Abstract
The development of a lithographic method that can rapidly define nanoscale features across centimetre-scale surfaces has been a long-standing goal for the nanotechnology community. If such a ‘desktop nanofab’ could be implemented in a low-cost format, it would bring the possibility of point-of-use nanofabrication for rapidly prototyping diverse functional structures. Here we report the development of a new tool that is capable of writing arbitrary patterns composed of diffraction-unlimited features over square centimetre areas that are in registry with existing patterns and nanostructures. Importantly, this instrument is based on components that are inexpensive compared with the combination of state-of-the-art nanofabrication tools that approach its capabilities. This tool can be used to prototype functional electronic devices in a mask-free fashion in addition to providing a unique platform for performing high-throughput nano- to macroscale photochemistry with relevance to biology and medicine.
Similar content being viewed by others
Introduction
The pace of development in many areas of nanotechnology, physics, electronics, chemistry and biology is determined by the availability of reliable pattern generation tools. Therefore, a long-standing goal in these communities is the realization of a desktop nanofabrication tool that combines low-cost and high-resolution patterning with high-throughput operation. Such a tool would revolutionize the field in a manner analogous to the way that the desktop printer has revolutionized information transfer. However, desktop nanofabrication remains a formidable challenge because direct write systems available today, such as those that employ electron beam lithography (EBL)1, near-field optical lithography2,3,4,5,6,7, zone plate array lithography8, dip-pen nanolithography9,10 and related molecular printing techniques11,12,13,14, impose tradeoffs between throughput, cost and feature size. The low cost and parallel nature of photolithography make it a promising candidate for desktop nanofabrication, but for this to be realized, diffraction-unlimited features must be attainable. There are many methods to circumvent the diffraction limit, including operating in the near-field regime15, utilizing two-photon processes16, incorporating plasmonic materials to locally enhance light17,18 and constructing superlenses from negative index of refraction materials19. One promising technique that utilizes near-field apertures to overcome the diffraction limit is beam pen lithography (BPL)6, in which apertures with sub-wavelength dimensions at the tip of each gold-coated elastomeric pen in a massive array are used to perform scanning near-field optical lithography. However, there are two major challenges that have prevented BPL from being transitioned into a legitimate desktop nanofabrication tool: (1) all pens in the array act in unison, making this technique useful only for generating replicas of patterns, and (2) apertures are either constructed serially using a focused ion beam or in parallel using a mechanical stripping technique that yields >500 nm pores.
Here, we report advances that address both of these issues and transform BPL into a real desktop tool capable of nanofabrication. This approach was made possible by combining BPL with a digital micromirror device such as those used in maskless lithography20,21 and developing a novel strategy for coordinating the light addressing each pen with the motion of the pen array (Fig. 1 and Supplementary Fig. S1). Once the light reaches the pen array, three structural aspects of the array6,22 enable it to effectively perform near-field lithography: (1) a rigid and transparent glass backing layer allows light to reach the pens while structurally supporting the pen array, (2) the mechanical compliance of the polydimethylsiloxane pens allows them to be in gentle simultaneous contact with the surface and (3) the opaque gold coating and nanoscale size of the apertures in the array allow for nanoscale confinement of light. Using the resulting tool, we have fabricated centimetre-scale arrangements of nanoscale features to illustrate the ability of this actuated BPL approach to function as a general desktop nanofab. This transformative combination preserves the high spatial resolution of near-field optical lithography while gaining the ability to independently control the patterns generated by each pen in a massive and parallel fashion, creating a unified tool for constructing and studying nanomaterials.
Results
Diffraction-unlimited nanopatterning
The sub-wavelength apertures at the tip of each probe of a BPL pen array are crucial to the operation of actuated BPL and must be fabricated in a parallel and uniform fashion to preserve the low cost and scalable nature of this process. In a typical experiment, polymer pen arrays are moulded from Si masters and coated with an opaque layer (see Methods). To fabricate small and uniform apertures at the tip of each probe, we utilized a variant of a method that combines dry and wet etching23 (Supplementary Fig. S2) to controllably fabricate apertures with diameters of 103±12 nm (Fig. 1b). This important advance in BPL pen array fabrication allows for massively parallel diffraction-unlimited writing.
As with any lithography system, it is important to establish the fundamental constitutive units from which patterns can be generated. In a typical experiment, a BPL pen array was mounted in a scanning probe lithography system and leveled with respect to a photoresist-coated Si wafer using an optical leveling procedure. To expose a region of the resist, the pens were brought into contact with the surface, and the back side of the pen array was illuminated with ultraviolet light with wavelength λ=405 nm while the array was held still for a specified exposure time. The sub-λ apertures block propagating light, and create an intensity profile that decays exponentially with distance from the aperture3,24. To optimize the exposure time, a dose test was performed in which the pen array wrote a series of dots (Fig. 2a) with exposure times between 2 and 4 s. At an effective exposure dose of 2 s, the dot features had an average diameter of 122±12 nm, which is substantially smaller than λ/2, demonstrating diffraction-unlimited performance. At longer exposure times, larger features were written, demonstrating control over feature size with exposure dose (Fig. 2b)15. In contrast to writing dots with the pens held still, moving the pens at a constant velocity across the sample while in contact allows one to write lines. Au lines with widths of 380±19, 842±17, 1,170±20 and 1,530±20 nm were written by scanning the tip array at 4, 2, 1 and 0.5 μm s−1, respectively. In these experiments, the structures written by the pens were visualized by scanning electron microscopy after they had been coated with 5 nm of Cr and 25 nm of Au in a standard lift-off process. Interestingly, the root-mean-square line edge roughness of these features was 30 nm, highlighting the ability of actuated BPL to write high-quality lines.
Large-area arbitrary nanolithography
Having established the core structures that actuated BPL can be used to write, we explored the potential of using its massively parallel and individually addressable nature to generate centimetre-scale arbitrary patterns composed of nanoscale features. The lithographic procedure entailed sequentially moving the pen array through an array of points on the sample while the digital micromirror device displayed images extracted from a master image. To achieve registry between the projected image and the pens, a novel alignment procedure (Supplementary Fig. S3) and custom software were used (Supplementary Fig. S4). To evaluate whether this technique could be used to generate centimetre-scale patterns composed of nanoscale features, a 8,100 pen array was used to generate a mosaic map of the world (Fig. 3a) wherein each tile of the world image (Fig. 3c) was a bitmap depicting the structure of a unique molecule from the PubChem database (for the high-resolution master image, see Supplementary Fig. S5). Importantly, this pattern was chosen to highlight the multiscale nature of patterning as the macroscale pattern (the map of the world) is composed of microscale objects (chemical formulae), which are in turn entirely composed of nanoscale dot features. The final pattern consists of 1.3 million dot features arranged to define 900 molecular structures in a 9 × 9 mm2 area. In order to differentiate between molecules in the ‘land’ and ‘ocean’ regions of the world map, the exposure dose used to define the points in the land regions was twice that of the points in the ocean regions. After gold deposition and resist lift-off, the pattern consisted of 144±11 nm average diameter dot features in the regions corresponding to ocean (Fig. 3d) and 750±22 nm average diameter dot features written in the regions corresponding to land (Fig. 3c), all with a 1 μm pitch, demonstrating high quality control of light over the macro- to nanoscale. It is important to note that both the large and small features were written in the same experiment through control of the fraction of the total time that each mirror was activated. This pattern contains features that are too small to be fabricated using conventional optical techniques; it would be necessary to use EBL to even attempt to write such a pattern.
As many example applications for which this tool would be useful require line features in addition to dot features, it is necessary to evaluate whether actuated BPL can be used to write large-area arbitrary patterns consisting of lines with sub-wavelength dimensions. To probe this, a patterning experiment was performed in which each probe was directed to write a 10 × 10 μm2 resistor or capacitor at high resolution (50 nm pitch between points) and subsequently connect these elements together with a network of wires written in a 100 × 100 μm2 region at low resolution (500 nm pitch between points). The result is a continuous network of ~2-μm-wide lines that span the entire surface (Fig. 3e) and connect an array of circuit elements comprised of 120±35-nm-wide wires (Fig. 3f–i). This pattern design was chosen as a proof-of-concept to mimic the architecture of small devices connected by larger interconnects commonly found in integrated circuits.
Fabrication of functional devices
The capabilities of actuated BPL were further evaluated by attempting to pattern functional circuits whose performance would be an indicator of successful patterning. To this end, arrays of Au serpentine resistors with varying lengths were fabricated on a Si wafer using actuated BPL (Fig. 4a). All resistors required the coordination of multiple pens with the largest requiring 15 pens and consisting of a 4-mm-long, 2-μm-wide continuous wire. Current–voltage characterization of 61 simultaneously patterned devices revealed that all measured devices exhibited Ohmic behaviour with resistances that depended linearly on the programmed line length (Fig. 4b). The sheet resistance of the resistors was computed by determining the slope of the linear fit and used to a sheet resistance of 0.32 Ω per square, in agreement with the tabulated value of 0.4 Ω per square for 50-nm-thick gold25. Furthermore, planar capacitors, inductors and surface acoustic wave (SAW) transducers were also patterned (Fig. 4c). It required 57 pens to write each capacitor, 51 pens to write each inductor and 110 pens to generate a pair of SAW transducers. To verify the function of the SAW transducers, they were combined with radio frequency amplifiers (Supplementary Fig. S6) to form a delay line oscillator26,27 whose resonance frequency of 11.9 MHz matches very well with the theoretical prediction of 12.3 MHz (Fig. 4d).
Patterning in registry with existing nanostructures
While piezoelectric control over the sample position allows features to be written with exceptionally high control over their position relative to one other, for many applications it is also necessary to generate patterns that are aligned to existing structures on a surface. To evaluate the potential of actuated BPL to pattern in registry with existing patterns, 150-nm-diameter semiconductor nanowires were dispersed on a silicon wafer with electrical contact pads and fiducial marks, imaged by optical microscopy (Supplementary Fig. S7), and spin-coated with photoresist. Actuated BPL was then used to make electrical connection to the randomly dispersed nanowires by patterning electrical leads designed for this arrangement of nanowires (Supplementary Fig. S8) after aligning the BPL pen array to the alignment marks on the sample, and writing the pattern (Fig. 5a). In this experiment, an array consisting of 729 (27 × 27) pens was used to write connections to 60 wires that had been located by optical microscopy. Patterning of this type, traditionally done by EBL1, shows how actuated BPL can be used to rapidly pattern in a mask-free fashion with registry to existing nanostructures. The success of this task was evaluated by measuring the number of patterned connections (59/60) and working devices after the lift-off process (40/60) (Fig. 5b). Finally, the electrical transport of the nanowire structures exhibited clear semiconducting behaviour (Fig. 5c), as one would expect for a working device.
Discussion
Taken together, these data provide evidence for the first true desktop nanofabrication tool based upon easily fabricated BPL pen arrays, a novel strategy of actuation and a relatively simple scanning probe platform. This is the first such tool to allow one to rapidly generate structures of interest that span the macro-, micro- and nanoscales all in one experiment. The unique cantilever-free architecture makes this possible as light can be independently guided down the microscopic pyramid backing of each pen and confined through the nanoscale apertures in a high-throughout and high-yield fashion. Here, we show that features with sizes spanning 120 nm to several micrometres can be easily generated in a mask-free and scalable fashion; however, it is important to emphasize that these results represent only a proof-of-concept demonstration and not the fundamental limitation of the technique. For example, smaller apertures should enable sub-100 nm features5 and improved engineering could enable writing speeds up to 2 mm2 s−1 (Supplementary Methods). It is also worth noting that in addition to rapid prototyping applications in industrial or academic settings, this technique will also enable controlled light-mediated synthesis in localized spaces, which is becoming increasingly important in chemistry and biology.
Methods
Pen array fabrication
BPL pen arrays were fabricated starting with PPL pen arrays whose fabrication is described elsewhere6,11. The pen arrays were coated with 5 nm of Ti followed by 200 nm of Au to make them opaque, and then spin-coated with poly(methyl methacrylate) (PMMA 950 c7, MicroChem Inc., USA). Following coverage of the array, reactive ion etching was employed to isotropically etch the PMMA until the apexes of the pens were exposed. Subsequently, the gold at the apex of each pen was removed through a selective chemical etch (Gold Etchant TFA, Transense Company Inc., USA), leaving an aperture at the tip of each pen in the array. Residual PMMA was removed by rinsing in acetone.
Lithographic procedure
Si wafers with 500 nm of thermal oxide were spin-coated with lift-off resist (LOR Series, MicroChem Inc.) followed by S1805 (MicroChem Inc.) or AZ 1505 photoresist (MicroChemicals GmbH, Germany). Samples were then mounted in the actuated BPL apparatus and leveled following an optical leveling procedure. Patterns were then exposed in a frame-by-frame manner and subsequently developed in MF24A (MicroChem Inc.). Typically, 5 nm Cr and 15 nm Au were evaporated onto the sample followed by an overnight lift-off in Remover PG (MicroChem Inc.). Final patterns were characterized using atomic force microscopy (Dimension Icon, Bruker, USA), optical microscopy (Axiovert, Zeiss, USA) and scanning electron microscopy (S-4800-II and SU8030, Hitachi, Japan).
Additional details
The Supplementary Methods contains further details regarding the actuated BPL apparatus, the fabrication of BPL pen arrays, the alignment procedure used to align the projected light to the BPL pen arrays, the software control of actuated BPL and the general lithography procedure used to generate patterns. In addition, further details are provided regarding the design and testing of the SAW delay line oscillator and the nanowire connection procedure.
Additional information
How to cite this article: Liao, X. et al. Desktop nanofabrication with massively multiplexed beam pen lithography. Nat. Commun. 4:2103 doi: 10.1038/ncomms3103 (2013).
References
Vieu, C. et al. Electron beam lithography: resolution limits and applications. Appl. Surf. Sci. 164, 111–117 (2000).
Betzig, E. & Trautman, J. K. Near-field optics: microscopy, spectroscopy, and surface modification beyond the diffraction limit. Science 257, 189–195 (1992).
Novotny, L., Pohl, D. W. & Regli, P. Light propagation through nanometer-sized structures: the two-dimensional-aperture scanning near-field optical microscope. J. Opt. Soc. Am. A 11, 1768–1779 (1994).
Smolyaninov, I. I., Mazzoni, D. L. & Davis, C. C. Near-field direct-write ultraviolet lithography and shear force microscopic studies of the lithographic process. Appl. Phys. Lett. 67, 3859–3861 (1995).
Sun, S. & Leggett, G. J. Matching the resolution of electron beam lithography by scanning near-field photolithography. Nano Lett. 4, 1381–1384 (2004).
Huo, F. et al. Beam pen lithography. Nat. Nanotech. 5, 637–640 (2010).
Haq, E. u. et al. Parallel scanning near-field photolithography: the snomipede. Nano Lett. 10, 4375–4380 (2010).
Chao, D., Patel, A., Barwicz, T., Smith, H. I. & Menon, R. Immersion zone-plate-array lithography. J. Vac. Sci. Technol. B 23, 2657–2661 (2005).
Piner, R. D., Zhu, J., Xu, F., Hong, S. & Mirkin, C. A. ‘Dip-Pen’ nanolithography. Science 283, 661–663 (1999).
Salaita, K., Wang, Y. & Mirkin, C. A. Applications of dip-pen nanolithography. Nat. Nanotech. 2, 145–155 (2007).
Huo, F. et al. Polymer pen lithography. Science 321, 1658–1660 (2008).
Giam, L. R. & Mirkin, C. A. Cantilever-free scanning probe molecular printing. Angew. Chem. Int. Ed. 50, 7482–7485 (2011).
Braunschweig, A. B., Huo, F. & Mirkin, C. A. Molecular printing. Nat. Chem. 1, 353–358 (2009).
Shim, W. et al. Hard-tip, soft-spring lithography. Nature 469, 516–520 (2011).
Leggett, G. J. Light-directed nanosynthesis: near-field optical approaches to integration of the top-down and bottom-up fabrication paradigms. Nanoscale 4, 1840–1855 (2012).
Tanaka, T., Sun, H.-B. & Kawata, S. Rapid sub-diffraction-limit laser micro/nanoprocessing in a threshold material system. Appl. Phys. Lett. 80, 312–314 (2002).
Srituravanich, W. et al. Flying plasmonic lens in the near field for high-speed nanolithography. Nat. Nanotech. 3, 733–737 (2008).
Pan, L. et al. Maskless plasmonic lithography at 22 nm resolution. Sci. Rep. 1, 175 (2011).
Zhang, X. & Liu, Z. Superlenses to overcome the diffraction limit. Nat. Mater. 7, 435–441 (2008).
Sun, C., Fang, N., Wu, D. M. & Zhang, X. Projection micro-stereolithography using digital micro-mirror dynamic mask. Sens. Actuators A 121, 113–120 (2005).
Ryoo, H., Kang, D. W. & Hahn, J. W. Analysis of the line pattern width and exposure efficiency in maskless lithography using a digital micromirror device. Microelectron. Eng. 88, 3145–3149 (2011).
Qin, D., Xia, Y. & Whitesides, G. M. Elastomeric light valves. Adv. Mater. 9, 407–410 (1997).
Huan, H. et al. Nano-fabrication with a flexible array of nano-apertures. Nanotechnology 23, 175303 (2012).
Hecht, B. et al. Scanning near-field optical microscopy with aperture probes: fundamentals and applications. J. Chem. Phys. 112, 7761–7774 (2000).
CRC Handbook of Chemistry and Physics 93rd edn (ed. Haynes, W. M.)12–41CRC Press/Taylor and Francis (2012).
Slobodnik, A. J. Jr. Surface acoustic waves and SAW materials. Proc. IEEE 64, 581–595 (1976).
Wohltjen, H. & Dessy, R. Surface acoustic wave probe for chemical analysis. I. Introduction and instrument description. Anal. Chem. 51, 1458–1464 (1979).
Acknowledgements
This material is based upon work supported by DARPA/MTO Award N66001-08-1-2044, AOARD Award FA2386-10-1-4065, AFOSR Awards FA9550-12-1-0280 and FA9550-12-1-0141, NSF Awards DBI-1152139 and DMB-1124131, DoD/NPS/NSSEF Fellowship Awards N00244-09-1-0012 and N00244-09-1-0071, Chicago Biomedical Consortium with support from Searle Funds at The Chicago Community Trust and CCNE initiative of NIH Award U54 CA151880. Any opinions, findings, and conclusions or recommendations expressed in this publication are those of the authors and do not necessarily reflect the views of the sponsors. K.A.B. and X.L. gratefully acknowledge support from Northwestern University’s International Institute for Nanotechnology.
Author information
Authors and Affiliations
Contributions
X.L., K.A.B. and C.A.M designed all experiments. X.L., K.A.B. and C.A.M contributed to this work in analysing results and drafting the manuscript. A.L.S., G.L., S.H. and W.S. also performed experiments and helped with revisions.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures S1-S8 and Supplementary Methods (PDF 1194 kb)
Rights and permissions
About this article
Cite this article
Liao, X., Brown, K., Schmucker, A. et al. Desktop nanofabrication with massively multiplexed beam pen lithography. Nat Commun 4, 2103 (2013). https://doi.org/10.1038/ncomms3103
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms3103
This article is cited by
-
Massively parallel direct writing of nanoapertures using multi-optical probes and super-resolution near-fields
Microsystems & Nanoengineering (2022)
-
Massively parallel cantilever-free atomic force microscopy
Nature Communications (2021)
-
Dip-Pen Nanolithography(DPN): from Micro/Nano-patterns to Biosensing
Chemical Research in Chinese Universities (2021)
-
Near-field sub-diffraction photolithography with an elastomeric photomask
Nature Communications (2020)
-
Polymer brush hypersurface photolithography
Nature Communications (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.