Formation of planar heterojunction perovskite solar cells exhibiting both high efficiency and stability under continuous operation remains a challenge. Here, we show this can be achieved by using a defective TiO2 thin film as the electron transport layer. TiO2 layers with native defects are deposited by electron beam evaporation in an oxygen-deficient environment. Deep-level hole traps are introduced in the TiO2 layers and contribute to a high photoconductive gain and reduced photocatalytic activity. The high photoconductivity of the TiO2 electron transport layer leads to improved efficiency for the fabricated planar devices. A maximum power conversion efficiency of 19.0% and an average PCE of 17.5% are achieved. In addition, the reduced photocatalytic activity of the TiO2 layer leads to enhanced long-term stability for the planar devices. Under continuous operation near the maximum power point, an efficiency of over 15.4% is demonstrated for 100 h.
Organo-lead halide perovskites show significant potential as candidates for next-generation thin-film photovoltaics, with demonstrated solar cell efficiencies increasing from 3.8% in 2009 to over 20% in 2015 (refs 1, 2). This unprecedented progress is made possible by the outstanding material properties of perovskites, including direct bandgaps suitable for capturing the solar spectrum, long and balanced charge carrier diffusion lengths, and high defect tolerance3,4,5. Despite the ultra-long carrier diffusion lengths in these materials4, progress in the field has been dominated by perovskite solar cells (PSCs) that use mesoscopic TiO2 electron transport layers (ETLs) derived from the dye-sensitized solar cell community. For example, the first PSC with a power conversion efficiency (PCE) above 15% was demonstrated with a mesoscopic device using a sequential deposition process6. More recently, a series of breakthroughs were made by the Seok group using mesoscopic devices through solvent7, composition8 and process engineering2. On the other hand, device simplicity and process compatibility would benefit from eliminating the mesoscopic layer and it has been suggested that all devices may ultimately adopt the simple planar architecture9. Recently, impressive advances in planar heterojunction PSCs have been realized using organic ETLs10. However, the combination of high PCE and long-term stability in these devices remains elusive11. Meanwhile, planar PSCs based on compact TiO2 are still plagued by lower PCEs and larger current–voltage (JV) hysteresis than the mesoscopic embodiments. It has been suggested that the origin of this performance gap is the much higher electron extraction efficiency from mesostructured TiO2 layers9. Therefore, improving the electron extraction efficiency from compact TiO2 layers could provide a path to simultaneously achieving high efficiency and improved stability by overcoming basic performance limitations in planar heterojunction PSCs.
Although compact TiO2 layers are crucial components of planar PSCs, little attention has been paid to understanding and controlling how the characteristics of this material affect device performance. These layers are usually deposited using solution-based processes, such as spin coating and spray pyrolysis, with limited control over their optoelectronic properties. For example, electrical conductivities of compact TiO2 films are known to be one order of magnitude lower than those of commonly used organic hole transport layers (HTLs)12.
In this work, we consider that the TiO2 layer is illuminated during operation of PSCs and show that the photoexcited state properties of compact ETLs play critical roles in defining device performance in terms of efficiency and stability. Both the photoconductivity and photocatalytic activity of TiO2 are greatly affected by deep-level trap states associated with native point defects. Here, we have engineered a defective TiO2 thin film containing such hole trap states and used it as the ETL for planar heterojunction PSCs. Photoconductive measurements show that the defective TiO2 thin film has an internal gain higher than 103 at a small bias of 0.5 V, which is attributed to the minority carrier trapping mechanism in the film. By coupling the highly photoconductive TiO2 ETL with a high-quality perovskite light absorber synthesized using a low-pressure vapour annealing process, a highly efficient planar heterojunction PSC with relatively small hysteresis is achieved. The maximum PCEs under reverse scan, forward scan and steady state are 19.0, 17.1 and 17.6%, respectively. Thus, the performance gap between mesoscopic and planar TiO2-based devices has been significantly narrowed. Moreover, the stability of the planar heterojunction PSC is greatly improved by using defective TiO2 as the ETL. TiO2 is known to be an effective ultraviolet photocatalyst for oxidizing organic materials and the hybrid perovskite can be photocatalytically degraded under ultraviolet illumination, which typically leads to poor stability for the PSCs. The incorporation of hole-trap states in the TiO2 ETL reduces its activity for photocatalytic oxidation. As a result, the stability of fabricated planar heterojunction PSCs is greatly improved and we show, for the first time, steady-state PCE >15% during continuous operation for 100 h. These results demonstrate that engineering defects in the TiO2 ETL is a promising way to improve the efficiency and stability of planar heterojunction PSCs.
Photoconductive properties of defective TiO2
The compact TiO2 thin films used in this work were deposited using electron beam (EB) evaporation with a substrate temperature of 350 °C in an oxygen-deficient environment. We note that this substrate temperature is considerably lower than that required for the formation of mesoscopic TiO2 films. X-ray diffraction confirms that the as-deposited TiO2 thin films are anatase phase (Supplementary Fig. 1). The thin films are characterized by strong absorption in the ultraviolet region and very low absorption in the visible region, as determined by spectroscopic ellipsometry (Fig. 1a). An indirect bandgap of ∼3.3 eV is extracted from the Tauc plot of the absorption spectrum (Fig. 1b), consistent with that of anatase TiO2. The high transmittance in the visible range is important for its application as an ETL, as the perovskite light absorber in the solar cell is illuminated through this layer. Despite low sub-bandgap absorption, temperature-dependent photoluminescence (PL) reveals a broad emission centred at around 600 nm (Fig. 1c). Consistent with prior reports, this defect-related emission from anatase TiO2 is very weak at room temperature, indicating that dominant recombination processes are non-radiative13. However, this weak radiative recombination indicates the presence of deep-level native defects within the material that are related to oxygen vacancies and/or under-coordinated Ti sites. This finding is consistent with composition analysis by X-ray photoelectron spectroscopy (Supplementary Fig. 2), which reveals that the low-temperature EB-deposited TiO2 thin films are slightly (∼2 at%) deficient in oxygen.
The presence of deep-level trap states in the TiO2 thin film could have a significant impact on its photoconductive properties and, thus, on PSC performance. To explore the role of defects on the photoconductivity of the TiO2 thin films, measurements were performed using a photoconductor made by depositing a Ti metal top contact on the TiO2 thin film on a fluorine-doped tin oxide (FTO)/glass substrate, as shown in Fig. 2a. For comparison, the conductivity of a conventional solution-processed TiO2 film was also measured using the same device architecture (Supplementary Fig. 3). The linear current–voltage (JV) curve measured in the dark indicates Ohmic contacts are formed at both FTO/TiO2 and TiO2/Ti interfaces (Fig. 1d). The conductivity of the TiO2 thin film was greatly increased under ultraviolet illumination. At a bias of 0.5 V, an unexpectedly large photocurrent density of ∼1.1 A cm−2 was generated under 365 nm illumination at an irradiance of 3.6 mW cm−2. This value greatly exceeds the light-limited photocurrent density that can be generated; even at an external quantum efficiency (EQE) of 100%, the photocurrent density should not exceed 1.1 mA cm−2 under these conditions. The observation of an exceptionally high photocurrent density, which is not observed for the case of the conventional solution-processed TiO2 film, indicates that there exists a mechanism for internal photoconductive gain in the TiO2 thin film. Indeed, as shown in Fig. 1e, a photoconductive gain of more than 103 is obtained at a bias of 0.5 V. Such high photoconductive gain in TiO2 has been reported for single crystalline nanorods14, but not for polycrystalline thin films. Examination of the temporal evolution of the photoconductivity reveals slow rise and fall times on the order of hours, as shown in Fig. 1f. Such behaviour is characteristic of persistent photoconductivity and, together with the large photoconductive gain, indicates a hole-trapping mechanism in the defective TiO2 thin film that results in photo-induced accumulation of excess majority carriers, as shown schematically in Fig. 2b. These electrons contribute to the improved conductivity before eventually recombining with the trapped holes, with long recombination times due to either atomic-scale reorganization following hole trapping at the defect site or spatial segregation of the two carrier types (for instance, trapping of holes at grain boundaries or surfaces).
Photovoltaic performance of PSCs using defective TiO2 as ETL
Defective TiO2 thin films exhibiting high photoconductive gain were employed as ETLs for the fabrication of planar heterojunction PSCs. Halide perovskite light-absorbing layers were synthesized using a modified low-pressure vapour annealing process (see Methods section)15,16. Briefly, mixed lead iodide (PbI2) and lead bromide (PbBr2) precursor films were annealed in methylammonium iodide (MAI) vapour to produce bromine-doped methylammonium lead iodide perovskites (MAPbI3-xBrx). This method yielded high-quality perovskite thin films with large-area uniformity and excellent optical properties (Supplementary Fig. 4). Although most of the bromine in the precursor film was replaced via exchange with iodine in the MAI vapour, a low concentration of bromine was detected in the synthesized perovskite films (Supplementary Fig. 5). The incorporation of a small amount of bromine was found to greatly enhance the stability of the perovskite in ambient atmosphere (Supplementary Fig. 6), consistent with previous findings from solution-processed MAPbI3-xBrx (ref. 7). In addition, it has been demonstrated that the photovoltaic performance of perovskite-based devices can be greatly improved by low-level bromine incorporation17. Therefore, MAPbI3-xBrx perovskite films are used for the fabrication of efficient planar heterojunction PSCs in the present work.
By coupling highly photoconductive TiO2 ETLs with MAPbI3-xBrx perovskites, we demonstrate planar heterojunction PSCs with efficiencies rivaling those of the best mesoscopic devices. The schematic structure and the cross-sectional scanning electron microscopy image of the fabricated planar heterojunction PSCs are shown in Fig. 3a,b. The device architecture consists of an FTO layer on glass substrate as the bottom transparent electrode, an EB-deposited defective TiO2 layer (∼100 nm) as the ETL, a MAPbI3-xBrx perovskite layer (∼400 nm) as the light absorber, a spin-coated Spiro-OMeTAD (2,2’,7,7’-tetrakis-(N,N-di-p-methoxyphenylamine)9,9’-spirobifluorene) layer (∼200 nm) as the HTL and an EB-deposited gold layer (∼100 nm) as the top electrode. The JV curves in Fig. 4a were obtained after light soaking of one of the highest performing devices. Under reverse scan, the device yielded a short-circuit current density (JSC) of 23.11 mA cm−2, an open-circuit voltage (VOC) of 1.055 V and a fill factor (FF) of 0.78. A maximum PCE of 19.0% is extracted from the JV curve with AM 1.5G illumination at an intensity of 100 mW cm−2. Edge effects were found to be small in the PSCs (Supplementary Fig. 7). The EQE spectrum of the planar PSC is shown in Fig. 4b. The data were collected following 20 min of full spectrum light soaking and the photocurrent at each wavelength was measured at steady state after 30 s illumination, to eliminate the influence of transient photocurrents (Supplementary Fig. 8). High EQE values of ∼90% were observed in the visible range, demonstrating the high electron extraction efficiency enabled by the defective TiO2 ETL. Integration of the EQE spectrum with the AM 1.5G (ASTM G173-03 reference spectrum) photon flux yields a photocurrent density of 22.93 mA cm−2, which agrees to within 1% of the values obtained from the JV curves presented in Fig. 4a.
Although hysteresis is observed for this planar device, it is much smaller than is found in other PSCs based on planar TiO2 (refs 7, 12, 18). Under forward scan, although the JSC was almost unchanged, slightly reduced VOC and FF were observed, leading to a lower PCE of 17.1% at the maximum power point. To determine the steady-state PCE, the device was held at an external bias close to the maximum power point and the current was recorded. As shown in Fig. 4c, a stable photocurrent density of 20.7 mA cm−2 was observed at a bias of 0.85 V, indicating that the steady-state PCE of the device is at least 17.6%. It was confirmed that the steady-state PCE lies between the values extracted from JV curves measured in the reverse and forward scan directions (Supplementary Fig. 9). The stable steady-state photocurrent observed here is also improved relative to the steadily decaying photocurrent observed in previously reported planar devices18. In that work, the photocurrent decay under steady-state operation was ascribed to a reduction of electron extraction efficiency of the planar TiO2 layer18. The stable steady-state photocurrent in our case suggests that the electron extraction efficiency of the TiO2 ETL remained high during operation. The high electron extraction efficiency of the TiO2 ETL is also supported by the fact that the hysteresis is relatively small in our devices. As shown in Fig. 4d,e, the JV curves do not show a strong dependence on the step size or the delay time during testing. Although the reduced hysteresis in mesoscopic PSCs remains a topic of investigation, some reports have ascribed it to the enhanced electron extraction efficiency of the TiO2 layer9. By increasing the conductivity of the planar TiO2 layer, the electron extraction efficiency is also improved, thereby contributing to a reduced hysteresis in the fabricated planar PSCs. The enhanced electron extraction efficiency of the EB-deposited TiO2 thin film compared with the conventional solution-processed TiO2 thin film was further confirmed via PL quenching measurements (Supplementary Fig. 10). The performance of a planar PSC fabricated using solution-processed TiO2 as the ETL is given in Supplementary Fig. 11 for reference.
Table 1 summarizes the photovoltaic performance from 50 planar heterojunction PSCs fabricated using defective TiO2 as the ETL. Corresponding box charts of the data are given in the Supplementary Fig. 12. In the reverse scan direction, the average values of JSC, VOC and FF were 22.5 mA cm−2, 1.05 V and 0.74, respectively, yielding an average PCE of 17.5%. In the forward scan direction, average values of VOC and FF dropped to 1.00 V and 0.70, respectively, leading to a lower average PCE of 15.8%. Hysteresis was evaluated by comparing the PCE values obtained under reverse and forward scan [(PCEreverse−PCEforward)/PCEreverse], which yielded values <10%. Importantly, standard deviation of all photovoltaic performance metrics were small, exhibiting values of <6%. These results indicate that planar heterojunction PSCs fabricated using the defective TiO2 provide high efficiency, low hysteresis and good reproducibility.
Improved electron extraction efficiency by defective TiO2
The large photoconductivity of the defective TiO2 ETL is essential for achieving high efficiency with low hysteresis. For comparison, planar heterojunction PSCs were also fabricated using TiO2 thin films annealed at 500 °C in air as the ETL. The photoconductivity of the EB-deposited TiO2 thin films decreased drastically after annealing (Supplementary Fig. 13). This finding is consistent with increased electron-hole recombination rates in the annealed TiO2 due to reduced concentrations of beneficial long-lived hole-trap states associated with photoconductive gain and persistent photoconductivity. Consequently, the photovoltaic performance of the planar PSCs fabricated using post-annealed TiO2 thin films as ETL was lowered (Supplementary Fig. 14). Compared with PSCs fabricated with as-deposited TiO2, PSCs fabricated with post-annealed TiO2 yielded lower FF (Supplementary Table 1), which is consistent with the increased series resistance due to the decreased photoconductivity of the TiO2 ETL. The larger hysteresis that is observed following annealing is also in agreement with the reduced electron extraction efficiency due to the decreased photoconductivity.
As the conductivity of the TiO2 is mainly affected by ultraviolet illumination (Supplementary Fig. 15), the effect of hole trapping in the TiO2 ETL on the photovoltaic properties of the planar PSCs was investigated by measurement with and without an ultraviolet cutoff (425 nm-long pass) filter. As discussed above and shown in Fig. 1f, under full spectrum illumination, the photocurrent from the TiO2 thin film photoconductor increased and decreased gradually when the light was switched on and off, respectively. Likewise, the photocurrent of the complete PSC increased gradually on illumination with full-spectrum AM 1.5G light, as shown in Fig. 5a. In contrast, no obvious light-soaking process was observed when ultraviolet light was blocked from the illumination (Fig. 5a). Therefore, the effect of light soaking on increasing photocurrent in complete PSCs under full spectrum illumination is attributed to the gradually increased conductivity of the TiO2 ETL in the presence of ultraviolet illumination, which is enabled by incorporation of long-lived deep-level hole trap states. This assignment is also supported by the absence of a significant light-soaking process under AM 1.5G illumination in planar PSCs fabricated using post-annealed TiO2 thin films as the ETL (Supplementary Fig. 16).
The effect of hole trapping and de-trapping on the photocurrent of PSCs was further revealed by repeatedly applying and removing the ultraviolet filter during measurement. As shown in Fig. 5b, the photocurrent of the PSC gradually increased with ultraviolet illumination due to hole trapping and accumulation of unpaired electrons in the TiO2. When the ultraviolet filter was applied, the photocurrent gradually decreased due to recombination of the accumulated electrons with trapped holes. The photocurrent rise and decay with and without ultraviolet illumination can be repeated, because the hole trapping and de-trapping is reversible. These results provide additional support for the finding that the high efficiency achieved in the fabricated planar PSCs is related to the hole trapping in the defective TiO2 thin film.
Improved PSC stability with defective TiO2 ETLs
A significant concern associated with using TiO2 as ETL is that the organic/inorganic hybrid perovskite could be photocatalytically degraded by TiO2 on photoexcitation with the ultraviolet portion of the solar spectrum, leading to poor stability for TiO2-based PSCs19. Several methods have been proposed to overcome this instability, including replacing TiO2 with ultraviolet inactive materials such as C60 and alumina20,21, inserting a buffer layer between TiO2 and perovskite22, and using ultraviolet filters23. However, these methods lead to lower device efficiencies due to reduced electron extraction efficiencies and/or parasitic light absorption. As photogenerated holes in the TiO2 are required to facilitate oxidation of organic materials24, incorporation of deep-level hole traps into defective TiO2 provides opportunity to suppress photocatalytic activity and increase the stability of the TiO2/perovskite interface. We tested the photocatalytic activity of defective TiO2 thin films by photoelectrochemical oxidation of methylamine (CH3NH2) in aqueous solution. As shown in Fig. 6a, the photocurrent of the defective as-deposited TiO2 thin film was much lower than that of the post-annealed sample, which possessed fewer long-lived hole trap states. This decrease in the photocatalytic activity of the defective TiO2 thin film has important implications for stability of functional photovoltaic devices. Indeed, the planar PSC employing as-deposited TiO2 as the ETL shows dramatically enhanced long-term stability. As shown in Fig. 6b, the photocurrent decayed by only about 10% from its maximum value after continuous operation near the maximum power point for 100 h. In contrast, the photocurrent of the PSC fabricated using post-annealed TiO2 decayed by >30% after 100 h. In addition, the planar PSC fabricated using defective TiO2 yielded a maximum PCE of 17.6% and PCEs over 15.4% for the entire 100 h testing period. To the best of our knowledge, this combination of high efficiency (over 15%) with long-term stability has not been demonstrated with either planar or mesoscopic PSCs. The results suggest that employing defective TiO2 with hole traps as the ETL is an effective way to enhance the stability of the planar PSCs while maintaining, and even promoting, the high efficiency of the device.
We find that incorporation of deep-level hole traps in EB-deposited TiO2 thin films leads to an unexpectedly large photoconductive gain under ultraviolet illumination. The highly photoconductive TiO2 thin film was employed as the ETL for a planar heterojunction PSC. The large photoconductivity of this layer improves electron extraction efficiency in planar PSC devices, increases the PCE and reduces JV hysteresis. In addition, the hole traps in the TiO2 thin film reduce its ultraviolet photocatalytic activity for degradation of the hybrid perovskite. As a consequence, the long-term stability of planar PSCs is significantly improved and yields PCEs >15.4% for at least 100 h, for the first time. Furthermore, the beneficial effects of defect incorporation are achieved with a maximum temperature of 350 °C, which is significantly lower than is normally required for processing of mesoscopic TiO2 ETLs. Our results demonstrate an effective way to not only enhance the efficiency but also improve the stability of planar heterojunction PSCs by engineering defects in TiO2 ETLs.
TiO2 thin film deposition
Compact TiO2 thin films (100 nm) were deposited on fluorine-doped tin oxide-coated glass (FTO/glass), quartz or silicon substrates by EB evaporation (Angstrom Engineering, NEXDEP). Before deposition, the chamber was evacuated to a base pressure of ∼2 × 10−6 Torr and the substrate was heated to 350 °C. TiO2 pieces (Kurt J. Lesker, 99.9% purity) were used as the source for evaporation. The deposition was conducted under an acceleration voltage of 7 kV and the current was adjusted to reach a deposition rate of about 0.5 Å s−1. Following deposition, the substrates were allowed to cool overnight in vacuum. Post-annealing of the TiO2 thin film was carried out in air at 500 °C for 2 h using a tube furnace. Solution-processed TiO2 compact layers were deposited by spin coating a mildly acidic solution of titanium isopropoxide in ethanol (350 μl in 5 ml ethanol with 0.013 M HCl) at 2,000 r.p.m. and annealing in air at 500 °C for 30 min.
Solar cell fabrication
Substrates for solar cell fabrication consisted of compact TiO2 ETLs, deposited on FTO/glass, as described above. A mixture of 0.8 M PbI2 (Alfa Aesar, 99.9985%) and 0.2 M PbBr2 (Sigma-Aldrich, 99.999%) was dissolved in N,N-dimethylformamide (Sigma-Aldrich, 99.9%) and filtered with a 0.2 μm syringe filter. Mixed PbI2/PbBr2 films were deposited by spin coating in air at 1,500 r.p.m. for 3 min and dried on a hot plate at 110 °C for 15 min. Samples were then transferred to test tubes charged with 0.1 g of MAI. The tube was evacuated with a rotary pump and heated with a silicone oil bath. The mixed PbI2/PbBr2 film was annealed in MAI vapour at 120 °C for 2 h under a pressure of ∼0.4 Torr, to form MAPbI3-xBrx. The perovskite films were then washed with isopropyl alcohol (Sigma-Aldrich, 99.5%) and the HTL was applied immediately afterwards. The precursor solution for the HTL was prepared by dissolving 80 mg spiro-OMeTAD (Lumtec, 99.5%), 28.5 μl 4-tert-butylpyridine (Sigma-Aldrich, 96%) and 17.5 μl lithium-bis(trifluoromethanesulfonyl)imide (Sigma-Aldrich, 99.95%) solution (520 mg lithium-bis(trifluoromethanesulfonyl)imide in 1 ml acetonitrile) in 1 ml chlorobenzene (Sigma-Aldrich, 99.8%). The HTL was deposited by spin coating at 3,000 r.p.m. for 30 s in air. Samples were then stored in a desiccator overnight. A 100-nm-thick Au layer was then deposited on top of the HTL through a metal shadow mask by EB evaporation at a base pressure of about 2 × 10−6 Torr and a deposition rate of about 2 Å s−1. The active area for all solar cells was 0.16 cm2.
X-ray diffraction spectra were measured with a Rigaku SmartLab X-ray diffractometer using Cu Kα radiation at 40 kV and 40 mA. Spectroscopic ellipsometry data were collected on a J.A. Woollam Co. M-2000 ellipsometer with extended NIR range. Data fitting was performed with CompleteEASE software to extract the absorption spectrum. Scanning electron microscopy images of the samples were acquired using a FEI QUANTA FEG 250. Ultraviolet–vis spectra of the perovskite films were measured with a Shimadzu SolidSpec-3700 spectrometer. PL spectra of TiO2 thin films were recorded using an Andor spectrometer equipped with 600 lines per mm grating with 500 nm blaze under 350 nm excitation using a Coherent OPerA Solo optical parametric amplifier pumped with a Coherent Libra amplified Ti:S system. Photoconductivity data from TiO2 thin films were collected using a potentiostat (BioLogic SP-200) and an ultraviolet lamp (365 nm, 3.6 mW cm−2) in N2 atmosphere. JV curves and steady-state photocurrent data of the solar cells were measured in air using a solar simulator (Newport, 91192) equipped with a 150 W Xe lamp and an AM 1.5G filter as light source and a Keithley 2400 source meter. The light intensity was calibrated with an NREL-calibrated Si solar cell with a KG-5 filter to 1 sun (100 mW cm−2). The EQE spectrum was measured at zero bias under continuous illumination by monochromatic light obtained using a 300 W Xenon lamp and a monochromator. The incident beam was focused within the active area of the device. Long-term stability of solar cells was measured under 100 mW cm−2 simulated sunlight (Solar Light 16S-300-005) in N2 atmosphere. The spectrum of the solar simulator used for long-term stability testing and the light-induced temperature increase during stability testing are shown in Supplementary Fig. 17. Photoelectrochemical properties of TiO2 thin films were measured with a three-electrode configuration using a Ag/AgCl reference electrode and a Pt wire counter electrode. An aqueous solution of 1 wt.% methylamine was used as the electrolyte. JV curves were measured under chopped simulated sunlight (Solar Light 16S-300-005) and anodic scan at a rate of 10 mV s−1.
The authors declare that all data that support the findings of this study are available within an associated file in the Supplementary Data of this article.
How to cite this article: Li, Y. et al. Defective TiO2 with high photoconductive gain for efficient and stable planar heterojunction perovskite solar cells. Nat. Commun. 7:12446 doi: 10.1038/ncomms12446 (2016).
Kojima, A., Teshima, K., Shirai, Y. & Miyasaka, T. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 131, 6050–6051 (2009).
Yang, W. S. et al. High-performance photovoltaic perovskite layers fabricated through intramolecular exchange. Science 348, 1234–1237 (2015).
Green, M. A., Ho-Baillie, A. & Snaith, H. J. The emergence of perovskite solar cells. Nat. Photonics 8, 506–514 (2014).
Xing, G. et al. Long-range balanced electron- and hole-transport lengths in organic-inorganic CH3NH3PbI3 . Science 342, 344–347 (2013).
Gao, P., Gratzel, M. & Nazeeruddin, M. K. Organohalide lead perovskites for photovoltaic applications. Energy Environ. Sci. 7, 2448–2463 (2014).
Burschka, J. et al. Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 499, 316–319 (2013).
Jeon, N. J. et al. Solvent engineering for high-performance inorganic–organic hybrid perovskite solar cells. Nat. Mater. 13, 897–903 (2014).
Jeon, N. J. et al. Compositional engineering of perovskite materials for high-performance solar cells. Nature 517, 476–480 (2015).
Gratzel, M. The light and shade of perovskite solar cells. Nat. Mater. 13, 838–842 (2014).
Shao, Y., Yuan, Y. & Huang, J. Correlation of energy disorder and open-circuit voltage in hybrid perovskite solar cells. Nat. Energy 1, 15001 (2016).
Kim, H., Lim, K.-G. & Lee, T.-W. Planar heterojunction organometal halide perovskite solar cells: roles of interfacial layers. Energy Environ. Sci. 9, 12–30 (2016).
Zhou, H. et al. Interface engineering of highly efficient perovskite solar cells. Science 345, 542–546 (2014).
Knorr, F. J., Mercado, C. C. & McHale, J. L. Trap-state distributions and carrier transport in pure and mixed-phase TiO2: influence of contacting solvent and interphasial electron transfer. J. Phys. Chem. C 112, 12786–12794 (2008).
Chen, R.-S., Liu, Y.-L., Chan, C.-H. & Huang, Y.-S. Photoconductivities in anatase TiO2 nanorods. Appl. Phys. Lett. 105, 153107 (2014).
Li, Y. et al. Fabrication of planar heterojunction perovskite solar cells by controlled low-pressure vapor annealing. J. Phys. Chem. Lett. 6, 493–499 (2015).
Sutter-Fella, C. M. et al. High photoluminescence quantum yield in band gap tunable bromide containing mixed halide perovskites. Nano Lett. 16, 800–806 (2016).
Ibrahim Dar, M. et al. Understanding the impact of bromide on the photovoltaic performance of CH3NH3PbI3 solar cells. Adv. Mater. 27, 7221–7228 (2015).
Unger, E. L. et al. Hysteresis and transient behavior in current-voltage measurements of hybrid-perovskite absorber solar cells. Energy Environ. Sci. 7, 3690–3698 (2014).
Leijtens, T. et al. Stability of metal halide perovskite solar cells. Adv. Energy Mater. 5, 1500963 (2015).
Wojciechowski, K. et al. C60 as an efficient n-type compact layer in perovskite solar cells. J. Phys. Chem. Lett. 6, 2399–2405 (2015).
Leijtens, T. et al. Overcoming ultraviolet light instability of sensitized TiO2 with meso-superstructured organometal tri-halide perovskite solar cells. Nat. Commun. 4, 2885 (2013).
Ito, S., Tanaka, S., Manabe, K. & Nishino, H. Effects of surface blocking layer of sb2s3 on nanocrystalline TiO2 for CH3NH3PbI3 perovskite solar cells. J. Phys. Chem. C 118, 16995–17000 (2014).
Chander, N. et al. Reduced ultraviolet light induced degradation and enhanced light harvesting using YVO4:Eu3+ down-shifting nano-phosphor layer in organometal halide perovskite solar cells. Appl. Phys. Lett. 105, 033904 (2014).
Chen, Q. et al. Under the spotlight: The organic–inorganic hybrid halide perovskite for optoelectronic applications. Nano Today 10, 355–396 (2015).
This study is based on work performed by the Joint Center for Artificial Photosynthesis, a DOE Energy Innovation Hub, supported through the Office of Science of the U.S. Department of Energy under Award Number DE-SC0004993. Perovskites PL and PL mapping measurements were supported by the Electronic Materials programme, funded by the Director, Office of Science, Office of Basic Energy Sciences, Materials Sciences and Engineering Division of the U.S. Department of Energy under Contract Number DE-AC02-05CH11231. Photovoltaic characterization was performed at the Molecular Foundry, which is supported by the U.S. Department of Energy (DOE), Office of Basic Energy Sciences, Scientific User Facilities Division, under Contract Number DE-AC02-05CH11231. C.M.S.-F. acknowledges financial support from the Swiss National Science Foundation (P2EZP2_155586).
The authors declare no competing financial interests.
About this article
Cite this article
Li, Y., Cooper, J., Liu, W. et al. Defective TiO2 with high photoconductive gain for efficient and stable planar heterojunction perovskite solar cells. Nat Commun 7, 12446 (2016). https://doi.org/10.1038/ncomms12446
Density of states characterization of TiO2 films deposited by pulsed laser deposition for heterojunction solar cells
Nano Research (2021)
Introducing an Organic Hole Transporting Material as a Bilayer to Improve the Efficiency and Stability of Perovskite Solar Cells
Macromolecular Research (2021)
Photo-stable perovskite solar cells with reduced interfacial recombination losses using a CeOx interlayer
Science China Materials (2021)
A low-temperature TiO2/SnO2 electron transport layer for high-performance planar perovskite solar cells
Science China Materials (2020)
Journal of Nanoparticle Research (2019)