Main

Natural circular dichroism (NCD) and gyrotropy are observed respectively as the change in the ellipticity and the rotation of the polarization of light transmitted through chiral media. Because the sign of these quantities depends on the handedness of the material, NCD is a common probe of chirality over a broad spectrum of the electromagnetic radiation, as reviewed in Fig. 1, when applied to the chiroptical study of proteins. Ultraviolet NCD spectroscopy of peptide-bond excitations is a well-established method for the determination of the secondary structure of proteins3,13. Recent extensions of NCD spectroscopy to the infrared and X-ray regions have shed light on new signatures of chirality of matter expressed by molecular vibrations2,5,14 and core electron excitations15. Extending this context, the handedness of magnetic matter should also be detected in the NCD spectra of spin excitations, typically at gigahertz to terahertz frequencies, although these have seldom been investigated.

Figure 1: Chiroptical spectroscopy: an efficient probe of chirality both via charge and spin excitations.
figure 1

Depending on the wavelength, λ, light interacts with various degrees of freedom and detects the handedness of matter at different levels. The soft X-ray natural circular dichroism (SXNCD) picks up chirality via the core-electron excitations, whereas the circular dichroism in the ultraviolet and visible region (UV/VIS CD) probes it through transitions of valence electrons. Molecular vibrations are also sensitive to the handedness, which is manifested in the vibrational circular dichroism (VCD) or the Raman optical activity (ROA). We predict that besides the charge excitations above, spin-wave excitations in the gigahertz–terahertz region (λ100 μm–10 mm) of the electromagnetic spectrum can also probe the chirality of magnetic materials and show SOA.

When chirality is accompanied by magnetism, an intriguing optical cross effect, the magneto-chiral dichroism8,9 (MChD), emerges besides the conventional magnetically induced circular dichroism (MCD). MChD is a directional dichroism and is measured as the absorption difference for unpolarized (or linearly polarized) light propagating parallel and antiparallel to the magnetization of the media. MChD is generally recognized as a weak effect and has been found for visible light in metallic complexes10, molecular magnets16, inorganic crystals17 and cholesteric liquid crystals18. However, a recent study of the chiral phase of CuB2O4 proved that MChD can reach the order of unity (100%) in crystal field transitions of d shell electrons19. An optical second harmonic generation study of the multiferroic LiCoPO4 also indicated that the electric dipole excitations of the d shell electrons can probe chirality20.

Spin-waves (magnons) in conventional magnets are excited by the magnetic component of light and they naturally show the MCD effect, whereas NCD and MChD effects are forbidden. A prerequisite to observe such phenomena in the long-wavelength region is the existence of dynamical coupling between spins and microscopic electric dipoles in the material2. In multiferroic materials, where magnetization (M) and ferroelectric polarization (P) are interlocked, such cross-coupling is possible and was indeed observed as electrically excited magnetic resonance in several compounds, including RMnO3 (refs 21, 22), RMn2O5 (ref. 23), BiFeO3 (ref. 24), and most recently in Ba2CoGe2O7 (ref. 25). However, the question of chirality has not been addressed so far in these systems. We predict that a magnetically induced chiral state with switchable handedness can emerge in magnets with non-centrosymmetric but non-chiral crystal structure, as we demonstrate for Ba2CoGe2O7. Cross-resonances between electric and magnetic dipole active transitions existing at spin excitations in Ba2CoGe2O7 provide us with an excellent opportunity to observe gigantic NCD and MChD effects.

Ba2CoGe2O7 has a tetragonal crystal structure where Co2+ cations with S = 3/2 spin form square-lattice layers stacked along the tetragonal [001] axis (see Fig. 2a). Néel-type antiferromagnetic order develops below TN = 6.7 K, with spins lying in the plane of the layers (tetragonal plane)26. Moderate magnetic fields, Bdc1 T, applied in this plane effectively induce a ferromagnetic moment by canting the spins, while the antiferromagnetic component of the magnetization aligns perpendicular to the field, as shown in Fig. 2b. When the ferromagnetic moment points along the [110] axis, a ferroelectric polarization appears parallel to the [001] axis27. Rotation of the magnetic field within the tetragonal plane rotates M, accompanied by the sinusoidal modulation of P (ref. 27). Whereas ferroelectricity vanishes in magnetic fields applied along the [100] or [010] axis, the corresponding spin patterns break all mirror-plane symmetries of the lattice, as visualized in Fig. 2b,c, and the material becomes chiral19,28. We emphasize that although neither the spin nor the lattice structure alone is chiral, the whole spin–lattice system forms a chiral object: the π/2 rotation of the magnetic field from [100] to [010] direction switches between the left- and right-handed forms of the magnetic crystal, corresponding to the chiral space groups P21212 and P21212, respectively28 (see Fig. 2b,c). Such soft switching of handedness is hardly conceivable in molecules and crystals with purely structural chirality.

Figure 2: Main aspects of magnetically induced chirality.
figure 2

a, The crystal structure of Ba2CoGe2O7 belongs to the tetragonal space group . The corresponding point group can be represented by a single tetrahedron compressed in the [001] direction. Its two longer edges are indicated with blue lines. b, When the external magnetic field points along the [100] or [010] axis, the antiferromagnetic spin pattern with field-induced canting (blue arrows) breaks all mirror-plane symmetries of the lattice, hence, it makes the crystal chiral with the point symmetry of 222 or 222, respectively. Switching between the left-handed (L) and right-handed (R) enantiomers can be carried out by rotation of the magnetic field from the [100] to the [010] direction, being equivalent to the m(110) mirror reflection (dashed line). c, The magnetically induced chirality of the material and the corresponding point symmetries can be schematized by the compressed tetrahedron together with a magnetic moment connecting midpoints of two opposite shorter edges (representing the lattice symmetry and the spin system, respectively). In the mirror image obtained by m(110) reflection, the tetrahedron remains unchanged, while the magnetic moment (axial vector) is rotated by π/2. Image and mirror image are enantiomeric pairs as they cannot be brought into coincidence with each other by pure rotations and translations even when combined with time-reversal operation.

The nature of the spin excitations in the magnetically induced chiral state of Ba2CoGe2O7 was studied by polarization-sensitive optical spectroscopy over the gigahertz–terahertz regime (see Methods). We found two spin resonances located at frequencies f≈0.5 THz and f≈1 THz in zero field. With increasing magnetic field a third mode appears from low frequencies, which corresponds to the gapless Goldstone mode in the zero-field limit26. These modes exhibit strong polarization rotation and ellipticity for each propagation direction and polarization configuration whenever the static magnetic field, Bdc, points along [100] or [010] direction. (The full polarization study is presented in the Supplementary Information.) When the light propagates along the [001] axis perpendicular to the static magnetic field and , as in a typical case shown in Fig. 3a, all three resonances are excited. In Bdc = 7 T, the ‘Goldstone mode’ is located at f≈0.27 THz and the other two modes are split into several bands. The band around 1 THz induces a strong polarization change characterized by θ≈90° mm−1, η≈35° mm−1 close to the resonance frequency, whereas the effect is a factor of three smaller for the lower-frequency magnon modes.

Figure 3: Absorption (α), polarization rotation (θ) and ellipticity (η) spectra of the spin-wave modes for light propagation along the [001] axis as measured by time-domain terahertz spectroscopy and calculated theoretically.
figure 3

a, The modes observed at 0.5 THz and 1 THz in zero field show clear splittings in high magnetic fields parallel to the [010] axis, as indicated by arrows. The ‘Goldstone mode’ (G) is centred around 0.27 THz. The large polarization rotation and ellipticity are even functions of the magnetic field. b, When the external magnetic field direction is rotated from the [100] to the [010] axis, both θ and η change sign, whereas they are zero within the experimental accuracy when the magnetic field points along the [110] direction and the m(110) mirror-plane symmetry is restored. Thus, these polarization phenomena can be identified as SOA in a chiral media.

These polarization phenomena are even functions of the magnetic field, thereby excluding any contributions from conventional MCD. Furthermore, the sign of the polarization rotation and ellipticity spectra are reversed by the simultaneous rotation of Bdc and Eω from [100] to [010], as shown in Fig. 3b. In the case of magnetically induced linear birefringence/dichroism, the optical axes would be linked to the direction of Bdc as the (001) plane is originally isotropic in the paramagnetic state. As Eω is kept parallel with Bdc, the sign change observed in θ and η is not compatible with linear birefringence and dichroism, although the magnitude of the rotation and ellipticity spectra can be influenced by these linear polarization effects (see Supplementary Information). Instead, this sign reversal is specific to optical activity and provides a direct proof of the true chirality and the field-induced switching of the handedness of matter. In fields applied along the intermediate [110] direction, by contrast, no NCD and gyrotropy appear, indicating the lack of chirality as the m(110) mirror-plane symmetry is restored.

The existence of MChD was investigated in the chiral state by keeping Bdc along the [010] or [100] axis, while choosing the light propagation to be parallel or antiparallel to Bdc (see Fig. 4). In this configuration, called the Faraday geometry, the magnetic resonance at 0.5 THz is silent. The mode at 1 THz is split in larger fields and the ‘Goldstone mode’ enters from lower frequencies above 4 T. The magnetically induced handedness is also manifested in strong NCD and gyrotropy (see Supplementary Information).

Figure 4: Magneto-chiral effect in the field-induced chiral state.
figure 4

Absorption is studied when light propagates along the [010] axis parallel (+Bdc) and antiparallel (−Bdc) to the external magnetic field. a,b, Absorption spectra for light polarizations Eω[100] (a) and Eω[001] (b), measured as a function of the magnetic field, are shifted in proportion to the corresponding Bdc values. Red and blue curves indicate the case of +Bdc and −Bdc, respectively. Between the spin resonances the material is transparent, as α≈0. The magneto-chiral dichroism, corresponding to the difference of the absorption coefficients for counter-propagating beams, is huge both for the ‘Goldstone mode’ (highlighted green) and the low-frequency branch of the resonance at 1 THz (highlighted orange). Δα/αmax70% in the highlighted regions. c,d, The sign and magnitude of the experimentally observed MChD effect (coloured curves) are reproduced by our theoretical model (black curves) for two polarizations Eω[100] and Eω[100] as in c and d, respectively.

The difference in absorption, Δα = α+α, for light propagating parallel and antiparallel to the external field is large for all optically active spin resonances (Fig. 4c,d). Note that the ‘Goldstone mode’ exhibits MChD as large as Δα/αmax70% for both polarizations in high fields, where αmax = max{α+,α}. For the light polarization Eω[001] shown in Fig. 4, the absorption nearly vanishes at the low-frequency branch of the 1 THz resonance for the beam propagating antiparallel to the direction of Bdc. It means that the material becomes transparent at these frequencies when viewed from the direction of the magnetization, whereas the absorption remains fairly large for light travelling in the opposite direction, that is, Δα/αmax is close to 100%. As is clear from Fig. 3c,d, the effect is still appreciable in low magnetic fields.

NCD and MChD, emerging in Ba2CoGe2O7 with large magnitude in the gigahertz–terahertz range, are observed for the first time for spin excitations. In the conventional view spins respond to the magnetic field of light, which induces their precession described by the dynamical magnetic permeability . In this multiferroic material, where spins are coupled to microscopic electric dipoles, a new channel opens to excite the spins via the electric field of light29, the so-called electromagnon process. Consequently, the dynamics of the spins also induces oscillating electric polarization in the material, expressed by the dielectric permittivity .

Because these spin resonances can simultaneously be excited by the magnetic and electric components of light with similar strength, the dynamical magnetoelectric tensor also affects the optical response. It describes the oscillations of the magnetization in the material induced by the electric field of light, , in analogy with the d.c. magnetoelectric effect (ɛ0 and μ0 are the dielectric permittivity and magnetic permeability of vacuum). In Ba2CoGe2O7, the symmetry of the magnetically ordered phase and the corresponding form of can be controlled by the magnetic field. Specifically, fields Bdc1 T applied parallel to the [100] or [010] crystallographic axis yield

where Bdc and the [001] tetragonal axis are set parallel to the y- and the z-axis, respectively. The sign change of on π/2 rotation of the crystal around the z-axis is related to the switching between the two enantiomers. The diagonal components (invariant under time-reversal) are responsible for NCD, whereas the off-diagonal elements (changing sign on time-reversal) generate MChD. The existence of magnetically induced chirality and NCD in Ba2CoGe2O7 can alternatively be predicted by the symmetry analysis of the magneto-gyration tensor Fα β γ δ in its paramagnetic space group . This response function is related to the magnetoelectric tensor according to Fα β γ δ = (2gα β)/( Bγ Bδ)|B = 0 = 1/c(2(χβ αmeχγ γme·δα β))/( Bγ Bδ)|B = 0, where gα β is the gyration tensor, B is the magnetic field and c is the speed of light2. Here the Greek symbols stand for cartesian indices x,y and z while δ denotes Kronecker delta. In accordance with the observed sign change of NCD on rotation of Bdc from the [100] to the [010] direction, Neumann’s principle gives that Fz z x x and Fz z y y components are finite (Fz z x x = −Fz z y y), while the lack of NCD for Bdc[110] corresponds to Fz z x y = 0.

We have successfully described the magnetically induced chirality in the ground state of Ba2CoGe2O7 and its spin excitation spectrum based on a microscopic spin model. Next, we solved the Maxwell equations using , and obtained from this theory. (For details see the Supplementary Information.) The calculated absorption and gyrotropy/NCD spectra—as approximated by and θ+i η = (i ω/2c){χγ γme+χδ δme}, respectively—reproduce the experimental results as shown in Fig. 3. Furthermore, the measured MChD spectra shown in Fig. 4c,d show an overall agreement with the theoretical curves Δα = α+α = (4ω)/(c)Im{χγ δme}.

The observed strong NCD and gyrotropy—what we call SOA—together with the giant MChD are the direct manifestations of the dynamical magnetoelectric effect. Because simple spin orders, such as ferromagnetic or antiferromagnetic, can effectively generate magnetoelectric coupling in crystals without inversion symmetry, we expect that a broad variety of magnetic materials offer these novel optical functionalities for the polarization and directional control of light.

Methods

Samples.

Single crystals of Ba2CoGe2O7 were grown by a floating zone method. Crystals were characterized by ferroelectric polarization and magnetization measurements. The precisely oriented samples used in the terahertz study had slab-like shapes with a typical thickness of 1 mm and cross-section of 10 mm2.

Circular dichroism spectroscopy.

We adopted terahertz time-domain spectroscopy30,31 to obtain the complex transmission spectrum in the frequency range 0.2–2 THz with a resolution of 0.05 THz. The femtosecond laser pulses delivered from a mode-locked Ti:sapphire laser (centre wavelength of 800 nm, pulse width of 100 fs, repetition rate of 80 MHz) were irradiated to a biased photo-switching device made of low-temperature-grown GaAs (LT-GaAs) coupled with a dipole antenna, or to the surface of a p-type InAs crystal. The terahertz pulses radiated by such emitters were collimated by a pair of off-axis paraboloidal mirrors and were focused on the sample. After passing through the sample the beam was collimated again and focused on the detector by a second pair of off-axis paraboloidal mirrors. For the detection, another LT-GaAs photo-switching device coupled with a dipole antenna or an electro-optic sampling method with a (110) ZnTe crystal was used. The light polarization was carefully set parallel to each crystallographic axis using a wire-grid polarizer. The polarization state of the beam transmitted through the sample was analysed by another wire-grid polarizer. To obtain the absolute transmission of the material, the sample was replaced by a hole with the same diameter, through which the direct beam was measured. Static magnetic fields up to ±7 T were applied by a superconducting split-coil magnet.

From the time-domain transmission experiments, performed in several polarization configurations, we determined each element of the complex transmission matrix. Besides the absorption coefficient, , changes in the polarization state of linearly polarized light due to NCD and gyrotropy were determined according to

where d is the sample thickness, and are the complex transmission coefficients for the sample placed between parallel and crossed polarizers, while θ and η are the polarization rotation and ellipticity, respectively (for more details see Supplementary Information).

Magnetochiral dichroism experiment.

For the study of the MChD effect, we used Fourier transform absorption spectroscopy. The measurement system, which is based on a Martin–Puplett interferometer, a mercury arc lamp as a light source, and a Si bolometer cooled down to 300 mK as a light intensity detector, covered the spectral range 0.13–6 THz with a maximum resolution of 0.004 THz. A single wire-grid polarizer was inserted to set the polarization state of the beam before the sample. However, the detection side, that is, the light path after the sample including the detector, was insensitive to the polarization of light. Static magnetic fields up to ±12 T were applied by a superconducting solenoid magnet.