Metal halide perovskites are of great interest for various high-performance optoelectronic applications1. The ability to tune the perovskite bandgap continuously by modifying the chemical composition opens up applications for perovskites as coloured emitters, in building-integrated photovoltaics, and as components of tandem photovoltaics to increase the power conversion efficiency2,3,4. Nevertheless, performance is limited by non-radiative losses, with luminescence yields in state-of-the-art perovskite solar cells still far from 100 per cent under standard solar illumination conditions5,6,7. Furthermore, in mixed halide perovskite systems designed for continuous bandgap tunability2 (bandgaps of approximately 1.7 to 1.9 electronvolts), photoinduced ion segregation leads to bandgap instabilities8,9. Here we demonstrate substantial mitigation of both non-radiative losses and photoinduced ion migration in perovskite films and interfaces by decorating the surfaces and grain boundaries with passivating potassium halide layers. We demonstrate external photoluminescence quantum yields of 66 per cent, which translate to internal yields that exceed 95 per cent. The high luminescence yields are achieved while maintaining high mobilities of more than 40 square centimetres per volt per second, providing the elusive combination of both high luminescence and excellent charge transport10. When interfaced with electrodes in a solar cell device stack, the external luminescence yield—a quantity that must be maximized to obtain high efficiency—remains as high as 15 per cent, indicating very clean interfaces. We also demonstrate the inhibition of transient photoinduced ion-migration processes across a wide range of mixed halide perovskite bandgaps in materials that exhibit bandgap instabilities when unpassivated. We validate these results in fully operating solar cells. Our work represents an important advance in the construction of tunable metal halide perovskite films and interfaces that can approach the efficiency limits in tandem solar cells, coloured-light-emitting diodes and other optoelectronic applications.

Access optionsAccess options

Rent or Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.


  1. 1.

    & Metal-halide perovskites for photovoltaic and light-emitting devices. Nat. Nanotechnol. 10, 391–402 (2015)

  2. 2.

    et al. Perovskite–perovskite tandem photovoltaics with optimized band gaps. Science 354, 861–865 (2016)

  3. 3.

    et al. A mixed-cation lead mixed-halide perovskite absorber for tandem solar cells. Science 351, 151–155 (2016)

  4. 4.

    et al. 23.6%-efficient monolithic perovskite/silicon tandem solar cells with improved stability. Nat. Energy 2, 17009 (2017)

  5. 5.

    et al. Incorporation of rubidium cations into perovskite solar cells improves photovoltaic performance. Science 354, 206–209 (2016)

  6. 6.

    et al. Efficient vacuum deposited p-i-n and n-i-p perovskite solar cells employing doped charge transport layers. Energy Environ. Sci. 9, 3456–3463 (2016)

  7. 7.

    Nonradiative losses in metal halide perovskites. ACS Energy Lett. 2, 1515–1525 (2017)

  8. 8.

    et al. Reversible photo-induced trap formation in mixed-halide hybrid perovskites for photovoltaics. Chem. Sci. 6, 613–617 (2015)

  9. 9.

    et al. Defect-assisted photoinduced halide segregation in mixed-halide perovskite thin films. ACS Energy Lett. 2, 1416–1424 (2017)

  10. 10.

    , , & Correlation between photoluminescence and carrier transport and a simple in situ passivation method for high-bandgap hybrid perovskites. J. Phys. Chem. Lett. 8, 3289–3298 (2017)

  11. 11.

    et al. Cesium-containing triple cation perovskite solar cells: improved stability, reproducibility and high efficiency. Energy Environ. Sci. 9, 1989–1997 (2016)

  12. 12.

    , & Strong internal and external luminescence as solar cells approach the Shockley–Queisser limit. IEEE J. Photovoltaics 2, 303–311 (2012)

  13. 13.

    et al. Recombination kinetics in organic–inorganic perovskites: excitons, free charge, and subgap states. Phys. Rev. Appl. 2, 034007 (2014)

  14. 14.

    , , & The role of intrinsic defects in methylammonium lead iodide perovskite. J. Phys. Chem. Lett. 5, 1312–1317 (2014)

  15. 15.

    , , & Strong covalency-induced recombination centers in perovskite solar cell material CH3NH3PbI3. J. Am. Chem. Soc. 136, 14570–14575 (2014)

  16. 16.

    et al. Enhancing photoluminescence yields in lead halide perovskites by photon recycling and light out-coupling. Nat. Commun. 7, 13941 (2016)

  17. 17.

    et al. High photoluminescence efficiency and optically pumped lasing in solution-processed mixed halide perovskite semiconductors. J. Phys. Chem. Lett. 5, 1421–1426 (2014)

  18. 18.

    et al. Direct–indirect character of the bandgap in methylammonium lead iodide perovskite. Nat. Mater. 16, 115–120 (2017)

  19. 19.

    , , , & Rumbles, G. Grain-size-limited mobility in methylammonium lead iodide perovskite thin films. ACS Energy Lett. 1, 561–565 (2016)

  20. 20.

    et al. Photo-induced halide redistribution in organic–inorganic perovskite films. Nat. Commun. 7, 11683 (2016)

  21. 21.

    , & Nonnegative matrix factorization for spectral data analysis. Linear Algebra Appl. 416, 29–47 (2006)

  22. 22.

    et al. Impact of monovalent cation halide additives on the structural and optoelectronic properties of CH3NH3PbI3 perovskite. Adv. Energy Mater. 6, 1502472 (2016)

  23. 23.

    et al. Hysteresis-free perovskite solar cells made of potassium-doped organometal halide perovskite. Sci. Rep. 7, 12183 (2017)

  24. 24.

    et al. Improved carriers injection capacity in perovskite solar cells by introducing A-site interstitial defects. J. Mater. Chem. A 5, 7905–7911 (2017)

  25. 25.

    et al. Potassium incorporation for enhanced performance and stability of fully inorganic cesium lead halide perovskite solar cells. Nano Lett. 17, 2028–2033 (2017)

  26. 26.

    et al. Phase segregation in Cs-, Rb- and K-doped mixed-cation (MA)x(FA)1−xPbI3 hybrid perovskites from solid-state NMR. J. Am. Chem. Soc. 139, 14173–14180 (2017)

  27. 27.

    et al. Understanding the impact of bromide on the photovoltaic performance of CH3NH3PbI3 solar cells. Adv. Mater. 27, 7221–7228 (2015)

  28. 28.

    et al. High photoluminescence quantum yield in band gap tunable bromide containing mixed halide perovskites. Nano Lett. 16, 800–806 (2016)

  29. 29.

    et al. Electron–hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 342, 341–344 (2013)

  30. 30.

    & The opto-electronics which broke the efficiency record in solar cells. In Proc. Conference on Lasers and Electro-Optics 2012 CF2J.1 (Optical Society of America, 2012)

  31. 31.

    et al. Photon recycling in lead iodide perovskite solar cells. Science 351, 1430–1433 (2016)

  32. 32.

    et al. Impact of a mesoporous titania–perovskite interface on the performance of hybrid organic–inorganic perovskite solar cells. J. Phys. Chem. Lett. 7, 3264–3269 (2016)

  33. 33.

    , & An improved experimental determination of external photoluminescence quantum efficiency. Adv. Mater. 9, 230–232 (1997)

  34. 34.

    et al. Chemical engineering of methylammonium lead iodide/bromide perovskites: tuning of opto-electronic properties and photovoltaic performance. J. Mater. Chem. A 3, 21760–21771 (2015)

  35. 35.

    , , & Charge carriers in planar and meso-structured organic–inorganic perovskites: mobilities, lifetimes, and concentrations of trap states. J. Phys. Chem. Lett. 6, 3082–3090 (2015)

  36. 36.

    et al. Chemical distribution of multiple cation (Rb+, Cs+, MA+, and FA+) perovskite materials by photoelectron spectroscopy. Chem. Mater. 29, 3589–3596 (2017)

Download references


M.A.-J. thanks Nava Technology Limited and Nyak Technology Limited for their funding and technical support. Z.A.-G. acknowledges funding from a Winton Studentship, and ICON Studentship from the Lloyd’s Register Foundation. This project has received funding from the European Union’s Seventh Framework Programme (FP7/2007-2013) under REA grant agreement number PIOF-GA-2013-622630, the European Research Council (ERC) under the European Union’s Horizon 2020 research and innovation programme (grant agreement number 756962), and the Royal Society and Tata Group (UF150033). We thank the Engineering and Physical Sciences Research Council (EPSRC) for support. XMaS is a mid-range facility at the European Synchrotron Radiation Facility supported by the EPSRC and we are grateful to the XMaS beamline team staff for their support. We thank Diamond Light Source for access to beamline I09 and staff member T.-L. Lee as well as U. Cappel for assistance during the HAXPES measurements. S.C., C.D. and G.D. acknowledge funding from the ERC under grant number 25961976 PHOTO EM and financial support from the European Union under grant number 77 312483 ESTEEM2. M.A. thanks the president of the UAE’s Distinguished Student Scholarship Program, granted by the Ministry of Presidential Affairs. H.R. and B.P. acknowledge support from the Swedish research council (2014-6019) and the Swedish foundation for strategic research. E.M.H. and T.J.S. were supported by the Netherlands Organization for Scientific Research under the Echo grant number 712.014.007.

Author information


  1. Cavendish Laboratory, Department of Physics, University of Cambridge, JJ Thomson Avenue, Cambridge CB3 0HE, UK

    • Mojtaba Abdi-Jalebi
    • , Zahra Andaji-Garmaroudi
    • , Camille Stavrakas
    • , Johannes M. Richter
    • , Mejd Alsari
    • , Edward P. Booker
    • , Andrew J. Pearson
    • , Richard H. Friend
    •  & Samuel D. Stranks
  2. Department of Materials Science and Metallurgy, University of Cambridge, 27 Charles Babbage Road, Cambridge CB3 0FS, UK

    • Stefania Cacovich
    • , Giorgio Divitini
    •  & Caterina Ducati
  3. Department of Physics and Astronomy, Uppsala University, Box 516, 75120 Uppsala, Sweden

    • Bertrand Philippe
    •  & Håkan Rensmo
  4. Department of Chemical Engineering, Delft University of Technology, van der Maasweg 9, 2629 HZ Delft, The Netherlands

    • Eline M. Hutter
    •  & Tom J. Savenije
  5. Department of Physics and Astronomy, University of Sheffield, Sheffield S3 7RH, UK

    • Samuele Lilliu
  6. The UAE Centre for Crystallography, United Arab Emirates

    • Samuele Lilliu


  1. Search for Mojtaba Abdi-Jalebi in:

  2. Search for Zahra Andaji-Garmaroudi in:

  3. Search for Stefania Cacovich in:

  4. Search for Camille Stavrakas in:

  5. Search for Bertrand Philippe in:

  6. Search for Johannes M. Richter in:

  7. Search for Mejd Alsari in:

  8. Search for Edward P. Booker in:

  9. Search for Eline M. Hutter in:

  10. Search for Andrew J. Pearson in:

  11. Search for Samuele Lilliu in:

  12. Search for Tom J. Savenije in:

  13. Search for Håkan Rensmo in:

  14. Search for Giorgio Divitini in:

  15. Search for Caterina Ducati in:

  16. Search for Richard H. Friend in:

  17. Search for Samuel D. Stranks in:


M.A.-J. and S.D.S. conceived and planned the experiments with additional input from R.H.F. M.A.-J. fabricated all samples and devices and performed and analysed the PLQE experiments, the photoluminescence stability experiments, the time-resolved photoluminescence, absorption and photothermal deflection spectroscopies, the SEM and the device characterisation measurements. M.A.-J., Z.A.-G. and C.S. obtained and analysed the confocal photoluminescence maps. S.C., G.D. and C.D. performed and analysed the STEM–EDX measurements. M.A. and S.L. performed the GIWAXS experiments and analysed the data. E.M.H. and T.J.S. performed the TRMC measurements and analysed the data. M.A.-J., B.P. and H.R. performed and analysed HAXPES measurements. M.A.-J. and E.P.B. performed X-ray diffraction measurements and J.M.R. calculated the internal PLQE and assisted with time-resolved photoluminescence measurement and analysis. M.A.-J. and A.J.P. carried out the device stability tests. M.A.-J. and S.D.S. took the lead in drafting the manuscript and compiled the figures. All authors discussed the results and provided feedback on the manuscript.

Competing interests

The authors declare no competing financial interests.

Corresponding author

Correspondence to Samuel D. Stranks.

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data

About this article

Publication history







By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.