Abstract
Engineering domains in ferroelectric thin films is crucial for realizing technological applications including non-volatile data storage and solar energy harvesting. Size and shape of domains strongly depend on the electrical and mechanical boundary conditions. Here we report the origin of nonswitchable polarization under external bias that leads to energetically unfavourable head-to-head domain walls in as-grown epitaxial PbZr0.2Ti0.8O3 thin films. By mapping electrostatic potentials and electric fields using off-axis electron holography and electron-beam-induced current with in situ electrical biasing in a transmission electron microscope, we show that electronic band bending across film/substrate interfaces locks local polarization direction and further produces unidirectional biasing fields, inducing nonswitchable domains near the interface. Presence of oxygen vacancies near the film surface, as revealed by electron-energy loss spectroscopy, stabilizes the charged domain walls. The formation of charged domain walls and nonswitchable domains reported in this study can be an origin for imprint and retention loss in ferroelectric thin films.
Similar content being viewed by others
Introduction
One method of realizing a non-volatile logic element1 is to use a ferroelectric material to induce a charge-mediated change of state in an adjacent material. A ferroelectric has a spontaneous electrical polarization that is switchable upon the application of a DC voltage2,3. However, a major issue for commercialization has been the poor reliability of ferroelectric memory devices including a decrease in polarization with repeated switching (fatigue), polarization backswitching leading to loss of data (retention loss) and preferential polarization state (imprint)3,4,5,6,7. Ground-state domain structures and switching processes in ferroelectric thin films are difficult to predict because of the importance of electrical and mechanical boundary conditions present at the film interfaces8. The primary mechanical boundary condition for an epitaxial thin film is the strain that results from the lattice mismatch between the film and substrate8,9,10,11. Electrical boundary conditions can dramatically influence ground-state domain structures and switching via polarization charge compensation mechanisms at the interfaces12,13, the formation of 180° stripe domains14, flux-closure domain structures15,16 and interfacial reconstructions17. Mobile charge carriers arising from vacancies and impurities also play an important role by internally compensating the polarization charges or by modifying the electric field within the ferroelectric in response to an external bias17,18,19,20. In addition, achieving chemical potential equilibrium between ferroelectric thin films and electrode materials can cause the accumulation or depletion of mobile charge carriers, thereby leading to built-in potentials at the interfaces18,19,21.
The macroscopic ferroelectric domain structures and their switching properties can be understood by directly visualizing domains during switching and characterizing the electrostatic potentials. Here, we report the unusual formation of charged 180° domain walls in head-to-head configuration in ferroelectric epitaxial thin films observed by dark-field transmission electron microscopy (TEM) combined with in situ electrical biasing22,23,24,25,26. Electrostatic potential and electric field distributions within ferroelectric films under external biases were, for the first time in our knowledge, mapped out using two techniques: off-axis electron holography27 and electron-beam-induced current (EBIC) measurement28. We found that electronic band bending across the film/substrate interfaces pins the local polarization direction and produces unidirectional biasing fields, inhibiting local domain switching and leading to formation of charged 180° domain walls in an unstable head-to-head configuration. Surprisingly, these positively charged domain walls were found to be stable over several months. Our electron-energy loss spectroscopy data revealed higher concentration of oxygen vacancies near the film surface, which implies internal charge compensation by mobile charge carriers.
Results
Characterization of domain structures
Epitaxial PbZr0.2Ti0.8O3 (001) (PZT) thin films were grown on 0.5 wt.% Nb-doped SrTiO3 (001) (Nb-STO) by off-axis radiofrequency magnetron sputtering at 515 °C and cooled to room temperature in 225 mTorr of process gases. To facilitate in situ electrical biasing of the PZT films, a capacitor geometry with conventional Pt electrodes is fabricated using focused-ion beam (FIB) after Au sputtering, as shown in Fig. 1a (ref. 27). A probe electrical contact in the TEM holder (Nanofactory Instruments AB) is made to the top electrode in situ in TEM, while the counter electrode is connected to the conducting Nb-STO substrate using silver paste. To maximize contrast associated with 180° ferroelectric domains because of violation of Friedel’s law29,30, samples were tilted from the [010] zone axis for a two-beam condition and dark-field images were obtained with series of external biases (Figs 1a and 2a–e). Owing to ~1.2% biaxial compressive strain, the PZT thin films consist primarily of domains with out-of-plane polarization31, although they are likely fully relaxed because of the presence of misfit dislocations near the interface. The c domains in as-grown PZT thin films have the polarization direction, either upwards or downwards, which are henceforth referred to as Pup or Pdown domains, respectively. Conventionally, stripe patterns with alternating polarization direction have been predicted theoretically as a ground domain structure and experimentally observed for ferroelectric thin films1. However, we observed the domain structure in as-grown PZT film shown in Fig. 1c showing surprisingly two domains with opposite polarizations met in the middle of a film in a head-to-head configuration. Previously, occurrence of charged domain walls, especially during polarization-switching process, has been reported from various in situ switching experiments22,23,24,32. However, the head-to-head domain structure observed in the as-grown PZT thin films is remarkable as such domain walls are positively charged and thus energetically unfavourable for a ground state. Furthermore, domain walls are not flat, but rather zigzag in shape, with an additional energy cost associated with this configuration. The zigzag-like domain walls can be a consequence of domain wall pinning at structural defects within the film33. Piezoresponse force microscopy (PFM) result (Fig. 1d) also supports the presence of charged domain walls embedded in PZT thin films showing an intermediate piezoresponse signal for an as-grown region compared with two oppositely poled regions with ±10 V. Note that stripe domains with alternating 180° domains can be ruled out by the monotonous contrast in the PFM image. A typical current–voltage (I–V) curve (Fig. 1b) taken from the TEM sample in Fig. 1a shows a rectifying property of Au top electrode/PZT/Nb-STO structure. Similar electric transport properties have been reported for PZT films grown on Nb-STO substrates, attributed to pn junction-like band bending at the film/substrate interface34. We notice two paths of leakage currents for TEM samples prepared by FIB milling. The first contribution is from mobile charge carriers in ferroelectric films because of vacancies and impurities serving as dopants and defect-mediated conduction such as Frenkel-Poole conduction considering large concentration of structural defects associated with strain relaxation3. The second is from FIB-milling-induced damages on the top and bottom surfaces of cross-sectioned TEM samples27. The latter can be minimized by careful FIB milling with low-energy Ga+ ions. These leakage currents can be approximated as a linear resistor connected in parallel to the ferroelectric films. However, the clear rectifying behaviour shown in Fig. 1b suggests that charge transport is not controlled by the leakage. We also point out that illuminating the PZT/Nb-STO interface with the TEM electron beam generates excess charge carriers and thus increases conductivity of the film similar to optical excitations. With illumination of 200 kV electron beam at a beam current of ~1 nA, additional currents are measured for both positive and negative biases, as shown in Fig. 1b. A small open-circuit voltage (VOC) of −0.4 eV is measured under electron beam illumination, as shown in the inset of Fig. 1b.
In situ domain switching
The domain evolution under various external biases using dark-field TEM imaging combined with in situ electrical biasing is summarized in Fig. 2. Upon application of positive bias, Pup domains (dark region) grow towards the top interface. With 3-V bias, some Pup domains reached the top electrode but significant areas near the top electrode are left unswitched, indicating that domain switching is highly inhomogeneous, possibly because of random domain wall pinning by structural defects. Under a negative applied bias, Pdown domains (bright region) grow towards the bottom interface. However, in this case, no Pdown domain reaches the bottom interface, resulting in the formation of charged 180o domain walls in the film. Application of negative bias up to −15 V (not shown here) does not result in domain switching beyond that shown in Fig. 2e. It can be concluded that switching behaviour observed in Fig. 2 is highly asymmetric (Pup domain is preferred) and Pup domain near the bottom interface is not switchable. A P-E loop obtained from PZT thin films also shows an asymmetric switching, as shown in Fig. 2f. Here the electric fields are estimated with the PZT film thickness of 150 nm. The remnant polarizations are about 80 and 50 μC cm−2 for Pup and Pdown domains, respectively. We find that this P-E loop agrees well with the TEM observations in Fig. 2a–e. The negative switching current sharply peaked near −0.2 MV cm−1 agrees with rapid switching at −4 V (Fig. 2d) followed by almost no additional switching with −10 V (Fig. 2e). For the positive switching, a dramatic switching occurs between 0 and 3 V (Fig. 2b) and switching continues between 3 V (Fig. 2b) and 10 V (Fig. 2c) without completing switching, implying that the coercive field for Pup switching is not sharply defined but rather broadly ranged around 10 V (~0.67 MV cm−1), in agreement with the P-E loop.
To ensure that the contrasts observed in dark-field TEM images are indeed 180o head-to-head domains, we obtained atomic resolution high-angle annular dark-field (HAADF) scanning TEM (STEM) images after further thinning the TEM sample using low-energy (900 eV) Ar-ion milling. As shown in Fig. 2g, a triangular domain is clearly visible and the Ti/Zr columns are displaced in the opposite direction along the c axis across the domain wall. For Ti-rich PZT thin films, the polarization direction is antiparallel with the Ti/Zr displacement direction with respect to the Pb latttice13,16. We attribute the development of triangular domain shapes to anisotropy of domain growth3. Considering two components of domain wall speed for a given electric field, va and vc, along the a axis and c axis, respectively, we estimate that νc is approximately two to three times faster than νa based on the domain shapes in Fig. 2. It should be noted that both domain wall pinning by defects and anisotropic domain growth can be ruled out as an origin for the asymmetric domain switching and nonswitchable Pup domains near the bottom interface. Especially, domain wall pinning can be easily overcome by applying a larger field. Recently, Gao et al.24 reported that the pinning force of misfit dislocations on domain wall motion is rather weak and slows down domain wall speed slightly. The domain wall pinning at defects plays some important roles in domain switching. However, the focus of this study is on the origins of the asymmetric switching and the nonswitchable Pup domains near the PZT/Nb-STO interface.
Electric field mapping
In order to understand the origin of the nonswitchable interface polarization, we have mapped out electrostatic potentials and electric field distributions in PZT thin films under biased conditions using two different techniques: off-axis electron holography (Fig. 3) and EBIC measurements (Fig. 4). Electrostatic potential distributions were determined via electron-wave phase retrieval with various external biases, as shown in Fig. 3a–c. Electric potentials in the Nb-STO substrate increases with +15 V compared with that in PZT film and vice versa for −15 V, clearly showing local potential changes because of application of external biases. However, any potential changes associated with the charged domain walls or depolarization field within domain are not detected in the unbiased (0 V) phase map (Fig. 3a), possibly because of effective compensation of the polarization charges at domain walls by mobile charge carriers or insufficient phase sensitivity of electron holography. In addition, no significant built-in potential across the PZT/Nb-STO interface is observed in the reconstructed phase image under 0 V biasing. In our experiment, to avoid diffraction contrast related with dynamic variation of external biases resulted from the converse piezoelectric effect and non-uniform sample thickness, we extract the changes in electrostatic potential distributions solely caused by external biases by taking differences between the phase shifts obtained under external bias conditions and that under 0 V (see Methods section). The line profiles in Fig. 3d show a considerable deviation from a linear potential distribution that one would expect for a pure dielectric assumption where no mobile charge carriers are considered. Especially, a noticeable potential barrier develops at the PZT/Nb-STO interface and increases as the positive bias applied to Nb-STO is increased. In addition, distribution of electric fields along the c axis (Fig. 3e), obtained by taking the first derivative of potential line profiles (Fig. 3d), shows that the electric fields are concentrated near the PZT/Nb-STO interface under positive biases. Here the positive sign of the electric field points from the bottom electrode to the top electrode. When negative biases are applied to Nb-STO, nearly no potential barriers and potential slopes are found at the PZT/Nb-STO interface (blue lines in Fig. 3e). This unidirectional bias field near the PZT/Nb-STO interface can yield only Pup domains, not Pdown domains, because applying negative bias to the substrate generates insufficient fields to initiate domain switching from Pup to Pdown. As a consequence, Pup domains near the PZT/Nb-STO interface are unswitchable, in agreement with domain switching behaviour observed in Fig. 2.
We also measured EBIC signals under various external biases to further investigate electric field distributions. Total electric currents flowing through the sample have been collected as an analogue signal for each electron-beam position during electron beam scanning with dwell time of 32 μs during the STEM-HAADF image acquisition, as shown in Fig. 4a. When a 200-keV-electron beam passes through the sample, it excites core level and valence electrons to conduction bands (CBs), generating electron–hole pairs (ehps). In the absence of electric field, these ehps diffuse out before they eventually recombine, yielding no net current. However, nonzero local electric fields can separate these ehps, generating an additional current (IEBIC). Since ehp separation occurs more effectively under higher electric fields, IEBIC is proportional to local electric field intensities smoothed by excess carrier diffusion. Previously, in the case of Si TEM samples, we have shown that the excess carrier diffusion length can be significantly reduced because of the enhanced surface recombinations28. We note that the EBIC signals collected with negative biases on Nb-STO were very noisy because of large forward currents flowing through the sample (Fig. 1b). Figure 4b–e shows a series of simultaneously acquired STEM-EBIC and STEM-HAADF images under various positive biases. Although EBIC images are noisy because of the dynamic scanning noise of the electron beam, we can clearly see a bright band developing near the PZT/Nb-STO interface with increasing positive applied biases. This bright band suggests that large electric fields are indeed induced at the heterojunction with positive biasing, agreeing with the electric fields mapped out by electron holography (Fig. 3e). Under zero bias, there is a small and broad EBIC signal near the interface suggesting nonzero electric field associated with the band bending across the interface. Interestingly, EBIC signals expand more rapidly in the Nb-STO side with increasing positive biases than in the PZT film. EBIC signals in PZT film are confined to ~40 nm near the interface and are independent of bias voltage. This behaviour is also observed in potential profiles (Fig. 3d) obtained by off-axis electron holography. We attribute this to the presence of a higher concentration of deep levels continuously distributed throughout the band gap of PZT film, especially near the heterojunction due to large amount of structural defects associated with the lattice mismatch at the interface. These deep levels are perhaps mostly acceptor-like and trap electrons. In addition, converse piezoelectric effect of the PZT film may induce additional polarization charges with increasing biases.
The observed nonlinear potential profiles (that is, inhomogeneous electric fields) and unidirectional bias fields, consistently observed by both off-axis electron holography and EBIC measurements, can be explained if we consider PZT and Nb-STO as wide band gap semiconductors that have electronic band bending across the heterojunction. According to the electron affinity rule, there is a type II band alignment across the PZT/Nb-STO heterojunction with 0.4 eV CB offset and 0.3 eV valence band offset35, as shown in Fig. 3f. The electron concentration in 0.5 wt% Nb-doped STO is ~2.2 × 1020cm−3, which pushes the Fermi level of Nb-STO close to the edge of the CB edge36. The PZT film behaves as a highly compensated semiconductor because of Pb and O vacancies, as well as deep levels associated with large amounts of structural defects because of the lattice mismatch37,38. In this work, we assume PZT is a p-type conductor with effective dopant concentration (Neff) of ~1020cm−3 considering acceptor-type deep levels and shallow doping levels39. Without considering local polarization charges, 1.9-V built-in potential is drawn for the heterojunction between PZT thin film and Nb-STO substrate, as shown in Fig. 3f. According to the heterojunction band alignment theory40, the potential drops (VPZT and VSTO) and depletion region widths (WPZT and WSTO) supported by each PZT and Nb-STO under thermal equilibrium and the depletion approximation can be determined as:
where Vbi is the built-in potential, εPZT and εSTO dielectric constants for PZT and Nb-STO, respectively, ND dopant concentration in Nb-STO, q electronic charge and V reverse bias. An estimate of each built-in potentials and depletion regions can be made if the dielectric constants of PZT and Nb-STO are known. Inserting εPZT=200ε0 (ref. 39) and εSTO=50 ε0 (ref. 41) into the above equations gives Vbi_PZT=0.67 V and Vbi_STO=1.23 V, and WPZT=12 nm and WSTO=6 nm, respectively, under zero bias. The charge neutrality condition is met by qWPZTNeff=qWSTOND ~19.2 μC cm−2.
The PZT/Nb-STO heterojunction is therefore expected to exhibit a rectifying property since positive bias or negative bias applied to Nb-STO will increase or decrease, respectively, the energy barrier for an electron injection from the Nb-STO. Under reverse (positive) bias, most of the applied voltage is drawn across the reverse-biased PZT/Nb-STO, while under forward (negative) bias, negligibly small voltage across the forward-biased PZT/Nb-STO, being consistent with electron holography (Fig. 3) and EBIC results (Fig. 4). Linear potential profiles near the top interface for both positive and negative biases in Fig. 3 suggest Ohmic-like behaviour of the top interface. This Ohmic behaviour can be attributed to high density of interface states due to extended exposure of PZT film surface to atmosphere after film deposition and room-temperature top electrode (Au) deposition. Conduction across the top electrode/PZT interface occurs through these interface states, not by band bending. As a consequence, electric transport is mainly governed by minority carrier (electron) injection across the PZT/Nb-STO interface, leading to a rectifying behaviour.
The polarization charge near the interface will influence the zero-bias band bending and the associated built-in potential. Conceptually, polarization charge can be treated as an equivalent to an external bias to induce the same amount of charge within the PZT film42. The presence of negative polarization charge of Pup domain near the PZT/Nb-STO interface can be considered as a forward biasing the heterojunction (negative bias to Nb-STO), inducing the same amount of charge as the spontaneous polarization (PS). Consequently, the negative polarization charge of the Pup domain counteracts total space charges on both sides of the heterojunction. The sum of total space charge densities stored in both depletion regions in the band diagram shown in Fig. 3f under zero bias is 38.4 μC cm−2, which is comparable to typical polarization charges reported for epitaxial PZT thin films. Another simple way to estimate influence of polarization charges on band bending is using the dielectric gap model39 that considers polarization charge as a sheet charge separated from the interface by a dielectric gap to give rise to a change in built-in potential, . Here ΔV is a change in built-in potential because of presence of polarization charge located from the heterojunction by a gap (d). Estimation of ΔV requires knowledge of exact values of PS, εPZT and d. For an epitaxial PZT film, it is reported that the band bending modulation because of polarization charge can be of the order of 0.71 eV43 using 150 as the PZT dielectric permittivity, 1 nm gap and 95 μC cm−2 of polarization charge. We note that the dielectric constant in the gap within the PZT film near the interface can be significantly lower than that of intrinsic PZT. This would significantly increase the band bending modulation. Interestingly, a dielectric permittivity of ~50 for the gap layer results in a flat band condition across the PZT/Nb-STO heterojunction (exactly cancelling out the built-in potential of 1.9 eV) if we assume 80 μC cm−2 polarization charge for PZT film and 1-nm dielectric gap. This ‘flat-band’ scenario (Fig. 3g) is supported by off-axis electron holography and EBIC data that show no measurable band bending or small IEBIC across the PZT/Nb-STO interface under zero-bias condition, as shown in Figs 3 and 4.
Origin of the charged domain wall formation
One scenario leading to the formation of head-to-head domain walls in as-grown PZT thin films is as follows. We assume that the PZT films were grown in the paraelectric phase because of the high deposition temperature of 515 °C. Owing to the band bending across the PZT/Nb-STO heterojunction, a built-in electric field pointing from Nb-STO to PZT will be induced within the depletion region. When the PZT film goes through the paraelectric–ferroelectric phase transition upon cooling, the Pup domain will be induced near the interface because its polarization direction is parallel to the built-in electric field within the PZT depletion region. However, near the surface of the PZT film depending on local chemistry and defect natures, opposite built-in electric field can be present. We investigated local Ti valence changes in the PZT thin films using electron-energy loss spectroscopy (EELS). Figure 5a shows a series of Ti-L edges from several positions in the PZT film as a function of distance from the top interface. A systematic trend, especially regarding the change of the Ti L2 peak intensities, is observed when comparing with the Ti L2 edge taken from 94 nm away from the top interface. The Ti L2 edge taken near the top interface (3 nm away from the surface) shows two main constituent peaks (t2g and eg) develop noticeable shoulders, as shown in the inset of Fig. 5a, in agreement with trends reported in the literature44. Using the Ti-L edge far from the surface (94 nm away) as a reference, we plotted the differences in Ti-L edges using a multiple least-square fitting (Fig. 5b). This shows a progressive transition in the relative Ti valence state towards the surface of the PZT film. Although the exact valence state of Ti at the surface is difficult to quantify, the subtle change of Ti valence suggests more conduction electrons near the surface of PZT film, implying the presence of oxygen vacancy in the PZT film. A higher concentration of oxygen vacancy near the surface of PZT film will generate a net electric field pointing from the surface to the film/substrate interface, inducing Pdown domains near the surface region of PZT, despite of the energy cost for the formation of head-to-head 180° domain walls. Mobile electrons from near-surface oxygen vacancies will migrate and accumulate around the charged domain walls for its stabilization via internal charge screening. Mokry et al.45 reported in their theoretical study that free charge compensation of bound charge can lead to a strong reduction in the pressure exerted on charged domain wall from an external electric field. This supports the scenario described here, of bound charge compensation by mobile charge carriers for their stabilization. A schematic for charge distributions and built-in electric fields in paraelectric phase of the PZT film is shown in Fig. 5c. This scenario is similar to a back-to-back Schottky diode model for metal–ferroelectric–metal structures39, where two opposite built-in electric fields pointing at each other are set from the top and bottom electrode interfaces.
Discussion
Our study reveals that the built-in electric fields associated with electronic band bending across the PZT/Nb-STO heterojunction and higher oxygen vacancy concentration near the surface of the PZT film induce Pup and Pdown domains, respectively, upon paraelectric–ferroelectric phase transition, which counteract each built-in electric field. The heterojunction behaves as a pn junction and produces unidirectional bias fields, prohibiting domain switching of Pup domains near the heterojunction. As a result, energetically unfavourable charged domain walls with head-to-head configuration are induced in the middle of PZT films during domain switching process initiated by external biasing. These charged domain walls are found to be stable because of internal charge compensation by mobile charge carriers in the PZT film. Our observation of nonswitchable Pup domains near the PZT/Nb-STO interface and formation of charged domain walls in the middle of the PZT film can be an origin of imprint (preferred Pup (Pdown) domains near the bottom (top) interface) and retention loss (possible backswitching near the top and bottom interfaces) in ferroelectric thin films. We also point out that the switchable diode effects have not been previously observed for PZT thin films42, in contrary to BiFeO3 (ref. 46). Our results imply that a nonswitchable Pup domain near the bottom interface can be the origin for the absence of band bending modulation by polarization charge in the PZT/Nb-STO system.
Methods
Thin film growth and characterization
Thin films of PZT are grown on 5 × 5 × 0.5 mm samples of 0.5 wt.% Nb-STO (001) obtained from Crystec. The films of PZT are grown using off-axis radiofrequency magnetron sputtering, under flowing Ar (33.7 sccm) and O2 (13.7 sccm), where sccm refers to the cubic centimetres per minute at standard temperature and pressure. The chamber pressure is maintained at 225 mTorr and the substrate temperature is 515 °C. The deposition rate is calibrated using X-ray reflectivity and is ~4.5 Å min−1. The samples are cooled in the process gases at a chamber pressure of 225 mTorr. The thickness of films analysed here are ~150 nm. X-ray diffraction scans (Supplementary Fig. 1) demonstrate the growth of high-quality single crystalline films of PZT. The (001) rocking curve (Supplementary Fig. 1c) has a full-width half maximum of 0.04°, the same as the Nb-STO substrate.
PFM
PFM was performed by writing squares with a DC bias voltage of ±10 V. Readout was performed with an AC-excitation voltage of 1 V, at a frequency far off resonance. P-E loop measurement was performed with an aixACCT ferroelectric tester on a PZT thin film sample using a pulsed positive up negative down measurement (150 nm PZT on Nb-STO (001)). The pulsed measurement facilitates subtraction of the leakage current, leaving only the switching current.
TEM
Final FIB milling for TEM sample preparation was carried out using 5 keV Ga+ ions to minimize ion-beam-induced damages. For STEM-HAADF, the sample was further milled with 900 eV Ar ions with ±10° incidence angles using Nanomill (Fischione Instruments Inc.). A JEOL 2100F Lorentz microscope was used for off-axis electron holography. A JEOL ARM 200CF equipped with a cold field-emission gun and double-spherical aberration correctors at the Brookhaven National Laboratory operated at 200 kV was used for STEM-HAADF. The collection angles for HAADF detectors were from 68 to 280 mrad. EBIC signals were acquired simultaneously with STEM-HAADF images with the preamplifier installed with holder controller provided by Nanofactory Instruments AB. EELS data were obtained with 0.1 eV/ch dispersion.
Data analysis of electron holograms
The electrostatic potential distributions across top electrode/PZT/Nb-STO under external biases were mapped out by off-axis electron holography. Phase shift φ(x)0V in imaging 200 keV electron wave measured using electron holography under zero external bias condition is quantitatively related to electrostatic potentials within the sample and local thickness t(x) in (nm) as the following;
where CE is a constant of 0.00729, rad V−1·nm for 200 keV electron beam, VMIP (x) the mean inner potential in (V) and Vbi (x) the built-in potential in (V). Here the x axis is taken along the c axis and no fringing fields outside TEM samples are assumed. VMIP (x) is the mean inner potential that the imaging electron would see in the crystal and differs for PZT film and Nb-STO substrate. If we neglect unit-cell volume changes under biased conditions because of converse piezoelectric effects of PZT thin films, then VMIP (x) can be treated as a constant. Vbi (x) is associated both with the depolarization fields because of uncompensated polarization charges in PZT thin films and the built-in electric fields across top and bottom interfaces because of electronic band bending to reach a electrochemical equilibrium. If we assume the full polarization charge compensation at the top interface, then Vbi (x) across the PZT film is mainly attributed to the electronic band bending across the PZT/Nb-STO heterojunction as a result of charge exchange considering the effects of polarization charge. We estimate that Vbi (x) at 0 V is small for Pup domain in PZT film from EBIC (Fig. 4) because the EBIC is proportional to charge collection volumes in the sample, that is, product of depletion region width and thickness of the sample. Thus, phase shift measured by electron holography at 0 V mainly shows the contribution due to the product of VMIP (x) and local thickness t(x). Under external biases, the term Vext (x) describes electrostatic potential distributions due to external biases on the Nb-STO substrate.
In a pure dielectric assumption where no mobile charge carriers are considered, application of external bias results in constant electric fields and thus linearly changing electrostatic potentials Vext (x) across PZT thin films. However, when there are mobile carriers in the PZT thin film and interface dipoles due to formation of PZT/Nb-STO heterojunction in an electrochemical equilibrium, electric fields due to external biases will be more concentrated around top or bottom interfaces due to corresponding electronic band bending. We extract the changes in electrostatic potential distributions solely caused by external biases (Vext (x)) by taking differences between the phase shifts obtained under external bias conditions and that under 0 V as the followings:
We estimated the local sample thickness t(x) in the reconstructed amplitude images from electron holograms47. The sample thickness is found to be linearly increasing towards the substrate (Supplementary Fig. 2). To calibrate thickness from amplitude images, we used 115 nm as the mean free path for inelastic scattering to find thickness profile in Nb-STO region48. The determined thickness profile was extended towards the PZT film to obtain whole thickness profile across PZT thin film/Nb-STO substrate to obtain the line profiles of Vext (x) using the equation (8).
Additional information
How to cite this article: Han, M.-G. et al. Interface-induced nonswitchable domains in ferroelectric thin films. Nat. Commun. 5:4693 doi: 10.1038/ncomms5693 (2014).
References
Catalan, G., Seidel, J., Ramesh, R. & Scott, J. Domain wall nanoelectronics. Rev. Mod. Phys. 84, 119–156 (2012).
Ahn, C. H., Triscone, J. M. & Mannhart, J. Electric field effect in correlated oxide systems. Nature 424, 1015–1018 (2003).
Dawber, M., Rabe, K. M. & Scott, J. F. Physics of thin-film ferroelectric oxides. Rev. Mod. Phys. 77, 1083–1130 (2005).
Setter, N. et al. Ferroelectric thin films: review of materials, properties, and applications. J. Appl. Phys. 100, 051606 (2006).
Warren, W. L. et al. Voltage shifts and imprint in ferroelectric capacitors. Appl. Phys. Lett. 67, 866–868 (1995).
Warren, W. L., Tuttle, B. A. & Dimos, D. Ferroelectric fatigue in perovskite oxides. Appl. Phys. Lett. 67, 1426–1428 (1995).
Damjanovic, D. Ferroelectric, dielectric and piezoelectric properties of ferroelectric thin films and ceramics. Rep. Prog. Phys. 61, 1267–1324 (1998).
Choi, K. J. et al. Enhancement of ferroelectricity in strained BaTiO3 thin films. Science 306, 1005–1009 (2004).
Ederer, C. & Spaldin, N. A. Effect of epitaxial strain on the spontaneous polarization of thin film ferroelectrics. Phys. Rev. Lett. 95, 257601 (2005).
Schlom, D. G. et al. Strain tuning of ferroelectric thin films. Annu. Rev. Mater. Res. 37, 589–626 (2007).
Pertsev, N. A., Zembilgotov, A. G. & Tagantsev, A. K. Effect of mechanical boundary conditions on phase diagrams of epitaxial ferroelectric thin films. Phys. Rev. Lett. 80, 1988–1991 (1998).
Gerra, G., Tagantsev, A. K., Setter, N. & Parlinski, K. Ionic polarizability of conductive metal oxides and critical thickness for ferroelectricity in BaTiO3 . Phys. Rev. Lett. 96, 107603 (2006).
Chisholm, M. F., Luo, W. D., Oxley, M. P., Pantelides, S. T. & Lee, H. N. Atomic-scale compensation phenomena at polar interfaces. Phys. Rev. Lett. 105, 197602 (2010).
Streiffer, S. K. et al. Observation of nanoscale 180 degrees stripe domains in ferroelectric PbTiO3 thin films. Phys. Rev. Lett. 89, 067601 (2002).
Nelson, C. T. et al. Spontaneous vortex nanodomain arrays at ferroelectric heterointerfaces. Nano Lett. 11, 828–834 (2011).
Jia, C. L., Urban, K. W., Alexe, M., Hesse, D. & Vrejoiu, I. Direct observation of continuous electric dipole rotation in flux-closure domains in ferroelectric Pb(Zr,Ti)O3 . Science 331, 1420–1423 (2011).
Xiao, Y., Shenoy, V. B. & Bhattacharya, K. Depletion layers and domain walls in semiconducting ferroelectric thin films. Phys. Rev. Lett. 95, 247603 (2005).
Zubko, P., Jung, D. J. & Scott, J. F. Space charge effects in ferroelectric thin films. J. Appl. Phys. 100, 114112 (2006).
Zhang, J., Tang, M. H. & He, J. Doping concentration and thickness effects in ferroelectric thin films. Appl. Phys. Lett. 96, 122905 (2010).
Gureev, M. Y., Tagantsev, A. K. & Setter, N. Head-to-head and tail-to-tail 180o domain walls in an isolated ferroelectric. Phys. Rev. B 83, 184104 (2011).
Balke, N. et al. Direct observation of capacitor switching using planar electrodes. Adv. Funct. Mater. 20, 3466–3475 (2010).
Nelson, C. T. et al. Domain dynamics during ferroelectric switching. Science 334, 968–971 (2011).
Chang, H. J. et al. Watching domains grow: in-situ studies of polarization switching by combined scanning probe and scanning transmission electron microscopy. J. Appl. Phys. 110, 052014 (2011).
Gao, P. et al. Revealing the role of defects in ferroelectric switching with atomic resolution. Nat. Commun. 2, 1–6 (2011).
Winkler, C. R., Damodaran, A. R., Karthik, J., Martin, L. W. & Taheri, M. L. Direct observation of ferroelectric domain switching in varying electric field regimes using in situ TEM. Micron 43, 1121–1126 (2012).
Han, M. G. et al. Ferroelectric switching dynamics of topological vortex domains in a hexagonal manganite. Adv. Mater. 25, 2415–2421 (2013).
Han, M. G., Smith, D. J. & McCartney, M. R. In situ electron holographic analysis of biased Si n(+)-p junctions. Appl. Phys. Lett. 92, 143502 (2008).
Han, M. G. et al. Direct measurement of electron beam induced currents in p-type silicon. Solid State Electron 54, 777–780 (2010).
Blank, H. & Amelinckx, S. Direct observation of ferroelectric domains in barium titanate by means of the electron microscope. Appl. Phys. Lett. 2, 140–142 (1963).
Tanaka, M. Acta Crystallogr. A A 31, 59 (1975).
Klein, L. J. et al. J. Vac. Sci. Technol. B 28, C5A20 (2010).
McQuaid, R. G. P., McMillen, M., Chang, L.-W., Gruverman, A. & Gregg, J. M. Domain wall propagation in meso- and nanoscale ferroelectrics. J. Phys. Condens. Matter 24, 024204 (2012).
Chu, M.-W. et al. Impact of misfit dislocations on the polarization instability of epitaxial nanostructured ferroelectric perovskites. Nat. Mater. 3, 87–90 (2004).
Pintilie, L., Pintilie, I., Vrejoiu, I. & Alexe, M. In2008 International Semiconductor Conference, CAS 2008 Proceedings 2, 295–298 (2008).
Robertson, J. Band offsets of wide-band-gap oxides and implications for future electronic devices. J. Vac. Sci. Technol. B 18, 1785–1791 (2000).
Watanabe, Y. & Okano, M. Photoresponse of Zener tunneling junctions of Pb(Ti,Zr)O3/SrTiO3 at low temperature. J. Appl. Phys. 94, 7187–7192 (2003).
Gerson, R. & Jaffe, H. Electrical condductivity in lead titanate zirconate ceramics. J. Phys. Chem. Solids 24, 979–984 (1963).
Pintilie, L., Vrejoiu, I., Le Rhun, G. & Alexe, M. Short-circuit photocurrent in epitaxial lead zirconate-titanate thin films. J. Appl. Phys. 101, 064109 (2007).
Pintilie, L. & Alexe, M. Metal-ferroelectric-metal heterostructures with Schottky contact: I. Influence of the ferroelectric properties. J. Appl. Phys. 98, 1242013 (2005).
Shur, M. Physics of Semiconductor Devices Prentice-Hall Inc. (1990).
Ruotolo, A., Lam, C. Y., Cheng, W. F., Wong, K. H. & Leung, C. W. High-quality all-oxide Schottky junctions fabricated on heavily doped Nb:SrTiO3 substrates. Phys. Rev. B 76, 075122 (2007).
Tayebi, N. et al. Tuning the built-in electric field in ferroelectric Pb(Zr0.2Ti0.8)O3 films for long-term stability of single-digit nanometer inverted domains. Nano Lett. 12, 5455–5463 (2012).
Hrib, L. M. et al. Electrode interface control of the Schottky diode-like behavior in epitaxial Pb(Zr0.2Ti0.8)O3 thin films: a critical analysis. J. Appl. Phys. 113, 214108 (2013).
Shao, Y., Maunders, C., Rossouw, D., Kolodiazhnyi, T. & Botton, G. A. Quantification of the Ti oxidation state in BaTi1−xNbxO3 compounds. Ultramicroscopy 110, 1014–1019 (2010).
Morky, P., Tagantsev, A. K. & Fousek, J. Pressure on charged domain walls and additional imprint mechanism in ferroelectrics. Phys. Rev. B 75, 094110 (2007).
Choi, T. et al. Switchable ferroelectric diode and photovoltaic effect in BiFeO3 . Science 324, 63 (2009).
McCartney, M. R. & Gajdardziskajosifovska, M. Absolute measurement of normalized thickness, T/λ(I), from off-axis electron holography. Ultramicroscopy 53, 283–289 (1994).
Egerton, R. F. Electron Energy-Loss Spectroscopy in the Electron Microscope Springer (1996).
Acknowledgements
R. Dunin-Borkowski and M. McCartney are acknowledged for their fruitful discussions on electron holography data. M. McCartney is also acknowledged for providing the Digital Micrograph script used in reconstruction of electron holograms. L.Q. Chen is acknowledged for helpful phase field simulations. TEM sample preparation in part was carried out by K. Kisslinger at the Center for Functional Nanomaterials, Brookhaven National Laboratory. Research carried out in part at the Center for Functional Nanomaterials, Brookhaven National Laboratory, which is supported by the U.S. Department of Energy, Office of Basic Energy Sciences. We acknowledge support from NSF MRSEC DMR 119826 (CRISP), DMR 1309868 and FAME. This work is supported by the U.S. Department of Energy, Office of Basic Energy Science, Division of Materials Science and Engineering, under Contract number DE-AC02-98CH10886. Supplementary Information is available online.
Author information
Authors and Affiliations
Contributions
M.-G.H., M.A.S., F.J.W., C.H.A. and Y.Z. conceived the research. M.S.J.M., J.H. and F.J.W. deposited epitaxial thin films. M.S.J.M. performed P-E, PFM and XRD measurements and analysed data with F.J.W. M.-G.H. and M.A.S. performed in situ domain switching experiments. M.-G.H. performed holography and analysed data. M.-G.H. and R.T. performed STEM-EBIC experiments. M.-G.H. and T.A. obtained STEM images and EELS data. L.W. analysed STEM images and EELS data. Y.Z., F.J.W. and C.H.A. directed research. M.-G.H. wrote the manuscript with Y.Z. All authors discussed and contributed to the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-2 (PDF 167 kb)
Rights and permissions
About this article
Cite this article
Han, MG., Marshall, M., Wu, L. et al. Interface-induced nonswitchable domains in ferroelectric thin films. Nat Commun 5, 4693 (2014). https://doi.org/10.1038/ncomms5693
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms5693
This article is cited by
-
Electric-field control of the nucleation and motion of isolated three-fold polar vertices
Nature Communications (2022)
-
Control of photocurrent and multi-state memory by polar order engineering in 2H-stacked α-In2Se3 ferroelectric
Science China Materials (2022)
-
Thermodynamic equilibrium theory revealing increased hysteresis in ferroelectric field-effect transistors with free charge accumulation
Communications Physics (2021)
-
Van der Waals negative capacitance transistors
Nature Communications (2019)
-
Ferroelectrics with a controlled oxygen-vacancy distribution by design
Scientific Reports (2019)