Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

A 160-kilobit molecular electronic memory patterned at 1011 bits per square centimetre


The primary metric for gauging progress in the various semiconductor integrated circuit technologies is the spacing, or pitch, between the most closely spaced wires within a dynamic random access memory (DRAM) circuit1. Modern DRAM circuits have 140 nm pitch wires and a memory cell size of 0.0408 μm2. Improving integrated circuit technology will require that these dimensions decrease over time. However, at present a large fraction of the patterning and materials requirements that we expect to need for the construction of new integrated circuit technologies in 2013 have ‘no known solution’1. Promising ingredients for advances in integrated circuit technology are nanowires2, molecular electronics3 and defect-tolerant architectures4, as demonstrated by reports of single devices5,6,7 and small circuits8,9. Methods of extending these approaches to large-scale, high-density circuitry are largely undeveloped. Here we describe a 160,000-bit molecular electronic memory circuit, fabricated at a density of 1011 bits cm-2 (pitch 33 nm; memory cell size 0.0011 μm2), that is, roughly analogous to the dimensions of a DRAM circuit1 projected to be available by 2020. A monolayer of bistable, [2]rotaxane molecules10 served as the data storage elements. Although the circuit has large numbers of defects, those defects could be readily identified through electronic testing and isolated using software coding. The working bits were then configured to form a fully functional random access memory circuit for storing and retrieving information.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Get just this article for as long as you need it


Prices may be subject to local taxes which are calculated during checkout

Figure 1: SEMs of the nanowire crossbar memory.
Figure 2: Structural formula of the bistable [2]rotaxane used in the crossbar memory.
Figure 3: Data from evaluating the performance of the 128 ebits within the crossbar memory circuit.
Figure 4: Demonstration of memory storage and retention characteristics from the molecular electronic crossbar memory.


  1. The International Technology Roadmap for Semiconductors (ITRS): process integration, devices, and structures. (Semiconductor Industry Association, San Jose, California, 2005). 〈〉.

  2. Yang, P. & Kim, F. Langmuir-Blodgett assembly of one-dimensional nanostructures. ChemPhysChem 3, 503–506 (2002)

    Article  CAS  Google Scholar 

  3. Heath, J. R. & Ratner, M. A. Molecular electronics. Phys. Today 56, 43–49 (2003)

    Article  ADS  CAS  Google Scholar 

  4. Heath, J. R., Kuekes, P. J., Snider, G. S. & Williams, R. S. A defect-tolerant computer architecture: Opportunities for nanotechnology. Science 280, 1716–1721 (1998)

    Article  CAS  Google Scholar 

  5. Xiang, J. et al. Ge/Si nanowire heterostructures as high-performance field-effect transistors. Nature 441, 489–493 (2006)

    Article  ADS  CAS  Google Scholar 

  6. Zhou, X., Park, J. Y., Huang, S., Liu, J. & McEuen, P. L. Band structure, phonon scattering, and the performance limit of single-walled carbon nanotube transistors. Phys. Rev. Lett. 95, 146805 (2005)

    Article  ADS  Google Scholar 

  7. Pop, E. et al. Negative differential conductance and hot phonons in suspended nanotube molecular wires. Phys. Rev. Lett. 95, 155505 (2005)

    Article  ADS  Google Scholar 

  8. Chen, Z. et al. An integrated logic circuit assembled on a single carbon nanotube. Science 311, 1735 (2006)

    Article  CAS  Google Scholar 

  9. Zhong, Z. H., Wang, D. L., Cui, Y., Bockrath, M. W. & Lieber, C. M. Nanowire crossbar arrays as address decoders for integrated nanosystems. Science 302, 1377–1379 (2003)

    Article  ADS  CAS  Google Scholar 

  10. Choi, J. W. et al. Ground-state equilibrium thermodynamics and switching kinetics of bistable [2]rotaxanes switched in solution, polymer gels, and molecular electronic devices. Chem. Eur. J. 12, 261–279 (2006)

    Article  CAS  Google Scholar 

  11. DeHon, A. & Naeimi, H. Seven strategies for tolerating highly defective fabrication. IEEE Design Test Comput. 22, 306–315 (2005)

    Article  Google Scholar 

  12. Lee, M. H., Kim, Y. K. & Choi, Y. H. A defect-tolerant memory architecture for molecular electronics. IEEE Trans. Nanotechnol. 3, 152–157 (2004)

    Article  ADS  Google Scholar 

  13. DeHon, A., Goldstein, S. C., Kuekes, P. J. & Lincoln, P. Nonphotolithographic nanoscale memory density prospects. IEEE Trans. Nanotechnol. 4, 215–228 (2005)

    Article  ADS  Google Scholar 

  14. Snider, G., Kuekes, P., Hogg, T. & Williams, R. S. Nanoelectronic architectures. Appl. Phys. A 80, 1183–1195 (2005)

    Article  CAS  Google Scholar 

  15. Stan, M. R., Franzon, P. D., Goldstein, S. C., Lach, J. C. & Ziegler, M. M. Molecular electronics: From devices and interconnect to circuits and architecture. Proc. IEEE 91, 1940–1957 (2003)

    Article  CAS  Google Scholar 

  16. Diehl, M., Beckman, R., Yaliraki, S. & Heath, J. R. Self-assembly of deterministic carbon nanotube wiring networks. Angew. Chem. Int. Edn Engl. 41, 353–356 (2002)

    Article  CAS  Google Scholar 

  17. Wu, W. et al. One-kilobit cross-bar molecular memory circuits at 30-nm half-pitch fabricated by nanoimprint lithography. Appl. Phys. A 80, 1173–1178 (2005)

    Article  CAS  Google Scholar 

  18. Huang, Y., Duan, X. F., Wei, Q. Q. & Lieber, C. M. Directed assembly of one-dimensional nanostructures into functional networks. Science 291, 630–633 (2001)

    Article  ADS  CAS  Google Scholar 

  19. Melosh, N. A. et al. Ultrahigh-density nanowire lattices and circuits. Science 300, 112–115 (2003)

    Article  ADS  CAS  Google Scholar 

  20. Luo, Y. et al. Two-dimensional molecular electronics circuits. ChemPhysChem 3, 519–525 (2002)

    Article  CAS  Google Scholar 

  21. Vieu, C. et al. Electron beam lithography: resolution limits and applications. Appl. Surf. Sci. 164, 111–117 (2000)

    Article  ADS  CAS  Google Scholar 

  22. Beckman, R., Johnston-Halperin, E., Luo, Y., Green, J. E. & Heath, J. R. Bridging dimensions: demultiplexing ultrahigh-density nanowire circuits. Science 310, 465–468 (2005)

    Article  ADS  CAS  Google Scholar 

  23. Parkin, S. S. P. et al. Exchange-biased magnetic tunnel junctions and application to nonvolatile magnetic random access memory. J. Appl. Phys. 85, 5828–5833 (1999)

    Article  ADS  CAS  Google Scholar 

  24. McCreery, R. L. Molecular electronic junctions. Chem. Mater. 16, 4477–4496 (2004)

    Article  CAS  Google Scholar 

  25. Chen, Y. et al. Nanoscale molecular-switch crossbar circuits Nanotechnology. 14, 462–468 (2003)

    Article  ADS  CAS  Google Scholar 

  26. Allwood, D. A. et al. Magnetic domain-wall logic. Science 309, 1688–1692 (2005)

    Article  ADS  CAS  Google Scholar 

  27. Waser, R. & Rudiger, A. Ferroelectrics—pushing towards the digital storage limit. Nature Mater. 3, 81–82 (2004)

    Article  ADS  CAS  Google Scholar 

  28. Katz, E., Baron, R., Willner, I., Richke, N. & Levine, R. D. Temperature-dependent and friction-controlled electrochemically induced shuttling along molecular strings associated with electrodes. ChemPhysChem 6, 2179–2189 (2005)

    Article  CAS  Google Scholar 

  29. Jung, G. Y. et al. Circuit fabrication at 17 nm half-pitch by nanoimprint lithography. Nano Lett. 6, 351–354 (2006)

    Article  ADS  CAS  Google Scholar 

Download references


This work was supported primarily by the DARPA MolApps Program with additional support from the MARCO Center for Advanced Materials and Devices and the National Science Foundation. J.W.C. and Y.S.S. acknowledge fellowships from the Samsung Corporation. We are grateful to Y. Liu and S. Saha for preparing the [2]rotaxane molecule used in this work. Author Contributions The [2]rotaxane molecular switches were designed and originally synthesized by H.-R.T. and J.F.S. All other authors contributed to the design, fabrication and testing of the memory circuit.

Author information

Authors and Affiliations


Corresponding author

Correspondence to James R. Heath.

Ethics declarations

Competing interests

Reprints and permissions information is available at The authors declare no competing financial interests.

Supplementary information

Supplementary Information

This file contains Supplementary Methods (including Supplementary Figures 1-4 and Legends); Supplementary Discussion (including Supplementary Figure 5 and Legend) and Supplementary Notes. The Supplementary Methods include a detailed description of the fabrication and testing of the memory circuit. The Supplementary Discussion presents what is known about the current rectification of the individual bits (crosspoint junctions) within the memory, as well as discussion related to the limits of scaling that are possible using our nanofabrication methods. (PDF 812 kb)

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Green, J., Wook Choi, J., Boukai, A. et al. A 160-kilobit molecular electronic memory patterned at 1011 bits per square centimetre. Nature 445, 414–417 (2007).

Download citation

  • Received:

  • Accepted:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing