The need for sustainable catalysts for an efficient hydrogen evolution reaction is of significant interest for modern society. Inspired by comparable structural properties of [FeNi]-hydrogenase, here we present the natural ore pentlandite (Fe4.5Ni4.5S8) as a direct ‘rock’ electrode material for hydrogen evolution under acidic conditions with an overpotential of 280 mV at 10 mA cm−2. Furthermore, it reaches a value as low as 190 mV after 96 h of electrolysis due to surface sulfur depletion, which may change the electronic structure of the catalytically active nickel–iron centres. The ‘rock’ material shows an unexpected catalytic activity with comparable overpotential and Tafel slope to some well-developed metallic or nanostructured catalysts. Notably, the ‘rock’ material offers high current densities (≤650 mA cm−2) without any loss in activity for approximately 170 h. The superior hydrogen evolution performance of pentlandites as ‘rock’ electrode labels this ore as a promising electrocatalyst for future hydrogen-based economy.
The increasing global need of energy marks the finding of alternative and storable energy sources an important enterprise. In this view, hydrogen is of particular interest since it combines the possibility to efficiently ‘store’ energy, possesses the highest-energy density of common fuels and reveals a sustainable combustion process1. Currently, platinum and its alloys play a dominant role in the H2 evolution reaction (HER) and allow production of H2 at low overpotentials with fast reaction rates and high current densities in acidic electrolytes2. The actual price and low natural abundance, however, render platinum a dinosaur in a future sustainable ‘hydrogen economy’. Among the numerous suggested non-noble metal HER catalysts, nanostructured transition metal dichalcogenides are promising candidates for this reaction3,4,5,6. The establishment of MS2-based HER electrocatalysts, however, with satisfactory stability and activity yet remains elusive. Likewise, nanostructured transition metal chalcogenides, for example, NiSe2 nanofibres7, MoS2/CoSe2 hybrid catalysts8, Ni3S2 nanosheets9 and FeS2 nanostructures10, induced a high HER activity in such materials. An improved performance has been observed when these materials were anchored to graphene5,11,12,13,14,15, Ni/NiO (ref. 16) or gold surfaces17. This observation also reveals a significant problem of non-noble metals—their intrinsically low electrical conductivity compared with noble metal HER electrocatalysts. Recently, ultrathin metallic FeNi sulfide nanosheets with unknown composition showed significantly improved HER activity18. This material was operated as a HER electrocatalyst with a low overpotential (117 mV) at current densities of ∼10 mA cm−2 for 200 h without any loss in activity. Although this material is very effective, the need for specific surface shapes and the concomitant synthetic procedures required render those materials non-economical.
Contrary to such systems, nature utilizes highly efficient machineries to generate H2. Enzymes such as the [FeNi]- as well as the [FeFe]-hydrogenase comprising Ni- and Fe-sulfide containing active sites are well known for their capability to reduce protons to H2 (ref. 19). Notably, electrons are provided to the bimetallic active sites by closely neighbored [4Fe4S] clusters. The property to combine a highly conductive backbone with a well-defined bimetallic catalytic center rather than well-defined nanoparticles, therefore, seems to be a key towards a sustainable and endurable HER catalyst. A material that combines all of those properties is the ore pentlandite, which has the composition Ni4.5Fe4.5S8. Pentlandites show high electronic conductivity and possess Fe- and Ni-centres bridged by sulfur (Fig. 1a)20,21. The special assembly of iron, nickel and sulfur, comprising short intermetallic distances (2.51 Å) closely resembles structural features of both the active site of the [FeNi]-hydrogenase (dNiFe=2.573 Å)22 and [FeFe]-hydrogenase (dFeFe=2.566 Å)23. A striking advantage is that these minerals are a main source for the production of nickel24. Thus, they can be hauled from natural deposits at low cost and used without major processing if sufficiently pure.
Herein, we report on the application of pentlandite as electrocatalyst for the HER. We show that this material can be used as ‘rock’-electrodes without the need of further surface modifications and they provide high activity and stability at low overpotential for the generation of hydrogen. With the help of density functional theory calculations, we show a plausible pathway for the formation of H2 on the catalyst surface.
Synthesis and characterization
The natural pentlandite ore contains considerable amounts of silicates in the structure. Thus, for better comparison we synthesized Ni4.5Fe4.5S8 from the elements by means of solid-state synthesis at 1,100 °C for 10 h (ref. 24). Powder X-ray diffraction and X-ray photoemission spectroscopic (XPS) measurements were performed to analyse the quality and composition of both materials. Whereas the natural pentlandite showed several reflections besides the main pentlandite phase, the synthetic Ni4.5Fe4.5S8 revealed high purity20 without the commonly observed monosulfide solid solution phases (Fig. 2a)25. Likewise, Mössbauer spectroscopy confirmed the presence of similar iron sites in both materials (Fig. 2b). The synthetic material reveals two distinct different iron sites with isomeric shifts of 0.13 (±0.02) and 0.50 (±0.02) mm s−1 as well as quadrupole couplings of 0.12 (±0.02) and 0.13 (±0.02), respectively. This observation is in good agreement with literature reports and structural findings showing two different iron sites26.
The chemical composition of the natural ore is obviously different from the synthetic material. Energy dispersive X-ray spectroscopy (EDX) analysis confirmed the different overall surface composition of both materials (Supplementary Figs 1 and 2). Whereas synthetic pentlandites showed an ideal iron to nickel to sulfur ratio of 1:1:2.25, the natural mineral revealed only negligible small amounts of nickel and contained a significant amount of silicates (Supplementary Figs 1 and 3). This phase is also visible in scanning electron micrographs (SEMs) and is absent in synthetic Ni4.5Fe4.5S8 (Fig. 2c,d). Notably, no appreciable periodical surface features were observed in either case. XPS spectra show that both Fe and Ni in the surface appear severely oxidized in pristine samples (Supplementary Figs 4 and 5; Supplementary Note 1), reflecting the presence of metal oxide species. Peaks at 706.5 and 852.7 eV can be attributed to metallic states that are in good agreement with values reported for NiS2 (ref. 27) and FeS2 (ref. 28) compounds. The results display the oxidation states of iron and nickel in the synthetic material to be 0 as well as III with the relative ratios provided in Supplementary Table 1. The metallic character of pentlandite as well as the close structural resemblance with the hydrogenases’ active sites inspired us to apply the pentlandite ‘rock’ material as an electrode material for the HER reaction without further surface modification.
Electrochemical hydrogen evolution
Electrodes for HER were subsequently prepared from the bulk materials by directly connecting the solid materials with a copper wire surrounded by a Teflon tube using epoxide glue (Supplementary Fig. 6).
Electrochemical HER measurements of as-prepared ‘rock electrodes’ were performed using a three-electrode cell containing 0.5 M sulfuric acid as electrolyte. Ag/AgCl (3 M KCl) and a platinum wire were utilized as reference and counter electrode, respectively. Figure 3a shows the linear sweep voltammograms obtained at a scan rate of 5 mV s−1 in argon-saturated solution.
Initial experiments on the natural pentlandite ore exhibited HER activity at an overpotential of ∼500 mV and low current density (≤10 mA cm−2). This poor HER activity of natural pentlandite ‘rock’ is most likely attributed to the low conductivity of the material due to the presence of large amounts of Si- and Mg-containing phases incorporated into the ore. In contrast to natural pentlandites, synthetic pentlandite ‘rock’ electrodes with a defined Ni4.5Fe4.5S8 composition revealed a substantially improved electrocatalytic activity at low overpotentials of ∼280 mV at a current density of 10 mA cm−2. In fact, compared with NiS2, FeS2 and MoS2 nanomaterials applied as reference materials within this study, synthetic pentlandite ‘rock’ electrodes reveal a superior performance as evidenced from the voltammograms (Fig. 3a; Supplementary Table 2). The essentially higher HER activity of the synthetic pentlandite may be attributed to a larger number of exposed active sites. We hence determined the electrochemical surface area (ECSA) of NiS2, FeS2, MoS2, the natural and the synthetic pentlandite from the electrochemical double-layer capacitance (Cdl) of the catalysts using cyclic voltammetry (Fig. 3b; Supplementary Fig. 7). The linear slope of the capacitive current as a function of scan rate (Fig. 3c) is equivalent to twice of the double-layer capacitance and represented as ECSA18. Notably, the ECSA of the synthetic pentlandite is significantly larger than that of the other materials tested and suggests an increased HER activity of the synthetic pentlandite with a large number of exposed surface sites (Supplementary Fig. 8).
The influence of surface structure
We subsequently focused on the synthetic pentlandites as an idealized mineral. Whereas effective non-noble metal-based HER catalysts require nanostructured particles mounted on a conductive electrode9,18 pentlandites do not require any artificial nanostructuring or grafting to achieve high HER activities at low overpotentials. In contrast to bulk materials, the high surface area of a nanoscaled material is considered to have an impact on the interaction with the surrounding electrolyte and the observed improved catalytic activity. Therefore, understanding the interactions occurring at electrode/electrolyte interfaces at the atomic level is considered to be of utmost importance for the design of effective electrocatalysts. The mere fact that the herein reported pentlandites reveal such high HER activity at low potentials indicates that besides a high surface area commonly arising from nanostructuring additional factors need to be addressed. Notably, neither measurement with exfoliated nor ball-milled nanosized pentlandite samples revealed any improved electrocatalytic behaviour (Supplementary Figs 9 and 10).
HER reaction kinetics
Elementary reaction steps on the electrode surface are a key factor to understand the materials’ performance. To understand such steps involved in the HER kinetics, we analysed the Tafel plots (η=ρ log j+log j0, overpotential η, current density j, Tafel slope ρ and exchange current density j0) that allow for an initial mechanistic hypothesis (Fig. 3d). In general, HER mechanisms can involve the following three steps29
For Pt nanopowder the Tafel slope is ∼29 mV dec−1, which is close to the theoretical value (b=2.3 RT/2F) and can be assigned to a HER mechanism including Volmer and Tafel steps. The recombination step (equation (3)) was shown to be the rate-limiting step at low overpotentials, where the chemisorption of hydrogen by the metal is not favoured. For MoS2 nanosheets, a Tafel slope of 95 mV dec−1 gives rise to a Volmer- and Heyrovsky-based mechanism with electrochemical desorption of hydrogen as the rate-limiting step. In contrast to MoS2 nanosheets, the synthetic Ni4.5Fe4.5S8 ‘rocks’ exhibit a Tafel slope of 72 mV dec−1. Tafel slopes of 60–70 mV dec−1 can be assigned to a fast Volmer-type discharge reaction (equation (1)), followed by a rate-limiting recombination step (equation (3)), where the chemisorption of hydrogen from aqueous solutions at the electrode surface only requires small activation energy. In the rate-determining process, the adsorbed H atoms migrate over the electrode surface to interact with other adsorbed H atoms to form molecular hydrogen29.
We assumed the resistance of the electrocatalyst to be responsible for the surprisingly high activity of the synthetic pentlandite. We therefore performed electrochemical impedance spectroscopy to characterize the interfacial electrode kinetics and resistance of the material. Figure 4a shows the Nyquist plots of natural (black curve) and Ni4.5Fe4.5S8 pentlandite rocks (red curve) at an applied overpotential of 300 mV versus reversible hydrogen electrode (RHE). The impedance data were fitted to an equivalent circuit (Fig. 4a), employing a constant phase element to determine the charge-transfer resistance Rct. The electrochemical impedance spectroscopy data reveal a significantly lower charge-transfer resistance (Rct, 57.2 Ω) of the Ni4.5Fe4.5S8 bulk electrode as compared with the natural pentlandite (1.05 kΩ), MoS2 nanosheets (412.4 Ω), NiS2 (213.2 Ω) as well as FeS2 (374.6 Ω) nanoparticles (Supplementary Fig. 11), revealing a faster electron transfer and a higher Faradaic efficiency during HER. We believe that the high HER activity stems from synergetic effects between the bi-transition metals and sulfur sites resulting in a high conductivity as well as the ‘right’ surface assembly of the catalytic sites. This is consistent with XPS data from sputtered pentlandite, revealing a higher metallic character on ‘cleaning’ of the electrode surface.
Although Ni4.5Fe4.5S8 reveals an excellent performance as a noble metal-free electrocatalyst, long-time durability under different conditions at high current densities is an important demand for its potential application. Hence, the long-term stability of the Ni4.5Fe4.5S8 electrode was investigated by electrochemical cycling in 0.5 M H2SO4 in a potential range between −0.4 and 0.4 V versus RHE for 1,000 cycles at 50 mV s−1. No appreciable change in the catalytic performance after 1,000 cycles was observed indicating excellent electrochemical stability of the Ni4.5Fe4.5S8 electrode (Fig. 4b). In addition, constant-potential electrolysis supported this finding and revealed HER at a current density of 10 mA cm−2 for at least 60 h in 0.5 M H2SO4 as shown in the inset of Fig. 4b.
Durability and activation studies
To determine the Faradaic efficiency and to study the long-term stability at higher current densities, we performed HER experiments at Ni4.5Fe4.5S8 ‘rocks’ for 170 h (Fig. 4c) at a constant overpotential of 0.6 V. The increase in the H2 gas concentration was quantitatively monitored by gas chromatography with a thermal conductivity detector (GC-TCD) during the first 4 h giving rise to 2.14 mmol h−1 cm−2 of H2 (inset of Fig. 4c) produced during electrolysis at Ni4.5Fe4.5S8 ‘rocks’. This amount of H2 is surprising and comparable to that of Pt-based electrolysers that were shown to afford 11 mmol h−1 cm−2 at a constant potential of −1.2 V (versus RHE) with a Faradaic efficiency of 94% (ref. 30). Similar values for non-noble metal HER catalysts were never observed for any ‘rock’-like bulk compound before. Whereas chronoamperometric experiments at a current density of 10 mA cm−2 revealed a constant potential over time, the performed electrolysis at 0.6 V overpotential versus RHE showed an unexpected phenomenon (Fig. 4c). Notably, with time, the current density increases and a constant current was only observed after ∼48 h. This indicates that the electrode surface can be activated under reductive conditions at more negative potentials leading concomitantly to higher HER activity. This activation could, in principle, further lead to a downshift of the onset potential for the HER reaction and is evidenced from the linear sweep voltammograms (Fig. 4d; Supplementary Fig. 12). Subsequently, H2 formation occurs with overpotentials of only ∼190 mV at 10 mA cm2 current density. A likely explanation for this phenomenon is the depletion of surface sulfur from the material. However, Pt oxidation and subsequent deposition at the working electrode was reported to show a similar behaviour31. To clarify this hypothesis, we performed analogous electrochemical experiments applying a glassy carbon counter electrode (Supplementary Note 2). Similar to our observations with the Pt counter electrode, a decrease of the overpotential for HER (Supplementary Fig. 13) as well as an increase of activity was observed. This observation clearly confirms that the activation is not a result from a deposition of Pt on the working electrode and more likely stems from depletion of surface sulfur from the catalyst, thus, affording more exposed nickel–iron surface sites21. During the activation process, the surface structure and overall composition of the electrode remained unaltered (Supplementary Figs 14 and 15). We therefore investigated S 2p core-level XPS spectra of the electrode before and after electrolysis (Fig. 4e; Supplementary Fig. 16). Contrary to pentlandite electrodes before electrolysis, the activated sample solely showed sulfur 2p doublets at the lower binding energies of 161.3 and 162.5 eV attributable to the S2− ion (Fig. 4e) and the amount of disulfide-type sulfur (S22−) was significantly decreased resulting in sulfur vacancies on the catalyst surface32. Such a behaviour inevitably promotes the reactivity of the exposed Ni–Fe sites and thus the HER performance. Along this line, treatment with additional sulfides thus can be expected to reverse the activation of the electrode. We hence investigated the activated electrodes in H2S saturated 0.5 M H2SO4 solutions for HER (Fig. 4f). The onset potential shifts by 30 mV to more negative potentials suggesting occupation of S vacancies and further supporting the reversible activation by S depletion.
Hydrogen quantification and alternative proton sources
In addition, the Faradaic efficiency (η) of the Ni4.5Fe4.5S8 ‘rock’ electrode was determined for the first 4 h to be 91±5% confirming the high activity of the electrode material to efficiently catalyse the HER reaction in 0.5 M H2SO4. Next, we investigated the influence of the pH value on the turnover frequency from the slope of the Clark electrode signal during the first hour of the catalytic HER at different pH values and normalized to the amount of H2 quantified by gas chromatography measurements (Supplementary Fig. 17). Notably, the high activity is not restricted to sulfuric acid solutions. Different tests with strong acids such as HCl, HNO3, HBr, as well as H3PO4 revealed H2 evolution at comparable overpotentials and current densities. Likewise, acetic acid as well as citric acid were tested as potential proton sources and allowed for moderate H2 generation, which is expected due to their lower pKa value and the subsequent lower ionic strength (Supplementary Fig. 18).
Commonly noble metal catalysts are severely poisoned by sulfur-containing species present in waste acidic materials33. We hence simulated sulfur-poisoning conditions by performing proton reduction in H2S atmosphere. The presence of H2S did not affect the catalytic H2 evolution notably. We noticed that although revealing a smaller activity, H2S can be directly utilized as a proton source for H2 evolution. It is only limited by its low solubility (∼0.2 M in H2O) and acidity (pKa=7; Supplementary Fig. 19).
To gain some insight into the roles of Ni, Fe and S in promoting the HER activity theoretical investigations on Ni4.5Fe4.5S8 were performed. Since full-scale modelling of a Ni4.5Fe4.5S8 surface is computationally extremely time demanding, a zeroth-order model was considered in a cluster approach with main structural features extracted from the bulk and saturated by protons and water molecules.
The crystal structure of pentlandites can be best described as a M8S6 cuboctahedra interconnected by tetrahedrally bound sulfur and additional in-plane metal atoms (Supplementary Note 3). The exposure of the M8S6 cuboctahedra surface results in significant structural changes of this unit (Supplementary Fig. 20), large distortions of the metal framework with a motif that is highly flexible and sensitive to protonation as well as change of charge/spin state (Supplementary Table 3). The relevant structures during the H2 formation are shown in Fig. 5. For the potential hydrogen formation, optimizations of systems protonated at different water molecules bound to the metals were performed (Supplementary Fig. 21). In all cases, the proton was transferred from the hydronium ion to a metal atom leading to a hydride between a nickel and an iron atom (Fig. 5a). For the case with the largest negative charge on the hydrogen, a reaction path for the hydrogen formation was determined by a series of constrained geometry optimizations, using the shortest H–H distance as a reaction coordinate (Supplementary Fig. 22). During this process, another proton that was originally bonded to a sulfur atom is pulled towards the hydride (Fig. 5b) and leads to the formation of H2 as an exothermic process (ΔE=−6.4 kcal mol−1; Fig. 5c). Sulfur vacancies created during electrolysis may change the electronic structure of the catalytically active Ni–Fe centres and thus facilitate the HER process. These results for the model system corroborate the potential of pentlandite to electrocatalyse the HER process with a mechanism strikingly similar to the biological [FeNi]-hydrogenase34.
We have successfully synthesized pentlandites with a composition of Fe4.5Ni4.5S8, exhibiting superior activity and stability for the HER. Notably, whereas exhaustive nanoparticle and electrode preparation is commonly required, the high conductivity of Fe4.5Ni4.5S8 allows for a direct application as ‘rock’ electrode without any additional artificial surface structuring. The prepared non-noble metal electrodes reveal a high endurance in corrosive solutions such as sulfuric acid at an overpotential of 280 mV at 10 mA cm−2, but reaches lower values as low as 190 mV after 96 h of electrolysis due to sulfur depletion from the surface creates sulfur vacancies. Most likely this depletion changes the electronic structure of the catalytically active Ni–Fe centres facilitating the HER process. The HER activity of the pentlandite ‘rock’ electrodes reveal comparable overpotential and Tafel slope in comparison with some of well-developed metallic catalysts. Notably, these electrodes even allow H2 evolution under catalyst poisoning conditions. In addition, the electrodes can be operated at current densities as high as 650 mA cm−1 for 170 h without loss in activity. Altogether, the natural ore pentlandite is a highly abundant, cheap, robust and highly efficient electrocatalyst for the HER reaction that will allow for a significant boost of non-noble metal catalysts.
Synthesis of pentlandite
Natural pentlandite from Intsilä, Finland, was obtained from the mineral and ‘rock’ collection of the Department of Geology, Mineralogy and Geophysics at the Ruhr-University in Bochum. The synthesis of Fe4.5Ni4.5S8 was performed from the elements. The high-purity elements iron (1.67 g, 29.8 mmol), nickel (1.75 g, 29.8 mmol) and sulfur (1.70 g, 53.1 mmol) were ground until a homogeneous mixture was obtained. This mixture was placed in a 10 mm silica tube. Subsequently, the silica tube was sealed under a static vacuum and was heated to 700 °C with 5 °C min−1. After 3 h of annealing at 700 °C, the temperature was raised to 1,100 °C within 30 min. After 10 h at 1,100 °C, the mixture was allowed to cool down to room temperature.
SEM images and EDX analysis were performed using a Quanta 3D FEG scanning electron microscope (FEI) operated at 20 kV for imaging and at 4.4 kV for EDX analysis. X-ray diffraction measurements were recorded using a Bruker AXS Advance powder diffractometer (40 kV, 50 mA, sealed Cu-Kα X-ray tube) equipped with a graphite monochromator. The diffraction pattern was collected in the continuous scan mode at a scan rate of 0.03° per 5 s.
Zero-field Mössbauer spectra were recorded at 298.15 K using a SeeCo constant acceleration spectrometer equipped with a temperature controller maintaining temperatures within ±0.1 K and a 57Co radiation source in a Rh matrix. Isomer shifts are referred to α-Fe metal at room temperature. Data were fit with a sum of Lorentzian quadrupole doublets using a least-squares routine with WMOSS program.
XPS measurements were carried out in an ultrahigh vacuum set-up equipped with a monochromatic Al Kα X-ray source (hν=1486.6 eV), operated at 14.5 kV and 35 mA, and a high-resolution Gammadata-Scienta SES 2002 analyser. The base pressure in the measurement chamber was maintained at ∼5 × 10−10 mbar. The measurements were carried out in the fixed transmission mode with a pass energy of 200 eV, resulting in an overall energy resolution of 0.25 eV. A flood gun was applied to compensate the charging effects. High-resolution spectra for C 1s, O 1s, S 2p, and Fe 2p and Ni 2p photoelectron lines were recorded. The C 1s signal of the adventitious carbon was an external standard attributed to 284.5 eV binding energy. The Casa XPS software with a pseudo-Voigt Gaussian-Lorentzian product (oxide species) or asymmetric LA (metallic states) functions and Shirley background subtraction was used for peak deconvolution. Atomic ratios were calculated from XPS intensities corrected to corresponding Scofield photoemission cross-sections. Measurements were carried out on pristine synthetic pentlandite and after sputtering for 30 and 60 min. Sputtering was carried out in a preparation chamber with Ar+ accelerated to 2.5 keV using SPECS IQE 11/35 ion source.
Exfoliation of bulk Ni4.5Fe4.5S8 crystals
Bulk-layered Ni4.5Fe4.5S8 crystals were exfoliated by dispersing 5 mg ml−1 of the crystals in cetyltrimethylammonium bromide (CTAB) surfactant solution (2 mg ml−1), in water followed by sonication for 10 h in a 100 W tip sonicator. After sonication, the dispersions were subjected to differential centrifugation to narrow down the size distribution. In a typical method, the dispersions were centrifuged at 1,000 r.p.m. for 1 h, and the supernatant was separated and subjected to successive centrifugation at 4,000 and 6,000 r.p.m. for periods of 2 h. The process was terminated at this stage (at 6,000 r.p.m.); the final sediment was collected and redispersed in water under sonication and used for further investigations.
Ball milling of bulk Ni4.5Fe4.5S8
The planetary ball mill (Fritsch Pulverisette 7, classic line) with a SiC milling containers (diameter: 2.5 cm, volume: 13 cm3) and four SiC milling balls (diameter: 1 cm) was used to milled the bulk material. In a typical milling process, ∼1 g of bulk Ni4.5Fe4.5S8 was milled for duration of 10 min at a speed rate of 650 r.p.m.
Synthesis of MoS2 nanosheets
Bulk MoS2 crystals were synthesized by chemical vapour transport method. In a typical synthesis, elemental powders of Mo and S were mixed in stoichiometric proportions (1:1) and inserted into a quartz tube. The quartz tube was evacuated to ∼10−6 mbar and sealed. The sealed quartz tube was placed in a tube furnace at 800 °C for 2 weeks to ensure the crystal formation. The quartz tube was cooled down to room temperature and opened for collecting the formed crystals (Supplementary Fig. 23).
Liquid exfoliation of MoS2 sheets
Bulk-layered MoS2 crystals were exfoliated by dispersing 5 mg ml−1 of the crystals in CTAB surfactant solution (2 mg ml−1), in water followed by a sonication for 10 h in a 100 W bath sonicator. After sonication, the dispersions were subjected to differential centrifugation to narrow down the size distribution. In a typical method, the dispersions were centrifuged at 1,000 r.p.m. for 1 h, and the supernatant was separated and subjected to successive centrifugation at 2,000 and 4,000 r.p.m. for periods of 2 h. The process was terminated at this stage (at 4,000 r.p.m.); the sediment was collected and redispersed in water under sonication. After sonication the dispersion was stable for 3 months without any flocculation and used for further investigations (Supplementary Fig. 24).
Synthesis of NiS2 nanoparticles
NiS2 nanosheets were synthesized by a one-step hydrothermal method. In a typical method, 4 mmol of nickel chloride hexahydrate (NiCl2·6H2O) and 4 mmol of Na2S2O3·5H2O were mixed in a beaker containing 30 ml of milliQ water and stirred for 1 h. The mixed solution was transferred to a 60 ml Teflon-lined stainless steel autoclave and heated for 24 h at 180 °C. The precipitate was collected by centrifugation and repeatedly washed with ethanol and water (1:2) mixture, and then dried (Supplementary Fig. 25).
Synthesis of FeS2 nanoparticles
FeS2 nanosheets were synthesized by a step hydrothermal method. In a typical method, 4 mmol of ferric chloride tetrahydrate (FeCl2·4H2O) and 4 mmol of Na2S2O3·5H2O were mixed in a beaker containing 30 ml of milliQ water and stirred for 1 h. The mixed solution was transferred to a 60 ml Teflon-lined stainless steel autoclave and heated for 24 h at 180 °C. The precipitate was collected by centrifugation and repeatedly washed with ethanol and water (1:2) mixture, and then dried (Supplementary Fig. 26).
Synthetic or natural pentlandite ‘rocks’ were cut into blocks of ∼0.5 × 0.5 × 0.5 cm and placed in a crimp that was soldered to a copper cable. Subsequently, the assembly was housed in a Teflon tube, insulating the copper wire from solution. The tip of the prepared electrode was then covered with epoxide glue, dried and polished to reveal solely a pure pentlandite surface as potential electrode. The polished electrode was then directly used in the electrochemical measurements (Supplementary Fig. 6). The geometric area of the prepared electrode was 0.135 cm2.
Electrochemical testing of the catalyst was conducted using a standard three-electrode set-up using a GAMRY Reference 600 Potentiostat or an Autolab potentiostat/galvanostat (PGSTAT12). The catalyst materials were directly used in bulk as the working electrode. Ag/AgCl (saturated KCl) or Ag/AgCl (3 M KCl) and a Pt grid were used as reference and counter electrode, respectively. If not otherwise stated, 0.5 M H2SO4 was used as the electrolyte and the measured potential was converted to the RHE potential according to ERHE=EAg/AgCl+X+0.059 pH (X=+0.197 V) (saturated KCl) or 0.210 V (3 M KCl).
Before each measurement, the cell was electrochemically washed by cycling at least five times in the potential window −0.4 V<EAg/AgCl<0.4 V at a scan rate of 100 mV s−1 until a stable cyclic voltammogram was obtained. Linear sweep voltammetry was then performed at a scan rate of 5 mV s−1. Long-term durability measurements were done using controlled potential coulometry at ERHE=−0.6 V monitoring the transferred charge and the current. Chronopotentiometric measurements (galvanostatic electrolysis) were performed at a current density of 10 mA cm−2 for 60 h. Electrochemical impedance spectroscopy was recorded in the frequency range from 50 kHz to 1 Hz at the corresponding open-circuit potential and HER overpotential of the electrode using an ac perturbation of 10 mVpp. The resistance of the solution was determined from the resulting Nyquist plot. All measurements were carried out at room temperature.
Gas samples were directly taken from the headspace of the electrochemical cell after a specific time interval and injected into a Shimadzu GC-2010 gas chromatograph. The data were then evaluated using a calibration curve for the correlation between the peak area and the hydrogen amount.
Electrochemical measurements of powder or nanosized samples
All electrochemical measurements were performed using an Autolab potentiostat/galvanostat (PGSTAT12, Eco Chemie) in a conventional three-electrode cell in combination with a speed control unit (CTV101) and a rotating disk electrode rotator (EDI101; Radiometer). A disc-shaped glassy carbon electrode of geometric area 0.126 cm2 modified with the catalysts was used as working electrode, a Ag/AgCl/3 M KCl as reference electrode and a platinum mesh as counter electrode. The reference electrode was calibrated with respect to the RHE. before the experiments, the glassy carbon electrode was polished on a polishing cloth using different alumina pastes (3.0–0.05 μm) to obtain a mirror-like surface followed by ultrasonic cleaning in water. For electrochemical measurements, the catalyst ink was prepared by dispersing 5.0 mg ml−1 of the catalyst in water followed by ultra-sonication for 30 min. A volume of 5.0 μl of the catalyst suspension was drop coated onto the polished glassy carbon electrode and dried in air at room temperature. Before the HER measurements, modified electrodes were subjected to continuous potential cycling in the potential window of −0.5 to 0.5 V versus Ag/AgCl/3 M KCl, until reproducible voltammograms were obtained.
Determination of the Faradaic efficiency
The Faradaic efficiency was determined according to equation (4)
with n number of transferred electrons, F is Faradaic constant, [H2] is detected concentration of hydrogen, I is current and t is time.
All quantum-chemical calculations were performed within the framework of density functional theory, employing the Perdew, Burke and Ernzerhof (PBE0) hybrid functional35,36,37 together with Ahlrichs’ double-zeta split valence all electron basis sets38. Further details on the computational methods are given in the Supplementary Information (Supplementary Note 4).
The authors declare that the data supporting the findings of this study are available within the article and its Supplementary Information files, and from the authors on reasonable request.
How to cite this article: Konkena, B. et al. Pentlandite rocks as sustainable and stable efficient electrocatalysts for hydrogen generation. Nat. Commun. 7:12269 doi: 10.1038/ncomms12269 (2016).
May, M. M., Lewerenz, H.-J., Lackner, D., Dimroth, F. & Hannappel, T. Efficient direct solar-to-hydrogen conversion by in situ interface transformation of a tandem structure. Nat. Commun. 6, 8286 (2015).
Sheng, W. et al. Correlating hydrogen oxidation and evolution activity on platinum at different pH with measured hydrogen binding energy. Nat. Commun. 6, 5848 (2015).
Merki, D. & Hu, X. Recent developments of molybdenum and tungsten sulfides as hydrogen evolution catalysts. Energy Env. Sci. 4, 3878–3888 (2011).
Kibsgaard, J., Chen, Z., Reinecke, B. N. & Jaramillo, T. F. Engineering the surface structure of MoS2 to preferentially expose active edge sites for electrocatalysis. Nat. Mater. 11, 963–969 (2012).
Kong, D., Cha, J. J., Wang, H., Lee, H. R. & Cui, Y. First-row transition metal dichalcogenide catalysts for hydrogen evolution reaction. Energy Env. Sci. 6, 3553–3558 (2013).
Voiry, D. et al. Enhanced catalytic activity in strained chemically exfoliated WS2 nanosheets for hydrogen evolution. Nat. Mater. 12, 850–855 (2013).
Gao, M.-R. et al. Mixed-solution synthesis of sea urchin-like NiSe nanofiber assemblies as economical Pt-free catalysts for electrochemical H2 production. J. Mater. Chem. 22, 13662–13668 (2012).
Gao, M.-R. et al. An efficient molybdenum disulfide/cobalt diselenide hybrid catalyst for electrochemical hydrogen generation. Nat. Commun. 6, 5982 (2015).
Feng, L.-L. et al. High-index faceted Ni3S2 nanosheet arrays as highly active and ultrastable electrocatalysts for water splitting. J. Am. Chem. Soc. 137, 14023–14026 (2015).
Jasion, D. et al. Low-Dimensional Hyperthin FeS2 Nanostructures for Efficient and Stable Hydrogen Evolution Electrocatalysis. ACS Catal. 5, 6653–6657 (2015).
Li, Y. et al. MoS2 Nanoparticles Grown on Graphene: An Advanced Catalyst for the Hydrogen Evolution Reaction. J. Am. Chem. Soc. 133, 7296–7299 (2011).
Yang, J. et al. Two-dimensional hybrid nanosheets of tungsten disulfide and reduced graphene oxide as catalysts for enhanced hydrogen evolution. Angew. Chem. Int. Ed. 52, 13751–13754 (2013).
Chen, D. et al. Graphene-like layered metal dichalcogenide/graphene composites: synthesis and applications in energy storage and conversion. Mater. Today 17, 184–193 (2014).
Liu, Z., Li, N., Zhao, H. & Du, Y. Colloidally synthesized MoSe2/graphene hybrid nanostructures as efficient electrocatalysts for hydrogen evolution. J. Mater. Chem. A 3, 19706–19710 (2015).
Wang, Y. et al. Freestanding 3D graphene/cobalt sulfide composites for supercapacitors and hydrogen evolution reaction. RSC Adv. 5, 6886–6891 (2015).
Xu, Y.-F., Gao, M.-R., Zheng, Y.-R., Jiang, J. & Yu, S.-H. Nickel/nickel(II) oxide nanoparticles anchored onto cobalt(IV) diselenide nanobelts for the electrochemical production of hydrogen. Angew. Chem. Int. Ed. 52, 8546–8550 (2013).
Wang, T. et al. Enhanced electrocatalytic activity for hydrogen evolution reaction from self-assembled monodispersed molybdenum sulfide nanoparticles on an Au electrode. Energy Env. Sci. 6, 625–633 (2013).
Long, X. et al. Metallic iron–nickel sulfide ultrathin nanosheets as a highly active electrocatalyst for hydrogen evolution reaction in acidic media. J. Am. Chem. Soc. 137, 11900–11903 (2015).
Kylie, A. V., Alison, P. & Armstrong, F. A. Investigating and exploiting the electrocatalytic properties of hydrogenases. Chem. Rev. 107, 4366–4413 (2007).
Pearson, A. D. & Buerger, M. J. Confirmation of the crystalstructure of pentlandite. Am. Mineral. 41, 804–805 (1956).
Thornber, M. R. Mineralogical and electrochemical stability of the nickel-iron sulphides—pentlandite and violarite. J. Appl. Electrochem. 13, 253–267 (1983).
Ogata, H., Nishikawa, K. & Lubitz, W. Hydrogens detected by subatomic resolution protein crystallography in a [NiFe] hydrogenase. Nature 520, 571–574 (2015).
Nicolet, Y., Piras, C., Legrand, P., Hatchikian, C. E. & Fontecilla-Camps, J. C. Desulfovibrio desulfuricans iron hydrogenase: the structure shows unusual coordination to an active site Fe binuclear center. Structure 7, 13–23 (1999).
Xia, F., Pring, A. & Brugger, J. Understanding the mechanism and kinetics of pentlandite oxidation in extractive pyrometallurgy of nickel. Miner. Eng. 27–28, 11–19 (2012).
Drebushchak, V. A., Kravchenko, T. A. & Pavlyuchenko, V. S. Synthesis of pure pentlandite in bulk. J. Cryst. Growth 193, 728–731 (1998).
Knop, O., Huang, C.-H., Reid, K. I. G., Carlow, J. S. & Woodhams, F. W. D Chalkogenides of the transition elements. X. X-ray, neutron, Mössbauer, and magnetic studies of pentlandite and the π phases π(Fe, Co, Ni, S), Co8MS8, and Fe4Ni4MS8 (M = Ru, Rh, Pd). J. Solid State Chem. 16, 97–116 (1976).
Shalvoy, R. B. & Reucroft, P. J. Characterization of a sulfur‐resistant methanation catalyst by XPS. J. Vac. Sci. Technol. 16, 567–569 (1979).
Binder, H. Die Anwendung der Röntgenphotoelektronenspektroskopie zur Klärung von Bindungsfragen in Eisen-Schwefelverbindungen. Z. Naturforsch. 28 b, 255–262 (1973).
Thomas, J. G. N. Kinetics of electrolytic hydrogen evolution and the adsorption of hydrogen by metals. Trans. Faraday Soc. 57, 1603–1611 (1961).
Siracusano, S. et al. An electrochemical study of a PEM stack for water electrolysis. 10th Int. Conf. Clean Energy 2010 37, 1939–1946 (2012).
Dong, G. et al. Insight into the electrochemical activation of carbon-based cathodes for hydrogen evolution reaction. J. Mater. Chem. A 3, 13080–13086 (2015).
Smart, R. S. C., Skinner, W. M. & Gerson, A. R. XPS of sulphide mineral surfaces: metal-deficient, polysulphides, defects and elemental sulphur. Surf. Interface Anal. 28, 101–105 (1999).
Jayaraj, P., Karthika, P., Rajalakshmi, N. & Dhathathreyan, K. S. Mitigation studies of sulfur contaminated electrodes for PEMFC. Int. J. Hydrogen Energy 39, 12045–12051 (2014).
Lubitz, W., Ogata, H., Rüdiger, O. & Reijerse, E. Hydrogenases. Chem. Rev. 114, 4081–4148 (2014).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 78, 1396 (1997).
Adamo, C. & Barone, V. Toward reliable density functional methods without adjustable parameters: The PBE0 model. J. Chem. Phys. 110, 6158–6170 (1999).
Schäfer, A., Horn, H. & Ahlrichs, R. Fully optimized contracted Gaussian basis sets for atoms Li to Kr. J. Chem. Phys. 97, 2571–2577 (1992).
We thank Sandra Schmidt for SEM images. Financial support by the Deutsche Forschungsgemeinschaft (DFG) in the framework of the Cluster of Excellence Resolv (EXC1069) is gratefully acknowledged. U.-P.A. is grateful for the financial support by the Fonds of the Chemical Industry (Liebig grant to U.-P.A.) and the Deutsche Forschungsgemeinschaft (Emmy Noether grant to U.-P.A., AP242/2-1).
The authors declare no competing financial interests.
About this article
Cite this article
Konkena, B., junge Puring, K., Sinev, I. et al. Pentlandite rocks as sustainable and stable efficient electrocatalysts for hydrogen generation. Nat Commun 7, 12269 (2016). https://doi.org/10.1038/ncomms12269
This article is cited by
Advanced Composites and Hybrid Materials (2021)
Nature Communications (2019)
The Birthplace of Proto-Life: Role of Secondary Minerals in Forming Metallo-Proteins through Water-Rock Interaction of Hadean Rocks
Origins of Life and Evolution of Biospheres (2018)
Nature Communications (2017)
Enhanced electrocatalytic activity of Co@N-doped carbon nanotubes by ultrasmall defect-rich TiO2 nanoparticles for hydrogen evolution reaction
Nano Research (2017)