Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Metallic molybdenum disulfide nanosheet-based electrochemical actuators


Actuators that convert electrical energy to mechanical energy are useful in a wide variety of electromechanical systems and in robotics1,2,3,4,5,6, with applications such as steerable catheters7, adaptive wings for aircraft and drag-reducing wind turbines8. Actuation systems can be based on various stimuli, such as heat, solvent adsorption/desorption4,9, or electrochemical action (in systems such as carbon nanotube electrodes1,10, graphite electrodes11, polymer electrodes6,12,13,14 and metals15). Here we demonstrate that the dynamic expansion and contraction of electrode films formed by restacking chemically exfoliated nanosheets of two-dimensional metallic molybdenum disulfide (MoS2) on thin plastic substrates can generate substantial mechanical forces. These films are capable of lifting masses that are more than 150 times that of the electrode over several millimetres and for hundreds of cycles. Specifically, the MoS2 films are able to generate mechanical stresses of about 17 megapascals—higher than mammalian muscle (about 0.3 megapascals)3 and comparable to ceramic piezoelectric actuators (about 40 megapascals)—and strains of about 0.6 per cent, operating at frequencies up to 1 hertz. The actuation performance is attributed to the high electrical conductivity of the metallic 1T phase of MoS2 nanosheets, the elastic modulus of restacked MoS2 layers (2 to 4 gigapascals) and fast proton diffusion between the nanosheets. These results could lead to new electrochemical actuators for high-strain and high-frequency applications.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Figure 1: Experimental set-up for actuation measurements.
Figure 2: Measurements of strain and in-plane modulus using the beam bending model.
Figure 3: Inverted-series-connected (ISC) bimorph actuation device based on metallic MoS2 nanosheet electrodes.

Similar content being viewed by others


  1. Baughman, R. H. Carbon nanotube actuators. Science 284, 1340–1344 (1999)

    Article  CAS  ADS  Google Scholar 

  2. Zhang, Q. M. Giant electrostriction and relaxor ferroelectric behavior in electron-irradiated poly(vinylidene fluoride-trifluoroethylene) copolymer. Science 280, 2101–2104 (1998)

    Article  CAS  ADS  Google Scholar 

  3. Brochu, P. & Pei, Q. Advances in dielectric elastomers for actuators and artificial muscles. Macromol. Rapid Commun. 31, 10–36 (2010)

    Article  CAS  Google Scholar 

  4. Aliev, A. E. et al. Giant-stroke, superelastic carbon nanotube aerogel muscles. Science 323, 1575–1578 (2009)

    Article  CAS  ADS  Google Scholar 

  5. Biener, J. et al. Surface-chemistry-driven actuation in nanoporous gold. Nat. Mater. 8, 47–51 (2009)

    Article  CAS  ADS  Google Scholar 

  6. Bar-Cohen, Y. (ed.) Electroactive Polymer (EAP) Actuators as Artificial Muscles: Reality, Potential, and Challenges 2nd edn (SPIE, 2004)

  7. Mazzoldi, A. & De Rossi, D. Conductive-polymer-based structures for a steerable catheter. Proc. SPIE 3987, 273 (2000)

    Article  CAS  ADS  Google Scholar 

  8. Barbarino, S., Bilgen, O., Ajaj, R. M., Friswell, M. I. & Inman, D. J. A review of morphing aircraft. J. Intell. Mater. Syst. Struct. 22, 823–877 (2011)

    Article  Google Scholar 

  9. Ma, M., Guo, L., Anderson, D. G. & Langer, R. Bio-inspired polymer composite actuator and generator driven by water gradients. Science 339, 186–189 (2013)

    Article  CAS  ADS  Google Scholar 

  10. Yun, Y. et al. A multi-wall carbon nanotube tower electrochemical actuator. Nano Lett. 6, 689–693 (2006)

    Article  CAS  ADS  Google Scholar 

  11. Koyama, Y. et al. Harnessing the actuation potential of solid-state intercalation compounds. Adv. Funct. Mater. 16, 492–498 (2006)

    Article  CAS  Google Scholar 

  12. Lu, W. Use of ionic liquids for π-conjugated polymer electrochemical devices. Science 297, 983–987 (2002)

    Article  CAS  ADS  Google Scholar 

  13. Pei, Q. & Inganaes, O. Electrochemical applications of the bending beam method. 1. Mass transport and volume changes in polypyrrole during redox. J. Phys. Chem. 96, 10507–10514 (1992)

    Article  CAS  Google Scholar 

  14. Shahinpoor, M., Bar-Cohen, Y., Simpson, J. O. & Smith, J. Ionic polymer-metal composites (IPMCs) as biomimetic sensors, actuators and artificial muscles — a review. Smart Mater. Struct. 7, R15–R30 (1998)

    Article  CAS  ADS  Google Scholar 

  15. Jin, H.-J. et al. Nanoporous Au−Pt alloys as large strain electrochemical actuators. Nano Lett. 10, 187–194 (2010)

    Article  CAS  ADS  Google Scholar 

  16. Spinks, G. M., Mottaghitalab, V., Bahrami-Samani, M., Whitten, P. G. & Wallace, G. G. Carbon-nanotube-reinforced polyaniline fibers for high-strength artificial muscles. Adv. Mater. 18, 637–640 (2006)

    Article  CAS  Google Scholar 

  17. Cheng, C. & Ngan, A. H. W. Reversible electrochemical actuation of metallic nanohoneycombs induced by pseudocapacitive redox processes. ACS Nano 9, 3984–3995 (2015)

    Article  CAS  Google Scholar 

  18. Gu, G. et al. V2O5 nanofibre sheet actuators. Nat. Mater. 2, 316–319 (2003)

    Article  CAS  ADS  Google Scholar 

  19. Weissmuller, J. Charge-induced reversible strain in a metal. Science 300, 312–315 (2003)

    Article  CAS  ADS  Google Scholar 

  20. Chin, T. E., Rhyner, U., Koyama, Y., Hall, S. R. & Chiang, Y.-M. Lithium rechargeable batteries as electromechanical actuators. Electrochem. Solid-State Lett. 9, A134 (2006)

    Article  CAS  Google Scholar 

  21. Cooper, R. C. et al. Nonlinear elastic behavior of two-dimensional molybdenum disulfide. Phys. Rev. B 87, 035423 (2013)

    Article  ADS  Google Scholar 

  22. Come, J. et al. Controlling the actuation properties of MXene paper electrodes upon cation intercalation. Nano Energy 17, 27–35 (2015)

    Article  CAS  Google Scholar 

  23. Acerce, M., Voiry, D. & Chhowalla, M. Metallic 1T phase MoS2 nanosheets as supercapacitor electrode materials. Nat. Nanotechnol. 10, 313–318 (2015)

    Article  CAS  ADS  Google Scholar 

  24. Feng, P., Bu, X. & Zheng, N. The interface chemistry between chalcogenide clusters and open framework chalcogenides. Acc. Chem. Res. 38, 293–303 (2005)

    Article  CAS  Google Scholar 

  25. Du, P., Lin, X. & Zhang, X. A multilayer bending model for conducting polymer actuators. Sens. Actuators Phys. 163, 240–246 (2010)

    Article  CAS  Google Scholar 

  26. Come, J. et al. Nanoscale elastic changes in 2D Ti3C2Tx (MXene) pseudocapacitive electrodes. Adv. Energy Mater. 6, 1502290 (2016)

    Article  Google Scholar 

  27. Ge, Y. et al. A robust free-standing MoS2/poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) film for supercapacitor applications. Electrochim. Acta 235, 348–355 (2017)

    Article  CAS  Google Scholar 

  28. Jia, K., Pal, S. & Xie, H. An electrothermal tip-tilt-piston micromirror based on folded dual S-shaped bimorphs. J. Microelectromech. Syst. 18, 1004–1015 (2009)

    Article  CAS  Google Scholar 

  29. Otero, T. F., Cortes, M. T. & Boyano, I. Macroscopic devices and complex movements developed with artificial muscles. Proc. SPIE 4695, 395–402 (2002)

    Article  CAS  ADS  Google Scholar 

  30. Ham, R., Sugar, T., Vanderborght, B., Hollander, K. & Lefeber, D. Compliant actuator designs. IEEE Robot. Autom. Mag. 16, 81–94 (2009)

    Article  Google Scholar 

  31. Eda, G. et al. Photoluminescence from chemically exfoliated MoS2 . Nano Lett. 11, 5111–5116 (2011)

    Article  CAS  ADS  Google Scholar 

  32. Timoshenko, S. & Goodier, J. N. Theory of Elasticity (McGraw-Hill, 1951)

  33. Sokolnikoff, I. S. Mathematical Theory of Elasticity (McGraw-Hill, 1946)

  34. Klein, C. A. How accurate are Stoney’s equation and recent modifications. J. Appl. Phys. 88, 5487 (2000)

    Article  CAS  ADS  Google Scholar 

  35. Stoney, G. G. The tension of metallic films deposited by electrolysis. Proc. R. Soc. Lond. A 82, 172–175 (1909)

    Article  CAS  ADS  Google Scholar 

  36. Pelrine, R. High-speed electrically actuated elastomers with strain greater than 100%. Science 287, 836–839 (2000)

    Article  CAS  ADS  Google Scholar 

  37. Haines, C. S. et al. Artificial muscles from fishing line and sewing thread. Science 343, 868–872 (2014)

    Article  CAS  ADS  Google Scholar 

  38. Hara, S., Zama, T., Takashima, W. & Kaneto, K. Artificial muscles based on polypyrrole actuators with large strain and stress induced electrically. Polym. J. 36, 151–161 (2004)

    Article  CAS  Google Scholar 

  39. Foroughi, J. et al. Torsional carbon nanotube artificial muscles. Science 334, 494–497 (2011)

    Article  CAS  ADS  Google Scholar 

  40. Mirfakhrai, T. et al. Electrochemical actuation of carbon nanotube yarns. Smart Mater. Struct. 16, S243–S249 (2007)

    Article  CAS  Google Scholar 

  41. Xie, X., Bai, H., Shi, G. & Qu, L. Load-tolerant, highly strain-responsive graphene sheets. J. Mater. Chem. 21, 2057 (2011)

    Article  Google Scholar 

  42. Jiménez Sandoval, S., Yang, D., Frindt, R. & Irwin, J. Raman study and lattice dynamics of single molecular layers of MoS2 . Phys. Rev. B 44, 3955–3962 (1991)

    Article  ADS  Google Scholar 

  43. Calandra, M. Chemically exfoliated single-layer MoS2: stability, lattice dynamics, and catalytic adsorption from first principles. Phys. Rev. B 88, 245428 (2013)

    Article  ADS  Google Scholar 

Download references


M.A. acknowledges the Turkish Ministry of Education for a graduate fellowship. M.C. acknowledges support from NSF grant ECCS 1128335. E.K.A. acknowledges support from Rutgers MSE Department.

Author information

Authors and Affiliations



M.C. and M.A. conceived the idea and designed the experiments. M.A. synthesized the materials, carried out the electrochemical measurements, performed bending beam analyses and assisted E.K.A. with beam bending models. M.C. wrote the manuscript with assistance from M.A. and E.K.A. All authors discussed the results and commented on the manuscript.

Corresponding author

Correspondence to Manish Chhowalla.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Figure 1 Structural characterization of 1T phase MoS2 nanosheets.

a, b, High-resolution X-ray photoelectron spectrum from the Mo 3d region (a) and the S 2p region (b) of as-exfoliated 1T MoS2 film. Spectra from 1T and 2H phases are indicated as blue and red curves, respectively. c, 1T phase MoS2 has distinctive Raman peaks (J1, J2 and J3 peaks at 156 cm−1, 226 cm−1 and 333 cm−1, respectively) in addition to two main Raman modes—the in-plane mode , and the out-of-plane mode, A1g (refs 42, 43). The 1T phase of MoS2 was identified from the presence of , J1, J2 and J3 peaks. d, e, The MoS2 flake size analyses were conducted by counting the individual flakes in multiple SEM images (example in d). The size of the exfoliated monolayer MoS2 flakes varies from 50 nm to 700 nm; the average flake size is 226.5 nm with 109 nm standard deviation (e).

Extended Data Figure 2 Relationship between capacitance and curvature.

a, b, Current–voltage curves at different scan rates (see keys) for 1T phase MoS2 film electrodes. The similarity in behaviour at different scan rates indicates that charging and discharging can be done slowly or rapidly, allowing stable actuation at varying frequencies. SCE, standard calomel electrode. c, d, Variation of electrochemical actuation and capacitance with frequency. c, Curvature change (blue points) and capacitance (red points) as a function of frequency. d, Curvature versus capacitance (data points); the dashed line represents a linear fit at low scan rates. The deviation from this line represents the influence of drag forces from the liquid.

Extended Data Figure 3 Influence of electrochemical parameters on curvature.

a, Variation of electrochemical actuation and capacitance with applied potential. b, Curvature change induced by square wave potentials over different potential ranges. c, The curvature change induced by triangular wave potentials; the curvature response to triangular potentials at voltages from 0.1 V to 0.6 V is shown. d, Capacitance–voltage curves with expanding electrochemical potential window (key). e, Curvature as a function of electrochemical potential. f, Capacitance versus curvature change.

Extended Data Figure 4 Typical nanoindentation loading versus depth traces for 8-μm-thick MoS2 film.

The elastic modulus values (E) of dry, charged and discharged states of the film are shown. Results for the 3-μm-thick films were similar to those of the 8-μm-thick films.

Extended Data Figure 5 Photographs of the ISC actuator device at different states of induction.

a, b, The displacement of the ISC actuator (4.1 mm) under loading of 265 mg. cf, Also shown is the displacement (5.5 mm) via electrochemical induction (0.3 to −0.3 V) without the load (c, d), and the displacement (3.6 mm) via the same electrochemical induction with the load (265 mg; e, f).

Extended Data Figure 6 Diagrams showing beam-bending modelling of the actuation behaviour.

a, Schematic summarizing the bending behaviour of the 1T-MoS2-based bimorph actuator as a function of voltage polarity. b, Cantilever actuator configuration representing the mechanics of electrochemical actuation due to the diffusion flux (J) of intercalating species into the 1T MoS2 film of the bimorph structure under isothermal conditions. The constant temperature makes constant the diffusivity (D) of the intercalating species in 1T MoS2. Here, the ingress of the intercalating species is through all surfaces that are exposed to the liquid medium. The driving force for the ingress is the concentration gradient of the intercalating species (ξ) that is formed between the 1T MoS2–liquid interface and the interior of the 1T MoS2 film. c, Free body diagram of the bimorph showing the elastic (recoverable) strains developed in the 1T MoS2 film due to the intercalation process. The intercalating species cause the 1T MoS2 film to contract in the direction perpendicular to the normal surface of the film, resulting in a compressive out-of-plane strain ε. The compressive ε induces an in-plane expansion as represented by the tensile in-plane strain . The in-plane and out-of-plane strains are related via due to the plane state of stress32,33, where and E are the in-plane and out-of-plane elastic moduli, respectively. The () ratio represents the Poisson’s ratio. The normal in-plane strains are assumed to be isotropic, while the in-plane shear strain is presumed to be completely relieved: both these are a consequence of the in-plane rotation of 1T MoS2 nanosheets comprising the film being random around the normal axis, that is, the existence of mosaic structure. d, The resultant deformation of the cantilever bimorph actuator. The tensile in-plane strain in the 1T MoS2 film induces deformation in the substrate due to traction at the film–substrate interface, that is, clamping of the electrochemically active film by the substrate. The consequence is a tip displacement (Δz) of the bimorph actuator (the system) that does work on the surroundings (the inertial weight). The inverse bell-shaped bimorph actuator (see Extended Data Fig. 6) can be thought of as back-to-back bimorph cantilever actuators that are ‘welded’ at the tips where maximum (Δzmax) deflection occurs.

Extended Data Table 1 Literature survey of actuator performance

Supplementary information

Actuation of MoS2 film on Au film by electrochemical induction from 0 to +0.3V.

Video showing actuation of MoS2 film on Au film by electrochemical induction from 0 to +0.3V. (MP4 2631 kb)

Actuation of a Kapton beam via electrochemical charging and discharging of ions in MoS2 nanosheet electrodes.

The operating voltage varies from –0.3 V to +0.3 V. (MP4 7931 kb)

Video of ISC bimorph actuator lifting a 265 mg weight.

The MoS2 nanosheet thin film electrodes are seen as black coating on the Kapton actuator. The weight of MoS2 electrodes is 1.6 mg. (MP4 5598 kb)

PowerPoint slides

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Acerce, M., Akdoğan, E. & Chhowalla, M. Metallic molybdenum disulfide nanosheet-based electrochemical actuators. Nature 549, 370–373 (2017).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing