Abstract
Spin impurities in diamond have emerged as a promising building block in a wide range of solid-state-based quantum technologies. The negatively charged silicon-vacancy centre combines the advantages of its high-quality photonic properties with a ground-state electronic spin, which can be read out optically. However, for this spin to be operational as a quantum bit, full quantum control is essential. Here we report the measurement of optically detected magnetic resonance and the demonstration of coherent control of a single silicon-vacancy centre spin with a microwave field. Using Ramsey interferometry, we directly measure a spin coherence time, T2*, of 115±9 ns at 3.6 K. The temperature dependence of coherence times indicates that dephasing and decay of the spin arise from single-phonon-mediated excitation between orbital branches of the ground state. Our results enable the silicon-vacancy centre spin to become a controllable resource to establish spin-photon quantum interfaces.
Similar content being viewed by others
Introduction
Spin-free materials, such as diamond and silicon, are ideal hosts to investigate and control the dynamics of spin-carrying defects. Among such systems, the nitrogen-vacancy (NV) centre in diamond has attracted great interest for electromagnetic field sensing1,2,3,4, bio-labelling5,6 and quantum information processing7,8,9,10,11. However, the NV centre only emits around 4% of its fluorescence into the zero-phonon line, limiting its use for quantum information processing in the absence of elaborate photonic structures such as photonic cavities12. In contrast, the negatively charged silicon-vacancy centre in diamond (SiV−) emits around 80% of its photons into the zero-phonon line13, with optical properties characterized by spectral stability and narrow inhomogeneous distribution in bulk diamond14. This makes the SiV− an ideal building block for a distributed quantum network15,16. Furthermore, the SiV− offers two possible realizations of a quantum bit: one consists in using the two readily available orbital branches of the ground state, split by 50 GHz (ref. 17). The other takes advantage of the SiV− ground-state spin S=1/2, optical signatures of which have previously been reported18 and which promises longer coherence times, as estimated through coherent population trapping19,20. Using the spin as a quantum bit allows tuning of the resonance frequency with a magnetic field in the few GHz range, routinely used for NV centres. Achieving coherent control of this spin is a fundamental step for the implementation of spin-based quantum computing algorithms. Using microwave control provides more flexibility in the orientation of the magnetic field than all-optical control, which requires lambda-type transitions to be allowed. Furthermore, the capacity to address the spin state of the SiV− with microwave pulses is crucial to use the SiV− as an interface between optical and microwave photons for hybrid quantum computing21. Similar efforts are also undertaken with other colour centres in diamond22.
Here we report the realization of coherent control of the silicon-vacancy centre electronic spin. We perform optically detected magnetic resonance (ODMR) by tuning the frequency of a microwave field into resonance with the Zeeman splitting between two electronic spin states of a single SiV− centre. This allows us to perform spectroscopy of the magnetic dipolar transitions between ground-state levels of opposite electronic spin. By fixing the frequency of the microwave field in resonance with one of those transitions and varying the duration of the pulse, we coherently drive the SiV− electronic spin. We then perform Ramsey interferometry and measure a spin dephasing time of 115±9 ns at 3.6 K. The temperature dependence of the spin coherence times reveals that spin dephasing and population decay are dominated by single-phonon excitation to the upper orbital branch of the ground state.
Results
Spin initialization and read-out
The SiV− centre is composed of a silicon atom replacing two neighbouring carbon atoms in the diamond lattice (Supplementary Note 1). Its energy levels are characterized by orbitally split ground and excited states (Fig. 1a). We study single SiV− centres in bulk diamond, created by implantation of isotopically purified 29Si followed by annealing (see the ‘Methods’ section). An external magnetic field lifts the degeneracy of the electronic spin S=1/2, resulting in the energy level diagram shown in Fig. 1a. In our experiment, this magnetic field is applied at an angle of 109.5°±1° with respect to the SiV− symmetry axis, which dictates that all transitions between ground and excited states are optically allowed19. We use an optical pulse from a diode laser tuned to resonance with transition D1 (between ground-state level 1 and excited-state level D, red double arrow in Fig. 1a) to pump the SiV− optically into the spin-down ground state. Fluorescence from the SiV− is collected on the remaining transitions (solid grey arrows in Fig. 1a) following thermalization among excited states (dashed grey arrows in Fig. 1a). The decrease of fluorescence during the laser pulse (Fig. 1b) allows to extract an initialization fidelity of about 85% through a master equation model (Supplementary Note 5). We perform the spin read-out analogously by measuring the recovery of the leading edge of the fluorescence generated by a second optical pulse resonant with the same transition. The spin-state measurement corresponds to the peak ratio between the integrated areas under the leading edge of the read-out pulse and that of the initialization pulse. By varying the time delay between the two pulses, we extract from the exponential recovery a spin relaxation time T1,spin=350±11 ns (Fig. 1c) at 3.5 K, setting an upper time bound for subsequent driving of the SiV− spin in this configuration.
Optically detected magnetic resonance
To address the electronic spin of the SiV−, we apply a microwave pulse between the optical initialization and read-out pulses (Fig. 2a). Owing to the nuclear spin 1/2 of the 29Si isotope, each electronic spin state displays a hyperfine splitting, as depicted in Fig. 2b. The microwave field drives the electronic spin, while preserving the nuclear spin state, which results in two distinct microwave resonance frequencies (orange and green circular arrows in Fig. 2b). When on resonance with one of the two transitions, the microwave transfers population from the initialized spin state to the depleted one, resulting in a recovery of fluorescence during the read-out pulse and thus a peak in the ODMR spectrum with a contrast around 33% (Fig. 2c and Supplementary Note 3). We measure the frequencies of the two resonances at different values of the applied magnetic field, as shown in Fig. 2d. We fit the observed frequency shift using an effective Hamiltonian described in ref. 23, which includes the Jahn-Teller effect, spin–orbit coupling and electronic Zeeman effect, and accounts for the nuclear spin via the nuclear Zeeman effect and the hyperfine interaction (Supplementary Note 4). From the fit, we extract a value of A||=70±2 MHz for the hyperfine constant along the SiV− axis, in agreement with previously reported experimental20,24 and theoretical25,26 values (Supplementary Note 4).
Coherent control of the spin
Having determined the frequencies of the electron spin-flipping transitions, we fix the microwave frequency in resonance with one of them and vary the duration of the microwave pulse, as illustrated in Fig. 3a. Figure 3b shows the evolution of the read-out to initialization peak ratio with respect to the microwave pulse duration when the microwave pulse is resonant with the transition between states and (green dots) and when it is resonant with the transition between states and (orange dots). The signal displays Rabi oscillations, sign of the coherent driving of the electronic spin of the SiV− (the nuclear spin orientation remaining unchanged). The upward drift of the oscillations arises from spin-preserving population transfers between the two orbital branches of the ground state. This is confirmed by an eight-level master equation model (Supplementary Note 5), used to reproduce the experimental curve (green and orange curves in Fig. 3b). This phenomenon highlights the importance of inter-branch dynamics at temperatures around a few kelvins. The detuned driving of the electron spin associated with the other nuclear spin orientation and of the transitions in the upper branch of the ground state (containing approximately one-third of the population at 4 K) is responsible for a decreased contrast of the oscillations and their slightly irregular shape (Supplementary Figs 7 and 8). The linear dependence of the Rabi frequency with the square root of the microwave power (Fig. 3c), as well as its variation with respect to detuning (Fig. 3d) confirms the coherent nature of those oscillations. The observed bare Rabi frequency of about 15 MHz is comparable to what is obtained with NV− centres in similar conditions.
Ramsey interferometry
To measure the free induction decay time of the spin directly, we perform microwave Ramsey interferometry. We use a pulse sequence consisting of two π/2 microwave pulses separated by a variable delay (Fig. 4a). We fix the frequency of the microwave pulses such that in one case (Fig. 4b), the microwave frequency is in the middle of the two resonances, corresponding to a detuning of about 27 MHz from each of them, and in the other case (Fig. 4c), the detuning from one resonance equals twice that from the other (36 and 18 MHz, respectively). The measured peak ratio displays oscillations as a function of the free precession interval separating the two pulses. Since the frequency of Ramsey fringes corresponds to the value of the detuning of the microwave frequency, in Fig. 4b, the oscillations due to both resonances add constructively, while in Fig. 4c, they display a beating signal between two frequencies with one being twice the other. The decay of the Ramsey fringes gives a direct measurement of the dephasing time of the electronic spin T2*=115±9 ns at 3.6 K. This value is commensurate with the characteristic time of population transfer between the two orbital branches of the ground state, taken as twice the orbital decay time 2T1,orbital=133±4 ns at 3.6 K in our measurements. Shorter dephasing times have previously been obtained at slightly higher temperatures through coherent population trapping19,20, which provides a lower bound due to additional sources of dephasing, including noise from the driving fields. A strain-induced increase of orbital splitting to an energy at which phonon population is larger27 is also a cause for shorter dephasing times (see below).
Single-phonon-mediated spin dephasing and decay
The strongest candidate for the cause of limited T2* is expected to be phonon excitations from the lower to the upper orbital branches in the ground-state manifold. To verify this directly, we measure the spin dephasing rate 1/T2* as a function of temperature, as shown in Fig. 5a as blue dots. At the temperatures measured in the experiment, the orbital transition rate from the lower to the upper branch of the ground state is expected to be lower than that from the upper to the lower branch by a Boltzmann factor (Supplementary Note 5). Since in our set-up configuration, we underestimate the absolute temperature at the SiV, we take 1/(2T1,orbital) as a reference for the orbital decay rate and display it as grey dots in Fig. 5a. The orbital decay rate is obtained in the absence of magnetic field similarly to the spin population decay presented in Fig. 1b,c, with initialization into the lower orbital branch of the ground state and measurement of the population recovery into the upper branch (Supplementary Note 6). The orbital decay rate increases linearly with temperature, a signature attributed to single-phonon excitation process between the two orbital branches of the ground state20,28. The spin dephasing rate follows closely the orbital decay rate dependence on temperature, manifesting that spin dephasing is dominated by single-phonon-mediated transitions between the orbital branches. We also measure the temperature dependence of the spin decay rate 1/(2T1,spin), as shown in Fig. 5b. Its linear dependence with temperature indicates that it is also dominated by a single-phonon process. The suggested mechanism responsible for spin decay relies on excitation to the upper orbital branch of the ground state through the absorption of a single phonon followed by decay back to the lower branch. Owing to a slight mismatch of spin quantization axes between the two orbitals (Supplementary Note 4), such transitions can result in a spin flip. This mechanism also explains why T1,spin can reach several milliseconds20 when the magnetic field is aligned with the SiV symmetry axis, which otherwise constitutes a competing quantization axis for the spin via the spin–orbit interaction19,23. The phonons responsible for those decoherence mechanisms have a frequency around 50 GHz corresponding to the orbital splitting of the SiV− and still have a significant population around 4 K.
Discussion
In conclusion, we have achieved coherent control of a single SiV− spin with a microwave field, following the identification of spin-flipping transitions through ODMR. We have subsequently implemented Ramsey interferometry to get direct access to the spin dephasing time. The temperature dependence of the dephasing and decay rates reveal that both processes are governed by excitation from the lower to the upper orbital branch of the ground state through single-phonon absorption. This indicates that the coherence times of the SiV− spin will improve significantly by cooling the system to lower temperatures. An alternative approach consists in splitting the orbital branches further apart by applying strain to the SiV−, thus increasing the energy required for phonons to cause decoherence. Those approaches would not necessarily improve significantly the coherence time of the orbital-based qubit, which is limited by phonon absorption and emission processes, simultaneously. The latter could be addressed by decreasing the phonon density of states around the frequency of the orbital splitting, which most likely requires nanostructures with dimensions smaller than about 120 nm, corresponding to half the phonon wavelength. Microwave control of the spin offers a strong advantage compared to all-optical control in that it gives much more flexibility for the orientation of the external magnetic field with respect to the SiV− symmetry axis. In particular, control through microwave pulses allows to bring the magnetic field axis close to alignment with the SiV− axis, thus giving access to cycling optical transitions19 for single-shot read-out of the spin state29. The combination of the optical qualities of the SiV− with the microwave addressing of some of its states also make the SiV− a promising system to be used as a quantum transducer between optical and microwave photons21. Finally, the nuclear spin associated with 29Si can offer the opportunity of a quantum register, if it can be controlled coherently using radio-frequency pulses and hyperfine coupling to the electron spin.
Methods
Sample preparation
The sample used for this experiment is a high-pressure high-temperature type IIa bulk diamond (Element Six) with surface oriented orthogonally to the [111] crystallographic axis. SiV− centres were subsequently created by ion implantation of isotopically purified 29Si+ ions at an implantation energy of 900 keV. Simulations using the stopping range of ions in matter algorithm1 showed that the Si+ stop at 500±50 nm below the diamond surface. Implantation doses were tuned from one implantation site to the other from 109 to 1012 ions per cm2. Following the implantation, the sample was annealed at 1,000 °C in vacuum for 3 h, followed by an oxidation step in air for 1 h at 460 °C. Single SiV− centres have been found in the 1010 ions per cm2 area.
Experimental set-up
The diamond sample is mounted in a closed-cycle liquid helium cryostat (Attodry 1000) reading 3.5 K at the sample and the temperature can be tuned via a resistive heater positioned under the sample mount or using heating caused by the microwave pulses. A superconducting coil around the sample space allows to apply a vertical magnetic field from 0 to 9 T. The optical part of the set-up consists of a home-built confocal microscope mounted on top of the cryostat and a microscope objective with numerical aperture=0.82 inside the sample chamber. The sample is moved with respect to the objective utilizing piezoelectric stages (Attocube) on top of which the sample is mounted. SiV− excitation is performed using a frequency tunable diode laser (Toptica DL pro design) whose frequency is maintained in resonance with an optical transition of the SiV− through continuous feedback from a wavemeter (High Finesse WSU). Optical pulses are generated with an acousto-optic modulator (AAOptoelectronic MT350-A0.12-800) controlled by a delay generator (Stanford Research Instruments DG645). The fluorescence from the SiV− is collected through the same objective. The laser light and SiV− fluorescence from the excited transition are filtered out using a home-built monochromator, and the fluorescence from the remaining transitions is sent to an avalanche photodiode (PicoQuant Tau-Spad). The signal from the avalanche photodiode is sent to a time-to-digital converter (qutools quTAU) triggered by the delay generator. The microwave is generated by a frequency generator (Stanford Research Instruments SG384), pulses are generated with a switch connected to the delay generator used for optical pulses. Microwave pulses are then amplified by a microwave amplifier (Mini-Circuits ZHL-16W-43-S+). They travel through semi-rigid cables installed inside the cryostat. A single copper wire (20 μm diameter) positioned on top of the sample allows the microwave to be radiated to <20 μm away from the studied SiV−.
Experimental details
The results presented in Fig. 1b have been acquired with a repetition rate of 500 kHz and an integration time of 300 s. Those in Fig. 2c were obtained with a repetition rate of 500 kHz and an integration time of 200 s per data point. The results in Fig. 3b were recorded with a repetition rate of 20 kHz to minimize heating from the microwave and an integration time of 7,200 s per data point for the green curve and 3,000 s per data point for the orange curve. Finally, the results in Fig. 4b,c were measured with a repetition rate of 50 kHz (to minimize heating) with 2,000 s integration and 200 kHz with 400 s integration, respectively.
Data availability
The data that support the findings of this study are available from the corresponding author on reasonable request.
Additional information
How to cite this article: Pingault, B et al. Coherent control of the silicon-vacancy spin in diamond. Nat. Commun. 8, 15579 doi: 10.1038/ncomms15579 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Degen, C. L. Scanning magnetic field microscope with a diamond single-spin sensor. Appl. Phys. Lett. 92, 243111 (2008).
Taylor, J. et al. High-sensitivity diamond magnetometer with nanoscale resolution. Nat. Phys. 4, 810–816 (2008).
Dolde, F. et al. Electric field sensing using single diamond spins. Nat. Phys. 7, 459–463 (2011).
Grinolds, M. S. et al. Nanoscale magnetic imaging of a single electron spin under ambient conditions. Nat. Phys. 9, 215–219 (2013).
Mohan, N. et al. In vivo imaging and toxicity assessments of fluorescent nanodiamonds in Caenorhabditis elegans. Nano Lett. 10, 3692–3699 (2010).
Hegyi, A. & Yablonovitch, E. Molecular imaging by optically detected electron spin resonance of nitrogen-vacancies in nanodiamonds. Nano Lett. 13, 1173–1178 (2013).
Wrachtrup, J. & Jelezko, F. Processing quantum information in diamond. J. Phys. Condens. Matter 18, S807–S824 (2006).
Neumann, P. et al. Quantum register based on coupled electron spins in a room temperature solid. Nat. Phys. 6, 249–253 (2010).
Bernien, H. et al. Heralded entanglement between solid-state qubits separated by three metres. Nature 497, 86–90 (2013).
Pfaff, W. et al. Unconditional quantum teleportation between distant solid-state quantum bits. Science 345, 532–535 (2014).
Hensen, B. J. et al. Loophole-free Bell inequality violation using electron spins separated by 1.3 kilometres. Nature 526, 682–686 (2015).
Riedrich-Möller, J. One- and two-dimensional photonic crystal microcavities in single crystal diamond. et al. Nano Lett. 14, 5281–5287 (2014).
Neu, E. et al. Single photon emission from silicon-vacancy colour centres in chemical vapour deposition nano-diamonds on iridium. New J. Phys. 13, 025012 (2011).
Sipahigil, A. et al. Indistinguishable photons from separated silicon-vacancy centers in diamond. Phys. Rev. Lett. 113, 113602 (2014).
Kimble, H. J. The quantum internet. Nature 453, 1023–1030 (2008).
Sipahigil, A. et al. An integrated diamond nanophotonics platform for quantum optical networks. Science 354, 847–850 (2016).
Becker, J. N. et al. Ultrafast all-optical coherent control of single silicon vacancy colour centres in diamond. Nat. Commun. 7, 13512 (2016).
Müller, T. et al. Optical signatures of silicon-vacancy spins in diamond. Nat. Commun. 5, 3328 (2014).
Pingault, B. et al. All-optical formation of coherent dark states of silicon-vacancy spins in diamond. Phys. Rev. Lett. 113, 263601 (2014).
Rogers, L. J. et al. All-optical initialization, readout, and coherent preparation of single silicon-vacancy spins in diamond. Phys. Rev. Lett. 113, 263602 (2014).
Williamson, L. A. et al. Magneto-optic modulator with unit quantum efficiency. Phys. Rev. Lett. 113, 203601 (2014).
Siyushev, P. et al. Optical and microwave control of germanium-vacancy center spins in diamond. Preprint at https://arxiv.org/abs/1612.02947 (2016).
Hepp, C. et al. Electronic structure of the silicon vacancy color center in diamond. Phys. Rev. Lett. 112, 036405 (2014).
Edmonds, A. M. et al. Electron paramagnetic resonance studies of silicon-related defects in diamond. Phys. Rev. B 77, 245205 (2008).
Goss, J. P. et al. Density functional simulations of silicon-containing point defects in diamond. Phys. Rev. B 76, 075204 (2007).
Gali, A. & Maze, J. R. Ab initio study of the split silicon-vacancy defect in diamond: electronic structure and related properties. Phys. Rev. B 88, 235205 (2013).
Arend, C. et al. Photoluminescence excitation and spectral hole burning spectroscopy of silicon vacancy centers in diamond. Phys. Rev. B 94, 045203 (2016).
Jahnke, K. D. et al. Electron–phonon processes of the silicon-vacancy centre in diamond. New J. Phys. 17, 043011 (2015).
Robledo, L. et al. High-fidelity projective read-out of a solid-state spin quantum register. Nature 477, 574–578 (2011).
Acknowledgements
We acknowledge financial support by the University of Cambridge, the ERC Grant PHOENICS, FP7 Marie Curie Initial Training Networks S3NANO and SPIN NANO, and the NQIT programme. This research has been partially funded by the European Community’s Seventh Framework Programme (FP7/2007-2013) under Grant agreement no. 611143 (DIADEMS). B.P. thanks Wolfson College (Cambridge) for support through a Research Fellowship. Ion implantation was performed at and supported by RUBION, the central unit of the Ruhr-Universität Bochum. We thank D. Rogalla for the implantation, and C. Pauly for SIL fabrication. We thank M. Gündoğan, C. Stavrakas, A. Gali, J. Beitner, D. Kara, H.S. Knowles and Y. Kubo for helpful discussions.
Author information
Authors and Affiliations
Contributions
M.A. and C.B. supervised the project; M.M., J.N.B. and C.B. prepared the sample; B.P., D.-D.J., C.H., L.K. and J.N.B. set up the experimental apparatus; B.P. conducted the experiments and analysis of the results, designed the theoretical models, and wrote the manuscript. All authors participated in the writing of the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures, Supplementary Notes and Supplementary References (PDF 1228 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Pingault, B., Jarausch, DD., Hepp, C. et al. Coherent control of the silicon-vacancy spin in diamond. Nat Commun 8, 15579 (2017). https://doi.org/10.1038/ncomms15579
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms15579
This article is cited by
-
Entanglement of nanophotonic quantum memory nodes in a telecom network
Nature (2024)
-
Single photon sources for quantum radiometry: a brief review about the current state-of-the-art
Applied Physics B (2022)
-
Highly tunable magneto-optical response from magnesium-vacancy color centers in diamond
npj Quantum Information (2021)
-
A polarization encoded photon-to-spin interface
npj Quantum Information (2021)
-
Coherent control and high-fidelity readout of chromium ions in commercial silicon carbide
npj Quantum Information (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.