Stainless steels are used in countless diverse applications for their corrosion resistance. Although they have extremely good general resistance, they are nevertheless susceptible to pitting corrosion. This localized dissolution of an oxide-covered metal in specific aggressive environments is one of the most common and catastrophic causes of failure of metallic structures. The pitting process has been described as random, sporadic and stochastic and the prediction of the time and location of events remains extremely difficult1. Many contested models of pitting corrosion exist, but one undisputed aspect is that manganese sulphide inclusions play a critical role. Indeed, the vast majority of pitting events are found to occur at, or adjacent to, such second-phase particles2,3. Chemical changes in and around sulphide inclusions have been postulated4 as a mechanism for pit initiation but such variations have never been measured. Here we use nanometre-scale secondary ion mass spectroscopy to demonstrate a significant reduction in the Cr:Fe ratio of the steel matrix around MnS particles. These chromium-depleted zones are susceptible to high-rate dissolution that ‘triggers’ pitting. The implications of these results are that materials processing conditions control the likelihood of corrosion failures, and these data provide a basis for optimizing such conditions.
This is a preview of subscription content
Subscribe to Journal
Get full journal access for 1 year
only $3.90 per issue
All prices are NET prices.
VAT will be added later in the checkout.
Tax calculation will be finalised during checkout.
Rent or Buy article
Get time limited or full article access on ReadCube.
All prices are NET prices.
Williams, D. E., Westcott, C. & Fleischmann, M. Stochastic models of pitting corrosion of stainless steels. 1. Modeling of the initiation and growth of pits at constant potential. J. Electrochem. Soc. 132, 1796–1804 (1985).
Eklund, G. S. Initiation of pitting at sulfide inclusions in stainless steel. J. Electrochem. Soc. 121, 467–473 (1974).
Wranglen, G. Pitting and sulphide inclusions in steel. Corrosion Sci. 14, 331–349 (1974).
Williams, D. E. & Zhu, Y. Y. Explanation for initiation of pitting corrosion of stainless steels at sulfide inclusions. J. Electrochem. Soc. 147, 1763–1766 (2000).
Galvele, J. R. Transport processes and the mechanism of pitting of metals. J. Electrochem. Soc. 123, 464–474 (1976).
Hoar, T. P., Mears, D. C. & Rothwell, G. P. The relationships between anodic passivity, brightening and pitting. Corrosion Sci. 5, 279–289 (1981).
Chao, C. Y., Lin, L. F. & Macdonald, D. D. A point defect model for anodic passive films. J. Electrochem. Soc. 128, 1187–1194 (1981).
Uhlig, H. H. Adsorbed and reaction-production films on metals. J. Electrochem. Soc. 97, 215C (1950).
Sato, N. A. Theory for breakdown of anodic oxide films on metals. Electrochim. Acta. 16, 1683–1692 (1971).
Richardson, J. A. & Wood, G. C. Study of the pitting corrosion of Al by scanning electron microscopy. Corrosion Sci. 10, 313–323 (1970).
Suter, T. & Bohni, H. Microelectrodes for corrosion studies in microsystems. Electrochim. Acta 47, 191–199 (2001).
Lott, S. E. & Alkire, R. C. The role of inclusions on initiation of crevice corrosion of stainless steel. 1. Experimental studies. J. Electrochem. Soc. 136, 973–979 (1989).
Marcus, P., Teissier, A. & Oudar, J. The influence of sulphur on the dissolution and passivation of a NiFe Alloy. 1. Electrochemical and radio tracer measurements. Corrosion Sci. 24, 259–268 (1984).
Baker, M. A. & Castle, J. E. The initiation of pitting corrosion at MnS inclusions. Corrosion Sci. 34, 667–682 (1993).
Ryan, M. P., Laycock, N. J., Newman, R. C. & Isaacs, H. S. The pitting behaviour of thin film FeCr alloys in hydrochloric acid. J. Electrochem. Soc. 145, 1566–1571 (1998).
Stewart, J. & Williams, D. E. The initiation of pitting corrosion on austenitic stainless steels: on the role and importance of sulphide inclusions. Corrosion Sci. 33, 457–474 (1992).
Monnartz, P. Iron–chromium alloys with special consideration of resistance to acids. Metallurgie 8, 161–176 (1911).
Williams, D. E., Newman, R. C., Song, Q. & Kelly, R. G. Passivity breakdown and pitting corrosion of binary alloys. Nature 350, 216–219 (1991).
Webb, E. G., Suter, T. & Alkire, R. C. Microelectrochemical measurements of the dissolution of single MnS inclusions, and the prediction of critical conditions for pit initiation on stainless steel. J. Electrochem. Soc. 148, B186–B195 (2001).
Williams, D. E., Mohiuddin, T. F. & Zhu, Y. Elucidation of a trigger mechanism for pitting corrosion of stainless steels using sub-micron resolution SECM and photoelectrochemical microscopy. J. Electrochem. Soc. 145, 2664–2672 (1998).
Brossia, C. S. & Kelly, R. G. Influence of sulfur content and bulk electrolyte composition on crevice corrosion initiation of austenitic stainless steel. Corrosion 54, 145–154 (1998).
Frankel, G. S. Pitting corrosion of metals: a review of the critical factors. J. Electrochem. Soc. 145, 2186–2197 (1998).
This work was supported by the Engineering and Physical Sciences Research Council, UK.
The authors declare no competing financial interests.
About this article
Cite this article
Ryan, M., Williams, D., Chater, R. et al. Why stainless steel corrodes. Nature 415, 770–774 (2002). https://doi.org/10.1038/415770a
Metallurgical and Materials Transactions B (2021)
An experimental approach for the utilization of tannery sludge-derived Bacillus strain for biosorptive removal of Cr(VI)-contaminated wastewater
Environmental Science and Pollution Research (2021)
Long-Lasting Superhydrophilic and Instant Hydrophobic Micropatterned Stainless Steel Surface by Thermally-Induced Surface Layers
International Journal of Precision Engineering and Manufacturing-Green Technology (2021)
Journal of Coatings Technology and Research (2021)
Journal of Materials Science (2021)