Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Near-field photocurrent nanoscopy on bare and encapsulated graphene


Optoelectronic devices utilizing graphene have demonstrated unique capabilities and performances beyond state-of-the-art technologies. However, requirements in terms of device quality and uniformity are demanding. A major roadblock towards high-performance devices are nanoscale variations of the graphene device properties, impacting their macroscopic behaviour. Here we present and apply non-invasive optoelectronic nanoscopy to measure the optical and electronic properties of graphene devices locally. This is achieved by combining scanning near-field infrared nanoscopy with electrical read-out, allowing infrared photocurrent mapping at length scales of tens of nanometres. Using this technique, we study the impact of edges and grain boundaries on the spatial carrier density profiles and local thermoelectric properties. Moreover, we show that the technique can readily be applied to encapsulated graphene devices. We observe charge build-up near the edges and demonstrate a solution to this issue.


As large scale integration and wafer scale device processing capabilities of graphene have become available1,2,3,4,5,6,7,8, technological implementations of electronic and optoelectronic graphene devices are within reach9,10,11. At the same time, to achieve high device performance, any imperfections at the nanometer or even atomic scale need to be minimized or even eliminated. For example, in large area graphene, grown by chemical vapour deposition (CVD), grain boundaries are the stitching regions between different monocrystalline parts of graphene and act as carrier scatterers, limiting the graphene mobility and uniformity12,13. In addition, even perfectly monocrystalline graphene is still highly sensitive to its environment, and on typical substrates charge–density inhomogeneities (charge puddles)14,15,16,17,18,19 and additional doping near contacts, defects and edges arise, which reduce the device performance as well. Therefore, it is important to efficiently probe the nanoscale optoelectronic properties of graphene devices and to understand their microscopic physical behaviour.

A major challenge is that many of the available characterization techniques are invasive20, need specifically designed device structures13,21,22, image only very small areas14,15,21,23,24,25, rely on high doping of the graphene,26 require unhindered electrical access of the probe to the graphene14,15,21,23,24 or lack the desired nanometer resolution27 and are expensive and difficult to implement. For the direct quality control of graphene devices, a method that can image electrical and optical properties of graphene devices, at nanoscale resolution, without any special preparation and without modifying the devices is required.

Here we demonstrate fully non-invasive room-temperature scanning near-field photocurrent nanoscopy28,29,30,31,32,33,34,35,36,37,38 for the first time applied on graphene with infrared frequencies and use it to study the nanoscale optoelectronic properties of graphene devices that can later be used for real applications. This technique is based on electrical probing of the photoresponse due to strongly localized heating. We apply this technique to study the microscopic physics of grain boundaries and charge–density inhomogeneities. In the case of grain boundaries, we were able to identify the magnitude of their Seebeck coefficient, while for charge–density inhomogeneities, we show how they influence the global charge neutrality point of graphene devices. In addition, we study encapsulated graphene devices39,40, where the encapsulation would prevent many other scanning probe techniques from accessing local properties of graphene. In these devices, we find a charge build-up near the edges and show that using local metal gates instead of a global backgate effectively suppresses this type of edge doping. In general, this technique operates most effectively with mid-infrared light because it does not lead to photodoping41 and it is more stable in operation, compared with visible light.


Measurement principle

The measurement principle is sketched in Fig. 1a. The setup is based on a scattering-type scanning near-field optical microscope (s-SNOM)26,42 augmented with electrical contact to the sample to measure currents in situ28,29,30,31,32,33,34,35,36,37,38. In contrast to conventional s-SNOM, we do not need to measure the outscattered light but rather directly measure current induced by the near-field as explained in the following. A 10.6-μm mid-infrared laser illuminates a metallized atomic force microscope probe, tapping at its mechanical resonance frequency. Part of the incoming light, polarized parallel to the shaft of the probe, excites a strong electric field at the tip apex due to an antenna effect43. The spatial extent of this near-field is on the order of 25nm, limited only by the tip radius and much smaller than the free space wavelength of the impinging light43.

Figure 1: Near-field photocurrent working principle and photocurrent from grain boundaries.

(a) Sketch of the scattering-type scanning near-field optical microscope setup. A mid-infrared laser illuminates the atomic force microscope tip, which generates a locally concentrated optical field, which is absorbed by the graphene generating a position dependent photocurrent. The blue region in the graphene lattice represents a grain boundary with a modified Seebeck coefficient. The arrows sketch the photocurrent flow pattern. For each position only the magnitude and direction of the current are measured. The sketch is not to scale. (b) IPC map at at backgate voltage VBG=0 V of a single layer CVD graphene device (Supplementary Fig. 1) with three contacts: top left (drain), right (source) and bottom left (ground). Both grain boundaries and wrinkles show characteristic photocurrent patterns. (scale bar, 5 μm) The green box indicates the measurement region in c,d. (c) Topography of etched CVD graphene does not show grain boundary but only wrinkles and other inhomogeneities due to the transfer process. (scale bar, 500 nm) (d) IPC at VBG=0 V clearly shows a grain boundary and the expected sign change around it. The black dashed line indicates the measurement positions in Fig. 2a,d. (scale bar, 500 nm) (e) Topography (orange) and IPC (red) measured at the orange line in c and the red line in d, respectively.

The near and far fields impinging on the device induce charge flows in the device (by mechanisms discussed below), and drive currents into an external current amplifier via contacts on the device. We isolate the part of the current that is induced by near fields by demodulating the current at the second harmonic of the tip tapping frequency43. This demodulated current is denoted IPC and referred to as near-field photocurrent and is obtained together with near-field optical and topography information. A typical map of IPC, obtained by scanning the tip over a CVD graphene device, is shown in Fig. 1b.

We can assess the spatial resolution of the photocurrent maps by comparing a region near the edge (Fig. 1d) with a topographic image from the same region (Fig. 1c). As can be seen, IPC falls to zero for tip locations away from the graphene on a similar length scale as the topography, demonstrating the successful isolation of near-field contributions. In Fig. 1e, we quantify the resolution by observing the change in IPC as the tip is moved over the edge of graphene. The full-width at half maximum of the photocurrent peak at this location is 100 nm, matching the rise distance in the topographic signal. This resolution is far below any limits relating to the 10.6 μm free space light wavelength.

Photothermoelectric photocurrent generation mechanism

As to the physical mechanism of the photocurrent, we consider the photothermoelectric effect that has been shown to dominate the photoresponse of graphene11,44,45,46,47,48: the light (in this case, the tip-enhanced near-field) locally heats the graphene, and this heat acts via non-uniformities in Seebeck coefficient S to drive charge currents within the device and into the contacts (see Methods section). Therefore, we interpret the variations of IPC in terms of microscopic variations in S. The Seebeck coefficient, which depends on material properties such as carrier density and mobility, is a measure of the electromotive force driven by a temperature difference in a material. A complete description of IPC needs to take into account the carrier cooling length45,46 and overall sample geometry49. The carrier cooling length , where κ the sheet thermal conductivity in plane and g the interfacial thermal conductivity out of plane to the heat sinking substrate, describes how far heat propagates through the charge carriers, before dissipating to the environment (see Supplementary Fig. 2)46. A quantitative model of the thermoelectric photocurrent mechanism can be found in the Methods section.

Grain boundary characterization

We first discuss the application of this infrared near-field photocurrent technique to grain boundaries. They are not visible in the simultaneously acquired topography, and are responsible for some of the line-shaped features in the photocurrent map in Fig. 1b. Some of the other features stem from large scale inhomogeneities of the sample. The region within the green frame is shown with higher resolution in Fig. 1d, exhibiting a strong photocurrent signal that changes sign along a sharp boundary, yet the graphene is topographically flat in the vicinity of this boundary (Fig. 1c). We show now that this type of feature indicates a grain boundary.

Figure 2a shows a line profile of IPC across the boundary feature identified in Fig. 1d. This antisymmetric IPC can be explained by a localized deviation in S at the boundary, that is, a line defect within an otherwise uniform thermoelectric medium (Supplementary Figs 3,4 and Supplementary Note 1). Indeed, grain boundaries behave as localized lines of strongly modified electronic properties, within otherwise uniform graphene20,21,26,50,51. We remark that the decay of the photocurrent away from the boundary extends over more than 100 nm, which is due to a larger hot carrier cooling. We find in this case lcool=140 nm.

Figure 2: Photocurrent profile at a grain boundary and its gate voltage dependence.

(a) Photocurrent profile, measured at the black dashed line in Fig. 1d, perpendicular to the grain boundary at VBG=0 V shows good agreement with the photothermoelectric model with lcool=140 nm. The modelled spatial Seebeck profile (with FWHM 20 nm) is shown in black. (b) Two-probe device resistance as a function of VBG. (c) Simulated Seebeck coefficient SG for pristine graphene (solid line) and SGB for polycrystalline graphene with an average grain size of 25 nm (dashed line; Supplementary Note 2). (d) Backgate dependent photocurrent profile perpendicular to the grain boundary shows that the grain boundary changes its sign at the charge neutrality point. (e) Simulated backgate dependent photocurrent profile based on the Seebeck profiles in c normalized to the simulated photocurrent maximum.

To gain more insight in the Seebeck coefficient at the grain boundary, we tune the carrier density by a global gate (Fig. 2d). We observe that the antisymmetric spatial photocurrent profile changes sign as the backgate voltage VBG passes the peak in resistance, that is, the global charge neutrality point VD. The Seebeck coefficient SG of graphene itself changes sign at the charge neutrality point44,45,52,53 (Fig. 2c). Thus, after calibrating the sign to the known sign of the contact photocurrent, our data implies that the Seebeck coefficient of the grain boundary SGB is always smaller in magnitude than SG, since IPC(VBG)SG(VBG)−SGB(VBG).

Using a polycrystalline graphene model, we compute the resistance due to grain boundaries using a Kubo transport formalism and real space simulations54. SGB is the ratio of the first- and zero-order Onsager coefficients (Supplementary Note 2). Indeed, we find that SGB is always smaller in magnitude and has a similar lineshape as SG in the carrier density range measured (Fig. 2c). Figure 2e shows a simulation of the photocurrent for the calculated Seebeck coefficients, which is in agreement with the measurements (Supplementary Figs 5,6).

Charge puddle characterization

We next examine near-field photocurrent in a typical two-probe exfoliated graphene device (Fig. 3). A strong photocurrent is obtained with the tip near the metal contacts, similar to previous near- and far-field measurements34,47,55. In addition, an apparently random pattern of photocurrent is present throughout the device, as in high-resolution far-field measurements55 but at a much finer scale.

Figure 3: Photocurrent from charge puddles.

(a) Near-field photocurrent map of an exfoliated graphene device on 300 nm SiO2 at VBG=20 V. The dashed lines indicate the position of the contacts and solid lines the graphene edges. The green box indicates the measurement region in b (scale bar, 5 μm). (b) Detailed photocurrent map at the charge neutrality point of the device (VBG=7 V) reveals the charge puddles and the high spatial resolution of the technique. (scale bar, 1 μm) (c) Autocorrelation of the photocurrent from charge puddles at VD (data points) compared to photocurrent expected from a random charge puddle distribution and lcool=200 nm (blue curve). Autocorrelation is taken along the source drain current path.

The random photocurrent pattern between the contacts in Fig. 3a indicates random variations in Seebeck coefficient over short length scales (Supplementary Fig. 7). Random variations of the Seebeck coefficient are indeed expected since it depends on carrier density52, which in turn has fine-scaled inhomogeneities (charge puddles)14,15,16,17,18. The photocurrent variations can thus be used to gain insight in the charge puddle distribution. A more detailed view of the photocurrent due to charge puddles in Fig. 3b shows that the length scale that can be resolved is on the order of hundreds of nanometres.

Quantitatively, from the autocorrelation of the photocurrent in comparison with a photothermoelectric model taking into account the size of the charge puddles in Fig. 3c we extract lcool200 nm. The charge puddles are modelled to have a size of 20 nm, in accordance with measurements of graphene on silicon oxide (SiO2; refs 15, 16, 17, 18).

By changing the gate voltage we study the carrier density profile with high spatial resolution (Fig. 4) and highlight the possibility of spatially resolving the charge neutrality point for a large device. IPC from charge puddles is largest around the charge neutrality point and varies with position. This is consistent with the very high sensitivity of the Seebeck coefficient to changes in carrier density, near-zero density (Fig. 4b). The magnitude of photocurrent from charge puddles depends on the difference of Seebeck coefficient between two adjacent charge puddles or in other words the strongest photocurrent from charge puddle appears at the position of highest Seebeck gradient. This allows us to map the local carrier density offset (charge inhomogeneity) throughout the device, as indicated by the extremum of photocurrent in a scan of photocurrent versus gate voltage (Fig. 4c). The photocurrent from adjacent charge puddles with a given charge carrier density offset does not change sign when sweeping through the charge neutrality point. This is because the difference in Seebeck coefficient between these puddles does not change sign.

Figure 4: Dependence of photocurrent profiles on backgate voltage reveals doping inhomogeneities.

(a) Backgate dependence of the resistance of the device measured simultaneously to the photocurrent in blue. The red curve shows the normalized root mean square of the photocurrent across the device. The green curve shows a single normalized photocurrent backgate trace, corresponding to the green dashed dotted line in c. (b) Backgate dependent Seebeck coefficient of graphene, calculated from the gate dependent resistance in a using the Mott formula52. (c) Backgate dependence of the photocurrent across the device. Graphene is between the black dashed lines, which indicate the edges of the metal contacts.

We can thus resolve the local charge neutrality point at a given position of the device (green curve, Fig. 4a), which can be different from the global charge neutrality point VD, the backgate voltage VBG at which the resistance is maximum (blue curve, Fig. 4a). We show that the global charge neutrality point (blue curve, Fig. 4a) is determined by an average of the gate voltages at which the local charge neutrality points appear (red curve, Fig. 4a). Spatially resolved puddle photocurrent can be much narrower (green curve, Fig. 4a) than the average of all possible current paths (red curve, Fig. 4a) This indicates that the graphene locally has less inhomogeneity. Thus the technique gives insight not only in the global but also in the local behaviour of the device.

Characterization of encapsulated devices

Finally, we apply this technique to a graphene device encapsulated between two layers of hexagonal boron nitride (h-BN), using the polymer-free van der Waals assembly technique39,40 as sketched in Fig. 5e. This device lies on top of an oxidized silicon wafer, used as a backgate. The stack is etched into a triangle and electrically side-contacted by two metal contacts39. Recent studies in vacuum and low temperatures56,57 have shown that the edges affect where current flows in the device, in particular near charge neutrality. In the following we study the build-up of edge doping in ambient conditions and provide a solution to this.

Figure 5: Near-field photocurrent maps revealing edge doping in encapsulated graphene.

(a) Spatial photocurrent profile versus backgate voltage VBG (minus voltage of the resistance maximum VD) near the edge of encapsulated graphene. These data are taken directly after annealing the device. (VD=−0.3 V). (b) The same scan on the same device after three hours in air, (VD=−0.5 V) and c, after annealing and applying VBG up to 3 V (VD=3 V). (d) The same scan after approximately 20 h in air and after applying VBG up to 50 V (VD=30 V). (e) Sketch of the device, a stack of h-BN(46 nm)/Graphene/h-BN(7 nm) on a Si/SiO2(300 nm) wafer used as global backgate. In this sketch we only show one of the two contacts used for electrical measurements. (f) Photocurrent close to the resistance maximum at VBG=−28 V shows a triangular photocurrent pattern, due to edge p-doping. The dashed dotted line indicates where the measurements in ad were taken. (scale bar, 2 μm).

While monitoring the photocurrent of such encapsulated devices, we observe indications of strong carrier density variations near the edges over micrometre scales. These variations are influenced by lighting conditions (Supplementary Fig. 8), gate voltages, and temperature, and evolve over timescales ranging from minutes to weeks. As an example, Fig. 5a–d shows a progression of photocurrent maps, taken after annealing the device at 200 °C for 30 min in ambient conditions to temporarily remove charge density variations near the edges. Initially in Fig. 5a we see very small photocurrents indicating a flat carrier density landscape. After some time (hours), in the dark with only gate voltages smaller than 3 V applied, a small doping gradient between the contacts builds up. This gradient leads to the stronger photocurrent shown in Fig. 5b. The local charge neutrality point, indicated by the maximum of photocurrent, is at the same position close to the edge of the device as further inside the bulk. After keeping the device for 3 h in ambient conditions we can see a change of the local charge neutrality point at the edge of the graphene compared to the bulk in Fig. 5c. The edge is slightly more p-type compared to the bulk. Finally, we apply high gate voltages, of in this case 50 V for 20 h, to increase the edge doping. A strong p-doping at the edge and an n-doping in the bulk of the graphene is induced in Fig. 5d. This indicates that electric field accelerates the speed and increases this type of edge doping.

We exploit the observed edge doping to create a natural p–n junction along the edge of the device. For this we apply a backgate voltage at which the edge of the graphene is p-type and the bulk n-type. This is similar to the situation in Fig. 5d at VBG=VD. We observe photocurrent at the junction in Fig. 5f around the whole device, indicating that the edge doping is uniform around the graphene. The photocurrent decays gradually towards the midline between the electrodes as a result of how the triangular geometry modifies the ability of the contacts to capture photocurrents49. The sign change in the middle of the device is because in the current direction the junction changes from a p–n junction to an n–p junction (Supplementary Fig. 9 and Supplementary Note 2). We are able to temporarily reset the edge doping by annealing the device on a hotplate at 200 °C for 30 min as we show in Fig. 5a.

Local gates prevent charge build-up at the device edges

While we have not been able to precisely identify the origin of the edge doping, we suspect that water molecules are able to penetrate between the boron nitride and the SiO2 due to the surface of the h-BN being not completely conformal with the underlying SiO2 substrate. This water molecule penetration then leads to trapped charges is responsible for the observed edge doping. We also present here a technique to completely eliminate the edge doping. We place encapsulated graphene on top of a local conductive gate, such as a 15 nm AuPd alloy sketched in Fig. 6a. As the photocurrent measurement in Fig. 6b shows, we find that edge doping is efficiently suppressed even after extended periods of time at ambient conditions and high gate voltages. Furthermore, such devices efficiently suppress the photodoping effect observed for devices where the h-BN is in contact with SiO2 (ref. 41; Supplementary Fig. 10 and Supplementary Note 1).

Figure 6: Edge doping is efficiently suppressed using devices with local metal gates.

(a) Sketch of the device with local metal gate with the two h-BN layers in light blue and the local metal gate in gold. The layers are from bottom to top SiO2(300 nm)/AuPd(15 nm)/h-BN(42 nm)/Graphene/h-BN(13 nm). (b) Photocurrent from charge puddles in encapsulated graphene on a metal gate close to the charge neutrality point. The electrical contacts are on the left and right outside of this figure. (scale bar, 2 μm).

In the device with a local metal gate used to suppress both edge- and photodoping, we find small features due to charge puddles on top of a slowly varying background photocurrent, due to large-scale carrier density inhomogeneities. The size of the features due to charge puddles determined by autocorrelation is 800 nm. The long length scale of those features is either due to the longer cooling length of the encapsulated graphene compared to the graphene on SiO2 or due to larger charge puddle size in the encapsulated devices. Further work is required to clearly distinguish these effects.


To conclude, we have demonstrated that scanning near-field photocurrent nanoscopy is a versatile technique to characterize the electronic and optoelectronic and even previously inaccessible properties of relevant graphene devices. This technique is highly promising for spatially resolved quality control of regular graphene devices without the need for special device structures and can therefore be readily applied.


Photocurrent model

Photocurrent IPC in graphene as generated by the photothermoelectric effect and is described as:45,46,47

where R is the total resistance including graphene, contacts and circuitry, W the device width and x the current flow direction. This is valid for rectangular graphene devices and special care needs to be taken for arbitrary shapes, such as in Fig. 5 (ref. 49). For the temperature profile T(x) we consider that the heat spreads in two dimensions with heat sinking to lattice and substrate, producing a T(x) profile described by a modified Bessel function of the second kind, with a finite tip size correction (Supplementary Note 2). A 25-nm finite tip-size correction was used for all simulations.

Measurement details

The s-SNOM used was a NeaSNOM from Neaspec GmbH, equipped with a CO2 laser operated at 10.6 μm, away from the phonon resonance of SiO2, which can lead to strong substrate contributions to the photocurrent48. The laser power used was 20 mW. The probes were commercially available metallized atomic force microscopy probes with an apex radius of approximately 25 nm. The tip height was modulated at a frequency of approximately 250 kHz with a 60–80 nm amplitude. A Femto DLPCA-200 current pre-amplifier was used. The probe tip was electrically grounded. Because of the different device geometries and the fact that all the measurements were taken at different times and slightly different device conditions the absolute values of the photocurrents are not comparable.

Device fabrication

The CVD graphene, grown on copper, was transferred onto a self-assembled monolayer58 on 285 nm of SiO2 to stabilize the charge neutrality point. The contacts were defined using optical lithography with Ti (5 nm)/Pd (35 nm). The graphene was transferred onto deposited contacts.

The exfoliated graphene device was fabricated on a Si/SiO2(300 nm) wafer, used as backgate. The Cr(0.8 nm)/Au(80 nm) contacts were defined using electron beam lithography.

The Si/SiO2(300 nm)/h-BN(46 nm)/Graphene/h-BN(7 nm) and the Si/SiO2(300 nm)/AuPd(15 nm)/h-BN(42 nm)/Graphene/h-BN(13 nm) stacks, were fabricated using the polymer-free van der Waals assembling technique39.

Additional information

How to cite this article: Woessner, A. et al. Near-field photocurrent nanoscopy on bare and encapsulated graphene. Nat. Commun. 7:10783 doi: 10.1038/ncomms10783 (2016).


  1. 1

    Li, X. et al. Large-area synthesis of high-quality and uniform graphene films on copper foils. Science 324, 1312–1314 (2009).

    CAS  ADS  Article  Google Scholar 

  2. 2

    Reina, A. et al. Large area, few-layer graphene films on arbitrary substrates by chemical vapor deposition. Nano Lett. 9, 30–35 (2009).

    CAS  ADS  Article  Google Scholar 

  3. 3

    Bae, S. et al. Roll-to-roll production of 30-inch graphene films for transparent electrodes. Nat. Nanotech. 5, 574–578 (2010).

    CAS  ADS  Article  Google Scholar 

  4. 4

    Bonaccorso, F. et al. Production and processing of graphene and 2d crystals. Mater. Today 15, 564–589 (2012).

    CAS  Article  Google Scholar 

  5. 5

    Ren, W. & Cheng, H.-M. The global growth of graphene. Nat. Nanotech. 9, 726–730 (2014).

    CAS  ADS  Article  Google Scholar 

  6. 6

    Lee, J.-H. et al. Wafer-scale growth of single-crystal monolayer graphene on reusable hydrogen-terminated germanium. Science 344, 286–289 (2014).

    CAS  ADS  Article  Google Scholar 

  7. 7

    Gao, L. et al. Face-to-face transfer of wafer-scale graphene films. Nature 505, 190–194 (2014).

    CAS  ADS  Article  Google Scholar 

  8. 8

    de Heer, W. A. et al. Large area and structured epitaxial graphene produced by confinement controlled sublimation of silicon carbide. Proc. Natl Acad. Sci. USA 108, 16900–16905 (2011).

    CAS  ADS  Article  Google Scholar 

  9. 9

    Ferrari, A. C. et al. Science and technology roadmap for graphene, related two-dimensional crystals, and hybrid systems. Nanoscale 7, 4598–4810 (2014).

    ADS  Article  Google Scholar 

  10. 10

    Akinwande, D., Petrone, N. & Hone, J. Two-dimensional flexible nanoelectronics. Nat. Commun. 5, 5678 (2014).

    CAS  ADS  Article  Google Scholar 

  11. 11

    Koppens, F. H. L. et al. Photodetectors based on graphene, other two-dimensional materials and hybrid systems. Nat. Nanotech. 9, 780–793 (2014).

    CAS  ADS  Article  Google Scholar 

  12. 12

    Yazyev, O. V. & Louie, S. G. Electronic transport in polycrystalline graphene. Nat. Mater. 9, 806–809 (2010).

    CAS  ADS  Article  Google Scholar 

  13. 13

    Yu, Q. et al. Control and characterization of individual grains and grain boundaries in graphene grown by chemical vapour deposition. Nat. Mater. 10, 443–449 (2011).

    CAS  ADS  Article  Google Scholar 

  14. 14

    Martin, J. et al. Observation of electron-hole puddles in graphene using a scanning single-electron transistor. Nat. Phys. 4, 144–148 (2008).

    CAS  Article  Google Scholar 

  15. 15

    Chen, J.-H., Jang, C., Xiao, S., Ishigami, M. & Fuhrer, M. S. Intrinsic and extrinsic performance limits of graphene devices on SiO2 . Nat. Nanotech. 3, 206–209 (2008).

    CAS  Article  Google Scholar 

  16. 16

    Zhang, Y., Brar, V. W., Girit, C., Zettl, A. & Crommie, M. F. Origin of spatial charge inhomogeneity in graphene. Nat. Phys. 5, 722–726 (2009).

    CAS  Article  Google Scholar 

  17. 17

    Decker, R. et al. Local electronic properties of graphene on a BN substrate via scanning tunneling microscopy. Nano Lett. 11, 2291–2295 (2011).

    CAS  ADS  Article  Google Scholar 

  18. 18

    Xue, J. et al. Scanning tunnelling microscopy and spectroscopy of ultra-flat graphene on hexagonal boron nitride. Nat. Mater. 10, 282–285 (2011).

    CAS  ADS  Article  Google Scholar 

  19. 19

    Burson, K. M. et al. Direct imaging of charged impurity density in common graphene substrates. Nano Lett. 13, 3576–3580 (2013).

    CAS  ADS  Article  Google Scholar 

  20. 20

    Duong, D. L. et al. Probing graphene grain boundaries with optical microscopy. Nature 490, 235–239 (2012).

    CAS  ADS  Article  Google Scholar 

  21. 21

    Huang, P. Y. et al. Grains and grain boundaries in single-layer graphene atomic patchwork quilts. Nature 469, 389–392 (2011).

    CAS  ADS  Article  Google Scholar 

  22. 22

    Yasaei, P. et al. Bimodal phonon scattering in graphene grain boundaries. Nano Lett. 15, 4532–4540 (2015).

    CAS  ADS  Article  Google Scholar 

  23. 23

    Deshpande, A., Bao, W., Miao, F., Lau, C. & LeRoy, B. Spatially resolved spectroscopy of monolayer graphene on SiO2 . Phys. Rev. B 79, 205411 (2009).

    ADS  Article  Google Scholar 

  24. 24

    Gibertini, M., Tomadin, A., Guinea, F., Katsnelson, M. I. & Polini, M. Electron-hole puddles in the absence of charged impurities. Phys. Rev. B 85, 201405 (2012).

    ADS  Article  Google Scholar 

  25. 25

    Cho, S. et al. Thermoelectric imaging of structural disorder in epitaxial graphene. Nat. Mater. 12, 913–918 (2013).

    CAS  ADS  Article  Google Scholar 

  26. 26

    Fei, Z. et al. Electronic and plasmonic phenomena at graphene grain boundaries. Nat. Nanotech. 8, 821–825 (2013).

    CAS  ADS  Article  Google Scholar 

  27. 27

    Ferrari, A. C. & Basko, D. M. Raman spectroscopy as a versatile tool for studying the properties of graphene. Nat. Nanotech. 8, 235–246 (2013).

    CAS  ADS  Article  Google Scholar 

  28. 28

    Hsu, J. W. P., Fitzgerald, E. A., Xie, Y. H. & Silverman, P. J. Near-field scanning optical microscopy imaging of individual threading dislocations on relaxed GexSi1-x films. Appl. Phys. Lett. 65, 344–346 (1994).

    CAS  ADS  Article  Google Scholar 

  29. 29

    Buratto, S. K. et al. Imaging InGaAsP quantum-well lasers using near-field scanning optical microscopy. J. Appl. Phys. 76, 7720 (1994).

    CAS  ADS  Article  Google Scholar 

  30. 30

    Goldberg, B. B., Ünlü, M. S., Herzog, W. D., Ghaemi, H. F. & Towe, E. Near-field optical studies of semiconductor heterostructures and laser diodes. IEEE J. Sel. Top. Quantum Electron. 1, 1073–1081 (1995).

    CAS  ADS  Article  Google Scholar 

  31. 31

    Richter, A., Tomm, J. W., Lienau, C. & Luft, J. Optical near-field photocurrent spectroscopy: A new technique for analyzing microscopic aging processes in optoelectronic devices. Appl. Phys. Lett. 69, 3981 (1996).

    CAS  ADS  Article  Google Scholar 

  32. 32

    McNeill, C. R. et al. Direct photocurrent mapping of organic solar cells using a near-field scanning optical microscope. Nano Lett. 4, 219–223 (2004).

    CAS  ADS  Article  Google Scholar 

  33. 33

    Gu, Y. et al. Near-field scanning photocurrent microscopy of a nanowire photodetector. Appl. Phys. Lett. 87, 043111 (2005).

    ADS  Article  Google Scholar 

  34. 34

    Mueller, T., Xia, F., Freitag, M., Tsang, J. & Avouris, P. Role of contacts in graphene transistors: a scanning photocurrent study. Phys. Rev. B 79, 245430 (2009).

    ADS  Article  Google Scholar 

  35. 35

    Rauhut, N. et al. Antenna-enhanced photocurrent microscopy on single-walled carbon nanotubes at 30 nm resolution. ACS Nano 6, 6416–6421 (2012).

    CAS  Article  Google Scholar 

  36. 36

    Mauser, N. & Hartschuh, A. Tip-enhanced near-field optical microscopy. Chem. Soc. Rev. 43, 1248–1262 (2014).

    CAS  Article  Google Scholar 

  37. 37

    Mauser, N. et al. Antenna-enhanced optoelectronic probing of carbon nanotubes. Nano Lett. 14, 3773–3778 (2014).

    CAS  ADS  Article  Google Scholar 

  38. 38

    Grover, S., Dubey, S., Mathew, J. P. & Deshmukh, M. M. Limits on the bolometric response of graphene due to flicker noise. Appl. Phys. Lett. 106, 051113 (2015).

    ADS  Article  Google Scholar 

  39. 39

    Wang, L. et al. One-dimensional electrical contact to a two-dimensional material. Science 342, 614–617 (2013).

    CAS  ADS  Article  Google Scholar 

  40. 40

    Kretinin, A. V. et al. Electronic properties of graphene encapsulated with different two-dimensional atomic crystals. Nano Lett. 14, 3270–3276 (2014).

    CAS  ADS  Article  Google Scholar 

  41. 41

    Ju, L. et al. Photoinduced doping in heterostructures of graphene and boron nitride. Nat. Nanotech. 9, 348–352 (2014).

    CAS  ADS  Article  Google Scholar 

  42. 42

    Fei, Z. et al. Infrared nanoscopy of dirac plasmons at the graphene-SiO2 interface. Nano Lett. 11, 4701–4705 (2011).

    CAS  ADS  Article  Google Scholar 

  43. 43

    Keilmann, F. & Hillenbrand, R. Near-field microscopy by elastic light scattering from a tip. Phil. Trans. R Soc. A 362, 787–805 (2004).

    CAS  ADS  Article  Google Scholar 

  44. 44

    Lemme, M. C. et al. Gate-activated photoresponse in a graphene p-n junction. Nano Lett. 11, 4134–4137 (2011).

    CAS  ADS  Article  Google Scholar 

  45. 45

    Gabor, N. M. et al. Hot carrier-assisted intrinsic photoresponse in graphene. Science 334, 648–652 (2011).

    CAS  ADS  Article  Google Scholar 

  46. 46

    Song, J. C. W., Rudner, M. S., Marcus, C. M. & Levitov, L. S. Hot carrier transport and photocurrent response in graphene. Nano Lett. 11, 4688–4692 (2011).

    CAS  ADS  Article  Google Scholar 

  47. 47

    Tielrooij, K. J. et al. Hot-carrier photocurrent effects at graphene’ metal interfaces. J. Phys. Condens. Matter 27, 164207 (2015).

    CAS  ADS  Article  Google Scholar 

  48. 48

    Badioli, M. et al. Phonon-mediated mid-infrared photoresponse of graphene. Nano Lett. 14, 6374–6381 (2014).

    CAS  ADS  Article  Google Scholar 

  49. 49

    Song, J. C. W. & Levitov, L. S. Shockley-Ramo theorem and long-range photocurrent response in gapless materials. Phys. Rev. B 90, 075415 (2014).

    ADS  Article  Google Scholar 

  50. 50

    Tsen, A. W. et al. Tailoring electrical transport across grain boundaries in polycrystalline graphene. Science 336, 1143–1146 (2012).

    CAS  ADS  Article  Google Scholar 

  51. 51

    Van Tuan, D. et al. Scaling properties of charge transport in polycrystalline graphene. Nano Lett. 13, 1730–1735 (2013).

    CAS  ADS  Article  Google Scholar 

  52. 52

    Zuev, Y., Chang, W. & Kim, P. Thermoelectric and magnetothermoelectric transport measurements of graphene. Phys. Rev. Lett. 102, 096807 (2009).

    ADS  Article  Google Scholar 

  53. 53

    Wei, P., Bao, W., Pu, Y., Lau, C. N. & Shi, J. Anomalous thermoelectric transport of dirac particles in graphene. Phys. Rev. Lett. 102, 166808 (2009).

    ADS  Article  Google Scholar 

  54. 54

    Cummings, A. W. et al. Charge transport in polycrystalline graphene: challenges and opportunities. Adv. Mater. 26, 5079–5094 (2014).

    CAS  Article  Google Scholar 

  55. 55

    Lee, E. J. H., Balasubramanian, K., Weitz, R. T., Burghard, M. & Kern, K. Contact and edge effects in graphene devices. Nat. Nanotech. 3, 486–490 (2008).

    CAS  ADS  Article  Google Scholar 

  56. 56

    Ben Shalom, M. et al. Quantum oscillations of the critical current and high-field superconducting proximity in ballistic graphene. Nat. Phys. doi:10.1038/nphys3592 (2015).

  57. 57

    Allen, M. T. et al. Spatially resolved edge currents and guided-wave electronic states in graphene. Nat. Phys. 12, 128–133 (2016).

    CAS  Article  Google Scholar 

  58. 58

    Chen, S. Y., Ho, P. H., Shiue, R. J., Chen, C. W. & Wang, W. H. Transport/magnetotransport of high-performance graphene transistors on organic molecule-functionalized substrates. Nano Lett. 12, 964–969 (2012).

    CAS  ADS  Article  Google Scholar 

Download references


We thank Stijn Goossens, Klaas-Jan Tielrooij and Misha Fogler for many fruitful discussions and Fabien Vialla for the assistance in rendering the graphics in Fig. 1a. Open source software was used (,, F.H.L.K. acknowledges financial support from the Spanish Ministry of Economy and Competitiveness, through the ‘Severo Ochoa’ Programme for Centres of Excellence in R&D (SEV-2015-0522), support by Fundacio Cellex Barcelona, the ERC Career integration grant (294056, GRANOP), the ERC starting grant (307806, CarbonLight), the Government of Catalonia trough the SGR grant (2014-SGR-1535), the Mineco grants Ramón y Cajal (RYC-2012-12281) and Plan Nacional (FIS2013-47161-P), and project GRASP (FP7-ICT-2013-613024-GRASP). F.H.L.K. and R.H. acknowledge support by the E.C. (European Commission) under Graphene Flagship (contract no. CNECT-ICT-604391). D.J. acknowledges support from the Ramón y Cajal Fellowship Program. Y.G. and J.H. acknowledge support from the US Office of Naval Research N00014-13-1-0662. We acknowledge financial support from the Spanish Ministry of Economy and Competitiveness and ‘Fondo Europeo de Desarrollo Regional’ through Grant TEC2013-46168-R. Q.M. and P.J.-H. have been supported by AFOSR Grant No. FA9550-11-1-0225 and the Packard Fellowship program. This work made use of the Materials Research Science and Engineering Center Shared Experimental Facilities supported by the National Science Foundation (NSF) (Grant No. DMR-0819762) and of Harvard’s Center for Nanoscale Systems, supported by the NSF (Grant No. ECS-0335765). S.R. acknowledges the Spanish Ministry of Economy and Competitiveness for funding (MAT2012-33911), the Secretaria de Universidades e Investigacion del Departamento de Economia y Conocimiento de la Generalidad de Catalunya and the Severo Ochoa Program (MINECO SEV-2013-0295). J.E.B.-V. acknowledges support from SECITI (Mexico, D.F.).

Author information




A.W. performed the experiments, analysed the data and wrote the manuscript. P.A.-G. helped with measurements, interpretation and discussion of the results. M.B.L. helped with data analysis, measurements, interpretation, discussion of the results and manuscript writing. Y.G. fabricated the h-BN/graphene/h-BN devices. G.N. and D.J. fabricated the CVD graphene devices. Q.M. fabricated the exfoliated graphene devices. K.W. and T.T. synthesized the h-BN. J.E.B.-V., A.W.C. and S.R. performed the simulations of the Seebeck coefficient at grain boundaries. R.H. and F.H.L.K. supervised the work, discussed the results and co-wrote the manuscript. All authors contributed to the scientific discussion and manuscript revisions.

Corresponding author

Correspondence to Frank H. L. Koppens.

Ethics declarations

Competing interests

R.H. is co-founder of Neaspec GmbH, a company producing scattering-type scanning near-field optical microscope systems such as the ones used in this study. All other authors declare no competing financial interests.

Supplementary information

Supplementary Information

Supplementary Figures 1-10, Supplementary Notes 1-2 and Supplementary References (PDF 3017 kb)

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Woessner, A., Alonso-González, P., Lundeberg, M. et al. Near-field photocurrent nanoscopy on bare and encapsulated graphene. Nat Commun 7, 10783 (2016).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing