Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Processing and properties of magnesium containing a dense uniform dispersion of nanoparticles


Magnesium is a light metal, with a density two-thirds that of aluminium, is abundant on Earth and is biocompatible; it thus has the potential to improve energy efficiency and system performance in aerospace, automobile, defence, mobile electronics and biomedical applications1,2,3,4,5. However, conventional synthesis and processing methods (alloying and thermomechanical processing) have reached certain limits in further improving the properties of magnesium and other metals6. Ceramic particles have been introduced into metal matrices to improve the strength of the metals7, but unfortunately, ceramic microparticles severely degrade the plasticity and machinability of metals7, and nanoparticles, although they have the potential to improve strength while maintaining or even improving the plasticity of metals8,9, are difficult to disperse uniformly in metal matrices10,11,12,13,14. Here we show that a dense uniform dispersion of silicon carbide nanoparticles (14 per cent by volume) in magnesium can be achieved through a nanoparticle self-stabilization mechanism in molten metal. An enhancement of strength, stiffness, plasticity and high-temperature stability is simultaneously achieved, delivering a higher specific yield strength and higher specific modulus than almost all structural metals.

This is a preview of subscription content

Access options

Rent or Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Figure 1: Uniform dispersion of SiC nanoparticles in as-solidified magnesium alloy matrix.
Figure 2: Mechanical behaviour of as-solidified samples at room temperature.
Figure 3: Structure refinement and strength enhancement by HPT.
Figure 4: Mechanical behaviour of as-solidified sample at elevated temperatures.


  1. 1

    Pollock, T. M. Weight loss with magnesium alloys. Science 328, 986–987 (2010)

    CAS  Article  Google Scholar 

  2. 2

    Lu, K. The future of metals. Science 328, 319–320 (2010)

    CAS  ADS  Article  Google Scholar 

  3. 3

    Nie, J. F., Zhu, Y. M., Liu, J. Z. & Fang, X. Y. Periodic segregation of solute atoms in fully coherent twin boundaries. Science 340, 957–960 (2013)

    CAS  ADS  Article  Google Scholar 

  4. 4

    Erbel, R. et al. Temporary scaffolding of coronary arteries with bioabsorbable magnesium stents: a prospective, non-randomised multicentre trial. Lancet 369, 1869–1875 (2007)

    CAS  Article  Google Scholar 

  5. 5

    Knochel, P. A flash of magnesium. Nature Chem . 1, 740 (2009)

    CAS  ADS  Article  Google Scholar 

  6. 6

    Nie, J.-F. Precipitation and hardening in magnesium alloys. Metall. Mater. Trans. A 43, 3891–3939 (2012)

    CAS  Article  Google Scholar 

  7. 7

    Mortensen, A. & Llorca, J. Metal Matrix Composites. Annu. Rev. Mater. Res. 40, 243–270 (2010)

    CAS  ADS  Article  Google Scholar 

  8. 8

    Liu, G. et al. Nanostructured high-strength molybdenum alloys with unprecedented tensile ductility. Nature Mater . 12, 344–350 (2013)

    CAS  ADS  Article  Google Scholar 

  9. 9

    Zhang, Z. & Chen, D. Consideration of Orowan strengthening effect in particulate-reinforced metal matrix nanocomposites: a model for predicting their yield strength. Scr. Mater. 54, 1321–1326 (2006)

    CAS  Article  Google Scholar 

  10. 10

    Ferguson, J. B., Sheykh-Jaberi, F., Kim, C. S., Rohatgi, P. K. & Cho, K. On the strength and strain to failure in particle-reinforced magnesium metal-matrix nanocomposites (Mg MMNCs). Mater. Sci. Eng. A 558, 193–204 (2012)

    CAS  Article  Google Scholar 

  11. 11

    Tjong, S. C. Novel nanoparticle-reinforced metal matrix composites with enhanced mechanical properties. Adv. Eng. Mater. 9, 639–652 (2007)

    CAS  Article  Google Scholar 

  12. 12

    Chen, L. Y. et al. Novel nanoprocessing route for bulk graphene nanoplatelets reinforced metal matrix nanocomposites. Scr. Mater. 67, 29–32 (2012)

    CAS  Article  Google Scholar 

  13. 13

    Ferkel, H. & Mordike, B. L. Magnesium strengthened by SiC nanoparticles. Mater. Sci. Eng. A 298, 193–199 (2001)

    Article  Google Scholar 

  14. 14

    Sillekens, W. H. et al. The ExoMet project: EU/ESA research on high-performance light-metal alloys and nanocomposites. Metall. Mater. Trans. A 45, 3349–3361 (2014)

    CAS  Article  Google Scholar 

  15. 15

    Xu, J. Q., Chen, L. Y., Choi, H. & Li, X. C. Theoretical study and pathways for nanoparticle capture during solidification of metal melt. J. Phys. Condens. Matter 24, 255304 (2012)

    CAS  ADS  Article  Google Scholar 

  16. 16

    Chen, L.-Y., Peng, J.-Y., Xu, J.-Q., Choi, H. & Li, X.-C. Achieving uniform distribution and dispersion of a high percentage of nanoparticles in metal matrix nanocomposites by solidification processing. Scr. Mater. 69, 634–637 (2013)

    CAS  Article  Google Scholar 

  17. 17

    Min, Y., Akbulut, M., Kristiansen, K., Golan, Y. & Israelachvili, J. The role of interparticle and external forces in nanoparticle assembly. Nature Mater . 7, 527–538 (2008)

    CAS  ADS  Article  Google Scholar 

  18. 18

    Somekawa, H. & Schuh, C. A. Nanoindentation behavior and deformed microstructures in coarse-grained magnesium alloys. Scr. Mater. 68, 416–419 (2013)

    CAS  Article  Google Scholar 

  19. 19

    Pozuelo, M., Chang, Y. W. & Yang, J. M. Effect of diamondoids on the microstructure and mechanical behavior of nanostructured Mg-matrix nanocomposites. Mater. Sci. Eng. A 633, 200–208 (2015)

    CAS  Article  Google Scholar 

  20. 20

    Ye, J., Mishra, R. K., Sachdev, A. K. & Minor, A. M. In situ TEM compression testing of Mg and Mg-0.2 wt.% Ce single crystals. Scr. Mater. 64, 292–295 (2011)

    CAS  Article  Google Scholar 

  21. 21

    Barnett, M. R., Keshavarz, Z., Beer, G. & Atwell, D. Influence of grain size on the compressive deformation of wrought Mg-3Al-1Zn. Acta Mater. 52, 5093–5103 (2004)

    CAS  Article  Google Scholar 

  22. 22

    Stanford, N. & Barnett, M. R. Effect of particles on the formation of deformation twins in a magnesium-based alloy. Mater. Sci. Eng. A 516, 226–234 (2009)

    Article  Google Scholar 

  23. 23

    Watanabe, H. Effect of second-phase precipitates on local elongation in extruded magnesium alloys. J. Mater. Eng. Perform. 22, 3450–3454 (2013)

    CAS  Article  Google Scholar 

  24. 24

    Hutchinson, W. B. & Barnett, M. R. Effective values of critical resolved shear stress for slip in polycrystalline magnesium and other hcp metals. Scr. Mater. 63, 737–740 (2010)

    CAS  Article  Google Scholar 

  25. 25

    Jian, W. W. et al. Ultrastrong Mg alloy via nano-spaced stacking faults. Mater. Res. Lett . 1, 61–66 (2013)

    CAS  Article  Google Scholar 

  26. 26

    Inoue, A. et al. Novel hexagonal structure of ultra-high strength magnesium-based alloys. Mater. Trans. 43, 580–584 (2002)

    CAS  Article  Google Scholar 

  27. 27

    Luo, A. A. Recent magnesium alloy development for elevated temperature applications. Int. Mater. Rev. 49, 13–30 (2004)

    CAS  ADS  Article  Google Scholar 

  28. 28

    Luo, A. & Pekguleryuz, M. O. Cast magnesium alloys for elevated temperature applications. J. Mater. Sci. 29, 5259–5271 (1994)

    CAS  ADS  Article  Google Scholar 

  29. 29

    Friedrich, H. E. & Mordike, B. L. Magnesium Technology—Metallurgy, Design Data, Applications (Springer, 2006)

  30. 30

    Xiao, Y., Zhang, X., Chen, J. & Jiang, H. Microstructures and mechanical properties of extruded Mg-9Gd-4Y–0.6Zr-T5 at elevated temperatures. Chin. J. Nonferr. Met . 16, 709–714 (2006)

    CAS  Article  Google Scholar 

  31. 31

    Zhilyaev, A. P. & Langdon, T. G. Using high-pressure torsion for metal processing: fundamentals and applications. Prog. Mater. Sci. 53, 893–979 (2008)

    CAS  Article  Google Scholar 

  32. 32

    Oh, Y., Asif, S. A. S., Cyrankowski, E. & Warren, O. L. Microelectro-mechanical heater. US patent WO2011066018 A1 (2011)

  33. 33

    Israelachvili, J. N. Intermolecular and Surface Forces 211 (Academic Press, 2011)

  34. 34

    Hashim, J., Looney, L. & Hashmi, M. S. J. The wettability of SiC particles by molten aluminium alloy. J. Mater. Process. Technol. 119, 324–328 (2001)

    CAS  Article  Google Scholar 

  35. 35

    Eustathopoulos, N., Nicholas, M. G. & Drevet, B. Wettability at High Temperatures 396 (Pergamon, 1999)

  36. 36

    Zhang, D., Shen, P., Shi, L. X., Lin, Q. L. & Jiang, Q. C. Wetting and evaporation behaviors of molten Mg on partially oxidized SiC substrates. Appl. Surf. Sci. 256, 7043–7047 (2010)

    CAS  ADS  Article  Google Scholar 

  37. 37

    Nardone, V. C. & Prewo, K. M. On the strength of discontinuous silicon carbide reinforced aluminum composites. Scr. Metall. 20, 43–48 (1986)

    CAS  Article  Google Scholar 

  38. 38

    Choi, H. J., Kim, Y., Shin, J. H. & Bae, D. H. Deformation behavior of magnesium in the grain size spectrum from nano- to micrometer. Mater. Sci. Eng. A 527, 1565–1570 (2010)

    Article  Google Scholar 

  39. 39

    Gu, R. & Ngan, H. W. Size effect on the deformation behavior of duralumin micropillars. Scr. Mater. 68, 861–864 (2013)

    CAS  Article  Google Scholar 

  40. 40

    Gong, J. & Wilkinson, A. J. A microcantilever investigation of size effect, solid-solution strengthening and second-phase strengthening for 〈a〉 prism slip in alpha-Ti. Acta Mater. 59, 5970–5981 (2011)

    CAS  Article  Google Scholar 

  41. 41

    Choi, W. S., De Cooman, B. C., Sandlöbes, S. & Raabe, D. Size and orientation effects in partial dislocation-mediated deformation of twinning-induced plasticity steel micro-pillars. Acta Mater. 98, 391–404 (2015)

    CAS  Article  Google Scholar 

  42. 42

    Guo, E. Y. et al. Mechanical characterization of microconstituents in a cast duplex stainless steel by micropillar compression. Mater. Sci. Eng. A 598, 98–105 (2014)

    CAS  Article  Google Scholar 

  43. 43

    Chen, P. et al. Microscale-calibrated modeling of the deformation response of dual-phase steels. Acta Mater. 65, 133–149 (2014)

    CAS  Article  Google Scholar 

  44. 44

    Girault, B., Schneider, A. S., Prick, C. P. & Arzt, E. Strength effects in micropillars of a dispersion strengthened superalloy. Adv. Eng. Mater. 12, 385–388 (2010)

    CAS  Article  Google Scholar 

  45. 45

    Cordero, Z. C. et al. Powder-route synthesis and mechanical testing of ultrafine grain tungsten alloys. Metall. Mater. Trans. A 45, 3609–3618 (2014)

    CAS  Article  Google Scholar 

Download references


This work is supported in part by the National Institute of Standards and Technology (NIST). We thank Y.-W. Chang, N. Bodzin and T. McLouth at the University of California, Los Angeles, for their help with FIB experiments, micropillar testing and elastic modulus measurements. We also thank C. Cao at the University of California, Los Angeles for his help with measuring the grain size of the as-solidified Mg2Zn samples.

Author information




X.-C.L. and L.-Y.C. conceived the idea and designed the experiments. L.-Y.C. and H.C. fabricated the nanocomposites. X.-C.L. and J.-Q.X. developed the theoretical model for nanoparticle dispersion. X.M. conducted the high-pressure torsion experiment. L.-Y.C. and M.P. characterized the properties and microstructures. S.B. conducted micropillar compression testing at high temperature. L.-Y.C., X.-C.L., J.-Q.X., M.P. and S.M. analysed the data. L.-Y.C., X.-C.L., M.P. and S.M. wrote the paper. J.-M.Y. supervised M.P. for TEM characterization. S.M. supervised X.M. for the high-pressure torsion experiment. X.-C.L. supervised the whole work.

Corresponding author

Correspondence to Xiao-Chun Li.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Extended data figures and tables

Extended Data Figure 1 Fabrication of nanocomposites.

a, Ultrasonic processing for nanoparticle feeding and dispersion. b, Vacuum evaporation for concentrating nanoparticles in magnesium.

Extended Data Figure 2 Uniform distribution of nanoparticles across the whole sample.

a, Bright-field TEM image showing the dispersed SiC nanoparticles in the magnesium matrix. b, A histogram indicating the SiC nanoparticle size distribution. c, d, Plots representing the amount of Si (wt%; c) and Vickers microhardness (Hv; d) as a function of the position in the sample (bottom, middle, top, centre and edge). Error bars represent s.d. of six data sets in d and three data sets in c.

Extended Data Figure 3 TEM analysis showing non-basal deformation mechanisms in a polycrystalline sample under microcompression.

a, Bright-field TEM image showing a SiC nanoparticle embedded in the magnesium matrix. b, High-resolution TEM image from the region highlighted in a showing dislocations (indicated in yellow) terminated at stacking faults on the pyramidal planes in a grain oriented to the zone axis as indicated by its fast Fourier transform in c. The angle between the loading and pyramidal directions is around 30°.

Supplementary information

SEM video showing deformation behavior of Mg2Zn sample during micro-compression test.

After yielding, Mg2Zn sample exhibits sudden slips, which results in repeated loading-unloading cycles in stress-strain curve. (MP4 36336 kb)

SEM video showing deformation behaviour of Mg2Zn (14 vol% SiC) sample during micro-compression test.

After yielding, Mg2Zn (14 vol% SiC) sample deforms uniformly without sudden slips, which results in a smooth stress-strain curve. (MP4 25737 kb)

PowerPoint slides

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Chen, LY., Xu, JQ., Choi, H. et al. Processing and properties of magnesium containing a dense uniform dispersion of nanoparticles. Nature 528, 539–543 (2015).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links