surface results in the polarization of electrons away from the sulphur atoms to the electropositive titanium and/or oxygen vacancies at the interface (Fig. 2a). The terminal sulphur is more affected owing to its higher electron density. A relatively small shift of −0.2 eV to lower binding energy in the Ti 2p spectrum was also observed indicating increased electron density at the metal centre (Supplementary Fig. 4d,f). A chemical reaction such as oxidation of Li2S4 by the Ti4O7 host can be ruled out as a source of the shift, since the oxide has a lower redox potential (~1.75 V; typical of that of slightly reduced titanium oxides)34. This is confirmed by the fact that the discharge profile and voltage of the Li2S4/Ti4O7 is very different than elemental sulphur (Supplementary Fig. 5). We further note that binding energy shifts of a similar magnitude (1.1–3.8 eV) have been predicted on the basis of theory, and experimentally recorded, for anions such as NOxn− species adsorbed on alumina clusters35. The minor, broad background contribution between 166 and 169.5 eV on S 2p spectra (Fig. 2e,f) is characteristic of sulphite or sulphate36 arising from a trace amount of water in the solvent.
In contrast, the S 2p spectrum of Li2S4/VC shows two contributions at 161.6 and 163.1 eV, identical to that of Li2S4 (Fig. 2f). This, along with the intense colour of the Li2S4 solution even after long-term contact with VC, suggests that almost no adsorption occurs, resulting in essentially unaltered Li2S4 spectral features. An additional peak at 163.8 eV (Fig. 2f) is at the same energy for elemental sulphur supported on carbon (S0-C)37. Similar results were obtained for Li2S4/graphite (Supplementary Fig. 4c). This can be explained by the fact that where little or no interaction of LiPSs with support is present—as in the case of VC and graphite—the polysulphide species exist in rapid equilibria in solution. Disproportionation of intermediate-length LiPSs such as S42− to sulphur with lower and higher oxidation states is known to occur under these conditions38,39. Shifting of the equilibrium towards elemental sulphur formation is driven both by its insolubility and strong interaction with the carbon surface, thus accounting for the C-S0 contribution. The accompanying (lower oxidation state) LiPS does not contribute significantly to the averaged spectrum (that is, of the ‘Li2S4-x’) as long as the extent of the disproportionation reaction remains minor. These findings are in full accord with the LiPS adsorption studies described above.
The electrochemical performance of Ti4O7/S cathodes
To evaluate their electrochemical properties, the Ti4O7/S composites with either 60 or 70 wt% sulphur were cycled from 1.8 to 3.0 V versus Li/Li+. These performed almost identically. The galvanostatic profiles of the Ti4O7/S nanocomposite at different current densities (after an initial activation cycle at C/20, Fig. 3a) exhibit two typical well-defined plateaus at ~2.3 and 2.1 V. There is little increase in polarization with increasing rate, indicating favourable kinetics owing to the high electronic conductivity of the Ti4O7 support and good electrolyte accessibility of the discharged/charged products. The Ti4O7 host itself does not contribute to the capacity of the electrode as it accounts for a capacity of only ~6 mAh g−1 (Supplementary Fig. 6a,b). Improved long-term cycling performance compared with Vulcan carbon is very evident (Fig. 3b). The Ti4O7/S-60 cell experienced good capacity retention over 250 cycles at C/2 with a fade rate as low as 0.08% per cycle, whereas the VC/S-60 cell faded at twice the rate, 0.16%. As noted above, the Ti4O7-S/70 cell exhibited the same performance as that of Ti4O7-S/60, with 88% capacity retention over 100 cycles at C/2 (Fig. 3c). At a rate of C/5, an initial capacity of 1,069 mAh g−1 was achieved with the same capacity retention. Figure 3d shows high-rate cycling, where an initial capacity of 850 mAh g−1 at 2C was attained for Ti4O7, with a fade rate of only 0.06% per cycle over 500 cycles. The sulphur/electrolyte ratio was maintained at ~1:30 (g ml−1) for both Ti4O7/S and VC/S cells. To probe the effectiveness of the chemical interaction on the suppression of the polysulphide shuttle, cells without LiNO3 additive in the electrolyte were also examined. A greatly improved average Coulombic efficiency (~96% versus 80% for VC/S-60) for Ti4O7/S-60 composite (Supplementary Fig. 6c,d) was observed, demonstrating the defining role of the interfacial interaction.
Operando XANES study on the Ti4O7/S electrode
Surface-mediated reduction of the sulphide species on Ti4O7 was further confirmed by an operando XANES study. This powerful tool has been previously used by us for monitoring sulphur speciation in Li-S cells31, and a significant theoretical understanding of the spectroscopic signatures has been recently reported40. Sulphur K-edge spectra collected throughout discharge and charge of a Ti4O7/S electrode were fitted with a linear combination of α-S8, Li2S6, Li2S4 and Li2S and compared with a VC/S electrode. In order to necessarily avoid self-absorption in the XANES experiments31 and also to preferentially probe the sulphur host interface, both working electrodes were prepared with a low sulphur weight fraction (see details in Supplementary Fig. 7). The contributions of the species at various states of discharge are shown in Fig. 4, with Li2S6 and Li2S4 summed as LiPS for clarity. Compared with a hydrophobic carbon host, the fraction of LiPS intermediates is significantly lessened at all states of discharge (reaching a max of 40% for Ti4O7 versus 87% for carbon, respectively), and Li2S precipitates much earlier and more progressively for Ti4O7. LiPSs chemically adsorbed on the Ti4O7 host are much more readily reduced to Li2S than in the case of carbon, as indicated by the reduced overpotential (Supplementary Fig. 7), strongly supporting a more efficient electron transfer from the oxide host to the electroactive mass owing to hydrophilic interactions19,21, and intimate contact, which leads to increased capacity and longevity.
Morphology of positive electrodes after cycling
The underlying reason for the stable capacity delivery was further explored by examining the positive electrode nanostructure evolution over cycling. Cycled cells stopped at different discharged/charged points were disassembled and examined by SEM. Figure 5a,d shows the images for the pristine Ti4O7/S-60 and VC/S-60 electrodes, respectively. On the first discharge, although an expanded layer of Li2S is evident on the surface in both cases, the underlying support is more defined for the Ti4O7 host (Fig. 5b,e), indicative of the conformal deposition of Li2S on the particle surface as highlighted by the white boxes (the result of better wetting). In contrast, the Li2S on carbon is broadly and non-specifically distributed (area encompassed by the dotted white line). This is in agreement with the XANES results that show the gradual deposition of Li2S on Ti4O7 (compared with its much more sudden precipitation on carbon, Fig. 4).
The function of a metallic oxide as a sulphur host is quite different from an insulating oxide such as TiO2 used as a coating to physically inhibit LiPS diffusion. It also stands in contrast to mesoporous TiO2, which functions as a polysulphide reservoir to bind LiPS22, or metal-organic frameworks that rely on porosity and acid–base interactions between the LiPS and the metal centre to constrain diffusion. In such oxides, LiPSs cannot engage in redox behaviour at the interface owing to their insulating nature. The metallic oxide, in contrast, triggers surface-mediated reduction of sulphur/oxidation of Li2S. This is illustrated in Fig. 6. On a typical carbon support (Fig. 6a), elemental sulphur undergoes reduction to form LiPSs that then dissolve into the electrolyte (as evident in Fig. 2b). Initial reduction is thought to give S82− that disproportionates in solution to elemental sulphur and S62− (refs 31, 38, 39). The soluble S62− can either undergo cleavage to form soluble, reducible S3−; or further reduce to S42− and ultimately precipitate Li2S; and/or reduce and disproportionate to form a higher order polysulphide and Li2S. These solution-mediated reactions are highly complex38,39. Nonetheless, data clearly show the high concentration or supersaturation of LiPS before the end of discharge (Fig. 4) that results in a broadly distributed deposition of Li2S with high interfacial impedance (Fig. 5e; Supplementary Fig. 8b). In the presence of a strong support interaction as witnessed for Ti4O7, however, our collective results show these processes are significantly affected (Fig. 6b). Not only is the concentration of LiPS in solution greatly diminished on discharge but also a slow, controlled deposition of Li2S is observed (Fig. 4). This is evidenced not only using XANES but also using the XPS, SEM and impedance data (see below). We ascribe this to the interface-mediated, spatially controlled reduction of the LiPS, where SEM suggests that a conformal coating is produced.
Electrochemical impedance (EIS) spectroscopy on the cycled electrodes lends additional support to the concept of surface-mediated reduction of sulphur (Supplementary Table 2). These studies provide measure of the charge-transfer resistance at the positive (or negative) electrode interface resulting from deposition of products on discharge and charge41. On the first discharge, the Ti4O7/S-60 cell exhibits a charge-transfer resistance in the high-intermediate frequency range (attributable to the positive electrode) that is twofold lower that of the VC/S-60 (Supplementary Figs 8a,b and 9). We ascribe this to the enhanced interaction of the LiPSs—and subsequently the Li2S—with Ti4O7, in full concert with the findings from SEM and XANES data. Thus, as expected, the nonspecific precipitation of Li2S on the carbon-based electrode gives rise to higher resistance, whereas charge transfer at the ionic Li2S–Ti4O7 interface is more efficient. After the fifth charge or discharge, the Ti4O7/S-60-positive electrode also exhibited a very similar morphology to the pristine electrode, that is, sulphur (on charge) or Li2S (on discharge) was re-deposited on the Ti4O7 support uniformly (Supplementary Fig. 10a,b). In accord, EIS spectra at both discharge and charge for Ti4O7/S-60 over 50 cycles show negligible change (Supplementary Fig. 8c,d).
Even after 500 cycles at C/2, SEM images of the cathodes show that the original morphology of the electrode structure is better preserved on charge for Ti4O7/S-60 (Fig. 5c) than in the VC/S-60-positive electrode (Fig. 5f). In the latter case, this could arise from residual unoxidized Li2S, as it has been shown that Li2S particles easily detach from carbon electrode surfaces leading to loss in electrical contact21. Conversely, for Ti4O7/S, the maintenance of nanostructure integrity along with the minimal variation in the charge-transfer resistance on cycling demonstrate strong interaction between the host and the (poly)sulphide species. Our results suggest that this allows for their reversible, homogeneous deposition to Li2S (and its subsequent oxidation) and accounts for the observed enhanced cell longevity. Cell charging to form elemental sulphur is also assisted by the presence of hydrophobic carbon in the composite.
In summary, we have demonstrated a new class of inorganic sulphur host materials that combine electronic conductivity for redox electron transfer with a polar surface for strong LiPSs/Li2S binding, which provide a bifunctional positive electrode material for Li-S batteries that enables low capacity fade rates to be sustained. At sulphur fractions comparable to those of mesoporous carbons, electrodes show better cycling stability. This indicates that surface interactions play a larger role in containing sulphide dissolution and deposition than mesoporous confinement that relies on physical barriers. Particularly important in directing gradual reduction to Li2S, and enhancing redox electron transfer, this is even more important for lithium sulphide than for sulphur (which is partly soluble), to reduce interfacial impedance. When the sulphur/sulphide host is both sulphiphilic and metallic, redox is further facilitated. The concept extends not only to the other members of the Magnéli phase family but is also widely applicable to conductive materials with intrinsic polar character, as we will show in subsequent reports. This opens the path to a departure from traditional cathode design for Li-S cells based on functionalized carbons and should inspire further studies on the nature of the sulphide–support interaction. These will be particularly important for catholyte cells that will benefit from spatially controlled precipitation of sulphides and lowered charge potentials on charge.
Synthesis of Ti4O7 and related sulphur composites
In a typical synthesis, titanium(IV) ethoxide (Sigma-Aldrich) and polyethylene glycol (Mw~400, Sigma-Aldrich) were mixed in the desired weight ratio followed by addition of ethanol to control the viscosity. The solution was then stirred at 60–80 °C for overnight to form an amber yellow gel. This gel was further heated at 100 °C for 4–6 h and then fired at ~950 °C under an Ar stream in a tubular furnace using a heating ramp of 4 °C min−1. A black powder product was obtained. Ti4O7/S-60 (and Ti4O7/S-70) were prepared with either 60 or 70 wt% percent sulphur, respectively, via a well-established melt-diffusion method at 155 °C. For comparison, the VC/S-60 composite was similarly prepared from VULCAN XC72 carbon (Cabot Corporation, denoted as VC) with a surface area of 260 m2 g−1.
Synthesis of lithium and sodium polysulphides for XPS
Solid Li2S4 was synthesized by reacting elemental sulphur and lithium superhydride (LiEt3BH) in the desired ratio in anhydrous THF at room temperature for 1 h inside an Ar-filled glovebox. The THF was removed in vacuo and the precipitate was washed with toluene and vacuum dried, as reported previously31. Na2S2 and Na2S4 as reference materials for XPS were prepared by reacting sodium sulphide nonahydrate with elemental sulphur in the desired ratios in absolute ethanol under an N2 flow. The mixture was refluxed for 1 h and then cooled down at room temperature for overnight. The powder was dried in vacuo and further heated at 80 °C for 2 h.
Polysulphide adsorption study and XPS sample preparation
Three Li2S4 solutions were prepared by dissolving 4 mg of Li2S4 in 5 ml of THF in each case. Graphite (Alfa Aesar), VULCAN XC72 carbon (Cabot Corporation) and mesoporous Ti4O7 were added to each solution. The mass added was adjusted so the total surface areas of the solids based on Brunauer–Emmett–Teller measurements were the same (5.8 m2) for each. For example, for Ti4O7 with a surface area of 290 m2 g−1, 20 mg were added. To inspect the solution colour, in the first step, immediately upon stirring, the suspensions were allowed to settle for a few minutes. For the second step, the solutions were further stirred for 1 h. Afterwards, the suspensions were centrifuged and the solids for XPS analysis were obtained after drying in vacuo for 5 h. All procedures were completed in an Ar-filled glovebox.
Sulphur composites (Ti4O7/S or VC/S) with Super P and Kynar Powerflex binder at a weight ratio of 8:1:1 were dispersed in dimethylformamide to form a thin slurry that was drop-cast on carbon paper with an area of 2 cm2 (AvCarb P50, Fuel Cell Store) to prepare the positive electrodes. The electrodes were dried at 60 °C overnight before use. Coin cells were assembled inside the glovebox with lithium foil as anode and an electrolyte consisting of 1 M bis(trifluoromethanesulfonyl)imide lithium and 2 wt% of LiNO3 in a mixed solvent of 1,2-dimethoxyethane and 1,3-dioxolane (v/v=1:1; BASF). The typical sulphur loading was 1.5–1.8 mg per electrode, with an electrolyte volume of 50 μl in all cases. The cells were galvanostatically cycled between 1.8 and 3.0 V at different C rates (1C=1,675 mA g−1) using a BT2000 battery cycler (Arbin Instruments). A voltage window of 1.9–3.0 V was used for cycling at C/20 and 1.7–3.0 V for 2C. EIS measurements were carried out on a VMP3 potentiostat/galvanostat station with EIS/Z capabilities (Bio-Logic Science Instruments). The DC voltage was kept at open-circuit voltage and an AC voltage of 5 mV in amplitude was applied with a frequency of 200 kHz–20 mHz.
XANES measurements were carried out at the sector 13-ID-E at the Argonne National Laboratory using a Si(111) crystal monochromator under helium flow and the data were collected in fluorescence mode using a four-element vortex detector. The cell used to perform operando XANES was adapted from the 2,325 coin cell as described in ref. 31. In order to both avoid self-absorption and preferentially probe the sulphur host interface, the working electrodes were made of Ti4O7/S-6 wt% or VC/S-6 wt%, Super P carbon and polyvinylidene difluoride (1.6 wt% sulphur overall) and were cycled against a LiNO3-protected Li-negative electrode in 1 M LiClO4, DME:DOL (1:1) electrolyte at a rate of C/5. The experimental spectra acquired operando were compared with a set of reference materials including α-S8, Li2S6, Li2S4 and Li2S31. Since the standards represent the sulphur species successively formed by electrochemistry, operando spectra can be described with a linear combination fitting31, as shown in Fig. 4 and Supplementary Fig. 7.
Preparation of cycled electrode samples for SEM imaging
Positive electrodes (Ti4O7/S-60 and VC/S-60) were retrieved after a specified number of cycles at either a charged or discharged status by dissembling the cells in the glovebox. Electrodes were washed with acetonitrile twice to remove dissolved lithium polysulphides and lithium salt on the surface, followed by drying in vacuo for 30 min. Dried electrodes were then transferred to the SEM chamber under an Ar atmosphere for imaging.
Elemental microanalysis on the as-synthesized Ti4O7 material was conducted on a Carlo Erba elemental analyzer (CHNS-O EA1108, Italy) coupled to a Deltaplus continuous flow stable isotope ratio mass spectrometer (Thermo Finnigan, Bremen, Germany). The X-ray diffraction pattern was collected on a Bruker D8-Advance powder X-ray diffractometer, operating at 40 kV/30 mA and using Cu-Kα radiation (λ=0.15405, nm). The SEM imaging and EDX elemental mapping were performed using a LEO 1530 field emission SEM equipped with an EDX attachment (Zeiss). The TEM samples were imaged on JEOL 2010F TEM/STEM operating at 200 KeV. N2 adsorption/desorption isotherms were obtained using a Quantachrome Autosorb-1 system at 77 K. Surface areas were calculated using the Brunauer–Emmett–Teller method based on a multipoint analysis. Ti4O7, VC and graphite were degassed at 180 °C before measurement. Thermogravimetric analysis was conducted using a TA Instruments SDT Q600 under a N2 flow at a heating rate of 10 °C min−1. Electronic conductivity was measured using a Jandel four-point probe connected to an RM3000 test unit. The Ti4O7 powder was pressed into a pellet and sintered at 800 °C under Ar for 12 h before measurement. Different spots and currents were used to obtain an average conductivity value. XPS analysis was performed on a Thermo ESCALAB 250 instrument configured with a monochromatic Al Kα (1,486.6 eV) for conductive composite materials and non-monochromatic Al Kα (from a twin anode) for non-conductive materials (Na2Sx, Li2S4 and S8). The air-sensitive samples were transported to the spectrometer under an Ar atmosphere and transferred into the chamber anaerobically. All spectra were fitted with Gaussian–Lorentzian functions and a Shirley-type background using the CasaXPS software. For S 2p spectra, three constraints were used on the fitting for 2p3/2 and 2p1/2 doublets: (a) a peak position difference of 1.18 eV between them, (b) a peak area ratio of 2:1 for 2p3/2: 2p1/2 and (c) equal full-width half maximum. For the Ti 2p spectrum, a peak position difference of 5.7 eV was used. The binding energy values were all calibrated using the C 1s peak at 285.0 eV.
How to cite this article: Pang, Q. et al. Surface-enhanced redox chemistry of polysulphides on a metallic and polar host for lithium-sulphur batteries. Nat. Commun. 5:4759 doi: 10.1038/ncomms5759 (2014).
Goodenough, J. B. & Park, K.-S. The Li-ion rechargeable battery: a perspective. J. Am. Chem. Soc. 135, 1167–1176 (2013).
Choi, N.-S. et al. Challenges facing lithium batteries and electrical double-layer capacitors. Angew. Chem. Int. Ed. 51, 9994–10024 (2012).
Manthiram, A., Fu, Y. & Su, Y.-S. Challenges and prospects of lithium–sulfur batteries. Acc. Chem. Res. 46, 1125–1134 (2012).
Evers, S. & Nazar, L. F. New approaches for high energy density lithium–sulfur battery cathodes. Acc. Chem. Res. 46, 1135–1143 (2012).
Bresser, D., Passerini, S. & Scrosati, B. Recent progress and remaining challenges in sulfur-based lithium secondary batteries - a review. Chem. Commun. 49, 10545–10562 (2013).
Elazari, R. et al. Morphological and structural studies of composite sulfur electrodes upon cycling by HRTEM, AFM and Raman spectroscopy. J. Electrochem. Soc. 157, A1131–A1138 (2010).
Fu, Y., Su, Y.-S. & Manthiram, A. Highly reversible lithium/dissolved polysulfide batteries with carbon nanotube electrodes. Angew. Chem. Int. Ed. 52, 6930–6935 (2013).
Lin, Z., Liu, Z., Dudney, N. J. & Liang, C. Lithium superionic sulfide cathode for all-solid lithium–sulfur batteries. ACS Nano 7, 2829–2833 (2013).
Hassoun, J. & Scrosati, B. Moving to a solid-state configuration: a valid approach to making lithium-sulfur batteries viable for practical applications. Adv. Mater. 22, 5198–5201 (2010).
Nagao, M., Hayashi, A. & Tatsumisago, M. High-capacity Li2S–nanocarbon composite electrode for all-solid-state rechargeable lithium batteries. J. Mater. Chem. 22, 10015–10020 (2012).
Lin, Z., Liu, Z., Fu, W., Dudney, N. J. & Liang, C. Lithium polysulfidophosphates: a family of lithium-conducting sulfur-rich compounds for lithium-sulfur batteries. Angew. Chem. Int. Ed. 52, 7460–7463 (2013).
Ji, X., Lee, K. T. & Nazar, L. F. A highly ordered nanostructured carbon-sulphur cathode for lithium-sulphur batteries. Nat. Mater. 8, 500–506 (2009).
Jayaprakash, N., Shen, J., Moganty, S. S., Corona, A. & Archer, L. A. Porous hollow carbon@sulfur composites for high-power lithium-sulfur batteries. Angew. Chem. Int. Ed. 50, 5904–5908 (2011).
He, G. et al. Tailoring porosity in carbon nanospheres for lithium–sulfur battery cathodes. ACS Nano 7, 10920–10930 (2013).
Evers, S. & Nazar, L. F. Graphene-enveloped sulfur in a one pot reaction: a cathode with good Coulombic efficiency and high practical sulfur content. Chem. Commun. 48, 1233–1235 (2012).
Wang, H. L. et al. Graphene-wrapped sulfur particles as a rechargeable lithium-sulfur battery cathode material with high capacity and cycling stability. Nano Lett. 11, 2644–2647 (2011).
Xiao, L. et al. A soft approach to encapsulate sulfur: polyaniline nanotubes for lithium-sulfur batteries with long cycle life. Adv. Mater. 24, 1176–1181 (2012).
Su, Y.-S. & Manthiram, A. Lithium–sulphur batteries with a microporous carbon paper as a bifunctional interlayer. Nat. Commun. 3, 1166 (2012).
Ji, L. et al. Graphene oxide as a sulfur iImmobilizer in high performance lithium/sulfur cells. J. Am. Chem. Soc. 133, 18522–18525 (2011).
Song, M. K., Zhang, Y. & Cairns, E. A long-life, high-rate lithium-sulfur cell: a multifaceted approach to enhancing cell performance. Nano Lett. 13, 5891 (2013).
Zheng, G. et al. Amphiphilic surface modification of hollow carbon nanofibers for improved cycle life of lithium sulfur batteries. Nano Lett. 13, 1265–1270 (2013).
Ji, X., Evers, S., Black, R. & Nazar, L. F. Stabilizing lithium–sulphur cathodes using polysulphide reservoirs. Nat. Commun. 2, 325 (2011).
Evers, S., Yim, T. & Nazar, L. F. Understanding the nature of absorption/adsorption in Nnanoporous polysulfide sorbents for the Li–S battery. J. Phys. Chem. C 116, 19653–19658 (2012).
Wei Seh, Z. et al. Sulphur-TiO2 yolk-shell nanoarchitecture with internal void space for long-cycle lithium-sulphur batteries. Nat. Commun. 4, 1331 (2013).
Kim, H. et al. Plasma-enhanced atomic layer deposition of ultrathin oxide coatings for stabilized lithium-sulfur batteries. Adv. Energy Mater. 3, 1308–1315 (2013).
Demir-Cakan, R. et al. Cathode composites for Li-S batteries via the use of oxygenated porous architectures. J. Am. Chem. Soc. 133, 16154–16160 (2011).
Zheng, J. et al. Lewis acid-base interactions between polysulfides and metal organic framework in lithium sulfur batteries. Nano Lett. 14, 2345–2352 (2014).
Smith, J. R., Walsh, F. C. & Clarke, R. L. Electrodes based on Magnéli phase titanium oxides: the properties and applications of Ebonex materials. J. Appl. Electrochem. 28, 1021–1033 (1998).
Yao, C., Li, F., Li, X. & Xia, D. Fiber-like nanostructured Ti4O7 used as durable fuel cell catalyst support in oxygen reduction catalysis. J. Mater. Chem. 22, 16560–16565 (2012).
Ioroi, T. et al. Stability of corrosion-resistant Magnéli-phase Ti4O7-supported PEMFC catalysts at high potentials. J. Electrochem. Soc. 155, B321–B326 (2008).
Cuisinier, M. et al. Sulfur Speciation in Li–S batteries determined by operando X-ray absorption spectroscopy. J. Phys. Chem. Lett. 4, 3227–3232 (2013).
Kartio, I. J., Basilio, C. I. & Yoon, R. H. An XPS study of sphalerite activation by copper. Langmuir 14, 5274–5278 (1998).
Zhou, G. et al. Fibrous hybrid of graphene and sulfur nanocrystals for high-performance lithium–sulfur batteries. ACS Nano 7, 5367–5375 (2013).
Wagemaker, M. & Mulder, F. M. Properties and promises of nanosized insertion materials for Li-Ion batteries. Acc. Chem. Res. 46, 1206–1215 (2012).
Baltrusaitis, J., Jayaweera, P. M. & Grassian, V. H. XPS study of nitrogen dioxide adsorption on metal oxide particle surfaces under different environmental conditions. Phys. Chem. Chem. Phys. 11, 8295–8305 (2009).
Moulder, J. F., Stickle, W. F. S. & Bomben, K. D. Handbook of X-ray Photoelectron Spectroscopy Perkin-Elmer Corporation (1992).
Park, M.-S. et al. One-step synthesis of a sulfur-impregnated graphene cathode for lithium-sulfur batteries. Phys. Chem. Chem. Phys. 14, 6796–6804 (2012).
Chivers, T. & Elder, P. J. W. Ubiquitous trisulfur radical anion: fundamentals and applications in materials science, electrochemistry, analytical chemistry and geochemistry. Chem. Soc. Rev. 42, 5996–6005 (2013).
Lu, Y. C., He, Q. & Gasteiger, H. Probing the lithium-sulfur redox reactions: A Rotating Ring Disk Electrode Study. J. Phys. Chem. C 118, 5733–5741 (2014).
Pascal, T. A. et al. X-ray absorption spectra of dissolved polysulfides in lithium–sulfur batteries from first-principles. J. Phys. Chem. Lett. 5, 1547–1551 (2014).
Deng, Z. et al. Electrochemical impedance spectroscopy study of a lithium/sulfur battery: modeling and analysis of capacity fading. J. Electrochem. Soc. 160, A553–A558 (2013).
We thank NRCan for financial support through their EcoEII programme. D.K. acknowledges partial support of research as part of the Joint Center for Energy Storage Research, an Energy Innovation Hub funded by the US Department of Energy, Office of Science, Basic Energy Sciences and M.C. received support from the BASF International Scientific Network for Electrochemistry and Batteries. Use of the Advanced Photon Source was supported by the US DOE, Office of Science, Office of Basic Energy Sciences, under contract DE-AC02-06CH11357. We thank Dr Mahalingam Balasubramanian, Dr Antonio Lanzirotti and Dr Matthew Newville for help with acquisition of the XANES.
The authors declare no competing financial interests.
About this article
Cite this article
Pang, Q., Kundu, D., Cuisinier, M. et al. Surface-enhanced redox chemistry of polysulphides on a metallic and polar host for lithium-sulphur batteries. Nat Commun 5, 4759 (2014). https://doi.org/10.1038/ncomms5759
Nature Communications (2021)
Nano-Micro Letters (2021)
Novel NiCo2O4 nanofibers prepared via electrospinning method as host materials for perfect polysulfide inhibition
New insights into the relationship between capacity fading and sulfur loading and electrolyte/sulfur ratio obtained from Li–S pouch cell
The composite of Ketjen black and Ti4O7-modified separator for enhancing the electrochemical properties of lithium sulfur battery