For the first time, we harness the unique phase-selectivity of chip-integrated graphene oxide (GO) membranes to significantly enhance flow control on centrifugal microfluidic platforms. In this paper, we present novel processes for the assembly of these GO membranes into polymeric microfluidic systems and demonstrate that multilayer GO membranes allow the passage of water while blocking pressurized air and organic solutions.
Flow control is of paramount importance for sample-to-answer automated Lab-on-a-Chip systems. Centrifugal microfluidics offers the benefit that the force field can be accurately controlled over several orders of magnitude by a spindle motor1. Such ‘Lab-on-a-Disc’ (LoaD) platforms have emerged as a highly useful tool in biomedical diagnostics because many of the necessary laboratory unit operations (LUOs) in bioanalysis, such as pumping2, plasma extraction3, mixing4, and metering5, can be fully automated and implemented. Liquid-handling steps can then be controlled by running a designated spin-frequency protocol to modulate interactions between on-disc liquids and microstructures1. The disc cartridge can also be designed to store all required reagents and then safely encapsulate potentially biohazardous samples6.
Due to the ubiquitous nature of the centrifugal field during rotation, flow control constitutes a particular challenge on integrated LoaD platforms. The coordination of sequential or parallelized LUOs (such as sample and reagent storage) requires high-performance flow control, such as passive and active valving.
Passive valves include capillary valves, hydrophobic valves, and siphon valves7. These types of valves are controlled primarily by the rotational frequency, surface properties, and channel design of the disc. Johnson et al.8 used capillary valves for the sequential handling of fluids. Siegrist et al.9 developed a more integrated system by implementing a robust serial siphoning method of fluid handling. This system was advanced further by integrating the serial siphoning system with a heterogeneous sandwich immunoassay and surface-confined supercritical angle fluorescence (SAF) detection of human immunoglobulin G (hIgG)10. Godino et al.11 integrated a paper siphon into a centrifugal LoaD platform, which introduced rotationally controlled bidirectional flow into the system. However, these valving schemes control only the liquid bulk, not its vapor phase.
Other valving mechanisms rely on the use of sacrificial materials for functional enhancement of microfluidic systems. These physical-barrier-based flow control elements are removed on demand by physical or chemical stimuli12,13. Wax valves, for instance, can be actuated by exposure to a heat source13. García-Cordero et al.14 integrated cyclo-olefin polymer (COP) and polyethylene terephthalate (PET) films, using laser printer lithography, as optofluidic valves that opened using a solid-state laser. Another example is hydrogels, which can act as valves when actuated by size change in the presence of water15. Hwang et al.16 incorporated an elastomeric membrane into a centrifugal microfluidic platform that could be controlled by the membrane thickness and rotational speed of the disc.
Gorkin et al.12 used a dissolvable film material that opens upon contact with the onboard liquid in conjunction with a pneumatic structure to develop a novel, essentially passive valving system on a centrifugal microfluidic platform. Nwankire et al.17,18 built on this system by integrating and automating multistep bioassay protocols actuated by the dissolvable-film-based centrifugo-pneumatic valving scheme. Kinahan et al. advanced this sacrificial technology to an event-triggered valving paradigm that enables the more dynamic control of fluids on a centrifugal microfluidic platform19,20. Dimov et al.21 combined a hydrophobic membrane and dissolvable film to improve on-disc solid-phase purification of nucleic acids. Although these sacrificial materials offer benefits for flow control, they often require some form of external stimulus for activatation; additionally, they are capable of acting on only one type of fluid (for example, hydrogels that activate only in the presence of water). The introduction of a single membrane that is capable of handling both aqueous and organic solutions would be of significant importance for the complex fluid handling requirements of numerous biological testing processes, particularly for nucleic acid testing.
Fluidic routing to direct flow to a selected output at a junction between a waste and an elution outlet is critical for centrifugally implemented automation, especially in the area of nucleic acid purification in which the sequence of fluids, some aqueous and some organic, must be passed through a single channel, but each of these fluids must be routed away from the final collection chamber. Kim et al.22 developed a flow switch by using a capillary valve upstream of an open chamber and unique three-dimensional (3D) junction geometry. A similar router, solely controlled by the rotationally actuated hydrodynamic Coriolis pseudo-force, was reported by Brenner et al.23. This virtual routing concept was further refined by Haeberle et al., who successfully extracted DNA from calf thymus using silica beads by alternating the sense of rotation24. Automated extraction of human genomic DNA was demonstrated by Kloke et al.25, who implemented novel ball-pen pierceable seals to route the sample lysate through an integrated silica membrane in a Lab Tube platform. Although these routing systems are effective, they often required an external stimulus to direct the fluids. The combination of advanced routing solutions based on disc-integrated functional materials could enable more dynamic fluid control.
In this work, we harness graphene oxide (GO)-based membranes for advanced flow control on LoaD platform. As its ground-breaking discovery in 2004 (Ref. 26), a wide spectrum of fascinating characteristics of graphene and its compounds, such as the GO considered here, have been extensively investigated by the scientific community. In recent years, microfluidic systems have been used to characterize the distinctive properties of graphene, such as its electrochemical responses27. Ang et al.28 used a graphene transistor array in a microfluidic chip for the detection of malaria-infected red blood cells. Lo et al.29 included glycidyl methacrylate-functionalized graphene oxide within a hydrogel, which showed a significant increase in size change when exposed to infrared radiation. However, although graphene oxide is under investigation by a large scientific community, its often unique properties have not yet been used for microfluidic flow control. This lack of use for microfluidic flow control is presumably because GO does not bind well to polymer surfaces. To address this issue, we first developed a scheme for the integration of GO membranes in common, polymeric microfluidic devices.
The properties of such integrated GO membranes are anticipated to enable a multitude of applications and advanced flow control. We demonstrate two such properties of the GO membranes: their solvent selectivity and air impermeability (Figure 1). Beyond a specific burst pressure, GO membranes allow water to pass through at very low flow resistance while completely blocking the organic solutions, isopropyl alcohol (IPA) and EtOH, or air, even at high pressure heads. Nair et al. postulated that the spacing between the GO flakes in multilayers act as nanocapillaries that allow the low-friction flow of a monolayer of water; the stacked membrane is analogous to a monolayer of water (≈5 Ǻ)30.
We employed these unique solvent- and phase-selective features of GO to show, for the first time, graphene-oxide-enabled advanced centrifugal flow control.
Materials and methods
The membranes were synthesized from a suspension of GO flakes in water (Bluestone, Manchester, UK). The suspension was first compressed by vacuum filtration through a 0.45-μm pore size cellulose filter (Millipore, Cork, Ireland). As they filled the pores of the cellulose, the flakes formed a multilayer structure across the entire filter surface. This process eventually created a free-standing, 35-mm diameter GO-filter hybrid, whose diameter was defined by the vacuum filtration apparatus. The thickness of the membranes was governed by the volume and concentration of the GO flakes in suspension. The process time ranged from 4 to 8 h, depending on the volume being filtered (Figure 2a).
After completion, the membranes were removed from the vacuum filtration setup and left to dry for ~4 h. During this time, the membranes remained in contact with the cellulose filters. The completion of this drying step was crucial because prior handling of the membranes could lead to tearing. The membrane was then peeled from the cellulose filters and handled with ease (Figure 2b).
To incorporate the GO into a microfluidic device, a method for attaching the membrane to the polymer surface had to be devised. Using a method adopted from Gorkin et al., the membrane was adhered to double-sided pressure-sensitive adhesive (PSA), which featured a small, 1-mm through hole. The contours and size of the combined GO and PSA ‘tab’ were then flexibly defined using a precision knife cutter (Graphtec, Craft Robo Pro, Wrexham, UK). Next, the GO tab was integrated into a microfluidic system using ‘sticky’ PSA backing (Figures 2c and d).
Figure 2f shows an SEM image of a cross section of a GO membrane, which clearly displays the multilayer structure. This stacked membrane possesses a thickness of ~10 μm. From this image, the even distribution of the flakes can be observed. Also shown in this figure is the relative clean cut of the tab edge, achieved using a precision knife cutter (Graphtec, Craft Robo Pro, Wrexham, UK).
Two distinct properties of the GO were investigated: its air impermeability and solvent selectivity. These properties were tested over a given pressure range on two centrifugal microfluidic discs.
Figure 3 shows the design for testing the impermeability of the GO tabs to air. This disc consisted of three layers of PMMA and two layers of PSA (Figure 3a). The discs contained four identical structures, each of which featured a loading chamber and two symmetric side arms that were connected via a common inlet channel. Both side arms exhibited a hole at the top, which had been sealed by either a PSA or GO tab (Figure 3a). For the sake of clarity in these tests, colored food–dye in water was used, although the liquid would not make direct contact with the tabs.
A 180-μl volume was placed in the loading chamber. This liquid trapped and hence enclosed the air inside the inlet channel and side arms. With the increasing rotationally induced centrifugal field, liquid extends down the inlet channel to compress the air in the side arms. The liquid reached the interface between the channel and side arm at a rotational frequency of 10 Hz. As the disc was spun faster up to a rotational frequency of 100 Hz, the liquid reached the side arms and continued to rise (Figure 3b). Figure 3c shows that there was no discernible difference of the liquid levels in both side arms between the upper spin frequency and when the spin frequency was once again reduced to 0 Hz, thereby proving the air impermeability and pressure tightness of the GO tab.
Another interesting feature is the relatively high rotationally induced pressures
where Δpω is the burst pressure in pascals, ρ is the density of the liquid, Δr is the length of the liquid plug, is the distance of the tab from the centre of rotation, and ω is the angular frequency that the tabs are able to withstand.
Upon loading, the liquid sealed the air inside the channel and arms essentially under atmospheric pressure. As the spin frequency was increased to 10 Hz, the air pocket sealed by the GO tab was compressed to ~25 mbar (obtained using Boyle’s law). Finally, at 100 Hz, there was a significant increase in pressure of ~750 mbar. This result verifies the sufficient mechanical strength of the integrated GO membranes. This result can be observed in Figure 3c, in which the GO tab bends without disruption.
Figure 4 shows the disc used to test the solvent selectivity of the GO. The disc was made up of four layers of Poly(methyl methacrylate) (PMMA) (green) and four layers of PSA (gray). It contained 10 identical structures. Each structure consisted of a 3D architecture containing a loading chamber with a 1-mm hole at the base of the chamber. This vertical through-hole is connected to a channel on the bottom layer of the disc. The hole was sealed by one of the GO tabs. The channel is then connected to a collection chamber (Figure 4b).
To test the solvent-selective properties of the GO, five liquids were added to the chambers: deionized (DI) water, 2-propanol (IPA), ethanol (EtOH), Fluorinert FC40 (Sigma-Aldrich, Arklow, Ireland) and mineral oil. A 50-μl volume was added to the loading chamber. Under centrifugation, the liquid generated a hydrostatic pressure head acting on the GO tab. The rotational frequency was increased at regular intervals until the membrane yielded. In the case of DI water, the plug passed through the GO at ~50 Hz (Figure 4c). Notably, once the ‘burst’ pressure was exceeded, the water penetrated with very low flow resistance. By contrast, the organic solutions IPA and EtOH and the oil solutions FC40 and mineral oil, were fully retained in the loading chamber, even at the highest spin frequency of 125 Hz that we could implement on our test stand.
This simple test demonstrates the complete impermeability of the GO membrane to the organic solutions IPA and EtOH and the oil solutions FC40 and mineral oil, while offering very little flow resistance to water above a certain pressure threshold.
Characterization of GO tabs
Using the structure shown in Figure 4, the capabilities of the solvent-selective nature of the GO tabs was investigated. First, because the membranes had been shown to be permeable to water but completely impermeable to IPA, water and IPA mixtures were tested. Solutions with varying water concentration in IPA were flowed through the GO tabs, up to the water concentration at which a burst could no longer be achieved. The tab used in these experiments was ~10-μm thick.
The burst pressure, Equation (1), required for flow increases with decreasing water content (Figure 5). It was also determined that any solution with a concentration less than 40% water was incapable of passing through the GO tab, even at the highest spin frequency we could realize for safety reasons.
The second experiment revealed the correlation between the thickness of the GO membrane and the burst pressure for water. The variation in the tab thickness was achieved by filtering different concentrations of GO flakes (Figure 2). In this case, four different membrane thicknesses were used, approximately 27, 35, 38, and 44 μm. The thickness of the GO membrane was then measured using a 3D microscope (Keyence, VHX-5000 series, Digital Microscope, Itasca, IL, USA). For this experiment, a 100% DI water solution was used, and the burst frequency required for flow was once again recorded and converted to burst pressure using Equation (1). As seen in Figure 6, the burst pressure increases with increasing thickness of the membrane.
These two experiments demonstrate the dynamic range of capabilities of the GO tabs. By varying their thickness, the tabs can be tailored to work for a multitude of designs within a centrifugal system.
We have shown a new method for the integration of a GO tab within a polymeric microfluidic structure. Using centrifugal flow control, we have furthermore investigated various unique features of GO, notably its solvent selectivity and air impermeability. We envision the engineering of a solvent-selective burst valve based on this surprising, selective permeability of GO membranes. The tabs also offer avenues for enhanced centrifugal flow control towards comprehensive assay automation on the Lab-on-a-Disc platform.
Gorkin R, Park J, Siegrist J et al. Centrifugal microfluidics for biomedical applications. Lab on a Chip 2010; 10: 1758–1773.
Gorkin R, Clime L, Madou M et al. Pneumatic pumping in centrifugal microfluidic platforms. Microfluid Nanofluidics 2010; 9: 541–549.
Haeberle S, Brenner T, Zengerle R et al. Centrifugal extraction of plasma from whole blood on a rotating disk. Lab on a Chip 2006; 6: 776–781.
Noroozi Z, Kido H, Micic M et al. Reciprocating flow-based centrifugal microfluidics mixer. Review of Scientific Instruments 2009; 80: 075102.
Mark D, Weber P, Lutz S et al. Aliquoting on the centrifugal microfluidic platform based on centrifugo-pneumatic valves. Microfluid Nanofluidics 2011; 10: 1279–1288.
Hoffmann J, Mark D, Lutz S et al. Pre-storage of liquid reagents in glass ampoules for DNA extraction on a fully integrated lab-on-a-chip cartridge. Lab on a Chip 2010; 10: 1480–1484.
Ducrée J, Haeberle S, Lutz S et al. The centrifugal microfluidic Bio-Disk platform. Journal of Micromechanics Microengineering 2007; 17: S103–S115.
Johnson RD, Badr IHA, Barrett G et al. Development of a fully integrated analysis system for ions based on ion-selective optodes and centrifugal microfluidics. Analytical Chemistry 2001; 73: 3940–3946.
Siegrist J, Gorkin R, Clime L et al. Serial siphon valving for centrifugal microfluidic platforms. Microfluid Nanofluidics 2009; 9: 55–63.
Nwankire CE, Donohoe GG, Zhang X et al. At-line bioprocess monitoring by immunoassay with rotationally controlled serial siphoning and integrated supercritical angle fluorescence optics. Analytica Chimica Acta 2013; 781: 54–62.
Godino N, Vereshchagina E, Gorkin R et al. Centrifugal automation of a triglyceride bioassay on a low-cost hybrid paper-polymer device. Microfluid Nanofluidics 2013; 16: 895–905.
Gorkin R, Nwankire CE, Gaughran J et al. Centrifugo-pneumatic valving utilizing dissolvable films. Lab on a Chip 2012; 12: 2894–2902.
Park J, Cho Y, Lee B et al. Multifunctional microvalves control by optical illumination on nanoheaters and its application in centrifugal microfluidic devices. Lab on a Chip 2007; 7: 557–564.
Garcia-Cordero JL, Kurzbuch D, Benito-Lopez F et al. Optically addressable single-use microfluidic valves by laser printer lithography. Lab on a Chip 2010; 10: 2680–2687.
van der Linden HJ, Herber S, Olthuis W et al. Stimulus-sensitive hydrogels and their applications in chemical (micro)analysis. Analyst 2003; 128: 325–331.
Hwang H, Kim H-H, Cho Y-K . Elastomeric membrane valves in a disc. Lab on a Chip 2011; 11: 1434–1436.
Nwankire CE, Chan D-SS, Gaughran J et al. Fluidic automation of nitrate and nitrite bioassays in whole blood by dissolvable-film based centrifugo-pneumatic actuation. Sensors 2013; 13: 11336–11349.
Nwankire CE, Czugala M, Burger R et al. A portable centrifugal analyser for liver function screening. Biosensensors & Bioelectronics 2014; 56: 352–358.
Kinahan DJ, Kearney SM, Dimov N et al. Event-triggered logical flow control for comprehensive process integration of multi-step assays on centrifugal microfluidic platforms. Lab on a Chip 2014; 14: 2249–2258.
Kinahan DJ, Kearney SM, Faneuil OP et al. Paper imbibition for timing of multi-step liquid handling protocols on event-triggered centrifugal microfluidic lab-on-a-disc platforms. RSC Advances 2015; 5: 1818–1826.
Dimov N, Clancy E, Gaughran J et al. Solvent-selective routing for centrifugally automated solid-phase purification of RNA. Microfluid Nanofluidics 2015; 18: 859–871.
Kim J, Hee Jang S, Jia G. . Cell lysis on a microfluidic CD (compact disc). Lab on a Chip 2004; 4: 516–522.
Brenner T, Glatzel T, Zengerle R et al. Frequency-dependent transversal flow control in centrifugal microfluidics. Lab on a Chip 2005; 5: 146–150.
Haeberle S, Pausch S, Burger R et al. Automation of nucleic acid extraction by a Coriolis-force actuated droplet router. 11th International Conference on Miniaturized Systems for Chemistry and Life Sciences (μTAS 2007); 7–11 Oct 2007; Paris, France; 2007: 1231–1233.
Kloke A, Fiebach AR, Zhang S et al. The LabTube - a novel microfluidic platform for assay automation in laboratory centrifuges. Lab on a Chip 2014; 14: 1527–1537.
Novoselov KS, Geim A K, Morozov S V et al. Electric field effect in atomically thin carbon films. Science 2004; 306: 666–669.
Pumera M, Ambrosi A, Bonanni A et al. Graphene for electrochemical sensing and biosensing. TrAC Trends in Analytical Chemistry 2010; 29: 954–965.
Ang PK, Li A, Jaiswal M et al. Flow sensing of single cell by graphene transistor in a microfluidic channel. Nano Letters 2011; 11: 5240–5246.
Lo C-W, Zhu D, Jiang H . An infrared-light responsive graphene-oxide incorporated poly(N-isopropylacrylamide) hydrogel nanocomposite. Soft Matter 2011; 7: 5604–5609.
Nair RR, Wu H A, Jayaram PN et al. Unimpeded permeation of water through helium-leak-tight graphene-based membranes. Science 2012; 335: 442–444.
This work is partially funded under the Programme for Research in Third Level Institutions (PRTLI) Cycle 5. The PRTLI is co-funded through the European Regional Development Fund (ERDF), part of the European Union Structural Funds Programme 2007–2013.
The authors declare no conflict of interest.
About this article
Cite this article
Gaughran, J., Boyle, D., Murphy, J. et al. Phase-selective graphene oxide membranes for advanced microfluidic flow control. Microsyst Nanoeng 2, 16008 (2016). https://doi.org/10.1038/micronano.2016.8
This article is cited by
On-board reagent storage and release by solvent-selective, rotationally opened membranes: a digital twin approach
Microfluidics and Nanofluidics (2022)
Systematic review of centrifugal valving based on digital twin modeling towards highly integrated lab-on-a-disc systems
Microsystems & Nanoengineering (2021)
Microfluidics and Nanofluidics (2019)