Hydrogen production through water splitting has been considered as a green, pure and high-efficient technique. As an important half-reaction involved, hydrogen evolution reaction is a complex electrochemical process involving liquid-solid-gas three-phase interface behaviour. Therefore, new concepts and strategies of material design are needed to smooth each pivotal step. Here we report a multiscale structural and electronic control of molybdenum disulfide foam to synergistically promote the hydrogen evolution process. The optimized three-dimensional molybdenum disulfide foam with uniform mesopores, vertically aligned two-dimensional layers and cobalt atoms doping demonstrated a high hydrogen evolution activity and stability. In addition, density functional theory calculations indicate that molybdenum disulfide with moderate cobalt doping content possesses the optimal activity. This study demonstrates the validity of multiscale control in molybdenum disulfide via overall consideration of the mass transport, and the accessibility, quantity and capability of active sites towards electrocatalytic hydrogen evolution, which may also be extended to other energy-related processes.
The properties of two-dimensional (2D) MoS2 are significantly different in comparison with its three-dimensional (3D) form. Thus, it has been considered for a number of applications, such as solar cells1,2,3, photocatalysis4,5,6, lithium ion batteries7,8,9 and electrocatalysis10,11,12,13. Owing to its natural abundance, low cost and good catalytic performance, recently MoS2 has become a representative non-precious material for electrocatalytic hydrogen evolution reaction (HER) of water splitting14,15,16,17,18,19,20,21. Such liquid-to-gas electrochemical conversion, with a complex reaction process at the interface of liquid (H+), solid (catalyst) and gas (H2), require a multiscale structural and electronic control of MoS2 to make each involved reaction step to proceed smoothly. This includes sufficient transport of reactants and products, accessibility of catalyst surface, abundant active sites and enough catalytic capability. Similar to the recent developments in the mesoporous framework of graphene22,23,24 or polymer25,26 foam, the design and preparation of a uniform mesoporous MoS2 foam could simultaneously facilitate the mass transport and accessibility of active sites. Yet, unlike the flexibility of carbon atoms skeleton in graphene and organic small molecules in polymers, MoS2 with single-crystal layer composed of three molecular layers (S–Mo–S) appears much more inflexible, which leads to such engineering still remaining a great challenge. Also, the S-edges of 2D MoS2 is usually considered as the active sites, while the in-plane structure is not active in catalysis15,27,28,29,30,31. Our recent work demonstrated that introducing different dopant atoms into the MoS2 matrix can enhance the intrinsic activity of its in-plane S atoms32. Therefore, further atomic-scale engineering via doping hetero atoms into the mesoporous MoS2 foam may achieve a multiscale modulation to synergistically boost the HER electrochemical process. However, such all-round structural and electronic control within MoS2 to enhance the HER performance has not been reported before.
Herein, we present a multiscale structural and electronic control of MoS2 foam for highly efficient HER process: (i) the macro-scale: a uniform mesoporous MoS2 foam (mPF-MoS2, average pore size ∼30 nm) facilitate the transport of H3O+ and H2, and increases the accessibility of MoS2 surface; (ii) the nano-scale: oriented vertical growth of MoS2 nanosheets around the mesopores increase the number of edges as the active sites; (iii) the atomic-scale: further chemical doping with transition metal Co atoms into the mPF-MoS2 framework enhance the intrinsic HER activity (mPF-Co-MoS2). Such mPF-Co-MoS2 electrocatalyst exhibits an excellent durability and a low overpotential of only 156 mV at the current density of 10 mA cm−2, comparable to the most active MoS2-based HER electrocatalysts in acidic medium (Supplementary Table 1). Furthermore, the density functional theory (DFT) calculations confirmed the experimental results that an appropriate Co doping content can greatly promote the HER activity of MoS2. The strategies, introduced in the present work, may open new opportunities for the rational design of MoS2 through a multiscale structural and electronic control to strengthen the electrocatalytic HER and other energy-related process, and possibly for the structural control of other 2D materials.
Synthesis of mesoporous MoS2 foam
The uniform mesoporous MoS2 foam (mPF-MoS2) was prepared with the synthetic procedure illustrated in Fig. 1. First, (NH4)6Mo7O24 molecules were homogeneously adsorbed onto the colloidal SiO2 nanospheres via a wet impregnation method. Then, the direct chemical reaction with CS2 on SiO2 surface was conducted to convert Mo precursors into small MoS2 domains. Because of the induction of the monodisperse SiO2 nanospheres template, these small domains would further self-assembly into vertically aligned MoS2 layers around the SiO2 nanospheres. Finally, the mPF-MoS2 can be obtained via etching the SiO2 template with HF solution. Note that the etching process will not influence the structure of MoS2 because the MoS2 can not be dissolved by HF solution (Supplementary Fig. 1).
Structural analysis of mesoporous MoS2 foam
The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) as well as high-angle annular dark field-scanning transmission electron microscopy (HAADF-STEM) show that the mPF-MoS2 possessed abundant spherical voids derived from the residual spaces after the removal of SiO2 nanospheres, leading to a uniform porous framework (Fig. 2a–d, Supplementary Figs 2 and 3a). Note that these uniform nanopores are interconnected throughout the entire 3D MoS2 foam at different orientations by 3D tomography (Supplementary Figs 4 and 5, Supplementary Movies 1 and 2), which facilitates the mass transport and accessibility of active sites during the catalytic process. The energy-dispersive X-ray (EDX) maps exhibits that the Mo and S elements were distributed homogeneously in the porous framework (Fig. 2e). The N2 adsorption-desorption isotherms indicate the presence of mesopores with a narrow pore size distribution at ∼24 nm (Fig. 2f).
The high resolution (HR) TEM image shows a typical interlayer distance of 0.62 nm corresponding to the (002) plane of MoS2 (Fig. 2g), and the hexagonal 2H-MoS2 crystal characteristics could also be gain from the X-ray diffraction (XRD) pattern (Fig. 2h). Remarkably, the MoS2 layers were almost vertically aligned around the mesopores with a large fraction of exposed edge sites (Fig. 2g and Supplementary Fig. 3b). Compared with random-oriented MoS2 nanosheet (rNS-MoS2) sample prepared without SiO2 template, the mPF-MoS2 showed no obvious difference in the XRD patterns (Fig. 2h), Raman spectra (Supplementary Fig. 6), X-ray photoelectron spectroscopy (XPS) (Supplementary Fig. 7) and X-ray absorption near-edge structure (XANES) spectra (inset of Fig. 2i). But according to the HRTEM images comparison (Supplementary Fig. 3), the mPF-MoS2 with vertical aligned layer and smaller lateral size possessed much more exposed edge sites. In addition, the extended X-ray absorption fine structure (EXAFS) spectra (Fig. 2i) exhibited that mPF-MoS2 had less Mo-Mo coordination than rNS-MoS2, also confirming the mPF-MoS2 possessed more edge sites. This should increase the catalytic activity of mPF-MoS2 significantly.
Electrocatalytic performance of mesoporous MoS2 foam
A typical three-electrode setup in 0.5 M H2SO4 electrolyte was adopted to conduct the electrocatalytic measurements. Bulk MoS2 shows a poor HER activity with only a minor improvement observed for rNS-MoS2 (Fig. 3a). From Fig. 3b, one could see that compared with rNS-MoS2, the required overpotential to drive a HER current density of 10, 20 and 50 mA cm−2 within mPF-MoS2 reduced 195, 219 and 262 mV, respectively. Particularly, the overpotential at a current density of 10 mA cm−2 for mPF-MoS2 is 210 mV, which is superior to the reported dense vertically aligned MoS2 film30. Furthermore, the mPF-MoS2 showed a long-term stable performance within the accelerated degradation measurements by 5,000 cyclic voltammetric (CV) sweeps (Fig. 3c), which also indicated mPF-MoS2 is a good non-precious alternative for HER electrocatalyst.
It is usually considered that only the edge sites of pure MoS2 own the HER activity, while the basal plane is catalytically inert14,15. Therefore, the mPF-MoS2, possessing rich vertical edge sites, is expected to be more catalytically active. Moreover, numerous mesopores in mPF-MoS2 facilitate the mass transport. Meanwhile, according to the contact angle measurements (Supplementary Fig. 8), the mPF-MoS2 (23°) become more hydrophilic relative to the rNS-MoS2 (32°) and bulk MoS2 (105°), leading to the more easy accessibility of reactants on active sites for the mPF-MoS2 catalyst. In addition, the massive mesopores with curved surface in MoS2 2D plane may induce the strain, which can further increase the electrocatalytic activity referring to the literatures19,33.
Chemical doping of mesoporous MoS2 foam
Doping of different transition metal atoms into the MoS2 matrix can enhance the intrinsic activity of its in-plane S atoms32. Here, we introduced Co atoms into the mPF-MoS2 framework by in situ adding Co precursors within the impregnation procedure (see the experimental section for details), yielding a Co-doped mesoporous MoS2 foam (mPF-Co-MoS2). As shown in the SEM (Supplementary Fig. 9), TEM (Supplementary Fig. 10a) and HAADF-STEM (Fig. 4a) images, the mesoporous MoS2 foam has been well retained after Co doping, with MoS2 flakes still assembling as vertically aligned layers around the mesopores (Supplementary Fig. 10b). The Co dopants bring indiscernible chemical state variation of the MoS2 framework according to the XPS spectra (Supplementary Fig. 11) and Mo K-edge XANES spectra (Supplementary Fig. 12). No Co-containing nanoparticles were observed from TEM images, consistent with the EDX maps showing the homogeneous distribution of Co, Mo and S elements over the entire mesoporous framework (Fig. 4a).
Co doping contents within the mesoporous MoS2 foam can be easily modulated by varying the amount of Co precursors, resulting in a series of mPF-Co-MoS2-x samples (x represents the Co doping contents in wt.%). As shown in the Co K-edge XANES spectra (Fig. 4b) and EXAFS spectra (Fig. 4c), all Co atoms in different mesoporous MoS2 foam possess the valence and the Co–S bonds are distinguished from those in commercial CoS crystal. This indicates that Co atoms are covalently doped into the MoS2 2D plane rather than being adsorbed on the surface. This finding is also confirmed by the Mo K-edge EXAFS spectra (Fig. 4d) showing a decrease of Mo-Mo coordination caused by the substituted-doping of Co atoms within the MoS2 2D plane. In addition, the decrease of Mo-Mo coordination accompanied with the increase of Co doping contents (Fig. 4d) was also consistent with the stepwise red shift of E12g and A1g modes in Raman spectra (Fig. 4e) resulted from the progressively increased Co dopants in MoS2 2D plane to soften the Mo-S related modes and decrease their vibration frequency34. Nevertheless, the E12g and A1g modes of MoS2 will change significantly when the Co doping contents exceeded 16.7% (Fig. 4e), suggesting a structural variation in the mesoporous MoS2 foam. This correlates with the XRD patterns showing that the crystal structure of MoS2 was well maintained with no other phases appearing after Co doping, until the Co doping contents were 21.1% or more (Fig. 4f). Meanwhile, distinct change in pore structure of mPF-Co-MoS2 samples appeared when the Co doping contents exceeds 16.7% (Supplementary Fig. 13). Note that mesoporous MoS2 foam with different Co doping contents showed no obvious difference in the contact angle measurements (Supplementary Fig. 14). The above analyses indicated that there is an optimum doping content (16.7% from our experience) which will provide significant Co contents but still preserving the mPF-Co-MoS2 integrated mesoporous vertically aligned framework.
Effect of Co dopant on electrocatalytic performance
In view of the additional atomic-scale modulation in mesoporous MoS2 foam, a further enhanced HER process was expected. Thus, mPF-Co-MoS2-3.4 exhibited a distinctly enhanced activity, reducing the overpotential of 26 and 53 mV at the current density of 10 and 50 mA cm−2 relative to mPF-MoS2 (Fig. 5a). The sample with Co doping content of 16.7% demonstrates the optimum activity (Fig. 5b). The volcano-shaped relationship between HER activity and Co doping contents confirmed our finding that there is an optimum Co doping level which, from one hand enhances the intrinsic catalytic activity of mPF-MoS2 and at the same time maintains the inherent framework within mesoporous MoS2 foam. Remarkably, the mPF-Co-MoS2-16.7 showed a high HER activity with the overpotential at a current density of 10 mA cm−2 of only 156 mV (Fig. 5a), comparable to the most active MoS2-based non-precious HER electrocatalysts in acidic medium (Supplementary Table 1). Moreover, mPF-Co-MoS2-16.7 also showed a long-term stable performance even after 5,000 CV sweeps within the accelerated degradation measurements (Fig. 5c). Tafel plots showed that mPF-Co-MoS2-16.7 with a Tafel slope value of 74 mV dec−1 and mPF-MoS2 (90 mV dec−1) followed a similar reaction process via the Volmer–Heyrovsky mechanism35,36,37, deviating from the Pt/C electrocatalyst (30 mV dec−1) via the Volmer-Tafel mechanism (Fig. 5d). These results demonstrated that the Co doping content will significantly affect the activity modulation of MoS2, and a moderate value can maximally promote the multiscale structural and electronic control in mesoporous MoS2 foam for the HER activity optimization.
Theoretical studies of Co doping effect
DFT calculations were carried out to gain further insights into the influence of different Co doping contents within the basal plane of MoS2 on the HER activity. The hydrogen adsorption free energy (ΔGH) is a widely accepted descriptor of HER activity for various catalytic materials, where the optimal value of ΔGH is around zero (∼0) eV to compromise the reaction barriers and achieve the best HER activity38,39. For the basal plane of pristine MoS2, the ΔGH is ∼2 eV, far away from the optimal value. With Co atoms introduced into the MoS2 in-plane, taking the coverage (θH) of 1/4 monolayer (ML) as an example, the ΔGH decreased continuously and reached ∼0 eV at the Co doping content of 13.3 wt.% (atomic ratio of Co:Mo is 1:2), beyond which the ΔGH will depart away from the optimal values again (Fig. 6a). These simulations indicate that there indeed exists a moderate Co doping content to promote MoS2 to gain the optimal HER activity, confirming the experimental results.
To understand the origin of the increased HER activity with increased Co doping content, an analysis of the electronic properties has been made. First, the projected density of state of S atoms show a significant increase in the electronic states of in-plane S sites around Fermi level after Co atoms doping (Supplementary Fig. 16), resulting in the enhanced catalytic activity, in accordance with our previous study32. Furthermore, according to the molecular orbital theory, when H atom is absorbed on surface S atom, the combination of H 1s orbital and S 3p orbital will form a bonding orbital (σ) and anti-bonding orbital (σ*), where the degree of energy level matching between H atom and S atom determines the H–S bonding strength (Fig. 6b). Because of the very high energy level of S 3p orbital relative to H 1s orbital, the H adsorption on basal plane of pristine MoS2 is too weak (ΔGH=∼2 eV), leading to a poor HER performance of MoS2 for HER. When doping another metal atom such as Co into the MoS2 in-plane, the electron number on S atom will decrease (Fig. 6c) to offset the energy level mismatching for enhancing the H adsorption and HER activity. Different metal atoms own the different capability to modify the electron density on S atoms (see Fig. 6d and Supplementary Table 2 for detailed data), and the metal dopants that tune the Bader charge of S atoms into the range of ∼6.73 to ∼6.78 will lead to a moderate ΔGH (Fig. 6d) and high HER activity (Supplementary Fig. 17). Among them, the Co atom is indeed a good regulator to bring the ΔGH get ∼0 eV. Nevertheless, further increasing Co doping contents will cause the excessive decrease of electron on S atoms to make the interaction between H atoms and S atoms too strong (Fig. 6d). In addition, high Co doping contents can also lead to less stable of MoS2 surface according to the surface energy (γ) calculations (Supplementary Fig. 18), which is also harmful to the HER activity.
In summary, we introduce a multiscale structural and electronic control of MoS2 strategy to achieve the high-efficient HER electrocatalysis. First, a uniform mesoporous MoS2 foam (mPF-MoS2) was fabricated with a significantly enhanced HER performance compared with that of random-oriented MoS2 nanosheet (rNS-MoS2). It originates from the macro-scale modulation fabricating massive mesopores to gain the sufficient transport of H3O+ and H2, the favourable accessibility of MoS2 surface and the strain-induced promotion, as well as the nano-scale modulation with vertically aligned layers to provide abundant active edge sites. Second, chemical doping was introduced to add further atomic-scale engineering in the mesoporous MoS2 foam for the intrinsic activity increase. The optimum Co-doped mesoporous MoS2 foam (mPF-Co-MoS2) with a Co content of 16.7% showed a further distinct enhancement of HER activity, which possessed a long-term durability with more than 5,000 recycles and an overpotential of only 156 mV at the current density of 10 mA cm−2, comparable to the most active MoS2-based electrocatalysts in acidic medium. DFT calculations confirmed the experimental results that a moderate Co doping content can modulate the H adsorption on MoS2 to a suitable degree and simultaneously maintain the structure stability to promote the HER activity reach optimum value. The findings in the present work pave a rational pathway to strengthen the electrocatalytic HER performance of MoS2 via the multiscale structural and electronic control, and the involved concept and strategy can be extended to other energy-related process or other 2D materials.
The mPF-MoS2 was synthesized through a direct chemical synthesis method. First, 400 mg (NH4)6Mo7O24·4H2O and 5,333.4 mg SiO2 colloidal disperse (30 wt.% SiO2 in ethylene glycol, Alfa Aesar) were dispersed in 20 ml deionized water, followed by stirring under room temperature to remove the solvent and drying under 80 °C. Then, the gained solid and 10 ml CS2 were transferred into a 40 ml stainless steel autoclave under Ar and maintained at 400 °C for 4 h. The final product was treated with HF (aq.) under room temperature for 5 h, followed by washing with water and absolute ethanol for several times and drying at 80 °C. For comparison, the rNS-MoS2 was synthesized by using 900 mg (NH4)6Mo7O24·4H2O dissolved in 20 ml deionized water and 10 ml CS2 conducted within the same chemical reaction as the mPF-MoS2 without using SiO2 template. The series of mPF-Co-MoS2 samples were synthesized by using 400 mg (NH4)6Mo7O24·4H2O, specified amount of Co(NO3)2·6H2O and 5,333.4 mg SiO2 colloidal dispers to gain the impregnated solid, and then with 10 ml CS2 to proceed within the same process as the mPF-MoS2. The Co doping contents in final mPF-Co-MoS2 samples were measured by inductively coupled plasma atomic emission spectroscopy.
SEM was conducted on Hitachi S4800 operated at 20 kV. TEM, HAADF-STEM and EDX mapping were carried out on a FEI Tecnai 30 microscope and a 20 microscope operated at an accelerating voltage of 300 and 200 kV, respectively. The 3D tomography in the STEM mode was carried out on the FEI Talos F200 × microscope operated at 200 kV. N2 adsorption–desorption was measured with a Micromeritics Tristar 3020 Surface Area and Porosimetry analyzer. XRD measurements were conducted on a Rigaku Ultima IV diffractometer with Cu Kα radiation at 35 kV and 15 mA. XANES and EXAFS were measured at the BL14W1 beamline of the Shanghai Synchrotron Radiation Facility (SSRF). Raman spectroscopy was performed on a Renishaw inVia Raman microscope with a 532 nm excitation laser at a power of 0.29 mW. XPS measurements were carried out on an Omicron XPS System used Al Kα X-rays as the excitation source with a voltage of 15 kV and power of 300 W. Contact angle of water solution droplet on the surface of catalyst layer were conducted on SDC-100 contact angle measurement instrument (Shengding Precision Instrument Co., Ltd., China) at room temperature. Inductively coupled plasma atomic emission spectroscopy was carried out in Varian AA240z graphite furnace atomic absorption spectrometer.
HER polarization curve tests were conducted on a Princeton Parstat MC potentiostat/galvanostat with a three-electrode electrochemical cell equipped with a gas flow controlling system. Graphite rod was used as the counter electrode and Ag/AgCl (saturated KCl-filled) as the reference electrode. A glassy carbon rotating disk electrode with a diameter of 5 mm covered by a thin catalyst film was used as the working electrode. Typically, 4 mg catalyst was suspended in 1 ml ethanol with 20 μl Nafion solution (5 wt.%, Du Pont) to form a homogeneous ink assisted by ultrasound. Then 25 μl of the ink was spread onto the surface of glassy carbon by a micropipette and dried under room temperature. The final loading for the catalysts and 40% Pt/C electrocatalysts on work electrode is 0.5 mg cm−2. HER tests were conducted in an Ar-saturated 0.5 M H2SO4 electrolyte at 25 °C. The potential range was from 0 to −1.0 V (versus Ag/AgCl) and the scan rate was 2 mV s−1. Before measurements, the samples were repeatedly swept from −0.4 to 0.3 V (versus Ag/AgCl) in the electrolyte until a steady voltammogram curve was obtained. All the final potentials have been calibrated with respect to a reversible hydrogen electrode (RHE).
All theoretical calculations were performed using Vienna ab initio simulation packages (VASP)40 with projector-augmented wave scheme41. The generalized gradient approximation with the Perdew–Burke–Ernzerhof (PBE)42 functional was used for the exchange–correlation interaction. The plane wave cutoff was set to 400 eV. The convergence of total energy and forces were set to 1 × 10−5 eV and 0.05 eV Å−1, respectively. A periodically repeated single-layer MoS2 (a trilayer unit of S-Mo-S as a single layer43) crystal model with a 20 Å vacuum space has been built for DFT calculations. The Brillouin zone was sampled by a 3 × 3 × 1 k-point grid with the Monkhorst–Pack scheme44 for structural optimization and a 6 × 6 × 1 k-point grid for electronic structure calculations. More details see the Supplementary Methods.
The data that support the findings of this study are available from the corresponding authors on request.
How to cite this article: Deng, J. et al. Multiscale structural and electronic control of molybdenum disulfide foam for highly efficient hydrogen production. Nat. Commun. 8, 14430 doi: 10.1038/ncomms14430 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Liu, Z. K., Lau, S. P. & Yan, F. Functionalized graphene and other two-dimensional materials for photovoltaic devices: device design and processing. Chem. Soc. Rev. 44, 5638–5679 (2015).
Wang, Q. H., Kalantar-Zadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 7, 699–712 (2012).
Gu, X. et al. A solution-processed hole extraction layer made from ultrathin MoS2 nanosheets for efficient organic solar cells. Adv. Energy Mater. 3, 1262–1268 (2013).
Xiang, Q. J., Yu, J. G. & Jaroniec, M. Synergetic effect of MoS2 and graphene as cocatalysts for enhanced photocatalytic H2 production activity of TiO2 nanoparticles. J. Am. Chem. Soc. 134, 6575–6578 (2012).
Ding, Q. et al. Efficient photoelectrochemical hydrogen generation using heterostructures of Si and chemically exfoliated metallic MoS2 . J. Am. Chem. Soc. 136, 8504–8507 (2014).
Chang, K. et al. MoS2/graphene cocatalyst for efficient photocatalytic H2 evolution under visible light irradiation. ACS Nano 8, 7078–7087 (2014).
Stephenson, T., Li, Z., Olsen, B. & Mitlin, D. Lithium ion battery applications of molybdenum disulfide (MoS2) nanocomposites. Energy Environ. Sci. 7, 209–231 (2014).
Chhowalla, M. et al. The chemistry of two-dimensional layered transition metal dichalcogenide nanosheets. Nat. Chem. 5, 263–275 (2013).
Zhu, C. B., Mu, X. K., van Aken, P. A., Yu, Y. & Maier, J. Single-layered ultrasmall nanoplates of MoS2 embedded in carbon nanofibers with excellent electrochemical performance for lithium and sodium storage. Angew. Chem. Int. Ed. 53, 2152–2156 (2014).
Deng, D. H. et al. Catalysis with two-dimensional materials and their heterostructures. Nat. Nanotechnol. 11, 218–230 (2016).
Asadi, M. et al. Cathode based on molybdenum disulfide nanoflakes for lithium-oxygen batteries. ACS Nano 10, 2167–2175 (2016).
Yuwen, L. H. et al. General synthesis of noble metal (Au, Ag, Pd, Pt) nanocrystal modified MoS2 nanosheets and the enhanced catalytic activity of Pd-MoS2 for methanol oxidation. Nanoscale 6, 5762–5769 (2014).
Huang, H., Feng, X., Du, C. C., Wu, S. Y. & Song, W. B. Incorporated oxygen in MoS2 ultrathin nanosheets for efficient ORR catalysis. J. Mater. Chem. A 3, 16050–16056 (2015).
Hinnemann, B. et al. Biornimetic hydrogen evolution: MoS2 nanoparticles as catalyst for hydrogen evolution. J. Am. Chem. Soc. 127, 5308–5309 (2005).
Jaramillo, T. F. et al. Identification of active edge sites for electrochemical H2 evolution from MoS2 nanocatalysts. Science 317, 100–102 (2007).
Li, Y. G. et al. MoS2 nanoparticles grown on graphene: an advanced catalyst for the hydrogen evolution reaction. J. Am. Chem. Soc. 133, 7296–7299 (2011).
Huang, X. et al. Solution-phase epitaxial growth of noble metal nanostructures on dispersible single-layer molybdenum disulfide nanosheets. Nat. Commun. 4, 1444 (2013).
Deng, J. et al. High-performance hydrogen evolution electrocatalysis by layer-controlled MoS2 nanosheets. RSC Adv. 4, 34733–34738 (2014).
Li, H. et al. Activating and optimizing MoS2 basal planes for hydrogen evolution through the formation of strained sulphur vacancies. Nat. Mater. 15, 48–53 (2016).
Lukowski, M. A. et al. Enhanced hydrogen evolution catalysis from chemically exfoliated metallic MoS2 nanosheets. J. Am. Chem. Soc. 135, 10274–10277 (2013).
Liao, L. et al. MoS2 formed on mesoporous graphene as a highly active catalyst for hydrogen evolution. Adv. Funct. Mater. 23, 5326–5333 (2013).
Lin, T. Q. et al. Nitrogen-doped mesoporous carbon of extraordinary capacitance for electrochemical energy storage. Science 350, 1508–1513 (2015).
Jiao, Y. C. et al. Highly ordered mesoporous few-layer graphene frameworks enabled by Fe3O4 nanocrystal superlattices. Angew. Chem. Int. Ed. 54, 5727–5731 (2015).
Wang, G. et al. Controlled synthesis of N-doped carbon nanospheres with tailored mesopores through self-assembly of colloidal silica. Angew. Chem. Int. Ed. 54, 15191–15196 (2015).
Liu, S. H. et al. Patterning two-dimensional free-standing surfaces with mesoporous conducting polymers. Nat. Commun. 6, 8817 (2015).
Fang, Y. et al. Growth of single-layered two-dimensional mesoporous polymer/carbon films by self-assembly of monomicelles at the interfaces of various substrates. Angew. Chem. Int. Ed. 54, 8425–8429 (2015).
Kibsgaard, J., Chen, Z. B., Reinecke, B. N. & Jaramillo, T. F. Engineering the surface structure of MoS2 to preferentially expose active edge sites for electrocatalysis. Nat. Mater. 11, 963–969 (2012).
Gao, M. R., Chan, M. K. Y. & Sun, Y. G. Edge-terminated molybdenum disulfide with a 9.4-angstrom interlayer spacing for electrochemical hydrogen production. Nat. Commun. 6, 7493 (2015).
Xie, J. F. et al. Defect-rich MoS2 ultrathin nanosheets with additional active edge sites for enhanced electrocatalytic hydrogen evolution. Adv. Mater. 25, 5807–5813 (2013).
Kong, D. S. et al. Synthesis of MoS2 and MoSe2 films with vertically aligned layers. Nano Lett. 13, 1341–1347 (2013).
Ye, G. L. et al. Defects engineered monolayer MoS2 for improved hydrogen evolution reaction. Nano Lett. 16, 1097–1103 (2016).
Deng, J. et al. Triggering the electrocatalytic hydrogen evolution activity of the inert two-dimensional MoS2 surface via single-atom metal doping. Energy Environ. Sci. 8, 1594–1601 (2015).
Lee, J. H., Jang, W. S., Han, S. W. & Baik, H. K. Efficient hydrogen evolution by mechanically strained MoS2 nanosheets. Langmuir. 30, 9866–9873 (2014).
Li, H. L. et al. Growth of alloy MoS2xSe2(1−x) nanosheets with fully tunable chemical compositions and optical properties. J. Am. Chem. Soc. 136, 3756–3759 (2014).
Conway, B. E. & Tilak, B. V. Interfacial processes involving electrocatalytic evolution and oxidation of H2, and the role of chemisorbed H. Electrochim. Acta 47, 3571–3594 (2002).
Merki, D., Vrubel, H., Rovelli, L., Fierro, S. & Hu, X. L. Fe, Co, and Ni ions promote the catalytic activity of amorphous molybdenum sulfide films for hydrogen evolution. Chem. Sci. 3, 2515–2525 (2012).
Bockris, J. O. M. & Potter, E. C. The mechanism of the cathodic hydrogen evolution reaction. J. Electrochem. Soc. 99, 169–186 (1952).
Norskov, J. K. et al. Trends in the exchange current for hydrogen evolution. J. Electrochem. Soc. 152, J23–J26 (2005).
Greeley, J., Jaramillo, T. F., Bonde, J., Chorkendorff, I. B. & Norskov, J. K. Computational high-throughput screening of electrocatalytic materials for hydrogen evolution. Nat. Mater. 5, 909–913 (2006).
Kresse, G. & Furthmuller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Blochl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Tsai, C., Abild-Pedersen, F. & Norskov, J. K. Tuning the MoS2 edge-site activity for hydrogen evolution via support interactions. Nano Lett. 14, 1381–1387 (2014).
Monkhorst, H. J. & Pack, J. D. Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).
We gratefully acknowledge the financial support from the Ministry of Science and Technology of China (No. 2016YFA0204100 and 2016YFA0200200), the National Natural Science Foundation of China (No. 21573220 and 21621063), the Key Research Program of Frontier Sciences of the Chinese Academy of Sciences (No. QYZDB-SSW-JSC020), the strategic Priority Research Program of the Chinese Academy of Sciences (No. XDA09030100). We thank staff at the BL14W1 beamline of the Shanghai Synchrotron Radiation Facilities (SSRF) for assistance with the EXAFS and XANES measurements. We also acknowledge the computational resources from National Supercomputing Center in Shenzhen.
The authors declare no competing financial interests.
Supplementary Figures, Supplementary Tables and Supplementary Methods (PDF 18319 kb)
Reconstructed structure of mPF-MoS2 by rotating 360° around the sample tilting axis from the 3D STEM tomography. The pore structure can be clearly seen through the movie. (AVI 1641 kb)
Reconstructed structure of mPF-MoS2 by the 3D STEM tomography, showing the cross-section images at different depth of the sample. The distribution and size of the pore in the mesoporous MoS2 foam can be clearly seen through the movie. (MOV 1791 kb)
About this article
Cite this article
Deng, J., Li, H., Wang, S. et al. Multiscale structural and electronic control of molybdenum disulfide foam for highly efficient hydrogen production. Nat Commun 8, 14430 (2017). https://doi.org/10.1038/ncomms14430
Rational strain engineering of single-atom ruthenium on nanoporous MoS2 for highly efficient hydrogen evolution
Nature Communications (2021)
Nature Reviews Materials (2021)
Theoretical Chemistry Accounts (2021)
Palladium phosphide nanoparticles embedded in 3D N, P co-doped carbon film for high-efficiency oxygen reduction
Journal of Materials Science (2021)
Enhanced performance of in-plane transition metal dichalcogenides monolayers by configuring local atomic structures
Nature Communications (2020)