Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

General observation of n-type field-effect behaviour in organic semiconductors


Organic semiconductors have been the subject of active research for over a decade now, with applications emerging in light-emitting displays and printable electronic circuits. One characteristic feature of these materials is the strong trapping of electrons but not holes1: organic field-effect transistors (FETs) typically show p-type, but not n-type, conduction even with the appropriate low-work-function electrodes, except for a few special high-electron-affinity2,3,4 or low-bandgap5 organic semiconductors. Here we demonstrate that the use of an appropriate hydroxyl-free gate dielectric—such as a divinyltetramethylsiloxane-bis(benzocyclobutene) derivative (BCB; ref. 6)—can yield n-channel FET conduction in most conjugated polymers. The FET electron mobilities thus obtained reveal that electrons are considerably more mobile in these materials than previously thought. Electron mobilities of the order of 10-3 to 10-2 cm2 V-1 s-1 have been measured in a number of polyfluorene copolymers and in a dialkyl-substituted poly(p-phenylenevinylene), all in the unaligned state. We further show that the reason why n-type behaviour has previously been so elusive is the trapping of electrons at the semiconductor–dielectric interface by hydroxyl groups, present in the form of silanols in the case of the commonly used SiO2 dielectric. These findings should therefore open up new opportunities for organic complementary metal-oxide semiconductor (CMOS) circuits, in which both p-type and n-type behaviours are harnessed.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Figure 1: F8BT and OC1C10 - PPV n-channel FETs with BCB/SiO2 dielectric and Ca source-drain electrodes.
Figure 2: Evidence from vibrational spectroscopy for interfacial electron trapping on standard silicon oxide/silicon backgate device structures during attempted n-channel FET operation.
Figure 3: F8BT n-channel FETs with various siloxane self-assembled monolayers (SAMs) on SiO2 as dielectric, or with polyethylene as buffer dielectric.
Figure 4: Ambipolar F8T2 and regioregular-P3HT FETs.

Similar content being viewed by others


  1. Dimitrakopoulos, C. D. & Malenfant, P. R. L. Organic thin film transistors for large area electronics. Adv. Mater. 14, 99–117 (2002)

    Article  CAS  Google Scholar 

  2. Dodabalapur, A., Katz, H. E., Torsi, L. & Haddon, R. C. Organic heterostructure field-effect transistors. Science 269, 1560–1562 (1995)

    Article  ADS  CAS  Google Scholar 

  3. Katz, H. E. et al. A soluble and air-stable organic semiconductor with high electron mobility. Nature 404, 478–481 (2000)

    Article  ADS  CAS  Google Scholar 

  4. Babel, A. & Jenekhe, S. A. High electron mobility in ladder polymer field-effect transistors. J. Am. Chem. Soc. 125, 13656–13657 (2003)

    Article  CAS  Google Scholar 

  5. Meijer, E. J. et al. Solution-processed ambipolar organic field-effect transistors and inverters. Nature Mater. 2, 678–682 (2003)

    Article  ADS  CAS  Google Scholar 

  6. Chua, L. L., Ho, P. K. H., Sirringhaus, H. & Friend, R. H. High stability ultrathin spin-on benzocyclobutene gate dielectric for polymer field-effect transistors. Appl. Phys. Lett. 84, 3400–3402 (2004)

    Article  ADS  CAS  Google Scholar 

  7. Veres, J., Ogier, S. D., Leeming, S. W., Cupertino, D. C. & Khaffaf, S. M. Low-k insulators as the choice of dielectrics in organic field-effect transistors. Adv. Funct. Mater. 13, 199–204 (2003)

    Article  CAS  Google Scholar 

  8. Chua, L. L., Ho, P. K. H., Sirringhaus, H. & Friend, R. H. Observation of field-effect behaviour at self-organised interfaces. Adv. Mater. 16, 1609–1615 (2004)

    Article  CAS  Google Scholar 

  9. Brown, A. R., De Leeuw, D. M., Lous, E. J. & Havinga, E. E. Organic n-type field-effect transistors. Synth. Met. 66, 257–261 (1994)

    Article  CAS  Google Scholar 

  10. Sirringhaus, H. et al. Mobility enhancement in conjugated polymer field-effect transistors through chain alignment in a liquid-crystalline phase. Appl. Phys. Lett. 77, 406–408 (2000)

    Article  ADS  CAS  Google Scholar 

  11. Kim, J. S., Ho, P. K. H., Greenham, N. C. & Friend, R. H. Electroluminescence emission pattern of organic light-emitting diodes: Implications for device efficiency calculations. J. Appl. Phys. 88, 1073–1081 (2000)

    Article  ADS  CAS  Google Scholar 

  12. Bozano, L., Carter, S., Scott, J., Malliaras, G. & Brock, P. Temperature- and field-dependent electron and hole mobilities in polymer light-emitting diodes. Appl. Phys. Lett. 74, 1132–1134 (1999)

    Article  ADS  CAS  Google Scholar 

  13. Ho, P. K. H. et al. Molecular-scale interface engineering for polymer light-emitting diodes. Nature 404, 481–484 (2000)

    Article  ADS  CAS  Google Scholar 

  14. Nagasawa, Y. et al. The study of the thermal oxide films on silicon wafers by Fourier transform infrared attenuated total reflection spectroscopy. J. Appl. Phys. 68, 1429–1434 (1990)

    Article  ADS  CAS  Google Scholar 

  15. Dugas, V. & Chevalier, Y. Surface hydroxylation and silane grafting on fumed and thermal silica. J. Colloid Interf. Sci. 264, 354–361 (2003)

    Article  ADS  CAS  Google Scholar 

  16. Perry, C. C. & Li, X. Structural studies of gel phases. J. Chem. Soc. Faraday Trans. 87, 3857–3862 (1991)

    Article  CAS  Google Scholar 

  17. Tardif, F., Chabli, A., Kanel, A., Rochat, N. & Veillerot, M. Thermal evolution of chemical oxides and (100) silicon at 300 °C in ambient air as seen by attenuated total reflection infrared spectroscopy. J. Electrochem. Soc. 150, G333–G338 (2003)

    Article  CAS  Google Scholar 

  18. Nicollian, E. H., Berglund, C. N., Schmidt, P. F. & Andrews, J. M. Electrochemical charging of thermal SiO2 films by injected electron currents. J. Appl. Phys. 42, 5654–5664 (1971)

    Article  ADS  CAS  Google Scholar 

  19. Hartstein, A. & Young, D. R. Identification of electron traps in thermal silicon dioxide films. Appl. Phys. Lett. 38, 631–633 (1981)

    Article  ADS  CAS  Google Scholar 

  20. Malenfant, P. R. L. et al. N-type organic thin-film transistor with high field-effect mobility based on a N-N′-dialkyl-3,4,9,10-perylene tetracarboxylic diimide derivative. Appl. Phys. Lett. 80, 2517–2519 (2002)

    Article  ADS  CAS  Google Scholar 

  21. Salleo, A., Chabinyc, M. L., Yang, M. S. & Street, R. A. Polymer thin-film transistors with chemically modified dielectric interfaces. Appl. Phys. Lett. 81, 4383–4385 (2002)

    Article  ADS  CAS  Google Scholar 

  22. Angst, D. L. & Simmons, G. W. Moisture absorption characteristics of organosiloxane self-assembled monolayers. Langmuir 7, 2236–2242 (1991)

    Article  CAS  Google Scholar 

  23. Wasserman, S. R., Tao, Y. T. & Whitesides, G. M. Structure and reactivity of alkylsiloxane monolayers formed by reaction of alkyltrichlorosilanes on silicon substrates. Langmuir 5, 1074–1087 (1989)

    Article  CAS  Google Scholar 

  24. Sirringhaus, H. et al. Two-dimensional charge transport in self-organised, high-mobility conjugated polymers. Nature 401, 685–688 (1999)

    Article  ADS  CAS  Google Scholar 

  25. Wilson, R. J. Polymer Field-effect Transistors from Polyfluorene-based Conjugated Polymers. PhD thesis, Univ. Cambridge (2002)

    Google Scholar 

Download references


We thank A. Achen for providing the BCB material, which is commercially available as Dow Cyclotene, and Merck KGaA for P3HT. L-L.C. and J-F.C. thank the EPSRC Carbon-Based Electronics programme for support, and J.Z. thanks the Gates Cambridge Trust for support. P.K-H.H. thanks St John's College for a research fellowship, the National University of Singapore for research support, and S. J. Chua for technical discussions, support and access to laboratory facilities. We also thank C.-C. Chum for technical support.

Author information

Authors and Affiliations


Corresponding authors

Correspondence to Peter K.-H. Ho or Richard H. Friend.

Ethics declarations

Competing interests

H.S. and R.H.F. are directors of Plastic Logic Ltd, a University of Cambridge start-up company with activities within this broad field.

Supplementary information

Supplementary Figures S1-S3

Supplementary Figure S1 provides further examples of polymer gate dielectrics that have also yielded n-channel FETs. Supplementary Figure S2 provides evidence that long chain self-assembled monolayers slow down occupation but do not completely passivate the electron traps at the SiO2 interface. Supplementary Figure S3 provides further evidence for electron-trapping from the gate-threshold shifts in p-type FETs after positive gate biasing. (PDF 187 kb)

Supplementary Discussion

This section discusses the differing time scales for trapping of electrons, which is probed by decay of the electron field-effect current, and for advancement of the electrochemical reaction front across the channel length, which is probed by the ATR-FTIR experiment. (PDF 78 kb)

Rights and permissions

Reprints and permissions

About this article

Cite this article

Chua, LL., Zaumseil, J., Chang, JF. et al. General observation of n-type field-effect behaviour in organic semiconductors. Nature 434, 194–199 (2005).

Download citation

  • Received:

  • Accepted:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing