Rechargeable lithium batteries have ushered the wireless revolution over last two decades and are now matured to enable green automobiles. However, the growing concern on scarcity and large-scale applications of lithium resources have steered effort to realize sustainable sodium-ion batteries, Na and Fe being abundant and low-cost charge carrier and redox centre, respectively. However, their performance is limited owing to low operating voltage and sluggish kinetics. Here we report a hitherto-unknown material with entirely new composition and structure with the first alluaudite-type sulphate framework, Na2Fe2(SO4)3, registering the highest-ever Fe3+/Fe2+ redox potential at 3.8 V (versus Na, and hence 4.1 V versus Li) along with fast rate kinetics. Rare-metal-free Na-ion rechargeable battery system compatible with the present Li-ion battery is now in realistic scope without sacrificing high energy density and high power, and paves way for discovery of new earth-abundant sustainable cathodes for large-scale batteries.
Lithium (Li)-ion battery was intensely explored in 1980s leading to its commercialization in 1990s. Ever since, the synergistic effort in basic science and industrial optimization has led to the doubling of energy density. Currently, Li-ion batteries are ubiquitous in suites of small-scale consumer electronics, power tools as well as large-scale power sources driving the (plug-in) hybrid electric transportation and power-grid systems. The ever-growing global population and the meteoric rise in demand of easy access to modern technologies (gadgets/automobiles) have created multi-billion dollar battery industry. The current generation Li-ion batteries use oxides (such as LiCoO2 and LiMn2O4) and olivine LiFePO4 as cathodes1,2,3. Suddenly, this manifold consumption of Li has led to its scarcity and price rise, with many raising a concern whether Li is the new gold that may trigger geo-political tension in future4. The vast range of battery applications can be divided into two broad categories: volume/weight-restricted applications such as electronics/automobiles and volume/weight-less-dependent uses such as remote area large power-grid systems for efficient use of electricity transmitted from thermal power plants and solar/wind mills. While the Li batteries are indispensable for former category, the later category has been economically catered in part by Na–S batteries operating at high temperature over 300 °C. Resource optimization and tailor-made battery design for different applications, including dense smart grid with self-management housing system, is a global call, where Na-ion batteries operating at ambient temperatures can have vital role. Contrary to Li, sodium (Na) has abundant natural resources with even geographic distribution. Being the fifth most abundant element in earth’s crust, Na charge carrier is also the second lightest alkali element in periodic table. In this context, mammoth effort has been geared to build efficient Na-ion batteries with optimization of energy density, rate kinetics, low cost as well as safe and sustainable production and operation. In this pursuit, numerous Fe-based cathode compounds capable of efficient Na (de)insertion have been reported5,6,7,8,9,10,11.
Looking back to the history, soon after the conceptualization of intercalation reaction into TiS2 host in 1976 (ref. 12), research into Li-based and Na-based insertion compounds kick-started in early 1980s (LixCoO2 in 1980 (ref. 1) and NaxCoO2 in 1981 (ref. 5)). However, the commercial prospects of light-weight Li-ion batteries in portable electronics steered massive effort on Li systems, resulting in a two-decade-long hibernation period for Na counterparts. Over the past few years, the renewed interest on Na-ion chemistry has seen extensive research on various P2- and O3-type oxide-layered compounds and their solid solutions, mostly based on expensive transition metals such as Co and Ni. The large-scale Na-batteries will be commercially viable with earth-abundant transition metal such as Fe. Till date, O3-type NaFeO2 (ref. 13) and P2-type Nax[Fe1/2Mn1/2]O2 (ref. 7) are reported, both suffering from low operating potential even by using Fe4+/Fe3+ redox couple, and stable reversible capacity is limited. Using the inductive effect in polyanion framework systems, Fe3+/Fe2+ redox potential can be enhanced with full utilization of one-electron reaction14. In this pursuit, many ~3 V Fe-based phosphate PO43− insertion compounds have been reported. They are Na2FePO4F (3.06 V; ref. 8), NaFePO4 (2.7 V; ref. 9), Na2FeP2O7 (3 V; ref. 10) and Na4Fe3(PO4)2(P2O7) (3.2 V; ref. 11). Newer Fe-based compounds with higher electrode potential can be realized by replacing phosphate PO43− with sulphate SO42− units taking advantage of their higher electronegativity14. This avenue is not yet realized with the only known SO42−-based compounds NaFeSO4F and NaFeSO4F.2H2O being electrochemically inactive15,16. Herein, we report an entirely new class of cathode, Na2Fe2(SO4)3, combining the unusually high Fe redox potential ~3.8 V versus Na with excellent rate kinetics as well as good economy. It benchmarks the highest-ever Fe3+/Fe2+ redox potential by far observed among all known oxides and oxyanionic insertion materials for Na-ion batteries.
Materials synthesis and crystal structure
Unlike the oxides and various polyanions (BO33−, PO43− and SiO44−) compounds, the SO42− containing systems are acutely prone to thermal decomposition above ~400 °C (leading to SO2 gas evolution). In addition, inherent dissolution of SO42− in water makes it unstable in aqueous media. It rules out conventional high-temperature solid-state and aqueous solution-based synthetic routes. Thus, we used low-temperature (Tr ≤350 °C) solid-state methods to obtain Na2Fe2(SO4)3 target compound. The unknown crystal structure of this new cathode material was determined by synchrotron powder X-ray diffraction (XRD) (Fig. 1). Rietveld refinement and Mössbauer data (Fig. 1, inset) confirm trace amount of Fe(III) impurity phase(s). Mössbauer spectrum of the pristine material, consisting only Fe(II) species, could be fitted with two doublets having 1:1 intensity ratio, which can be assigned to two distinct crystallographic sites, Fe(1) and Fe(2). All the Bragg reflections were indexed in a monoclinic lattice assuming P21/c (No. 14) symmetry with lattice parameters a=11.46964(8) Å, b=12.77002(9) Å, c=6.51179(5) Å, β=95.2742(4)° and V=949.73(1) Å3. Although non-stoichiometry was to be considered, the fitting was satisfactory (Rwp=4.87%, Rp=3.94%, RBragg=1.58% and Goodness of fit (GoF)=1.74). Trace amount (about 4 wt%) of bata-FeSO4 as an impurity was included in the analysis. The crystallographic data are summarized in Supplementary Tables 1 and 2. Indexing and analysis adopting alternative C2/c symmetry with one Fe site was also possible with slight increase in RBragg as summarized in Supplementary Tables 3 and 4, indicating that local environments of two Fe sites are quite similar. Although P21/c symmetry seems more suitable in the present analysis, further systematic approach by electron diffraction and/or single-crystal XRD would be necessary for the firm conclusion on P21/c versus C2/c.
The refined crystal structure of Na2Fe2(SO4)3 is shown in Fig. 2a. To the best of our knowledge, the composition and crystal structure of Na2Fe2(SO4)3 are completely new and have never been reported in the literature. Deviating sharply from most of the AxM2(XO4)3-type compounds adopting the NASICON-related structures, Na2Fe2(SO4)3 does not contain the lantern units [M2(XO4)3], forming a unique structure with alluaudite-type framework. It would be convenient to denote AA′BM2(XO4)3 as general alluaudite-type compounds, where A=partially occupied Na(2), A′=partially occupied Na(3), B=Na(1), M=Fe2+ and X=S in the present case. To the best of our knowledge, this is the first sulphate compound with alluaudite-type framework. The Fe ions occupy octahedral sites that share edges with a crystallographically equivalent octahedron, forming Fe2O10 dimer units. These Fe ions were assigned to two distinct crystallographic sites, Fe(1) and Fe(2) (Fig. 2b). Even though the local structures of Fe(1) and Fe(2) are similar to each other, they are crystallographically distinct as revealed by two doublets in the Mössbauer spectrum (Fig. 1, inset). These isolated edge-sharing Fe2O10 dimers are in turn bridged together by SO4 units strictly by corner-sharing mode, hence forming a three-dimensional framework with large tunnels along c axis. The constituent Na occupies three distinct crystallographic sites; one fully occupied and two partially occupied. This new structure type should open up an entirely new Na2−xM2(SO4)3 (M=Mg, Ti, Mn, Co, Ni, V and VO) family of compounds as potential cathodes/anodes/solid electrolytes for further material exploration. Although NaMnFe2(PO4)3 compounds with alluaudite-type AA′BM2(XO4)3 framework of A, A′=partially occupied Na, B=Mn2+ and Fe2+, M=Mn3+ and Fe3+ and X=P was previously synthesized17, it showed weak electrochemical reactivity. Great advantage to use (SO4)2− instead of (PO4)3− is to stabilize the nearly Na–Fe equi-amount Na2Fe2(SO4)3 compound including only Fe2+ with partially occupied Na+ sites suitable for fast Na+ diffusion upon electrode reaction.
The electrode properties of as-synthesized Na2Fe2(SO4)3 were examined with no further optimization such as particle downsizing or carbon coating. The primary particle size was evaluated to be ~100–200 nm by scanning electron microscope observation (Supplementary Fig. 1), and the electrode loading was ca. 3 mg cm−2. The corresponding voltage-capacity profiles for first few cycles between 2.0–4.5 V (versus Na/Na+) at a rate of C/20 (25 °C) is shown in Fig. 3a. The Na2Fe2(SO4)3 cathode offers an average potential of 3.8 V (versus Na/Na+), which is the highest-ever Fe3+/Fe2+ redox potential in any materials environment. The well-known NASICON-type Fe(III)2(SO4)3 (ref. 18) has same composition with desodiated Na2Fe2(SO4)3 in the present study, but NASICON phase delivers an average potential of 3.3 V (versus Na/Na+) upon Na insertion19.
Thereby, Na2Fe2(SO4)3 cathode is characterized by three distinctive features: (i) totally new pristine composition with structure with edge-sharing FeO6 octahedra different from NASICON- or NASICON-like phases with corner-sharing FeO6 octahedra; (ii) initial valence state is Fe(II) with inherent existence of Na in the structure allowing to function as a cathode of Na-‘ion’ battery system; and (iii) much higher electrode potential by ~0.5 V comparing to the NASICON phases, providing very suitable operating potential of 3.8 V (versus Na/Na+) with smooth sloppy charge–discharge profiles over a narrow voltage range in 3.3–4.3 V window. Features (i) and (ii) account for the abnormally high potential of Na2Fe2(SO4)3 (ref. 20). The voltage E can be expressed as E=ΔG°/nF=(xG°Na+G°Host−G°NaxHost)/nF, where n, F and G are number of electrons, Faraday constant and Gibbs free energy, respectively. For Na2Fe2(SO4)3, the difference G°Host−G°NaxHost is large since the sodiated state is synthesized as stable state (low G°NaxHost), whereas the desodiated one is electrochemical-generated (possibly metastable) state (high G°Host). This is reverse for NASICON-type Fe2(SO4)3 and any related Fe(III) cathodes. Another factor, the edge-sharing geometry of the Fe octahedra in Na2Fe2(SO4)3, will push up G°Host owing to the strong Fe3+–Fe3+ repulsion, leading to high E19. This geometric characteristics can be found in other high-voltage materials such as triplite-type LiFeSO4F (ref. 21), and Li2FeP2O7 (ref. 22). In fact, Na2Fe2(SO4)3 has the shortest Fe–Fe distance among these materials. Thus, the operating potential of 3.8 V by Na2−xFe2(SO4)3 (that is, 4.1 V versus Li) records the highest value among all Fe-based battery cathodes; it is even higher than those of Fe4+/Fe3+ redox couple in simple oxides as Na1−xFeO2 (Fig. 5). Surprisingly, it exceeds the highest record in Li system in Li1−xFeSO4F, Li2FeP2O7 and Li2Fe(SO4)2 (~3.9 V versus Li and hence 3.6 V versus Na)21,22,23,24. Unlike the fluorosulphate cathodes, this high redox voltage is obtained without using electronegative F− units that make the synthesis cumbersome and enhances hygroscopic/instability in the final cathodes.
The initial reversible capacity of 102 mAh g−1, which corresponds to 85% of one-electron theoretical capacity (ca. 120 mAh g−1) based on Fe3+/Fe2+ redox couple, was highly reversible over 30 cycles under various current rate (Fig. 3b). Irreversible capacity of <14 mAh g−1 (>88% charge–discharge efficiency) in Fig. 3a may come from electrolyte decomposition as the cell was charged up to very high voltage, 4.5 V versus Na (4.8 V versus Li). When the current is further increased, 86% (versus the value at C/20) of the initial capacity can be delivered in 1 h (1C), 85% in 30 min (2C) and 70% in 6 min (10C) as shown in Fig. 3b. This high-rate capability of Na2−xFe2(SO4)3 electrode suggests that Na-ion migration in the framework structure is fast, as will be discussed in the later section.
In spite of its high power operation and excellent cyclability, the voltage profile of the initial charge was slightly different from those of the subsequent cycles. During the first charge segment, the average redox reaction occurs at 3.9 V (versus Na), which drops to 3.8 V in subsequent cycles. The differential galvanostatic profiles (dQ/dV) of Na2−xFe2(SO4)3 cathode (inset of Fig. 3a) showing two distinctive peaks (3.65 and 4.06 V versus Na/Na+) at the first charge and broader three peaks (3.42, 3.80, and 4.04 V in the middle points versus Na/Na+) upon subsequent discharging/charging processes. These indicate the occurrence of some irreversible structural transformation during first desodiation process, similar to the cases of Li2FeSiO4 and Li2FeP2O7 (ref. 22). The sloping voltage curve over the entire range of Na composition suggests a single-phase homogeneous reaction mechanism involving minimal volume change. This hypothesis was verified by comparative XRD patterns and Mossbauer Spectra of the Na2−xFe2(SO4)3 (x=0–1.6) compositions prepared by chemical oxidation (Supplementary Fig. 2 and Supplementary Table 5), as well as by in situ XRD measurement during electrochemical charge–discharge (Supplementary Fig. 3). Continuous shift of diffraction peaks with mere volume change (ΔV) of −1.6% was confirmed, and in striking contrast to the LixFePO4 system dominated by the two-phase separation25. This is beneficial for long-term cycling, uniform reaction over the whole electrode and longevity of the cathode involving less aggressive electromechanical grinding during its operation26. Such a small volume change in charge–discharge reaction may give another explanation for the high-rate capability but is quite surprising, considering much larger ionic radius of Na+ than that of Li+. Indeed, the ΔV= −17.6% in NaxFePO4 has been reported to be much larger than ΔV= −6.9% in LixFePO4 (refs 9, 27).
Na2Fe2(SO4)3 turns out to be an ideal host structure for efficient and fast Na+ (de)insertion with unusually high Fe redox potential. To gain further insight on this suitable structure, bond valence (BV) method was used to evaluate the validity of the crystal structure as well as to elucidate possible Na diffusion paths by utilizing the soft-BV parameters28,29. Difference of the BV sum from the ideal value (ΔBVS) provides a simple measure of positional suitability of mobile ions in solid frameworks30. Figure 4 shows a map of ΔBVS as equi-value surface. Inner side of the equi-value surface shows accessible spaces for Na+ in the [Fe2(SO4)3]2– framework. All the refined Na positions are consistent with the ΔBVS map where the maximum ΔBVS at Na positions are <0.2. Although the Na1 and the Na2 looks to have rather localized character in the present analysis, the Na3 site are clearly permeating along the  direction.
Ab initio calculations were performed to gain more quantitative understandings. The calculations were conducted for the Na poor region (see Methods section for details). At this concentration, we found that the binding energy of Na to the Na2 site is most favourable and to the Na3 least favourable. The activation energies for the Na-ion migration within the Na3 channel indeed is found to be low, which is 0.28 eV. Liquid-like value of 0.14 eV was calculated for defect diffusion along the channel and is among the lowest for Na-ion conductors31. The value for the Na2 channel is 0.54 eV similar to that for Na2FeP2O7, which shows very fast charge–discharge kinetics10,32,33. For migrations between channels, the activation energies are 0.88 and 0.58 eV for back-and-forth transport between Na1 and Na2 sites, and they are 0.54 and 0.05 eV for that between Na1 and Na3. We can therefore postulate that this material has one-dimensional Na+ conduction channels along the c axis for both the Na2 and Na3 sites, while the Na1 ion can be extracted through the Na3 sites. As a result, all the Na ions are accessible for (de)intercalation reaction with no limitation towards theoretical capacity. In particular, the continuous space around Na3 site can act as a fast Na transport channel during the charge–discharge reaction, which can be the origin of excellent kinetics of Na2Fe2(SO4)3 cathode material. Similar technical strategies applied for LixFePO4, which also shows one-dimensional diffusion34, should be effective to enhance electrode performance such as diminishing defect density and minimizing particle size along c axis35.
Finally, the material stability (chemical/thermal/storage) was examined36. Similar to other sulphate-based cathodes (for example, fluorosulphates and bisulphates), Na2Fe2(SO4)3 was found to dissolve completely in water. Thus, it is not stable in aqueous condition, a fact that was further verified by observation of its steady degradation upon long-time moisture exposure (in ambient condition) to form a hydrated derivative Na2Fe(SO4)2.4H2O. Nevertheless, with minimal exposure of freshly prepared sample to ambient air and careful packaging/storage (in inert atmosphere), this metastable compound remains intact with no deterioration in its electrochemical properties. Further, the thermal analysis of Na2Fe2(SO4)3 noticed gradual weight loss upon heating above 450 °C with simultaneous decomposition of SO4 units, release of SO2 gas and oxidation of Fe2+ species leading to the formation of Na2SO4, Fe2O3 and Fe3O4. In spite of this thermal decomposition above 450 °C, it should be noted that Na2Fe2(SO4)3 compound offers sufficient thermal stability of real-life battery applications.
Searching for novel low-cost cathode materials for rechargeable Na-ion batteries, we have synthesized a whole new family of cathode materials with general formula Na2M2(SO4)3. The first such candidate, Fe-based Na2Fe2(SO4)3, delivers a reversible capacity exceeding 100 mAh g−1 with the working Fe3+/Fe2+ potential located at 3.8 V (versus Na/Na+), the highest known value among all Fe-based insertion compounds. This abnormally high voltage is compatible with the thermodynamic limit of current generation organic electrolytes offering stable/safe operation. In addition, it offers excellent rate kinetics and cycling stability without demanding any additional cathode optimization. It forms an open framework host for efficient (de)intercalation of Na ions with very low activation energy. Operating voltage and reversible capacity of various known iron-based cathode for Na-‘ion’ (cathode functions as whole Na source) battery system are summarized in Fig. 5. The new material Na2Fe2(SO4)3 is benchmarking and worth further optimizing as it is the first Fe-based cathode for Na battery to offer high voltage compatible with Li battery system. Moreover, further effort to reach theoretical capacity by full utilization of inherent Na ions (85% in the present paper) can lead to energy density of >540 Wh kg−1, which is higher than those of LiMn2O4 (430 Wh kg−1) and LiFePO4 (500 Wh kg−1).
Complementing this electrode performance, Na2Fe2(SO4)3 can be easily prepared and upscaled by low-temperature solid-state methods, although care should be taken on the hygroscopic nature. The sustainability of Na2Fe2(SO4)3 further arises from its economic Na–Fe–S–O elemental constitution. In earth’s upper crust, Na and Fe are the most abundant and geographically distributed alkali and 3d transition metal, respectively. Talking about sulphur and sulphate compounds, they are very economic and widely used in fertilizers, pesticides and chemical industries. In fact, they are extremely cheap, being a byproduct of fuel combustion, coal power plants and oil/petrochemical industries. Thus, Na2Fe2(SO4)3 form an ideal material for economic production and large-scale battery manufacturing. We strongly believe that Na2Fe2(SO4)3 cathode will not only open up a new sub-group of polyanionic cathodes with commercial potential, but also inspire future success in discovering superior electrode materials for next-generation secondary batteries.
The target material was synthesized by reacting 1.54 g Na2SO4 (Wako, 99%) and 2.73 g FeSO4. The anhydrous FeSO4 precursor was prepared in-house by annealing commercial FeSO4.7H2O (Wako, 99%) under vacuum at 200 °C for 12 h (ref. 35). Na2Fe2(SO4)3 cathode compound was obtained via classical solid-state synthesis by ball milling the precursors for 4 h followed by annealing the mixture at 350 °C for 24 h under steady Ar flow. As SO4-based compounds are prone to dissolvation (in water) and thermal decomposition, we used these sustainable non-aqueous, low-temperature methods. Chemical oxidation was performed to obtain desodiated Na2−xFe2(SO4)3 samples using NO2BF4 (Alfa Aesar, 96%) oxidant dissolved in acetonitrile solvent (Wako, H2O level <5 p.p.m.). The solution was stirred overnight (with steady Ar flow), and the final products were filtered and dried at 60 °C under vacuum.
X-ray powder diffraction patterns were acquired in the 2θ range of 10–80° by a Bruker AXS D8 ADVANCE powder diffractometer equipped with a Co Kα radiation source operating at 35 kV and 40 mA. Synchrotron powder XRD data for Rietveld refinement was obtained under vacuum at the BL-4B2 beam line of Photon Factory (PF), High Energy Accelerator Research Organization (KEK), Tsukuba, Japan. The wavelength was calibrated to be 1.196179(10) Å. For all the XRD measurements, samples were mounted on an air-tightened custom-designed sample holder, which was covered with polyimide film inside an Ar-filled glove box to avoid any undesirable influence of air exposure. The determination of the peak positions and indexing were carried out with TOPAS-Academic Ver. 4.1 programme. The structure of Na2Fe2(SO4)3 was solved by the parallel tempering algorithm37 available in the global optimization programme FOX38, where tetrahedral constraints are applied to SO4 units. The positions and occupancies were refined by subsequent Rietveld refinement using TOPAS-Academic Ver.5 programme, and the final structure was illustrated with VESTA software39. The BVS for Na is calculated for whole space in the unit cell of Na2Fe2(SO4)3 within a grid resolution of 0.1 Å. The modified ‘soft-BV’ parameters are used by utilizing an expanded evaluation range of the bonding interaction; r0=1.5602 and B=0.483 for Na–O bond28. The penalty term of asymmetric coordinate was neglected. The Mössbauer spectra were taken with a Topologic System Inc. spectrometer with a 57Co γ–ray source, calibrated with α–Fe as standard. The model fitting was performed with MossWinn 3.0 software. Particle morphology of powder samples was analysed by a Hitachi S-4800 field-emission scanning electron microscope operating at 2 kV.
For electrochemical measurements, the working electrode was formulated by mixing 80 wt% Na2Fe2(SO4)3 active material, 15 wt% carbon black (Ketjen Black ECP, Lion Corp.) and 5 wt% polytetrafluoro-ethylene binder. This working electrode tape was pressed on an Ti mesh working as the current collector, with an average cathode loading of ca. 3 mg cm−2. Beaker-type three-electrode cells were assembled inside an Ar-filled glove box by taking the cathode film as the working electrode and Na metal foils acting as counter and reference electrodes. These beaker cells were filled with 1 M NaClO4 dissolved in propylene carbonate acting as electrolyte with no additives. Galvanostatic charge–discharge cycling was conducted in the voltage ranges, 2.0–4.5 V, at different rates from C/20 to 20C (at 25 °C). Rate capability tests were carried out using 2032-type coin cells with Na metal anode. Composite positive electrodes of 85 wt% active materials, 10 wt% ECP and 5 wt% polyvinylidene fluoride were mixed in N-methylpyrrolidone. The slurry was uniformly casted on an Al foil with an average loading of ca. 1 mg cm−2, and dried at 120 °C under vacuum. The electrolyte solution was 1.0 mol dm−3 NaPF6 dissolved in a mixture of ethylene carbonate:diethyl carbonate (5:5 by vol., Kishida Chemical) with 2 vol% of fluorinated ethylene carbonate (Kishida Chemical) as an electrolyte additive40. A glass fibre filter (GB-1000R, ADVANTEC) was used as a separator. The coin cells were discharged to 1.5 V at different rate from C/20 to 20C. Before each discharge, the cells were charged at C/20 to 4.2 V.
In situ XRD
In situ XRD measurements were conducted on BL-3A at KEK-PF using synchrotron radiation (λ=0.12 nm) at room temperature. Diffraction data (exposure time, 30 s) were collected with reflection geometry by a two-dimensional detector (PILATUS-100K, DECTRIS). As an electrode, 80 wt% Na2Fe2(SO4)3, 10 wt% ECP and 10 wt% polytetrafluoro-ethylene binder were mixed, pressed onto a 10 μm Al foil and dried at 120 °C under vacuum. An in situ XRD cell (RIGAKU) filled with 1 M NaClO4 dissolved propylene carbonate electrolyte was assembled in the following order: Be window, Na2Fe2(SO4)3 pellet on Al foil, a glass fibre filter and Na metal. The cell was cycled in the voltage range of 2–4.2 V at C/5 current rate (at 25 °C).
All the density functional theory (DFT) calculations were performed with the Vienna ab initio simulation package VASP41. The projector augmented wave method42 as implemented in the VASP code was used. The generalized gradient approximation (GGA) (PBE43) exchange-correlation functional was assumed, this eliminated the contribution of polaron transport in the migration calculations when the GGA+U method was used and allowed comparison with literature values. Spin-polarized calculations assuming ferromagnetic orderings of the Fe ions were conducted. A cutoff of 520 eV for the planewave expansion was used. The integration in the reciprocal space was conducted at the Γ point. Both Na poor and rich regions were investigated and was modelled with a 1 × 1 × 2 supercell that has a formula of Na1Fe16S24O96 per unit cell containing 137 atoms. The activation energy for Na+ migration was calculated with the climbing nudged elastic band44 method. The unit cell dimensions were fixed at the optimized unit cell size of this concentration during the nudged elastic band runs, otherwise all the ions were allowed to relax. Convergence of the forces were set to 0.015 eV Å−1 and the equilibrium pressure was smaller than |0.5| kbar.
How to cite this article: Barpanda, P. et al. A 3.8-V earth-abundant sodium battery electrode. Nat. Commun. 5:4358 doi: 10.1038/ncomms5358 (2014).
Mizushima, K., Jones, P. C., Wiseman, P. J. & Goodenough, J. B. LixCoO2 (0<x<1): A new cathode material for batteries of high energy density. Mater. Res. Bull. 15, 783–789 (1980).
Thackeray, M. M., David, W. I. F., Bruce, P. G. & Goodenough, J. B. Lithium insertion into manganese spinels. Mater. Res. Bull. 18, 461–472 (1983).
Padhi, A. K., Nanjundaswamy, K. S. & Goodenough, J. B. Phospho-olivines as positive-electrode materials for rechargeable lithium batteries. J. Electrochem. Soc. 144, 1188–1194 (1997).
Tarascon, J. M. Is lithium the new gold? Nat. Chem. 2, 510 (2010).
Delmas, C., Braconnier, J. J., Fouassier, C. & Hagenmuller, P. Electrochemical insertion of sodium in NaxCoO2 bronzes. Solid State Ion 3–4, 165–169 (1981).
Komaba, S. et al. Electrochemical Na insertion and solid electrolyte interphase for hard-carbon electrodes and application to Na-ion batteries. Adv. Funct. Mater. 21, 3859–3867 (2011).
Yabuuchi, N. et al. P2-type Nax[Fe1/2Mn1/2]O2 made from earth-abundant elements for rechargeable Na batteries. Nat. Mater. 11, 512–517 (2012).
Ellis, B. L., Makahnouk, W. R. M., Makimura, Y., Toghill, K. & Nazar, L. F. A multifunctional 3.5V iron-based phosphate cathode for rechargeable batteries. Nat. Mater. 6, 749–753 (2007).
Moreau, P., Guyomard, D., Gaubicher, J. & Boucher, F. Structure and stability of sodium intercalated phases in olivine FePO4 . Chem. Mater. 22, 4126–4128 (2010).
Barpanda, P. et al. Sodium iron pyrophosphate: A novel 3.0V iron-based cathode for sodium-ion batteries. Electrochem. Commun. 24, 116–119 (2012).
Kim, H. et al. New iron-based mixed-polyanion cathodes for lithium and sodium rechargeable batteries: combined first principles calculations and experimental study. J. Am. Chem. Soc. 134, 10369–10372 (2012).
Whittingham, M. S. Electrical energy storage and intercalation chemistry. Science 192, 1126–1127 (1976).
Okada, S. et al. Layered transition metal oxides as cathodes for sodium secondary battery. ECS Meeting Abstract MA2006-02, 201 (2006).
Padhi, A. K., Nanjundaswamy, K. S., Masquelier, C. & Goodenough, J. B. Mapping of transition metal redox energies in phosphates with NASICON structure by lithium intercalation. J. Electrochem. Soc. 144, 2581–2586 (1997).
Barpanda, P. et al. Structural, transport, and electrochemical investigation of novel AMSO4F (A=Na, Li; M=Fe, Co, Ni, Mn) metal fluorosulphates prepared using low temperature synthesis routes. Inorg. Chem. 49, 7401–7413 (2010).
Ati, M. et al. Synthesis, structural, and transport properties of novel bihydrated fluorosulphates NaMSO4F.2H2O (M=Fe, Co, and Ni). Chem. Mater. 22, 4062–4068 (2010).
Trad, K. et al. NaMnFe2(PO4)3 alluaudite phase: synthesis, structure, and electrochemical properties as positive electrode in lithium and sodium batteries. Chem. Mater. 22, 5554–5562 (2010).
Manthiram, A. & Goodenough, J. B. Lithium insertion into Fe2(SO4)3 frameworks. J. Power Sources. 26, 403–408 (1989).
Okada, S., Arai, S. & Yamaki, J. Iron complex cathodes. Denki Kagaku 65, 802–808 (1997).
Chung, S. C., Barpanda, P., Nishimura, S., Yamada, Y. & Yamada, A. Polymorphs of LiFeSO4F as cathode materials for lithium ion batteries – a first principle computational study. Phys. Chem. Chem. Phys. 14, 8678–8682 (2012).
Barpanda, P. et al. A 3.90V iron-based fluorosulphate material for lithium-ion batteries crystallizing in the triplite structure. Nat. Mater. 10, 772–779 (2011).
Nishimura, S., Nakamura, M., Natsui, R. & Yamada, A. New lithium iron pyrophosphate as 3.5V class cathode material for lithium ion battery. J. Am. Chem. Soc. 132, 13596–13597 (2010).
Reynaud, M. et al. Li2Fe(SO4)2 as a 3.83V positive electrode material. Electrochem. Commun. 21, 77–80 (2012).
Ye, T. et al. General observation of Fe3+/Fe2+ redox couple close to 4V in partially substituted Li2FeP2O7 pyrophosphate solid-solution cathodes. Chem. Mater. 25, 3623–3629 (2013).
Yamada, A. et al. Room-temperature miscibility gap in LixFePO4 . Nat. Mater. 5, 357–360 (2006).
Wang, Y. et al. A zero-strain layered metal oxide as the negative electrode for long-life sodium-ion batteries. Nat. Commun. 4, 2365 (2013).
Lu, J., Chung, S. C., Nishimura, S. & Yamada, A. Phase diagram of olivine NaxFePO4 . Chem. Mater. 25, 3623–3629 (2013).
Brown, I. D. IUCr Monographs on Crystallography 12, Oxford University Press (2002).
Adam, S. Relationship between bond valence and bond softness of alkali halides and chalcogenides. Acta Cryst. B57, 278–287 (2001).
Adam, S. From bond valence maps to energy landscapes for mobile ions in ion-conducting solids. Solid State Ion 177, 1625–1630 (2006).
Ong, S. P. et al. Voltage, stability and diffusion barrier differences between sodium-ion and lithium-ion intercalation materials. Energy Environ. Sci. 4, 3680–3688 (2011).
Clark, J. M. et al. High-voltage pyrophosphate cathode: insights into local structure and lithium diffusion pathways. Angew. Chem. Int. Ed. 51, 13149–13153 (2012).
Kim, H. et al. Na2FeP2O7 as a promising iron-based pyrophosphate cathode for sodium rechargeable batteries: a Combined Experimental and Theoretical Study. Adv. Funct. Mater. 23, 1147–1155 (2013).
Nishimura, S. et al. Experimental visualization of lithium diffusion in LixFePO4 . Nat. Mater. 7, 707–711 (2008).
Malik, R. et al. Particle size dependence of the ionic diffusivity. Nano Lett. 10, 4123–4127 (2010).
Subban, C. V. et al. Preparation, structure, and electrochemistry of layered polyanionic hydroxysulfates: LiMSO4OH (M=Fe, Co, Mn) electrodes for Li-ion batteries. J. Am. Chem. Soc. 135, 3653–3661 (2013).
Falcioni, M. & Deem, M. W. A biased Monte Carlo scheme for zeolite structure solution. J. Chem. Phys. 110, 1754–1766 (1999).
Favre-Nicolin, V. & Cerny, R. FOX, ‘free objects for crystallography’: a modular approach to ab initio structure determination from powder diffraction. J. Appl. Cryst. 35, 734–743 (2002).
Momma, K. & Izumi, F. VESTA 3 for three-dimensional visualization of crystal volumetric and morphology data. J. Appl. Cryst. 44, 1272–1276 (2011).
Komaba, S. et al. Fluorinated ethylene carbonate as electrolyte additive for rechargeable Na batteries. ACS Appl. Mater. Interfaces 3, 4165–4168 (2011).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3869 (1996).
Henkelman, G., Uberuaga, B. P. & Jónsson, H. A climbing image nudged elastic band method for finding saddle points and minimum energy paths. J. Chem. Phys. 113, 9901–9904 (2000).
We acknowledge the financial support from the Ministry of Education, Culture, Sports, Science and Technology, Japan (MEXT) under the ‘Element Strategy Initiative for Catalysts and Batteries’ (ESICB) project. P.B. is thankful to the Japan Society for the Promotion of Sciences for a JSPS Fellowship. Research Center for Computational Science, Okazaki, Japan is thanked for the computer time. The synchrotron XRD experiments were performed under KEK-PF under programme no. 2013G670.
The authors declare no competing financial interests.
About this article
Cite this article
Barpanda, P., Oyama, G., Nishimura, Si. et al. A 3.8-V earth-abundant sodium battery electrode. Nat Commun 5, 4358 (2014). https://doi.org/10.1038/ncomms5358
Rare Metals (2021)
A novel low-cost and environment-friendly cathode with large channels and high structure stability for potassium-ion storage
Science China Materials (2021)
A fumarole in a one-pot: synthesis, crystal structure and properties of Zn- and Mg-analogs of itelmenite and a synthetic analog of glikinite
Physics and Chemistry of Minerals (2021)
First-principles study of electronic structure, sodium diffusion, and (de)intercalation in NASICON NaMR(MoO4)3 (M = Mg, Ni; R = Cr, Fe)