Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Electromotive force and huge magnetoresistance in magnetic tunnel junctions


The electromotive force (e.m.f.) predicted by Faraday’s law reflects the forces acting on the charge, –e, of an electron moving through a device or circuit, and is proportional to the time derivative of the magnetic field. This conventional e.m.f. is usually absent for stationary circuits and static magnetic fields. There are also forces that act on the spin of an electron; it has been recently predicted1,2 that, for circuits that are in part composed of ferromagnetic materials, there arises an e.m.f. of spin origin even for a static magnetic field. This e.m.f. can be attributed to a time-varying magnetization of the host material, such as the motion of magnetic domains in a static magnetic field, and reflects the conversion of magnetic to electrical energy. Here we show that such an e.m.f. can indeed be induced by a static magnetic field in magnetic tunnel junctions containing zinc-blende-structured MnAs quantum nanomagnets. The observed e.m.f. operates on a timescale of approximately 102–103 seconds and results from the conversion of the magnetic energy of the superparamagnetic MnAs nanomagnets into electrical energy when these magnets undergo magnetic quantum tunnelling. As a consequence, a huge magnetoresistance of up to 100,000 per cent is observed for certain bias voltages. Our results strongly support the contention that, in magnetic nanostructures, Faraday’s law of induction must be generalized to account for forces of purely spin origin. The huge magnetoresistance and e.m.f. may find potential applications in high sensitivity magnetic sensors, as well as in new active devices such as ‘spin batteries’.

This is a preview of subscription content, access via your institution

Relevant articles

Open Access articles citing this article.

Access options

Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Figure 1: Device structure.
Figure 2: Transport characteristics of an MTJ.
Figure 3: Huge magnetoresistance.
Figure 4: Magnetic energy.


  1. Barnes, S. E. & Maekawa, S. Generalization of Faraday’s law to include nonconservative spin forces. Phys. Rev. Lett. 98, 246601 (2007)

    Article  ADS  CAS  Google Scholar 

  2. Barnes, S. E. Spin motive forces, “measurements”, and spin-valves. J. Magn. Magn. Mater. 310, 2035–2037 (2007)

    Article  ADS  CAS  Google Scholar 

  3. Fulton, T. A. & Dolan, G. J. Observation of single-electron charging effects in small tunnel junctions. Phys. Rev. Lett. 59, 109–112 (1987)

    Article  ADS  CAS  Google Scholar 

  4. Sanvito, S. & Hill, A. N. Ground state of half-metallic zinc-blende MnAs. Phys. Rev. B 62, 15553–15560 (2000)

    Article  ADS  CAS  Google Scholar 

  5. Sato, K., Katayama–Yoshida, H. & Dederichs, P. H. High Curie temperature and nano-scale spinodal decomposition phase in dilute magnetic semiconductors. Jpn. J. Appl. Phys. 44, L948–L951 (2005)

    Article  CAS  Google Scholar 

  6. Moreno, M., Trampert, A., Jenichen, B., Daweritz, L. & Ploog, K. H. Correlation of structure and magnetism in GaAs with embedded Mn(Ga)As magnetic nanoclusters. J. Appl. Phys. 92, 4672–4677 (2002)

    Article  ADS  CAS  Google Scholar 

  7. Yokoyama, M., Yamaguchi, H., Ogawa, T. & Tanaka, M. Zinc-blende-type MnAs nanoclusters embedded in GaAs. J. Appl. Phys. 97, 10D317 (2005)

    Article  Google Scholar 

  8. Kwiatkowski, A. et al. Structure and magnetism of MnAs nanocrystals embedded in GaAs as a function of post-growth annealing temperature. J. Appl. Phys. 101, 113912 (2007)

    Article  ADS  Google Scholar 

  9. Binasch, G., Grünberg, P., Saurenbach, F. & Zinn, W. Enhanced magnetoresistance in layered magnetic structures with antiferromagnetic interlayer exchange. Phys. Rev. B 39, 4828–4830 (1989)

    Article  ADS  CAS  Google Scholar 

  10. Baibich, M. N. et al. Giant magnetoresistance of (001)Fe/(001)Cr magnetic superlattices. Phys. Rev. Lett. 61, 2472–2475 (1988)

    Article  ADS  CAS  Google Scholar 

  11. Moodera, J. S., Kinder, L. R., Wong, T. M. & Meservey, R. Large magnetoresistance at room temperature in ferromagnetic thin film tunnel junctions. Phys. Rev. Lett. 74, 3273–3276 (1995)

    Article  ADS  CAS  Google Scholar 

  12. Miyazaki, T. & Tezuka, N. Giant magnetic tunnelling effect in Fe/Al2O3/Fe junction. J. Magn. Magn. Mater. 139, L231–L234 (1995)

    Article  ADS  CAS  Google Scholar 

  13. Parkin, S. S. P. Giant tunnelling magnetoresistance at room temperature with MgO (100) tunnel barriers. Nature Mater. 3, 862–867 (2004)

    Article  ADS  CAS  Google Scholar 

  14. Yuasa, S., Nagahama, T., Fukushima, A., Suzuki, Y. & Ando, K. Giant room-temperature magnetoresistance in single-crystal Fe/MgO/Fe magnetic tunnel junctions. Nature Mater. 3, 868–871 (2004)

    Article  ADS  CAS  Google Scholar 

  15. Jin, S. et al. Thousandfold change in resistivity in magnetoresistive La-Ca-Mn-O films. Science 264, 413–415 (1994)

    Article  ADS  CAS  Google Scholar 

  16. Tokura, Y. (ed.) Advances in Condensed Matter Science Vol. 2, Colossal Magnetoresistance Oxides (Gordon & Breach, 2000)

    Google Scholar 

  17. Barnes, S. E., Ieda, J. & Maekawa, S. Magnetic memory and current amplification devices using moving domain walls. Appl. Phys. Lett. 89, 122507 (2006)

    Article  ADS  Google Scholar 

  18. Barnes, S. E. & Maekawa, S. Currents induced by domain wall motion in thin ferromagnetic wires. Preprint at 〈〉 (2004)

  19. Barbara, B. et al. Mesoscopic quantum tunnelling of magnetization. J. Magn. Magn. Mater. 140–144, 1825–1828 (2002)

    Google Scholar 

  20. Tanaka, M. et al. Epitaxial orientation and magnetic properties of MnAs thin films grown on (001) GaAs: Template effects. Appl. Phys. Lett. 65, 1964–1966 (1994)

    Article  ADS  CAS  Google Scholar 

  21. Tanaka, M. Ferromagnet (MnAs)/III–V semiconductor hybrid structures. Semicond. Sci. Technol. 17, 327–341 (2002)

    Article  ADS  CAS  Google Scholar 

Download references


This work was partly supported by Grant-in-Aids for Scientific Research No. 18106007, No. 19048018 and No. 20686002, the Special Coordination Programs for Promoting Science and Technology, and R&D for Next-Generation Information Technology by MEXT, PRESTO of JST, and EPSRC (UK). We thank B.-H. Yu for his help in the transport measurements. P.N.H. acknowledges a JSPS Research Fellowship for Young Scientists and the Global COE Program (CO4).

Author Contributions P.N.H. designed the experiment, fabricated the samples, collected most of data and performed analysis of data; S.O. set up measurement apparatuses and gave experimental advice; M.T. managed and planned the research and supervised the experiment; and S.E.B. and S.M. developed the theoretical explanation of the experiment. All authors discussed the results and commented on the manuscript.

Author information

Authors and Affiliations


Corresponding author

Correspondence to Masaaki Tanaka.

Supplementary information

Supplementary Information

This file contains Supplementary Notes, Supplementary Figures S1-S5 with Legends and Supplementary References (PDF 835 kb)

PowerPoint slides

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Hai, P., Ohya, S., Tanaka, M. et al. Electromotive force and huge magnetoresistance in magnetic tunnel junctions. Nature 458, 489–492 (2009).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing