Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Extended carrier lifetimes and diffusion in hybrid perovskites revealed by Hall effect and photoconductivity measurements


Impressive performance of hybrid perovskite solar cells reported in recent years still awaits a comprehensive understanding of its microscopic origins. In this work, the intrinsic Hall mobility and photocarrier recombination coefficient are directly measured in these materials in steady-state transport studies. The results show that electron-hole recombination and carrier trapping rates in hybrid perovskites are very low. The bimolecular recombination coefficient (10−11 to 10−10 cm3 s−1) is found to be on par with that in the best direct-band inorganic semiconductors, even though the intrinsic Hall mobility in hybrid perovskites is considerably lower (up to 60 cm2 V−1 s−1). Measured here, steady-state carrier lifetimes (of up to 3 ms) and diffusion lengths (as long as 650 μm) are significantly longer than those in high-purity crystalline inorganic semiconductors. We suggest that these experimental findings are consistent with the polaronic nature of charge carriers, resulting from an interaction of charges with methylammonium dipoles.


Hybrid (organic–inorganic) perovskite solar cells represent the recent breakthrough in photovoltaic applications with reported power conversion efficiencies reaching 20% (refs 1, 2, 3). In addition to the abundance of the applied studies on this topic, there is a great interest in understanding the fundamental transport and photophysical properties of these materials, the picture of which is not firmly established yet, thereby calling for more reliable experimental studies. For instance, a possibility of high charge-carrier mobility has been considered as one important factor that contributes to the excellent photovoltaic performance of hybrid lead-halide perovskites. Yet, an unambiguous determination of the intrinsic mobility in these materials is missing. Existing experimental values in similar materials range from 0.6 to 50 cm2 V−1 s−1 (refs 4, 5, 6). However, most of the important transport and photophysical parameters, including the carrier mobilities, lifetimes and recombination rates, were so far determined either in materials different from those relevant for high-performance solar cells (for instance, in metallic tin-halide instead of insulating lead-halide perovskites, or perovskites that adopt 2D layered rather than 3D cubic structure) or obtained indirectly, under the conditions less relevant to applications (for instance, in ultrafast spectroscopic experiments, rather than steady-state transport measurements).

Here, we report artefact-corrected Hall effect and steady-state photoconductivity measurements carried out in a range of thin films and single crystals of exemplary hybrid perovskites, CH3NH3PbI3 and CH3NH3PbBr3, of current interest for photovoltaic applications. Hall effect allows us to directly and independently address the density of photogenerated carriers, nHall, and the intrinsic carrier mobility, μHall, without assumptions typical for other methods, such as in ultrafast spectroscopic techniques or space-charge-limited current measurements. We find that, in a wide range of illumination intensities, the dynamics of photocarriers is governed by bimolecular electron-hole (e-h) recombination with a very small recombination coefficient γ in the range of 10−11 to 10−10 cm3 s−1, which is comparable to the values observed in the best single-crystalline direct-band inorganic semiconductors, such as GaAs, even though the measured intrinsic Hall mobilities are moderate (μHall of up to 60 cm2 V−1 s−1 in perovskite single crystals) and smaller than μ in typical inorganic semiconductors by 1–3 orders of magnitude. In addition, the carrier lifetime, τ, and diffusion length, l, directly measured in our steady-state transport experiments are found to be remarkably long (τ is up to 30 μs and l is up to 23 μm in polycrystalline films, and up to 3 ms and 650 μm in single crystals, respectively). Our experiment thus provides a direct steady-state measurement quantitatively revealing a low-rate photocarrier recombination and negligible trapping, as well as extremely long carrier lifetimes and diffusion lengths in hybrid perovskites. While in agreement with some of the recent theoretical predictions7,8,9,10, these results accentuate important questions as of the physical origins of the found intrinsic carrier mobility, e-h recombination and trapping rates in these materials synthesized via inexpensive vapour- or solution-based routes at temperatures close to room temperature. We propose rationalization of some of our findings based on the picture of re-organization of the methylammonium dipoles around the charge carriers. This interaction leads to carrier relaxation into polarons, whose properties differ from the bare band carriers11,12,13.


a.c. Hall effect measurements of charge-carrier mobility

It should be emphasized that unambiguous determination of the intrinsic (that is, not dominated by traps) charge-carrier mobility requires precise Hall effect measurements, which are quite challenging in highly resistive materials with relatively low μ, such as organic semiconductors or the hybrid perovskites studied here (see, for example, ref. 14). The major challenges are associated with a very high resistivity of pure stoichiometric perovskites (greater than GΩ), related to the negligible (in the dark) density of charge carriers, and a poor signal-to-noise ratio in conventional d.c. Hall measurements of low-μ materials. To overcome these difficulties, here, we have developed a specialized highly sensitive a.c. Hall measurement technique, corrected for the Faraday-induction artefacts, in which a low-frequency a.c. magnetic field, B, is applied perpendicular to the sample’s surface, while a d.c. current, I, is passed through the sample, and an a.c. Hall voltage, VHall, is detected across the channel by a phase-sensitive lock-in technique, which allows to markedly increase the signal-to-noise ratio15. A parasitic Faraday-induction electro-motive force, occurring in a.c. Hall measurements at the same frequency as VHall, is usually comparable to the actual Hall voltage signal and can easily compromise these measurements. Therefore, Faraday-induction-corrected a.c. Hall measurements, as implemented here in perovskites, are absolutely necessary to obtain reliable data (see the ‘Methods’ section, Supplementary Fig. 1 and Supplementary Note 1)15. Pure CH3NH3PbI3 samples are highly resistive in the dark (typical R100 GΩ), and thus we utilize a steady-state monochromatic photo-excitation (λ=465 nm) to generate a population of carriers and be able to measure Hall effect. In CH3NH3PbBr3 single crystals, we were able to measure a Hall effect in the dark as well, because these crystals are weakly conducting in the dark (at a level of 50 MΩ). We perform all our measurements in a 4-probe/Hall bar geometry to account for contact-resistance effects and ensure that channel conductivity, σ, as well as the Hall mobility and carrier density, μHall and nHall, are determined correctly.

Steady-state photoconductivity vs. light intensity

Three types of hybrid perovskite samples were used in our study (Fig. 1). (a) Semi amorphous, solution-grown thin films, (b) polycrystalline, vapour-grown thin films and (c) highly ordered, solution-grown single crystals. The microscopy and X-ray diffraction clearly show that the vapour-processed films have a much better crystallinity than the solution-processed ones, and our single crystals have excellent quality (see Fig. 1 and see the ‘Methods’ section for details).

Figure 1: Morphological and structural characterization of hybrid perovskites used in this study.
figure 1

(a,b) Helium-ion microscope images of CH3NH3PbI3 thin films grown by solution and vapour methods, respectively (see the ‘Methods’ section). Vapour-grown films clearly show much higher crystallinity. (c) Optical photograph of solution-grown CH3NH3PbBr3 single crystals. (d) A reconstructed precession image of the hk0 level from single-crystal X-ray diffraction of these single crystals, showing perfect cubic crystalline structure with low density of defects. (e) Typical powder X-ray diffraction curves of all three types of samples shown in ac, semi amorphous film (black), polycrystalline film (green) and single crystals (red). The arrow indicates the peak corresponding to unreacted PbI2 precursor, and vertical dashed lines show the (110) and (220) peaks of the fully stoichiometric CH3NH3PbI3.

We have found that all our high-quality (stoichiometric) samples exhibit a very low dark conductivity. Nevertheless, a significant photoconductivity is observed in all of them. Figure 2 shows typical dependences of a steady-state photoconductivity, σPC, on photo-excitation density, G, which always follows a power law, σPCGα, with the exponent α=1 or ½ (linear or square-root regimes). Photo-excitation density, G, is defined as the incident photon flux F (in cm−2 s−1) divided by the absorption length of the material.

Figure 2: Steady-state photoconductivity measured as a function of photo-excitation density in thin films and single crystals of hybrid perovskites.
figure 2

Measurements are carried out by 4-probe technique under a cw photo-excitation with a blue light (λ=465 nm) in CH3NH3PbBr3 single crystals (red squares), vapour-grown polycrystalline CH3NH3PbI3 films (green triangles) and solution-grown semi amorphous CH3NH3PbI3 films (black circles). Dashed lines are the power law fits, σPCGα, with the exponents α=1 or ½ (as indicated). It is clear that bimolecular e–h recombination (α=½) dominates the behaviour at high photo-excitation densities (note the double-log scale).

The observed σPC(G) dependence can be understood in terms of charge-carrier monomolecular decay (trapping in the linear regime) or bimolecular decay (e-h recombination in the square-root regime). The photocarrier density, n (nnenh), in steady-state measurements is found from the following rate equation, with dn/dt=0 at dynamic equilibrium (see, for example,16):

Here, κG is the rate of carrier generation via photon absorption resulting in production of free electrons and holes with probability κ per photon (the photocarrier-generation efficiency). The second and third terms represent the two channels of carrier decay: the trapping and e-h recombination, where τtr is the trap-limited carrier lifetime (an average time carriers diffuse before being trapped), and γ is the coefficient of e-h recombination. In the carrier density range probed here, we do not see any experimental evidence of the third-order (Auger) processes, which are therefore excluded from equation (1). At low photo-excitation intensities, when the concentration of electrons and holes is small, the dominant process limiting the carrier lifetime is trapping, and γn2 term in equation (1) can be neglected, leading to a linear regime in photoconductivity: σPCeμn=eμκτtrG, where e is the elementary charge. With increasing excitation intensity, the bimolecular recombination eventually becomes dominant, resulting in a transition from the linear to a sublinear regime: σPC=·(κ/γ)1/2·G1/2, obtained from equation (1) by neglecting the n/τtr term. Figure 2 shows that these two regimes are indeed what is observed in hybrid perovskites. Highly crystalline samples exhibit bimolecular recombination regime (α=1/2) in a wider range of excitation intensities, which is consistent with the higher σPC and μHall in the crystal samples (see below).

Hall measurements under photo-excitation and in the dark

To decouple the carrier density and mobility in σPC=enμ and obtain the microscopic parameters describing the carrier dynamics, τtr and γ, from the rate equation for n (equation (1)) and experimental data, one needs to know the intrinsic charge-carrier mobility μ. For this purpose, we have performed Hall effect measurements, as discussed above, using 4-probe/Hall-bar device structures (Fig. 3a) and a variant of an a.c. Hall measurement technique (Fig. 3b) specifically adjusted for these materials (see the ‘Methods’ section, Supplementary Fig. 1 and Supplementary Note 1). A typical measurement result is shown in Fig. 3c: a very clear and quiet a.c. Hall signal as detected in a solution-grown CH3NH3PbI3 thin film that has a Hall mobility of only μHall=1.5 cm2 V−1 s−1. Reliable Hall measurements with such an excellent signal-to-noise ratio in highly resistive systems with carrier mobilities as low as 1 cm2 V−1 s−1 are unprecedented. For comparison, conventional d.c. Hall measurements performed in a perovskite single crystal with a much higher mobility, μHall=11 cm2 V−1 s−1, shown in Fig. 3d, evidently exhibit a much noisier signal. It is clear that Faraday-induction-corrected a.c. Hall measurements are by far superior to the conventional d.c. technique in terms of the signal-to-noise ratio, even though it uses a smaller magnetic field (r.m.s. B=0.23 T).

Figure 3: Hall effect measurements in hybrid lead-halide perovskites.
figure 3

(a) A photo of typical solution-grown CH3NH3PbI3 thin film on glass with Au contacts in a 4-probe/Hall bar geometry. (b) A diagram of the a.c. Hall effect measurement setup (see description in text and ref. 15). (c) A representative Faraday-induction-corrected a.c. Hall measurement in a solution-grown CH3NH3PbI3 thin film shown in a. When a d.c. excitation current of 4 nA is driven through the film uniformly illuminated with a blue light (λ=465 nm) and subjected to an a.c. B field of r.m.s. magnitude 0.23 T at 0.5 Hz, an a.c. Hall voltage of 100 μV is detected above the zero-bias background by using a lock-in technique shown in b. The vertical and horizontal dashed lines show the moment d.c. excitation current is turned on (at t=28 min) and the two levels of the Hall voltage, at I=0 and 4 nA, respectively. Note that even though Hall mobility of this sample is only μHall=1.5 cm2 V−1 s−1, the signal-to-noise ratio is excellent (the standard deviation in VHall among consecutive six measurements is only about 0.5%). (d) A representative d.c. Hall measurement in CH3NH3PbBr3 single crystals. VHall is measured with an electrometer at a constant excitation current I=200 nA, while B field is slowly swept between −0.5 T and 0.5 T. Despite the much higher mobility of this sample (μHall=11±3 cm2 V−1 s−1), the signal-to-noise ratio is much worse, with the large error imposed by the noise.

As expected for pure undoped band insulators, our CH3NH3PbI3 samples are highly resistive in the dark (with a typical sample resistance >100 GΩ). Thus, we used a cw photo-excitation to generate photocarriers and perform steady-state photo a.c. Hall measurements. In a system with photogenerated electrons and holes (nenhn) and a negligible concentration of dark carriers, Hall voltage is given by:

where W and L are the channel's width and length, respectively, VL is the longitudinal voltage drop along the channel (corrected for contact effects by using the 4-probe technique), and μh, μe are the mobilities of holes and electrons, respectively. Equation (2) shows that photo Hall effect measurements yield the difference between the electron and hole mobilities, rather than their absolute values. In the context of the perovskites under study, recent calculations showed that μe and μh in these materials should differ from each other by an amount comparable to the mobilities themselves7,17,18,19,20. Indeed, theoretical calculations have consistently indicated that while effective masses of electrons, me, and holes, mh, have the same order of magnitude, there is also a noticeable difference between the two, ranging from 20 to 200%, depending on the specific computational method used18. A recent THz spectroscopy study also suggests a difference of a factor of 2 between the electron and hole mobilities21.

Therefore, even though precise values of μe and μh cannot be obtained from photo Hall measurements, the difference, Δμμhμeμ, extracted from equation (2) would yield a faithful representation. In turn, the carrier density obtained from the photo Hall effect measurements is: n=ne+nh=σPC/(e·μ), which is also a good approximation for the actual density of photogenerated charges. The data presented below are analysed using this association. The dark Hall effect measurements possible in weakly conducting single-crystal CH3NH3PbBr3 samples give further credence to the approach.

Figure 4 presents Hall effect data for a variety of hybrid perovskite samples. Fig. 4a shows that Hall mobility, μHall=8±0.4 cm2 V−1 s−1, measured in a polycrystalline CH3NH3PbI3 film remains almost constant over the range of nearly three orders of magnitude in light intensity (the error is defined by the fluctuations in Fig. 4a). The 4-probe photoconductivity, σPC, and the density of photogenerated charge carriers, nHall, determined from the simultaneous longitudinal σPC and Hall effect measurements in these polycrystalline films are plotted in Fig. 4b. Within the entire measurement range, the carrier density dependence on the illumination intensity exhibits α=½ power law: nHallG1/2. We emphasize that independent measurements of μHall as a function of photo-excitation density are essential for obtaining nHall(G) dependence and therefore for determination of the microscopic transport parameters, τtr and γ, by using equation (1) to fit the data. With the density of photogenerated carriers determined experimentally, we can now interpret their dynamics with the help of equation (1). As pointed out above, under a steady-state photo-excitation, equation (1) gives n=(κ/γ)1/2·G1/2 in the regime governed by a bimolecular recombination, that is, when the carrier trapping time τtr well exceeds the time of e-h recombination τr, τtr>>τr≡(γn)−1. Fitting the experimental Hall carrier density in Fig. 4b with this n(G) relationship yields the upper bound for the bimolecular e-h recombination coefficient γ in polycrystalline perovskite films, γ≤3 × 10−11 cm3 s−1 (for the photocarrier-generation efficiency κ≤100%).

Figure 4: Steady-state photoconductivity and Hall effect measurements in perovskite films and crystals.
figure 4

(a) μHall in a vapour-grown 100 nm-thick polycrystalline CH3NH3PbI3 film (similar to that shown in Fig. 1b), measured at different photo-excitation densities, is nearly a constant (the dashed line indicates an average value of≈8 cm2 V−1 s−1). (b) Photoconductivity and Hall carrier density measured in this film as a function of absorbed photon density. (c) nHall(G) in six thin-film samples with very different morphologies and μHall values, showing that bimolecular recombination (nHallG1/2) governs all these samples. Hall mobility and the method of fabrication are indicated for each film in the legend. (d) Photoconductivity and Hall carrier density measured in a macroscopic, bulky CH3NH3PbBr3 single crystal (as the ones shown in Fig. 1c) with a (dark) Hall mobility μHall≈60 cm2 V−1 s−1 (for holes). Dashed lines in bd are the power law fits with exponent α=½: n or σ=constant·G1/2.

The measurements shown in Fig. 4 can also be used to directly estimate the steady-state charge-carrier lifetime, either τtr or τr, and diffusion length, l. Indeed, since bimolecular recombination (α=½) apparently dominates in the entire range of photon densities in Fig. 4b, we must have the condition n/τtr<<γn2 (or, τtr>>τr≡(γn)−1) fulfilled for all the incident photon intensities, including the lowest one, at which nHall=9 × 1014 cm−3 (Fig. 4b). Therefore, the effective trap-limited carrier lifetime τtr in the disordered polycrystalline film in Fig. 4b must be longer than the lifetime limited by bimolecular e-h recombination, τtr>τr≈30 μs. This estimate shows that even in disordered CH3NH3PbI3 thin films, charge carriers have an extremely long lifetime, as far as trapping is concerned, and thus the effective density of the corresponding deep traps must be very low, or the traps must be electronically passivated. The corresponding lower bound of trap-limited carrier diffusion lengths in these polycrystalline perovskite films is: l=(tr)1/223 μm. Here, we needed the Hall mobility again to calculate the diffusion coefficient, DμHallkBT/e, where kB is the Boltzmann constant and T=300 K. Note that negligible trapping and a very long diffusion length, greater than the grain size in our polycrystalline films (Fig. 1b), are consistent with the recent theoretical studies predicting the presence of only shallow traps and benign grain boundaries that do not trap carriers in perovskites9,10. Of course, given the dominant e-h recombination, the actual carrier lifetime in the α=½ regime is a decreasing function of photo-excitation density G: τr=(γn)−1 (see also16).

Figure 4c shows nHall and μHall in six different solution and vapour-grown polycrystalline thin films. In general, vapour-grown samples have an appreciably higher μHall, consistent with their better crystallinity. In sharp contrast, nHall(G) does not seem to correlate much with the preparation method and mobility. Indeed, while μHall differs among the six samples by as much as a factor of 20, nHall varies only within a factor of two. Correspondingly, γ values are also very similar for all these samples, γ(1–5) × 10−11 cm3 s−1. This suggests that while film morphology has a clear effect on charge transport, it has little effect on photocarrier generation and recombination. This is consistent with the notion that bimolecular recombination in this system is not governed by carrier diffusion, therefore we do not see a strong correlation between the recombination dynamics and charge-carrier mobility.

Finally, we have performed Hall measurements in CH3NH3PbBr3 single crystals (Fig. 4d). One important difference in this case is that these crystals are weakly conducting in the dark, which allows us to perform Hall effect measurements in the dark and obtain the mobility of holes (μHall=60±5 cm2 V−1 s−1), without having an ambiguity of charge compensation as in photo Hall measurements. Photoconductivity in these crystals is much higher than that in thin films and also exhibits a well-defined α=½ behaviour (Fig. 4d). A similar analysis of nHall(G) dependence shows that the e-h recombination coefficient in these crystals is γ8 × 10−11 cm3 s−1 (for more details on the extraction procedure see Supplementary Note 2). By defining the effective recombination-limited carrier lifetime again as τr=(γn)−1 and using the experimental carrier density from Hall effect measurements, we can determine the carrier lifetime and diffusion length in these single crystals. At the lowest incident photo-excitation flux in Fig. 4d, corresponding to the measured projected carrier density nHall=3 × 1011 cm−2 and the effective bulk carrier density n4.6 × 1012 cm−3 (Supplementary Note 2), we find: τr2.7 ms, and l≡(r)1/2650 μm, which are remarkably long for a solution-grown semiconductor. We emphasize that these values represent the lower limit for the trap-limited carrier lifetime, τtr, and diffusion length, ltr, since the condition τtr>>τr must be satisfied in the entire regime dominated by a bimolecular recombination, thus indicating again that trapping is strongly suppressed in these materials. We must add that σPC(G) in analogous lead iodide (CH3NH3PbI3) single crystals (not shown here) are qualitatively similar, except that these crystals are highly insulating in the dark, and thus only photo Hall measurements were possible, yielding an estimate for μfew cm2 V−1 s−1.

Theoretical estimates of e-h recombination coefficients

E-h recombination in semiconductors is a fundamentally important process, and various approaches have been developed for assessing the corresponding kinetic coefficient γ. In one approach, for instance, γ is associated with the product sv of the Coulomb capture cross section s and carrier thermal velocity v (ref. 16). In the case of disordered organic and inorganic semiconductors, recombination of charge carriers is often described by the Langevin model22,23, which leads to for the recombination coefficient, where ɛ0 and ɛr are the dielectric permittivities of vacuum and the material, respectively. Evaluating these expressions for our systems would yield estimates of γ on the order of 10−6 cm3 s−1 or higher, that is 4–5 orders of magnitudes greater than what we find experimentally. One, of course, realizes that the above models, evidently not applicable to our case, refer to the e-h collision events rather than to the radiative recombination per se. A more appropriate approach that was successfully applied to the actual radiative recombination in inorganic semiconductors is based on the van Roosbroeck–Shockley’s theory rooted in the principle of detailed balance (for reviews, see, for instance, refs 24, 25). This theory, in particular, explains well the values of γ10−10 cm3 s−1 exhibited by high-purity direct-band inorganic semiconductors, such as, for instance, GaAs26,27 (see also, which, remarkably, are comparable to the values we extract from our observations in hybrid perovskites. In the van Roosbroeck–Shockley’s approach, the radiative recombination coefficient γ is established by the system’s properties in the thermal equilibrium (that is, in the dark):

where, Req and neq are the equilibrium (dark) recombination rate and concentration of electrons (equal to that of holes), respectively. Furthermore, Req is related thermodynamically to the optical properties of the system as25:

utilizing the frequency ω-dependent refraction, nr(ω), and extinction, κ(ω), coefficients. An assessment of equation (3) can be made using model considerations (as illustrated in Supplementary Note 3). Even more attractively, one can use the actual experimental optical data to evaluate Req in equation (4), for which here we use the optical parameters (see Supplementary Fig. 2 and Supplementary Note 3) of CH3NH3PbI3 perovskite extracted from accurate ellipsometric measurements in ref. 28. On the other hand, the dark carrier concentration at the thermal equilibrium neq is not measured directly. If one were to use the standard textbook expression for a non-degenerate semiconductor with energy gap Eg separating two parabolic bands27:

equation (3) then yields the recombination coefficient:

Here, the prefactor was calculated with T=300 K and memh=m=0.2m0 (m0 being the free electron mass). Equation (6) features the absorption onset parameter denoted Eopt, which is equal to 1.553 eV in the parameterization of ref. 28. The excitonic (e-h attraction) effects11,25 are known to reduce the onset of optical absorption in comparison with the semiconductor band-gap in perovskites (see, for example, the discussion of excitons in ref. 29). One can approximately assess the resulting exponential factor in equation (6) from the corresponding exciton binding energy EX. For m=0.2m0 and the relative permittivity equal to 5, for instance, EX54 meV, indicating that the exponential factor is of the order of 10, which would make result (6) for γ larger than our experimental values by about one order of magnitude. The discrepancy here might result from the underestimate of neq by equation (5) for the conventional band carriers, and the larger values of neq would lead to a better agreement with the experiment. We suggest that larger concentrations neq might be actually realized in perovskites due to the interaction of band charge carriers with methylammonium dipoles, as illustrated in Fig. 5.

Figure 5: Dipolar polarons in hybrid perovskite lattice.
figure 5

Schematically, charge carriers can induce rotational re-organization of the surrounding CH3NH3 dipoles (green arrows), leading to the formation of dipolar polarons. Such polarons could account for the relatively low intrinsic charge-carrier mobilities and reduced bimolecular recombination coefficients experimentally revealed in this work. The structure of hybrid perovskite unit cell, with PbI6 or PbBr6 octahedra and a polar methylammonium molecular cation at the centre, is shown in the upper left corner. The green arrows in the main panel represent these polar methylammonium cations.

Accounting for polaronic effects

Theoretical calculations by Frost et al.7 demonstrate that the methylammonium dipoles in hybrid perovskites carry a significant dipole moment, P=2.29 D, and create a rough potential landscape at the nanoscale, but can be easily rotated or locally aligned by overcoming a small rotational energy barrier, Urot≈1 kJ mol−1 (1.6 × 10−21 J or 10 meV per dipole). Here, we propose that a charge carrier moving through the perovskite lattice may itself induce a local orientational rearrangement of the surrounding methylammonium dipoles tending to align them along its electric field (Fig. 5), thus resulting in a type of a dipolar polaron, conceptually similar to polarons known in ionic crystals and polar semiconductors11,12,13. The estimates outlined in Supplementary Note 3 show that such polarons in perovskites should be characterized as intermediate-coupling polarons12, with the dimensionless electron–phonon coupling constant αe−ph2.5 being a good representative value for the interaction of the band carriers with the longitudinal dipolar vibrational modes of energy ħω010 meV. The ‘dressing’ of a band carrier by a phonon cloud is known to change its properties11,12,13: the standard band carrier dispersion E(k)=ħ2k2/2m would be modified to the polaronic energy-momentum relation Ep(k). Two aspects of this modification are important here.

First, polaron formation is energetically favourable, resulting in the polaronic energy shift Ep(0)−αe−phħω0. The effective band-gap for the equilibrium concentration of electron- and hole-polarons is thus reduced: . With the estimates above, this reduction largely negates the effect of the exciton binding EX and substantially decreases the exponential factor in equation (6). (One could also say that the thermal dissociation of an exciton into a polaron pair is more efficient than into a pair of band carriers.)

Second, polarons are ‘heavier’ than the band carriers. While this is qualitatively clear already at the level of the effective mass renormalization12: mmpm(1+αe−ph/6), the actual changes are even more significant, as the polaron dispersion becomes non-parabolic (see Fig. 6 with the accompanying caption, Supplementary Figs 3,4 and Supplementary Note 3)30,31,32. This results in the increased density of the polaronic states and corresponding increase in the equilibrium carrier concentration neq. The data in Fig. 6 show that this effect can be substantial: in this illustration, the volume of phase space available for polarons with energies Ep(k)−Ep(0)≤ħω0 increases approximately by a factor of 1.5433.7 relative to the bare band carriers (compare the solid red and dashed black lines). Thereby the denominator in equation (3) could additionally increase by about an order of magnitude.

Figure 6: Polaron energy-momentum relation.
figure 6

This plot compares the shape of the energy-momentum curves for different models calculated with the electron–phonon coupling constant αe−ph2.5. The energy is measured in units of the vibrational energy ħω0 and the wave number in units of kp=(20/ħ)1/2. The dashed lines show the parabolic dispersion, for the bare band carrier (black) and for the polaronic carrier with renormalized mass mp (blue). The solid lines display the non-parabolic dispersion obtained with variational calculations, according to Lee–Low–Pines theory11,30 (green curve) and according to Larsen theory13,31 (red curve). The latter is shown in the limited range of its applicability, but it is this type of the dispersion that was actually confirmed in the state-of-the-art diagrammatic Monte-Carlo calculations32.


While currently there is no analytical framework that would afford quantitatively reliable calculations of the interplay of excitonic and polaronic effects in the relevant parameter range (all energy parameters: kBT, ħω0, polaronic and excitonic bindings, are of the same order of magnitude), the above estimates and analysis demonstrate that the polaronic effects might provide an explanation that brings the experimental optical data and our measurements of the radiative recombination coefficient γ in a reasonably good agreement with each other. Indeed, the experimental estimates for γ derived above from the Hall effect measurements span the range of (1–8) × 10−11 cm3 s−1. On the other hand, the polaronic effects we discussed evidently lead to a substantial decrease of the value in equation (6) evaluated without such effects and likely reducing this estimate below 10−10 cm3 s−1. Given the fact that photo Hall measurements could precisely address only the difference of the hole and electron mobilities, and some uncertainty in theoretical estimates, the consistency of our results appears quite satisfactory. In addition, we note that the non-parabolic polaron dispersion displayed in Fig. 6 clearly features carrier group velocities vgr(k)=Ep(k)/ħ k considerably lower than those, ħk/m, of the bare band carriers. This, of course, leads to lower carrier mobilities as indeed observed in our experiments.

Another important experimental observation is that we have not found the monomolecular decay regime (trapping) down to rather low carrier densities, n≈1015 cm−3 in thin films, and 5 × 1012 cm−3 in single crystals (Fig. 4). If present, such a regime would manifest itself as a linear σPC(G) dependence (α=1). The absence of trapping is exactly the reason why bimolecular e-h recombination dominates down to such a low carrier density, leading to a remarkably long carrier lifetime and diffusion length at diluted photo-excitation densities, consistent with prior observations33,34. In direct-band inorganic semiconductors, even though similarly small values of γ=10−11—10−10 cm3 s−1 are observed in high-purity crystalline samples, achieving a millisecond carrier lifetime and nearly a millimetre-long diffusion length is unheard of. Ordinarily, other recombination mechanisms such as trapping on recombination centres (or even Auger processes) would start to dominate at a higher crossover carrier density, given the rather small e–h recombination probability. In fact, in well-optimized high-purity single crystals of GaAs, InP or InAs, τ and l are a few μs and a few tens of μm at best26,27 (see also This accentuates the question of why charge carriers in the (disordered) hybrid perovskites are less affected by trapping. The electronic aspects of the unusual defect physics in CH3NH3PbI3 perovskites have already been discussed10. Here, we are wondering if the interaction of defects with methylammonium dipoles could also contribute to the suppression of trapping. Indeed, typical medium-energy traps in semiconductors have energies δUtr=0.1–0.3 eV relative to the band edge. Typical physical size of the traps is of the order of a lattice constant, δrtr≈5 Å. The local rearrangement of methylammonium dipoles by the effective forces in the vicinity of a defect could then occur, if the potential barrier for the methylammonium dipole rotation, Urot≈10 meV, is smaller than the energy gain associated with a dipole-trap interaction, for instance, if estimated as: 10–75 meV (for P=2.29 D). The re-arranged dipoles would thus reduce the defect’s trapping cross section. Such a defect decoration would be reminiscent of the recently observed trap healing effect at two-dimensional semiconductor/polymer interfaces35, with the important distinction that in hybrid perovskites the functional (rotationally responsive) dipoles are naturally available throughout the entire bulk of the sample. The question arises if the dipole rearrangement effect could be greater than that afforded in the standard continuous-dielectric electrostatics. Detailed microscopic computational studies are needed to clarify this issue.

To conclude, we have measured Hall effect in hybrid (organo–inorganic) perovskites films and single crystals and found Hall mobilities ranging from 0.5 to 60 cm2 V−1 s−1, depending on the sample composition and crystallinity. Concurrent measurements of a steady-state photoconductivity and Hall carrier density have allowed to directly determine bimolecular recombination coefficients (as low as 10−10 to 10−11 cm3 s−1), carrier lifetimes (up to 30 μs and 2.7 ms in polycrystalline films and single crystals, respectively) and diffusion lengths (up to 23 and 650 μm in films and crystals, respectively). These measurements provide a direct and conclusive evidence of low e–h recombination rates and remarkably weak charge trapping in hybrid perovskites. They show that photophysical properties of these materials are quite different from those of conventional organic or inorganic semiconductors. We emphasize that our study determines these important transport parameters directly, from steady-state transport measurements, relevant to practical applications. The dipolar polaron model has been found helpful to explain the observed relatively low intrinsic carrier mobilities and radiative recombination rates.


Growth of hybrid perovskite thin films and single crystals

For fabrication of thin-film perovskite samples, we followed the published procedures36,37. Solution of PbI2 in dimethylformamide was spin-coated onto cleaned glass substrates, resulting in a homogeneous PbI2 films. For solution-grown samples, PbI2 films were immersed in a solution of methylammonium iodide in isopropanol. For vapour-grown perovskite films, PbI2 was annealed in a saturated methylammonium iodide vapour at 190 °C. The resulting CH3NH3PbI3 thin films were uniform, large-area (centimetre-scale) films on glass. CH3NH3PbBr3 single crystals were grown through anti-vapour diffusion process38. In brief, 1:1 ratio of methylammonium bromide (CH3NH3Br, synthesized following ref. 39) and lead bromide (PbBr2, Sigma Aldrich, 98%) were dissolved in N,N-dimethylformamide. This solution was filtered into an inner container. The inner container was then put into a bigger container with dichloromethane. The outer container was sealed and kept at room temperature. Square bulky CH3NH3PbBr3 single crystals (3–5 mm on a side) grew at the bottom of the inner container within a few days.

Device fabrication

Devices in Hall bar geometry were fabricated by depositing Au or Ti through a shadow mask on freshly grown films or crystals. After wiring, the devices were capped under vacuum (10−5 Torr) with a protective PFPE (perfluoropolyether) oil, which is a chemically and electrically inert perfluorinated polymer. We find that PFPE can effectively protect samples from degradation due to moisture and other environmental factors. Control tests showed that PFPE does not cause any qualitative changes in the electrical properties of hybrid perovskite samples.

Magneto-transport and photoconductivity measurements

All measurements in this work were carried out at room temperature. a.c. Hall measurements were performed in an a.c. magnetic field of B=0.23 T (r.m.s.), referenced to a Stanford Research lock-in amplifier that measures a.c. VHall. To reduce the parasitic Faraday induction, frequencies below 1 Hz were typically used. More importantly, VHall generated across the sample at a non-zero d.c. excitation (I0) was always compared with that generated at zero current (I=0), which yields a pure, Faraday-induction-corrected, Hall voltage15. We have verified that VHall in all our samples was independent of the frequency in the range 0.3 to 5 Hz, which confirms that undesirable Faraday-induction signal was eliminated. Keithley 6221 current source was used to drive a d.c. excitation current through the sample. Calibration of our a.c. Hall setup has been done by carrying out measurements of a control Si sample with known carrier density and mobility. Longitudinal (photo)conductivity was measured by 4-probe technique, which ensured that ambiguities associated with contact-resistance were eliminated. It is important to emphasize that although 2-probe σPC also exhibits a sublinear power dependence (σPCGα, with α<1), the power exponent α in 2-probe measurements may vary in a wider range from sample to sample due to contact effects. In contrast, 4-probe photoconductivity systematically shows α=½ at high illumination intensities, which signifies a regime governed by bimolecular recombination. Photo-excitation was achieved by illumination with a calibrated blue LED (max. power: 20 W, λ=465 nm) driven by a Keithley 2400 source meter. The highest photon flux used was close to that of one sun (integrating over the part of the spectrum absorbed by the perovskites). Thus, measurements in this work were performed within the range of light intensities relevant for solar cell applications. The errors in Hall mobility values obtained for polycrystalline and single-crystal samples (μHall=8±0.4 and 60±5 cm2 V−1 s−1, respectively) are defined by standard deviation in VHall measurements.

Data availability

The data that support the findings of this study are available from the corresponding author on request.

Additional information

How to cite this article: Chen, Y. et al. Extended carrier lifetimes and diffusion in hybrid perovskites revealed by Hall effect and photoconductivity measurements. Nat. Commun. 7:12253 doi: 10.1038/ncomms12253 (2016).


  1. 1

    Green, M. A., Ho-Baillie, A. & Snaith, H. J. The emergence of perovskite solar cells. Nat. Photon. 8, 506–514 (2014).

    CAS  Google Scholar 

  2. 2

    Sum, T. C. & Mathews, N. Advancement in perovskite solar cells: photophysics behind the photovoltaics. Energy Environ. Sci. 7, 2518–2534 (2014).

    CAS  Google Scholar 

  3. 3

    Kojima, A., Teshima, K., Shirai, Y. & Miyasaka, T. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 131, 6050–6051 (2009).

    CAS  Google Scholar 

  4. 4

    Mitzi, D. B., Feild, C. A., Schlesinger, Z. & Laibowitz, R. B. Transport, optical and magnetic properties of the conducting halide perovskite CH3NH3SnI3 . J. Solid State Chem. 114, 159–163 (1995).

    CAS  Google Scholar 

  5. 5

    Kagan, C. R., Mitzi, D. B. & Dimitrakopoulos, C. D. Organic-inorganic hybrid materials as semiconducting channels in thin-film field-effect transistors. Science 286, 945–947 (1999).

    CAS  Google Scholar 

  6. 6

    Wehrenfennig, C., Eperon, G. E., Johnston, M. B., Snaith, H. J. & Herz, L. M. High charge carrier mobilities and lifetimes in organolead trihalide perovskites. Adv. Mater. 26, 1584–1589 (2014).

    CAS  Google Scholar 

  7. 7

    Frost, J. M. et al. Atomistic origins of high-performance in hybrid halide perovskite solar cells. Nano Lett. 14, 2584–2590 (2014).

    CAS  Google Scholar 

  8. 8

    Frost, J. M., Butler, K. T. & Walsh, A. Molecular ferroelectric contributions to anomalous hysteresis in hybrid perovskite solar cells. Appl. Mater. 2, 081506 (2014).

    Google Scholar 

  9. 9

    Yin, W.-J., Shi, T. & Yan, Y. Unique properties of halide perovskites as possible origins of the superior solar cell performance. Adv. Mater. 26, 4653–4658 (2014).

    CAS  Google Scholar 

  10. 10

    Yin, W.-J., Shi, T. & Yan, Y. Unusual defect physics in CH3NH3PbI3 perovskite solar cell absorber. Appl. Phys. Lett. 104, 063903 (2014).

    Google Scholar 

  11. 11

    Kuper C. G., Whitfield G. D. (eds) Polarons and Excitons Plenum Press (1963).

  12. 12

    Appel, J. Polarons. in Solid State Physics Vol. 21, eds Seitz al. 193–391Academic Press (1968).

    Google Scholar 

  13. 13

    Devreese J. T. (ed) Polarons in Ionic Crystals and Polar Semiconductors North-Holland (1972).

  14. 14

    Podzorov, V. Organic single crystals: addressing the fundamentals of organic electronics. MRS Bull. 38, 15–24 (2013).

    Google Scholar 

  15. 15

    Chen, Y., Yi, H. T. & Podzorov, V. High resolution ac measurements of the Hall effect in organic field-effect transistors. Phys. Rev. Appl. 5, 034008 (2016).

    Google Scholar 

  16. 16

    Bube, R. H. in Photoconductivity of Solids Ch. 3.4 and 11.1, (Wiley (1960).

  17. 17

    Brivio, F., Butler, K. T., Walsh, A. & van Schilfgaarde, M. Relativistic quasiparticle self-consistent electronic structure of hybrid halide perovskite photovoltaic absorbers. Phys. Rev. B 89, 155204 (2014).

    Google Scholar 

  18. 18

    Umari, P., Mosconi, E. & De Angelis, F. Relativistic GW calculations on CH3NH3PbI3 and CH3NH3SnI3 perovskites for solar cell applications. Sci. Rep. 4, 4467 (2014).

    Google Scholar 

  19. 19

    Feng, J. & Xiao, B. Crystal structures, optical properties, and effective mass tensors of CH3NH3PbX3 (X=I and Br) phases predicted from HSE06. J. Phys. Chem. Lett. 5, 1278–1282 (2014).

    CAS  Google Scholar 

  20. 20

    Giorgi, G., Fujisawa, J., Segawa, H. & Yamashita, K. Small photocarrier effective masses featuring ambipolar transport in methylammonium lead iodide perovskite: a density functional analysis. J. Phys. Chem. Lett. 4, 4213–4216 (2013).

    CAS  Google Scholar 

  21. 21

    Ponseca, C. S. et al. Organometal halide perovskite solar cell materials rationalized: ultrafast charge generation, high and microsecond-long balanced mobilities, and slow recombination. J. Am. Chem. Soc. 136, 5189–5192 (2014).

    CAS  Google Scholar 

  22. 22

    Pope, M. & Swenberg, C. E. Electronic Processes in Organic Crystals and Polymers Oxford University Press (1999).

  23. 23

    Pivrikas, A., Neugebauer, H. & Sariciftci, N. S. Charge carrier lifetime and recombination in bulk heterojunction solar cells. IEEE J. Select. Top. Quant. Electron 16, 1746–1758 (2010).

    CAS  Google Scholar 

  24. 24

    Varshni, Y. P. Band-to-band radiative recombination in groups IV, VI and III-V semiconductors (I). Phys. Status Solidi 19, 459 (1967).

    CAS  Google Scholar 

  25. 25

    Pankove, J. I. Optical Processes in Semiconductors Dover Publications (1971).

  26. 26

    Levinstein, M., Rumyantsev, S. & Shur, M. Handbook Series on Semiconductor Parameters Vol. 1, (World Scientific (1996).

  27. 27

    Piprek, J. Semiconductor Optoelectronic Devices—Introduction to Physics and Simulations Ch. 3.7, (Academic Press (2003).

  28. 28

    Löper, P. et al. Complex refractive index spectra of CH3NH3PbI3 perovskite thin films determined by spectroscopic ellipsometry and spectrophotometry. J. Phys. Chem. Lett. 6, 66–71 (2015).

    Google Scholar 

  29. 29

    Sheng, C. et al. Exciton versus free carrier photogeneration in organometal trihalide perovskites probed by broadband ultrafast polarization memory dynamics. Phys. Rev. Lett. 114, 116601 (2015).

    Google Scholar 

  30. 30

    Lee, T. D., Low, F. E. & Pines, D. The motion of slow electrons in a polar crystal. Phys. Rev. 90, 297 (1953).

    Google Scholar 

  31. 31

    Larsen, D. M. Polaron energy spectrum. Phys. Rev. 144, 697–702 (1966).

    CAS  Google Scholar 

  32. 32

    Prokof’ev, N. V. & Svistunov, B. S. Polaron problem by diagrammatic quantum Monte Carlo. Phys. Rev. Lett. 81, 2514–2517 (1998).

    Google Scholar 

  33. 33

    deQuilettes, D. W. et al. Impact of microstructure on local carrier lifetime in perovskite solar cells. Sci. Express 348, 683–686 (2015).

    CAS  Google Scholar 

  34. 34

    Dong, Q. et al. Electron-hole diffusion lengths &gt;175 μm in solution-grown CH3NH3PbI3 single crystals. Sci. Express 347, 967–970 (2015).

    CAS  Google Scholar 

  35. 35

    Lee, B. et al. Trap healing and ultralow-noise Hall effect at the surface of organic semiconductors. Nat. Mater. 12, 1125–1129 (2013).

    CAS  Google Scholar 

  36. 36

    Burschka, J. et al. Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 499, 316–320 (2014).

    Google Scholar 

  37. 37

    Chen, Q. et al. Planar heterojunction perovskite solar cells via vapor-assisted solution process. J. Am. Chem. Soc. 136, 622–625 (2014).

    CAS  Google Scholar 

  38. 38

    Shi, D. et al. Low trap-state density and long carrier diffusion in organolead trihalide perovskite single crystals. Science 347, 519–522 (2015).

    CAS  Google Scholar 

  39. 39

    Kim, H.-S. et al. Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9%. Sci. Rep. 2, 591 (2012).

    Google Scholar 

Download references


We thank Hang-Dong Lee and Torgny Gustafsson for their help with helium-ion microscopy, Pavel Irkhin for his help with the calibration of light sources, Szu-Ying Wang for her help with thin-film sample fabrication. Y.C., H.T.Y. and V.P. thank the National Science Foundation for the financial support of this work under the grant DMR-1506609 and the Institute for Advanced Materials and Devices for Nanotechnology (IAMDN) of Rutgers University for providing necessary facilities. X.-Y.Z. acknowledges support by the US Department of Energy, Office of Science—Basic Energy Sciences, Grant ER46980, A.Z. thanks the Increase Competitiveness Program of NUST «MISIS» (No. К2-2015-014 ) for partial support and appreciates the Welch Foundation for their partial support under grant AT-1617, Y.N.G. is grateful for support from the Department of Energy, Office of Basic Energy Science (DOE/OBES) grant DE-SC0010697.

Author information




V.P. designed the research project and supervised the experiment. Y.C. and H.T.Y. performed device fabrication and measurements. Y.C., X.W., R.H., X.-Y.Z and A.Z. grew perovskite thin films and single crystals, Y.N.G., Y.I.R. and K.S.T. performed theoretical calculations, Y.C., Y.N.G. and V.P. wrote the paper. All authors discussed the results.

Corresponding author

Correspondence to V. Podzorov.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary Information

Supplementary Figures 1-4, Supplementary Notes 1-3 and Supplementary References (PDF 664 kb)

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Chen, Y., Yi, H., Wu, X. et al. Extended carrier lifetimes and diffusion in hybrid perovskites revealed by Hall effect and photoconductivity measurements. Nat Commun 7, 12253 (2016).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing