Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Superconductivity in diamond


Diamond is an electrical insulator well known for its exceptional hardness. It also conducts heat even more effectively than copper, and can withstand very high electric fields1. With these physical properties, diamond is attractive for electronic applications2, particularly when charge carriers are introduced (by chemical doping) into the system. Boron has one less electron than carbon and, because of its small atomic radius, boron is relatively easily incorporated into diamond3; as boron acts as a charge acceptor, the resulting diamond is effectively hole-doped. Here we report the discovery of superconductivity in boron-doped diamond synthesized at high pressure (nearly 100,000 atmospheres) and temperature (2,500–2,800 K). Electrical resistivity, magnetic susceptibility, specific heat and field-dependent resistance measurements show that boron-doped diamond is a bulk, type-II superconductor below the superconducting transition temperature Tc ≈ 4 K; superconductivity survives in a magnetic field up to Hc2(0) ≥ 3.5 T. The discovery of superconductivity in diamond-structured carbon suggests that Si and Ge, which also form in the diamond structure, may similarly exhibit superconductivity under the appropriate conditions.

This is a preview of subscription content

Access options

Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Figure 1: Optical and scanning electron microscopy images of the material.
Figure 2: X-ray diffraction and Raman spectra of B-doped diamond.
Figure 3: Electrical resistivity and upper critical field curves for B-doped diamond.
Figure 4: Magnetic susceptibility of B-doped diamond near Tc.


  1. Field, J. E. The Properties of Natural and Synthetic Diamond (Academic, New York, 1992)

    Google Scholar 

  2. May, P. W. Diamond thin films: a 21st-century material. Phil. Trans. R. Soc. Lond. A 358, 473–495 (2000)

    ADS  CAS  Article  Google Scholar 

  3. Kalish, R. The search for donors in diamond. Diamond Relat. Mater. 10, 1749–1755 (2001)

    ADS  CAS  Article  Google Scholar 

  4. Geis, M. W., Twitchell, J. C., Macauley, J. & Okano, K. Electron field emission from diamond and other carbon materials after H2, O2 and Cs treatment. Appl. Phys. Lett. 67, 1328–1330 (1995)

    ADS  CAS  Article  Google Scholar 

  5. Teukam, Z. et al. Shallow donors with high n-type electrical conductivity in homoepitaxial deuterated boron-doped diamond layers. Nature Mater. 2, 482–486 (2003)

    ADS  CAS  Article  Google Scholar 

  6. Garrido, J. A. et al. Fabrication of in-plane gate transistors on hydrogenated diamond surfaces. Appl. Phys. Lett. 82, 988–990 (2003)

    ADS  CAS  Article  Google Scholar 

  7. Williams, A. W. S., Lightowlers, E. C. & Collins, A. T. Impurity conduction in synthetic semiconducting diamond. J. Phys. C 3, 1727–1735 (1970)

    ADS  CAS  Article  Google Scholar 

  8. Vishnevskii, A. S., Gontar', A. G., Torishnii, V. I. & Shul'zhenko, A. A. Electrical conductivity of heavily doped p-type diamond. Sov. Phys. Semicond. 15, 659–661 (1981)

    Google Scholar 

  9. Werner, M. et al. Charge transport in heavily B-doped, polycrystalline diamond films. Appl. Phys. Lett. 64, 595–597 (1994)

    ADS  CAS  Article  Google Scholar 

  10. Borst, T. H. & Weis, O. Boron-doped homoepitaxial diamond layers: fabrication, characterization and electronic applications. Phys. Status Solidi A 154, 423–444 (1996)

    ADS  CAS  Article  Google Scholar 

  11. Zhang, R. J., Lee, S. T. & Lam, Y. W. Characterization of heavily boron-doped diamond films. Diamond Relat. Mater. 5, 1288–1294 (1996)

    ADS  CAS  Article  Google Scholar 

  12. Eremets, M. I., Struzhkin, V. V., Mao, H.-K. & Hemley, R. J. Superconductivity in boron. Science 293, 272–274 (2001)

    ADS  CAS  Article  Google Scholar 

  13. Werthamer, N. R., Helfand, E. & Hohenberg, P. C. Temperature and purity dependence of the superconducting critical field Hc2. III. Electron spin and spin-orbit effects. Phys. Rev. 147, 295–302 (1966)

    ADS  CAS  Article  Google Scholar 

  14. McMillan, W. L. Transition temperature of strongly coupled superconductors. Phys. Rev. 167, 331–344 (1968)

    ADS  CAS  Article  Google Scholar 

  15. Gurevich, V. L., Larkin, A. I. & Firsov, Yu. A. On the possibility of superconductivity in semiconductors. Sov. Phys. Solid State 4, 131–135 (1962)

    Google Scholar 

  16. Cohen, M. L. Superconductivity in many-valley semiconductors and in semimetals. Phys. Rev. 134, A511–A521 (1964)

    ADS  Article  Google Scholar 

  17. Cohen, M. L. in Superconductivity (ed. Parks, R. D.) Vol. 1, 615–644 (Marcel Dekker, New York, 1969)

    Google Scholar 

  18. Kohmoto, M. & Takada, Y. Superconductivity from an insulator. J. Phys. Soc. Jpn 59, 1541–1544 (1990)

    ADS  Article  Google Scholar 

  19. Nozières, P. & Pistolesi, F. From semiconductors to superconductors: a simple model for pseudogaps. Eur. Phys. J. B 10, 649–662 (1999)

    ADS  Article  Google Scholar 

  20. Hulm, J. K., Ashkin, M., Deis, D. W. & Jones, C. K. in Progress in Low Temperature Physics (ed. Gorter, C. J.) Vol. VI, 205–242 (North-Holland, Amsterdam, 1970)

    Google Scholar 

  21. Kawaji, H., Horie, H., Yamanaka, S. & Ishikawa, M. Superconductivity in the silicon clathrate compound (Na,Ba)xSi46 . Phys. Rev. Lett. 74, 1427–1429 (1995)

    ADS  CAS  Article  Google Scholar 

  22. Grosche, F. M. et al. Superconductivity in the filled cage compounds Ba6Ge25 and Ba4Na2Ge25 . Phys. Rev. Lett. 87, 247003 (2001)

    ADS  CAS  Article  Google Scholar 

  23. Khvostantsev, L. G., Vereshchagin, L. F. & Novikov, A. P. Device of toroid type for high pressure generation. High Temp. High Press. 9, 637–639 (1977)

    Google Scholar 

  24. Voronov, O. A. & Rakhmanina, A. V. Parameter of the cubic cell of diamond doped with boron. Inorg. Mater. 29, 707–710 (1993)

    Google Scholar 

  25. Brunet, F., Deneuville, A., Germi, P., Pernet, M. & Gheeraert, E. Variation of the cell parameter of polycrystalline boron doped diamond films. J. Appl. Phys. 81, 1120–1125 (1997)

    ADS  CAS  Article  Google Scholar 

  26. Bean, C. P. Magnetization of hard superconductors. Phys. Rev. Lett. 8, 250–253 (1962)

    ADS  Article  Google Scholar 

Download references


We thank D. Wayne for mass spectrometry measurements of the B content of our samples, A. Presz for SEM images and S. Gierlotka for help in sample analysis. This work was supported by the Russian Foundation for Basic Research and by the Strongly Correlated Electrons Program of the Department of Physical Sciences, Russian Academy of Sciences. Work at Los Alamos was performed under the auspices of the US DOE.Authors' contributions Boron-doped diamond samples were synthesized by E.A.E., and their physical properties measured by V.A.S., E.D.B., N.N.M., N.J.C., J.D.T. and S.M.S.

Author information

Authors and Affiliations


Corresponding author

Correspondence to V. A. Sidorov.

Ethics declarations

Competing interests

The authors declare that they have no competing financial interests.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Ekimov, E., Sidorov, V., Bauer, E. et al. Superconductivity in diamond. Nature 428, 542–545 (2004).

Download citation

  • Received:

  • Accepted:

  • Issue Date:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing