Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

A pressure-amplifying framework material with negative gas adsorption transitions


Adsorption-based phenomena are important in gas separations1,2, such as the treatment of greenhouse-gas3 and toxic-gas4 pollutants, and in water-adsorption-based heat pumps5 for solar cooling systems. The ability to tune the pore size, shape and functionality of crystalline porous coordination polymers—or metal–organic frameworks (MOFs)—has made them attractive materials for such adsorption-based applications3,6,7,8. The flexibility and guest-molecule-dependent response9,10 of MOFs give rise to unexpected and often desirable adsorption phenomena11,12,13,14. Common to all isothermal gas adsorption phenomena, however, is increased gas uptake with increased pressure. Here we report adsorption transitions in the isotherms of a MOF (DUT-49) that exhibits a negative gas adsorption; that is, spontaneous desorption of gas (methane and n-butane) occurs during pressure increase in a defined temperature and pressure range. A combination of in situ powder X-ray diffraction, gas adsorption experiments and simulations shows that this adsorption behaviour is controlled by a sudden hysteretic structural deformation and pore contraction of the MOF, which releases guest molecules. These findings may enable technologies using frameworks capable of negative gas adsorption for pressure amplification in micro- and macroscopic system engineering. Negative gas adsorption extends the series of counterintuitive phenomena such as negative thermal expansion15,16 and negative refractive indices17 and may be interpreted as an adsorptive analogue of force-amplifying negative compressibility transitions proposed for metamaterials18.

This is a preview of subscription content, access via your institution

Relevant articles

Open Access articles citing this article.

Access options

Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Figure 1: Gas adsorption isotherms, pressure and kinetic profiles.
Figure 2: In situ PXRD during methane adsorption at 111 K.
Figure 3: Structure of DUT-49op and DUT-49cp.
Figure 4: Temperature-dependent methane adsorption and simulations.


  1. de Vos, R. M. & Verweij, H. High-selectivity, high-flux silica membranes for gas separation. Science 279, 1710–1711 (1998)

    Article  ADS  CAS  Google Scholar 

  2. Nenoff, T. M. Hydrogen purification: MOF membranes put to the test. Nature Chem. 7, 377–378 (2015)

    Article  ADS  CAS  Google Scholar 

  3. McDonald, T. M. et al. Cooperative insertion of CO2 in diamine-appended metal-organic frameworks. Nature 519, 303–308 (2015)

    Article  ADS  CAS  Google Scholar 

  4. Barea, E., Montoro, C. & Navarro, J. A. R. Toxic gas removal—metal-organic frameworks for the capture and degradation of toxic gases and vapours. Chem. Soc. Rev. 43, 5419–5430 (2014)

    Article  CAS  Google Scholar 

  5. Furukawa, H. et al. Water adsorption in porous metal–organic frameworks and related materials. J. Am. Chem. Soc. 136, 4369–4381 (2014)

    Article  CAS  Google Scholar 

  6. Kitagawa, S., Kitaura, R. & Noro, S.-i. Functional porous coordination polymers. Angew. Chem. Int. Ed. 43, 2334–2375 (2004)

    Article  CAS  Google Scholar 

  7. Furukawa, H., Cordova, K. E., O’Keeffe, M. & Yaghi, O. M. The chemistry and applications of metal-organic frameworks. Science 341, (2013)

  8. Nugent, P. et al. Porous materials with optimal adsorption thermodynamics and kinetics for CO2 separation. Nature 495, 80–84 (2013)

    Article  ADS  CAS  Google Scholar 

  9. Horike, S., Shimomura, S. & Kitagawa, S. Soft porous crystals. Nature Chem. 1, 695–704 (2009)

    Article  ADS  CAS  Google Scholar 

  10. Schneemann, A. et al. Flexible metal-organic frameworks. Chem. Soc. Rev. 43, 6062–6096 (2014)

    Article  CAS  Google Scholar 

  11. Matsuda, R. Materials chemistry: selectivity from flexibility. Nature 509, 434–435 (2014)

    Article  ADS  CAS  Google Scholar 

  12. Sato, H. et al. Self-accelerating CO sorption in a soft nanoporous crystal. Science 343, 167–170 (2014)

    Article  ADS  CAS  Google Scholar 

  13. Takashima, Y. et al. Molecular decoding using luminescence from an entangled porous framework. Nature Commun. 2, 168 (2011)

    Article  ADS  CAS  Google Scholar 

  14. Yang, S. et al. A partially interpenetrated metal–organic framework for selective hysteretic sorption of carbon dioxide. Nature Mater. 11, 710–716 (2012)

    Article  ADS  CAS  Google Scholar 

  15. Martinek, C. & Hummel, F. A. Linear thermal expansion of three tungstates. J. Am. Ceram. Soc. 51, 227–228 (1968)

    Article  CAS  Google Scholar 

  16. Takenaka, K. Negative thermal expansion materials: technological key for control of thermal expansion. Sci. Technol. Adv. Mater. 13, 013001 (2012)

    Article  CAS  Google Scholar 

  17. Shelby, R. A., Smith, D. R. & Schultz, S. Experimental verification of a negative index of refraction. Science 292, 77–79 (2001)

    Article  ADS  CAS  Google Scholar 

  18. Nicolaou, Z. G. & Motter, A. E. Mechanical metamaterials with negative compressibility transitions. Nature Mater. 11, 608–613 (2012)

    Article  ADS  CAS  Google Scholar 

  19. Fairen-Jimenez, D. et al. Opening the gate: framework flexibility in ZIF-8 explored by experiments and simulations. J. Am. Chem. Soc. 133, 8900–8902 (2011)

    Article  CAS  Google Scholar 

  20. Kondo, A. et al. Novel expansion/shrinkage modulation of 2D layered MOF triggered by clathrate formation with CO2 molecules. Nano Lett. 6, 2581–2584 (2006)

    Article  ADS  CAS  Google Scholar 

  21. Serre, C. et al. An explanation for the very large breathing effect of a metal–organic framework during CO2 adsorption. Adv. Mater. 19, 2246–2251 (2007)

    Article  CAS  Google Scholar 

  22. Férey, G. & Serre, C. Large breathing effects in three-dimensional porous hybrid matter: facts, analyses, rules and consequences. Chem. Soc. Rev. 38, 1380–1399 (2009)

    Article  CAS  Google Scholar 

  23. Salles, F. et al. Multistep N2 breathing in the metal—organic framework Co(1,4-benzenedipyrazolate). J. Am. Chem. Soc. 132, 13782–13788 (2010)

    Article  CAS  Google Scholar 

  24. Thommes, M. et al. Physisorption of gases, with special reference to the evaluation of surface area and pore size distribution (IUPAC Technical Report). Pure Appl. Chem. 87, 1051–1069 (2015)

    Article  CAS  Google Scholar 

  25. Stoeck, U., Krause, S., Bon, V., Senkovska, I. & Kaskel, S. A highly porous metal-organic framework, constructed from a cuboctahedral super-molecular building block, with exceptionally high methane uptake. Chem. Commun. 48, 10841–10843 (2012)

    Article  CAS  Google Scholar 

  26. Traa, Y. & Weitkamp, J. in Handbook of Porous Solids (eds, Schüth, F., Sing, K. S. W. & Weitkamp, J. ) 1015–1057 (Wiley, 2008)

  27. Bon, V. et al. In situ monitoring of structural changes during the adsorption on flexible porous coordination polymers by X-ray powder diffraction: instrumentation and experimental results. Micropor. Mesopor. Mater. 188, 190–195 (2014)

    Article  CAS  Google Scholar 

  28. Tan, J. C. & Cheetham, A. K. Mechanical properties of hybrid inorganic–organic framework materials: establishing fundamental structure–property relationships. Chem. Soc. Rev. 40, 1059–1080 (2011)

    Article  CAS  Google Scholar 

  29. Neimark, A. V., Coudert, F.-X., Boutin, A. & Fuchs, A. H. Stress-based model for the breathing of metal–organic frameworks. J. Phys. Chem. Lett. 1, 445–449 (2010)

    Article  CAS  Google Scholar 

  30. Riekert, L. Instability of sorption complexes in synthetic faujasites. J. Phys. Chem. 73, 4384–4386 (1969)

    Article  CAS  Google Scholar 

Download references


V.B. thanks the German Federal Ministry for education and research (project BMBF number 05K13OD3). S. Krause, V.B., I.S. and S. Kaskel thank the Helmholtz-Zentrum Berlin for financial support and allocation of synchrotron radiation beam time at the KMC-2 beamline. F.-X.C. thanks GENCI (grant number x2015087069) for access to High-Performance Computing resources. G.M. thanks Institut Universitaire de France for its support. We thank U. Koch for scanning electron microscope images, as well as L. Sarkisov and A. Fuchs for discussions.

Author information

Authors and Affiliations



S. Krause and U.S. synthesized and activated the material investigated; S. Krause, V.B., I.S. and S. Kaskel conducted and interpreted volumetric and gravimetric sorption experiments. S. Krause, V.B., D.W. and D.M.T. conducted the in situ PXRD investigations. S. Krause V.B., D.W. and S.Z. conducted the in situ EXAFS investigations. V.B. solved the crystal structure and performed structure modelling. S. Krause performed filming and animation of the structural transitions. F.-X.C. performed quantum mechanical calculations. G.M. and R.S.P. performed the grand canonical Monte Carlo simulations of adsorption. S. Krause, V.B., I.S., F.-X.C., G.M. and S. Kaskel wrote the manuscript.

Corresponding author

Correspondence to Stefan Kaskel.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Additional information

The following crystal structures are available free of charge from the Cambridge Crystallographic Data Centre under reference numbers CCDC-1413081, CCDC-1413083, CCDC-1413082 and CCDC-1413084, respectively: DUT-49op in vacuum at 111 K; DUT-49cp432CH4 (where indicates the number of methane molecules per unit cell) at a relative pressure of 0.28 for methane at 111 K during adsorption; DUT-49op1,344CH4 at a relative pressure of 0.97 for methane at 111 K during adsorption; and DUT-49ip1,176CH4 at a relative pressure of 0.25 for methane at 111 K during desorption.

Supplementary information

Supplementary Information

This file contains Supplementary Methods and Data, Supplementary Schemes 1-2, Supplementary Tables 1-15, Supplementary Figures 1-44 and Supplementary References. (PDF 4061 kb)

Visualization of a framework material during NGA

This video clip shows macroscopic movement of a DUT-49 sample bed filmed in a glass capillary during adsorption of n-butane at 298 - 299 K. (WMV 9263 kb)

Visualization of the framework’s structural transition

This video clip illustrates in an animation the framework structural transition including visualization of ligand deformation and changes of pore size occurring upon contraction of DUT-49op to DUT-49cp. (WMV 93412 kb)

PowerPoint slides

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Krause, S., Bon, V., Senkovska, I. et al. A pressure-amplifying framework material with negative gas adsorption transitions. Nature 532, 348–352 (2016).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing