Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Reading and writing single-atom magnets


The single-atom bit represents the ultimate limit of the classical approach to high-density magnetic storage media. So far, the smallest individually addressable bistable magnetic bits have consisted of 3–12 atoms1,2,3. Long magnetic relaxation times have been demonstrated for single lanthanide atoms in molecular magnets4,5,6,7,8,9,10,11,12, for lanthanides diluted in bulk crystals13, and recently for ensembles of holmium (Ho) atoms supported on magnesium oxide (MgO)14. These experiments suggest a path towards data storage at the atomic limit, but the way in which individual magnetic centres are accessed remains unclear. Here we demonstrate the reading and writing of the magnetism of individual Ho atoms on MgO, and show that they independently retain their magnetic information over many hours. We read the Ho states using tunnel magnetoresistance15,16 and write the states with current pulses using a scanning tunnelling microscope. The magnetic origin of the long-lived states is confirmed by single-atom electron spin resonance17 on a nearby iron sensor atom, which also shows that Ho has a large out-of-plane moment of 10.1 ± 0.1 Bohr magnetons on this surface. To demonstrate independent reading and writing, we built an atomic-scale structure with two Ho bits, to which we write the four possible states and which we read out both magnetoresistively and remotely by electron spin resonance. The high magnetic stability combined with electrical reading and writing shows that single-atom magnetic memory is indeed possible.

This is a preview of subscription content, access via your institution

Relevant articles

Open Access articles citing this article.

Access options

Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Figure 1: Experimental set-up and magnetic switching of holmium.
Figure 2: Controlling and measuring the magnetic states of holmium.
Figure 3: Example of a stable two-bit atomic Ho array.


  1. Loth, S., Baumann, S., Lutz, C. P., Eigler, D. M. & Heinrich, A. J. Bistability in atomic-scale antiferromagnets. Science 335, 196–199 (2012)

    ADS  CAS  Article  Google Scholar 

  2. Khajetoorians, A. A. et al. Current-driven spin dynamics of artificially constructed quantum magnets. Science 339, 55–59 (2013)

    ADS  CAS  Article  Google Scholar 

  3. Steinbrecher, M. et al. Absence of a spin-signature from a single Ho adatom as probed by spin-sensitive tunneling. Nat. Commun. 7, 10454 (2016)

    ADS  CAS  Article  Google Scholar 

  4. Ishikawa, N., Sugita, M., Ishikawa, T., Koshihara, S.-Y. & Kaizu, Y. Lanthanide double-decker complexes functioning as magnets at the single-molecular level. J. Am. Chem. Soc. 125, 8694–8695 (2003)

    CAS  Article  Google Scholar 

  5. Bogani, L. & Wernsdorfer, W. Molecular spintronics using single-molecule magnets. Nat. Mater. 7, 179–186 (2008)

    ADS  CAS  Article  Google Scholar 

  6. Kyatskaya, S. et al. Anchoring of rare-earth-based single-molecule magnets on single-walled carbon nanotubes. J. Am. Chem. Soc. 131, 15143–15151 (2009)

    CAS  Article  Google Scholar 

  7. Rinehart, J. D. & Long, J. R. Exploiting single-ion anisotropy in the design of f-element single-molecule magnets. Chem. Sci. 2, 2078–2085 (2011)

    CAS  Article  Google Scholar 

  8. Gatteschi, D., Sessoli, R. & Villain, J. Molecular Nanomagnets (Oxford Univ. Press, 2011)

  9. Westerström, R. et al. An endohedral single-molecule magnet with long relaxation times: DySc2N@C80 . J. Am. Chem. Soc. 134, 9840–9843 (2012)

    Article  Google Scholar 

  10. Liddle, S. T. & van Slageren, J. Improving f-element single molecule magnets. Chem. Soc. Rev. 44, 6655–6669 (2015)

    CAS  Article  Google Scholar 

  11. Wäckerlin, C. et al. Giant hysteresis of single-molecule magnets adsorbed on a nonmagnetic insulator. Adv. Mater. 28, 5195–5199 (2016)

    Article  Google Scholar 

  12. Layfield, R. A. Organometallic single-molecule magnets. Organometallics 33, 1084–1099 (2014)

    CAS  Article  Google Scholar 

  13. Giraud, R., Wernsdorfer, W., Tkachuk, A. M., Mailly, D. & Barbara, B. Nuclear spin driven quantum relaxation in LiY0.998Ho0.002F4 . Phys. Rev. Lett. 87, 057203 (2001)

    ADS  CAS  Article  Google Scholar 

  14. Donati, F. et al. Magnetic remanence in single atoms. Science 352, 318–321 (2016)

    ADS  CAS  Article  Google Scholar 

  15. Wiesendanger, R. Spin mapping at the nanoscale and atomic scale. Rev. Mod. Phys. 81, 1495–1550 (2009)

    ADS  CAS  Article  Google Scholar 

  16. Loth, S., Lutz, C. P. & Heinrich, A. J. Spin-polarized spin excitation spectroscopy. New J. Phys. 12, 125021 (2010)

    ADS  Article  Google Scholar 

  17. Baumann, S. et al. Electron paramagnetic resonance of individual atoms on a surface. Science 350, 417–420 (2015)

    ADS  CAS  Article  Google Scholar 

  18. Gambardella, P. et al. Giant magnetic anisotropy of single cobalt atoms and nanoparticles. Science 300, 1130–1133 (2003)

    ADS  CAS  Article  Google Scholar 

  19. Khajetoorians, A. A. et al. Spin excitations of individual Fe atoms on Pt(111): impact of the site-dependent giant substrate polarization. Phys. Rev. Lett. 111, 157204 (2013)

    ADS  CAS  Article  Google Scholar 

  20. Donati, F. et al. Tailoring the magnetism of Co atoms on graphene through substrate hybridization. Phys. Rev. Lett. 113, 177201 (2014)

    ADS  CAS  Article  Google Scholar 

  21. Baumann, S. et al. Origin of perpendicular magnetic anisotropy and large orbital moment in Fe atoms on MgO. Phys. Rev. Lett. 115, 237202 (2015)

    ADS  CAS  Article  Google Scholar 

  22. Vincent, R., Klyatskaya, S., Ruben, M., Wernsdorfer, W. & Balestro, F. Electronic read-out of a single nuclear spin using a molecular spin transistor. Nature 488, 357–360 (2012)

    ADS  CAS  Article  Google Scholar 

  23. Paul, W. et al. Control of the millisecond spin lifetime of an electrically probed atom. Nat. Phys. (2016)

  24. Miyamachi, T. et al. Stabilizing the magnetic moment of single holmium atoms by symmetry. Nature 503, 242–246 (2013)

    ADS  CAS  Article  Google Scholar 

  25. Donati, F. et al. Magnetism of Ho and Er atoms on close-packed metal surfaces. Phys. Rev. Lett. 113, 237201 (2014)

    ADS  CAS  Article  Google Scholar 

  26. Khajetoorians, A. A. & Heinrich, A. J. Toward single-atom memory. Science 352, 296–297 (2016)

    ADS  Article  Google Scholar 

  27. Coffey, D. et al. Antiferromagnetic spin coupling between rare earth adatoms and iron islands probed by spin-polarized tunneling. Sci. Rep. 5, 13709 (2015)

    ADS  Article  Google Scholar 

  28. Meservey, R., Paraskevopoulos, D. & Tedrow, P. M. Tunneling measurements of conduction-electron-spin polarization in heavy rare-earth metals. Phys. Rev. B 22, 1331–1337 (1980)

    ADS  CAS  Article  Google Scholar 

  29. Choi, T. et al. Atomic-scale sensing of the magnetic dipolar field from single atoms. Nat. Nanotechnol. (2017)

  30. Lacroix, C., Mendels, P. & Mila, F. Introduction to Frustrated Magnetism: Materials, Experiments, Theory (Springer, 2011)

  31. Paul, W., Baumann, S., Lutz, C. P. & Heinrich, A. J. Generation of constant-amplitude radio-frequency sweeps at a tunnel junction for spin resonance STM. Rev. Sci. Instrum. 87, 074703 (2016)

    ADS  Article  Google Scholar 

  32. Schintke, S. & Schneider, W.-D. Insulators at the ultrathin limit: electronic structure studied by scanning tunnelling microscopy and scanning tunnelling spectroscopy. J. Phys. Condens. Matter 16, R49–R81 (2004)

    CAS  Article  Google Scholar 

  33. Pal, J. et al. Morphology of monolayer MgO films on Ag(100): switching from corrugated islands to extended flat terraces. Phys. Rev. Lett. 112, 126102 (2014)

    ADS  Article  Google Scholar 

Download references


We thank B. Melior for technical assistance and F. Donati for discussions. We acknowledge financial support from the Office of Naval Research. F.D.N. appreciates support from the Swiss National Science Foundation under project numbers P300P2_158468 and PZ00P2_167965, and help from A. Natterer. K.Y. acknowledges support from National Natural Science Foundation of China (grant number 61471337). W.P. thanks the Natural Sciences and Engineering Research Council of Canada for fellowship support. P.W. acknowledges financial support from the German academic exchange service. T.G. thanks B. Delley for discussions and IBM Research for its hospitality.

Author information

Authors and Affiliations



F.D.N. conceived the experiment and wrote the manuscript. F.D.N., K.Y., W.P. and P.W. analysed the data. W.P. conceived the atom-switching routine. C.P.L. and A.J.H. enabled and supervised the project. All authors carried out measurements, discussed the results and contributed to the manuscript.

Corresponding authors

Correspondence to Fabian D. Natterer, Andreas J. Heinrich or Christopher P. Lutz.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Additional information

Reviewer Information Nature thanks N. Lorente, R. Sessoli and W. Wernsdorfer for their contribution to the peer review of this work.

Extended data figures and tables

Extended Data Figure 1 Switching-rate dependence of Ho atoms on MgO/Ag(100).

a, Switching rate at a constant current of 1.5 nA and a total field of 0.495 T (Bz ≈ 50 mT). The three threshold values (listed in c) are identical for positive and negative bias. The light blue circles represent the switching rate that was directly measured from current traces and the dark blue squares show a reduced-duty-cycle measurement for higher switching rates. The black line stems from a piecewise linear fit. b, The current-dependent switching rates follow a power law that has an exponent close to unity for all field and bias conditions. This scaling behaviour indicates a single-electron rate-limiting process in the reversal of the Ho moment by energetic electrons. c, Fit parameters for the switching rate in a. The uncertainties represent the standard deviation in the fit value.

Source data

Extended Data Figure 2 Temporal stability of a Ho bit at 4.3 K measured with STM-ESR.

a, ESR spectra for up (top, red) and down (bottom, blue) alignment of the Ho bit at 4.3 K. The sweeps were normalized to the ESR peak height and vertically offset for clarity. b, Monitoring the ESR signal at the two frequencies corresponding to up (blue) and down (orange) alignment of the Ho bit (arrows in a) versus time t (V = 60 mV, I = 20 pA, VRF = 25 mV). The Ho bit spontaneously switches to the up state at t = 1.55 h and remains in that state for the remainder of the sweep. A polynomial background was subtracted from each trace to correct for lateral tip drift. The gap at t = 1.1 h is an interruption that was used to realign the tip onto the Fe sensor to correct for tip drift.

Related audio

PowerPoint slides

Source data

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Natterer, F., Yang, K., Paul, W. et al. Reading and writing single-atom magnets. Nature 543, 226–228 (2017).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing