Abstract
Programmable stiff sheets with a single lowenergy folding motion have been sought in fields ranging from the ancient art of origami to modern metamaterials research. Despite such attention, only two extreme classes of crease patterns are usually studied; special MiuraOribased zeroenergy patterns, in which crease folding requires no sheet bending, and random patterns with highenergy folding, in which the sheet bends as much as creases fold. We present a physical approach that allows systematic exploration of the entire space of crease patterns as a function of the folding energy. Consequently, we uncover statistical results in origami, finding the entropy of crease patterns of given folding energy. Notably, we identify three classes of MountainValley choices that have widely varying ‘typical’ folding energies. Our work opens up a wealth of experimentally relevant selffolding origami designs not reliant on MiuraOri, the Kawasaki condition or any special symmetry in space.
Introduction
Programmed instabilities and weak spots have emerged as a powerful tool to design a unique preferred deformation mode into mechanical structures^{1,2}. Such mechanisms are attractive in actuators^{3,4}, metamaterials^{5}, art, architecture^{6,7}, robotics^{8} and other applications at different length scales, because mechanisms require minimal control at the time of deployment; as seen in folding chairs or unfolding umbrellas, the designed deformation is a unique onedimensional path in configuration space through which the structure is naturally guided under any external force. Mechanisms^{9}, even more so than marginal structures^{10}, are delicately poised at the boundary between being rigid and floppy. Despite much recent interest in large extended mechanisms^{6,11,12,13,14,15} and some critical contributions towards the same^{6,16,17,18,19,20}, most work has focused on deformations with high symmetry, and the space of designed disordered deformations remains largely unexplored.
A prominent and ancient example of designed deformation is origami. In particular, rigid origami is the study of stiff sheets that do not bend except at the prescribed creases^{6}. If creases are placed at just the correct angles relative to each other, the sheet as a whole has exactly one allowed deformation in which all the creases fold at the same time. Such sheets can be described^{21} as selffolding because the allowed mode will be actuated by almost any applied force; there is no need to precisely tailor the folding forces. While a general origami pattern might have several folding motions, a selffolding pattern will have a unique extended motion that requires less energy than all others.
However, even in this wellstudied area, most known examples of selffolding crease patterns are in fact rigidly foldable (that is, foldable at precisely zero energy cost). With the exception of some influential works discussed below^{6,16,17,18,19,20}, rigidly foldable crease patterns are often periodic structures made of repeating units, such as MiuraOri and its derivatives^{22,23}. Further, origami design has often been limited to the MountainValley (MV) pattern implicit in MiuraOri^{6,11,24}. Many such studies of rigid origami have also been restricted to socalled flatfoldable or nearflatfoldable vertices^{6,25} (that is, patterns in which all creases fold to angle π simultaneously); the flatfoldability restriction on angles in a crease pattern leads to dramatic algebraic simplifications in rigidity calculations. As a result, MiuraOri derivatives are often rigidly foldable, with the stiff sheet between creases (that is, the ‘faces’) not bending at all when the creases are folded.
Restricting study to the rigid foldable patterns with no face bending misses a larger space of nearperfect mechanisms, in which face bending or energy cost of actuation can be made arbitrarily small. Understanding the full space of crease patterns as a function of folding energy is also crucial for selffolding origami applications^{13}, since applications vary widely in material stiffness and actuation torques (or energies) available. For example, folding a structure made of stiff plates connected by shapememory polymer hinges^{26,27} that provide lowactuation torques might require nearly rigid foldable patterns; but using shapememory alloys^{28} or ionic electroactive polymer^{13} hinges that provide higher torques would allow use of less foldable patterns as well. Similarly, one might wish to prevent accidental deployment of a selffolding hydrogel capsule^{29} due to small pH fluctuations, necessitating less foldable patterns.
Surprisingly little is known about general selffolding origami patterns that are not exactly rigidly foldable. Important contributions include Huffman’s work^{17} on general nvalent vertices and Tachi’s simulation scheme of origami patterns^{6}. Wu and You ^{20} introduced analytic methods to analyse motions of multivertex patterns, extending Belcastro and Hull’s condition for testing rigidfoldability^{18} for nonflat foldable patterns. Tachi went beyond rigid foldability for general patterns by establishing design principles for first order foldability^{16,19}.
Energy scaledependent origami design and statistical properties of typical patterns are the basic building blocks needed for a physically motivated theory of origami^{15}, relevant to both natural^{4} and synthetic^{13,30} systems. In this work, we present a systematic exploration of the space of selffolding crease patterns as a function of folding energy by solving equations in sequence. We further show that MV choices strongly affect foldability, for example, 62% of all MV choices account for 10% of highly foldable patterns. Finally, we find an entropy–energy relationship quantifying the number of crease patterns with given folding energy, describing how many more crease patterns become available for a given increase in available actuation energy, for example, in active hinges^{13}.
Results
Vertex transfer function
As in past work^{6,11,23}, we study patterns made of general 4vertices, like those shown in Fig. 1, since vertices with three or fewer edges are completely rigid while vertices with more than four edges are too soft (that is, have multiple continuous degrees of freedom). Assuming the angles θ_{12},θ_{23},θ_{34},θ_{41} between creases of the vertex add to 2π, we note two primary facts about generalized 4vertices studied earlier^{23}; three out of the four creases must fold in a common orientation (say, Mountain, black in Fig. 2a) with the final oddoneout crease folding the other way (Valley state, red). The final oddoneout crease can be any one of the two creases whose neighbouring angles add to less than π (ref. 23) (Supplementary Fig. 1). Once the discrete oddoneout choice in MV has been made, a 4vertex has exactly one folding degree of freedom (Fig. 2a); the folding angle ρ_{i} at any crease i completely determines any other folding angle ρ_{j}. For two chosen adjacent creases, we symbolically write,
where {θ} are the four inplane angles between creases.
For small fold angles ρ_{i}, we can linearize the above relationship and write
R’s determine the mechanical advantage and dynamic range of folding angles at a vertex.
Similar transfer functions have appeared in the literature over the years^{6,9,15,17,31,32,33}. We emphasize that the transfer functions T, R depend on the MV configuration at the vertex^{23}. Explicit forms of T, R for general 4vertices, including their MV dependence, are presented in Supplementary Note 1.
Loop equation and tuneable stiffness
While a single 4vertex (Fig. 2a) always has one degree of freedom, 4vertices linked to form a quad are generically rigid. In fact, the number of folding degrees of freedom (that is, 12 folding angles ρ_{i}) exactly matches the number of constraints relating these folding angles (three at each vertex). Hence a generic quad has, at best, a discrete set of folded states—the folding motion between such states will generically involve face bending or other such violation of constraints.
Thus, smooth folding motions (modes) require fine tuning of the inplane angles at each vertex (design parameters). An intuitive way to understand the fine tuning required is to write a consistency loop condition for a fold angle ρ, say that of AD (see Fig. 2b), transported around the quad (that is, forming a closed loop),
This nonlinear loop equation needs to be satisfied as a function of ρ, not just at particular values of ρ, in order to have a smooth folding mode. Taylor expanding the right hand side and subtracting ρ,
where f_{1}=ΠR−1. Setting f_{i}=0 ∀i gives—potentially—an infinite set of equations for the design parameters (that is, inplane angles θs)—to have a folding motion to all orders in ρ. Similar loop equations for lowest order foldability were derived by Tachi^{16,19} earlier.
We can write the series of loop equations, defined term by term using the expansion of the transfer function of equation (4). The loop equations are computed explicitly in Supplementary Note 1, while here we write them symbolically as
As shown in Supplementary Note 1, R^{V} is a property of inplane angles at a single vertex V. K^{V}, L^{V},… are products of functions of a single vertex V and of R_{V′} at other vertices V≠V′.
MATLAB Code to compute loop equations to arbitrary order is given as Supplementary Material. For a quad, we verified that the first five equations are independent. Combined with Tachi’s earlier work^{6} that discovered a sixparameter family of rigidly foldable quads with a special symmetry (flat foldability), our work suggests that only the first fiveloop equations are fully independent (Supplementary Note 2), as each loop equation constrains one parameter of the 11d {θ} design space. Here we focus on exploring the full space of creases patterns as a function of foldability and MV choices.
When a quad does not satisfy all loop equations exactly, there is no perfect zeroenergy mode. Allowing a single diagonal fold (Fig. 2c, inset) adds an additional degree of freedom and thus allows any augmented quad (a quad with an additional face diagonal crease) to fold. Measuring the angle ρ_{face} of a freely folding diagonal is a proxy for the face bending energy in the presence of a stiff face (Supplementary Fig. 2).
We note that stretching energy in thin sheets scales the same way with ρ_{face} as bending energy due to a virial theorem^{34,35}, but is expected to be considerably smaller^{34,35}. Further, for thin sheets, bending strain is much larger than stretching strain in lowenergy configurations^{34,35}. Hence, in the following, we model both the energy and geometry by considering only face bending. We later check the validity of this thin sheet approximation using finite element simulations in COMSOL (Fig. 5 and Supplementary Fig. 2). Thickness in real application varies, for example, 0.05 mm thick NiTi sheets of width 50 mm for stents^{28} to 1μmthick GaAs sheets of width 100 μm (ref. 36) for optically actuated mirrors.
To study the relationship between loop equations and face bending quantitatively, we generated random quadrilateral patterns with random MV assignments and used them to solve loop equations order by order using gradient descent. We then added a crease along the face diagonal (Fig. 2c inset), simulated folding of each augmented quad from the unfolded state through small folding angles. In this way, we find,
where ρ_{crease}>0 is the median crease folding angle and the coefficient a_{i} depend on the details (that is, θ_{ij}) of the quad. Thus, as noted in Fig. 1a, the energy required to actuate the designed mode,
drops rapidly with the number n of the exactly satisfied loop equations in the hierarchy. Applying the loop equation hierarchy to different seeds of pattern designs allows discovery of soft foldable patterns devoid of symmetries or order in space (Fig. 1c–e). Such soft patterns may have interesting mechanical properties that distinguish them significantly from the wellstudied MiuraOri pattern (Fig. 1b).
Remarkably, the relationship between face bending ρ_{face} and n strongly persists even if face bending is determined after folding to a large angle Rad. As shown in Fig. 2c, the loop equations when solved in sequence provide a controlled and systematic reduction in face bending over nine orders of magnitude. Solving each successive equation reduces face bending by a factor of ∼10^{2}. In addition, the residue of the leading loop equation ‘not’ exactly solved is highly predictive of face bending. Thus the value of ΣK is predictive of face bending for quads that solve ΠR=1 (orange × ), while ΣL is predictive of face bending for quads that solve ΠR=1 and ΣK=0 (green +) and so on.
Equation (5) thus provides a simple design principle for exploring the crease patterns at any chosen folding energy scale over many orders of magnitude; one simply solves the hierarchy of loop equations to the extent needed. Note that if the creases themselves have nonzero folding energy (for example, due to finite thickness), the folding energy E_{designed} would be bounded from below by such an energy scale; crease patterns cannot be made softer than the intrinsic stiffness of individual creases.
MountainValley choice strongly affects foldability
The loop equations explicitly depend on the MV choices around the quad. The equations can be defined for any given MV choice, opening up the full space of origami patterns. Almost all worktodate on origami is based on MiuraOri’s MV choice. In the following, we show that different MV choices lead to different typical foldability in a statistical sense.
We find that some MV choices are intrinsically more conducive to solving the loop equations than others. Hence we can categorize MV choices by foldability classes. To define these classes precisely, note that at each vertex, one we can define the ‘broken’ direction to be the two longitudinal creases whose MV states differ (key in Fig. 3a). The two creases in the orthogonal ‘unbroken’ direction have the same MV state. The crucial observation is that the creases in the unbroken direction ‘typically’ fold more than the broken creases; hence if i is in the broken direction and j unbroken (see equation (2)).
Intuitively, some MV choices tend to make >1 at two of the 4vertices around a quad and <1 at the other two. These natural MV assignments (Fig. 3a) are most easily compatible with ΠR=1 (equation (5)). Seminatural MV patterns have >1 at three vertices and <1 at the fourth (or viceversa). Finally, unnatural quads have all four >1 (or <1); the inplane θ angles of such a quad must be finetuned to be foldable.
The class of a MV choice thus determines how easy it is to solve the first loop equation ΠR=1. Random quads with Unnatural MV choice are far less foldable than natural or seminatural types (Supplementary Fig. 3).
To quantify this statement, we sampled ∼10^{6} random quads by displacing the vertices of a regular square lattice randomly and independently. We then simulated folding each of these quads with a random folding torque to obtain a folding mode with Rad; we noted the resulting MV data as well as the resultant face bending ρ_{face} for each mode. The histogram, binned by face bending energy log E=log +const is shown in Fig. 3b; we define the entries of this histogram to be the entropy S(E) since gives the number of modes in our random ensemble in the energy range E_{1}−E_{2} (S(E) is defined only up to an additive normalization constant).
First, in Fig. 3b, we note that the total entropy follows a simple law up to quite stiff modes, that we explore further below. We also see that 90% of modes softer than E∼10^{−1} are accounted for by Natural MV configurations, even though such configurations only account for 6/16 of all MV choices. Most of the remaining 10% of soft modes are accounted for by seminatural configurations (8/16 of all choices). Among stiff modes E>10^{−1}, the situation is reversed and seminatural and unnatural configurations form a majority.
Thus, in addition to opening the door to arbitrary MV choices, our work suggests previously unnoticed MV classes that qualitatively differ in their typical foldability. Such widely varying entropy of MV classes suggests important lessons in design; natural configurations can be expected to be more forgiving of error in laying out creases while unnatural configurations need to be highly finetuned to be foldable.
Entropy–energy relationship for large crease patterns
We have seen that a quad’s folding mode can be made arbitrarily soft by solving a series of loop equations; but soft modes are rarer than stiff modes. In the following section we generalize these considerations to large origami meshes.
We sampled crease patterns made of A quads by displacing the vertices of a regular lattice with A inner faces plaquettes randomly and independently, in much the same way as for the quad above. We folded the resulting crease pattern using a torque that selects chosen MV data until max(ρ_{crease})=1 Rad and recorded the resulting face bending ρ_{face} on each quad. We then made a histogram of from a large sampling of such lattices of different sizes; see Fig. 4.
We again define the entropy of crease patterns (now for a given MV) as the logarithm of the above histogram. We find that this entropy is extensive in pattern size A and has a simple form,
where is the (intensive) face bending energy per quad, the ellipsis represent subleading corrections in A and E_{0} is a constant discussed later. By construction, is the number of crease patterns of chosen MV with folding energy within an interval d log around .
We can understand the extensive scaling of entropy S with A and the log E dependence using the loop equations. As seen in Fig. 2c, for a single quad, face bending energy is simply related to loop equation residues, for example, for the green points. On the other hand, we find that the fraction of quads in our random ensemble with loop residue less than is simply proportional to ; this is because patterns in our random ensemble appear to be uniformly distributed in their residues. Hence the total number of patterns of energy less than E scales as . Setting (by our definition of entropy), we find . (Note that the energy is not quite linear in the residue of the first loop equation ΠR−1 in Fig. 2c which is reflected in Fig. 3b as well.)
For large quad meshes, the above arguments apply to each quad since we need to solve loop equations independently for each quad in order to make softer patterns. For example, imposing a loop equation now removes A times as many design variables. Hence we find S=(A/2)log .
Finally, note the log E dependence for large lattices in equation (7) is expected to break down near an energy scale E_{0} (the 10^{5} samples generated here were not sufficient to probe this scale). In particular, Tachi’s results^{6} on rigid foldable patterns imply an entropy of at zero energy.
Our investigations of entropy of folding modes as a function of energy connects to earlier work on crumpling transitions^{37}; consider a sheet with a thermally variable crease pattern held at fixed temperature. At high temperatures, if the entropy of stiff modes is sufficiently high, the sheet might crumple for entropic reasons, even if energetically disfavoured. Earlier analytic approaches were restricted to the entropy of rigidfoldable modes on regular lattices^{38,39} while our work is offlattice and has a continuum energy E. Our entropy S(E), based on quad meshes, only grows logarithmically in energy and hence does not show a first order transition.
The entropy–energy relationship in equation (7) has theoretical and practical implications. In particular, the probability of a random pattern (when folded with a fixed MV) being softer than energy E decreases exponentially with mesh size A but only as a power law with E.
Such results are useful in understanding the tradeoff between energy scales and design freedom. Selffolding origami applications vary greatly in the energy E_{material} needed to bend an uncreased face to a given angle, for example, compare a Young’s modulus of ∼10^{3} Pa for hydrogels^{29} to ∼10^{7} Pa for NiTi alloy in origami stents^{28}. Similarly, actuation mechanisms for active hinges are diverse, including electric^{13}, optical^{36}, thermal^{28} and chemical (pH) (ref. 29) methods. Hence, the actuation energy E_{actuation} provided by active hinges (defined as work done by hinges during folding to 1 Rad) can vary widely, for example, compare torques of ∼6·10^{−3} Nm in 30 mmlong shapememory polymer hinges^{26,27} to 5 × or 400 × that torque in ionic electroactive polymers or shapememory alloys respectively^{13}.
Taken together, E_{actuation}/E_{material} can vary greatly across applications. Our energy–entropy relation shows that the fraction of all patterns suitable for such an application is (for large A).
In addition, micronscale applications might often have a design requirement to prevent inadvertent actuation due to uncontrolled noisy processes of a lower energy scale E_{noise}, for example, spontaneous temperature^{28} or pH fluctuations in hydrogels^{29} or random mechanical kicks. To avoid inadvertent actuation, the folding energy of patterns must be in the ‘Goldilocks’ zone between E_{noise} and E_{actuation}. The fraction of all patterns in the ‘Goldilocks’ zone can be computed to be (E_{actuation}/E_{material})^{A/2}−(E_{noise}/E_{material})^{A/2} for large A.
Equation (7) thus provides a basic guideline for how many more patterns become available if the actuation energy E_{actuation} is raised, say, at the cost of higher power input^{26} or if the energy of uncontrolled processes E_{noise} is lowered.
While our results were derived for the simplest random ensemble, they can be adapted to other ensembles of patterns relevant to specific applications.
Face bending along folding modes
In this work, face bending was measured by augmenting the quad with a diagonal crease (Supplementary Methods) and then setting crease folding to one representative angle (∼1 Rad) in equation (6). It is reasonable to expect face bending behaves as nonlinear function of crease folding for large folding angles. In this section we study the face bending of folding modes for variable crease folding amplitudes.
In Fig. 5a, we show face bending as a function of crease folding for four different folding modes. We see that the loop equation residue is a good predictor of face bending up to crease folding of ∼π/2 Rad. For larger folding, strongly nonlinear effects kick in; the initially soft red mode become stiffer than others rapidly, while other modes show nonmonotonic behaviour. Nonmonotonic bistable behaviour has been seen before in experiments on highly symmetric flatfoldable patterns^{11,22}.
To visualize what face bending stresses might look like in a real material without a diagonal crease, we show results of a finite element simulation in COMSOL in Fig. 5b of two select modes from Fig. 5a. Unlike our simplified model, this simulation accounts for stretching, bending of all nine faces, finite thickness of the material and finite width of creases. While our simple diagonal crease model cannot capture the precise folding energies seen in the COMSOL simulation, we see that the bending stress is localized to a furrow along the diagonal, a result expected for thin sheets^{34} (Supplementary Fig. 2 for more analysis and simulations). Further, when folded in COMSOL with a small but fixed folding force (note: not to fixed angle), the red mode shows higher stresses, implying that it is softer than the green mode, in agreement with our face bending model in Fig. 5a.
Discussion
In this work, we have studied selffolding origami meshes as a function of folding energy, free from assumptions about MV data or symmetries such as flatfoldability. We found a design principle for selffolding patterns of arbitrary stiffness in terms of a series of loop equations applied to each quad in the pattern. These general patterns can exhibit diverse curvatures in three dimensions as compared to MiuraOri. Related recent work^{11} has achieved remarkable three dimensional structures by gradual modulation of MiuraOri patterns on length scales much larger than the repeating unit cell; however, our work allows design on arbitrary length scales without being limited to any underlying repetitive motif.
MV data were found to greatly affect foldability. Natural MV types are typically much softer than Seminatural or Unnatural types. This notion informs design decisions for soft selffolding modes, both as soft Natural modes are more numerous, but also as they are projected to be less prone to large stiffness fluctuations due to manufacturing errors.
We complemented these design principles with a statistical understanding of the space of all large quad meshes; we determined the total entropy of crease patterns of any given folding energy. Such a relationship tells us the number of patterns with a ‘Goldilocks’ folding energy that is lower than available actuation energy but high enough to prevent inadvertent actuation due to noisy uncontrolled processes.
While our work focused on quad meshes for concreteness, the loop equation hierarchy applies to any pattern made of arbitrary combinations of polygons, provided all vertices have valence four. We leave investigations of mechanisms with other topologies to future work.
In conclusion, understanding the space of crease patterns as a function of an energy scale combined with statistical results on the foldability of ‘typical’ patterns are crucial ingredients in developing a physically relevant theory of selffolding origami.
Data availability
Data supporting the findings of this study are available from the corresponding author on request.
Additional information
How to cite this article: Pinson, M. B. et al. Selffolding origami at any energy scale. Nat. Commun. 8, 15477 doi: 10.1038/ncomms15477 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Pellegrino, S. Deployable Structures Springer (2014).
Reis, P. M., Jaeger, H. M. & van Hecke, M. Designer matter: a perspective. Extreme Mech. Lett. 5, 25–29 (2015).
Lee, H., Xia, C. & Fang, N. X. First jump of microgel; actuation speed enhancement by elastic instability. Soft Matter 6, 4342–4345 (2010).
Forterre, Y., Skotheim, J. M., Dumais, J. & Mahadevan, L. How the venus flytrap snaps. Nature 433, 421–425 (2005).
Shim, J., Perdigou, C., Chen, E. R., Bertoldi, K. & Reis, P. M. Bucklinginduced encapsulation of structured elastic shells under pressure. Proc. Natl Acad. Sci. USA 109, 5978–5983 (2012).
Tachi, T. in Proceedings of Evolution and Trends in Design, Analysis and Construction of Shell and Spatial Structures (eds Alberto, D. & Carlos, L.) 2295–2305 (Universidad Politecnica de Valencia, Spain, 2010).
Hoberman, C. Reversibly expandable doublycurved truss structure. US Patent Office. Patent number: US4942700 A (1990).
Merlet, J. P. Parallel Robots Springer Science & Business Media (2012).
Demaine, E. D. & O’Rourke, J. Geometric Folding Algorithms: linkages, Origami, Polyhedra Cambridge University Press (2007).
Liu, A. J. & Nagel, S. R. The jamming transition and the marginally jammed solid. Annu. Rev. Cond. Matter Phys. 1, 347–369 (2010).
Dudte, L. H., Vouga, E., Tachi, T. & Mahadevan, L. Programming curvature using origami tessellations. Nat. Mater. 15, 583–588 (2016).
Tachi, T. Geometric considerations for the design of rigid origami structures. Proc. Int. Assoc. Shell Spatial Struct. Symp. 12, 458–460 (2010).
PerazaHernandez, E. A., Hartl, D. J., Malak, Jr R. J. & Lagoudas, D. C. Origamiinspired active structures: a synthesis and review. Smart Mater. Struct. 23, 094001 (2014).
Chen, Y., Peng, R. & You, Z. Origami of thick panels. Science 349, 396–400 (2015).
Evans, A. A., Silverberg, J. L. & Santangelo, C. D. Lattice mechanics of origami tessellations. Phys. Rev. E 92, 013205 (2015).
Tachi, T. Simulation of rigid origami. Origami 4, 175–187 (2009).
Huffman, D. A. Curvature and creases: a primer on paper. IEEE Trans. Computers 25, 1010–1019 (1976).
Belcastro, S.M. & Hull, T. C. Modelling the folding of paper into three dimensions using affine transformations. Linear Algebra Appl. 348, 273–282 (2002).
Tachi, T. Design of infinitesimally and finitely flexible origami based on reciprocal figures. J. Geom. Graph. 16, 223–234 (2012).
Wu, W. & You, Z. in Proceedings of the Royal Society of London A: mathematical, Physical and Engineering Sciences Vol. 466, 2155–2174The Royal Society (2010).
Na, J.H. et al. Programming reversibly selffolding origami with micropatterned photocrosslinkable polymer trilayers. Adv. Mater. 27, 79–85 (2015).
Silverberg, J. L. et al. Origami structures with a critical transition to bistability arising from hidden degrees of freedom. Nat. Mater. 14, 389–393 (2015).
Waitukaitis, S., Menaut, R., Chen, B. G.g. & van Hecke, M. Origami multistability: from single vertices to metasheets. Phys. Rev. Lett. 114, 055503 (2015).
Miura, K. Method of packaging and deployment of large membranes in space. Inst. Space Astronaut. Sci. Rep. 618, 1–9 (1985).
Bern, M. & Hayes, B. in Proceedings of the 7th Annual ACMSIAM Symposium on Discrete Algorithms 175–183 (Atlanta, GA, USA, 1996).
Felton, S. M. et al. Selffolding with shape memory composites. Soft Matter 9, 7688–7694 (2013).
Hawkes, E. et al. Programmable matter by folding. Proc. Natl Acad. Sci. USA 107, 12441–12445 (2010).
Kuribayashi, K. et al. Selfdeployable origami stent grafts as a biomedical application of nirich TiNi shape memory alloy foil. Mater. Sci. Eng. A 419, 131–137 (2006).
Shim, T. S., Kim, S.H., Heo, C.J., Jeon, H. C. & Yang, S.M. Controlled origami folding of hydrogel bilayers with sustained reversibility for robust microcarriers. Angew Chem. Int. Ed. Engl. 51, 1420–1423 (2012).
Lang, R. J. The science of origami. Phys. World 20, 30 (2007).
Hull, T. in Project Origami: activities for Exploring Mathematics 2nd edn CRC Press (2012).
Huffman, D. A. Curvature and creases: a primer on paper. IEEE Trans. Comput. C25, 1010–1019 (1976).
Chen, B. Gg. et al. Topological mechanics of origami and kirigami. Phys. Rev. Lett. 116, 135501 (2016).
Lobkovsky, A., Gentges, S., Li, H., Morse, D. & Witten, T. Scaling properties of stretching ridges in a crumpled elastic sheet. Science 270, 1482 (1995).
Witten, T. Stress focusing in elastic sheets. Rev. Mod. Phys. 79, 643 (2007).
Zanardi Ocampo, J. M. et al. Optical actuation of micromirrors fabricated by the microorigami technique. Appl. Phys. Lett. 83, 3467 (2003).
Kantor, Y. & Nelson, D. R. Crumpling transition in polymerized membranes. Phys. Rev. Lett. 58, 2774 (1987).
Bowick, M., Di Francesco, P., Golinelli, O. & Guitter, E. Threedimensional folding of the triangular lattice. Nucl. Phys. B 450, 463–494 (1995).
David, F. & Guitter, E. Crumpling transition in elastic membranes: renormalization group treatment. Europhys. Lett. 5, 709 (1988).
Acknowledgements
We thank Michael Brenner, Levi Dudte, Heinrich Jaeger, Anand Murugan and Sidney Nagel for discussions and feedback. E.C. acknowledges NSF MSPRF grant DMS1204686. M.B.P. was supported by a ConocoPhillips fellowship from the American Australian Association. We acknowledge NSFMRSEC 1420709 for funding and the University of Chicago Research Computing Center for computing resources.
Author information
Authors and Affiliations
Contributions
All authors helped develop the theoretical tools. A.C.F. performed the experiment. M.S., M.B.P., A.M. carried out simulations, analysis and wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures, Supplementary Notes, Supplementary Methods and Supplementary References (PDF 3078 kb)
Supplementary Movie 1
Folding motion of the pattern of Figure 1c. (MP4 8682 kb)
Supplementary Movie 2
Folding motion of the pattern of Figure 1d. (MP4 5811 kb)
Supplementary Movie 3
Folding motion of the pattern of Figure 1e. (MP4 7163 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Pinson, M., Stern, M., Carruthers Ferrero, A. et al. Selffolding origami at any energy scale. Nat Commun 8, 15477 (2017). https://doi.org/10.1038/ncomms15477
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms15477
Further reading

Harnessing the power of chemically active sheets in solution
Nature Reviews Physics (2022)

Exploring multistability in prismatic metamaterials through local actuation
Nature Communications (2019)

Shaping the topology of folding pathways in mechanical systems
Nature Communications (2018)

Multistep selfguided pathways for shapechanging metamaterials
Nature (2018)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.