Abstract
All-in-one assemblies of separator, electrode and current collector (SECA) for lithium ion batteries are presented by using 1D nanowires of Si and Cu (nwSi and nwCu). Even without binders, integrity of SECA is secured via structural joints based on ductility of Cu as well as entanglement of nwSi and nwCu. By controlling the ratio of the nanowires, the number of contact points and voids accommodating volume expansion of Si active material are tunable. Zero volume expansion and high energy density are simultaneously achievable by the architecture.
Similar content being viewed by others
Introduction
We undo entangled lines of our earphone before connecting it to cell phones. The inter-tangled bundles of hairs are easily found on mesh drain traps or at the corners of dirty rooms. High-aspect-ratio structures are easily inter-tangled with high probability, forming 3D network occupying a volumetric space with voids within its structure as well as keeping integrity of the entangled object bodies. Here, we demonstrate 3D network electrodes of binary phases as anodes for lithium ion batteries (LIBs). The architecture was built by inter-tangling silicon nanowires (nwSi) as an active material with copper nanowires (nwCu) as a conductive pathway. Polymeric binders used in conventional LIBs were not used in this architecture because nwCu plays a role as the binder due to its ductile properties. Structural joints are developed by pressure in an inter-locking way that nwSi is fitted into concaved parts of nwCu. As the second point to distinguish it from conventional electrodes, the 3D architecture was built not on current collectors but on separators. Additional layer of nwCu stacked on bare face of the 3D architecture worked as an ultra-light porous current collector. The separator-electrode-current collector assembly (SECA) showed very superior performances in terms of cyclability and rate capability.
Electrochemical reactions, the potential of which is relatively negative enough to be close to that of Li+/Li, have been used as the chemistry for anodes of LIBs, including intercalation (graphites1,2), conversion reactions (metal oxides3,4) and alloying reactions (silicon5 and tin6). As higher energy densities are more emphasized with electric vehicles and stationary energy storage systems rising, high-capacity anode materials such as silicon are attracting interests from academic and industrial societies. Its theoretical capacity approaches ~4,000 mAh g−1 at room temperature that is ten times as large as that of widely used graphites (372 mAh g−1). However, serious drawbacks difficult to overcome come with the silicon anode materials, including not only low electric conductivity of silicon but also large volume change during lithiation up to ~400 % leading to pulverization of particles. Resultantly, serious decay of capacity with repeated cycles of charging/discharging follows with silicon7,8,9,10,11. To accommodate the volume expansion of silicon for blocking pulverization, the buffer space was introduced12,13,14,15,16,17,18,19,20 into silicon particles to form porous or hollow structures. Dead mass of silicon pulverized from particles after expansion was designed17,19,21,22,23,24,25 to keep integrity to electric pathways by coating the original particles of silicon with conductive materials such as carbon and conducting polymers. Different from the strategies to modify silicon particles, silicon nanowires were grown directly on stainless steel current collectors via vapor-liquid-solid methods or chemical-vapor-deposition methods26,27,28. Enhanced retention of capacity were guaranteed by efficient electron transport along the 1D structure, strain relaxation through the lateral sides of the nanowires and good contact between roots of the nanowires and current collectors. The similar results were achieved24 by spray-coating silicon nanowires on carbon textile matrix without binders. The 1D/1D contact between silicon nanowires and conductive materials was emphasized19 for good rate capability and remarkable cycling stability. Various works based on silicon 1D structures were compared with our work in terms of electrochemical performances (Table S1)29,30,31,32,33,34.
Based on the merits of 1D structures of nwSi and inter-tangled networking between nwSi and nwCu, we developed all-in-one architectures assembling electrodes and current collectors onto separators (SECA = separator-electrode-current collector assembly) (Figure 1a). An ethanol-based mixture of nwSi and nwCu was vacuum-filtered through a conventionally used polyethylene separator to form a mixed-nanowire electrode layer on the separator. Here, nwSi and nwCu works as an active material and a conducting agent. Then, only-nwCu layer was laminated as a current collector on the electrode layer by using the same filtration. Finally, the tri-layered laminates were dried and pressed to inter-locking structure between nwSi and nwCu in the electrode layer or between nwCu in the current collector layer or between the electrode layer and the current collector layer. The schematic of cross-sectional view (Figure 1b) is realized in the resultant SECA as shown in electron-microscopic images (Figure 1c, Figure S1 and S2) with inter-tangled nanowires confirmed. Line mapping of Si and Cu elements identified each layer consisting of Cu-dominant phase (I) and relatively Si-rich phase (II).
As the first merit achieved by SECA, higher specific and volumetric energy density of cells can be obtained by using small amount of current collectors as well as by eliminating binders. In the conventional tri-component (active material, binder and conducting agent) electrode of this work, copper foils of micrometer thickness (e.g. 18 um thick with 16 mg cm−2) are used. The value of thickness occupies 53 % of overall thickness of electrode and 94 % of total mass of electrode, when considering that electrode mass consisting of silicon, binder and conducting agents at 6:2:2 wt. ratio on current collector are 34 um thick with 17 mg cm−2. In our SECA of 30 % nwSi as a representative case, however, only 44 % of electrode thickness (14 um/32 um) and 39 % of total mass (1.3 mg cm−2/3.3 mg cm−2) were occupied by the current collectors of inter-tangled nwCu. Resultantly, for example, lighter electrodes including current collector can be possible by the SECA with only 30 % to 70 % of mass of a conventional tri-component electrode at the same silicon loading of 0.6 mg cm−2 (Figure 1d; detailed calculation in supporting information).
The number of contact points between nwSi and nwCu (nc) as well as the contact-to-contact distance (Lcc) totally depends on the nwSi contents (xSi) in the nwSi/nwCu composites. Based on the lines-on-a-plate model in which nanowires of the minor component is evenly distributed on the plate consisting of nanowires of the major component, the maximum values of nc (ncmax) and the minimum values of Lcc (Lccmin) were calculated as functions of xSi (Figure 1e and f; detailed calculation in supporting information). The ncmax per total electrode mass (mtot) was maximized at the optimized composition xSiopti (open circles in e and f) where the contactable area is matched between nwSi and nwCu. The increase in nwSi contents directly leads to the increase in ncmax/mtot up to the optimized composition because nwCu can provide enough contactable faces to nwSi. At nwSi concentrations higher than xSiopti, the lack of nwCu is experienced by nwSi so that the contact number decreases. From the viewpoint of the contact-to-contact distance, the values of Lccmin are equivalent to the diameter of nwCu, the smallest value at which a contact point can approach its nearest contact point, at compositions lower than xSiopti. After the composition, the contact points move further away from their neighborhoods as silicon contents increase and the lack of nwCu become more serious. The composition at xSiopti would be the best choice when considering that higher nwSi contents are required with a closer contact. The xSiopti can be traced with the radius ratio of rCu/rSi as an independent variable (dashed red lines with red arrows indicating the increasing direction of rCu/rSi in Figure 1e and f): xSiopti = 1/(1 + (dCu/dSi)(rCu/rSi)) with d = density. Relatively thinner nwCu leading to smaller values of rCu/rSi extends the region of the smallest Lccmin to higher nwSi composition: e.g. xSiopti was shifted from 9.3 % at rCu/rSi = 2.5 to 20 % at rCu/rSi = 1.0. Also, the thinner nwCu provides more number of contacts with shorter distance between contacts at the optimized composition.
By using nwCu as a conducting agent as well as a binder, the inter-tangled SECA was successfully developed, showing a stable physical integrity in terms of cohesion between particles and adhesion to separator (Figure 2a). Even when the composites were highly curved, there was no significant deterioration of their integrity observed. Such a good mechanical properties of SECA originates from development of inter-locking joints between nwSi and nwCu due to the ductile nature of copper (Figure 2b). nwCu was squashed by a pestle into flakes stick to a mortar or kneaded to a monolithic lump (photos in Figure 2b). Due to the ductility of copper, structural joints as the second merit of SECA are expected to be developed in the composites of nwSi with nwCu by pressure in an inter-locking way (Figure 2c). Concaved dents are formed in nwCu at contacts with nwSi (or other nwCu) by using the nwSi (or nwCu) as a mechanically hard template. Resultantly, nwCu grabs nwSi or other nwCu at the locking joints. The inter-locking integrity of SECA accommodated stretching strain impressively. Without pressing, SECA did not maintain its integrity under a stress causing the strain at 40 % (-Press in Figure 2d), showing very poor cyclability (black symbols in Figure 2e). After pressing, however, the inter-locking joints between nwSi and nwCu are developed so that the physical integrity of SECA under stretching and higher capacities were guaranteed (+Press in Figure 2d; red line in Figure 2e). Even after cycling change and discharge 100 times, the integrity of SECA was not damaged (Figure S3). Also, the charge transfer resistance (RCT, Figure S4) and sheet resistance (RSheet, measured by four probe conductivity measurement) of the SECA decreased after pressing: RCT from 30 ohm to 9 ohm; Rsheet from the very high value that is not measured to 50 ohm sq−1.
Cells were galvanostatically lithiated/delithiated at 0.2C/0.5C, respectively. The capacities (Q) were calculated based on the mass of silicon. Electrochemical performances were characterized in terms of rate capability and cyclability. Coin half cells were constructed with the SECA and lithium metal. For comparison, a conventional electrode consisting of nwSi, a binder (a mixture of poly(acrylic acid) and sodium carboxymethyl cellulose or PAA/CMC) and carbon black (Super P) at weight ratio of 6:2:2 was tested at the same condition35. The amount of nwSi loading was fixed at 0.6 to 0.8 mg cm−2 for all samples for fair comparison. In terms of specific capacity normalized by silicon weight (Q/mSi with Q = capacity and mSi = nwSi mass), as expected, the SECA of higher nwCu contents showed higher capacities with better rate capability due to the improvement of electric conduction by nwCu (Figure 3a and b). In the rate capability curve, the conventional electrode of 60 % nwSi as a control was found between SECAs of 50 % nwSi and 70 % nwSi. The capacity retention with cycles (Figure 3d) was comparable between the SECA of 30 % nwSi and the control, showing similarly shaped traces (Figure 3e). The SECA of 50 % and 70 % nwSi was inferior to the SECA of 30 % nwSi due to the lack of nwCu contents. The decay of capacity with cycles was not in a negligible level. However, it should be notified that the decayed capacity with cycles is not due to the electrode structure (SECA or conventional electrodes) but due to the electrochemical nature of nwSi used in our study (e.g., intrinsic pulverization of nwSi36). The inference comes from the fact that the similar or almost identical cyclability except of constant capacity gap was obtained with the SECA of 30 % nwSi and the conventional electrode (Figure 3e), both of which provide ideal environments of conduction pathways to nwSi mass.
To emphasize the merits of SECA over the conventional electrode, the rate capability and cyclability data were re-plotted by using the specific capacity normalized by electrode mass including both nwSi composites with other components and current collector (Q/mEd + CC with mEd + CC = the mass of electrode (Ed) + current collector (CC)) (Figure 3c and f). By saving the mass of current collector, the capacities of SECA are significantly superior to that of the conventional electrode. Therefore, the benefit achieved by our SECA makes high-energy density cells feasible (Figure S5).
The electrochemical performances of the SECA showing improved capacities results from the combination of its structural merits. Two points have been discussed above. Inter-locking joints between nwSi and nwCu (or nwCu and nwCu) possibly improve physical integrity without binders, accelerate charge transfer between electroactive mass (nwSi) and electric pathways (nwCu), percolate networking of electric conduction pathways and provide mechanical framework to suppress volume expansion of silicon. Ultra-light porous current collector enables high energy density cells by reducing total mass with keeping the electroactive mass. As the third benefit of the SECA structure, in addition, volume expansion of silicon was successfully accommodated by voids of the inter-tangled network of nwSi and nwCu (Figure 4). The conventional tri-component electrode experienced severe volume expansion around 300 % (estimated by thickness change from 15 um to 43 um; Figure 4a and b). However, there were no significant volume change observed with our SECA (Figure 4c and d), even if the thickness of only nwSi/nwCu composite part was difficult to be identified from that of the nwCu current collector after cycling. It was clearly observed that the expanded volume of silicon filled the void between nwCu completely after cycling (Figure 4e and f). Based on a simple model of cross-oriented stacks of nanowires (supporting information), volume fraction of available voids was compared between the SECA and the conventional electrode. Void between nwSi was estimated at 21.5 % of total volume when the nwSi are closely stacked in a configuration where longitudinal direction of aligned-nanowire stacks is 90°-oriented alternatively. The additional gap at 22 nm between nwSi (radius = 20 nm) is required to involve 20 wt. % binder and 20 wt. % conducting agents. In this case, however, there is no void fraction to accommodate the volume expansion of silicon. With the gap at 68.2 nm, void volume is generated enough to compensate 300 % volume expansion. The resultant silicon loading density of the conventional electrode configuration with enough void is calculated at 0.12 g cm−3. On the contrary, the SECA of 30 % nwSi had 64.2 % void volume without additional gap required, showing capability of accommodating 280 % volume expansion (355 % and 402 % accommodated by the SECA of 50 % and 70 % nwSi, respectively). The density of silicon loading was estimated at 0.52 g cm−3, which is significantly higher than that of the conventional electrode with enough void fraction (0.12 g cm−3).
In summary, 3D structures based on inter-tangling of two different nanowires (nwSi and nwCu) was developed in this work to achieve high-energy-density lithium ion batteries. Based on the nwSi/nwCu composites, uniquely designed electrode assemblies (SECA) unifying separator, active electrode part and current collector into one compartment were constructed (Figure S6). The three characteristics are emphasized: (1) inter-locking joints based on ductility of copper enabling binder-free electrode systems, (2) ultra-light porous current collectors enabling high energy densities and (3) optimized void fraction to accommodate volume expansion of silicon. With enhanced rate capability (Q15C = 67.3 % of Q0.5C for SECA with Q#C = capacity at indicated C rate; cf. Q15C = 14.1 % of Q0.5C for a conventional electrode system) and cyclability (Q at the 100th cycle = 71.4 % of Q at the initial cycle for SECA versus 55.7 % for the conventional), the specific capacity normalized by the weight including electrode and current collector was estimated at 350 to 570 mAh g−1 which is incomparable with that of the conventional electrode system (45 mAh g−1). Also, we believe that the 3D structure can be used as a platform to estimate the volume expansion of silicon material as shown in structure-related modeling.
Methods
SECA
10 mg of nwSi (diameter (D) = 40 nm, length (L) = 1 to 20 um; Sigma; Figure S7) and nwCu (D = 100 ~ 200 nm, L = 0.8 to 6 um, ACS material; Figure S7) with a defined ratio was well dispersed in 20 ml ethanol by ultrasonicator at 25°C for 30 min. The mixture was filtrated through a separator (polyethylene; Asahi NH716; Figure S8) by vacuum. Then, porous current-collector layer was laminated on the pre-developed active layer by filtrating 20 ml ethanolic solution of 10 mg nwCu in the same way. The SECA was dried in vacuum oven at 70°C for 3 h to remove ethanol and then mechanically pressed with 12 MPa by oil-hydraulic press.
Conventional electrode
An aqueous mixture slurry of nwSi, a binder and a conducting agent at 6:2:2 by weight was pasted in 15 um thickness on a current collector (18 um thick Cu foil) by doctor blade. The electrode was dried in vacuum at 150°C for 2 h. A mixture of poly(acrylic acid) (PAA, Mw = 3,000,000, Sigma) and sodium carboxymethyl cellulose (CMC, Mw = 250,000, Sigma) at a ratio of 1:1 by weight was used as the binder. Carbon black (Super P, TIMCAL) was used as the conducting agent. The loading amount of the active material was around 0.6 mg cm−2.
References
Winter, M., Besenhard, J. O., Spahr, M. E. & Novμk, P. Insertion Electrode Materials for Rechargeable Lithium battery. Adv. Mater. 10, 725–763 (1998).
Jia, X. L. et al. High-performance flexible lithium-ion electrodes based on robust network architecture. Energy Environ. Sci. 5, 6845–6849 (2012).
Poizot, P., Laruelle, S., Grugeon, S., Dupont, L. & Tarascon, J. M. Nano-sized transition-metaloxides as negative-electrode materials for lithium-ion batteries. Nature 407, 496–499 (2000).
Cabana, J., Monconduit, L., Larcher, D. & Palacin, M. R. Beyond intercalation-based Li-ion batteries: the state of the art and challenges of electrode materials reacting through conversion reactions. Adv. Mater. 22, E170–192 (2010).
Zhang, W. J. Lithium insertion/extraction mechanism in alloy anodes for lithium-ion batteries. J. Power Sources 196, 877–885 (2011).
Winter, M. & Besenhard, J. O. Electrochemical lithiation of tin and tin-based intermetallics and composites. Electrochim. Acta 45, 31–50 (1999).
Armand, M. & Tarascon, J. M. Building better batteries. Nature 451, 652–657 (2008).
Bruce, P. G., Scrosati, B. & Tarascon, J. M. Nanomaterials for rechargeable lithium batteries. Angew. Chem. Int. Ed. 47, 2930–2946 (2008).
Park, C. M., Kim, J. H., Kim, H. & Sohn, H. J. Li-alloy based anode materials for Li secondary batteries. Chem. Soc. Rev. 39, 3115–3141 (2010).
Tarascon, J. M. & Armand, M. Issues and challenges facing rechargeable lithium batteries. Nature 414, 359–367 (2001).
Wu, H. & Cui, Y. Designing nanostructured Si anodes for high energy lithium ion batteries. Nano Today 7, 414–429 (2012).
Park, M. H. et al. Silicon nanotube battery anodes. Nano Lett. 9, 3844–3847 (2009).
Bang, B. M., Kim, H., Song, H. K., Cho, J. & Park, S. Scalable approach to multi-dimensional bulk Si anodes via metal-assisted chemical etching. Energy Environ. Sci. 4, 5013–5019 (2011).
Yao, Y. et al. Interconnected Silicon Hollow Nanospheres for Lithium-Ion Battery Anodes with Long Cycle Life. Nano Lett. 11, 2949–2954 (2011).
Wu, H. et al. Stable cycling of double-walled silicon nanotube battery anodes through solid-electrolyte interphase control. Nat. Nanotechnol. 7, 310–315 (2012).
Wu, H. et al. Engineering Empty Space between Si Nanoparticles for Lithium-Ion Battery Anodes. Nano Lett. 12, 904–909 (2012).
Jung, D. S., Hwang, T. H., Park, S. B. & Choi, J. W. Spray Drying Method for Large-Scale and High-Performance Silicon Negative Electrodes in Li-Ion Batteries. Nano Lett. 13, 2092–2097 (2013).
Park, Y. et al. Si-Encapsulating Hollow Carbon Electrodes via Electroless Etching for Lithium-Ion Batteries. Adv. Energy Mater. 3, 206–212 (2013).
Wang, B. et al. Contact-engineered and void-involved silicon/carbon nanohybrids as lithium-ion-battery anodes. Adv. Mater. 25, 3560–3565 (2013).
Zhou, X., Wan, L. J. & Guo, Y. G. Electrospun silicon nanoparticle/porous carbon hybrid nanofibers for lithium-ion batteries. Small 9, 2684–2688 (2013).
Chen, X. et al. Conductive rigid skeleton supported silicon as high-performance Li-ion battery anodes. Nano Lett. 12, 4124–4130 (2012).
Yao, Y., Liu, N., McDowell, M. T., Pasta, M. & Cui, Y. Improving the cycling stability of silicon nanowire anodes with conducting polymer coatings. Energy Environ. Sci. 5, 7927–7930 (2012).
Zhou, X. S., Yin, Y. X., Wan, L. J. & Guo, Y. G. Self-Assembled Nanocomposite of Silicon Nanoparticles Encapsulated in Graphene through Electrostatic Attraction for Lithium-Ion Batteries. Adv. Energy Mater. 2, 1086–1090 (2012).
Liu, B. et al. Hierarchical silicon nanowires-carbon textiles matrix as a binder-free anode for high-performance advanced lithium-ion batteries. Sci. Rep. 3 10.1038/srep01622 (2013).
Zhu, Y. et al. Directing silicon-graphene self-assembly as a core/shell anode for high-performance lithium-ion batteries. Langmuir 29, 744–749 (2013).
Chan, C. K. et al. High-performance lithium battery anodes using silicon nanowires. Nat. Nanotechnol. 3, 31–35 (2008).
Cui, L. F., Yang, Y., Hsu, C. M. & Cui, Y. Carbon-Silicon Core-Shell Nanowires as High Capacity Electrode for Lithium Ion Batteries. Nano Lett. 9, 3370–3374 (2009).
Cui, L. F., Ruffo, R., Chan, C. K., Peng, H. L. & Cui, Y. Crystalline-Amorphous Core-Shell Silicon Nanowires for High Capacity and High Current Battery Electrodes. Nano Lett. 9, 491–495 (2009).
Wang, B. et al. Intertwined Network of Si/C Nanocables and Carbon Nanotubes as Lithium-Ion Battery Anodes. ACS Appl. Mater. Interfaces 5, 6467–6472 (2013).
Hu, L. B. et al. Silicon-conductive nanopaper for Li-ion batteries. Nano Energy 2, 138–145 (2013).
Wang, W. et al. Binder-free three-dimensional silicon/carbon nanowire networks for high performance lithium-ion battery anodes. Nano Energy 2, 943–950 (2013).
Wang, B. et al. High Volumetric Capacity Silicon-Based Lithium Battery Anodes by Nanoscale System Engineering. Nano Lett. 13, 5578–5584 (2013).
Bogart, T. D. et al. Lithium Ion Battery Peformance of Silicon Nanowires with Carbon Skin. ACS Nano 8, 915–922 (2014).
Yoo, J. K., Kim, J., Jung, Y. S. & Kang, K. Scalable Fabrication of Silicon Nanotubes and their Application to Energy Storage. Adv. Mater. 24, 5452–5456 (2012).
Koo, B. et al. A highly cross-linked polymeric binder for high-performance silicon negative electrodes in lithium ion batteries. Angew. Chem. Int. Ed. 51, 8762–8767 (2012).
Xia, H., Tang, S. B. & Lu, L. Properties of amorphous Si thin film anodes prepared by pulsed laser deposition. Mater. Res. Bull. 42, 1301–1309 (2007).
Acknowledgements
This work was supported by MOTIE (Green: 10042948 (KEIT), Star:20135020900030), MSIP (Mid: 2013R1A2A2A04015706 (NRF)) and MOE (BK21Plus: 10Z20130011057), Korea.
Author information
Authors and Affiliations
Contributions
C.H. and H.-K.S. conceived the idea and designed experiments. C.H. fabricated electrodes. C.H., T.-H.K., Y.-G.C. and J.K. carried out electrochemical characterization. C.H., T.-H.K. and J.K. performed morphological characterization. C.H. and H.-K.S. analyzed data and co-wrote the paper. H.-K.S. led overall project.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Supplementary Information
supporting information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Hwang, C., Kim, TH., Cho, YG. et al. All-in-one assembly based on 3D-intertangled and cross-jointed architectures of Si/Cu 1D-nanowires for lithium ion batteries. Sci Rep 5, 8623 (2015). https://doi.org/10.1038/srep08623
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep08623
This article is cited by
-
Kinked silicon nanowires-enabled interweaving electrode configuration for lithium-ion batteries
Scientific Reports (2018)
-
Copper nanowire/multi-walled carbon nanotube composites as all-nanowire flexible electrode for fast-charging/discharging lithium-ion battery
Nano Research (2018)
-
Breathing silicon anodes for durable high-power operations
Scientific Reports (2015)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.