The controllable and reversible modification of graphene by chemical functionalization can modulate its optical and electronic properties. Here we demonstrate the controlled patterning of graphane/graphene superlattices within a single sheet of graphene. By exchanging the sp3 C–H bonds in graphane with sp3 C–C bonds through functionalization, sophisticated multifunctional superlattices can be fabricated on both the macroscopic and microscopic scales. These patterns are visualized using fluorescence quenching microscopy techniques and confirmed using Raman spectroscopy. By tuning the extent of hydrogenation, the density of the sp3 C functional groups on graphene's basal plane can be controlled from 0.4% to 3.5% with this two-step method. Using such a technique, which allows for both spatial and density control of the functional groups, a route to multifunctional electrical circuits and chemical sensors with specifically patterned recognition sites might be realized across a single graphene sheet, facilitating the development of graphene-based devices.
Graphene has emerged as a remarkable material for diverse optoelectronics applications1,2,3,4,5,6 owing to the large-scale synthetic routes to produce it in monolayer form, its extraordinary carrier mobility and conductivity, and its versatility for band structure engineering1,7,8,9,10,11,12,13,14,15,16. Controllably tailoring graphene's electronic structure with selective synthetic methods could better shape this two-dimensional semi-metal material for use in different applications. It is known that physisorption of chemical species on graphene can temporarily alter its electrical properties; however, adsorbates are too volatile for long-term usage17. With stronger binding energy and electronic coupling, covalent functionalization can permanently change the electronic structure of graphene. Hydrogenation is one straightforward route to render graphene, which has a bandgap of zero, into a wide-gap semiconductor, and recent studies have indicated that this method is controllable and reversible1,2. However, hydrogenation produces a single type of functional group, a sp3 C–H bond, which may prevent the material from being useful in more complicated applications. To convert the proton into more diverse chemical substituents, an extra chemical step, functionalization using a diazonium salt reaction, is demonstrated here. Reaction of diazonium salts with mechanically cleaved graphene was found to be selective to the edges and defects rather than the basal plane18,19. However, for electronic applications of graphene, there is a need for more uniformity in grafting functionality to the surface.
Here using the hydrogenated graphene as the activated precursor, C–H bonds are effectively exchanged with C–C bonds through diazonium salt functionalization, which controllably endows this material with a new spectrum of chemical and electrical properties. Furthermore, superlattices formed with built-in multifunctional regions in desired templates could yield characteristics necessary for the development of applications in, for example, chemical sensors, thermoelectrics and metamaterials3,6,20. In many cases, to produce materials relevant for these applications requires controlled attachment of complex molecules into patterns21. Alternatively, the ability to take a single template, such as graphene, and use existing processes such as lithographic patterning to create such structures on a molecular level, facilitates a route towards the rapid development of such desired architectures. The ability to produce large-scale graphene transferable to varied host surfaces also makes graphene an excellent template for the development of well-established top-down patterning approaches for device fabrication. Recent theoretical studies have emphasized the viability of this route for making quantum dots from patterned interfaces of hydrogenated and pristine graphene22, and we extend this idea to large-scale patterning of multifunctional domains on graphene.
Fabrication of the superlattices in graphene
The typical process to pattern hydrogenated graphene domains and the subsequent imaging using fluorescence quenching microscopy (FQM) is illustrated in Figure 1a. First, large-area graphene, grown from Cu substrates by chemical vapour deposition or solid carbon methods, were transferred to an insulating substrate such as quartz or SiO2/Si, using the PMMA protection procedure as described elsewhere11,12. Following this, conventional photolithography was employed with a photoresist mask to define patterns atop the graphene films. Next, the exposed area of graphene was hydrogenated, using atomic hydrogen generated by a tungsten hot filament at low H2 pressure (10 to 20 Torr). The sample takes 2 h to be hydrogenated thoroughly at ~10 °C (ref. 2). This procedure was found to be effective for controlled hydrogenation, minimizing graphene etching that originates at defects or edges23. Finally, the photoresist mask was removed to yield a conductive graphene sheet patterned with domains of insulating graphane-containing regions.
Imaging the superlattices in graphene
Although the fabrication of the graphane/graphene superlattices, as we demonstrate here, was largely reliant on conventional techniques, the challenge is determining a straightforward and rapid method for imaging the product of the process, namely the substructure of the graphane/graphene hybrid material. Therefore, the FQM technique4, discovered by Kim et al., was used to image the existing hybrid patterns. According to the excited-state energy transfer mechanism, graphene may serve as an acceptor to quench the fluorescence of a thin spin-coated dye layer (0.02% rhodamine B mixed with 5% PMMA in acetone)4. Because graphene and its functionalized form are different in their conjugation, the differential quenching ability of the hybrid graphane/graphene pattern can be readily observed using FQM4. Using the technique illustrated in Figure 1a, graphane/graphene patterns have been made with photolithography and hydrogenation, and then imaged with FQM as shown in Figure 1b–d. In the photos, all of the dark areas are pristine graphene, which more efficiently quenches the fluorescence of the thin top dye layer. The bright areas are graphane; its fluorescence quenching ability is much weaker than in graphene because of the loss of conjugation in the former. This verifies that the formation of insulating domains on a conductive graphene sheet can be readily achieved. The bright spots or bands in the FQM images come from the aggregation and non-uniform coating of the dye layers, arising in part from the folds induced during transfer of the original graphene film. In all cases conventional photolithography was used, which is only capable of accuracy down to length scales of ~1 μm in our laboratory (Supplementary Fig. S1). However, well-defined structures that can be achieved using more advanced lithographic techniques can extend this technique to finer patterning24.
Towards hybrid superlattices in graphene
Typical atomic models of graphane and graphane/graphene superlattices are shown in Figure 2a,b. Although, in our cases, full hydrogenation is not achieved because of the substrate hindering effect, the hydrogenated section has more sp3 carbon characteristics than does the pristine section, as seen by the pronounced D peak in the Raman spectrum. The Raman spectra displayed in Figure 2c correspond well with those reported for single-layer graphene before and after hydrogenation2. With extended hydrogenation time, more sp3 C characteristics or higher D peaks were observed. In Raman spectra of pristine monolayer graphene, the D peak (1,350 cm−1) is much lower than the G peak (1,580 cm−1), and the 2D peak (2,685 cm−1) is about 4 times more intense than the G peak. After 180 min of hydrogenation, the D peak is almost as high as the G peak. An extra D' peak (1,620 cm−1) is detected on the shoulder of the G peak, and the 2D peak is suppressed because of the chemical functionalization. The D peak intensity was also recorded as a 2-dimensional map to confirm the formation of a graphene/graphane patterns in Supplementary Figure S2. However, compared with FQM that only takes a few seconds to image a large area of the sample, Raman mapping is relatively time-consuming (7 h for 50 μm×50 μm area in Supplementary Fig. S2) with a resolution limited by the laser spot size of the Raman instrument. Four-probe electrical measurements before and after the hydrogenation demonstrate a gradual transformation from semi-metallic graphene to near-insulating graphane-like material. After annealing at 520 °C for 30 min under high vacuum (10−6–10−7 Torr), the graphane is partially converted back to graphene based on the partial recovery of its conductivity (Supplementary Fig. S3). This provides further evidence that insulating graphane domains formed from a conductive graphene template2.
With this graphane/graphene superlattice in hand, the material can be additionally functionalized using diazonium salts. The diazonium salt reaction with the graphane/graphene intermediate is most likely to go through a free radical mechanism, as had been proposed for the diazonium functionalization of a hydrogen-passivated Si surface25. As shown in Figure 3, in this case, we propose a spontaneous electron transfer from the surface of the graphane/graphene substrate to the diazonium salt, generating an aryl radical on loss of N2 and a graphane/graphene radical cation. A proton is eliminated from the graphane/graphene to form HBF4 and a graphane/graphene radical. Within a common solvent shell, the free aryl radicals attack the surface near the sp3 C–H bond sites to form the new covalent sp3 C–C bonds.
Thermodynamically, pristine graphene is inert to many organic reactions except at structurally reactive spots with relatively high chemical potential, which make these latter sites more reactive. For example, the edges, strain sites (ripples) and the Stone-Wale defects are more reactive than the crystalline basal planes of graphene, based on experimental and theoretical studies19,26,27. Nevertheless, hydrogenation functionalizes the basal plane of graphene in a controllable, uniform and reversible manner. Here we show that hydrogenation also activates the basal plane towards diazonium functionalization. Similar to aryl radicals in the diazonium reaction, the atomic H works as a free radical (H•). This H-radical generated by the hot tungsten filament overcomes the high-energy barrier to break the sp2 bond in graphene and it, thereby, forms a new sp3 bond. Supplementary Figure S4 displays the reaction energy scheme for both the direct diazonium reaction (addition reaction, sp2 bond to sp3 bond) and the diazonium reaction after hydrogenation (substitution reaction, sp3 bond to sp3 bond). The diazonium reaction and FQM experiment to image the hybrid superlattices were performed as shown in Figure 4a.
The diazonium functionalized graphene film was lifted off from a SiO2/Si wafer and transferred onto a c-flat transmission electron microscope (TEM) grid (Protochips) with the PMMA protection method12. The etchant used here is buffered oxide etchant (J.T. Baker, Buffered Oxide Etch 6:1). In Figure 4b,c, the TEM image and selected area electron diffraction pattern prove that the graphene sample is maintained after the chemical process of hydrogenation and diazonium reaction. FQM was used to image the same diazonium-functionalized graphene superlattices with different dye molecules, such as rhodamine B, fluorescein isothiocyanate (FITC), and fluorescein sodium in Figure 4d–f, respectively. The diazonium functionality introduced was determined by analysis of the bromine content of the functionalized product using X-ray photoelectron spectroscopy (XPS); the Br content was due to the 4-bromophenyldiazonium tetrafluoroborate used in the functionalization. As shown in Figure 4g, under the same reaction conditions, pristine graphene has only 0.4% bromine content after functionalization with the diazonium salt, whereas graphane has bromine content >1%. The more graphane that is present in the sample, the more bromophenyl-functionalization that is introduced. The sample with the most graphane had a bromine content of 3.5%, which is approximately one new sp3 C–C bond in every 21.5 C atoms in the graphane domains.
With this two-step functionalization method, graphene's basal surface can be controllably grafted with Br content up to 3.5%, with a lithographically defined spacial resolution. Furthermore, to visualize the patterns, we used FQM, which, when combined with Raman spectroscopy, provides the necessary analytical tools to characterize the heterostructures. The two-step controlled covalent functionalization process described here permits modulation of the electronic properties of graphene's basal planes and could hold promise for specifically patterned optoelectronic and sensor devices based on this exciting new material.
Graphane/graphene superlattices fabrication
Graphene films were grown on 25-μm thick Cu foils (99.8%, Alfa Aesar, item No. 13382) and transferred onto various substrates, such as glass, quartz, and 100 nm SiO2/Si, according to the methods reported1,2. Graphene patterns were fabricated using a photoresist (Microposit S1813) mask in a standard photolithography process or a PMMA mask in an e-beam lithography process. Hydrogenation was performed in a vacuum system equipped with a hot tungsten filament (diameter=0.25 mm, 99.95%, Alfa Aesar) that splits the H2 gas into H atoms. Before the hydrogenation, the graphene samples (or graphene patterns) were heated in vacuum (10−6 Torr) at 400 °C (200 °C with polymer-defined patterns) for 15 min to remove physisorbed polymers and other contaminants that might block the hydrogenation of the graphene surface. 50 sccm H2 was then introduced into the system and the pressure was controlled at ~10 Torr using a valve connected to the vacuum pump. The filament current was slowly increased to ~13 A and the total power was maintained at ~60~65 W. The graphene samples were placed ~2 cm from hot filament for various times (15 min, 30 min, 1 h, 2 h or 3 h) to produce different levels of hydrogenation. The FQM pattern samples were made from the superlattices that had been hydrogenated for 2 h. After the hydrogenation, the polymer masks were removed by rinsing with 10 ml acetone 3×.
FQM imaging of the superlattices
A thin layer of dye (0.02 wt% Rhodamine B, FITC or fluorescein sodium, mixed with 5 wt% PMMA acetone solution) was deposited onto the superlattice sample surfaces by spin-coating at 5,000 rpm for 1 min (Headway Research). The samples were imaged under a fluorescence microscope (Zeiss Axioplan 2 imaging optical microscope). It was equipped with a Mercury Arc lamp (HBO 100 W) and in combination with a set of filters, coordinates the excitation and emission wavelengths corresponding to a particular fluorophore. In this work, Texas of Red (Ex: 555, 595/Em: 615 nm) and Cy3 (Ex: 514, 554/Em: 566, 615 nm) channels were used for rhodamine B, and FITC (Ex: 493/Em: 517 nm) channel was used for FITC and fluorescein sodium. Images were recorded and processed at room temperature using a Photometrics Cool Snap HQ camera and MetaMorph software. The objectives used were ×10, ×20, and ×40 in air; ×63 and ×100 in oil. The diazonium functionalized graphane/graphene superlattices have the same contrast as the unfunctionalized precursors, namely the graphane/graphene superlattices.
Diazonium functionalization of the hydrogenated graphene
In the diazonium functionalization experiments, the substrates (graphene hydrogenated for varied times of 0, 15, 30, 60, 120 to 180 min) were placed in a N2-purged, freshly prepared mg ml−1 diazonium salt solution (4-bromobenzenediazonium tetrafluoroborate in CH3CN) in the dark at room temperature for 20 h. The reactions could also be performed under UV light (254 nm) in 2 h. After the diazonium reaction, the samples were rinsed in CH3CN 3× to thoroughly remove any physisorbed diazonium salt residue and they were then dried using a flow of N2 before further characterization.
The Raman spectroscopy and mapping was performed on graphane/graphene superlattice films on quartz substrates using 514-nm laser excitation at room temperature with a Renishaw Raman RE02 microscope. XPS was performed using a PHI Quantera SXM scanning X-ray microprobe with 45° takeoff angle and a100-μm beam size.
How to cite this article: Sun, Z. et al. Towards hybrid superlattices in graphene. Nat. Commun. x:x doi: 10.1038/ncomms1577 (2011).
Balog, R. et al. Bandgap opening in graphene induced by patterned hydrogen adsorption. Nature Mater. 9, 315–319 (2010).
Elias, D. C. et al. Control of graphene's properties by reversible hydrogenation: Evidence for graphane. Science 323, 610–613 (2009).
Vakil, A. & Enghata, N. Transformational optics using graphene. Science 332, 1291–1294 (2011).
Kim, J., Cote, L. J., Kim, F. & Huang, J. Visualizing graphene based sheets by fluorescence quenching microscopy. J. Am. Chem. Soc. 132, 260–267 (2010).
Lin, Y. et al. Wafer-scale graphene integrated circuit. Science 332, 1294–1297 (2011).
Fowler, J. D. et al. Practical chemical sensors from chemically derived graphene. ACS Nano 3, 301–306 (2009).
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Kim, K. S. et al. Large-scale pattern growth of graphene films for stretchable transparent electrodes. Nature 457, 706–710 (2009).
Bae, S. et al. Roll-to-toll production of 30-inch graphene films for transparent electrodes. Nature Nanotech. 5, 574–578 (2010).
Reina, A. et al. Large area, few-layer graphene films on arbitrary substrates by chemical vapor deposition. Nano Lett. 9, 30–35 (2009).
Li, X. et al. Large-area synthesis of high quality and uniform graphene films on copper foils. Science 324, 1312–1314 (2009).
Sun, Z. et al. Growth of graphene from solid carbon sources. Nature 468, 549–552 (2010).
Kosynkin, D. V. et al. Longitudinal unzipping of carbon nanotubes to form graphene nanoribbons. Nature 458, 872–876 (2009).
Jiao, L., Zhang, L., Wang, X., Diankov, G. & Dai, H. Narrow graphene nanoribbons from carbon nanotubes. Nature 458, 877–880 (2009).
Bai, J., Zhong, X., Jiang, S., Huang, Y. & Duan, X. Graphene nanomesh. Nature Nanotech. 5, 190–194 (2010).
Zhang, Y. et al. Direct observation of a widely tunable bandgap in bilayer graphene. Nature 459, 820–823 (2009).
Schedin, F. et al. Detection of individual gas molecules adsorbed on graphene. Nature Mater. 6, 652–655 (2007).
Sun, Z., Kohama, S., Zhang, Z., Lomeda, J. R. & Tour, J. M. Soluble graphene through edge-selective functionalization. Nano Res. 3, 117–125 (2010).
Lim, H., Lee, J. S., Shin, H. J., Shin, H. S. & Choi, H. C. Spatially resolved spontaneous reactivity of diazonium salt on edge and basal plane of graphene without surfactant and its doping effect. Langmuir 26, 12278–12284 (2010).
Dragoman, D. & Dragoman, M. Giant thermoelectric effect in graphene. Appl. Phys. Lett. 91, 203116 (2007).
Zhang, J., Wang, Z. L., Liu, J., Chen, S. & Liu, G. Y. Self-assembled Nanostructures (Kluwer Academia/Plenum, NewYork, 2003).
Singh, A. K., Penev, E. S. & Yakobson, B.I. Vacancy cluster in graphane as quantum dots. ACS Nano 4, 3510–3514 (2010).
Yang, R. et al. An anisotropic etching effect in the graphene basal plane. Adv. Mater. 22, 4014–4019 (2010).
Gates, B. D. et al. New approaches to nanofabrication: molding, printing, and other techniques. Chem. Rev. 105, 1171–1196 (2005).
Stewart, M. P. et al. Direct covalent grafting of conjugated molecules onto Si, GaAs, and Pd surfaces from aryldiazonium salts. J. Am. Chem. Soc. 126, 370–378 (2004).
Boukhvalov, D. W. & Katsnelson, M. I. Enhancement of chemical activity in corrugated graphene. J. Phys. Chem. C. 113, 14176–14178 (2009).
Boukhvalov, D. W. & Katsnelson, M. I. Chemical functionalization of graphene with defects. Nano Lett. 8, 4373–4379 (2008).
We thank S. Ripley and C. Kittrell for assistance and discussions. This work was funded by the AFOSR (FA9550-09-1-0581), the Lockheed Martin LANCER Program, Sandia National Laboratory (1100745), the Nanoscale Science and Engineering Initiative of the National Science Foundation under NSF Award EEC-0647452 through the NSF Center for Biological and Environmental Nanotechnology, and the ONR MURI graphene program (00006766, N00014-09-1-1066).
The authors declare no competing financial interests.
About this article
Cite this article
Sun, Z., Pint, C., Marcano, D. et al. Towards hybrid superlattices in graphene. Nat Commun 2, 559 (2011). https://doi.org/10.1038/ncomms1577
Nature Communications (2021)
Nature Communications (2021)
Periodic surface functional group density on graphene via laser-induced substrate patterning at Si/SiO2 interface
Nano Research (2020)
Scientific Reports (2019)
Rendiconti Lincei. Scienze Fisiche e Naturali (2019)