Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Visualizing dislocation nucleation by indenting colloidal crystals


The formation of dislocations is central to our understanding of yield, work hardening, fracture, and fatigue1 of crystalline materials. While dislocations have been studied extensively in conventional materials, recent results have shown that colloidal crystals offer a potential model system for visualizing their structure and dynamics directly in real space2. Although thermal fluctuations are thought to play a critical role in the nucleation of these defects, it is difficult to observe them directly. Nano-indentation, during which a small tip deforms a crystalline film, is a common tool for introducing dislocations into a small volume that is initially defect-free3,4,5,6,7,8,9,10. Here, we show that an analogue of nano-indentation performed on a colloidal crystal provides direct images of defect formation in real time and on the single particle level, allowing us to probe the effects of thermal fluctuations. We implement a new method to determine the strain tensor of a distorted crystal lattice and we measure the critical dislocation loop size and the rate of dislocation nucleation directly. Using continuum models, we elucidate the relation between thermal fluctuations and the applied strain that governs defect nucleation. Moreover, we estimate that although bond energies between particles are about fifty times larger in atomic systems, the difference in attempt frequencies makes the effects of thermal fluctuations remarkably similar, so that our results are also relevant for atomic crystals.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Figure 1: Laser diffraction microscopy images of defect structure.
Figure 2: Defect formation on the particle scale.
Figure 3: Strain distribution in the indented crystalline film.
Figure 4: Continuum model prediction for the critical radius and energy of dislocation nucleation.

Similar content being viewed by others


  1. Hirth, J. P. & Lothe, J. Theory of Dislocations Edn 2 (Wiley, New York, 1982)

    Google Scholar 

  2. Schall, P., Cohen, I., Weitz, D. A. & Spaepen, F. Visualization of dislocation dynamics in collidal crystals. Science 305, 1944–1948 (2004)

    Article  ADS  CAS  PubMed  Google Scholar 

  3. Suresh, S., Nieh, T.-G. & Choi, B. W. Nano-indentation of copper thin films on silicon substrates. Scr. Mater. 41, 951–957 (1999)

    Article  CAS  Google Scholar 

  4. Kiely, J. D., Jarausch, K. F., Houston, J. E. & Russell, P. E. Initial stages of yield in nanoindentation. J. Mater. Res. 14, 2219–2227 (1999)

    Article  ADS  CAS  Google Scholar 

  5. Li, J., van Vliet, K. J., Zhu, T., Yip, S. & Suresh, S. Atomistic mechanism governing elastic limit and incipient plasticity in crystals. Nature 418, 307–310 (2002)

    Article  ADS  CAS  PubMed  Google Scholar 

  6. Gouldstone, A., Van Vliet, K. J. & Suresh, S. Simulation of defect nucleation in a crystal. Nature 411, 656 (2001)

    Article  ADS  CAS  PubMed  Google Scholar 

  7. Kelchner, C. L., Plimpton, S. J. & Hamilton, J. C. Dislocation nucleation and defect structure during surface indentation. Phys. Rev. B 58, 11085–11088 (1998)

    Article  ADS  CAS  Google Scholar 

  8. Lilleodden, E. T., Zimmerman, J. A., Foiles, S. M. & Nix, W. D. Atomistic simulations of elastic deformation and dislocation nucleation during nanoindentation. J. Mech. Phys. Sol. 51, 901–920 (2003)

    Article  ADS  CAS  Google Scholar 

  9. Stach, E. A. et al. Development of a nanoindenter for in situ transmission electron micoroscopy. Microsc. Microanal. 7, 507–517 (2001)

    Article  ADS  CAS  PubMed  Google Scholar 

  10. Minor, A. M., Lilleodden, E. T., Stach, E. A. & Morris, J. W. Direct observation of incipient plasticity during nanoindentation of Al. J. Mater. Res. 19, 176–182 (2004)

    Article  ADS  CAS  Google Scholar 

  11. van Blaaderen, A., Ruel, R. & Wiltzius, P. Template-directed colloidal crystallization. Nature 385, 321–324 (1997)

    Article  ADS  CAS  Google Scholar 

  12. Weeks, E. R., Crocker, J. C., Levitt, A. C., Schofield, A. & Weitz, D. A. Three-dimensional direct space imaging of structural relaxation near the colloidal glass transition. Science 287, 627–631 (2000)

    Article  ADS  CAS  PubMed  Google Scholar 

  13. Falk, M. L. & Langer, J. S. Dynamics of viscoplastic deformation in amorphous solids. Phys. Rev. E 57, 7192–7205 (1998)

    Article  ADS  CAS  Google Scholar 

  14. Frank, F. C. in Symposium on Plastic Deformation of Crystalline Solids 89–102 (Carnegie Institute of Technology and Office of Naval Research, Pittsburgh, 1950)

    Google Scholar 

  15. Hirth, J. P. in The Relation Between the Structure and the Mechanical Properties of Metals 217–228 (Her Majesty's Stationery Office, London, 1963)

    Google Scholar 

  16. Cottrell, A. H. Dislocations and Plastic Flow in Crystals (Oxford Univ. Press, Oxford, 1956)

    Google Scholar 

  17. Davies, R. M. The determination of static and dynamic yield stresses using a steel ball. Proc. R. Soc. Lond. A 197, 416–432 (1949)

    Article  ADS  Google Scholar 

  18. Chaikin, P. M. & Lubensky, T. C. Principles of Condensed Matter Physics Ch. 7.4.5 (Cambridge Univ. Press, Cambridge, 1995)

    Book  Google Scholar 

  19. Higashigaki, Y., Christensen, D. H. & Wang, C. H. Studies of the reorientational motion and intermolecular interaction of dimethylsulfoxide in water by depolarized Rayleigh-scattering. J. Phys. Chem. 85, 2531–2535 (1981)

    Article  CAS  Google Scholar 

  20. Frenkel, D. & Ladd, A. J. C. Elastic constants of hard-sphere crystals. Phys. Rev. Lett. 59, 1169 (1987)

    Article  ADS  CAS  PubMed  Google Scholar 

Download references


We thank R. Christianson and D. Blair for their help with the image analysis, M.L. Falk for discussions about the strain algorithm, and D. Bonner for help with programming the strain algorithm. This work was supported by a Lynen Fellowship from the Alexander von Humboldt Foundation (P.S.), and by NSF and Harvard MRSEC grants.

Author information

Authors and Affiliations


Corresponding author

Correspondence to Peter Schall.

Ethics declarations

Competing interests

Reprints and permissions information is available at The authors declare no competing financial interests.

Supplementary information

Supplementary Video

This movie shows laser diffraction microscopy images of the nucleation and growth of dislocations during indentation of a colloidal crystalline film. The time lapse covers a period of 10 h, during which we slowly move the indenting tip into the crystalline sediment at a rate of 3.4µm/h and subsequently pull it back at a rate of 20µm/min. After the initial emergence of a strain field depicted as a two-armed contrast profile and the nucleation of a first dislocation loop depicted as a dark circular spot, a complex dislocation structure evolves. This structure relaxes and partially heals when the needle moves back up. These images also show local intensity fluctuations in both the strained and unstrained crystal lattice that correspond to thermally excited fluctuations in the particle configurations. (MOV 8836 kb)

Rights and permissions

Reprints and permissions

About this article

Cite this article

Schall, P., Cohen, I., Weitz, D. et al. Visualizing dislocation nucleation by indenting colloidal crystals. Nature 440, 319–323 (2006).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing