Néel skyrmions are of high interest due to their potential applications in a variety of spintronic devices, currently accessible in ultrathin heavy metal/ferromagnetic bilayers and multilayers with a strong Dzyaloshinskii–Moriya interaction. Here we report on the direct imaging of chiral spin structures including skyrmions in an exchange-coupled cobalt/palladium multilayer at room temperature with Lorentz transmission electron microscopy, a high-resolution technique previously suggested to exhibit no Néel skyrmion contrast. Phase retrieval methods allow us to map the internal spin structure of the skyrmion core, identifying a 25 nm central region of uniform magnetization followed by a larger region characterized by rotation from in- to out-of-plane. The formation and resolution of the internal spin structure of room temperature skyrmions without a stabilizing out-of-plane field in thick magnetic multilayers opens up a new set of tools and materials to study the physics and device applications associated with chiral ordering and skyrmions.
Magnetic skyrmions are topologically non-trivial chiral spin textures present in systems with a strong Dzyaloshinskii–Moriya interaction (DMI) and a spatial extent of only tens to a few hundred nanometres. The discovery of skyrmions in bulk non-centrosymmetric magnets and thin films has led to the proposal of a variety of skyrmionic devices, in which the skyrmion is used as the basic information carrier in next-generation logic and memory devices1,2,3,4,5,6,7,8,9. Thin film heavy metal/ferromagnetic (HM/FM) bi- and multilayers have emerged as an ideal candidate for the development of such devices due to their tunability through a variation of the constituent components and relative layer thicknesses. Further, the spin Hall physics associated with the heavy metal underlayer allows for straightforward manipulation of the local magnetic state2,10,11. In these systems, strong interfacial spin–orbit coupling results in a large interfacial DMI (iDMI), characterized by the DMI constant, D. The iDMI acts as an effective symmetry breaking in-plane field, HDMI, which can stabilize Néel walls of a fixed chirality12. For films that satisfy the condition , where Hk is the anisotropy field, a stable Néel skyrmion can form13,14. Néel skyrmions are characterized by the magnetization rotating from one out-of-plane direction to the other radially from the skyrmion centre, where the sense of rotation is set by the skyrmion chirality.
Néel skyrmions have been experimentally observed at room temperature in a variety of the aforementioned bilayers. These skyrmions have been limited to sizes well over 100 nm, making them ill-suited for practical applications and, at these length scales, their claim as skyrmions is still controversial10,15,16. Furthermore, the total magnetic thickness in these systems is below 1.5 nm, posing challenges for thermal stability. Recently, Moreau-Luchaire et al.11 demonstrated sub-100 nm magnetic skyrmions in dipolar coupled Pt/Co/Ir multilayers, in which the assymetric Pt and Ir layers result in an enhanced HDMI strong enough to generate skyrmions in films as thick as 6.6 nm. However, to date, no skyrmions have been observed in thick ferromagnetic multilayers in which the disperate magnetic layers are exchange coupled. Furthermore, previous Néel skyrmion observations required either the presence of an out-of-plane bias field provided by either an external field or through dipole coupling to an adjacent ferromagnetic layer,10,11,15,16,17 or careful tuning of a geometric confining potential to stabilize the skyrmion structure18. Cobalt/palladium (Co/Pd) is a prototypical exchange coupled multilayer, which shows strong spin–orbit coupling effects in the bulk as evidenced by the large spin–orbit torque (SOT) efficiencies in nanowire geometries19,20. However, in HM/FM/HM systems, the contributions to the DMI from top and bottom interfaces is predicted to cancel out for identical HM layers11,21,22.
In this work, we have imaged the formation of room temperature Néel skyrmions in a symmetric 6.7-nm-thick Co/Pd multilayer with Lorentz transmission electron microscopy (L-TEM). Importantly, the size of the observed skyrmions is significantly smaller than previously reported systems in which non-multilayer films are used15,16,23, and of nearly identical extent as those measured in Ir/Co/Pt multilayers11. Following nucleation with an external magnetic field, the observed skyrmions persist even after removal of the external field and without geometric confinement. Furthermore, the film studied in this work is unique in that skyrmions are observed in an exchange-coupled system with a large magnetic volume despite utilizing symmetric interfaces, that is, Pd at both top and bottom interfaces for each layer as well as Pt layers at both outer surfaces. This work opens up a new set tools in which skyrmions can be designed, tuned and studied for use in possible spintronic devices.
Imaging Néel skyrmions with L-TEM
In comparison with other techniques such as Kerr microscopy and X-ray methods, which are limited by spatial resolution, L-TEM affords the advantage of a spatial resolution below 5 nm24,25,26. Furthermore, the scattering cross-section for electrons is significantly larger than that of X-rays27, allowing for improvements in signal contrast in the ultrathin films which are typical of skyrmion systems. The contrast formed in L-TEM is traditionally explained as the result of the deflection of the electron beam due to an in-plane magnetic field, which leads to either increased or decreased contrast at a region of varying magnetization. For Néel-type domain boundaries in materials with perpendicular magnetic anisotropy, the Lorentz deflection follows the length of the wall, and suggests that no magnetic contrast is observed when the film is normal to the beam propagation direction. Using the full electron-wave treatment of the electron beam within the small defocus limit28,29, the contrast in L-TEM resulting from the underlying magnetic structure is expressed by the curl of the magnetization along the beam propagation axis (), given by , where I(r, Δ) is the normalized intensity, Δ the defocus, e the electron charge, μ0 the vacuum permeability, λ is the electron wavelength, h Planck’s constant, t the film thickness and M(r) the film magnetization. The valid defocus range is determined by the region which the contrast transfer function is linear with defocus, and is dependent on a variety of microscope specific parameters such as beam divergence angle29. For a Néel skyrmion, the curl of the magnetization lies completely in the plane of the sample (Fig. 1a–d). Hence, with zero sample tilt, a Néel skyrmion produces no contrast,10 and therefore, while used extensively in the imaging of Bloch skyrmions4,5,30, L-TEM has not been utilized to observe Néel skyrmions. However, by tilting the sample with respect to the beam direction, a projection of the curl on the beam axis proportional to the degree of tilt can be obtained, enabling skyrmion contrast. This contrast corresponds to the projection of the magnetization that is directed out of the sample plane orthogonal to the beam direction.
Figure 1e–j shows a simulated tilt series of Néel skyrmion contrast in L-TEM31,32. As an input, a micromagnetically simulated Néel skyrmion of radius nominally 100 nm was used. It is apparent from the magnetization curl that the observed signal asymmetry is independent of the direction by which the magnetization rotates from the bulk state to the skyrmion centre; therefore, the chirality itself cannot be determined unless the sign of the DMI is known a priori. In the tilted geometry, L-TEM is sensitive to the Néel skyrmion polarity, defined as +1 when the magnetization at the skyrmion centre points up with respect to the film, and −1 when pointing down. This is in contrast to the signal obtained for a Bloch skyrmion, in which case L-TEM is sensitive to the helicity (that is, the sense of rotation of the skyrmion magnetization from the +z to −z direction), and not the polarity33,34,35. The contrast asymmetry of the Néel skyrmion reverses depending on the sign of the tilt, and disappears for zero tilt. At a given tilt angle, the largest contrast asymmetry occurs where the in-plane component of the magnetization curl is perpendicular to the tilt axis. Therefore, the distance between the point of minimum and maximum intensity represents the width of the projected skyrmion in the plane normal to the beam propagation direction.
Experimental observation of skyrmions in Co/Pd multilayers
To image nanoscale domain features with in situ L-TEM, including skyrmion structures, MgO (2 nm)/Pt (4 nm)/Co (0.7 nm)/[Pd (0.5 nm)/Co (0.7 nm)]5/Pt (2 nm) thin films, where the 5 denotes the layer repetition number as shown in Fig. 2a, were grown both on a 0.5-mm-thick Si substrate for magnetization and structural characterization measurements and on 100-nm-thick Si3N4 electron transparent membranes for TEM imaging and in situ magnetization experiments. High-resolution scanning TEM was performed on a cross-section of the deposited film and showed distinct Co/Pd layers (Fig. 2b). Electron energy loss spectroscopy (EELS) further confirmed the well separated nature of the respective Co and Pd layers (Fig. 2c). The films exhibit perpendicular magnetic anisotropy at room temperature with an effective anisotropy, Ku,eff=0.24 MJ m−3 and a saturation magnetization, Ms=880 kA m−1, as determined by vibrating sample magnetometry (VSM; Fig. 2d,e). For the determination of Ms, the Pd layer thickness is included in total magnetic volume as hybridization of the d-shell electrons at the Co/Pd interfaces results in a non-negligible magnetic moment in the Pd layer20. Before L-TEM imaging, the magnetization was saturated along the beam propagation direction (defined as the −z direction; Fig. 2f).
L-TEM imaging was performed at a defocus of −1.2 mm, at room temperature, and zero field36. A tilt series taken at −15°, 0° and 15° is shown in Fig. 3a–c, respectively. The contrast, identical to that of Néel skyrmions shown in Fig. 1h–j, indicates the presence of skyrmions stable at room temperature. The intensity asymmetry shows a polarity of +1, as expected from the initialization procedure. A line profile across the structure is shown in Fig. 3d, with a distance between maximum and minimum intensities giving a width of 90 nm. At this length scale, dipolar energy alone has been suggested to be insufficient to stabilize domains of this size11,37. We show, in the following sections, that due to the large DMI in this system, these domains are stable and chiral, consistent with that of Néel skyrmions.
To relate directly the L-TEM images to the structure of the skyrmion as well as map its internal spin structure, we have performed a phase reconstruction utilizing the differential transport-of-intensity (D-TIE) method38. This method relates the change in phase of the electron beam due to the Aharonov–Bohm effect to the difference in contrast between two magnetic states.25,39 We utilize an reference state of a saturated film along the +z direction, and a final state of an isolated Néel skyrmion with a polarity of −1. Both images were acquired with a tilt of −30° to the x axis. The use of D-TIE in this case has the primary advantage of allowing for the removal of the electrostatic contribution to the TIE signal from the film and substrate. As a result, a Néel skyrmion would appear as a dipole-like structure in D-TIE, with the projection of the magnetic induction appearing normal to the tilt axis. Furthermore, the total difference between the final and reference state also includes stray fields originating from the skyrmion core, as diagrammatically shown in Fig. 4a. Tilting the sample results in a projection of the magnetic structure and associated stray field into the plane normal to the beam direction. Hence, the phase reconstruction should show two flux closure loops in addition to a uniformly magnetized core region. The D-TIE reconstruction exhibits this structure, and confirms the presence and expected Néel skyrmion, as shown in Fig. 4b–e. From the phase reconstruction, we find the central core in which the spin structure is nearly uniform along the +z direction extends nominally 25 nm, with the total extent of the skyrmion, inclusive of magnetization rotation, to be ∼90 nm. It should be noted that, due to small thickness of these films, and hence weak magnetic signal, large defocus values were necessary. Large defocus values can artificially increase the apparent skyrmion size due to delocalization effects29. However, for the experimental conditions used here, this effect is expected to be minimal40,41.
These nanoscale skyrmions were observed without the presence of an out-of-plane stabilizing field or geometric confining potentials, which were necessary in prior works. We find that stable zero-field skyrmions in unpatterned thin films are possible within a narrow band of values of the DMI constant, D. We use micromagnetics to determine this range, as shown in Fig. 5, and obtain an approximate magnitude of D, assuming an exchange stiffness constant A=10.0±2.5 pJ m−1, consistent with the range of previous measurements in Co/Pd multilayers42. This results in an estimate of |D|=2.0±0.3 mJ m−2, similar to values obtained in other systems exhibiting a skyrmion structure. Outside of a narrow band of values of |D|, the skyrmion structure is no longer stable at small fields, as reported in ref. 11, and shown in Fig. 5b–d.
To verify that only one chirality of skyrmion is stable for a given sign of D, we have further utilized micromagnetics to simulate two skyrmions with opposite chiralities but with an identical polarity by seeding a skyrmion with opposite signs of D. Ms, Ku,eff and A were fixed at 880 kA m−1, 0.24 MJ m−3 and 10 pJ m−1, respectively. These states were then used as inputs to a single skyrmion state with a D=2.0±0.3 mJ m−2. While the seeded state corresponding to a D>0 skyrmion does not change, the D<0 skyrmion is unstable and transforms into a state identical to that of the initialized D>0 skyrmion (Supplementary Fig. 1 and Supplementary Note 1). This coupled with the fact that skyrmions are stable only above a critical value of D indicates that these structures must be chiral.
The large DMI found in our work is counter to previous reports, which suggest that the DMI strength in a symmetric multilayer stack is near zero as the contributions between the top and bottom Pd layers for each Co layer should cancel11,21. However, in Co/Pd multilayers, the large lattice mismatch between Co and Pd results in a lattice distortion that is 30% larger at the Co/Pd interface compared to the Pd/Co interface43, breaking the symmetry of the two interfaces and providing a mechanism for a non-zero DMI. The inequivalence between the interfaces was previously suggested as the mechanism for the large SOT efficiencies found in Co/Pd multilayer nanowires19.
To determine the sign of the D, which sets the chirality of the structures observed in our films, as well as rule out Pt as the origin for the strong positive DMI in the Co/Pd multilayer, we have performed polar Kerr microscopy to measure the asymmetric domain wall creep velocity21,44 in a MgO (2 nm)/Pt (4 nm)/Co (0.32)/[Pd (0.34 nm)/Co (0.32 nm)]N/MgO (2 nm)/SiO2 (3 nm) multilayer, where N represents the multilayer repetition number that is varied from two to five, as shown in Fig. 6a–d. For the measurements, a semicircular domain is nucleated around a pinning centre in the as deposited film, while a field is applied 5° from the sample plane. Domain expansion is driven by the out-of-plane component of the field. The in-plane component breaks the rotational symmetry, a result of strong DMI in these films. The sign and strength of D, determined by this asymmetry (as detailed in Supplementary Note 2), is shown in Fig. 6e. For the N=2 sample, we find D<0, indicative of a large, negative DMI strength, as is expected for a Pt underlayer45,46. However, for N>2, the asymmetry reverses, and a large D>0 is found. This sign change can only be explained by a large, positive contribution to D from the Co/Pd multilayer structure, and allows us to further exclude Pt as the source of the strong positive DMI in this work21,47.
Magnetization reversal and the emergence of skyrmions
To analyse the emergence of skyrmion ordering in the Co/Pd multilayer, and observe the role that iDMI plays in this process, the film magnetization was initialized in the +z direction, and then imaged while a magnetic field was applied nominally 30° from the −z direction. While a component of the magnetic field in the plane of the sample is present during the imaging process, it is not predicted to cause significant changes to the observed domain structure48. Figure 7 and Supplementary Movie 1 show the domain structure during in situ application of a magnetic field opposite the initialization direction. After initial application of small fields, snake-like structures emerge with contrast equivalent to 360° Néel domains, with a width of nominally 100 nm (Fig. 7a) similar to the contrast expected for the domain pattern outlined in Fig. 5d. A simulated L-TEM image for Fig. 5d is shown in Supplementary Fig. 2. Similar contrast has also been observed for homochiral Néel walls in thin film Pt/Co/AlOx samples in L-TEM, albeit with much larger domain spacings12. Minor increases in the field lead to the nucleation of a greater number of such domains (Fig. 7b,c), until the film becomes densely packed (Fig. 7d) making distinguishing individual domains difficult. This occurs over a narrow range of about 10 mT and corresponds to the initial drop in net magnetization seen in the VSM measurements in Fig. 2d.
Once formed, the domains are stable to significantly higher fields and do not merge with neighbouring walls, providing evidence of their chiral nature, as argued in ref. 12. For two walls of different chirality, there is an attractive interaction to each other, driving them to merge and create larger single domain regions, while the opposite is true for domain walls of the same chirality49. To annihilate Néel domain walls, the magnetization must rotate away from the easy axis defined by the iDMI. This is schematically shown in Fig. 7g. The size of the observed Néel domains are consistently below 200 nm, indicating that there is no significant merging of neighbouring domains and that the domains possess a single chirality, consistent with the effects of strong iDMI. The effect of these chiral domains on the macroscopic magnetization behaviour is seen in the VSM measurement in Fig. 2d, where the magnitude of the slope of the reversal clearly decreases after the film becomes saturated with 360° Néel walls, indicating the presence of an intermediate state where the domain wall density reaches a maximum due to the large energy barrier necessary to form additional chiral Néel walls with spacing below a few hundred nanometres. Increasing of the field breaks the 360° Néel domains into smaller regions (Fig. 7e), eventually transforming into skyrmions before the saturation field (Fig. 7f). This results in a mixed FM/skyrmion state. The skyrmion state remains after removing the applied field.
To verify thermal stability, we have also initialized a state with a high skyrmion density, then waited 3 h before subsequent imaging. No changes in the domain structure were observed, indicating the state is thermally stable at zero field. A note of caution here is warranted, as it appears that preferential domain propagation exists along the applied field direction in the early stages of the reversal. This is an artefact resulting from the lack of contrast associated with Néel walls along the tilt axis, and disappears when images are combined from both tilt axis. This issue is discussed in Supplementary Note 3 as well as Supplementary Figs 3 and 4.
In summary, we have used L-TEM to track the formation of nanoscale Néel skyrmions in Co/Pd multilayers. The size and spin structure of the Néel skyrmion have been confirmed through phase reconstruction with D-TIE. Further, these Néel skyrmions are observed with zero bias field in an unpatterned film, an important step in the design of functional devices based on magnetic skyrmions. The presence of zero-field stable skyrmions, coupled with measurements of asymmetric domain wall creep velocities in Co/Pd multilayers, has allowed us to estimate D=2.0±0.3 mJ m−2. Similar multilayers, which have already shown large SOT efficiencies in device geometries, merit further study in regards to skyrmion-based logic and storage devices.
Thin film growth and imaging
Thin film samples were grown via d.c. (metal layers) and r.f. (oxide layers) magnetron sputtering in an argon environment, with a base pressure of 7 × 10−9 torr. TEM measurements were performed at the Brookhaven National Laboratory, using both a specially designed JEOL 2100F-LM and a JEOL ARM 200F microscope. Zero-field imaging was performed in the JEOL 2100F-LM, which has a residual out-of-plane field in the specimen area of <0.4 mT and a spherical aberration coefficient, Cs, of 109 mm. Reversal experiments were carried out in the JEOL ARM 200F, in which the out-of-plane magnetic field was tuned by varying the strength of the microscopes objective lens. The magnetic field at a given objective lens current was determined by mounting a Hall probe onto a TEM sample holder and measuring the Hall signal as the objective lens current was varied. Principal component analysis was used to smooth the EELS line profiles with a Savitzky–Golay filter.
Simulated Lorentz images are taken from micromagnetically simulated skyrmion states in a 2 μm disc with a 4.2 nm thickness using object-oriented micromagnetic framework with a cell size of 2 nm × 2 nm × 4.2 nm cell, D=2.0 mJ m−2, Ku,eff=0.24 MJ m−3, A=10 pJ m−1 and Ms=880 kA m−1. The skyrmion was used as input for Lorentz image simulations using micromagnetic analysis to Lorentz TEM simulation, with input parameters taken from the specs of the JEOL 2100F-LM used in this work and a defocus of −1 mm, at tilt angles varying from −30° to 30° (Supplementary Movie 2). Micromagnetic simulations to obtain an estimate of D were performed using the experimentally determined Ms and Ku,eff. While D and A were varied over a range of values. A cell size equal to 2 nm × 2 nm × 6.7 nm and a damping of α=0.5 were used. More details, including how variations in anisotropy can affect the estimate of D, can be found in Supplementary Notes 4 and 5, as well as in Supplementary Fig. 5.
The data of this study can be obtained from the corresponding authors on request.
How to cite this article: Pollard, S. D. et al. Observation of stable Néel skyrmions in Co/Pd multilayers with Lorentz transmission electron microscopy. Nat. Commun. 8, 14761 doi: 10.1038/ncomms14761 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Münzer, W. et al. Skyrmion lattice in the doped semiconductor Fe1−xCox Si. Phys. Rev. B 81, 041203 (2010).
Sampaio, J., Cros, V., Rohart, S., Thiaville, A. & Fert, A. Nucleation, stability and current-induced motion of isolated magnetic skyrmions in nanostructures. Nat. Nanotechnol. 8, 839–844 (2013).
Fert, A., Cros, V. & Sampaio, J. Skyrmions on the track. Nat. Nanotechnol. 8, 152–156 (2013).
Yu, X. Z. et al. Real-space observation of a two-dimensional skyrmion crystal. Nature 465, 901–904 (2010).
Yu, X. Z. et al. Near room-temperature formation of a skyrmion crystal in thin-films of the helimagnet FeGe. Nat. Mater. 10, 106–109 (2011).
Romming, N. et al. Writing and deleting single magnetic skyrmions. Science 341, 636–639 (2013).
Zhou, Y. & Ezawa, M. A reversible conversion between a skyrmion and a domain-wall pair in a junction geometry. Nat. Commun. 5, 4652 (2014).
Zhang, X. et al. Skyrmion–skyrmion and skyrmion-edge repulsions in skyrmion-based racetrack memory. Sci. Rep. 5, 7643 (2015).
Wiesendanger, R. Nanoscale magnetic skyrmions in metallic films and multilayers: a new twist for spintronics. Nat. Rev. Mater. 1, 16044 (2016).
Jiang, W. et al. Mobile Néel skyrmions at room temperature: status and future. AIP Adv. 6, 055602 (2016).
Moreau-Luchaire, C. et al. Additive interfacial chiral interaction in multilayers for stabilization of small individual skyrmions at room temperature. Nat. Nanotechnol. 11, 444–448 (2016).
Benitez, M. J. et al. Magnetic microscopy and topological stability of homochiral Néel domain walls in a Pt/Co/AlOx trilayer. Nat. Commun. 6, 8957 (2015).
Emori, S. et al. Spin Hall torque magnetometry of Dzyaloshinskii domain walls. Phys. Rev. B 90, 184427 (2014).
Thiaville, A., Rohart, S., Jué, É., Cros, V. & Fert, A. Dynamics of Dzyaloshinskii domain walls in ultrathin magnetic films. Europhys. Lett. 100, 57002 (2012).
Jiang, W. et al. Blowing magnetic skyrmion bubbles. Science 349, 283–286 (2015).
Woo, S. et al. Observation of room-temperature magnetic skyrmions and their current-driven dynamics in ultrathin metallic ferromagnets. Nat. Mater. 15, 501–506 (2016).
Chen, G., Mascaraque, A., N’Diaye, A. T. & Schmid, A. K. Room temperature skyrmion ground state stabilized through interlayer exchange coupling. Appl. Phys. Lett. 106, 242404 (2015).
Boulle, O. et al. Room-temperature chiral magnetic skyrmions in ultrathin magnetic nanostructures. Nat. Nanotechnol. 11, 449–454 (2016).
Jamali, M. et al. Spin–orbit torques in Co/Pd multilayer nanowires. Phys. Rev. Lett. 111, 246602 (2013).
Smith, D. et al. Magnetization reversal and magnetic anisotropy in patterned Co/Pd multilayer thin films. J. Appl. Phys. 103, 023920 (2008).
Hrabec, A. et al. Measuring and tailoring the Dzyaloshinskii–Moriya interaction in perpendicularly magnetized thin films. Phys. Rev. B 90, 020402 (2014).
Dupé, B., Bihlmayer, G., Böttcher, M., Blügel, S. & Heinze, S. Engineering skyrmions in transition-metal multilayers for spintronics. Nat. Commun. 7, 11779 (2016).
Yu, G. et al. Room-temperature creation and spin–orbit torque manipulation of skyrmions in thin films with engineered asymmetry. Nano Lett. 16, 1981–1988 (2016).
Pollard, S. D., Huang, L., Buchanan, K. S., Arena, D. A. & Zhu, Y. Direct dynamic imaging of non-adiabatic spin torque effects. Nat. Commun. 3, 1028 (2012).
Volkov, V. & Zhu, Y. Lorentz phase microscopy of magnetic materials. Ultramicroscopy 98, 271–281 (2004).
Petford-Long, A. K. & De Graef, M. in Characterization of Materials (ed. Kaufmann) 1787–1801Wiley (2002).
Henderson, R. The potential and limitations of neutrons, electrons and X-rays for atomic resolution microscopy of unstained biological molecules. Q. Rev. Biophys. 28, 171–193 (1995).
Beleggia, M., Schofield, M. A., Volkov, V. V. & Zhu, Y. On the transport of intensity technique for phase retrieval. Ultramicroscopy 102, 37–49 (2004).
McVitie, S. & Cushley, M. Quantitative Fresnel Lorentz microscopy and the transport of intensity equation. Ultramicroscopy 106, 423–431 (2006).
Shibata, K. et al. Large anisotropic deformation of skyrmions in strained crystal. Nat. Nanotechnol. 10, 589–592 (2015).
Walton, S. K., Zeissler, K., Branford, W. R. & Felton, S. MALTS: a tool to simulate Lorentz transmission electron microscopy from micromagnetic simulations. IEEE Trans. Magn. 49, 4795–4800 (2013).
Rohart, S. & Thiaville, A. Skyrmion confinement in ultrathin film nanostructures in the presence of Dzyaloshinskii–Moriya interaction. Phys. Rev. B 88, 184422 (2013).
Du, H. et al. Edge-mediated skyrmion chain and its collective dynamics in a confined geometry. Nat. Commun. 6, 8504 (2015).
Tanigaki, T. et al. Real-space observation of short-period cubic lattice of skyrmions in MnGe. Nano Lett. 15, 5438–5442 (2015).
Zhao, X. et al. Direct imaging of magnetic field-driven transitions of skyrmion cluster states in FeGe nanodisks. Proc. Natl. Acad. Sci. USA 113, 4918–4923 (2016).
Schofield, M. A., Beleggia, M., Zhu, Y. & Pozzi, G. Characterization of JEOL 2100F Lorentz-TEM for low-magnification electron holography and magnetic imaging. Ultramicroscopy 108, 625–634 (2008).
Moutafis, C., Komineas, S. & Bland, J. A. C. Dynamics and switching processes for magnetic bubbles in nanoelements. Phys. Rev. B 79, 224429 (2009).
Pollard, S., Volkov, V. & Zhu, Y. Propagation of magnetic charge monopoles and Dirac flux strings in an artificial spin-ice lattice. Phys. Rev. B 85, 180402 (R) (2012).
Chapman, J. N. The investigation of magnetic domain structures in thin foils by electron microscopy. J. Phys. D 17, 623–647 (1984).
Kohn, A., Habibi, A. & Mayo, M. Experimental evaluation of the ‘transport-of-intensity’ equation for magnetic phase reconstruction in Lorentz transmission electron microscopy. Ultramicroscopy 160, 44–56 (2016).
Ishizuka, K. & Allman, B. Phase measurement of atomic resolution image using transport of intensity equation. J. Electron Microsc. (Tokyo) 54, 191–197 (2005).
Shaw, J. M. et al. Reversal mechanisms in perpendicularly magnetized nanostructures. Phys. Rev. B 78, 024414 (2008).
Kim, S. K., Koo, Y. M., Chernov, V. A. & Padmore, H. Clear evidence for strain changes according to Co layer thickness in metastable Co/Pd(111) multilayers: an extended x-ray absorption fine structure study. Phys. Rev. B 53, 11114–11119 (1996).
Je, S.-G. et al. Asymmetric magnetic domain-wall motion by the Dzyaloshinskii–Moriya interaction. Phys. Rev. B 88, 214401 (2013).
Yang, H., Thiaville, A., Rohart, S., Fert, A. & Chshiev, M. Anatomy of Dzyaloshinskii–Moriya interaction at Co/Pt Interfaces. Phys. Rev. Lett. 115, 267210 (2015).
Di, K. et al. Direct observation of the Dzyaloshinskii–Moriya interaction in a Pt/Co/Ni film. Phys. Rev. Lett. 114, 047201 (2015).
Chen, G. et al. Tailoring the chirality of magnetic domain walls by interface engineering. Nat. Commun. 4, 2671 (2013).
Schmidt, L. et al. Symmetry breaking in spin spirals and skyrmions by in-plane and canted magnetic fields. N. J. Phys. 18, 075007 (2016).
Hiramatsu, R., Kim, K.-J., Nakatani, Y., Moriyama, T. & Ono, T. Proposal for quantifying the Dzyaloshinsky–Moriya interaction by domain walls annihilation measurement. Jpn. J. Appl. Phys. 53, 108001 (2014).
The authors would like to thank Dr Anthony Bollinger for technical assistance in magnetic field calibration of the JEOL ARM 200F, as well as Dr Lijun Wu and Dr Myung-Geun Han for useful discussions. This research was supported by the National Research Foundation (NRF), Prime Minister’s Office, Singapore, under its Competitive Research Programme (CRP award no. NRFCRP12-2013-01) and the US Department of Energy, Office of Basic Energy Sciences, Division of Materials Science and engineering, under Contract No. DE-SC0012704. Research carried out, in part, at the Center for Functional Nanomaterials, Brookhaven National Laboratory, which is supported by the US Department of Energy, Office of Basic Energy Sciences, under Contract No. DE-AC02-98CH10886. Z.W. was supported by US-DOE under Grant No. DOE DE-SC0002136. The use of Center for Functional Nanomaterials, a DOE-BES user facility, is also acknowledged.
The authors declare no competing financial interests.
Supplementary Figures, Supplementary Notes, and Supplementary References (PDF 565 kb)
Supplementary Movie 1
Movie of the reversal. The movie shows reversal of a typical sample with an out-of-plane field, until a level just before saturation. Before saturation, the field is released, and a stable, dense skyrmion state is observed. The field is continuously increased during imaging. Nominal field values are shown at select portions of the reversal. The sample is tilted at -30 degrees. (MOV 12775 kb)
Supplementary Movie 2
Tilt dependent skyrmion contrast. The movie shows the change in contrast as the tilt is changed from +30 degrees to -30 degrees, with an initialized skyrmion along the -z direction. The skyrmion structure at each tilt angle is shown in the bottom left hand corner. (MOV 4796 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Pollard, S., Garlow, J., Yu, J. et al. Observation of stable Néel skyrmions in cobalt/palladium multilayers with Lorentz transmission electron microscopy. Nat Commun 8, 14761 (2017). https://doi.org/10.1038/ncomms14761
This article is cited by
Nature Materials (2022)
Dzyaloshinskii–Moriya interaction in noncentrosymmetric superlattices
npj Computational Materials (2021)
Antiferromagnetic skyrmion crystals in the Rashba Hund’s insulator on triangular lattice
Scientific Reports (2021)
Ultrafast high-harmonic nanoscopy of magnetization dynamics
Nature Communications (2021)
Room-temperature antiskyrmions and sawtooth surface textures in a non-centrosymmetric magnet with S4 symmetry
Nature Materials (2021)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.