Directing light emission is key for many applications in photonics and biology. Optical antennas made from nanostructured plasmonic metals are suitable candidates for this purpose but designing antennas with good directional characteristics can be challenging, especially when they consist of multiple elements. Here we show that strongly directional emission can also be obtained from a simple individual gold nanodisk, utilizing the far-field interference of resonant electric and magnetic modes. Using angle-resolved cathodoluminescence spectroscopy, we find that the spectral and angular response strongly depends on excitation position. For excitation at the nanodisk edge, interference between in-plane and out-of-plane dipole components leads to strong beaming of light. For large nanodisks, higher-order multipole components contribute significantly to the scattered field, leading to enhanced directionality. Using a combination of full-wave simulations and analytical point scattering theory we are able to decompose the calculated and measured scattered fields into dipolar and quadrupolar contributions.
Optical nanoantennas have the ability to control the emission and absorption of light at the nanoscale1. Nanoantennas composed of metallic nanoparticles that support localized surface plasmon resonances (LSPRs) in the ultraviolet-visible-infrared part of the electromagnetic spectrum have been used to control spontaneous emission2,3,4,5,6 and surface enhanced Raman scattering7,8, and find applications in targeted medicine9,10, solar steam generation11,12 or photovoltaics13. In many of these applications the directionality of the plasmon scattering plays a pivotal role.
The angular scattering profiles of single nanoparticle antennas are usually isotropic around the symmetry axis. To obtain strong directionality in plasmonic nanoantennas multi-element array antennas such as the Yagi–Uda geometry are used. These are composed of a locally driven feed element that is coupled to several parasitic director elements that collectively interfere in the far field14, giving rise to directional emission5,15,16,17,18,19,20. However, these array antennas are complex to design and fabricate, and have a relatively large spatial footprint. Strong directionality can also be achieved using just a single element antenna if the interference between electric dipole and higher-order multipole components can be controlled21,22,23,24,25,26,27,28. However, efficient excitation of higher-order magnetic and electric multipoles requires strong field gradients on the scale of the nanoparticle, which is difficult to obtain using plane wave excitation. Since each multipole component has its own complex vectorial near-field distribution, local excitation of the nanoantenna can enable excitation of the right combination of modes that interfere in such a way as to give strongly directional emission.
Here we use a tightly focused 30 keV electron beam as local excitation source to drive the resonant electric and magnetic modes in cylindrical Au nanoantennas. The evanescent electromagnetic field about the electron trajectory provides a stable and highly localized (~10 nm) broadband source of surface plasmons that does not perturb the dielectric environment enabling spatially resolved studies of plasmonic modes over a broad spectral range in a single experiment17,29,30,31,32,33,34,35,36,37. Using angle-resolved cathodoluminescence (CL) imaging spectroscopy (ARCIS)17,38, we show that the interference between locally excited multipole components in the Au particles can give rise to strongly directional emission in a single element nanoantenna. We demonstrate that the beaming direction is directly controlled by the precise electron beam position on the nanoparticle. From the spectrally filtered angular emission distributions we detect features in the locally excited plasmon radiation fields that provide key information on the modal composition of the plasmon excitation. By combining full-wave simulations and analytical point scattering theory we are able to decompose the measured far-field radiation patterns into electric dipole, magnetic dipole and electric quadrupole contributions and show that these all contribute to the antenna’s scattering profile.
We fabricated cylindrical gold nanoparticles with diameters ranging from 50–180 nm in 5 nm steps and a height of 80 nm on a crystalline silicon substrate using a combination of electron beam lithography, thermal evaporation and lift-off. For the hyperspectral imaging measurements we raster-scan the e-beam in small steps over the disk (5 nm steps for D≤100 nm and 7.5 nm steps for D>100 nm). Light is collected by a half-parabolic mirror placed between sample and the electron microscope pole piece and directed to a grating spectrometer equipped with a liquid nitrogen cooled CCD camera. At each excitation position we collect a spectrum in the visible/near-infrared spectral region. The integration time was 500 ms per pixel at a beam current of 0.8 nA. By integrating over all scanning pixels we also obtain the average CL spectrum for each nanodisk. The spectra are normalized to the peak intensity and corrected for background radiation from the Si substrate. Figure 1a shows spatially-averaged spectra for Au nanodisks with D=50, 100, and 180 nm, respectively. The corresponding scanning electron micrographs of the disks are shown as insets. For the D=50 nm particle we observe a LSPR peak at λ0=580 nm. The peak broadens and blueshifts when the diameter is increased to 100 nm. For the largest particle (D=180 nm) the spectrum is broadened further and shows a clear shoulder at λ0=700 nm suggesting a second LSPR resonance. The gradual blueshift of the main peak and the emergence of a shoulder at longer wavelengths can be seen in more detail in Fig. 1b where the spatially averaged CL spectrum is shown for all measured nanodisks with diameters in the range D=50–180 nm.
To gain further insight into the nature of the resonant modes we plot the two-dimensional (2D) spatial maps at the peak-wavelengths for the three diameters in Fig. 1a integrated over a 20 nm spectral bandwidth (Fig. 1c–e). As can be seen for these wavelengths, the 50 and 100 nm disks radiate most efficiently when excited in the centre, whereas the 180 nm particle radiates most strongly when excited at the edge. From our previous work, it is known that modes that are efficiently driven by the electron beam in the particle centre usually have m=0 (azimuthal) symmetry17,39,40 and an out-of-plane oriented electric dipole moment, whereas efficient edge excitation indicates the presence of strong in-plane dipole components (m=1), where m is the azimuthal quantum number. In the first case the vertical component of the electric field is strong in the centre while in the second case it is strong at the edge allowing strong coupling to the electron beam at those specific positions. Considering that the nanodisk diameter/height aspect ratio changes from 0.625 (50 nm diameter) to 2.25 (180 nm diameter) respectively, it is to be expected that the in-plane components become more dominant as their scattering efficiency increases for the larger nanodisks.
The evolution of the CL spectrum as function of disk diameter is governed by three effects. First, for the smaller diameters the out-of-plane dipole resonance is dominant and it is known that an increase in particle size transverse to the electric dipole resonance axis leads to a stronger restoring force and thus a blue-shifted resonance. Second, following the same reasoning the in-plane electric dipole resonance redshifts because the increase in size is now along the dipole axis. Third, higher-order resonant modes become more dominant for larger particles, having an effect on the CL spectrum.
To gain more insight into the nature of the particle resonances, we measured the far-field angular emission patterns by projecting the beam emanating from the parabolic mirror onto a 2D CCD array. The CCD data are subsequently converted to angular emission distributions38. We collect the angular patterns for free-space wavelenghts (λ0) from 400 to 750 nm using 40-nm band pass filters for D=50, 100, 140 and 180 nm disks. To optimize the signal-to-noise ratio, we have used 120 s integration time for λ0=400, 450, 700 and 750 nm and 60 s for λ0=500–650 nm.
Figure 2a shows the angular pattern for a D=180 nm particle at λ0=600 nm for excitation on the ‘left’ edge of the nanodisk. The pattern clearly shows a strong angular asymmetry. When excited at the edge, the particle preferentially radiates away from the excitation point. Angular patterns for four orthogonal edge positions are shown in Fig. 3, demonstrating that the beaming is always directed away from the excitation point. If the nanodisk is excited in the centre the emission intensity is lower (also see Fig. 1e) and an azimuthally symmetric toroidal emission pattern is observed consistent with the radiation pattern of a vertically oriented electric dipole on top of a high-index substrate. A similar beaming effect also occurs for D=100 nm disks, which is shown in Fig. 4a–c) for λ0=600 nm. In contrast, for D=50 nm disks the pattern remains almost toroidal for all excitation positions and very closely matches the angular pattern of a vertical electric dipole (see Fig. 4d–f).
Figure 2b shows the magnitude of the angular asymmetry as function of wavelength, calculated from the integrated ‘forward’ and ‘backward’ half of the angular hemisphere. Data are shown for four different disk diameters. For the D=50 nm disks the measured ratio is close to 1 (except for λ0=400 nm), indicating that there is no asymmetry in the emission pattern. As the diameter increases, stronger angular beaming is observed and the maximum beaming condition shifts to longer wavelengths. The strongest directionality (forward-to-backward intensity ratio of 2.8) is obtained for the D=180 nm disks at λ0=600 nm. The increase in directionality for increasing diameter is clearly visible in Fig. 2c, which shows crosscuts through the angular data at λ0=600 nm for the same disk diameters as in Fig. 2b. The data in Figs 2 and 3 show that directional angular emission can be achieved from a single nanodisk by precisely positioning the local electron beam source. Note that the directionality is reversed with respect to what was shown in ref. 41. This is due to the fact that we collect the angular patterns for the upper hemisphere, whereas in that case the patterns were measured on the substrate side where the dipole radiation ‘doughnut’ points towards the excitation point.
To study the nature of the different resonant modes that contribute to the radiation patterns we study the angular emission distribution for different wavelengths. Figure 5 shows normalized angular patterns for λ0=400–600 nm for the D=180 nm particle disk for edge excitation on the ‘left’ side. The pattern for λ0=400 nm shows a strong radiation lobe normal to the substrate. The relative contribution of this lobe becomes increasingly weaker for longer wavelength while the sideward lobe gradually becomes more pronounced. At λ0=600 nm the forward scattering ratio is maximum and most of the radiation is emitted into one strong crescent-shaped lobe pointing away from the excitation position (same data as in Fig. 2a).
Next, we derive a model for the single-disk radiation profiles. If the size of the nanodisk is much smaller than the wavelength it can accurately be described as a point dipole scatterer with a electric dipolar polarizability tensor42. For larger sizes higher-order multipole contributions become significant. The coupling efficiency to different moments strongly depends on the type of excitation43,44, particle shape and dielectric environment. In particular for cases where the particles have a non-spherical shape and/or are placed in an asymmetric dielectric environment like on a substrate, quantifying the contributions of the different multipoles is complex. Here we use a 3D surface integral equation method to find the relevant multipolar components for our experiment. In this full-wave method the nanodisk is discretized into triangular surface elements45,46. By locally solving Maxwell’s surface integrals for each individual element, the scattered fields for a particular type of driving field, eigenpolarizabilities, and the local density of optical states in the vicinity of a scatterer can be accurately calculated. This method recently has been successfully employed to describe the scattering properties of plasmonic split rings47.
To simulate our experiment, we discretize the surfaces of cylindrical particles with 50, 100 and 180 nm diameters into surface elements using a radius of curvature of 5 nm to prevent numerical inaccuracies in the fields. We calculate dipolar and quadrupolar polarizabilities by exciting the structures with orthogonal sets of counter-propagating waves and decomposing the calculated scattered field into vector spherical harmonics. This allows us to represent the nanodisk by a point scatterer of which the scattering properties are described by its superpolarizability tensor (F.B.A, T.C. and A.F.K., manuscript in preparation; see also ref. 46 for details). To account for the effect of the substrate a backaction substrate-correction to the superpolarizability tensor is applied to the initial calculation. To drive the disk we place a vertical point dipole at the xy electron beam excitation positions used in the experiment, thereby mimicking the electron beam driving. For the z position of the dipole we study both 40 nm (at the half-height of the disk) and 80 nm (top of the disk). We find that for both excitation dipole heights the relevant components for edge excitation (in the x direction at ϕ=90°, 270°) are electrical dipole moments pz and px, the magnetic component my, and quadrupolar moments Qxz (corresponding to the Q13 and Q31 elements in the quadrupole tensor48), and Qxy (corresponding to the Q11 and −Q22 elements in the tensor which is a quadrupole that is rotated 45° in the xy plane with respect to the Q12, Q21 quadrupole).
The angular patterns and corresponding charge distributions of these individual components are shown in the bottom panel of Fig. 5. These are calculated using asymptotic far-field approximations for dipoles and quadrupoles in the presence of a substrate49,50,51. Both electrical dipole components pz and px show the characteristic toroid shapes centred around the dipole axis. As the figure shows, the patterns deviate from a perfect toroid because of substrate interference50. Both of these dipole components have a significant Ez component at the edge of the nanodisk and thus can be driven by a z dipole or electron beam at this position. The magnetic dipole component my corresponds to an electrical current loop in the xz plane (indicated by the black dashed line in the schematic for my in the bottom panel of Fig. 5), which also has a significant Ez component at the edge of the disk. For the Qxz and Qxy quadrupoles the radiation patterns show multiple radiation lobes. These particular quadrupoles would show four radiation lobes in free space of which three are visible in the upper hemisphere for Qxz (because one lobe is oriented directly along the normal into the substrate where it can not be collected by our parabolic mirror) and all four are visible for Qxy because all lobes lie in the xy plane. Like for the dipole patterns the quadrupolar patterns are distorted relative to those in a homogeneous dielectric environment due to the presence of the reflective silicon substrate.
Next, using the theoretical far fields of the relevant multipole components we decompose the experimental far-field angular radiation patterns by numerically fitting the complex amplitudes using a least-squares numerical optimization routine44,52. For the smaller disks (D=50–100 nm) the patterns are dominated by px and pz due to their size compared with the wavelength, so using only those components for the data-fitting yields good results (see Fig. 4c,f). We find a ratio of |pz|/|px| of 1.9 for λ0=600 nm for the D=100 nm disk, so the pz component is strongest in that case. Because of their pure dipolar character the resulting asymmetry in the angular pattern is smaller than for the larger disks. For the D=50 nm disk a toroidal ‘doughnut’ shaped pattern is observed, consistent with the emission pattern of a vertically oriented point dipole source (so a pure pz contribution)49,50. This is consistent with the spatial profile in Fig. 1c, where we observed an excitation maximum in the centre of the nanodisk.
In contrast, for a D=180 nm disk all five dipolar and quadrupolar components mentioned above contribute to the observed radiation profiles. The bottom row of the top panel in Fig. 5 shows the angular patterns obtained from the numerical fits. They agree very well with the measured patterns. This demonstrates that the observed angular patterns indeed can be accurately described as the coherent superposition of the multipoles predicted by surface integral equation calculations. The absolute values of the different multipole moments are listed in Table 1. For all fits the in-plane electrical dipole component px is dominant as one might expect for a disk with this diameter and aspect ratio. Nevertheless in all fits there are significant contributions from the vertical electric dipole, magnetic dipole and electric quadrupoles.
As is the case for Kerker scattering in dielectric/semiconductor nanoparticles21,22,23,24,27, strong directionality is expected only when the different multipole components are similar in magnitude as that allows effective interference in the far field. Evidently this condition is not met for the D=50 nm disk, where the pattern is fully dominated by pz and no beaming is observed. However, when we look at the fitted values for the D=180 nm particle especially at λ0=600 nm, the px component is less dominant and there are significant multipolar contributions, leading to a weaker normal component of the radiation emission and strong asymmetric emission towards the side (Fig. 2a). For almost all measurements (except for D=50 nm at λ0=400 nm) the radiation is predominantly emitted away from the excitation point (see Fig. 2a), so for these nanodisks there are no significant relative phase-flips of the components as function of wavelength that would lead to inversion of the directionality.
Thus, the admixture of multipolar contributions that yields directionality can be controlled on one hand by particle size and shape, that is, by control of the multipole polarizabilities, and on the other hand by changing the particle driving by nanoscale changes in excitation position of a local source like the electron beam such that the structure is excited in an asymmetric way. An alternative way of achieving this driving asymmetry is by using circularly/elliptically polarized light as has been demonstrated recently in ref. 25.
In some cases it might be desirable to have a more universal unidirectionality, meaning that an antenna is designed in such a way that it emits in the same direction for a large variety of excitation conditions (even for symmetric excitations). This can be achieved by introducing an asymmetry in the nanostructure itself26,28. Also in this case, it has been shown that it is better to have larger structures with more polarizable material in order to promote the higher-order multipoles that facilitate a strong directional response. Rather than engineering either the driving or the structure to constrain the emitted patttern to a given asymmetric and directional distribution, we envision that the strong variability of directionality with excitation position can also be used advantageously. In particular, we propose that the type of position-dependent directionality as shown in this article lends itself perfectly for improving fluorescence correlation spectroscopy, for instance, where temporal correlations in fluorescence intensity can reveal the diffusion constant of single diffusing fluorophores53,54. By detecting fluorescence intensity of single molecules diffusing over the nanodisks in the Fourier plane with a quadrant photodiode for instance, one could utilize the antenna directionality to decrease the effective detection volume, thereby boosting the sensitivity.
Finally, in our experiment the antennas are on a high-index substrate that on one hand helps with the generation of significant multipole moments through backaction on the nanodisks (F.B.A, T.C., A.F.K., manuscript in preparation) but also leads to large radiation losses into the substrate. These radiation losses could be minimized by for instance using a ground-plane geometry where a mirror underneath the structure ensures that all of the light is emitted into the upper hemisphere. The concepts shown in this work can directly be applied to such ground-plane antennas, which may lead to novel highly efficient directional antenna designs.
In conclusion we have measured the directional emission properties of gold nanodisks as functions of size and wavelength using angle-resolved CL imaging spectroscopy. For the 50 nm diameter disks the angular pattern is toroidal, corresponding to an out-of-plane dipole resonance. For the larger disks the angular patterns are a coherent superposition of electric dipole, magnetic dipole and electric quadrupole contributions. For these disks we find that nanoscale lateral displacements of the electron beam over the nanodisk leads to drastic changes in the angular pattern. We find that off-centre excitation leads to an asymmetric radiation pattern where light is preferentially scattered in the forward direction, which is due to the complex far-field interference of different multipole moments generated in the disk. When the wavelength is large compared with the particle size the emission is dominated by electrical dipole components but when the particle size increases there are clear magnetic dipole and electric quadrupole contributions giving rise to strong directionality without the use of additional parasitic antenna elements. Our work could be utilized in the future to engineer strongly directional single-element antennae with a small spatial footprint, which could be used in a wide variety of applications.
We fabricated gold nanodisks on a crystalline silicon substrate using a combination of electron beam lithography, thermal evaporation and lift-off. We used a 350-nm-thick layer of ZEP520A as positive resist for electron beam lithography with a Raith E-line system. After exposure and development, a gold layer was deposited using thermal physical vapour deposition in vacuum. After lift-off in n-methylpyrollidone at 65 °C for 3 h, we obtained nanodisks on silicon with diameters ranging from 50–180 nm and a height of 80 nm.
How to cite this article: Coenen, T. et al. Directional Emission from a Single Plasmonic Scatterer. Nat. Commun. 5:3250 doi: 10.1038/ncomms4250 (2014).
Novotny, L. & van Hulst, N. Antennas for light. Nat. Photon. 5, 83–90 (2011).
Kuhn, S., Hakanson, U., Rogobete, L. & Sandoghdar, V. Enhancement of single-molecule fluorescence using a gold nanoparticle as an optical nanoantenna. Phys. Rev. Lett. 97, 017402 (2006).
Bharadwaj, P., Anger, P. & Novotny, L. Nanoplasmonic enhancement of single-molecule fluorescence. Nanotechnology 18, 044017 (2007).
Kinkhabwala, A. et al. Large single-molecule fluorescence enhancements produced by a bowtie nanoantenna. Nat. Photon. 3, 654–657 (2009).
Curto, A. G. et al. Unidirectional emission of a quantum dot coupled to a nanoantenna. Science 329, 930–933 (2010).
Frimmer, M. & Koenderink, A. F. Spontaneous emission control in a tunable hybrid photonic system. Phys. Rev. Lett. 110, 217405 (2013).
Ahmed, A. & Gordon, R. Single molecule directivity enhanced Raman scattering using nanoan-tennas. Nano Lett. 12, 2625–2630 (2012).
Wang, D., Zhu, W., Best, M. D., Camden, J. P. & Crozier, K. B. Directional raman scattering from single molecules in the feed gaps of optical antennas. Nano Lett. 13, 2194–2198 (2013).
Huschka, R. et al. Gene silencing by gold nanoshell-mediated delivery and laser-triggered release of antisense oligonucleotide and siRNA. ACS Nano 6, 7681–7691 (2012).
Kang, B., Ann, M. M., Austin, L. A. & El-Sayed, M. A. Exploiting the nanoparticle plasmon effect: observing drug delivery dynamics in single cells via Raman/fluorescence imaging spectroscopy. ACS Nano 7, 7420–7427 (2013).
Neumann, O. et al. Solar vapor generation enabled by nanoparticles. ACS Nano 7, 42–49 (2013).
Fang, Z. et al. Evolution of light-induced vapour generation at a liquid-immersed metallic nanoparticle. Nano Lett. 13, 1736–1742 (2013).
Atwater, H. A. & Polman, A. Plasmonics for improved photovoltaic devices. Nat. Mater. 9, 205–213 (2010).
de Waele, R., Koenderink, A. F. & Polman, A. Tunable nanoscale localization of energy on plasmon particle arrays. Nano Lett. 7, 2004–2008 (2007).
Koenderink, A. F. Plasmon nanoparticle array waveguides for single photon and single plasmon sources. Nano Lett. 9, 4228–4233 (2009).
Kosako, T., Kadoya, Y. & Hofmann, H. F. Directional control of light by a nano-optical Yagi-Uda antenna. Nat. Photon. 4, 312–315 (2010).
Coenen, T., Vesseur, E. J. R., Polman, A. & Koenderink, A. F. Directional emission from plasmonic Yagi-Uda antennas probed by angle-resolved cathodoluminescence spectroscopy. Nano Lett. 11, 3779–3784 (2011).
Dregely, D. et al. 3D optical Yagi-Uda nanoantenna-array. Nat. Commun. 2, 267 (2011).
Shegai, T. et al. A bimetallic nanoantenna for directional colour routing. Nat. Commun. 2, 481 (2011).
Bernal Arango, F., Kwadrin, A. & Koenderink, A. F. Plasmonic antennas hybridized with dielectric waveguides. ACS Nano 6, 10156–10167 (2012).
Kerker, M., Wang, D. S. & Giles, C. L. Electromagnetic scattering by magnetic spheres. J. Opt. Soc. Am. 73, 765–767 (1983).
Rolly, B., Stout, B. & Bonod, N. Boosting the directivity of optical antennas with magnetic and electric dipolar resonant particles. Opt. Express 20, 20376–20386 (2012).
Person, S. et al. Demonstration of zero optical backscattering from single nanoparticles. Nano. Lett. 13, 1806–1809 (2013).
Fu, Y. H., Kuznetsov, A. I., Miroshnichenko, A. E., Yu, Y. F. & Luk’yanchuk, B. Directional visible light scattering by silicon nanoparticles. Nat. Commun. 4, 1527 (2013).
Rodríguez-Fortuño, F. J. et al. Near-field interference for the unidirectional excitation of electromagnetic guided modes. Science 340, 328–330 (2013).
Vercruysse, D. et al. Unidirectional side scattering of light by a single-element nanoantenna. Nano Lett. 13, 3843–3849 (2013).
Staude, I. et al. Tailoring directional scattering through magnetic and electric resonances in subwavelength silicon nanodisks. ACS Nano 7, 7824–7832 (2013).
Hancu, I. M., Curto, A. G., Castro-Lopez, M., Kuttge, & van Hulst, N. F. Multipolar interference for directed light emission. Nano Lett. 14, 166–171 (2014).
García de Abajo, F. J. Optical excitations in electron microscopy. Rev. Mod. Phys. 82, 209275 (2010).
Nelayah, J. et al. Mapping surface plasmons on a single metallic nanoparticle. Nat. Phys. 3, 348–353 (2007).
Denisyuk, A. I. et al. Transmitting hertzian optical nanoantenna with free-electron feed. Nano Lett. 10, 3250–3252 (2010).
Yamamoto, N., Ohtani, S. & García de Abajo, F. J. Gap and Mie plasmons in individual silver nanospheres near a silver surface. Nano Lett. 11, 91–95 (2011).
Koh, A. L., Fernández-Domínguez, A., McComb, D., Maier, S. & Yang, J. High-resolution mapping of electron-beam-excited plasmon modes in lithographically defined gold nanostructures. Nano Lett. 11, 1323–1330 (2011).
Knight, M. W. et al. Aluminum plasmonic nanoantennas. Nano Lett. 12, 6000–6004 (2012).
Schmidt, F. P. et al. Dark plasmonic breathing modes in silver nanodisks. Nano Lett. 12, 5780–5783 (2012).
Scholl, J. A., Koh, A. L. & Dionne, J. A. Quantum plasmon resonances of individual metallic nanoparticles. Nature 483, 421–427 (2012).
Nicoletti, O. et al. Three-dimensional imaging of localized surface plasmon resonances of metal nanoparticles. Nature 502, 80–84 (2013).
Coenen, T., Vesseur, E. J. R. & Polman, A. Angle-resolved cathodoluminescence spectroscopy. Appl. Phys. Lett. 99, 143103 (2011).
Vesseur, E. J. R. & Polman, A. Plasmonic whispering gallery cavities as optical antennas. Nano Lett. 11, 5524–5530 (2011).
Coenen, T., Vesseur, E. J. R. & Polman, A. Deep subwavelength spatial characterization of angular emission from single-crystal Au plasmonic ridge nanoantennas. ACS Nano 6, 1742–1750 (2012).
Le Moal, E. et al. An electrically excited nanoscale light source with active angular control of the emitted light. Nano Lett. 13, 4198–4205 (2013).
Bohren, C. & Huffman, D. Absorption and scattering of light by small particles Wiley-Interscience (1983).
Mertens, H. & A., P. Strong luminescence quantum-efficiency enhacement near prolate metal nanoparticles: dipolar versus higher-order modes. J. Appl. Phys. 105, 044302 (2009).
Curto, A. G. et al. Multipolar radiation of quantum emitters with nanowire optical antennas. Nat. Commun. 4, 1750 (2013).
Kern, A. M. & Martin, O. J. F. Surface integral formulation for 3d simulations of plasmonic and high permittivity nanostructures. J. Opt. Soc. Am. A 26, 732–740 (2009).
Bernal Arango, F. & Koenderink, A. F. Polarizability tensor retrieval for magnetic and plasmonic antenna design. New J. Phys. 15, 073023 (2013).
Sersic, I., van de Haar, M. A., Bernal Arango, F. & Koenderink, A. F. Ubiquity of optical activity in planar metamaterial scatterers. Phys. Rev. Lett. 108, 223903 (2012).
Jackson, J. D. Classical Electrodynamics John Wiley and Sons (1999).
Lukosz, W. & Kunz, R. E. Light emission by magnetic and electric dipoles close to a plane interface. J. Opt. Soc. Am. 67, 1607–1619 (1977).
Novotny, L. & Hecht, B. Nano-Optics Cambridge University press (2006).
Ribaric, M. & Sustersic, L. Expansions in terms of moments of time-dependent, moving charges and currents. SIAM J. Appl. Math. 55, 593624 (1995).
Taminiau, T. H., Karaveli, S., van Hulst, N. F. & Zia, R. Quantifying the magnetic nature of light emission. Nat. Commun. 3, 1984 (2012).
Langguth, L., Punj, D., Wenger, J. & Koenderink, A. F. Plasmonic band structure controls single molecule fluorescence. ACS Nano 7, 8840–8848 (2013).
Punj, D. et al. A plasmonic ‘antenna-in-box’ platform for enhanced single-molecule analysis at micromolar concentrations. Nat. Nanotechnol. 8, 512–516 (2013).
We would like to acknowledge Gijs Vollenbroek for sample fabrication. This work is part of the research programme of the ‘Stichting voor Fundamenteel Onderzoek der Materie (FOM)’, which is financially supported by the ‘Nederlandse Organisatie voor Wetenschappelijk Onderzoek (NWO)’. This work is part of NanoNextNL, a nanotechnology programme funded by the Dutch ministry of economic affairs. It is also supported by the European Research Council (ERC).
A.P. is co-founder and co-owner of Delmic BV, a startup company that develops a commercial product based on the ARCIS cathodoluminescence system that was used in this work.
About this article
Cite this article
Coenen, T., Bernal Arango, F., Femius Koenderink, A. et al. Directional emission from a single plasmonic scatterer. Nat Commun 5, 3250 (2014). https://doi.org/10.1038/ncomms4250
Light: Science & Applications (2021)
Deep subwavelength control of valley polarized cathodoluminescence in h-BN/WSe2/h-BN heterostructure
Nature Communications (2021)
Experimental demonstration of linear and spinning Janus dipoles for polarisation- and wavelength-selective near-field coupling
Light: Science & Applications (2019)
Nature Materials (2019)
Light: Science & Applications (2019)