Letter | Published:

Site-ordering effects on element partitioning during rapid solidification of alloys

Naturevolume 383pages150152 (1996) | Download Citation



WHEN an alloy solidifies, the component elements are often redistributed between the solid and liquid phases, so that the composition of the growing solid differs from that of the liquid. This effect, known as solute partitioning1, is the main cause of inhomogeneity in alloys, affecting both the nature and the mechanical properties (for example, brittleness) of the solidified material. If solidification is rapid, the solid-liquid interface is no longer in equilibrium, and it is generally accepted—and has been demonstrated2 for solid solutions—that this gives rise to reduced partitioning, in the limit leading to a solid having the same composition as the liquid through a process known as 'solute trapping'3. We have recently argued4 on theoretical grounds that, when the solidifying phase shows site ordering, the partitioning behaviour can be considerably more complex: rapid solidification might lead to increased partitioning, a change in the direction of partitioning, or an absence of partitioning at solidification rates much lower than expected. Here we report the experimental verification of this phenomenon by demonstrating inverted partitioning during rapid solidification of the intermetallic compound NiAl.

Access optionsAccess options

Rent or Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.


  1. 1

    Chalmers, B. Principles of Solidification 126 (Wiley, New York, 1964).

  2. 2

    Smith, P. M. & Aziz, M. J. Acta Metall. Mater. 42, 3515–3525 (1994).

  3. 3

    Kar, A. & Mazumder, J. Acta Metall. Mater. 40, 1873–1881 (1992).

  4. 4

    Assadi, H. & Greer, A. L. Mater. Res. Soc. Symp. Proc. (in the press).

  5. 5

    Boettinger, W. J. & Aziz, M. J. Acta Metall. 37, 3379–3391 (1989).

  6. 6

    West, J. A., Manos, J. T. & Aziz, M. J. Mater. Res. Soc. Symp. Proc. 213, 859–864 (1991).

  7. 7

    Aziz, M. J. J. Appl. Phys. 53, 1158–1168 (1982).

  8. 8

    Koch, C. C. Int. Mater. Rev. 33, 201–219 (1988).

  9. 9

    Assadi, H. & Greer, A. L. Iron Steel Inst. Jpn Int. 35, 574–579 (1995).

  10. 10

    Tiller, W. A., Jackson, K. A., Rutter, J. W. & Chalmers, B. Acta Metall. 1, 428–437 (1953).

  11. 11

    Mullins, W. W. & Sekerka, R. F. J. Appl. Phys. 34, 444–451 (1964).

Download references

Author information


  1. Department of Materials Science and Metallurgy, University of Cambridge, Pembroke Street, Cambridge, CB2 3QZ, UK

    • H. Assadi
    •  & A. L. Greer


  1. Search for H. Assadi in:

  2. Search for A. L. Greer in:

About this article

Publication history



Issue Date



Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.