Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Magnetic ground state of FeSe

Abstract

Elucidating the nature of the magnetism of a high-temperature superconductor is crucial for establishing its pairing mechanism. The parent compounds of the cuprate and iron-pnictide superconductors exhibit Néel and stripe magnetic order, respectively. However, FeSe, the structurally simplest iron-based superconductor, shows nematic order (Ts=90 K), but not magnetic order in the parent phase, and its magnetic ground state is intensely debated. Here we report inelastic neutron-scattering experiments that reveal both stripe and Néel spin fluctuations over a wide energy range at 110 K. On entering the nematic phase, a substantial amount of spectral weight is transferred from the Néel to the stripe spin fluctuations. Moreover, the total fluctuating magnetic moment of FeSe is 60% larger than that in the iron pnictide BaFe2As2. Our results suggest that FeSe is a novel S=1 nematic quantum-disordered paramagnet interpolating between the Néel and stripe magnetic instabilities.

Introduction

Recently, FeSe has attracted considerable interest because of its atypical magnetism1,2,3,4,5,6 and fascinating superconducting properties7,8,9,10. Although the superconducting transition temperature Tc of bulk FeSe (Tc≈8 K) is low, it increases drastically under pressure (Tc≈37 K; ref. 7), by carrier doping (Tc≈40–48 K; refs 8, 9), or in the mono layer limit (Tc65-109 K, ref. 10). The unique superconducting properties of FeSe are presumably related to its magnetism, which has also been shown to be uncommon. FeSe displays nematic, but not stripe magnetic order1,11 that is unexpected because nematic order has been argued to be the consequence of stripe magnetic order, and both break the C4 lattice symmetry11. In iron pnictides, the stripe magnetic order invariably occurs at or immediately below the nematic-(tetragonal-to-orthorhombic) ordering temperature11. Although previous works have shown that the nematic order could be driven by spin fluctuations without the requirement of magnetic order2,3,4,12, the microscopic origin of the absence of the long-range stripe magnetic order in FeSe remains elusive.

Theoretical studies have suggested that the stripe magnetic order in FeSe is absent due to the development of other competing instabilities2,3,4,5,6. Several ground states have been proposed, including Néel order2, staggered dimer/trimers/tetramers magnetic order3, pair-checkerboard order5, spin antiferroquadrupolar order4 and charge current-density wave order6. In experimental studies, neutron-scattering measurements showed substantial low-energy stripe spin fluctuations in single crystal12 and powder samples13. However, because of the limitations of the q-space information that can be obtained for powder measurements and the relatively narrow energy range probed previously, the precise nature of the magnetic ground state remains undetermined; this elucidation requires measurements of the momentum structure of the spin-fluctuation spectrum from low energy to the zone boundary over the entire Brillouin zone.

In this paper, we used inelastic neutron scattering to map out the spin-fluctuation spectra over the entire Brillouin zone in single-crystalline FeSe (Methods). Our data reveal the coexistence of the stripe and Néel spin fluctuations, both of which are coupled with nematicity. In addition, although the spin-fluctuation bandwidth is lower, the total fluctuating magnetic moment (=5.19 /Fe) of FeSe is 60% larger than that in the iron pnictide BaFe2As2 (ref. 14). These findings suggest that FeSe is an S=1 nematic quantum-disordered paramagnet, interpolating between the Néel and stripe magnetic instabilities2.

Results

Momentum and energy dependence of spin fluctuations

Figure 1 shows the constant-energy images of spin fluctuations in the (H, K) plane. Here, in the high-temperature tetragonal phase (110 K), the spin response is strongest at Q=(1, 0) (marked by dashed ellipse) at 15 meV (Fig. 1b), which is consistent with previous low-energy measurements12,13. With an increase in energy (Fig. 1c–j), the spin fluctuations show anisotropic dispersion and counter-propagate mainly along the K direction. This is analogous to the stripe spin fluctuations detected in other iron-based superconductors11,14,15. Most notably, in addition to the stripe spin fluctuations, comparatively weaker, but clear scattering appears near (1, 1) (Fig. 1b, dashed circle), which implies the presence of spin fluctuations associated with the Néel magnetic instability (Methods); different from the anisotropic stripe spin fluctuations, the Néel spin fluctuations are nearly isotropic in the transverse and longitudinal directions (Fig. 1b–g). With an increase in the energy up to 150 meV, the Néel and stripe spin fluctuations overlap and cover a broad area centred at (1, 1) (Fig. 1j). On cooling to within the nematic phase (T=4 K), the Néel spin-fluctuation signal weakens considerably and is almost undetectable <35 meV (Fig. 1k,l). On the other hand, the momentum structure of the stripe spin fluctuation is essentially unchanged above and below Ts (Fig. 1k–s).

Figure 1: Momentum dependence of the spin fluctuations in FeSe at 4 and 110 K.
figure 1

(a) Schematic representation of the stripe and Néel spin fluctuations in the (H, K) plane. (bj) Constant-energy images acquired at 110 K at indicated energies. (ks) Constant-energy images obtained at 4 K at the same intensity scale as those acquired at 110 K. The measurements in (bd,km) and (ej,ns) were carried out on ARCS with the incident neutron energy of 79 and 294 meV, respectively. The sample has two equally populated orthogonal twin domains in the ab plane at 4 K and the intensities near (1, 0) and (0, 1) are roughly the same. Symmetry equivalent data were pooled to enhance statistical accuracy. The |Q|-dependent background is subtracted for the data (bd,km) below the aluminium phonon cutoff energy of 40 meV. Above 40 meV, raw data are presented (ej,ns). The colour bars indicate intensity in unit of mbar sr−1 meV−1 f.u.−1. The dashed ellipses and circles mark the stripe and Néel wavevectors, respectively.

To further elucidate the spin fluctuations in EQ space, we projected the spin fluctuations along the K direction near (1, 0) and (1, 1) (Fig. 2). Because the incident neutron beam was parallel to the c axis, the energy transfer was coupled with L. No L modulations were observed from the scattering near (1, 0, L) and (1, 1, L), which indicates a two-dimensional nature of the magnetism. As shown in Fig. 2a, the stripe spin fluctuations stem from (1, 0), split into two branches at 35 meV and extend up to above 150 meV at 110 K. The steeply dispersive Néel spin fluctuations are also visible (green arrowheads). As the temperature is lowered to 4 K, the Néel spin fluctuation exhibits a 30 meV gap, while the stripe spin fluctuations <70 meV are clearly enhanced (Fig. 2b).

Figure 2: Dispersions of the stripe and Néel spin fluctuations in FeSe at 4 and 110 K.
figure 2

Background-subtracted EK slice of the spin fluctuations at various incident energies: (a) T=110 K; (b) T=4 K. The data at E≥40 and E≤40 meV were collected on ARCS by using incident energy of 294 and 79 meV, respectively. The isotropic Fe2+ magnetic form factor is corrected for both sets of the data. The spectral weight transfer from the Néel (1, 1) to stripe (1, 0) wavevector below 70 meV on cooling to 4 K can be clearly seen. The open circles are dispersions obtained from the constant-energy cuts <68 meV in Fig. 3. The colour bar indicates intensity in unit of mbar sr−1 meV−1 f.u.−1. The vertical bars indicate the energy integration range. The horizontal bars at 15 meV indicate the full-width at half-maximum of the Gaussian fittings in Fig. 3i. The horizontal bars at other energies are the errors derived by least-square fittings. The dashed lines are a guide to the eye.

To quantify the dispersions and intensities of the stripe and Néel spin fluctuations, we made constant-energy cuts at distinct energies (Fig. 3). As Fig. 3d–i show, at T=110 K, the single peak centred at (1, 0) at 15 meV evolves into a pair of peaks along the K direction at E≥35 meV. By contrast, the peak position of the Néel spin fluctuation (see green arrowheads) shows little change; it only broadens gradually in wavevector with increasing energy. The Néel spin fluctuation is more clearly visible along the transverse direction (Fig. 3m–r) because of the comparatively weaker influence of the stripe spin fluctuations. Here, double peaks formed due to the dispersion are not seen <68 meV, because the Néel spin fluctuations are commensurate and steeply dispersive (Fig. 3m–r). At higher energies, the Néel and stripe spin-fluctuation spectra merge with each other, and their dispersions cannot be determined unambiguously (Fig. 3a–c,j–l). The Néel spin fluctuation becomes featureless at low energies (Fig. 3i,r) at 4 K, which agrees with the results shown in the constant-energy and EQ images (Figs 1k and 2b). We attempted to fit both types of spectra concurrently using a linear spin-wave theory for the two-neighbour (J1(a/b)–J2) or three-neighbour (J1(a/b)–J2–J3) Heisenberg model, where J1(a/b), J2 and J3 are nearest neighbour (in the a/b direction), next-nearest neighbour and next next-nearest neighbour exchange coupling constants, respectively; but this was unsuccessful mainly because this theory cannot account for the observed strong low-energy spin excitations at both (1, 0) and (1, 1).

Figure 3: Constant-energy cuts of the stripe and Néel spin fluctuations in FeSe at 4 and 110 K.
figure 3

(ai) Constant-energy cuts through the stripe and Néel magnetic wavevectors along the K direction at 4 and 110 K. (jr) Constant-energy cuts through the Néel magnetic wavevector Q=(1, 1) along the transverse direction. The scan directions are marked by the arrows in the insets. The peak positions (dispersions) are determined by fitting with Gaussian profiles convoluted with the instrumental resolution, with the Fe2+ magnetic form factor corrected. The fitted dispersions are shown in Fig. 2. The error bars indicate 1 s.d.

Momentum integrated local susceptibility above and below Ts

More insight into the nature of the underlying magnetic ground state and its interaction with the nematicity could be acquired by calculating in absolute units the energy dependence of the momentum integrated local susceptibility χ″(ω) above and below Ts; as Fig. 4a,b show, at T=110 K, the Néel spin-fluctuation spectral weight is roughly 26% of that of the stripe spin fluctuation <52 meV, where the two signals are well separated in q-space. Upon cooling to T=4 K, the spectral weight loss for the Néel spin fluctuations is approximately recovered by the enhanced stripe spin fluctuations (red shaded areas), and thus the total local susceptibility χ″(ω) does not show a marked change across Ts (Fig. 4c). Moreover, the detailed temperature dependence of the stripe and Néel spin fluctuations show that the spectral weight transfer is clearly coupled with the development of the nematic phase (Fig. 4d). At both 4 and 110 K, the total χ″(ω) exhibits a high maximum at 105 meV and extends up to 220 meV (Figs 2a,b and 4c). This bandwidth is considerably lower than that (340 meV) of the stripe ordered BaFe2As2 (ref. 14), which is very likely due to the competition between the Néel and stripe magnetic instabilities. Clearly, this type of competition also prevents the long-range magnetic order in FeSe. By integrating the spectral weight from low energy to the zone boundary, we determined that the total fluctuating moment at 4 and 110 K are =5.19±0.32 and 5.12±0.27 /Fe, respectively, which are larger than those in the superconducting BaFe1.9Ni0.1As2 (=3.2 /Fe) and stripe-ordered BaFe2As2 (=3.17 /Fe) (ref. 14). Accordingly, this yields an effective spin of S≈0.74 in FeSe, which likely corresponds to an S=1 ground state in the presence of itinerant electrons.

Figure 4: Energy dependence of the local susceptibility χ″(ω) for FeSe at 4 and 110 K.
figure 4

(ac) Energy dependence of χ″(ω), at 4 and 110 K, calculated for (a) the Néel spin fluctuations, (b) the stripe spin fluctuations, and (c) the sum of the stripe and Néel spin fluctuations. A resonance mode is clearly observed at 4 meV and 4 K, whose intensity is consistent with the previous low-energy measurements normalized with acoustic phonons12. (d) Temperature dependence of the intensities of the stripe and Néel spin fluctuations. The data in ac were collected on ARCS (incident energy Ei=294, 79, 40 meV) and 4SEASONS (Ei=21, 13.6 meV). The data in d were collected on MERLIN (Ei=123.4 meV). The horizontal and vertical bars indicate the energy integration range, and the statistical errors of 1 s.d., respectively. The solid and dashed lines are a guide to the eye.

Discussion

The coexistence of the Néel and stripe spin fluctuations is unexpected because FeSe contains only one type of magnetic ions. This differs from the Mn-doped nonsuperconducting iron-pnictide compound BaFe2−xMnxAs2, where the Néel magnetic correlation is induced by the local moments of Mn, while the stripe magnetic correlation is induced by Fe, given that pure BaMn2As2 is a local-moment Néel type antiferromagnet16. Although density functional theory and dynamical mean-field theory failed to reproduce the observed band structure of FeSe (refs 17, 18), a random-phase approximation calculation with an engineered tight-binding band structure19 predicted the spin fluctuations near (1, 0) and (1, q). However, in this phenomenological model19, the (1, q) spin fluctuation is incommensurate and gapless below Ts, which is inconsistent with our data. The relatively small spin-fluctuation bandwidth and large fluctuating moment together with the low-carrier density17,18 indicate that the magnetic moments in FeSe are more localized than in iron pnictides.

In the more localized case, we can exclude the previously proposed competing staggered dimer/trimers/tetramers magnetic order3 and pair-checkerboard order5. Here, the competition between the Néel and stripe magnetic instabilities could be instead understood within the framework of a frustrated J1–J2 model. In this model, for an S=1 system, the Néel order is stable for J2/J10.525, whereas the stripe order is the ground state for 0.555J2/J1 (refs 20, 21). It was predicted that FeSe would be an S=1 nematic quantum paramagnet in the intermediate coupling region (0.525J2/J10.555), which is characterized by gapped stripe and Néel spin fluctuations2,21. This agrees with our data that the majority of the spectral weight is concentrated at relatively high energies (100 meV) even in the presence of itinerant electrons (Figs 2a,b and 4c). Furthermore, in this scenario, the nematic order is viewed as a vestigial order that is retained when the static stripe order is suppressed by quantum fluctuations2. The finding that the stripe spin fluctuation carries considerably more spectral weight than the Néel spin fluctuation suggests that the system is indeed closer to stripe rather than to Néel order. On this basis, the temperature evolution of the spin fluctuations that we observed can be explained. As the stripe magnetic order breaks the C4 lattice symmetry, while the Néel order preserves it, the orthorhombic-/nematic-phase transition might partially lift the magnetic frustration and drive the system towards the stripe-ordered phase. Thus, the stripe spin fluctuations are enhanced, while the Néel spin fluctuations are suppressed and gapped in the nematic phase. These considerations lead to a natural understanding of the paramagnetic nematic phase in FeSe.

We now discuss the evolution of the magnetism, nematicity and superconductivity in FeSe, and its derivatives. Since the Néel spin fluctuation is gapped in the nematic phase, it is unlikely responsible for the electron pairing in bulk FeSe at ambient pressure. However, the competition between the Néel and stripe magnetic instabilities across Ts suggests that the magnetic ground state and superconductivity could be highly tunable. Indeed, it has been shown that high pressure not only enhances superconductivity, but also induces static magnetic order in FeSe (refs 22, 23). This is surprising as superconductivity always competes with the static magnetic order in iron pnictides. Further neutron diffraction measurements under pressure are required to clarify the nature of this magnetic order. In addition, the proximity of the Néel magnetic instability of FeSe might also have implications for our understanding of the magnetism in the K dosed9,24, molecule intercalated25 and mono layer10,26 FeSe, because in these heavily electron-doped compounds, the nematic order and the hole pockets are absent, and the electron pockets at two adjacent zone edges are connected by the Néel wavevector Q=(1, 1). Interestingly, this would be in analogy with the cuprate superconductors in terms of the magnetism and Fermi surface topology27. To further elucidate the role of the Néel spin fluctuations in iron-based superconductivity, a detailed study of the pressure-/electron-doping dependence of the spin correlations in FeSe would be desirable.

To conclude, we have reported the observation of the Néel spin fluctuations over a wide energy range in an iron-based superconductor. We show that the absence of the long-range magnetic order in FeSe is due to the competition between the Néel and stripe magnetic instabilities. This differs from the parent compounds of the cuprate and iron pnictide high-temperature superconductors, where only one type of magnetic order is observed. Our findings agree with a theoretical prediction that FeSe is a novel S=1 nematic quantum-disordered paramagnet interpolating between the Néel and stripe magnetic instabilities2, which indicates a connection between the magnetism of the cuprate- and iron-based superconductors. The experimental determination of the nematic magnetic ground state of FeSe will be extremely valuable in identifying the microscopic mechanism of superconductivity in FeSe-based materials8,9,10,24,25,26.

Methods

Sample growth and characterizations

Our FeSe single crystals were grown under a permanent gradient of temperature (400–330 °C) in the KCl–AlCl3 flux28. The single-crystal X-ray and neutron diffraction refinements on our samples indicated a stoichiometric chemical composition to within the error bars, and no interstitial atoms or impurity phases were observed (Supplementary Note 1; Supplementary Figs 1–3; Supplementary Table 1). The specific heat, magnetic susceptibility and resistivity measurements performed on randomly selected FeSe single crystals further demonstrate that our sample is a bulk superconductor without detectable impurities. (Supplementary Note 1; Supplementary Figs 4 and 5).

Neutron-scattering experiments

Our inelastic neutron-scattering measurements were carried out on the ARCS time-of-flight chopper spectrometer at the Spallation Neutron Source of Oak Ridge National Laboratory, USA, 4SEASONS chopper spectrometer at the Japan Proton Accelerator Research Complex and MERLIN chopper spectrometer at the Rutherford Appleton Laboratory, Didcot, UK. The large detector arrays on these instruments allowed us to measure spin excitations over a wide range of energy and momentum. The |Q|-dependent background is subtracted for the data below the aluminium phonon cutoff energy of 40 meV (Supplementary Note 2; Supplementary Fig. 7). To facilitate comparison with theory and previous measurements, our data were normalized into absolute units by using the elastic incoherent scattering of a standard vanadium sample. The absolute intensity of the resonance mode is consistent with previous low-energy data12 normalized with acoustic phonons (Supplementary Fig. 6). The incident neutron beam was aligned parallel to the c axis. The wavevector Q at (qx, qy, qz) is defined as (H, K, L)=(qxa/2π, qyb/2π, qzc/2π) in the reciprocal lattice units in the orthorhombic unit cell. In this unit cell, the magnetic wavevectors associated with the stripe and Néel magnetic order are Q=(1, 0) and Q=(1, 1), which correspond to the ordering wavevectors of the parent compounds of the iron pnictides and the cuprates, respectively.

Data availability

All relevant data that support the findings of this study are available from the corresponding author on request.

Additional information

How to cite this article: Wang, Q. et al. Magnetic ground state of FeSe. Nat. Commun. 7:12182 doi: 10.1038/ncomms12182 (2016).

References

  1. McQueen, T. et al. Tetragonal-to-orthorhombic structural phase transition at 90 K in the superconductor Fe1.01Se. Phys. Rev. Lett. 103, 057002 (2009).

    ADS  CAS  Article  PubMed  Google Scholar 

  2. Wang, F., Kivelson, S. A. & Lee, D. Nematicity and quantum paramagnetism in FeSe. Nat. Phys. 11, 959–963 (2015).

    CAS  Article  Google Scholar 

  3. Glasbrenner, J. K. et al. Effect of magnetic frustration on nematicity and superconductivity in iron chalcogenides. Nat. Phys. 11, 953–958 (2015).

    CAS  Article  Google Scholar 

  4. Yu, R. & Si, Q. Antiferroquadrupolar and Ising-nematic orders of a frustrated bilinear-biquadratic Heisenberg model and implications for the magnetism of FeSe. Phys. Rev. Lett. 115, 116401 (2015).

    ADS  Article  PubMed  Google Scholar 

  5. Cao, H.-Y., Chen, S., Xiang, H. & Gong, X.-G. Antiferromagnetic ground state with pair-checkerboard order in FeSe. Phys. Rev. B 91, 020504 (R) (2015).

    ADS  Article  Google Scholar 

  6. Chubukov, A. V., Fernandes, R. M. & Schmalian, J. Origin of nematic order in FeSe. Phys. Rev. B 91, 201105 (R) (2015).

    ADS  Article  Google Scholar 

  7. Medvedev, S. et al. Electronic and magnetic phase diagram of β-Fe1.01Se with superconductivity at 36.7 K under pressure. Nat. Mater. 8, 630–633 (2009).

    ADS  CAS  Article  PubMed  Google Scholar 

  8. Burrard-Lucas, M. et al. Enhancement of the superconducting transition temperature of FeSe by intercalation of a molecular spacer layer. Nat. Mater. 12, 15–19 (2013).

    ADS  CAS  Article  PubMed  Google Scholar 

  9. Miyata, Y., Nakayama, K., Sugawara, K., Sato, T. & Takahashi, T. High-temperature superconductivity in potassium-coated multilayer FeSe thin films. Nat. Mater. 14, 775–779 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  10. Ge, J.-F. et al. Superconductivity above 100 K in single-layer FeSe films on doped SrTiO3 . Nat. Mater. 14, 285–289 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  11. Dai, P. C. Antiferromagnetic order and spin dynamics in iron-based superconductors. Rev. Mod. Phys. 87, 855 (2015).

    ADS  MathSciNet  CAS  Article  Google Scholar 

  12. Wang, Q. et al. Strong interplay between stripe spin fluctuations, nematicity and superconductivity in FeSe. Nat. Mater. 15, 159–163 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  13. Rahn, M. C., Ewings, R. A., Sedlmaier, S. J., Clarke, S. J. & Boothroyd, A. T. Strong (π,0) spin fluctuations in β-FeSe observed by neutron spectroscopy. Phys. Rev. B 91, 180501 (R) (2015).

    ADS  Article  Google Scholar 

  14. Liu, M. et al. Nature of magnetic excitations in superconducting BaFe1.9Ni0.1As2 . Nat. Phys. 8, 376–381 (2012).

    CAS  Article  Google Scholar 

  15. Lumsden, M. D. et al. Evolution of spin excitations into the superconducting state in FeTe1−xSex . Nat. Phys. 6, 182–186 (2010).

    CAS  Article  Google Scholar 

  16. Tucker, G. S. et al. Competition between stripe and checkerboard magnetic instabilities in Mn-doped BaFe2As2 . Phys. Rev. B 86, 020503 (R) (2012).

    ADS  Article  Google Scholar 

  17. Watson, M. D. et al. Emergence of the nematic electronic state in FeSe. Phys. Rev. B 91, 155106 (2015).

    ADS  Article  Google Scholar 

  18. Shimojima, T. et al. Lifting of xz/yz orbital degeneracy at the structural transition in detwinned FeSe. Phys. Rev. B 90, 121111 (R) (2014).

    ADS  Article  Google Scholar 

  19. Kreisel, A., Mukherjee, S., Hirschfeld, P. J. & Andersen, B. M. Spin excitations in a model of FeSe with orbital ordering. Phys. Rev. B 92, 224515 (2015).

    ADS  Article  Google Scholar 

  20. Sushkov, O. P., Oitmaa, J. & Weihong, Z. Quantum phase transitions in the two-dimensional J 1 -J 2 model. Phys. Rev. B 63, 104420 (2001).

    ADS  Article  Google Scholar 

  21. Jiang, H. C. et al. Phase diagram of the frustrated spatially-anisotropic S =1 antiferromagnet on a square lattice. Phys. Rev. B 79, 174409 (2009).

    ADS  Article  Google Scholar 

  22. Bendele, M. et al. Coexistence of superconductivity and magnetism in FeSe1−x under pressure. Phys. Rev. B 85, 064517 (2012).

    ADS  Article  Google Scholar 

  23. Terashima, T. et al. Pressure-induced antiferromagnetic transition and phase diagram in FeSe. J. Phys. Soc. Jpn 84, 063701 (2015).

    ADS  Article  Google Scholar 

  24. Wen, C. H. P. et al. Anomalous correlation effects and unique phase diagram of electron-doped FeSe revealed by angle resolved photoemission spectroscopy. Nat. Commun. 7, 10840 (2016).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  25. Zhao, L. et al. Common electronic origin of superconductivity in (Li,Fe)OHFeSe bulk superconductor and single-layer FeSe/SrTiO3 films. Nat. Commun. 7, 10608 (2016).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  26. Tan, S. et al. Interface-induced superconductivity and strain-dependent spin density waves in FeSe/SrTiO3 thin films. Nat. Mater. 12, 634–640 (2013).

    ADS  CAS  Article  PubMed  Google Scholar 

  27. Lee, P. A., Nagaosa, N. & Wen, X. G. Doping a Mott insulator: Physics of high-temperature superconductivity. Rev. Mod. Phys. 78, 17 (2006).

    ADS  CAS  Article  Google Scholar 

  28. Chareev, D. et al. Single crystal growth and characterization of tetragonal FeSe1−x superconductors. Cryst. Eng. Commun. 15, 1989–1993 (2013).

    CAS  Article  Google Scholar 

Download references

Acknowledgements

We gratefully acknowledge H. Cao for the neutron diffraction experimental support, and Q. Si, R. Yu, A. Kreisel, P. Hirschfeld, B. M. Andersen and R. Valenti for discussions. This work was supported by the Ministry of Science and Technology of China (973 project: 2015CB921302), the National Natural Science Foundation of China (No. 11374059) and the Shanghai Pujiang Scholar Program (No. 13PJ1401100). Research at the Spallation Neutron Source of Oak Ridge National Laboratory was sponsored by the Scientific User Facilities Division, Office of Basic Energy Sciences, US Department of Energy. A.N.V. was supported in part by the Ministry of Education and Science of the Russian Federation in the framework of the Increase Competitiveness Program of NUST ‘MISiS’ (No. 2-2014-036). D.A.C. and A.N.V. also acknowledge the support of the Russian Foundation for Basic Research through grants 13-02-00174, 14-02-92002, 14-02-92693 and Act 211 Government of the Russian Federation (No. 02.A03.21.0006).

Author information

Authors and Affiliations

Authors

Contributions

J.Z. conceived the research. Q.W., X.Z., D.A.C. and A.N.V. synthesized the sample. Q.W., Y.S., B.P., M.A. and X.C. characterized the sample. Q.W., Y.S. and B.P. conducted the neutron experiments with experimental assistance from K. Ikeuchi, K. Iida, A.D.C., D.T.A. and H.C.W. J.Z., Q.W., Y.S. and B.P. analysed the data and wrote the paper. All authors provided comments for the paper.

Corresponding author

Correspondence to Jun Zhao.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary Information

Supplementary Figures 1-7, Supplementary Table 1, Supplementary Notes 1-2 and Supplementary References (PDF 1040 kb)

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Wang, Q., Shen, Y., Pan, B. et al. Magnetic ground state of FeSe. Nat Commun 7, 12182 (2016). https://doi.org/10.1038/ncomms12182

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1038/ncomms12182

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing