Formation of zirconium metallic glass

Article metrics

  • This article was retracted on 13 October 2005


Bulk metallic glasses are commonly produced by the rapid cooling of liquid alloys1. They have emerged over the past decade as a novel class of materials, with attractive properties and technological promise1,2. The bulk metallic glasses so far produced contain three or more component elements3,4. These complex compositions are necessary to frustrate the crystallization of the liquid melt on cooling, but can also lead to phase separation, which is detrimental to the thermal and mechanical properties of metallic glasses5,6,7,8. Here we report, using X-ray diffraction measurements, the formation of a bulk metallic glass from elemental zirconium at high static pressures and low temperatures (relative to its melting temperature at atmospheric pressure). Amorphous zirconium can be recovered at ambient conditions and demonstrates a superior thermal stability compared to amorphous alloys3,9, which could lead to new high-temperature applications of amorphous metals.

Access optionsAccess options

Rent or Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Figure 1: Glass-forming conditions and stability of amorphous zirconium.
Figure 2: Selected synchrotron X-ray diffraction patterns showing a reversible transformation between ω-phase and amorphous phases of zirconium metal.
Figure 3: Selected diffraction patterns showing the ω–β phase transition and formation of glass from the β-phase of zirconium metal at 8.6 GPa.
Figure 4: Experimental results demonstrating thermal stability/metastability of zirconium metallic glass.


  1. 1

    Loffler, J. F. Bulk metallic glasses. Intermetallics 11, 529–540 (2003)

  2. 2

    Johnson, W. L. Bulk glass-forming metallic alloys: science and technology. MRS Bull. 24, 42–56 (1999)

  3. 3

    Inoue, A. Stabilization of metallic supercooled liquid and bulk amorphous alloys. Acta Mater. 48, 279–306 (2000)

  4. 4

    Busch, R. The thermophysical properties of bulk metallic glass-forming liquids. J. Miner. Metals Mater. Soc. 52, 39–42 (2000)

  5. 5

    Miller, M. K. Decomposition of bulk metallic glasses. Mater. Sci. Eng. A 250, 133–140 (1998)

  6. 6

    Loffler, J. F. & Johnson, W. L. Model for decomposition and nano-crystallization of deeply undercooled Zr41.2Ti13.8Cu12.5Ni10Be22.5 . Appl. Phys. Lett. 76, 3394–3396 (2000)

  7. 7

    Kundig, A. A., Loffler, J. F., Johnson, W. L., Uggowitzer, P. J. & Thiyagarajan, P. Influence of decomposition on the thermal stability of undercooled Zr-Ti-Cu-Ni-Al alloys. Scripta Mater. 44, 1269–1273 (2001)

  8. 8

    Busch, R., Schneider, S., Peker, A. & Johnson, W. L. Decomposition and primary crystallization in undercooled Zr41.2Ti13.8Cu12.5Ni10Be22.5 melts. Appl. Phys. Lett. 67, 1544–1546 (1995)

  9. 9

    Wang, W. H. et al. Role of addition in formation and properties of Zr-based bulk metallic glasses. Intermetallics 10, 1249–1257 (2002)

  10. 10

    Eckert, J., Mattern, N., Zinkevitch, M. & Seidel, M. Crystallization behavior and phase formation in Zr-Al-Cu-Ni metallic glass containing oxygen. Mater. Trans. 39, 623–632 (1998)

  11. 11

    Busch, R., Masuhr, A., Bakke, E. & Johnson, W. L. Bulk metallic glass formation from strong liquids. Mater. Sci. Forum 269, 547–552 (1998)

  12. 12

    Ashby, M. F. & Jones, D. R. Engineering Materials 2: An Introduction to Microstructures, Processing and Design (Pergamon, Oxford, 1986)

  13. 13

    Weidner, D. J., et al. in High-Pressure Research: Application to Earth and Planetary Sciences (eds Syono, Y. & Manghnani, M. H.) 13–17 (Geophysics Monograph Series, Vol. 67, American Geophysical Union, Washington DC, 1992)

  14. 14

    Vaughan, M. T. et al. T-cup: A new high-pressure apparatus for X-ray studies. Rev. High Press. Sci. Technol. 7, 1520–1522 (1998)

  15. 15

    Zhao, Y., Von Dreele, R. B. & Morgan, J. G. A high P-T cell assembly for neutron diffraction up to 10 GPa and 1500 K. High Press. Res. 16, 161–177 (1999)

  16. 16

    Decker, D. L. High-pressure equation of state for NaCl, KCl and CsCl. J. Appl. Phys. 42, 3239–3244 (1971)

  17. 17

    Jayaraman, A., Klement, W. & Kennedy, G. C. Solid-solid transition in titanium and zirconium at high pressures. Phys. Rev. 131, 644–649 (1963)

  18. 18

    Xia, H., Duclos, S. J., Ruoff, A. L. & Vohra, Y. K. New high-pressure phase transition in zirconium metal. Phys. Rev. Lett. 64, 204–207 (1990)

  19. 19

    Xia, H., Ruoff, A. L. & Vohra, Y. K. Temperature-dependence of the ω-bcc phase transition in zirconium metal. Phys. Rev. B 44, 10374–10376 (1991)

  20. 20

    Jona, F. & Marcus, P. M. Zirconium under pressure: Structure anomalies and phase transitions. J. Phys. Condens. Matter 15, 5009–5019 (2003)

  21. 21

    Ostanin, S. A. & Trubitsin, V. Y. Calculation of the P-T phase diagram of Zr in different approximations for the exchange-correlation energy. Phys. Rev. B 57, 13485–13490 (1998)

  22. 22

    Hemley, R. J., Jephcoat, A. P., Mao, H. K., Ming, L. C. & Manghnani, M. H. Pressure-induced amorphization of crystalline silica. Nature 334, 52–54 (1988)

  23. 23

    Mishima, O., Calvert, L. D. & Whalley, E. Melting of ice-I at 77 K and 10 Kbar: A new method of making amorphous solids. Nature 310, 393–395 (1984)

  24. 24

    Highmore, R. J. & Greer, A. L. Eutectics and the formation of amorphous alloys. Nature 339, 363–365 (1988)

  25. 25

    Richet, P. & Gillet, P. Pressure-induced amorphization of minerals: a review. Eur. J. Miner. 9, 907–933 (1997)

  26. 26

    Heiming, A. et al. Phonon-dispersion of the bcc phase of group-IV metals 2: Bcc zirconium, a model case of dynamic precursors of martensitic transitions. Phys. Rev. B 43, 10948–10962 (1991)

  27. 27

    Olijnyk, H. & Jephcoat, A. P. Effect of pressure on Raman phonons in zirconium metal. Phys. Rev. B 56, 10751–10753 (1997)

  28. 28

    Pinsook, U. & Ackland, G. J. Calculation of anomalous phonons and the hcp-bcc phase transition in zirconium. Phys. Rev. B 59, 13642–13649 (1999)

Download references


This work was performed under the auspices of the US Department of Energy with the University of California. The synchrotron X-ray diffraction experiments were conducted at X17B2 beamline of NSLS and BM-13 beamline of APS, operated by COMPRES and GESCARS, respectively.

Author information

Correspondence to Jianzhong Zhang.

Ethics declarations

Competing interests

The authors declare that they have no competing financial interests.

Supplementary information

Supplementary Figure 1a

An x-ray scattering image recorded in a CCD detector. (PPT 216 kb)

Supplementary Figure 1b

The integrated diffraction pattern for the recovered zirconium specimen. (PPT 89 kb)

Supplementary Information (DOC 23 kb)

Rights and permissions

Reprints and Permissions

About this article

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.