Phase transformations observed at the interfaces between crystalline grains in pure metals

Rabkin, Eugen

doi:10.1038/d41586-020-00765-3

NEWS AND VIEWS
18 March 2020

Phase transformations observed at the interfaces between crystalline grains in pure metals

Interfaces between the tiny crystal grains that make up solid copper have been shown to change from one ordered phase to another, independently of the phase adopted by the crystals, opening up prospects for materials development.

Eugen Rabkin⁰

Eugen Rabkin
1. Eugen Rabkin is in the Department of Materials Science and Engineering, Technion – Israel Institute of Technology, 3200003 Haifa, Israel.
View author publications

You can also search for this author in PubMed Google Scholar

Access through your institution

Buy or subscribe

Some solid metals exist in various structural forms, a phenomenon known as polymorphism. Iron, for example, adopts one type of cubic lattice (α-iron) at room temperature, but transforms into another (γ-iron) above 912 °C. This is an example of a phase transformation — an abrupt change in the atomic structure of a material that occurs during a gradual change in temperature or pressure. The transformation of γ- to α-iron that occurs when iron alloyed with carbon is rapidly cooled from a high temperature has long been used to produce hard and strong steels; by contrast, pure iron is soft and ductile. Writing in Nature, Meiners et al.¹ report that polymorphic phase transformations can also occur at the interfaces between the tiny crystals that make up most pure metals. This discovery suggests a fresh approach for processing metallic materials to optimize their properties for applications.

Access options

Access through your institution

Rent or buy this article

Get just this article for as long as you need it

$39.95

Learn more

Prices may be subject to local taxes which are calculated during checkout

Nature 579, 350-351 (2020)

doi: https://doi.org/10.1038/d41586-020-00765-3

References

Meiners, T., Frolov, T., Rudd, R. E., Dehm, G. & Liebscher, C. H. Nature 579, 375–378 (2020).
Article Google Scholar
Rosenhain, W. & Ewen, D. J. Inst. Metals 10, 119–148 (1913).
Google Scholar
Brandon, D. G. & Wald, M. Phil. Mag. 6, 1035–1044 (1961).
Article Google Scholar
Sutton, A. P. & Balluffi, R. W. Interfaces in Crystalline Materials (Oxford Univ. Press, 1995).
Google Scholar
Rabkin, E. I., Semenov, V. N., Shvindlerman, L. S. & Straumal, B. B. Acta Metall. Mater. 39, 627–639 (1991).
Article Google Scholar
Cantwell, P. R. et al. Acta Mater. 62, 1–48 (2014).
Article Google Scholar
Maksimova, E. L., Shvindlerman, L. S. & Straumal, B. B. Acta Metall. 36, 1573–1583 (1988).
Article Google Scholar
Frolov, T., Divinski, S. V., Asta, M. & Mishin, Y. Phys. Rev. Lett. 110, 255502 (2013).
Article PubMed Google Scholar
Kaur, I., Mishin, Y. & Gust, W. Fundamentals of Grain and Interphase Boundary Diffusion 3rd edn (Wiley, 1995).
Google Scholar
Rittner, J. D. & Seidman, D. N. Phys. Rev. B 54, 6999–7015 (1996).
Article Google Scholar
Han, J., Vitek, V. & Srolovitz, D. J. Acta Mater. 104, 259–273 (2016).
Article Google Scholar
Watanabe, T. & Tsurekawa, S. Acta Mater. 47, 4171–4185 (1999).
Article Google Scholar
Homer, E. R. Comp. Mater. Sci. 161, 244–254 (2019).
Article Google Scholar