Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Superconductivity at 39 K in magnesium diboride


In the light of the tremendous progress that has been made in raising the transition temperature of the copper oxide superconductors (for a review, see ref. 1), it is natural to wonder how high the transition temperature, Tc, can be pushed in other classes of materials. At present, the highest reported values of Tc for non-copper-oxide bulk superconductivity are 33 K in electron-doped CsxRbyC60 (ref. 2), and 30 K in Ba1-xKxBiO3 (ref. 3). (Hole-doped C60 was recently found4 to be superconducting with a Tc as high as 52 K, although the nature of the experiment meant that the supercurrents were confined to the surface of the C60 crystal, rather than probing the bulk.) Here we report the discovery of bulk superconductivity in magnesium diboride, MgB2. Magnetization and resistivity measurements establish a transition temperature of 39 K, which we believe to be the highest yet determined for a non-copper-oxide bulk superconductor.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Figure 1
Figure 2
Figure 3: Magnetic susceptibility χ of MgB2 as a function of temperature.
Figure 4

Similar content being viewed by others


  1. Takagi, H. in Proc. Int. Conf. on Materials and Mechanisms of Superconductivity, High Temperature Superconductors VI. Physica C 341-348, 3–7 (2000).

    CAS  Google Scholar 

  2. Tanigaki, K. et al. Superconductivity at 33 K in CsxRbyC60. Nature 352, 222–223 (1991).

    Article  ADS  CAS  Google Scholar 

  3. Cava, R. V. et al. Superconductivity near 30 K without copper: the Ba0.6K0.4BiO3 perovskite. Nature 332, 814–816 (1988).

    Article  ADS  CAS  Google Scholar 

  4. Schön, J. H., Kloc, Ch. & Batlogg, B. Superconductivity at 52 K in hole-doped C60. Nature 408, 549–552 (2000).

    Article  ADS  Google Scholar 

  5. Jones, M. & Marsh, R. The preparation and structure of magnesium boride, MgB2. J. Am. Chem. Soc. 76, 1434–1436 (1954).

    Article  CAS  Google Scholar 

Download references


This work was partially supported by a Grant-in-Aid for Science Research from the Ministry of Education, Science, Sports and Culture, Japan and by a grant from CREST.

Author information

Authors and Affiliations


Corresponding author

Correspondence to Jun Akimitsu.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Nagamatsu, J., Nakagawa, N., Muranaka, T. et al. Superconductivity at 39 K in magnesium diboride. Nature 410, 63–64 (2001).

Download citation

  • Received:

  • Accepted:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing