Abstract
Sulphur is an attractive cathode material with a high specific capacity of 1,673 mAh g−1, but its rapid capacity decay owing to polysulphide dissolution presents a significant technical challenge. Despite much efforts in encapsulating sulphur particles with conducting materials to limit polysulphide dissolution, relatively little emphasis has been placed on dealing with the volumetric expansion of sulphur during lithiation, which will lead to cracking and fracture of the protective shell. Here, we demonstrate the design of a sulphur–TiO2 yolk–shell nanoarchitecture with internal void space to accommodate the volume expansion of sulphur, resulting in an intact TiO2 shell to minimize polysulphide dissolution. An initial specific capacity of 1,030 mAh g−1 at 0.5 C and Coulombic efficiency of 98.4% over 1,000 cycles are achieved. Most importantly, the capacity decay after 1,000 cycles is as small as 0.033% per cycle, which represents the best performance for long-cycle lithium–sulphur batteries so far.
Similar content being viewed by others
Introduction
There has been a steady increase in the demand for high-performance and long-lasting rechargeable batteries for a wide range of applications, ranging from portable electronics and consumer devices to electric vehicles and large-scale grid energy storage1,2,3,4,5,6,7,8,9. Unfortunately, the energy density and cycle life of existing lithium-ion batteries remain insufficient for many of the aforementioned applications, prompting the urgent need for new electrode materials with much higher charge capacities1,2,3,4,5. Over the years, significant progress has been made in the development of new high-performance anode materials (such as silicon and tin) for rechargeable batteries10,11,12,13,14, but the major limiting factor is still the relatively low capacity of cathodes. Sulphur is a promising cathode material with a theoretical specific capacity of 1,673 mAh g−1, which is ~5 times that of existing materials based on transition metal oxides and phosphates15,16,17,18. However, many challenges remain in developing a practical lithium–sulphur battery for commercialization. It is known that sulphur particles suffer from the problems of (a) poor electronic conductivity, (b) dissolution of intermediate polysulphides and (c) large volumetric expansion (~80%) upon lithiation, which results in rapid capacity decay and low Coulombic efficiency (Fig. 1a)15,16,17,18. Over the years, extensive efforts have been devoted to addressing the first two problems, by encapsulating sulphur particles with conducting materials, including porous carbon19,20,21,22,23,24,25,26,27, graphene oxide28,29 and conductive polymers30,31,32,33, in an attempt to improve their electronic conductivity and limit polysulphide dissolution. However, insufficient emphasis has been placed on dealing with the third challenge—the large volumetric expansion of sulphur during lithiation coupled with polysulphide dissolution. This poses a critical problem because volume expansion of the sulphur core will cause the protective coating layer to crack and fracture, rendering the conventional core–shell morphology32,33,34,35 ineffective in trapping polysulphides (Fig. 1b). In this respect, the strategy of adjusting the amount of sulphur infusion into mesoporous carbon has been demonstrated20,23, but it can be difficult to control the uniformity of sulphur filling within the pores of each particle and across different particles. Overall, the long-term cycling performance for lithium–sulphur batteries remains to be improved.
Herein, we demonstrate for the first time, the design of a sulphur–TiO2 yolk–shell nanoarchitecture for stable and prolonged cycling over 1,000 charge/discharge cycles in lithium–sulphur batteries. The unique advantage of the yolk–shell morphology lies in the presence of internal void space to accommodate the large volumetric expansion of sulphur during lithiation, thus preserving the structural integrity of the shell to minimize polysulphide dissolution (Fig. 1c). In comparison with bare sulphur and sulphur–TiO2 core–shell nanoparticles, the yolk–shell nanostructures are found to exhibit the highest capacity retention owing to the effectiveness of the intact TiO2 shell in limiting polysulphide dissolution. Using the yolk–shell nanoarchitecture, an initial specific capacity of 1,030 mAh g−1 at 0.5 C and Coulombic efficiency of 98.4% over 1,000 cycles is achieved. Most importantly, the capacity decay at the end of 1,000 cycles is found to be as small as 0.033% per cycle (3.3% per 100 cycles). To the best of our knowledge, this is the first time that a lithium–sulphur battery with this level of performance has been described.
Results
Synthesis of the sulphur–TiO2 yolk–shell nanostructures
The sulphur–TiO2 yolk–shell morphology was experimentally realized as shown schematically in Fig. 2a. First, monodisperse sulphur nanoparticles were prepared using the reaction of sodium thiosulfate with hydrochloric acid (Supplementary Fig. S1). The sulphur nanoparticles were then coated with TiO2 through controlled hydrolysis of a sol-gel precursor, titanium diisopropoxide bis(acetylacetonate), in an alkaline isopropanol/aqueous solution, resulting in the formation of sulphur–TiO2 core–shell nanoparticles (Supplementary Fig. S2; the transmission electron microscopy (TEM) image was taken immediately after the electron beam was turned on to avoid sublimation of sulphur under the beam). This was followed by partial dissolution of sulphur in toluene to create an empty space between the sulphur core and the TiO2 shell, resulting in the yolk–shell morphology. The scanning electron microscopy (SEM) image in Fig. 2b shows uniform spherical nanoparticles of ~800 nm in size. The TEM image in Fig. 2c, taken immediately after the electron beam was turned on, shows sulphur nanoparticles encapsulated within TiO2 shells (~15 nm thick) with internal void space. Owing to the two-dimensional projection nature of TEM images, the void space will appear as either an empty area or an area of lower intensity depending on the orientation of the particles (Fig. 2c). The TiO2 in the yolk–shell nanostructures were determined to be amorphous using X-ray diffraction (Supplementary Fig. S3). The ability of toluene to diffuse through the TiO2 shell to partially dissolve sulphur indicates its porous nature, which is typical of amorphous TiO2 prepared using sol-gel methods36. The average pore diameter was determined to be ~3 nm using the Barrett–Joyner–Halenda method, which corresponds to a mesoporous structure.
Volume expansion in the yolk–shell nanostructures
Next, we investigated the effectiveness of the yolk–shell morphology in accommodating the volume expansion of sulphur and limiting polysulphide dissolution. The sulphur–TiO2 yolk–shell nanostructures were drop-cast onto conducting carbon paper to form working electrodes, and pouch cells were assembled using lithium foil as the counter electrode. The cells were discharged at 0.1 C (1 C=1,673 mA g−1) to a voltage of 1.7 V versus Li+/Li, during which a capacity of 1,110 mAh g−1 was attained (Supplementary Fig. S4), and the voltage was maintained for over 20 h. The as-obtained discharge profile shows the typical two-plateau behaviour of sulphur cathodes, indicating the conversion of elemental sulphur to long-chain lithium polysulphides (Li2Sn, 4≤n≤8) at ~2.3 V, and the subsequent formation of Li2S2 and Li2S at ~2.1 V (Supplementary Fig. S4)15,16,17,18. After the discharge process, the contents of the cells (cathode, anode and separator) were washed with 1,3-dioxolane (DOL) solution for further characterization. This polysulphide-containing solution was then oxidized with concentrated HNO3 and diluted with deionized water for analysis of sulphur content using inductively coupled plasma (ICP) spectroscopy37. For comparison, electrode materials were also prepared using the bare sulphur and sulphur–TiO2 core–shell nanoparticles and subject to the same treatment.
There was little change in the morphology and size distribution of the sulphur–TiO2 yolk–shell nanostructures before and after lithiation (Fig. 3a–c). TEM image of a lithiated yolk–shell nanostructure shows a structurally intact TiO2 coating (Fig. 3d), indicating the ability of the yolk–shell design in accommodating the volume expansion of sulphur. The presence of lithiated sulphur and TiO2 in the yolk–shell nanostructure was confirmed using energy-dispersive X-ray spectroscopy and electron energy loss spectroscopy (Fig. 3e). In the case of bare sulphur and sulphur–TiO2 core–shell nanoparticles, random precipitation of irregularly shaped Li2S2 and Li2S particles was observed on the electrodes owing to dissolution of lithium polysulphides into the electrolyte (Supplementary Fig. S5)15,16,17,18. ICP analysis performed on the contents of the discharged cells showed a loss of 81 and 62% of the total sulphur mass into the electrolyte for the bare sulphur and sulphur–TiO2 core–shell nanoparticles, respectively. In comparison, only 19% of the total sulphur mass was found to be dissolved in the electrolyte in the case of the yolk–shell nanostructures, which indicates the effectiveness of the intact TiO2 shell in limiting polysulphide dissolution.
Electrochemical performance
To further evaluate the electrochemical cycling performance of the sulphur–TiO2 yolk–shell nanoarchitecture, 2,032-type coin cells were fabricated. The working electrodes were prepared by mixing the yolk–shell nanostructures with conductive carbon black and polyvinylidene fluoride binder in N-methyl-2-pyrrolidinone to form a slurry, which was then coated onto aluminium foil and dried under vacuum. Using lithium foil as the counter electrode, the cells were cycled from 1.7–2.6 V versus Li+/Li. The electrolyte used was lithium bis(trifluoromethanesulfonyl)imide in 1,2-dimethoxyethane and 1,3-DOL, with LiNO3 (1 wt%) as an additive to help passivate the surface of the lithium anode and reduce the shuttle effect17,18. Specific capacity values were calculated based on the mass of sulphur, which was determined using thermogravimetric analysis (Supplementary Fig. S6). The sulphur content was found to be ~71 wt% in the yolk–shell nanostructures, accounting for ~53 wt% of the electrode mix, with a typical sulphur mass loading of 0.4–0.6 mg cm−2. The contribution of TiO2 to the total capacity is very small in the voltage range used in our work38,39.
The sulphur–TiO2 yolk–shell nanoarchitecture exhibited stable cycling performance over 1,000 charge/discharge cycles at 0.5 C (1 C=1,673 mA g−1) as displayed in Fig. 4a (see also Supplementary Fig. S7). After an initial discharge capacity of 1,030 mAh g−1, the yolk–shell nanostructures achieved capacity retentions of 88, 87 and 81% at the end of 100, 200 and 500 cycles, respectively (Fig. 4a). Most importantly, after prolonged cycling over 1,000 cycles, the capacity retention was found to be 67%, which corresponds to a very small capacity decay of 0.033% per cycle (3.3% per 100 cycles), representing the best performance for long-cycle lithium–sulphur batteries so far. The average Coulombic efficiency over 1,000 cycles was calculated to be 98.4%, which shows little shuttle effect owing to polysulphide dissolution. In comparison, cells based on bare sulphur and sulphur–TiO2 core–shell nanoparticles suffered from rapid capacity decay, showing capacity retentions of 48 and 66%, respectively, after only 200 cycles (Fig. 4b), indicating a greater degree of polysulphide dissolution into the electrolyte.
Next, the sulphur–TiO2 yolk–shell nanostructures were subject to cycling at various C-rates to evaluate their robustness (Fig. 4c). After an initial discharge capacity of 1,215 mAh g−1 at 0.2 C, the capacity was found to stabilize at 1,010 mAh g−1. Further cycling at 0.5, 1 and 2 C showed high reversible capacities of 810, 725 and 630 mAh g−1, respectively (Fig. 4c). When the C-rate was switched abruptly from 2 to 0.2 C again, the original capacity was largely recovered (Fig. 4c), indicating robustness and stability of the cathode material. Moreover, there was little change in the thickness of the cathode before and after 70 cycles at these various C-rates (Supplementary Fig. S8), which further confirms the ability of the yolk–shell nanostructures in accommodating the volume expansion of sulphur.
Discussion
There are two important characteristics of such a yolk–shell design that imparts the sulphur–TiO2 nanostructures with stable cycling performance over 1,000 charge/discharge cycles. First, sufficient empty space was present to allow for volume expansion of sulphur. Using image processing software on the yolk–shell nanostructures (Fig. 2c), sulphur was determined to occupy ~62% of the volume within the TiO2 shell, which corresponds to 38% internal void space. This value is supported by thermogravimetric analysis of the relative wt% of sulphur versus TiO2 (Supplementary Fig. S6), from which the volume of empty space in the yolk–shell nanostructures was estimated to be 37%. This volume of void space can accommodate ~60% volume expansion of the sulphur present within the shell, allowing for 1,250 mAh g−1, that is, 75% of the maximum theoretical capacity of sulphur, to be utilized (assuming volume expansion is linearly dependent on the degree of lithiation). Experimentally, we have been able to achieve a maximum discharge capacity of 1,215 mAh g−1 (Fig. 4c), therefore there is sufficient void space for volume expansion without causing the shell to crack and fracture. Second, the intact TiO2 shell, with its small pore size of ~3 nm, was effective in minimizing polysulphide dissolution. Mesoporous structures, such as those based on carbon, have been shown to help trap polysulphides owing to their small pore sizes (~3 nm)20,27. Moreover, metal oxides such as TiO2 possess hydrophilic Ti–O groups and surface hydroxyl groups, which are known to bind favourably with polysulphide anions, hence further limiting the extent of polysulphide dissolution21,40.
In conclusion, we have demonstrated for the first time, the design of a sulphur–TiO2 yolk–shell nanoarchitecture for long cycling capability over 1,000 charge/discharge cycles, with a capacity decay as small as 0.033% per cycle. Compared with its bare sulphur and sulphur–TiO2 core–shell counterparts, the yolk–shell nanostructures exhibited the highest capacity retention owing to the presence of internal void space to accommodate the volume expansion of sulphur during lithiation, resulting in an intact shell to minimize polysulphide dissolution. Insight gained from this work can be applied to other high-capacity anode and cathode material systems, especially those that undergo large volumetric expansion, providing new avenues for the future development of high-performance rechargeable batteries.
Methods
Synthesis of sulphur–TiO2 yolk–shell nanostructures
First, sulphur nanoparticles were synthesized by adding concentrated HCl (0.8 ml, 10 M) to an aqueous solution of Na2S2O3 (100 ml, 0.04 M) containing a low concentration of polyvinylpyrrolidone (PVP, Mw~55,000, 0.02 wt%; we note that at much higher PVP concentrations, hollow sulphur particles are formed instead). After reaction for 2 h, the sulphur nanoparticles (100 ml) were washed by centrifugation and redispersed into an aqueous solution of PVP (20 ml, 0.05 wt%). For TiO2 coating, the solution of sulphur nanoparticles (20 ml) was mixed with isopropanol (80 ml) and concentrated ammonia (2 ml, 28 wt%). Titanium diisopropoxide bis(acetylacetonate) (50 ml, 0.01 M in isopropanol) was then added in five portions (5 × 10 ml) at half hour intervals. After reaction for 4 h, the solution of sulphur–TiO2 core–shell nanoparticles was washed by centrifugation to remove freely hydrolysed TiO2, followed by redispersion into deionized water (20 ml). To prepare the sulphur–TiO2 yolk–shell nanostructures, the solution of core–shell particles (20 ml) was stirred with isopropanol (20 ml) and toluene (0.4 ml) for 4 h to achieve partial dissolution of sulphur. The as-synthesized sulphur–TiO2 yolk–shell nanostructures were then recovered using centrifugation and dried under vacuum overnight.
Characterization
SEM and TEM images were taken using a FEI XL30 Sirion SEM (accelerating voltage 5 kV) and a FEI Tecnai G2 F20 X-TWIN (accelerating voltage 200 kV), respectively. Elemental analysis was performed using energy-dispersive X-ray spectroscopy and electron energy loss spectroscopy equipped in the TEM. X-ray diffraction patterns were obtained on a PANalytical X’Pert Diffractometer using Cu Kα radiation. Thermogravimetric analysis was carried out using a Netzsch STA 449 at a heating rate of 2 °C min−1 under argon atmosphere. ICP optical emission spectroscopy was performed using a Thermo Scientific ICAP 6300 Duo View Spectrometer. Nitrogen adsorption data were collected on a Micromeritics ASAP 2020 Analyser after degassing at 180 °C for 12 h.
Electrochemical measurements
To prepare the working electrodes, the various sulphur-based materials were mixed with carbon black (Super P) and polyvinylidene fluoride binder (75:15:10 by weight) in N-methyl-2-pyrrolidinone to form a slurry. This slurry was then coated onto aluminium foil using doctor blade and dried under vacuum to form the working electrode. 2032-type coin cells were assembled in an argon-filled glove box using lithium foil as the counter electrode. The electrolyte used was a freshly prepared solution of lithium bis(trifluoromethanesulfonyl)imide (1 M) in 1:1 v/v 1,2-dimethoxyethane and 1,3-DOL containing LiNO3 (1 wt%). Galvanostatic cycling was carried out using a 96-channel battery tester (Arbin Instruments) from 1.7–2.6 V versus Li+/Li. Specific capacity values were calculated based on the mass of sulphur in the samples, which was determined using thermogravimetric analysis (Supplementary Fig. S6). The sulphur content was found to be ~71 wt% in the yolk–shell nanostructures, accounting for ~53 wt% of the electrode mix, with a typical sulphur mass loading of 0.4–0.6 mg cm−2.
Additional information
How to cite this article: Seh, Z. W. et al. Sulphur–TiO2 yolk–shell nanoarchitecture with internal void space for long-cycle lithium–sulphur batteries. Nat. Commun. 4:1331 doi: 10.1038/ncomms2327 (2013).
References
Arico A. S., Bruce P., Scrosati B., Tarascon J. M., Van Schalkwijk W. Nanostructured materials for advanced energy conversion and storage devices. Nat. Mater. 4, 366–377 (2005).
Bruce P. G., Freunberger S. A., Hardwick L. J., Tarascon J.-M. Li-O2 and Li-S batteries with high energy storage. Nat. Mater. 11, 19–29 (2012).
Yang P. D., Tarascon J. M. Towards systems materials engineering. Nat. Mater. 11, 560–563 (2012).
Whittingham M. S. Lithium batteries and cathode materials. Chem. Rev. 104, 4271–4301 (2004).
Goodenough J. B., Kim Y. Challenges for rechargeable Li batteries. Chem. Mater. 22, 587–603 (2010).
Lee Y. J. et al. Fabricating genetically engineered high-power lithium ion batteries using multiple virus genes. Science 324, 1051–1055 (2009).
Kang B., Ceder G. Battery materials for ultrafast charging and discharging. Nature 458, 190–193 (2009).
Chung S. Y., Bloking J. T., Chiang Y. M. Electronically conductive phospho-olivines as lithium storage electrodes. Nat. Mater. 1, 123–128 (2002).
Nishizawa M., Mukai K., Kuwabata S., Martin C. R., Yoneyama H. Template synthesis of polypyrrole-coated spinel LiMn2O4 nanotubules and their properties as cathode active materials for lithium batteries. J. Electrochem. Soc. 144, 1923–1927 (1997).
Park C. M., Kim J. H., Kim H., Sohn H. J. Li-alloy based anode materials for Li secondary batteries. Chem. Soc. Rev. 39, 3115–3141 (2010).
Ji L. W., Lin Z., Alcoutlabi M., Zhang X. W. Recent developments in nanostructured anode materials for rechargeable lithium-ion batteries. Energy Environ. Sci 4, 2682–2699 (2011).
Kasavajjula U., Wang C., Appleby A. J. Nano- and bulk-silicon-based insertion anodes for lithium-ion secondary cells. J. Power Sources 163, 1003–1039 (2007).
Chan C. K. et al. High-performance lithium battery anodes using silicon nanowires. Nat. Nanotech. 3, 31–35 (2008).
Magasinski A. et al. High-performance lithium-ion anodes using a hierarchical bottom-up approach. Nat. Mater. 9, 353–358 (2010).
Mikhaylik Y. V., Akridge J. R. Polysulfide shuttle study in the Li/S battery system. J. Electrochem. Soc. 151, A1969–A1976 (2004).
Yamin H., Gorenshtein A., Penciner J., Sternberg Y., Peled E. Lithium sulfur battery - oxidation reduction-mechanisms of polysulfides in THF solutions. J. Electrochem. Soc. 135, 1045–1048 (1988).
Barchasz C., Lepretre J.-C., Alloin F., Patoux S. New insights into the limiting parameters of the Li/S rechargeable cell. J. Power Sources 199, 322–330 (2012).
Aurbach D. et al. On the surface chemical aspects of very high energy density, rechargeable Li-sulfur batteries. J. Electrochem. Soc. 156, A694–A702 (2009).
Elazari R., Salitra G., Garsuch A., Panchenko A., Aurbach D. Sulfur-impregnated activated carbon fiber cloth as a binder-free cathode for rechargeable Li-S batteries. Adv. Mater. 23, 5641–5644 (2011).
Ji X., Lee K. T., Nazar L. F. A highly ordered nanostructured carbon-sulphur cathode for lithium-sulphur batteries. Nat. Mater. 8, 500–506 (2009).
Ji X., Evers S., Black R., Nazar L. F. Stabilizing lithium-sulphur cathodes using polysulphide reservoirs. Nat. Commun. 2, 325 (2011).
Schuster J. et al. Spherical ordered mesoporous carbon nanoparticles with high porosity for lithium-sulfur batteries. Angew. Chem. Int. Ed. 51, 3591–3595 (2012).
Liang C. D., Dudney N. J., Howe J. Y. Hierarchically structured sulfur/carbon nanocomposite material for high-energy lithium battery. Chem. Mater. 21, 4724–4730 (2009).
Yang Y. et al. New nanostructured Li2S/silicon rechargeable battery with high specific energy. Nano Lett. 10, 1486–1491 (2010).
Zheng G., Yang Y., Cha J. J., Hong S. S., Cui Y. Hollow carbon nanofiber-encapsulated sulfur cathodes for high specific capacity rechargeable lithium batteries. Nano Lett. 11, 4462–4467 (2011).
Guo J., Xu Y., Wang C. Sulfur-impregnated disordered carbon nanotubes cathode for lithium-sulfur batteries. Nano Lett. 11, 4288–4294 (2011).
Jayaprakash N., Shen J., Moganty S. S., Corona A., Archer L. A. Porous hollow carbon@sulfur composites for high-power lithium-sulfur batteries. Angew. Chem. Int. Ed. 50, 5904–5908 (2011).
Wang H. et al. Graphene-wrapped sulfur particles as a rechargeable lithium-sulfur battery cathode material with high capacity and cycling stability. Nano Lett. 11, 2644–2647 (2011).
Ji L. et al. Graphene oxide as a sulfur immobilizer in high performance lithium/sulfur cells. J. Am. Chem. Soc. 133, 18522–18525 (2011).
Wang J. L., Yang J., Xie J. Y., Xu N. X. A novel conductive polymer-sulfur composite cathode material for rechargeable lithium batteries. Adv. Mater. 14, 963–965 (2002).
Xiao L. et al. A soft approach to encapsulate sulfur: polyaniline nanotubes for lithium-sulfur batteries with long cycle life. Adv. Mater. 24, 1176–1181 (2012).
Wu F. et al. Sulfur/polythiophene with a core/shell structure: synthesis and electrochemical properties of the cathode for rechargeable lithium batteries. J. Phys. Chem. C 115, 6057–6063 (2011).
Fu Y., Manthiram A. Core-shell structured sulfur-polypyrrole composite cathodes for lithium-sulfur batteries. RSC Adv. 2, 5927–5929 (2012).
Li X. et al. Hollow core-shell structured porous Si-C nanocomposites for Li-ion battery anodes. J. Mater. Chem. 22, 11014–11017 (2012).
Su L., Jing Y., Zhou Z. Li ion battery materials with core-shell nanostructures. Nanoscale 3, 3967–3983 (2011).
Zang L. et al. Amorphous microporous titania modified with platinum(IV) chloride - A new type of hybrid photocatalyst for visible light detoxification. J. Phys. Chem. B 102, 10765–10771 (1998).
Yan D., Kai X., Shizhao X., Xiaobin H. Analysis of polysulfide dissolved in electrolyte in discharge-charge process of Li-S battery. J. Electrochem. Soc. 159, A421–A425 (2012).
Yang Z. et al. Nanostructures and lithium electrochemical reactivity of lithium titanites and titanium oxides: a review. J. Power Sources 192, 588–598 (2009).
Furukawa H., Hibino M., Honma I. Electrochemical properties of nanostructured amorphous, sol-gel-synthesized TiO2/acetylene black composite electrodes. J. Electrochem. Soc. 151, A527–A531 (2004).
Evers S., Yim T., Nazar L. F. Understanding the nature of absorption/adsorption in nanoporous polysulfide sorbents for the Li-S battery. J. Phys. Chem. C 116, 19653–19658 (2012).
Acknowledgements
This work was supported by the Department of Energy, Office of Basic Energy Sciences, Division of Materials Sciences and Engineering, under Contract DE-AC02-76SF00515, through the SLAC National Accelerator Laboratory LDRD project. Z.W.S. and G.Z. acknowledge the support of an A*STAR National Science Scholarship. We thank Ming Gong for help in nitrogen adsorption measurements.
Author information
Authors and Affiliations
Contributions
Z.W.S. and Y.C. conceived the idea. Z.W.S. and W.L. carried out material synthesis and electrochemical tests. J.J.C., G.Z., Y.Y., M.T.M. and P.-C.H. performed material characterization. Z.W.S. and Y.C. co-wrote the paper. All the authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures S1-S8 (PDF 2393 kb)
Rights and permissions
About this article
Cite this article
Wei Seh, Z., Li, W., Cha, J. et al. Sulphur–TiO2 yolk–shell nanoarchitecture with internal void space for long-cycle lithium–sulphur batteries. Nat Commun 4, 1331 (2013). https://doi.org/10.1038/ncomms2327
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms2327
This article is cited by
-
Engineering Strategies for Suppressing the Shuttle Effect in Lithium–Sulfur Batteries
Nano-Micro Letters (2024)
-
Unique polysulfide reaction on VO2 for restraining shuttle effect in soft-packaged Li–S pouch cells
Rare Metals (2024)
-
Interface-induced polymerization strategy for constructing titanium dioxide embedded carbon porous framework with enhanced chemical immobilization towards lithium polysulfides
Nano Research (2024)
-
Preparation of NiCo2S4/carbon hollow sphere for long cycle lithium sulfur batteries
Journal of Materials Science: Materials in Electronics (2024)
-
Boosting Lean Electrolyte Lithium–Sulfur Battery Performance with Transition Metals: A Comprehensive Review
Nano-Micro Letters (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.