Abstract
To minimize the lattice thermal conductivity in thermoelectrics, strategies typically focus on the scattering of lowfrequency phonons by interfaces and highfrequency phonons by point defects. In addition, scattering of midfrequency phonons by dense dislocations, localized at the grain boundaries, has been shown to reduce the lattice thermal conductivity and improve the thermoelectric performance. Here we propose a vacancy engineering strategy to create dense dislocations in the grains. In Pb_{1−x}Sb_{2x/3}Se solid solutions, cation vacancies are intentionally introduced, where after thermal annealing the vacancies can annihilate through a number of mechanisms creating the desired dislocations homogeneously distributed within the grains. This leads to a lattice thermal conductivity as low as 0.4 Wm^{−1} K^{−1} and a high thermoelectric figure of merit, which can be explained by a dislocation scattering model. The vacancy engineering strategy used here should be equally applicable for solid solution thermoelectrics and provides a strategy for improving zT.
Introduction
Thermoelectric materials attract increasing interest, driven by the worldwide demand for clean energy^{1}. Based on either the Seebeck or Peltier effects, thermoelectrics can be used for power generation or for refrigeration, respectively. Thermoelectrics use the charge carriers inside a material as a working medium, therefore enabling a vibrationfree and emissionfree solution to the direct conversion between heat and electricity. The biggest challenge is to enhance the conversion efficiency, which is mostly limited by the materials’ dimensionless figure of merit, zT=S^{2}T/ρ(κ_{E}+κ_{L}), where S is the Seebeck coefficient, ρ is the electric resistivity, κ_{E} and κ_{L} are the electronic and the lattice contribution to the thermal conductivity, and T is the absolute temperature.
Owing to the strong coupling between S, ρ and κ_{E}, two straightforward strategies for improving zT are to increase the electrical performance via the power factor S^{2}/ρ and to reduce the independent material property, lattice thermal conductivity κ_{L}. The former strategy has been recently demonstrated by the band engineering concept^{2,3,4,5,6,7,8,9,10} and the later one can be accomplished by a few approaches that include nanostructuring^{11,12,13,14}, alloying^{15,16} and lattice anharmonicity^{17,18}.
Among all the demonstrated approaches for achieving a low lattice thermal conductivity mentioned above, the essential commonality is the strengthened phonon scattering, but in different ways. Specifically, nanostructuring increases boundary scattering and alloying introduces point defect scattering, whereas anharmonic lattice vibrations lead to a strong inherent phonon–phonon scattering. These different scattering mechanisms collectively contribute to shorten the overall relaxation time (τ_{tot}) of phonons, each with a characteristic frequency (ω) dependence, leading to a low lattice thermal conductivity. More quantitatively, boundary scattering by nanostructures leads to a relaxation time, τ_{B}∝ω^{0}, which enables effective scattering of lowfrequency phonons; point defect scattering in alloys results in a relaxation time, τ_{PD}∝ω^{−4}, effectively scattering the highfrequency phonons, and the inherent phonon–phonon scattering by anharmonic lattice vibrations has respectively a relaxation time, τ_{U,N}∝ω^{−2}, for Umklapp (τ_{U}) and normal (τ_{N}) processes, which enables effective scattering on phonons with all frequencies.
Although it is rarely focused on, dislocation scattering is another process that can be effective at reducing lattice thermal conductivity in thermoelectrics^{19,20}. The frequency dependence of phonon scattering on dislocation strian fields (τ_{DS}∝ω^{−1}) and dislocation cores (τ_{DC}∝ω^{−3}) makes this mechanism particularly effective at scattering midrange frequency phonons, phonons missed by the previously discussed scattering mechanisms^{21,22}. Even with scattering by grain boundary dislocations, which are known to have much shorter range strain fields than lattice dislocations^{23}, a large κ_{L} reduction has been recently observed experimentally^{20}. Therefore, it is believed that phonon scattering by dislocations, whether in the grain boundary structure or in the lattice, is an effective approach for advancing thermoelectrics.
Dislocations are generally undesired in semiconductors and ceramics^{24,25} when the thermal conductivity is not a major functionality, due to their detrimental effects on the mechanical properties, carrier mobility and optical properties^{26,27,28}. To achieve an effective κ_{L} reduction by dislocations in thermoelectric semiconductors, a simple estimation shows that the density of uniformly distributed dislocations within the grains (N_{D}) needs to be approaching 10^{12} cm^{−2} or higher^{29}, being at least two orders of magnitude higher than that can be normally obtained in semiconductors^{30}. The most straightforward way to introduce dislocations into a material is through plastic deformation. However, most thermoelectrics do not readily plastically deform and dislocations must be introduced by other means.
In thermoelectrics, dislocations have been introduced through the precipitation of secondary phases where misfit dislocations mediate the lattice mismatch at coherent phase boundaries^{16}. A large density of grain boundary dislocations has also been achieved by liquidphase compaction (N_{D}=2 × 10^{11} cm^{−2})^{20}. Another method for introducing a large density of dislocations is through the introduction of a large concentration of vacancies^{31}. On thermal annealing these vacancies will diffuse forming vacancy clusters of lower energy, these vacancy clusters then collapse into closed loops of edge dislocations. This mechanism was initially observed in metals^{32} and has since been observed in ionic crystals^{33}. In addition, vacancies in a material facilitate dislocation climb and at vacancy concentrations far from equilibrium the resulting dislocation motion can increase the dislocation content (that is, the activation of Bardeen–Herring sources)^{34,35}.
Frank^{34} highlights a situation where the concentration of point defects is far from equilibrium, which is common in semiconducting materials^{31}. When annealed, the resulting dislocation motion via climb will result in an increase in dislocation content^{34}. Although these mechanisms are well understood for ionic crystals where vacancies are produced through Frenkel defects or Schottky pairs, they are likely to be more complicated in systems where vacancies are introduced via charge compensation doping and one vacancytype dominates. These mechanisms lead to a strategy for obtaining uniformly distributed dense dislocations through vacancy engineering in thermoelectric materials.
Compared with the solvent compound, when a solute of a smaller cationtoanion ratio is dissolved forming a solid solution, either vacancies at the cation site or interstitial anions would be expected. Anion interstitials generally have a much larger defect formation energy than that of a cation site vacancy, because typically the anion radius is larger than that of the cation. This leads to the preferred formation of cation vacancies. Thus, the formation of dislocations would be expected due to the collapse of cation vacancy clusters. It is expected that the density of the dislocations can be easily controlled by tuning the composition of the solid solution.
This work focuses on the thermoelectric properties of PbSeSb_{2}Se_{3} solid solutions (Pb_{1−x}Sb_{2x/3}Se) to demonstrate this strategy. To maintain a chargebalanced, undoped semiconductor within the solid solution, with rock salt structure, it is believed that for three Pb sites replaced by two Sb atoms and a third site becomes vacant. The resulting cation vacancies lead to a high density of uniformly distributed dislocations (Fig. 1a,b). These dislocations provide a strong scattering of phonons in the midrange of frequencies (τ_{DC}∝ω^{−3}, τ_{DS}∝ω^{−1}). This is in addition to the point defect scattering (τ_{PD}∝ω^{−4}) from the Sb/Pb substitution for highfrequency phonons and strong inherent phonon–phonon scattering (τ_{U,N}∝ω^{−2}) for phonons at all frequencies. This full frequency spectrum scattering of phonons, with an emphasis on the midfrequency phonons, leads to the low value lattice thermal conductivity (κ_{L}), compared with intrinsic PbSe^{36}, approaching the amorphous limit estimated by assuming a phonon mean free path of minimal distance^{37} in a broad temperature range (Fig. 1c). Most importantly, the ultralow lattice thermal conductivity of ∼0.4 Wm^{−1} K^{−1} leads to higher zT than previously reported in PbSe (Fig. 1d). This vacancy engineering strategy for dislocation scattering to reduce the lattice thermal conductivity should be widely applicable in thermoelectric solid solutions.
Results
Microstructure and formation mechanisms of dislocations
The powder Xray diffraction (XRD) indicates all the materials obtained here crystalize in NaCl structure with high phase purity (Supplementary Fig. 1a). The formation of Pb_{1−x}Sb_{2x/3}Se solid solution in this work can be evident from the linear decrease in lattice parameter with increasing x (Supplementary Fig. 1b), which agrees well with the Vegard’s law. Neither precipitates nor nanometrescale grains are observed according to our XRD analyses and transmission electron microscope (TEM) observations.
As the cationtoanion ratio in Sb_{2}Se_{3} is 1/3 smaller than that in PbSe, formation of a rocksalt structured Pb_{1−x}Sb_{2x/3}Se solid solution would lead to x/3 negatively charged vacancies at the Pb site per formula unit rather than interstitial Se. Pb deficiency can be observed in the energy dispersive Xray spectroscopy analysis. These Pb vacancies can increase the dislocation content through a number of mechanisms that have been observed in ionic crystals^{33,23,38,39}. One possibility is the activation of Bardeen–Herring sources (the climb analogue to the Frank–Read source) where vacancy diffusion facilitates dislocation climb^{34}. These sources act as dislocation multiplication sites and are diffusionlimited processes. In addition, dislocations in ionic crystals can have an electrostatic charge^{23,38}. These charged regions interact with the negatively charged Pb vacancies retarding the motion of the dislocations via glide stopping their annihilation with each other or at a surface.
The samples in this study were annealed at 1,023 K for 2 days, giving the system sufficient thermal energy to activate the above mentioned, diffusionlimited dislocation nucleation and multiplication processes. These dislocations can subsequently climb, glide and tangle into the complex dislocation network seen in Fig. 1a,b. Although these mechanisms are well understood for ionic crystals where vacancies are produced through Frenkel defects or Schottky pairs, they are likely to be more complicated in systems where vacancies are introduced via charge compensation doping and one vacancy type dominates. Different thermal histories, composition and synthesis methods may explain why other Pb_{1−x}Sb_{x}Se studies show the formation of Sbrich impurity phases but not dislocations^{40}.
According to the theory of impurity diffusion, in particular in cubic crystals with vacancies^{41,42,43}, the existence of vacancies will significantly retard the diffusion of the substitutional impurities because of the coulombic interaction between them^{34,36,44,45}, whereas the diffusion of vacancies themselves can be largely accelerated when they are bound with dislocations^{46}. Therefore, the substitutional Sb impurity on the Pb sites do not diffuse fast enough to form an aggregation of Sbrich phases as confirmed by the TEM observations for Pb_{1−x}Sb_{2x/3}Se. This mechanism may further explain the formation of Sbrich impurity phases but not dislocations in Pb_{1−x}Sb_{x}Se, which may have fewer cation vacancies^{40}.
Density of dislocation
An example of a typical dislocation in the highresolution annular bright field scanninge TEM (STEM) image in Fig. 2a. Starting from the core (centre of the image) of the dislocation, one (001) and two (111) extra half planes of atoms are observed and marked by yellow arrows. The Burgers vectors of the dislocation is determined to be B_{D}=1/2[01], which is generally observed in NaCl structures^{47}. Based on a few low magnification STEM images, the average areal dislocation density (N_{D}) is estimated to be ∼4 × 10^{12} cm^{−2}; this is an extremely high value compared with that typically reported in semiconductors^{30}.
To estimate the density of dislocations more macroscopically and to compare with that determined by the local TEM observations, synchrotron XRD (Fig. 2b) was carried out and the modified Williamson–Hall model^{48,49} was employed for the high zT sample Pb_{0.95}Sb_{0.033}Se. According to this method, the broadening of the diffraction peaks strongly relate to the dislocation density and the crystallite size via: ΔK=0.9/d+(πA^{2}B_{D}^{2}/2)N_{D}^{1/2}K^{2}C±O(K^{4}C^{2}) with details shown in Supplementary Table 3. With the experimentally measured K and ΔK, the dislocation density can be determined via the slope of the modified Williamson–Hall plot as shown in Fig. 2c. The estimated dislocation density is ∼5 × 10^{12} m^{−2} for Pb_{0.95}Sb_{0.033}Se, which agrees well with the result determined by the TEM observations. Similarly, the modified Williamson–Hall plots, according to our normal XRD results, qualitatively show that the density of dislocations for Pb_{1−x}Sb_{2x/3}Se (x=0∼0.07) solid solutions increase with increasing Sb concentration (Supplementary Fig. 2).
Lattice thermal conductivity and modelling
The lattice thermal conductivity (Fig. 1c), determined by subtracting the electronic contribution via the Wiedemann–Franz law from the measured thermal conductivity, decreases with increasing Sb_{2}Se_{3} content, meaning a strengthened phonon scattering with increasing x. To ensure that the uniformly distributed dense dislocations are indeed responsible for the observed ultralow lattice thermal conductivity, modelling is carried out based on the Debye approximation with different scattering sources for phonons.
First, the literature values of κ_{L}, which are an average on a few degenerately doped polycrystalline PbSe samples, is used to estimate the ratio (=4) of N to Uprocesses for the phonon–phonon scattering^{36}. Second, the point defect scattering parameters including both mass and strain contributions are determined according to the literature^{50,51,52}. Third, the scattering by dislocations can be calculated^{21} with the experimental Burger vector and the dislocation density. Klemens’ expression for edge dislocation scattering was used. Besides our measured transverse and longitudinal sound velocities of υ_{L}=3,150 ms^{−1} and υ_{T}=1,600 ms^{−1}, respectively, other parameters including Gruneisen parameter of 1.7 (ref. 53) and Poisson ratio of 0.243(ref. 54) are taken from the literature. More details for the modelling can be found in the Supplementary Tables 1 and 2.
Next, one can calculate the temperaturedependent lattice thermal conductivity using the following equation^{55}:
where k_{B} is the Boltzmann constant, υ is average sound speed, ℏ is the reduced Plank constant, θ_{D} is Debye temperature, τ_{tot} is the total relaxation time and x=ℏω/k_{B}T. The total relaxation time includes the contributions from phonon–phonon, point defect and dislocation scattering by:
As shown in Fig. 3a, the model prediction agrees well with the measurements for the high thermoelectric figure of merit sample (x=0.05). It is then clear that the lattice thermal conductivity (κ_{L}) additionally decreases by at least 30% in the entire temperature range due to dislocation scattering. Assuming all the initially produced vacancies remains in the solid solution as random point defects, the lattice thermal conductivity is predicted to be as the blue dashed line (Fig. 3a), which is well above the model prediction including the contribution from dislocation scattering (green solid line). Therefore, dislocation scattering is believed to be the main reason for the observed κ_{L} reduction. Importantly, the nearly full phonon frequency spectrum scattering leads to a comparable κ_{L} with the theoretical minimum (κ_{L}^{min}=0.37 Wm^{−1} K^{−1}) obtained by the Cahill’s model^{37}. Comparing the dislocations in samples with x=0.03 (Fig. 1b), x=0.04 (Supplementary Fig. 3a,b), x=0.05 (Fig. 1a) and x=0.07 (Supplementary Fig. 3c,d), a roughly linear increase in the density of the dislocations (N_{D}) with increasing x is observed. Using this simple linear approximation between N_{D} and x, the above model further enables a nice prediction on κ_{L} versus x at a given temperature, as shown in Fig. 3b. This confirms the dislocation scattering is indeed helpful for reducing the lattice thermal conductivity.
The modelpredicted frequencydependent accumulative reduction in κ_{L} (Supplementary Fig. 4) indeed shows the significant effect of dislocations for midfrequency phonon scattering in Pb_{0.95}Sb_{0.33}Se. The predicted accumulative κ_{L} due to Umklapp and normal scattering in pure PbSe, further helps us understand the important range of mean free path^{56} that contributes to heat conduction. It is also worthy to note that the mechanical strength does not degrade a lot due to the existence of dense ingrain dislocations here (Supplementary Table 4).
Transport properties
In spite of the strong scattering of phonons, one needs also to be careful when evaluating the thermoelectric properties, because the formation of solid solutions may change the band structure, whereas the existence of dislocations may affect the scattering of charge carriers. To clarify this possibility, the Hall carrier concentrationdependent roomtemperature Seebeck coefficient is shown in Fig. 4a. It is seen that both the literature PbSe^{36} and the current Pb_{1−x}Sb_{2x/3}Se solid solution show nearly the same relationship between Seebeck coefficient and Hall carrier concentration. This indicates the band parameters such as the densityofstates effective mass remains unchanged. Therefore, they both can be described by a single Kane band model.
The temperaturedependent Hall mobility (Fig. 4b) helps understand the carrier scattering mechanism. With increasing x, thus an increase in dislocation density, it is shown that at T<500 K the Hall mobility (μ_{H}) decreases much slower with increasing temperature as compared with a relationship of μ_{H}∼T^{−2.25} that is normally expected for nPbSe^{53}. This can be understood, because a temperaturedependent mobility of μ_{H}∼T^{1.5} will be observed in case of carrier scattering dominated by dislocations^{57}, which is similar with that of ionized impurity scattering. This type of scattering can be effectively screened here, because of the high dielectric constant of PbSe^{53}; therefore, a high mobility can still be obtained. Similar dielectric screening effects for a high mobility has been found in semiconductors and graphene^{58,59,60}. However, the temperaturedependent Hall mobility in Pb_{1−x}Sb_{x}Se^{40}, without dense dislocations as in Pb_{1−x}Sb_{2x/3}Se, does not indicate a T^{1.5}type contribution to the Hall mobility. The electronic transport of Pb_{1−x}Sb_{x}Se^{40} without dislocations show normal ntype doped PbSe^{36} behaviour.
The temperaturedependent thermal conductivity (κ), Seebeck coefficient (S) and resistivity (ρ) are shown in Fig. 5a–c, respectively. With increasing x, the reduced thermal conductivity is largely from the lattice thermal conductivity reduction due to the vacancyinduced dislocations. It should be noted that the Lorenz factor is determined by the single Kane band model to estimate the electronic thermal conductivity (κ_{E}). At T<600 K, the decrease in resistivity in the heavily alloyed samples can be explained by the resulting dislocation scattering on carriers (Fig. 4b). The decrease in ρ and S at T>700 K is probably due to the existence of minority carriers, which is normally seen in narrow band gap semiconductors.
Discussion
In summary, this work presents a method to create uniformly distributed dense dislocations throughout the entire grains of Pb_{1−x}Sb_{2x/3}Se solid solutions by the introduction of cation vacancies. Owing to the strong phonon scattering by dislocation cores and strain fields, the lattice thermal conductivity reaches the theoretical minimum and, therefore, a high figure of merit zT is obtained. Unlike previously demonstrated approaches focusing on the scattering of phonons with either low or high frequencies, this work proposes a vacancy engineering strategy for welldispersed dense dislocations, enabling an effective demonstration of midrange frequency phonon scattering for low lattice thermal conductivity. This strategy emphasizes a thermal effect, which is independent of other existing strategies, such as band engineering, for increasing the electrical performance^{2}. Therefore, a combination with other strategies offers great potential for further improvements of thermoelectrics.
Methods
Synthesis
Starting with pure elements (Pb 99.99%, Sb 99.99%, Se 99.999%), Pb_{1−x}Sb_{2x/3}Se solid solutions with x from 0 to 9% were prepared by melting at 1,400 K for 6 h, followed by quenching in water and annealing at 1,023 K for 2 days. An Ag doping of ≤1% at the Pb site was also used to help control the carrier concentration precisely. The ingot materials were ground into fine powders for hot pressing^{58} at 973 K for 1 h under a uniaxial pressure of ∼90 MPa under vacuum. The disk samples for measurements were ∼2 mm in diameter and ∼1.5 mm in thickness, and the density (d) is higher than 96% of theoretical value.
Characterization
The phase impurity was characterized by lab XRD (Dandong Haoyuan Instrument Co. Ltd). The samples for (S)TEM observation were prepared by mechanical polishing, dimpling and ion milling with liquid nitrogen. TEM and STEM imaging including in highangle annular dark field and annular bright field modes, as well as energy dispersive Xray spectroscopy element mapping were carried out by JEOL ARM 200 equipped with a probe corrector and an image corrector. Synchrotron XRD measurements were carried out at the beamline number 14B of the Shanghai Synchrotron Radiation Facility. The energy of monochromatic Xray beam was 10 keV, corresponding to a wavelength of 0.687 nm. The reflection mode was applied and the signal was recorder by a NaI(Tl) scintillation detector. The beam size is 0.5 × 1 mm. The line profiles were recorded with a step size of 0.02° and a dwell time of 3 s.
Transport property measurements
The electrical properties including Seebeck coefficient, resistivity and Hall coefficient were simultaneously measured on the samples during both heating and cooling in vacuum. The Seebeck coefficient in the inplane direction was obtained from the slope of the thermoelectric voltage versus temperature gradients^{59}. The inplane resistivity and Hall coefficient were measured using the Van der Pauw technique under a reversible magnetic field of 1.5 T. The uncertainty of each transport property measurement is ∼5%. The thermal diffusivity D_{T} was measured by the laser flash method (Netzsch LFA 457) and the thermal conductivity κ was calculated from κ=dD_{T}C_{p}, where C_{p} is the heat capacity determined by C_{p}(k_{B}/atom)=(3.07+0.00047(T/K300))^{60,61}. The sound velocity was measured by an ultrasonic pulsereceiver (OlympusNDT) equipped with an oscilloscope (Keysight). The uncertainty for each measurement of transport property is ∼5%.
Data availability
The data that support the findings of this study are available from the corresponding author upon request.
Additional information
How to cite this article: Chen, Z. et al. Vacancyinduced dislocations within grains for highperformance PbSe thermoelectrics. Nat. Commun. 8, 13828 doi: 10.1038/ncomms13828 (2017).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
 1.
Bell, L. E. Cooling, heating, generating power, and recovering waste heat with thermoelectric systems. Science 321, 1457–1461 (2008).
 2.
Pei, Y. et al. Convergence of electronic bands for high performance bulk thermoelectrics. Nature 473, 66–69 (2011).
 3.
Liu, W. et al. Convergence of conduction bands as a means of enhancing thermoelectric performance of ntype Mg_{2}Si_{1−x}Sn_{x} solid solutions. Phys. Rev. Lett. 108, 166601 (2012).
 4.
Pei, Y. et al. Stabilizing the optimal carrier concentration for high thermoelectric efficiency. Adv. Mater. 23, 5674–5678 (2011).
 5.
Xie, H. et al. Beneficial contribution of alloy disorder to electron and phonon transport in halfHeusler thermoelectric materials. Adv. Funct. Mater. 23, 5123–5130 (2013).
 6.
Pei, Y., LaLonde, A. D., Heinz, N. A. & Snyder, G. J. High thermoelectric figure of merit in PbTe alloys demonstrated in PbTe–CdTe. Adv. Energy Mater. 2, 670–675 (2012).
 7.
Pei, Y., Wang, H., Gibbs, Z. M., LaLonde, A. D. & Snyder, G. J. Thermopower enhancement in Pb1xMnxTe alloys and its effect on thermoelectric efficiency. NPG Asia Mater. 4, e28 (2012).
 8.
Lin, S. et al. Tellurium as a highperformance elemental thermoelectric. Nat. Commun. 7, 10287 (2016).
 9.
Jian, Z. et al. Significant band engineering effect of YbTe for high performance thermoelectric PbTe. J. Mater. Chem. C 3, 12410–12417 (2015).
 10.
Li, W. et al. Band and scattering tuning for high performance thermoelectric Sn_{1−x}Mn_{x}Te alloys. J. Mater. 1, 307–315 (2015).
 11.
Hsu, K. F. et al. Cubic AgPb_{m}SbTe_{2+m}: bulk thermoelectric materials with high figure of merit. Science 303, 818–821 (2004).
 12.
Biswas, K. et al. Highperformance bulk thermoelectrics with allscale hierarchical architectures. Nature 489, 414–418 (2012).
 13.
Poudel, B. et al. Highthermoelectric performance of nanostructured bismuth antimony telluride bulk alloys. Science 320, 634–638 (2008).
 14.
Pei, Y., LenschFalk, J., Toberer, E. S., Medlin, D. L. & Snyder, G. J. High thermoelectric performance in PbTe due to large nanoscale Ag_{2}Te precipitates and La doping. Adv. Funct. Mater. 21, 241–249 (2011).
 15.
Vining, C. B. in CRC Handbook of Thermoelectrics ed. Rowe D. M. Ch. 28, CRC Press (1995).
 16.
Schemer, H. & Scherrer, S. in CRC Handbook of Thermoelectrics ed. Rowe D. M. Ch. 19, CRC Press (1995).
 17.
Zhao, L.D. et al. Ultralow thermal conductivity and high thermoelectric figure of merit in SnSe crystals. Nature 508, 373–377 (2014).
 18.
Morelli, D. T., Jovovic, V. & Heremans, J. P. Intrinsically minimal thermal conductivity in cubic IVVI_{2} semiconductors. Phys. Rev. Lett. 101, 035901 (2008).
 19.
He, J. Q., Girard, S. N., Kanatzidis, M. G. & Dravid, V. P. Microstructurelattice thermal conductivity correlation in nanostructured PbTe_{0.7}S_{0.3} thermoelectric materials. Adv. Funct. Mater. 20, 764–772 (2010).
 20.
Kim, S. I. et al. Thermoelectrics. Dense dislocation arrays embedded in grain boundaries for highperformance bulk thermoelectrics. Science 348, 109–114 (2015).
 21.
Klemens, P. G. The scattering of lowfrequency lattice waves by static imperfections. Proc. Phys. Soc. A68, 1113–1128 (1955).
 22.
Adams, A., Baumann, F. & Stuke, J. Thermal conductivity of selenium and tellurium single crystals and phonon drag of tellurium. Phys. Stat. Solid. (b) 23, K99–K104 (1967).
 23.
Hirth, J. P. Theory of Dislocations 2nd Edn John Willey & Sons (1982).
 24.
de Kock, A. J. R. The elimination of vacancy‐cluster formation in dislocation‐free silicon crystals. J. Electrochem. Soc. 118, 1851–1856 (1971).
 25.
Mott, N. F. CXVII. A theory of workhardening of metal crystals. LED Phil. Mag. J. Sci. 43, 1151–1178 (2010).
 26.
Jin, N. Y. Formation of dislocation structures during cyclic deformation of F.C.C. crystals—I. Formation of PSBs in crystals oriented for singleslip. Acta Metall. 37, 2055–2066 (1989).
 27.
Read, W. T. LXXXVII. Theory of dislocations in germanium. LED Phil. Mag. J. Sci. 45, 775–796 (2009).
 28.
Meyer, M. Some electrical and optical effects of dislocations in semiconductors. J. Appl. Phys. 38, 4481 (1967).
 29.
Koehler, J. S. A calculation of the changes in the conductivity of metals produced by coldwork. Phys. Rev. 75, 106–117 (1949).
 30.
Dexter, D. L. & Seitz, F. Effects of dislocations on mobilities in semiconductors. Phys. Rev. 86, 964–965 (1952).
 31.
Tan, T. Y., You, H.M. & Gösele, U. M. Thermal equilibrium concentrations and effects of negatively charged Ga vacancies in ntype GaAs. Appl. Phys. A 56, 249–258 (1993).
 32.
Hirsch, P. B., Silcox, J., Smallman, R. E. & Westmacott, K. H. Dislocation loops in quenched aluminium. Philos. Mag. 3, 897–908 (1958).
 33.
Suzuki, T., Ueno, M., Nishi, Y. & Fujimoto, M. Dislocation loop formation in nonstoichiometric (Ba,Ca)TiO_{3} and BaTiO_{3} ceramics. J. Am. Ceram. Soc. 84, 200–206 (2001).
 34.
Frank, F. Dislocations and point defects. Discuss. Farad. Soc. 23, 122–127 (1957).
 35.
Hollmon, J., Maurer, R., Seitz, F. & Shockley, W. in Imperfections in Nearly Perfect Crystals. Symposium held at Pocono Manor, Penna, USA, 12–14 October 1950 (eds Shockley W., Hollomon J. H., Maurer R. and Seitz F.), pp490 (Wiley: New York; Chapman and Hall: London, 1952).
 36.
Wang, H., Pei, Y., LaLonde, A. D. & Snyder, G. J. Weak electronphonon coupling contributing to high thermoelectric performance in ntype PbSe. Proc. Natl Acad. Sci. USA 109, 9705–9709 (2012).
 37.
Cahill, D. G., Watson, S. K. & Pohl, R. O. Lower limit to the thermal conductivity of disordered crystals. Phys. Rev. B 46, 6131 (1992).
 38.
Whitworth, R. W. Charged dislocations in ionic crystals. Adv. Phys. 24, 203–304 (1974).
 39.
Johnston, W. G. & Gilman, J. J. Dislocation multiplication in lithium fluoride crystals. J. Appl. Phys. 31, 632–643 (1960).
 40.
Lee, Y. et al. Contrasting role of antimony and bismuth dopants on the thermoelectric performance of lead selenide. Nat. Commun. 5, 3640 (2014).
 41.
Lidiard, A. B. CXXXIII. Impurity diffusion in crystals (mainly ionic crystals with the sodium chloride structure). LED Phil. Mag. J. Sci. 46, 1218–1237 (2009).
 42.
Hu, S. M. General theory of impurity diffusion in semiconductors via the vacancy mechanism. Phys. Rev. 180, 773–784 (1969).
 43.
Nichols, C. S., Van de Walle, C. G. & Pantelides, S. T. Mechanisms of dopant impurity diffusion in silicon. Phys. Rev. B 40, 5484–5496 (1989).
 44.
Christoph Mueller, D., Alonso, E. & Fichtner, W. Arsenic deactivation in Si: electronic structure and charge states of vacancyimpurity clusters. Phys. Rev. B 68, 045208 (2003).
 45.
Ranki, V., Nissila, J. & Saarinen, K. Formation of vacancyimpurity complexes by kinetic processes in highly Asdoped Si. Phys. Rev. Lett. 88, 105506 (2002).
 46.
Stark, J. P. The diffusivity, mobility, and correlation factor for solute vacancy diffusion in an edge dislocation in a facecenteredcubic crystal. J. Appl. Phys. 62, 3077 (1987).
 47.
Prasad, D. S., Munirathnam, N. R., Rao, J. V. & Prakash, T. L. Purification of tellurium up to 5N by vacuum distillation. Mater. Lett. 59, 2035–2038 (2005).
 48.
Ungár, T., Dragomir, I., Revesz, A. & Borbély, A. The contrast factors of dislocations in cubic crystals: the dislocation model of strain anisotropy in practice. J. Appl. Crystallogr. 32, 992–1002 (1999).
 49.
Ungar, T., Ott, S., Sanders, P., Borbély, A. & Weertman, J. Dislocations, grain size and planar faults in nanostructured copper determined by high resolution Xray diffraction and a new procedure of peak profile analysis. Acta Mater. 46, 3693–3699 (1998).
 50.
Pei, Y. & Morelli, D. Vacancy phonon scattering in thermoelectric In_{2}Te_{3}InSb solid solutions. Appl. Phys. Lett. 94, 122112 (2009).
 51.
Abeles, B. Lattice thermal conductivity of disordered semiconductor alloys at high temperatures. Phys. Rev. 131, 1906–1911 (1963).
 52.
Tian, Z. et al. Inelastic xray scattering measurements of phonon dispersion and lifetimes in PbTe_{1−x} Se_{x} alloys. J. Phys. Condens. Matter 27, 375403 (2015).
 53.
Ravich, Y. I., Efimova, B. A. & Smirnov, I. A. Semiconducting Lead Chalcogenides Plenum Press (1970).
 54.
Wang, H., Wang, J., Cao, X. & Snyder, G. J. Thermoelectric alloys between PbSe and PbS with effective thermal conductivity reduction and high figure of merit. J. Mater. Chem. A 2, 3169–3174 (2014).
 55.
Callaway, J. & Vonbaeyer, H. C. Effect of point imperfections on lattice thermal conductivity. Phys. Rev. 120, 1149–1154 (1960).
 56.
Tian, Z. et al. Phonon conduction in PbSe, PbTe, and PbTe_{1−x}Se_{x} from firstprinciples calculations. Phys. Rev. B 85, 184303 (2012).
 57.
Ng, H. M., Doppalapudi, D., Moustakas, T. D., Weimann, N. G. & Eastman, L. F. The role of dislocation scattering in ntype GaN films. Appl. Phys. Lett. 73, 821 (1998).
 58.
LaLonde, A. D., Ikeda, T. & Snyder, G. J. Rapid consolidation of powdered materials by induction hot pressing. Rev. Sci. Instrum. 82, 025104 (2011).
 59.
Zhou, Z. H. & Uher, C. Apparatus for Seebeck coefficient and electrical resistivity measurements of bulk thermoelectric materials at high temperature. Rev. Sci. Instrum. 76, 023901 (2005).
 60.
Pei, Y., LaLonde, A. D., Wang, H. & Snyder, G. J. Low effective mass leading to high thermoelectric performance. Energ. Environ. Sci. 5, 7963–7969 (2012).
 61.
Blachnik, R. & Igel, R. Thermodynamic properties of IVVI compounds lead chalcogenides. Z. Naturforsch. B 29, 625–629 (1974).
Acknowledgements
This work is supported by the National Natural Science Foundation of China (Grant Numbers 51422208, 11474219, 51401147 and 11374332), the National Recruitment Program of Global Youth Experts (1000 Plan), the fundamental research funds for the central universities, the BayerTongji EcoConstruction & Material Academy (TB20140001) and the SolidState SolarThermal Energy Conversion Center (S3TEC), an Energy Frontier Research Center funded by the U.S. Department of Energy, Office of Science, Basic Energy Sciences under award number DESC0001299.
Author information
Author notes
 Zhiwei Chen
 & Binghui Ge
These authors contributed equally to this work
Affiliations
Key Laboratory of Advanced Civil Engineering Materials of Ministry of Education, School of Materials Science and Engineering, Tongji University, 4800 Caoan Road, Shanghai 201804, China
 Zhiwei Chen
 , Wen Li
 , Siqi Lin
 , Jiawen Shen
 & Yanzhong Pei
Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Science, Beijing 100190, China
 Binghui Ge
 & Yunjie Chang
Department of Materials Science and Engineering, Northwestern University, 2220 Campus Drive, 3033 Cook Hall, Evanston, Illinois 60208 USA
 Riley Hanus
 & G. Jeffrey Snyder
Authors
Search for Zhiwei Chen in:
Search for Binghui Ge in:
Search for Wen Li in:
Search for Siqi Lin in:
Search for Jiawen Shen in:
Search for Yunjie Chang in:
Search for Riley Hanus in:
Search for G. Jeffrey Snyder in:
Search for Yanzhong Pei in:
Contributions
Y.P. designed this work. Z.C., W.L., S.L. and J.S. synthesized the samples and carried out the transport property measurements. Y.C. and B.G. performed the (scanning) TEM observations. Z.C., Y.P., B.G., R.H. and G.J.S. analysed the transport properties, the microstructures and the linkage between. Z.C., Y.P., R.H. and G.J.S. discussed the formation mechanism of the dense dislocations via the vacancy engineering approach. All authors wrote and edited the manuscript.
Competing interests
The authors declare no competing financial interests.
Corresponding authors
Correspondence to G. Jeffrey Snyder or Yanzhong Pei.
Supplementary information
PDF files
 1.
Supplementary Information
Supplementary Figures, Supplementary Tables, Supplementary Discussion, Supplementary References.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Further reading

1.
Enhanced thermoelectric performance of Cu12Sb4S13−δ tetrahedrite via nickel doping
Science China Materials (2018)

2.
Promising cubic MnGeTe2 thermoelectrics
Science China Materials (2018)

3.
Frontiers of Physics (2018)

4.
Enhanced thermoelectric performance of Nadoped PbTe synthesized under high pressure
Science China Materials (2018)

5.
Enhancing Thermoelectric Performance of PbSe by Se Vacancies
Journal of Electronic Materials (2018)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.