Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Strain–Age Hardening and Brittleness in Chromium

Abstract

CURRENT theories of the cause of brittleness in ‘pure’ chromium ascribe the phenomenon to Cottrell locking1, invoking the Mott–Stroh2,3 theory of crack formation as the operative mechanism of brittle fracture, and nitrogen as the associated interstitial solute atom. There are several features of the tensile behaviour of annealed chromium (containing approximately 0.002 per cent nitrogen and 0.015 per cent oxygen), however, which this picture does not wholly explain, namely: (1) the very high temperature up to which embrittlement extends (about 350° C.) compared with other body-centred cubic metals of similar structure such as α-iron, molybdenum and tungsten; (2) the abrupt nature of the transition from a highly ductile condition to a completely brittle one, behaviour which again differs markedly from other body-centred cubic metals; (3) the fact that embrittlement occurs (at this nitrogen level) at the bottom of a trough in the maximum stress/temperature and yield stress/temperature curves just below 350° C.4, and not on the steeply rising part of the yield stress/temperature curve, which occurs only below 200° C., and which has been ascribed directly to Cottrell locking.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Similar content being viewed by others

References

  1. Wain, H. L., Henderson, F., and Johnstone, S. T. M., J. Inst. Met., 83, 133 (1954).

    CAS  Google Scholar 

  2. Mott, N. F., J. Iron St. Inst., 183, 233 (1956).

    CAS  Google Scholar 

  3. Stroh, A. N., Phil. Mag., 46, 968 (1955).

    Article  Google Scholar 

  4. Weaver, C. W. (unpublished work).

  5. Hundy, B. B., Metallurgiea, 53, 203 (1956).

    CAS  Google Scholar 

  6. Caplan, D., Fraser, M. J., and Burr, A. A., “Solubility of Oxygen and Nitrogen in Solid Chromium”, a paper presented at the Conference on Ductile Chromium Metal and Its Alloys, National Metal Congress (Philadelphia, October, 1955).

    Google Scholar 

  7. Krupnik, N., and Ford, H., J. Inst. Met., 81, 601 (1953).

    CAS  Google Scholar 

  8. Kubaschewski, O., and Evans, E. L., “Metallurgical Thermochemistry”, 306 (Butterworth-Springer, London, 1951).

    Google Scholar 

  9. Thomas, W. R., and Leak, G. M., J. Iron St. Inst., 180, 155 (1955).

    CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Rights and permissions

Reprints and permissions

About this article

Cite this article

WEAVER, C. Strain–Age Hardening and Brittleness in Chromium. Nature 180, 806–808 (1957). https://doi.org/10.1038/180806b0

Download citation

  • Issue Date:

  • DOI: https://doi.org/10.1038/180806b0

This article is cited by

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing