Conventional adhesives show a decrease in the adhesion force with increasing temperature due to thermally induced viscoelastic thinning and/or structural decomposition. Here, we report the counter-intuitive behaviour of carbon nanotube (CNT) dry adhesives that show a temperature-enhanced adhesion strength by over six-fold up to 143 N cm−2 (4 mm × 4 mm), among the strongest pure CNT dry adhesives, over a temperature range from −196 to 1,000 °C. This unusual adhesion behaviour leads to temperature-enhanced electrical and thermal transports, enabling the CNT dry adhesive for efficient electrical and thermal management when being used as a conductive double-sided sticky tape. With its intrinsic thermal stability, our CNT adhesive sustains many temperature transition cycles over a wide operation temperature range. We discover that a ‘nano-interlock’ adhesion mechanism is responsible for the adhesion behaviour, which could be applied to the development of various dry CNT adhesives with novel features.
Adhesion between different solids permeates all aspects of our daily lives. Depending on the nature of applications, adhesives are subjected to diverse environments, ranging from the polymer-based adhesives (for example, Scotch tape, Scotch super glue, 3M Super Sticky Post-it Notes) used at ambient temperature for daily essentials, through specially designed rubbery sealants for automobile and aerospace vehicles in sub-freezing space or polar regions, to ceramic or metallic permanent glues for some specific operation processes at high temperatures (for example, solar cell panels, space shuttle launching and landing). However, conventional adhesives often show structural or performance deterioration at extreme temperatures, which could cause catastrophes1. For example, for high-temperature applications (for example, >500 °C), ceramic adhesives and/or metal welding are normally considered since they can stand up to temperatures even over 1,000 °C (refs 2, 3). Nevertheless, interfacial debonding cannot be prevented due to the differential thermal expansions between the adhesive layer and target surfaces, especially over thermal transitions with a wide temperature range.
Resembling a gecko’s adhesive foot hairs with additional superior mechanical, electrical, and thermal properties4, carbon nanotubes (CNTs) with hierarchical structures (for example, vertically aligned) are ideal stable adhesives for thermal and/or electrical management at high temperatures. However, this possibility has yet to be realized largely due to difficulties in the design and development of CNTs with optimized hierarchical structures. A strong shear adhesion force of ∼100 N cm−2—ten times that of the gecko foot adhesive (the strongest dry adhesion force among all climbing animals)—was previously reported for vertically aligned multi-walled CNTs (VA-MWNTs) against a glass substrate4, where the van der Waals (vdW) force was demonstrated to be responsible for the strong adhesion. In this particular case, it was found that the entangled nanotube tops enhanced their intimate contacts with smooth surfaces, and hence resulted in strong van der Waals forces4. Although a hierarchical CNT/polymer fibrillar structure was proposed in a subsequent study to promote the rough surface adaptability5, most reported carbon nanotube dry adhesives were tested against smooth surfaces (for example, glass plates, Si wafers) to enhance the vdW interaction4,6,7,8. Meanwhile, certain specially structured CNT adhesives with multi-functionalities have been explored. Examples include the patterning of VA-CNTs for self-cleaning6, depositing entangled nanotube segments on the top of VA-CNTs for anisotropic adhesion force distribution4, producing single-walled VA-CNTs to extend the operational temperature from room temperature (ca. 24 °C) to ∼200 °C (ref. 7), and using VA-CNTs as electrically and thermally conducting dry adhesives at ambient temperature8.
In this work, we achieve thermally enhanced CNT adhesives for high-temperature applications by rationally designing vertically aligned double-walled CNT (VA-DWNT) strands with bundled top nodes induced by plasma treatment. In contrast to our expectations, we find that the adhesion strength of our CNT dry adhesives on rough surfaces (for example, commercially-available copper foils, vide infra) increased with increasing temperature by over six-fold up to 143 N cm−2 at high temperatures (for example, 1,000 °C), one of the highest values reported. This unusual adhesion behaviour can be rationalized by a ‘nano-interlocking’ adhesion mechanism, in which the plasma-induced CNT top nodes can easily penetrate into cavities of a naturally or temperature-induced rough surface, followed by temperature-induced deformation of the flexible double-walled CNT segments along the surface profile to form nano-interlocks (vide infra). The screw-like nano-interlocking interaction distinguishes the CNT dry adhesive reported in this study from other conventional adhesives, including conventional CNT dry adhesives4,6,7,8 and polymeric dry adhesives9,10,11. Our CNT dry adhesives sustain many temperature transition cycles over a wide operational temperature range from −196 to 1,000 °C with a high thermal stability and a temperature-enhanced adhesion strength up to 143 N cm−2 (one of the highest adhesion strengths among all known pure CNT dry adhesives).
Figure 1a–d schematically shows the procedure for preparing our CNT dry adhesive (CNT length: ∼300–500 μm, diameter: 7–10 nm, Supplementary Figs 1 and 2) while details for the material preparation can be found in the Methods. Briefly, the VA-DWNT array was synthesized according to the published procedure12, followed by well-controlled oxygen plasma etching13,14 and argon annealing (Supplementary Figs 3 and 4) to remove the nonaligned nanotube segments, leading to the nanotube bundling and the top node formation (Fig. 1e,f). In previous studies, nonaligned nanotube top segments have been used to enhance the shear adhesion force (up to ∼100 N cm−2) for VA-MWNT arrays against smooth surfaces (for example, glass plates, Si wafers)4 whereas similar plasma-etched VA-MWNT arrays with bundled tops were found to show weak adhesions (<12 N cm−2) on the smooth surfaces8. However, plasma etching has been previously demonstrated to provide the additional advantage of facilitating the hydrogen-bonding mediated interaction between nanotubes and hydrophilic surfaces. Unlike previous studies, the plasma-induced bundled top nodes were designed in this study to facilitate a node-guided penetration into the surface cavities (Fig. 1c,d), initiating and ensuring an intimate contact of the VA-DWNT adhesive with temperature-induced rough surfaces.
By sandwiching a free-standing film of the CNT dry adhesive (4 mm × 4 mm, Fig. 1g) between two copper surfaces (Alfa Aesar, A Johnson Matthey Company) with the constituent CNTs normal to the target surface by finger pressing (∼7 N cm−2), we used a torch for heating to make a quick demonstration of the wide operation temperature range and measured the shear adhesion force using a digital spring balance (AWS H-110) (Fig. 1g–j, Methods, Supplementary Figs 5 and 6). The high melting temperature (1,083 °C), together with its excellent thermal and electrical properties for thermal and electrical managements15, makes the copper foil a model target surface for demonstrating CNT adhesion at high temperatures. Nevertheless, the methodology developed in this study is applicable to many other metallic and non-metallic substrates, including aluminum foil, glass plate, silicon wafer and polymer films (for example, a fluorinated ethylene propylene (FEP) film).
As seen in Fig. 1g, our newly developed CNT adhesive showed a room-temperature (24.2 °C) adhesion strength of ∼37 N cm−2, a value which is similar to that of a 3M double-side sticky tape (Methods). Upon continuous heating by a butane torch (Master Appliance MT-30 Table Top Self Igniting Microtorch with the flame temperature up to 1,970 °C), we found with surprise that the adhesion strength increased with increasing temperature from ∼37 N cm−2 (24.2 °C) through ∼60 N cm−2 (418.7 °C) to ∼124 N cm−2 (1,033 °C) (Fig. 1g–i). As far as we are aware, such a temperature-induced adhesion enhancement has never been reported for any existing adhesive materials, and the value of 124 N cm−2 is among the highest adhesion strength for all known pure CNT dry adhesives (Supplementary Table 1). On the other hand, it was found that the room temperature adhesion strength remained almost unchanged (∼34 N cm−2) even when our CNT dry adhesive was cooled down near to the liquid nitrogen temperature (−190.7 °C, Fig. 1j)—still outperforming all conventional viscoelastic tapes (for example, 3M double-sided sticky tape), which would have become glassy and detached from the target surface in such a cold environment.
Figure 1k shows the retained vertical alignment of the nanotube trunks for a VA-DWNT dry adhesive even after being tested at 1,033 °C. The corresponding Raman spectra (Fig. 1l) and X-ray photoelectron spectroscopic (XPS) results (Fig. 1m) show an improvement of the nanotube structure after the high temperature testing due to a thermally induced increase in the graphitization degree with a concomitant loss of physically adsorbed oxygen molecules16, as reflected by the increase in the Raman G band relative to the D band and decrease in the XPS O 1s peak with respect to the XPS C 1s peak. This, together with the absence of catalyst residue from our nanotube materials (Fig. 1m; Supplementary Fig. 1), ensured the superior thermal stability even in air for our VA-DWNTs, consistent with the previous report17.
To compare the temperature-enhanced adhesion of our CNT dry adhesive with commercially available adhesive tapes, we selected the Duro super glue (∼103 N cm−2) with a maximum operation temperature (MOT) of 93 °C, 3 M thermally conductive tape (32 N cm−2, MOT=260 °C), and 3 M double-side sticky tape (∼42 N cm−2, MOT=85 °C) of the same size (4 mm × 4 mm) as the benchmarks since they have either a high adhesion force or high-temperature resistance, or both, among viscoelastic tapes. We found that these conventional adhesives showed a dramatic decrease in the adhesion force with increasing temperature (inset of Fig. 1n) due to the thermally induced viscoelastic thinning and/or structural decomposition. In contrast, our CNT dry adhesive exhibited a steadily increased adhesion force with increasing temperature up to ∼1,000 °C (Fig. 1n). The above temperature dependence of the VA-DWNT adhesion demonstrated by torch heating was confirmed by more careful adhesion strength measurements on the CNT dry adhesive being thermally treated with an in situ (heated and adhesion measured in TA Instruments, RSA-G2 with Environmental Test Chamber) or ex situ (heated inside of a muffle furnace and cooled down to room temperature for the adhesion force measurements) temperature control (Supplementary Fig. 7). The in situ and ex situ temperature controlled measurements showed an agreement in the adhesion enhancement trend, implying that the irreversible adhesion enhancement with increasing temperature (≥∼200 °C) has been reliably measured.
Nano-interlocking dry adhesion mechanism
The observed thermally induced adhesion enhancement (Fig. 1n) is the result of a nano-interlocking dry adhesion mechanism. To elucidate the nano-interlocking dry adhesion mechanism, we took scanning electron microscopy (SEM) images of the CNT adhesive surface after detachment (Fig. 2a). The top-view image in Fig. 2a shows uniformly distributed web-like domains with a center-to-center distance of 1–2 μm, which is significantly different from the randomly entangled top segments on the as-grown VA-DWNT array (Fig. 2d, cf. Fig. 1e). The enlarged view of individual web-like domains (Fig. 2c) clearly shows the web-like structure with CNT segments radiated out from the center. We further found that there were residual CNTs adhered onto the target copper surface in a web-like shape (Fig. 2b) with some of CNTs being overstretched into aligned nanotubes parallel to the shear direction. These CNT webs are distributed uniformly on the target surface, about 1–2 μm apart from each other, (Fig. 2b), which is a close replication of the CNT coils shown in Fig. 2a. The formation of these web-like contacts is further revealed by SEM examination of the structural deformation of an individual CNT bundle as a model under the normal loading (Fig. 2e–j). Figure 2e,h shows that the adhesion process commences from the point-contact between the CNT node and the target surface. Under an appropriate pre-loading force (>25 N cm−2, Supplementary Fig. 8), the VA-DWNT bundle starts to deform (Fig. 2f,i) and finally collapses through the web-like deformation into the line contacts with the target surface around the node (Fig. 2g,j). Thus, it is likely that the node of the VA-DWNT bundle penetrates into a surface cavity during the contact process, from which CNTs in the bundle radiate out through the web-like deformation with some of them being overstretched into aligned nanotubes parallel to the shear direction upon shear (Fig. 2b,g). The screw-like, node-guided penetration of CNTs into the surface cavities and the associated side contacts between the nanotubes and cavities after the web-like deformation are evident in the SEM images shown in Fig. 2a,c. The observed web-like collapsing of the CNT bundle can be schematically depicted in Fig. 2h–j, which under normal compression collapses into a web-like structure to allow for line (side) contacts with the target surface around the node. Therefore, the node-guided contact mode, in conjunction with the web-like collapsing described above, provides synergistic effects for the use of our CNT dry adhesives on rough surfaces. The wall number of CNTs is a crucial factor to control the nanotube elasticity for plasma-induced bundling and node formation. Thus, the VA-DWNTs were chosen for their proper flexbility and good thermal stability associated with high purity17. The plasma-induced formation of the VA-DWNT bundles with a top node could overcome the over-softness of the individual DWNTs to ensure effective penetration into the cavities on rough surfaces and to allow for intimate point and side contacts with the target surface, and hence the maximized adhesion for the CNT dry adhesive4,7. As shown in Fig. 1c, however, the nonaligned top on the as-grown VA-DWNT array would prevent the CNTs from an intimate contact with a rough surface, though the top nonaligned nanotube segments on a VA-MWNT array have been reported to play an essential role in enhancing the CNT adhesion on a smooth surface (for example, glass plate) through shear-induced line contacts to enlarge the effective contact area, and hence the enhanced vdW force4,5.
Adhesion enhancement model
To more quantitatively study the interlock adhesion mechanism and the associated thermally induced adhesion enhancement, we replot the data from the ex situ measurements shown in Fig. 1n, along with the corresponding plot of the enhancement factor (defined as the normalization of adhesion strength at a specific temperature to the corresponding adhesion strength at room temperature), as a function of temperature in Fig. 3. As seen in the inset of Fig. 3a, the CNT adhesion increases by about six times (∼6.2 × ) with temperatures over −196 to ∼1,000 °C. However, either the vdW force dominated CNT adhesion4 or the viscoelastic interactions between the CNTs should be insensitive to the temperature variation, as demonstrated previously17. Clearly, therefore, an unknown yet decisive factor, in addition to the vdW and viscoelastic interactions, is regulating the observed temperature influence on the adhesion performance of the CNT adhesives.
Our SEM images taken from the copper foil under annealing at different temperatures show that surface segregation occurred upon heating the relatively smooth copper foil above ∼200 °C, leading to an increase in the surface roughness with increasing temperature (Supplementary Figs 9 and 10). It could guide the collapsed CNT segments around the node (cf. Fig. 3b) to penetrate further into the temperature-induced irregular profiles to mechanically lock them into the surface, which explained the enhanced adhesion under higher preloading by pushing more CNT (bundle) ``screws'' into deeper surface cavities to produce higher vdW forces for stronger surface fastening (Fig. 3b; Supplementary Fig. 11).
To verify the enhanced adhesion through this CNT nano-interlocking mechanism, we estimated the extra work to pull the CNT bundles out of pits. The VA-DWNT bundle was modelled as an elastic strand to be embedded in a surface asperity, which was assumed as a cylindrical rigid hole with depth of l and radius of a for simplicity, and subjected to pull-out force (F) (inset in Fig. 3c, cf. Supplementary Fig. 12). While the detailed derivation is given in Supplementary Equations 1–9 (Supplementary Discussions), equation (1) gives the enhancement factor at a specific temperature (T) as a function of the pull-out work associated with the asperities at T defined by l(T) and the fractional area of holes with CNT strand embedded in per unit area of surface, ϕ (where, ϕ=nπa2, ranging from 0 to 1, and there are n holes per unit area of the surface):18
The above equation illustrates that the screw-like enhancement mechanism at high temperatures produces deeper holes, leading to a deeper penetration of CNTs into the holes for stronger surface fastening. Equation (1) reveals that if once the depth l(T) is increased to greater than one-fourth (1/4) of the radius of the hole (a), the screw-like enhancement makes the contribution to the extra energy for detachment. The embedded length l(T) was approximated by using the roughness values (Rq) from the atomic force microscopic (AFM) investigation on the target copper surface at different temperatures (cf. Supplementary Fig. 10; Supplementary Table 2) and the radius of the hole was∼60 nm from SEM observation. We estimated the enhancement factors at different temperatures from equation (1) and found that it agreed well with the experimental data while ϕ was taken as 0.30 (red dots in Fig. 3c, along with the model calculation by using ϕ=0.05 and 0.50 for comparison). This result means that about 30% of the surface area contributes to the nano-interlocking extra energy in addition to the vdW contact.
Owing to the generic nature of the thermally induced surface roughness, the concept of the node-guided CNT nano-interlocking reported here could be regarded as a general strategy for the development of thermally enhanced CNT dry adhesives for a variety of target surfaces, ranging from polymer films to metal foils, over a wide range of operation temperatures (Supplementary Fig. 13). Indeed, Fig. 3d shows similar thermally induced adhesion enhancements for our CNT dry adhesives against a FEP film (American Durafilm, MOT=204 °C (ref. 19)) and aluminum foil (Al, Fisher Scientific, MOT=600 °C), but not against a silicon wafer (Silicon Quest International, MOT=1,300 °C). As expected, the temperature-invariant adhesion seen for the silicon plate in Fig. 3d suggests that the temperature-insensitive, hard and smooth silicon surface could not support the formation of the thermally induced interlocking structure with a very small value of 0.005 for ϕ. For the FEP and Al surfaces, a good agreement between the model fit with equation (1) and experimental data was obtained when ϕ is 0.46 and 0.23, respectively, indicating that 46% and 23% of the surface areas contribute to the nano-interlocking extra work in addition to the vdW force with the FEP and Al surface.
Electrical and thermal managements
As can be seen from the above discussions, our CNT dry adhesives have potential for various practical applications. In this context, the CNT dry adhesive was further subjected to electrical (Signatone S-1160 Probe Station) and thermal transport testing (LFA 457, Netzsch Laser flash) in the adhesive assembly (Supplementary Fig. 14). It was found that our CNT adhesive exhibited steadily increasing electrical conductivity (103–104 Scm−1) and thermal diffusivity (0.1–0.25 mm2 s−1, albeit relatively low in respect to the reported data for a VA-MWNT array20,21) with increasing temperature (adhesion strength) up to 1,000 °C (Fig. 4a,b, cf. Fig. 3). The one-order increase in the electrical conductivity is most probably associated with the thermally induced nano-interlocking, which enhances the CNT-target surface (that is, copper) contact, and hence the enhanced electrical conductivity and adhesion force (Fig. 4b). Compared with the temperature-enhanced electrical conductivity, the lesser increase in the thermal diffusivity (less than 2-fold) at high temperatures (Fig. 4b) indicates that some more stringent requirements on the CNT-target surface contact have to be met for efficient thermal transport21. We also investigated the long-term stability for the electrical transport during repeated temperature transition cycles over a wide temperature range from −196 to 1,000 °C. As seen in Fig. 4, our CNT dry adhesive could not only retain the adhesion force (Fig. 4b) but also exhibit increased charge-carry capacities over repeated heating (1,000 °C)–cooling (−196 °C)–heating (1,000 °C) cycles (Fig. 4c) due, once again, to the increased conductivity by the thermally enhanced CNT-copper contact. When performing the (1,000 °C)–cooling (25 °C)–heating (1,000 °C) cycles, we found that the CNT dry adhesive initially underwent the step-by-step increase in conductivity (inset of Fig. 4c, (g→n)) associated with an irreversible enhancement in the adhesion caused by the temperature-enhanced surface roughness. Thereafter, the step-by-step conductivity increase disappeared and a reversible sharp increase in current was observed upon heating up to about 65 cycles (Fig. 4c) due to the increased electrical conductivity of the nanotube array with increasing temperature (Supplementary Fig. 15), as is the case for VA-MWNTs22. We believed that the reversible fluctuation of the current at the cooling (−196 °C) — heating (25 °C) — cooling (−196 °C) cycles (inset of Fig. 4c, (a→f)) was also caused by the temperature-dependence of conductivity for the nanotube array. An ohmic contact between the Cu and CNT dry adhesive was also evident by linear I–V curves measured at different temperatures (Supplementary Fig. 16). For conventional adhesives, long term exposure to temperature variations often causes detachment even within their operation temperature ranges due to the thermal expansion mismatch between the adhesive layer and the target surface(s).
In addition to the thermally induced nano-interlocking interactions described above, similar adhesion behaviours were observed for our newly developed CNT dry adhesives against various naturally rough surfaces, including rough metal foils, plastic films, wood pieces, paper sheets, and even painted walls, at ambient temperature (Supplementary Figs 17 and 18 and associated Supplementary Movies 1 and 2, see also Supplementary Table 3). These results clearly indicate the potential of our CNT dry adhesives for room temperature applications with a variety of rough surfaces, apart from the low- and high-temperature applications described above. Thus, the newly discovered node-guided nano-interlocking adhesion mechanism can be applied for the development of high-performance CNT dry adhesives for a large variety of applications, ranging from adhesion to electrical and thermal management, over wide operation temperature ranges from −196 to 1,000 °C.
Double-walled CNT array synthesis and fabrication
The vertically-aligned carbon nanotube (VA-CNT) arrays were synthesized by low pressure chemical vapor deposition (CVD) on 4 × 4 mm2 SiO2 (400 nm)/Si wafers12. To start with, a 3-nm thick Fe layer was sputter coated on the wafers after the deposition of a 10-nm Al film. The catalyst coated substrate was then firstly inserted into a quartz tube furnace and heated up to 650 °C in air. This was followed by pumping the furnace chamber to a pressure less than 30 m torr. The aligned CNT arrays were grown by flowing a mixture gas of 40v/v% Ar, 30v/v% H2, 30v/v% C2H2 at 750 °C under 200 torr for 10–20 min. The resulting VA-CNT arrays were examined on scanning electron microscope (SEM, Hitachi S-4500), and VA-CNT arrays with length around 300–500 μm long were selected for dry adhesive testing in this experiment. Then, a piece of glass slide was used to gently push the VA-CNT array from its side in the direction parallel to the substrate. By so doing, the VA-CNT was easily removed whilst the structural integrity was maintained.
Adhesion force measurements
By using a digital spring balance (AWS H-110), the adhesion force was measured at the shear-direction by sandwiching the CNT dry adhesive (4 mm × 4 mm) between two copper surfaces (Alfa Aesar, A Johnson Matthey) by finger pressing (preloading force of ∼7 N cm−2) (Supplementary Fig. 5a). For a quick demonstration of the adhesion at high temperatures, the CNT dry adhesive was directly heated up to >1,000 °C by a butane torch (Master Appliance MT-30 Table Top Self Igniting Microtorch with the flame temperature up to 1,970 °C) within 15 s (Supplementary Fig. 5b). Even in the air, the CNT dry adhesive was sufficiently stable at temperatures for the test17. With the adhesion force increased with increasing temperature, the weight was increased by holding the hook of the spring balance and drawing down until debonding happened (Supplementary Fig. 5b). A digital camera (Sony DSC-TX100) was used to capture the temperature and adhesion force. As shown in Supplementary Fig. 5b, the CNT dry adhesive exhibited the held weight of 1.98 kg (that is, 124 N cm−2) at 1,033 °C. Finally, the adhesion failure happened at 1,085 °C (the melting point of copper, inset of Fig. 1i). For a quick demonstration of the low temperature test at −190.7 °C, we used a thick piece of tissue papers pre-immersed in Liquid N2 to quickly cool down the CNT adhesive (Supplementary Fig. 5c). The adhesion force measurements at both the high and low temperatures were repeated by heating the CNT dry adhesive inside of a muffle furnace (LABEC 240 V/2,000 W, Ceramic Engineering) and cooling in a liquid nitrogen container, respectively (see text). Plasma treatments were performed on a customer-built plasma reactor powered by commercial plasma generator (AGO201 HV, T&C Power Conversion, Inc.)14. We used the O2-plasma etching to treat both the top and bottom surfaces of the free-standing CNT film to create the similar bundled surface topography with nodes on the both sides.
Adhesion strength calculation
The adhesion strength was calculated by dividing the value of the adhesion force by the CNT adhesive size (that is, the contact area). Supplementary Figure 6 shows the relationship between the adhesion strength and the contact side length of square CNT adhesive samples (that is, the CNT adhesive contact area). As can be seen in Supplementary Fig. 6, the adhesion strength keeps unchanged with changing the adhesive contact area up to 1 cm × 1 cm, followed by a slight decrease in the adhesion strength with further increasing the adhesive contact area up to 2.5 cm × 2.5 cm, presumably because the contact is normally poorer with a larger contact area, as is the case for all sorts of dry adhesives.
For structure observation, SEM images were taken using a Hitachi S-4500 instrument to observe the surface morphologies of the CNT arrays and target surfaces.
For nanotube structural characterization, transmission electron microscopy images were taken using a JEOL JEM-2000FX instrument.
Raman spectroscopy was performed on a Thermo-Electron Raman spectrometer with 532-nm excitation wavelength.
X-ray photoelectron spectroscopic
XPS measurements were carried out on a VG Microtech ESCA 2000 using a monochromic Al X-ray source (97.9 W, 93.9 eV).
Electrical and thermal property measurements
Electrical conductivity was measured on Signatone S-1160 Probe Station while thermal diffusivity was measured on LFA 457, Netzsch Laser flash.
Atomic force microscopy
AFM investigation was carried out on a Model of 5420 from Agilent Technologies.
Surface roughness and morphology measurements
Surface roughness and morphology were measured by AFM in a non-contact mode. To remove the contamination, the samples were cleaned by ethanol and dried before measurements 1 × 1 μm area AFM images were used for analysis. The root mean squared roughness (Rq) as was adopted to distinguish the roughness features of various target surfaces. Five tests were conducted on different areas to get average values.
All the data that support the findings of this study are available from the corresponding author upon reasonable request.
How to cite this article: Xu, M. et al. Carbon nanotube dry adhesives with temperature-enhanced adhesion over a large temperature range. Nat. Commun. 7, 13450 doi: 10.1038/ncomms13450 (2016).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Baglin, J. E. E. Thin film adhesion: new possibilities for interface engineering. Mater. Sci. Eng. B 1, 1–7 (1988).
Wang, J., Jiang, N. & Jiang, H. The high-temperatures bonding of graphite/ceramics by organ resin matrix adhesive. Int. J. Adhes. Adhes. 26, 532–536 (2006).
Riedel, R. & Chen, I. W. Ceramics Science and Technology in Synthesis and Processing vol. 3, 228–243Wiley VCH (2012).
Qu, L., Dai, L., Stone, M., Xia, Z. & Wang, Z. L. Carbon nanotube arrays with strong shear binding-on and easy normal lifting-off. Science 322, 238–242 (2008).
Rong, Z. et al. Bio-inspired hierarchical polymer fiber-carbon nanotube adhesives. Adv. Mater. 26, 1456–1461 (2014).
Sethi, S., Ge, L., Ci, L., Ajayan, P. M. & Dhiojwala, A. Gecko-inspired carbon nanotube-based self-cleaning adhesives. Nano Lett. 8, 822–825 (2008).
Qu, L. & Dai, L. Gecko-foot-mimetic aligned single-walled carbon nanotube dry adhesives with unique electrical and thermal properties. Adv. Mater. 19, 3844–3849 (2007).
Zhao, Y. et al. Interfacial energy and strength of multiwalled-carbon-nanotube-based dry adhesive. J. Vac. Sci. Technol. B 24, 331–335 (2006).
Kim, S. et al. Microstructured elastomeric surfaces with reversible adhesion and examples of their use in deterministic assembly by transfer printing. Proc. Natl Acad. Sci. USA 107, 17095–17100 (2010).
Bartlett, M. D. et al. Looking beyond fibrillar features to scale gecko-like adhesion. Adv. Mater. 24, 1078–1083 (2012).
Zhang, W., Lin, Y., Qian, J., Chen, W. & Gao, H. Tuning molecular adhesion via material anisotropy. Adv. Funct. Mater. 23, 4729–4738 (2013).
Chakrabarti, S., Gong, K. & Dai, L. Structural evaluation along the nanotube length for super-long vertically aligned double-walled carbon nanotube arrays. J. Phys. Chem. C 112, 8136–8139 (2008).
Lu, X. K., Huang, H., Nemchuk, N. & Ruoff, R. S. Patterning of highly oriented pyrolytic graphite by oxygen plasma etching. Appl. Phys. Lett. 75, 193–195 (1999).
Huang, S. M. & Dai, L. Plasma etching for purification and controlled opening of aligned carbon nanotubes. J. Phys. Chem. 106, 3543–3545 (2002).
Hammond, C. R. in The Elements, in Handbook of Chemistry and Physics 81st ed. 4–98CRC press (2004).
Collins, P. G., Bradley, K., Ishigami, M. & Zettl, A. Extreme oxygen sensitivity of electronic properties of carbon nanotubes. Science 287, 1801–1804 (2000).
Xu, M., Futaba, D. N., Yamada, T., Yumura, M. & Hata, K. Carbon nanotubes with temperature-invariant viscoelasticity from -196 °C to 1000 °C. Science 330, 1364–1368 (2010).
Gent, A. N. & Yeoh, O. H. Failure loads for model adhesive joints subjected to tension, compression or torsion. J. Mater. Sci 17, 1713–1722 (1982).
McKeen, L. W. Fluorinated Coatings and Finishes Handbook: The Definitive User's 35–43William Andrew Inc. (2006).
Mäklin, J. et al. Thermal diffusivity of aligned multi-walled carbon nanotubes measured by the flash method. Phys. Status Solidi B 248, 2508–2511 (2011).
Xu, J. & Fisher, T. S. Enhancement of thermal interface materials with carbon nanotube arrays. Int. J. Heat Mass Transfer 49, 1658–1666 (2006).
Wang, X., Liu, Y., Yu, G., Zhang, J. & Zhu, D. Anisotropic electrical transport properties of aligned carbon nanotube films. J. Phys. Chem. B 105, 9422–9425 (2001).
This work was support by AFOSR (FA9550-12-1-0037) and NSF (CMMI-1400274). This work was jointly supported by the National Thousand Talents Plan of China, the National Natural Science Foundation of China (51402117, 51572095), State Key Laboratory of Materials Processing and Die & Mould Technology, Fundamental Research Funds for the Central Universities, and Shenzhen Basic Research Project (JCYJ20140903171444756).
The authors declare no competing financial interests.
Supplementary Figures 1-18, Supplementary Tables 1-3, Supplementary Discussion and Supplementary References. (PDF 1883 kb)
A carbon nanotube dry adhesive on a rough surface. (WMV 1008 kb)
A demonstration of a carbon nanotube dry adhesive hanging a human on a painted wall. (WMV 606 kb)
About this article
Cite this article
Xu, M., Du, F., Ganguli, S. et al. Carbon nanotube dry adhesives with temperature-enhanced adhesion over a large temperature range. Nat Commun 7, 13450 (2016). https://doi.org/10.1038/ncomms13450
Surface Nanostructure Control with Poly(ethylene glycol) (PEG) Spacer by Templateless Electropolymerization
Journal of Bionic Engineering (2021)
Highly Stretchable Shape Memory Self-Soldering Conductive Tape with Reversible Adhesion Switched by Temperature
Nano-Micro Letters (2021)
Maximizing ion accessibility in MXene-knotted carbon nanotube composite electrodes for high-rate electrochemical energy storage
Nature Communications (2020)
Optimized Bio-inspired Micro-pillar Dry Adhesive and Its Application for an Unmanned Aerial Vehicle Adhering on and Detaching from a Ceiling
Journal of Bionic Engineering (2020)
Applied Physics A (2018)