Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Perovskite oxides for visible-light-absorbing ferroelectric and photovoltaic materials


Ferroelectrics have recently attracted attention as a candidate class of materials for use in photovoltaic devices, and for the coupling of light absorption with other functional properties1,2,3,4,5,6,7. In these materials, the strong inversion symmetry breaking that is due to spontaneous electric polarization promotes the desirable separation of photo-excited carriers and allows voltages higher than the bandgap, which may enable efficiencies beyond the maximum possible in a conventional p–n junction solar cell2,6,8,9,10. Ferroelectric oxides are also stable in a wide range of mechanical, chemical and thermal conditions and can be fabricated using low-cost methods such as sol–gel thin-film deposition and sputtering3,5. Recent work3,5,11 has shown how a decrease in ferroelectric layer thickness and judicious engineering of domain structures and ferroelectric–electrode interfaces can greatly increase the current harvested from ferroelectric absorber materials, increasing the power conversion efficiency from about 10−4 to about 0.5 per cent. Further improvements in photovoltaic efficiency have been inhibited by the wide bandgaps (2.7–4 electronvolts) of ferroelectric oxides, which allow the use of only 8–20 per cent of the solar spectrum. Here we describe a family of single-phase solid oxide solutions made from low-cost and non-toxic elements using conventional solid-state methods: [KNbO3]1 −x[BaNi1/2Nb1/2O3 −δ]x (KBNNO). These oxides exhibit both ferroelectricity and a wide variation of direct bandgaps in the range 1.1–3.8 electronvolts. In particular, the x = 0.1 composition is polar at room temperature, has a direct bandgap of 1.39 electronvolts and has a photocurrent density approximately 50 times larger than that of the classic ferroelectric (Pb,La)(Zr,Ti)O3 material. The ability of KBNNO to absorb three to six times more solar energy than the current ferroelectric materials suggests a route to viable ferroelectric semiconductor-based cells for solar energy conversion and other applications.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Figure 1: KBNNO structural properties.
Figure 2: Experimental results for ferroelectricity and bandgap in KBNNO.
Figure 3: Photocurrent measurements for the KBNNO samples.

Similar content being viewed by others


  1. Choi, T., Lee, S., Choi, Y., Kiryukhin, V. & Cheong, S.-W. Switchable ferroelectric diode and photovoltaic effect in BiFeO3 . Science 324, 63–66 (2009)

    Article  ADS  CAS  Google Scholar 

  2. Yang, S. Y. et al. Above-bandgap voltages from ferroelectric photovoltaic devices. Nature Nanotechnol. 5, 143–147 (2010)

    Article  ADS  CAS  Google Scholar 

  3. Cao, D. et al. High-efficiency ferroelectric-film solar cells with an n-type Cu2O cathode buffer layer. Nano Lett. 12, 2803–2809 (2012)

    Article  ADS  CAS  Google Scholar 

  4. Alexe, M. & Hesse, D. Tip-enhanced photovoltaic effects in bismuth ferrite. Nature Commun. 2, 256 (2011)

    Article  ADS  Google Scholar 

  5. Qin, M., Ao, K. & Liang, Y. C. High efficiency photovoltaics in nanoscaled ferroelectric thin films. Appl. Phys. Lett. 93, 122904 (2008)

    Article  ADS  Google Scholar 

  6. Choi, W. S. et al. Wide bandgap tunability in complex transition metal oxides by site-specific substitution. Nature Commun. 3, 689 (2012)

    Article  ADS  Google Scholar 

  7. Kreisel, J., Alexe, M. & Thomas, P. A. A photoferroelectric material is more than the sum of its parts. Nature Mater. 11, 260 (2012)

    Article  ADS  CAS  Google Scholar 

  8. Fridkin, V. M. Photoferroelectrics (Springer, 1979)

    Book  Google Scholar 

  9. Inoue, Y., Sato, K., Sato, K. & Miyama, H. Photoassisted water decomposition by ferroelectric lead zirconate titanate ceramics with anomalous photovoltaic effects. J. Phys. Chem. 90, 2809–2810 (1986)

    Article  CAS  Google Scholar 

  10. Young, S. M. & Rappe, A. M. First principles calculation of the shift current photovoltaic effect in ferroelectrics. Phys. Rev. Lett. 109, 116601 (2012)

    Article  ADS  Google Scholar 

  11. Glass, A. M., Linde, D. V. D. & Negran, T. J. High-voltage bulk photovoltaic effect and photorefractive process in LiNbO3 . Appl. Phys. Lett. 25, 233–235 (1974)

    Article  ADS  CAS  Google Scholar 

  12. Cohen, R. E. Origin of ferroelectricity in perovskite oxides. Nature 358, 136–138 (1992)

    Article  ADS  CAS  Google Scholar 

  13. Basu, S. R. et al. Photoconductivity in BiFeO3 thin films. Appl. Phys. Lett. 92, 091905 (2008)

    Article  ADS  Google Scholar 

  14. Yang, S. Y. et al. Photovoltaic effects in BiFeO3 . Appl. Phys. Lett. 95, 062909 (2009)

    Article  ADS  Google Scholar 

  15. Zhang, G. et al. New high Tc multiferroics KBiFe2O5 with narrow band gap and promising photovoltaic effect. Sci. Rep. 3, 1265 (2013)

    Article  Google Scholar 

  16. Bennett, J. W., Grinberg, I. & Rappe, A. M. New highly polar semiconductor ferroelectrics through d8 cation-O vacancy substitution into PbTiO3: a theoretical study. J. Am. Chem. Soc. 130, 17409–17412 (2008)

    Article  CAS  Google Scholar 

  17. Gou, G. Y., Bennett, J. W., Takenaka, H. & Rappe, A. M. Post density functional theoretical studies of highly polar semiconductive Pb(Ti1−x Nix)O3−x solid solutions: effects of cation arrangement on band gap. Phys. Rev. B 83, 205115 (2011)

    Article  ADS  Google Scholar 

  18. Qi, T., Grinberg, I. & Rappe, A. M. Band-gap engineering via local environment in complex oxides. Phys. Rev. B 83, 224108 (2011)

    Article  ADS  Google Scholar 

  19. Liang, L., Li, Y. L., Chen, L.-Q., Hu, S. Y. & Lu, G.-H. A thermodynamic free energy function for potassium niobate. Appl. Phys. Lett. 94, 072904 (2009)

    Article  ADS  Google Scholar 

  20. Zhao, X., Qu, W. & Tan, X. Zr-modified Pb(Mg1/3Nb2/3)O3 with a long-range cation order. J. Am. Ceram. Soc. 91, 3031–3038 (2008)

    Article  CAS  Google Scholar 

  21. Kondo, M. & Kurihara, K. Sintering behavior and surface microstructure of PbO-rich Pb(Ni1/3Nb2/3)O3–PbZrO3 ceramics. J. Am. Ceram. Soc. 84, 2469–2474 (2001)

    Article  CAS  Google Scholar 

  22. Kröger, F. A. & Vink, H. J. Relations between the concentrations of imperfections in crystalline solids. 3, 307–435 (1956)

  23. Reuter, K. & Scheffler, M. First-principles atomistic thermodynamics for oxidation catalysis: surface phase diagrams and catalytically interesting regions. Phys. Rev. Lett. 90, 046103 (2003)

    Article  ADS  Google Scholar 

  24. Grinberg, I. & Rappe, A. M. Local structure and macroscopic properties in Pb(Zn1/3Nb2/3)O3–PbTiO3 and Pb(Mg1/3Nb2/3)O3–PbTiO3 solid solutions. Phys. Rev. B 70, 220101 (2004)

    Article  ADS  Google Scholar 

  25. Bartasyte, A., Kreisel, J., Peng, W. & Guilloux-Viry, M. Temperature-dependent Raman scattering of KTa1−xNbxO3 thin films. Appl. Phys. Lett. 96, 262903 (2010)

    Article  ADS  Google Scholar 

  26. Srihari, V. et al. Wide band gap tunability of bulk Cd1−xCaxO. J. Appl. Phys. 109, 013510 (2011)

    Article  ADS  Google Scholar 

  27. Ji, S. M., Choi, S. H., Jang, J. S., Kim, E. S. & Lee, J. S. Band gap tailored Zn(Nb1−x VxO6) solid solutions as visible light photocatalysts. J. Phys. Chem. C 113, 17824–17830 (2009)

    Article  CAS  Google Scholar 

  28. Kim, T. W. et al. Substitution effect of pentavalent bismuth ions on electronic structure and physicochemical properties of perovskite-structured Ba(In0. 5Ta0. 5)O3 semiconductors. Mater. Res. Bull. 42, 1914–1920 (2007)

    Article  CAS  Google Scholar 

  29. Brody, P. S. Temperature dependence of the short circuit photocurrent in ferroelectric ceramics. Ferroelectrics 10, 143–146 (1976)

    Article  CAS  Google Scholar 

  30. Poosanaas, P., Dogan, A., Thakoor, S. & Uchino, K. Influence of sample thickness on the performance of photostrictive ceramics. J. Appl. Phys. 84, 1508–1512 (1998)

    Article  ADS  CAS  Google Scholar 

  31. Park, J., Won, S. S., Ahn, C. W. & Kim, I. W. Ferroelectric photocurrent effect in polycrystalline lead-free (K0. 5 Na0. 5) (Mn0. 005Nb0. 995)O3 thin film. J. Am. Ceram. Soc. 96, 146–150 (2013)

    Article  CAS  Google Scholar 

  32. Giannozzi, P. et al. QUANTUM ESPRESSO: a modular and open-source software project for quantum simulations of materials. J. Phys. Condens. Matter 21, 395502 (2009)

    Article  Google Scholar 

  33. Hybertsen, M. S. & Louie, S. G. Electron correlation in semiconductors and insulators: band gaps and quasiparticle energies. Phys. Rev. B 34, 5390–5413 (1986)

    Article  ADS  CAS  Google Scholar 

Download references


Members of the Davies group—D.V.W., D.M.S., L.W. and P.K.D.—were supported by the Energy Commercialization Institute of BFTP. We also thank M. R. Suchomel for assistance with collection of the synchrotron X-ray data. Use of the Advanced Photon Source at Argonne National Laboratory was supported by the US Department of Energy, Office of Basic Sciences, under contract number DE-AC02-06CH11357. Members of the Spanier group—M.T. and J.E.S.—were supported by the Army Research Office, under grant number W911NF-08-1-0067. G.C. was supported by NSF grant DMR 0907381. A.R.A. was supported by the Energy Commercialization Institute of BFTP and by NSF grant DMR 1124696. E.M.G. was supported by an ASEE Postdoctoral Fellowship. Support for instrumentation used in this project was provided by the ARO DURIP programme and the NSF under grant DMR 0722845. J.E.S. also acknowledges C. L. Schauer for permitting access to the spectroscopic ellipsometer and the Drexel Centralized Research Facilities for access to instrumentation. We thank F. Yan, M. A. Islam and C. L. Johnson for assistance in transparent electrode thin-film deposition, Raman scattering, and sample thinning and polishing, respectively. Of the Rappe group, I.G. was supported by the Department of Energy, Office of Basic Energy Sciences, under grant number DE-FG02-07ER46431, G.G. was supported by the Energy Commercialization Institute and A.M.R. was supported by the Office of Naval Research, under grant number N00014-12-1-1033. Computational support was provided by a Challenge Grant from the High Performance Computing Modernization Office of the US Department of Defense and the National Energy Research Scientific Computing Center of the US Department of Energy.

Author information

Authors and Affiliations



I.G. and A.M.R. created the materials design strategy. D.V.W. and P.K.D. suggested the KBNNO composition. I.G., J.E.S., P.K.D. and A.M.R. designed the calculations and experiments and supervised the analysis of obtained results. D.V.W., D.M.S. and L.W. synthesized the KBNNO powders and pellets. D.V.W. obtained the X-ray diffraction and dielectric data. G.C. developed the procedure to prepare the lamellae from the pellets. M.T. performed the piezoresponse and ellipsometry measurements. A.R.A. and J.E.S. analysed the Raman spectra. A.R.A., G.C., E.M.G. and J.E.S. carried out the ferroelectric, photoresponse and photovoltage measurements. G.G. performed the DFT calculations. I.G., G.G., J.E.S., A.M.R. and P.K.D. co-wrote the paper.

Corresponding author

Correspondence to Andrew M. Rappe.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Extended data figures and tables

Extended Data Figure 1 Ferroelectric and dielectric data.

a, Dielectric data for x = 0.1–0.4 KBNNO. Two dielectric anomalies (arrows) at about 450 K and about 600 K are present (solid lines indicate heating; dotted lines indicate cooling). b, Ferroelectric hysteresis loops at 77 K, showing the effect of increasing the maximum poling voltage. c, Ferroelectric hysteresis loop for approximately 20-μm-thick x = 0.1 KBNNO film at 170–200 K. d, Ferroelectric hysteresis loop for approximately 20-μm-thick x = 0.1 KBNNO film at 300 K.

Extended Data Figure 2 Electronic Structure of KBNNO.

Band structures (top) and orbital-projected density of states (PDOS, bottom) for KBNNO Ni–VO–Ni and Ni–VO–Nb solid solutions near the Fermi level. The high-symmetry points in the Brillouin zone are Γ (0, 0, 0) A (−0.5, 0.5, 0), B (−0.5, 0, 0), D (−0.5, 0, 0.5), E (−0.5, 0.5, 0.5), Z (0, 0, 0.5), C (0, 0.5, 0.5) and Y (0, 0.5, 0). k is the wavevector. The more stable Ni–VO–Nb structure provides a smaller bandgap. As Ni concentration rises, Ni–VO–Ni becomes more common and the bandgap energy rises.

Extended Data Figure 3 Switchable bulk photovoltaic effect in KBNNO and the dependence of photocurrent on poling.

Ferroelectric photovoltaic effect for approximately 20-μm-thick x = 0.1 KBNNO film in ambient conditions under 4 mW cm−2 of above-bandgap illumination following poling by an 80-V pulse applied for 300 s (a), a 50-V pulse applied for 300 s (b), a 50-V pulse applied for 180 s (c), a 50-V pulse applied for 30 s (d) and a 50-V pulse applied for 10 s under 4 mW cm−2 of above-bandgap illumination (e). Black denotes collected dark current; blue and red traces indicate photocurrent following poling under positive and negative voltages, respectively. f, Short-circuit photocurrent Isc for different product of duration and magnitude of poling voltage. The current is collected through 200 µm × 200 µm ITO and Cr–Au electrodes on the top and bottom of the sample, respectively. The height of each error bar is two standard deviations in the measured short-circuit current. As the applied voltage and poling time are increased, the difference between the photocurrents for the up- and down-polarized sample increases and the photocurrent magnitude rises by two orders of magnitude until saturation caused by leakage. This indicates that the sample is not yet fully poled even for the highest voltage possible in our set-up. Therefore, our results are the lower limit for the photocurrent for a fully poled material that can be achieved by application of larger electric fields in thinner films.

Extended Data Table 1 Comparison of structural data from experiment and DFT calculations

PowerPoint slides

Rights and permissions

Reprints and permissions

About this article

Cite this article

Grinberg, I., West, D., Torres, M. et al. Perovskite oxides for visible-light-absorbing ferroelectric and photovoltaic materials. Nature 503, 509–512 (2013).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing