Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Centimetre-scale electron diffusion in photoactive organic heterostructures


The unique properties of organic semiconductors, such as flexibility and lightness, are increasingly important for information displays, lighting and energy generation. But organics suffer from both static and dynamic disorder, and this can lead to variable-range carrier hopping1,2, which results in notoriously poor electrical properties, with low electron and hole mobilities and correspondingly short charge-diffusion lengths of less than a micrometre3,4. Here we demonstrate a photoactive (light-responsive) organic heterostructure comprising a thin fullerene channel sandwiched between an electron-blocking layer and a blended donor:C70 fullerene heterojunction that generates charges by dissociating excitons. Centimetre-scale diffusion of electrons is observed in the fullerene channel, and this can be fitted with a simple electron diffusion model. Our experiments enable the direct measurement of charge diffusivity in organic semiconductors, which is as high as 0.83 ± 0.07 square centimetres per second in a C60 channel at room temperature. The high diffusivity of the fullerene combined with the extraordinarily long charge-recombination time yields diffusion lengths of more than 3.5 centimetres, orders of magnitude larger than expected for an organic system.

This is a preview of subscription content, access via your institution

Relevant articles

Open Access articles citing this article.

Access options

Rent or buy this article

Get just this article for as long as you need it


Prices may be subject to local taxes which are calculated during checkout

Figure 1: Device structure, experimental set-up and distance-dependent photocurrent.
Figure 2: Energetics of materials used in devices.
Figure 3: Temperature dependence of channel currents.


  1. Coropceanu, V. et al. Charge transport in organic semiconductors. Chem. Rev. 107, 926–952 (2007)

    Article  CAS  Google Scholar 

  2. Bässler, H. Charge transport in disordered organic photoconductors. Phys. Status Solidi B 175, 15–56 (1993)

    Article  ADS  Google Scholar 

  3. Sarkar, D. & Halas, N. J. Dember effect in C60 thin films. Solid State Commun. 90, 261–265 (1994)

    Article  ADS  CAS  Google Scholar 

  4. Tripathi, A. K., Tripathi, D. C. & Mohapatra, Y. N. Simultaneous and direct measurement of carrier diffusion constant and mobility in organic semiconductors and deviation from standard Einstein relation. Phys. Rev. B 84, 041201 (2011)

    Article  ADS  Google Scholar 

  5. Xue, J., Rand, B. P., Uchida, S. & Forrest, S. R. A hybrid planar-mixed molecular heterojunction photovoltaic cell. Adv. Mater. 17, 66–71 (2005)

    Article  CAS  Google Scholar 

  6. Xiao, X., Bergemann, K. J., Zimmerman, J. D., Lee, K. & Forrest, S. R. Small-molecule planar-mixed heterojunction photovoltaic cells with fullerene-based electron filtering buffers. Adv. Energy Mater. 4, 1301557 (2014)

    Article  Google Scholar 

  7. Griffith, O. L. et al. Charge transport and exciton dissociation in organic solar cells consisting of dipolar donors mixed with C70 . Phys. Rev. B 92, 085404 (2015)

    Article  ADS  Google Scholar 

  8. Ting, H. C. et al. Benzochalcogenodiazole-based donor–acceptor–acceptor molecular donors for organic solar cells. ChemSusChem 7, 457–465 (2014)

    Article  CAS  Google Scholar 

  9. Cheyns, D., Kim, M., Verreet, B. & Rand, B. P. Accurate spectral response measurements of a complementary absorbing organic tandem cell with fill factor exceeding the subcells. Appl. Phys. Lett. 104, 093302 (2014)

    Article  ADS  Google Scholar 

  10. Nunomura, S., Che, X. & Forrest, S. R. Charge trapping in mixed organic donor–acceptor semiconductor thin films. Adv. Mater. 26, 7555–7560 (2014)

    Article  CAS  Google Scholar 

  11. Itaka, K. et al. High-mobility C60 field-effect transistors fabricated on molecular-wetting controlled substrates. Adv. Mater. 18, 1713–1716 (2006)

    Article  CAS  Google Scholar 

  12. Anthopoulos, T. D. et al. High performance n-channel organic field-effect transistors and ring oscillators based on C60 fullerene films. Appl. Phys. Lett. 89, 213504 (2006)

    Article  ADS  Google Scholar 

  13. Kwiatkowski, J. J., Frost, J. M. & Nelson, J. The effect of morphology on electron field-effect mobility in disordered C60 thin films. Nano Lett. 9, 1085–1090 (2009)

    Article  ADS  CAS  Google Scholar 

  14. Liu, X., Ding, K., Panda, A. & Forrest, S. R. Charge transfer states in dilute donor–acceptor blend organic heterojunctions. ACS Nano 10, 7619–7626 (2016)

    Article  CAS  Google Scholar 

  15. Bürgi, L., Friend, R. H. & Sirringhaus, H. Formation of the accumulation layer in polymer field-effect transistors. Appl. Phys. Lett. 82, 1482–1484 (2003)

    Article  ADS  Google Scholar 

  16. Jarrett, C. P., Pichler, K., Newbould, R. & Friend, R. H. Transport studies in C60 and C60/C70 thin films using metal–insulator–semiconductor field-effect transistors. Synth. Met. 77, 35–38 (1996)

    Article  CAS  Google Scholar 

  17. Haddon, R. C. C70 thin film transistors. J. Am. Ceram. Soc. 118, 3041–3042 (1996)

    CAS  Google Scholar 

  18. Roichman, Y. & Tessler, N. Generalized Einstein relation for disordered semiconductors—implications for device performance. Appl. Phys. Lett. 80, 1948–1950 (2002)

    Article  ADS  CAS  Google Scholar 

  19. Sakanoue, T. & Sirringhaus, H. Band-like temperature dependence of mobility in a solution-processed organic semiconductor. Nat. Mater. 9, 736–740 (2010)

    Article  ADS  CAS  Google Scholar 

  20. Jurchescu, O. D., Popinciuc, M., Van Wees, B. J. & Palstra, T. T. M. Interface-controlled, high-mobility organic transistors. Adv. Mater. 19, 688–692 (2007)

    Article  CAS  Google Scholar 

  21. Leijtens, T., Lim, J., Teuscher, J., Park, T. & Snaith, H. J. Charge density dependent mobility of organic hole-transporters and mesoporous TiO2 determined by transient mobility spectroscopy: implications to dye-sensitized and organic solar cells. Adv. Mater. 25, 3227–3233 (2013)

    Article  CAS  Google Scholar 

  22. Tummala, N. R., Zheng, Z., Aziz, S. G., Coropceanu, V. & Brédas, J.-L. Static and dynamic energetic disorders in the C60, PC61BM, C70, and PC71BM fullerenes. J. Phys. Chem. Lett. 6, 3657–3662 (2015)

    Article  CAS  Google Scholar 

  23. Torricelli, F., Colalongo, L., Raiteri, D., Kovács-Vajna, Z. M. & Cantatore, E. Ultra-high gain diffusion-driven organic transistor. Nat. Commun. 7, 10550 (2016)

    Article  ADS  CAS  Google Scholar 

  24. Kim, M. et al. Lateral organic solar cells with self-assembled semiconductor nanowires. Adv. Energy Mater. 5, 1401317 (2015)

    Article  Google Scholar 

  25. Wang, N. et al. Snow cleaning of substrates increases yield of large-area organic photovoltaics. Appl. Phys. Lett. 101, 133901 (2012)

    Article  ADS  Google Scholar 

  26. Burlingame, Q. et al. Reliability of small molecule organic photovoltaics with electron-filtering compound buffer layers. Adv. Energy Mater. 6, 1601094 (2016)

    Article  Google Scholar 

  27. Olthof, S. et al. Ultralow doping in organic semiconductors: evidence of trap filling. Phys. Rev. Lett. 109, 176601 (2012)

    Article  ADS  Google Scholar 

Download references


This work was supported by the United States Department of Energy SunShot Program under awards DE-EE0006708 and DE-EE0005310, and the Air Force Office of Scientific Research under award FA9550-14-1-0245. We thank M. Ware for discussions regarding numerical simulations.

Author information

Authors and Affiliations



Q.B. fabricated all samples, performed all measurements, and assisted with data fitting and analysis. C.C. assisted with current measurements, formulated theory, and performed simulations and data analysis. X.C. analysed mismatch in organic photovoltaic devices between over- and under-filled device illumination measurements. A.P. assisted with ultraviolet photoelectron spectral measurement of film energy levels. Y.Q. calculated lateral electric field strength in the channel. S.R.F. supervised the project and analysed data. Q.B., C.C. and S.R.F. wrote the manuscript together.

Corresponding author

Correspondence to Stephen R. Forrest.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Additional information

Reviewer Information Nature thanks N. Banerji and the other anonymous reviewer(s) for their contribution to the peer review of this work.

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Figure 1 Impact of channel disruption on channel currents.

Room-temperature transient currents were measured on a DTDCTB-(10 nm C60)-mixed device at L = 3 mm before and after a series of razor blade cuts was made to the organic layers, as shown in the inset. The peak height of the current pulse was greatly reduced and the peak arrival time was delayed for devices with a ‘partial cut’ that was transverse to, and spanned the width of, the ITO anode between the illumination position and the silver cathode, compared with the pristine, uncut device. Charge-diffusion simulations were performed for both geometries, where the only difference was a blocking boundary condition at the position of the partial cut. We find that charge diffusion around the cut accounts for the differences between the cut and uncut device transients, as demonstrated by the agreement between fits (lines) and the data. The partial cut was also extended such that there was no continuous organic path between the illumination position and the cathode (a ‘full cut’ device). This eliminated the response except for a residual current at time t < 200 ms arising from scattered light absorbed in the organic layers between the cathode and cut. This effect was observed in all devices exhibiting channel currents.

Extended Data Figure 2 Electron diffusion in an electrical injection device.

a, A device was fabricated to characterize charge diffusion in an electron-only electrically injected channel, with the structure shown here. Charges were injected into the C60 channel by applying a 50 V pulse between the injecting contact and the silicon substrate for 5 s. b, The transient current collected at the buried contact. A steady-state current of 0.56 μA is observed approximately 3 s after the start of the pulse, with an exponential decay time of about 400 ms. A simulation of the turn-off transient using the same optically measured parameters for D and k in Table 1 for the DTDCPB-(10 nm C60)-neat device is also shown in b (solid line). The small deviations of the fits to the electrical data are probably due to slow de-trapping of charges in the BPhen and SiO2 that are injected during the 50 V pulse. Inset, photograph of the device with 1 cm scale bar.

PowerPoint slides

Rights and permissions

Reprints and Permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Burlingame, Q., Coburn, C., Che, X. et al. Centimetre-scale electron diffusion in photoactive organic heterostructures. Nature 554, 77–80 (2018).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing