Control of magnetism by applied voltage is desirable for spintronics applications. Finding a suitable material remains an elusive goal, with only a few candidates found so far. Graphene is one of them and attracts interest because of its weak spin–orbit interaction, the ability to control electronic properties by the electric field effect and the possibility to introduce paramagnetic centres such as vacancies and adatoms. Here we show that the magnetism of adatoms in graphene is itinerant and can be controlled by doping, so that magnetic moments are switched on and off. The much-discussed vacancy magnetism is found to have a dual origin, with two approximately equal contributions; one from itinerant magnetism and the other from dangling bonds. Our work suggests that graphene’s spin transport can be controlled by the field effect, similar to its electronic and optical properties, and that spin diffusion can be significantly enhanced above a certain carrier density.
Electric field control of magnetic properties has been the subject of considerable attention, with a few materials and hybrid magnetic systems found recently, where it is possible to control the magnetization direction and/or the Curie temperature1,2,3. Electric field tunability is one of the fundamental properties of graphene and has been widely used to control its electronic, optical and other properties related to the electronic structure4. On the other hand, graphene is believed to be an ideal material for spintronics5 because of the weak spin–orbit interaction and long spin relaxation lengths6,7 and the possibility to introduce paramagnetic centres via controlled introduction of defects, as recent experiments8,9 have shown that both vacancies and adatoms in graphene carry magnetic moments μ≈μB. In principle, the latter is not exceptional because defects and impurities in crystals without any d or f elements may have unpaired electrons and, therefore, exhibit paramagnetism10,11. However, achieving ferromagnetic alignment between these unpaired spins has proven practically impossible10. In graphene, the prospect of defect ferromagnetism is more realistic because, first, the presence of conduction electrons provides a medium for coupling between localized spins and, second, the defect-induced moments are believed to be due to the same π electrons that are responsible for electron transport12,13,14,15,16,17,18,19,20,21. Accordingly, it should be possible to use the electric-field effect to control not only the coupling between localized magnetic moments in graphene but also the presence of the moments themselves which so far has not been possible in other materials.
In this contribution, we have employed Superconducting Quantum Interference Device (SQUID) magnetometry and molecular doping to investigate graphene’s paramagnetism. We have found that magnetic moments due to vacancies and adatoms can be switched off by shifting the Fermi energy EF above ≈0.45 eV and then switched back on by returning to the neutral state or lower EF. This proves the itinerant nature of magnetic moments in graphene, that is, π magnetism. The localization radius rL for the itinerant spins is estimated as ≈2.0 nm. For the case of vacancies, we find them carrying two practically independent moments that are attributed to the π magnetism and an unpaired spin on broken bonds. Only half of vacancy magnetism can be switched off by doping. A profound implication of our findings is that π magnetism can be controlled by other means, notably by the electric field doping within realistically accessible carrier densities n≈2 × 1013 cm−2. Furthermore, it is likely that the unexpectedly quick spin relaxation found in graphene devices and attributed to magnetic defects22 can be quenched by doping above the above threshold.
Magnetic response of graphene with vacancies
Our samples were graphene laminates that were shown8 to be a well-characterized, clean reference system, providing enough material (typically, several mg of graphene) for SQUID magnetometry. Our magnetometer (Quantum Design MPMS XL7) allowed measurements at temperatures T between 300 and 1.8 K in fields H up to 7T. The samples were irradiated with 350 keV protons to achieve the desired density of single vacancies, nv (Methods). Irradiation resulted in a pronounced paramagnetic response arising from non-interacting moments8. Typical magnetization curves are shown in Fig. 1. For all vacancy concentrations, such curves were accurately described by the Brillouin function with spin S=1/2. The measured magnetic moment M was found to be proportional to nv as M, where μB is the Bohr magneton and NS is the number of spins extracted from Brillouin function fits, in agreement with the earlier report8.
Control of carrier concentration in graphene laminates
To probe the evolution of M as the valence (conduction) band gets progressively filled up with holes (electrons), we varied the carrier concentration by using molecular doping: nitric acid (HNO3) or NO2 gas as hole dopants23,24,25 and aniline as an electron dopant26. The properties of HNO3 and NO2 as acceptors were investigated both theoretically24 and experimentally23,25, and both were shown to be very effective, with each physisorbed molecule resulting in transfer of one electron25 (see Methods for details). However, finding an effective donor turned out to be problematic. Aniline is reported as one of the best donors but the maximum doping it allowed was only n≈5 × 1012 cm−2. Within the limited range of n achievable for aniline, we have found no difference with respect to hole doping with HNO3 and, therefore, focus below on the latter results.
Effect of doping on magnetization of irradiated graphene
Figure 1 shows the evolution of M(H) curves for one of the irradiated samples as it is doped from a nearly neutral state to EF ≈0.5 eV. It is clear that the doping has a strong effect on magnetization: M reduces to half its initial value, even though all M(H) curves look qualitatively the same and are accurately described by the Brillouin function with S=1/2. This indicates a reduction in the number of magnetic moments for the same number of vacancies. It also shows that high n do not lead to stronger interaction, as the vacancy magnetic moments remain noninteracting. This behaviour was found to be universal, even though nv varied for different samples by more than an order of magnitude, with the average separation between vacancies changing from ~3 to 10 nm. Figure 2 shows the evolution of the number of detected spins NS in two graphene samples with different nv as a function of EF. Initially, NS is gradually decreasing with increasing the hole concentration, but at EF≈0.4 eV, it falls sharply and seems to saturate to NS≈NS0/2 at the maximum doping, where NS0 is the number of spins before doping. As soon as the dopants were removed from graphene by mild annealing, M recovered its initial value, that is, the effect is fully reversible (Fig. 2).
EF ≈0.54 eV was the maximum doping that we were able to achieve with HNO3, in agreement with the calculated energy dependence of the density of states (DOS) for the NO2 molecule adsorbed on graphene24. The data scatter between different samples and doping levels does not allow us to follow the transition in Fig. 2 in more detail and confirm the apparent saturation to half magnetization above EF≈0.45 eV. However, this behaviour was observed for many samples and repeatedly after annealing cycles. To gain further insight, Fig. 3 plots the reduction in magnetization signal at maximum doping, which was measured for several samples with different vacancy densities. It is clear that, independent of the sample and its NS0, the 50% reduction in M is universal, as long as the Fermi level is shifted sufficiently away from the neutrality point.
We attribute this finding to the presence of two types of magnetic moments associated with a vacancy, and only one of them is being affected by such a shift in EF. Indeed, let us recall the origin of defect-induced magnetism in graphene. It lies in the imbalance that the defects create between its two sublattices and the resulting appearance of localized π states with energy close to the Dirac point12,13,14,15,16,17,18,19,20,21. As long as these states are singly occupied, due to Coulomb repulsion, UC, they give rise to magnetic moments μ=1μB. This simple picture is expected for adatoms, such as fluorine or hydrogen, whereas for vacancies the origin of magnetic moments is more complex. In addition to the above π moments, there are dangling σ bonds that can have some role too14,16,18,19,20,21. For example, vacancies in insulating boron nitride are expected to be magnetic27. The relative contribution of σ states to vacancy magnetism is unknown and a matter of debate18,20. Because of high chemical reactivity of the dangling bonds, it is often assumed that they are saturated with, for example, hydrogen and therefore do not contribute to magnetism (see, for example, Palacios and Yndurain18 and Nanda et al.21). Then, the magnetic moment is purely due to itinerant (conduction) electrons. Another possible scenario is a vacancy reconstruction and the associated Jan–Teller distortion that results in hybridization between the π and σ states14,19,20,21. Depending on the degree of hybridization, the magnetic moment for a vacancy has been predicted to be between ~1.45 and 2 μB14,16,19,21 (refs14,16,19,21).
Our experiment suggests an intermediate scenario in which the dangling bonds remain unsaturated and the hybridization does not have a significant role. In this case, each vacancy is expected to provide two independent contributions, which come from the singly occupied localized π state and the unsaturated σ bond. At sufficiently large doping, such that |EF|≥UC, the localized π state becomes doubly occupied and the corresponding magnetic moment disappears, whereas the unpaired σ electron remains unaffected by doping and provides the residual M. Because the two contributions appear to be nearly equal, hybridization between the two electronic states should be weak. This is also in agreement with the measured S=1/2. Note that it would require unrealistically high doping to occupy the σ state and fully suppress the vacancy magnetism.
To support the above interpretation, a neat experiment would be to compare the effect of doping on vacancy magnetism with that for adatoms, where there are no dangling bonds and only localized π states are expected13,14,15. However, it has proven difficult experimentally to introduce adatoms without their significant clustering. The latter locally opens a band gap, quenches nearest-neighbour magnetic moments and so on, so that the system can no longer be considered as graphene but becomes its chemical derivative8. We have circumvented this problem by exploiting the experimental fact that if graphene is heated at ≥350 °C, it results in the appearance of so-called resonant scatterers28,29,30,31. They reduce graphene’s electronic quality and result in the D peak in Raman spectra. The scatterers are attributed to some organic residue that is always present on graphene and strongly (sp3) bonds to it at high T28. Resonant scatterers is another name for the localized π states near the Dirac point in the context of electron transport. With these earlier studies in mind, we annealed several samples of pristine (nonirradiated) graphene laminates at 350 °C in Ar–H2 atmosphere. This induced notable paramagnetism with NS0≈3 × 1018 g−1. The observed M(H) curves were practically identical to those of irradiated laminates and, again, are accurately described by the Brillouin function with S=1/2. The found NS0 corresponds to 2–3 sp3 bonds induced by annealing per each graphene crystallite in the laminates.
In contrast to vacancy magnetism, the exposure of these sp3-defected samples to HNO3 resulted in an almost complete disappearance of the paramagnetic signal above the same EF ≈0.45 eV (Fig. 4), in agreement with expectations for the purely itinerant nature of sp3 magnetism. Similar to the case of vacancies, the switching effect is also fully reversible: as soon as HNO3 molecules were removed by mild annealing at ~100 °C, the paramagnetic signal recovered its initial value NS0.
The magnetic moment due to sp3 impurities and its variation with doping can be calculated analytically using the expression:
which describes the DOS in graphene due to resonant scatterers such as sp3 adsorbates (see Supplementary Note 1). Here, Ed is the states’ energy position and a the hybridization parameter, both in units of the half width W≈3t of graphene’ energy band (t is the nearest-neighbour hopping parameter). For sp3 impurities relevant to our experiment (monovalent organic groups or hydrogen adatoms), Ed=0.02 and a=2/3 (that is, hybridization strength ≈2t)31. The magnetic moment (number of spins) is given by the fraction of singly occupied impurity states, which is determined by the Hubbard energy U and can be found by integrating equation (1) over the occupied states:
Using equation (2), we obtained the NS(EF) shown in Fig. 4, which effectively has only one fitting parameter, U, because the dependence is found to be qualitatively insensitive to Ed and a over a wide range of the parameters (the best-fitting value of U as in Fig. 4 is U=0.5 eV). NS drops sharply at EF≈U as expected, exhibiting a cusp-like dependence 1/ln|EF−U|. Note that the cut off does not lead to zero magnetization, which seems surprising but is in agreement with the experiment. The reason for a finite remaining NS on the theoretical curve is that the DOS deviates significantly from the standard Lorentzian peak. This arises due to the linear increase in the DOS of conduction electrons in graphene and a renormalization of the positions of impurity states because of hybridization. As a result, N(E) decays as 1/|E|ln2|E| at large E, much slower than the standard 1/E2 dependence for the Lorentz distribution. This means that the magnetic states become totally doubly occupied only for EF>>U and, therefore, NS exhibits a long tail at higher EF such as in Fig. 4.
Finally, let us add several comments. First, the found value of the Coulomb energy U=0.5 eV allows us to estimate the spatial localization rL of the π states as rL≈2.0 nm (using the known effective Coulomb interactions in graphene32), that is, the π state is localized over several benzene rings, in agreement with theory13,14,16. Second, comparing the nearly constant NS at EF<0.3 eV for sp3 impurities in Fig. 4 (both theory and experiment) with gradually decreasing NS for vacancies indicates that the magnetic moment is sensitive to the shape of the DOS peak: the latter is much broader for vacancies14 resulting in a more gradual decrease of NS in equation (2), in agreement with experiment. Third, an alternative mechanism for quenching of the magnetic moments at high n could be the Kondo effect17,20. However, the observed cumulative contribution from localized and itinerant moments and their T dependence (Supplementary Figs S3 and S4) do not support this scenario (see Supplementary Note 2). Fourth, the discussed threshold doping is achievable in field-effect devices with high-quality gate dielectrics such as boron nitride. This should allow strong suppression of the rapid spin relaxation, characteristic to the existing graphene devices, so that spin currents can be efficiently switched on and off by gate voltage as required for a spin transistor operation.
Preparation of irradiated graphene laminates
Our graphene samples were prepared as described in Nair et al.8 In brief, we used ultrasonic cleavage of highly oriented pyrolytic graphite in an organic solvent, N-methylpyrrolidone, following the procedure described in Sepioni et al.33 The resulting laminates consist of predominantly 30–50 nm crystallites, aligned parallel to each other and electronically decoupled8. During filtration of the graphene suspension in N-methylpyrrolidone, the crystallites do not re-stack into graphite but remain rotationally disordered, with the average separation between graphene flakes ≈0.36 nm, significantly larger than the interplane distance in graphite. Vacancies were introduced by proton irradiation in a 500-kV ion implanter, at room temperature T and current density <0.2 μA cm−2. The energy (between 350–400 keV), fluence (1.2–11 × 1015 cm−2) and other irradiation parameters for each sample were chosen to achieve a desired defect density and ensure uniformity of defect distribution8. Proton irradiation under such conditions produces predominantly single vacancies12; their number for each sample was estimated on the basis of the corresponding fluence, surface area and the number of defects created by each proton as obtained from computer simulations (SRIM software package). Further details can be found in Nair et al.8 We note that impacts of energetic protons on graphene may also give rise to a finite concentration of other defects, such as divacancies and carbon adatoms, but their effect on magnetism is negligible, as the former do not possess magnetic moment and the latter are mobile at room temperature and tend to cluster with the loss of magnetism34.
In our SQUID measurements, the field was usually applied parallel to the lamination direction to avoid diamagnetism that is strong in the perpendicular field8. A small remnant diamagnetic background due to some misalignment was linear with H up to 7T at all T and subtracted for clarity from the plotted data.
Molecular doping and determination of carrier concentrations
Molecular doping has been shown to be an effective way of changing carrier concentration in graphene, with water, NO2 gas and HNO3 identified as acceptors (hole dopants) and ammonia, anisole, aniline and N,N,N′,N′-tetramethyl-p-phenylenediamine (TMPD) as donors (electron dopants)23,25,26,35,36,37,38,39. After testing the above molecules on graphene laminates, HNO3 was found to be the only molecule providing sufficiently high carrier concentrations, n (up to n≈2 × 1013 cm−2, see below), excellent stability (n remained same for several weeks) and uniform distribution (as manifested in same n measured in different locations on graphene laminates). To achieve gradual changes in n, the laminates were exposed to HNO3 diluted with water at different molar concentrations of 0.1–15 M. The maximum doping level that we could achieve corresponded to n≈2 × 1013 cm−2 or . Importantly, once exposed to HNO3, the carrier concentration remained stable for many days at room T, in agreement with relatively high adsorption energy for this molecule23 but recovered the initial value under mild annealing in argon.
Gaseous NO2 produced qualitatively similar results (in terms of both measured n and the effect on magnetization), but the doping level was difficult to control and showed significant nonuniformity. Ammonia did not produce any measurable permanent changes in n, presumably because of the difficulty in diffusing ammonia molecules between graphene layers and also much smaller adsorption energy compared with NO238 (ref. 38). The only donor that produced systematic changes in n was aniline36, but the maximum possible n was small (~5 × 1012 cm−2) and resulted in only a small reduction in paramagnetic magnetization, similar to the effect of hole doping at such n. Another known electron dopant N,N,N′,N′-tetramethyl-p-phenylenediamine (TMPD)39 was found to exhibit weak paramagnetism of its own and, therefore, was avoided.
To monitor the changes in n, we used Hall effect measurements (see Supplementary Fig. S1). They were done on 3 × 3 mm2 samples cut out of a 2-cm diameter laminate obtained after filtration. The concentration was calculated as n=I·B/(VH·e·Nl), where I is the applied current, B is the magnetic field, VH is the Hall voltage and Nl is the number of graphene layers in the laminate. The latter was calculated from the measured sample thickness, typically 3–5 μm, and the average separation between the layers d ≈0.36 nm, as determined using X-ray diffraction.
In addition to the Hall measurements, we used Raman spectroscopy that is also sensitive to n25,40,41 (refs 25,40,41). Raman measurements were carried out using a Renishaw spectrometer with a green laser. As graphene crystallites in the laminates are small (typically 30–50 nm), they produce a significant broadening of all Raman peaks, which makes it difficult to detect exact shifts in their positions that would otherwise yield n. Therefore, we used graphene mechanically exfoliated onto Si/SiO2 and treated these samples in parallel with graphene laminates used for the Hall and magnetization measurements. Raman spectroscopy on such isolated samples was found to be sufficiently sensitive to detect changes in n even for small changes in HNO3 concentration.
Examples of Raman spectra after exposure to different concentrations of HNO3 are shown in Supplementary Fig. S2. We examined the shift and intensity variations of the G peak that is most sensitive to n25,40,41. The changes were translated into n by using the calibration data for gated graphene41. The absence of the D peak either before or after exposure to HNO3 (not shown) confirmed that HNO3 molecules were physisorbed on graphene and not chemisorbed, as the D peak is known to be a measure of short-range defects such as sp3 bonds42. Corresponding Fermi energies for each n were calculated using the relation EF=(πn)1/2ħ vF, where vF=1.1 × 106 ms−1 is the Fermi velocity. We emphasize that the results, shown in Supplementary Fig. S2, are in good agreement with the concentrations obtained from our Hall measurements for the same exposure to HNO3.
As a further check, we also measured Raman spectra directly on graphene laminates at high doping (HNO3 concentrations of 11–15 M), where the shift in the G peak position was sufficiently large (peak at 1600–1605, cm−1) to overcome the broadening effect. Again, the results were consistent with the Hall measurements and with the values of n obtained from the Raman spectra on exfoliated monolayers. For these particular measurements, the extracted values of n were in a range of 1–2 × 1013 cm−2.
How to cite this article: Nair, R. R. et al. Dual origin of defect magnetism in graphene and its reversible switching by molecular doping. Nat. Commun. 4:2010 doi: 10.1038/ncomms3010 (2013).
Ohno, H. et al. Electric-field control of ferromagnetism. Nature 408, 944–946 (2000).
Shiba, D. et al. Electrical control of the ferromagnetic phase transition in cobalt at room temperature. Nat. Mater. 10, 853–856 (2011).
Shiota, Y. et al. Induction of coherent magnetization switching in a few atomic layers of FeCo using voltage pulses. Nat. Mater. 11, 39–43 (2012).
Geim, A. K. Graphene: status and prospects. Science 324, 1530–1534 (2009).
Pesin, D. & MacDonald, A. H. Spintronics and pseudospintronics in graphene and topological insulators. Nat. Mater. 11, 409–416 (2012).
Tombros, N. Jozsa, C. Popinciuc, M. Jonkman, H. T. & van Wees, B. J. Electronic spin transport and spin precession in single graphene layers at room temperature. Nature 448, 571–574 (2007).
Józsa, C. Popinciuc, M. Tombros, N. Jonkman, H. T. & van Wees, B. J. Controlling the efficiency of spin injection into graphene by carrier drift. Phys. Rev. B 79, 081402(R) (2009).
Nair, R. R. et al. Spin-half paramagnetism in graphene induced by point defects. Nat. Phys. 8, 199–202 (2012).
McCreary, K. M. Swartz, A. G. Han, W. Fabian, J. & Kawakami, R. K. Magnetic moment formation in graphene detected by scattering of pure spin currents. Phys. Rev. Lett. 109, 186604 (2012).
Blundell, J. & Pratt, F. L. Organic and molecular magnets. J. Phys.: Condens. Matter 16, R771–R828 (2004).
Schlager, H. G. & Löhneysen, H. V. Susceptibility of local magnetic moments in phosphorus-doped silicon near the metal-insulator transition. Europhys. Lett. 40, 661–666 (1997).
Lehtinen, P. O. Foster, A. S. Ma, Y. Krasheninnikov, A. V. & Nieminen, R. M. Irradiation-induced magnetism in graphite: a density-functional study. Phys. Rev. Lett. 93, 187202 (2004).
Pereira, V. M. Guinea, F. Lopes dos Santos, J. M. B. Peres, N. M. R. & Castro Neto, A. H. Disorder induced localized states in graphene. Phys. Rev. Lett. 96, 036801 (2006).
Yazyev, O. V. & Helm, L. Defect-induced magnetism in graphene. Phys. Rev. B 75, 125408 (2007).
Uchoa, B. Kotov, V. N. Peres, N. M. R. & Castro Neto, A. H. Localized magnetic states in graphene. Phys. Rev. Lett. 101, 026805 (2008).
Palacios, J. J. Fernández-Rossier, J. & Brey, L. Vacancy-induced magnetism in graphene and graphene ribbons. Phys. Rev. B 77, 195428 (2008).
Haase, P. Fuchs, S. Pruschke, T. Ochoa, H. & Guinea, P. Magnetic moments and Kondo effect near vacancies and resonant scatterers in graphene. Phys. Rev. B 83, 241408 (2011).
Palacios, J. J. & Yndurain, F. Critical analysis of vacancy-induced magnetism in monolayer and bilayer graphene. Phys. Rev. B 85, 245443 (2012).
Santos, E. J. G. Riikonen, S. Sánchez-Portal, D. & Ayuela, A. Magnetism of single vacancies in rippled graphene. J. Phys. Chem. C 116, 7602–7606 (2012).
Cazalilla, M. A. Iucci, A. Guinea, F. & Castro Neto, A. H. Local moment formation and Kondo effect in defective graphene. Preprint arXiv 1207, 3135 (2012).
Nanda, B. R. K. Sherafati, M. Popovíc, Z. S. & Satpathy, S. Electronic structure of the substitutional vacancy in graphene: density-functional and Green’s function studies. New J. Phys. 14, 083004 (2012).
Lundberg, M. B. Yang, R. Renard, J. & Folk, J. A. Defect-mediated spin relaxation and dephasing in graphene. Phys. Rev. Lett. 110, 156601 (2013).
Bae, S. et al. Roll-to-roll production of 30-inch graphene films for transparent electrodes. Nat. Nanotechnol. 5, 574–578 (2010).
Wehling, T. O. et al. Molecular doping of graphene. Nano Lett. 8, 173–177 (2008).
Crowther, A. C. et al. Strong charge-transfer doping of 1 to 10 layer graphene by NO2 . ACS Nano 6, 1865–1875 (2012).
Liu, H. Liu, Y. & Zhu, D. Chemical doping of graphene. J. Mater. Chem. 21, 3335–3345 (2011).
Du, A. et al. Dots versus antidots: Computational Exploration of structure, magnetism, and half-metallicity in boron-nitride nanostructures. J. Am. Chem. Soc. 131, 17354–17359 (2009).
Ni, Z. H. et al. On resonant scatterers as a factor limiting carrier mobility in graphene. Nano. Lett. 10, 3868–3872 (2010).
Yung-Chang, L. et al. Graphene annealing: How clean can it be? Nano. Lett. 12, 414–419 (2012).
Jieun, S. Yeoung, K. T. & Sunmin, R. Raman spectroscopy study of annealing-induced effects on graphene prepared by mechanical exfoliation. Bul. Korean Chem. Soc. 31, 2679–2682 (2010).
Wehling, T. O. Yuan, S. Lichtenstein, A. I. Geim, A. K. & Katsnelson, M. I. Resonant scattering by realistic impurities in graphene. Phys. Rev. Lett. 105, 056802 (2010).
Wehling, T. O. Şaşioğlu, E. Friedrich, C. Lichtenstein, A. I. & Katsnelson, M. I. Effective Coulomb interactions in graphene and graphite. Phys. Rev. Lett. 106, 236805 (2011).
Sepioni, M. et al. Limits on intrinsic magnetism in graphene. Phys. Rev. Lett. 105, 207205 (2010).
Lehtinen, P. O. et al. Magnetic properties and diffusion of adatoms on a graphene sheet. Phys. Rev. Lett. 91, 017202 (2003).
Schedin, F. et al. Detection of individual gas molecules adsorbed on graphene. Nat. Mater. 6, 652–655 (2007).
Dong, X. et al. Doping single-layer graphene with aromatic molecules. Small 5, 1422–1426 (2009).
Das, B. Voggu, R. Rout, C. S. & Rao, C. N. R. Changes in the electronic structure and properties of graphene induced by molecular charge-transfer. Chem. Commun. 5155–5157 (2008).
Leenaerts, O. Partoens, B. & Peeters, F. M. Adsorption of H2O, NH3, CO, NO2 and NO on graphene: a first-principles study. Phys. Rev. B 77, 125416 (2008).
Dettlaff-Weglikowska, U. Kim, G. Bulusheva, L. G. & Roth, S. Modification of the electronic structure in single-walled carbon nanotubes with aromatic amines. Physica Status Solidi B 248, 2458–2461 (2011).
Pisana, S. et al. Breakdown of the adiabatic Born–Oppenheimer approximation in graphene. Nat. Mater 6, 198–201 (2007).
Das, A. et al. Monitoring dopants by Raman scattering in an electrochemically top-gated graphene transistor. Nat. Nanotechnol. 3, 210–215 (2008).
Elias, D. C. et al. Control of graphene’s properties by reversible hydrogenation: evidence for graphane. Science 323, 610–613 (2009).
This work was supported by the UK Engineering and Physical Sciences Research Council. A.H.C.N. acknowledges support from NRF-CRP (R-144-000-295-281). A.V.K., O.L. and J.K. acknowledge support from the Academy of Finland through projects 218545 and 263416.
The authors declare no competing financial interests.
About this article
Cite this article
Nair, R., Tsai, IL., Sepioni, M. et al. Dual origin of defect magnetism in graphene and its reversible switching by molecular doping. Nat Commun 4, 2010 (2013). https://doi.org/10.1038/ncomms3010
Manipulating electronic structure of graphene for producing ferromagnetic graphene particles by Leidenfrost effect-based method
Scientific Reports (2020)
Nature Communications (2019)
Scientific Reports (2018)
Nature Reviews Materials (2018)
Nature Communications (2018)