Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Highly stretchable and tough hydrogels


Hydrogels are used as scaffolds for tissue engineering1, vehicles for drug delivery2, actuators for optics and fluidics3, and model extracellular matrices for biological studies4. The scope of hydrogel applications, however, is often severely limited by their mechanical behaviour5. Most hydrogels do not exhibit high stretchability; for example, an alginate hydrogel ruptures when stretched to about 1.2 times its original length. Some synthetic elastic hydrogels6,7 have achieved stretches in the range 10–20, but these values are markedly reduced in samples containing notches. Most hydrogels are brittle, with fracture energies of about 10 J m−2 (ref. 8), as compared with 1,000 J m−2 for cartilage9 and 10,000 J m−2 for natural rubbers10. Intense efforts are devoted to synthesizing hydrogels with improved mechanical properties11,12,13,14,15,16,17,18; certain synthetic gels have reached fracture energies of 100–1,000 J m−2 (refs 11, 14, 17). Here we report the synthesis of hydrogels from polymers forming ionically and covalently crosslinked networks. Although such gels contain 90% water, they can be stretched beyond 20 times their initial length, and have fracture energies of 9,000 J m−2. Even for samples containing notches, a stretch of 17 is demonstrated. We attribute the gels’ toughness to the synergy of two mechanisms: crack bridging by the network of covalent crosslinks, and hysteresis by unzipping the network of ionic crosslinks. Furthermore, the network of covalent crosslinks preserves the memory of the initial state, so that much of the large deformation is removed on unloading. The unzipped ionic crosslinks cause internal damage, which heals by re-zipping. These gels may serve as model systems to explore mechanisms of deformation and energy dissipation, and expand the scope of hydrogel applications.

This is a preview of subscription content, access via your institution

Relevant articles

Open Access articles citing this article.

Access options

Rent or buy this article

Get just this article for as long as you need it


Prices may be subject to local taxes which are calculated during checkout

Figure 1: Schematics of three types of hydrogel.
Figure 2: The hybrid gel is highly stretchable and notch-insensitive.
Figure 3: Mechanical tests under various conditions.
Figure 4: Composition greatly affects behaviour of the hybrid gel.


  1. Lee, K. Y. & Mooney, D. J. Hydrogels for tissue engineering. Chem. Rev. 101, 1869–1879 (2001)

    Article  CAS  Google Scholar 

  2. Qiu, Y. & Park, K. Environment-sensitive hydrogels for drug delivery. Adv. Drug Deliv. Rev. 53, 321–339 (2001)

    Article  CAS  Google Scholar 

  3. Dong, L., Agarwal, A. K., Beebe, D. J. & Jiang, H. R. Adaptive liquid microlenses activated by stimuli-responsive hydrogels. Nature 442, 551–554 (2006)

    Article  ADS  CAS  Google Scholar 

  4. Discher, D. E., Mooney, D. J. & Zandstra, P. W. Growth factors, matrices, and forces combine and control stem cells. Science 324, 1673–1677 (2009)

    Article  ADS  CAS  Google Scholar 

  5. Calvert, P. Hydrogels for soft machines. Adv. Mater. 21, 743–756 (2009)

    Article  ADS  CAS  Google Scholar 

  6. Okumura, Y. & Ito, K. The polyrotaxane gel: a topological gel by figure-of-eight cross-links. Adv. Mater. 13, 485–487 (2001)

    Article  CAS  Google Scholar 

  7. Haraguchi, K. & Takehisa, T. Nanocomposite hydrogels: a unique organic-inorganic network structure with extraordinary mechanical, optical and swelling/de-swelling properties. Adv. Mater. 14, 1120–1124 (2002)

    Article  CAS  Google Scholar 

  8. Lake, G. J. & Thomas, A. G. The strength of highly elastic materials. Proc. R. Soc. A 300, 108–119 (1967)

    ADS  CAS  Google Scholar 

  9. Simha, N. K., Carlson, C. S. & Lewis, J. L. Evaluation of fracture toughness of cartilage by micropenetration. J. Mater. Sci. Mater. Med. 14, 631–639 (2003)

    Google Scholar 

  10. Lake, G. J. Fatigue and fracture of elastomers. Rubber Chem. Technol. 68, 435–460 (1995)

    Article  CAS  Google Scholar 

  11. Gong, J. P., Katsuyama, Y., Kurokawa, T. & Osada, Y. Double-network hydrogels with extremely high mechanical strength. Adv. Mater. 15, 1155–1158 (2003)

    Article  CAS  Google Scholar 

  12. Huang, T. et al. A novel hydrogel with high mechanical strength: a macromolecular microsphere composite hydrogel. Adv. Mater. 19, 1622–1626 (2007)

    Article  CAS  Google Scholar 

  13. Sakai, T. et al. Design and fabrication of a high-strength hydrogel with ideally homogeneous network structure from tetrahedron-like macromonomers. Macromolecules 41, 5379–5384 (2008)

    Article  ADS  CAS  Google Scholar 

  14. Seitz, M. E. et al. Fracture and large strain behavior of self-assembled triblock copolymer gels. Soft Matter 5, 447–456 (2009)

    Article  ADS  CAS  Google Scholar 

  15. Lin, W.-C., Fan, W., Marcellan, A., Hourdet, D. & Creton, C. Large strain and fracture properties of poly(dimethylacrylamide)/silica hybrid hydrogels. Macromolecules 43, 2554–2563 (2010)

    Article  ADS  CAS  Google Scholar 

  16. Wang, Q. G. et al. High-water-content mouldable hydrogels by mixing clay and a dendritic molecular binder. Nature 463, 339–343 (2010)

    Article  ADS  CAS  Google Scholar 

  17. Haque, M. A., Kurokawa, T., Kamita, G. & Gong, J. P. Lamellar bilayers as reversible sacrificial bonds to toghen hydrogel: hysteresis, self-recovery, fatigue resistance, and crack blunting. Macromolecules 44, 8916–8924 (2011)

    Article  ADS  CAS  Google Scholar 

  18. Tuncaboylu, D. C., Sari, M., Oppermann, W. & Okay, O. Tough and self-healing hydrogels formed via hydrophobic interactions. Macromolecules 44, 4997–5005 (2011)

    Article  ADS  CAS  Google Scholar 

  19. Hui, C.-Y., Jagota, A., Bennison, S. J. & Londono, J. D. Crack blunting and the strength of soft elastic solids. Proc. R. Soc. Lond. A 459, 1489–1516 (2003)

    Article  ADS  Google Scholar 

  20. Yu, Q. M., Tanaka, Y., Furukawa, H., Kurokawa, T. & Gong, J. P. Direct observation of damage zone around crack tips in double-network gels. Macromolecules 42, 3852–3855 (2009)

    Article  ADS  CAS  Google Scholar 

  21. Webber, R. E., Creton, C., Brown, H. R. & Gong, J. P. Large strain hysteresis and mullins effect of tough double-network hydrogels. Macromolecules 40, 2919–2927 (2007)

    Article  ADS  CAS  Google Scholar 

  22. Henderson, K. J., Zhou, T. C., Otim, K. J. & Shull, K. R. Ionically cross-linked triblock copolymer hydrogels with high strength. Macromolecules 43, 6193–6201 (2010)

    Article  ADS  CAS  Google Scholar 

  23. Kong, H. J., Wong, E. & Mooney, D. J. Independent control of rigidity and toughness of polymeric hydrogels. Macromolecules 36, 4582–4588 (2003)

    Article  ADS  CAS  Google Scholar 

  24. Baumberger, T. & Ronsin, O. From thermally activated to viscosity controlled fracture of biopolymer hydrogels. J. Chem. Phys. 130, 061102 (2009)

    Article  ADS  CAS  Google Scholar 

  25. Evans, A. G. Perspective on the development of high-toughness ceramics. J. Am. Ceram. Soc. 73, 187–206 (1990)

    Article  CAS  Google Scholar 

  26. Brown, H. R. A model of fracture of double network gels. Macromolecules 40, 3815–3818 (2007)

    Article  ADS  CAS  Google Scholar 

  27. Tanaka, Y. A local damage model for anomalous high toughness of double-network gels. Europhys. Lett. 78, 56005 (2007)

    Article  ADS  Google Scholar 

  28. Jackson, A. P. Measurement of the fracture toughness of some contact lens hydrogels. Biomater. 11, 403–407 (1990)

    Article  CAS  Google Scholar 

  29. Hernández, R. M., Orive, G., Murua, A. & Pedraz, J. L. Microcapsules and microcarriers for in situ cell delivery. Adv. Drug Deliv. Rev. 62, 711–730 (2010)

    Article  Google Scholar 

  30. Maldonado-Codina, C. & Efron, N. Impact of manufacturing technology and material composition on the mechanical properties of hydrogel contact lenses. Ophthalmic Physiol. Opt. 24, 551–561 (2004)

    Article  Google Scholar 

Download references


The work at Harvard was supported by ARO (W911NF-09-1-0476), NSF (CMMI-0800161), DARPA (W911NF-10-1-0113), NIH (R37 DE013033) and MRSEC (DMR-0820484). X.Z. acknowledges the support of the NSF Research Triangle MRSEC (DMR-1121107) and Haythornthwaite Research Initiation grants. K.H.O. is supported by the National Research Foundation of Korea (NRF), funded by the Ministry of Education, Science and Technology (R11-2005-065). Z.S. acknowledges a sabbatical leave at the Karlsruhe Institute of Technology funded by the Alexander von Humboldt Award and by Harvard University.

Author information

Authors and Affiliations



J.-Y.S., X.Z., W.R.K.I., D.J.M., J.J.V. and Z.S. designed the study and interpreted the results. X.Z. developed the protocol for fabrication of the gels and prepared initial samples. J.-Y.S. and W.R.K.I. improved the protocol, and performed mechanical tests and recovery tests. J.-Y.S. obtained Fourier transform infrared spectra and performed thermogravimetric analysis. O.C. and J.-Y.S. conducted the experiment with fluorescent alginate and that using the atomic force microscope. K.H.O. contributed to the discussion of results. J.-Y.S., W.R.K.I. and Z.S. wrote the manuscript. All authors commented on the manuscript.

Corresponding author

Correspondence to Zhigang Suo.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary Information

This file contains Supplementary Text, Supplementary Figures 1-16, Supplementary References and Full Legends for Supplementary Movies 1-3. (PDF 1575 kb)

Supplementary Movie 1

This file contains a movie showing a crack initiating at the front of a blunted notch, and running rapidly across the sample (see Supplementary Information for full legend). (MOV 28645 kb)

Supplementary Movie 2

This file contains a movie that demonstrates large, recoverable deformation when a metal ball drops on a membrane of the hybrid gel (see Supplementary Information for full legend). (MOV 16813 kb)

Supplementary Movie 3

This file contains a movie that shows large deformation and rupture when a metal ball drops on a membrane of the hybrid gel (see Supplementary Information for full legend). (MOV 22398 kb)

PowerPoint slides

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Sun, JY., Zhao, X., Illeperuma, W. et al. Highly stretchable and tough hydrogels. Nature 489, 133–136 (2012).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing