Abstract
Wet-chemical synthesis is a promising alternative to the conventional vapour-phase method owing to its advantages in commercial-scale production at low cost. Studies on nanocrystallization in solution have suggested that growth rate is commonly affected by the size and density of surrounding crystals. However, systematic investigation on the mutual interaction among neighbouring crystals is still lacking. Here we report on strong interactive growth behaviours observed during anisotropic growth of zinc oxide hexagonal nanorods arrays. In particular, we found multiple growth regimes demonstrating that the diameter of the rod is dependent on its height. Local interactions among the growing rods result in cases where height is irrelevant to the diameter, increased with increasing diameter or inversely proportional to the diameter. These phenomena originate from material diffusion and the size-dependent Gibbs–Thomson effect that are universally applicable to a variety of material systems, thereby providing bottom-up strategies for diverse three-dimensional nanofabrication.
Similar content being viewed by others
Introduction
Precisely controlled growth of one-dimensional nanocrystals (that is, wires, tubes and rods) has created opportunities to fabricate new types of devices with generic vertical configurations possessing advantageous electrical, optical, biological and mechanical properties, as well as high-density integration1,2,3,4,5. This growth is usually achieved by a vapour-phase deposition method, in which key parameters determining the growth behaviours have been thoroughly investigated. In particular, there has been substantial interest in axial growth rate in correlation with the diameter and interspacing of nanocrystals6,7,8,9,10, yet experimental results on this topic have varied from case to case, and its mechanism has not been satisfactorily determined thus far. For example, it has been generally accepted that the Gibbs–Thomson (GT) effect leads to a shorter length for smaller diameters6,7,8, but the opposite dependence has also been reported and was ascribed to the role of material diffusion that prevails over interfacial reaction9,10,11,12. In particular, when growth occurs via a vapour–liquid–solid process, the crystallization reaction is further mediated by a nanosized catalyst, and the resulting interplay between the incorporation of reactants and crystallization makes the situation more complicated13,14. Accordingly, despite the fact that growth kinetics provide an additional degree of freedom for three-dimensional (3D) nanofabrication, the overall complexity makes precise control of crystal nanostructures difficult in practice. Moreover, these approaches were generally performed with high-temperature vacuum processing within a narrow growth window, and thus there are critical limits in cost-effective production and controllability.
There has been similar interest in solution-phase synthesis due to its simplicity and the capability to produce single-crystalline nanocrystals with controlled orientation, size and morphology15,16,17,18,19,20,21. Solution-phase synthesis is also available for epitaxial growth if the conditions are set to allow for heterogeneous solidification to take place at a low level of supersaturation22,23,24. This approach is further exemplified herein to achieve patterned arrays of vertically grown ZnO hexagonal rods. In the synthesis, strong interactions among the adjacent crystals, originating from GT, competitive and/or synergetic effects, are found to produce diverse relationships between diameter and axial growth velocity. Systematic study is performed to understand multiple types of growth mechanisms, and significant dependence of the rod diameter on the height. These unique behaviours are further exploited to construct more sophisticated nanostructures with artificially regulated 3D height profiles.
Results
Growth behaviours with different solute concentration
Solution-phase synthesis of ZnO rods is based on a hydrothermal reaction process involving the dissociation of zinc nitrate and hexamethylenetetramine (HMT) that produces Zn2+ and hydroxyl (OH−) ions, respectively25. As a polar crystal comprised of tetrahedrally coordinated Zn2+ and O2− ions, the preferential growth along the c axis orientation continues by iterative reaction involving association and dehydration of the precursor ions at the top (0001) surfaces. The precipitation occurs either directly (that is, Zn2++2OH−↔Zn(OH)2↔ZnOs+H2O) or via the zinc hydroxide (that is, Zn2++2OH−↔Zn(OH)2↔ZnOs+H2O), depending on the solution conditions26. Heating of the solution is required to activate the chain of processes, but growth usually occurs below the boiling point of water. Due to the low growth temperature as well as site-specific capture of ions, size- and position-controlled growth could be achieved by lithographically defined polymer patterns on a ZnO seed layer (Fig. 1d)27. We first grew ZnO rods via polymethylmethacrylate (PMMA) patterns consisting of circular hole arrays, in which the diameter in columns increased from 100 to 600 nm while the centre-to-centre distance Lc–c was set to 800 nm (see Methods for details). The resulting ZnO rods have near-perfect vertical alignment and in-plane hexagonal symmetry, as confirmed in the scanning electron microscopy images in Fig. 1a–c. In addition, although diameter DZnO (that is, hexagon diagonal) and height HZnO are sensitive to the growth parameters, they are relatively uniform for growth from holes of the same size under identical conditions with average s.d. of ~4% in diameter and ~2% in height.
Interestingly, the growth of ZnO rods is sensitive to solute concentration Cb, as characterized by the correlation between DZnO and HZnO. ZnO rod arrays grown at a Cb above 25 mM show that the HZnO is nearly independent of DZnO (Fig. 1a), while HZnO increases with increasing DZnO for the sample grown at an intermediate Cb of 2.5 mM (Fig. 1b); if the Cb decreases further to 1.6 mM, thinner rods become longer than thicker rods (Fig. 1c).
Growth under surface reaction-limited conditions
Solution-phase synthesis is analogous to vapour-phase growth, in that the reaction at the solid surface or mass transport through the boundary layer is rate limiting. Given that higher Cb provides a sufficient supply of precursor ions, the growth at higher Cb (Cb=25 mM) becomes more surface reaction dependent. In this growth regime, growth of rods is hardly affected by neighbouring rods. Notably, the GT effect, wherein the driving force for the phase transformation (that is, axial growth) is size dependent, is negligible (Fig. 1a,d).
GT effect under mass transport-limited conditions
On the other hand, growth rate of ZnO rods becomes dependent on DZnO with reduced Cb. When the precursor concentration decreased by a factor of 10 (Cb=2.5 mM), growth showed such a strong diameter dependence that the rods with an 800-nm diameter are roughly twice as high as those with a 200-nm diameter (Fig. 1b,e). The reduced supply of precursors makes growth more sensitive to mass transfer of the precursor ions. Under these circumstances, individual rods do not behave anymore as independent objects and interfere with each other, especially where the inter-rod spacing is much smaller than the thickness of the boundary layer formed over the substrate surface. We attribute this phenomenon mainly to the differences in local equilibrium concentration of the precursors in the regions of rods with different sizes. This is based on the GT effect, which generates increases in local concentration relative to the equilibrium concentration at a flat surface28 (radius of curvature r=∞) that are inversely proportional to the radius of crystal curvature, rZnO. The resulting concentration gradients cause a flux of precursor ions from the regions of thin rods to regions of thicker ones, thereby leading to diameter dependence of the growth velocity. An extreme case of the GT effect is Ostwald ripening29,30,31, in which the capillary forces cause larger-sized crystals to grow at the expense of smaller-sized crystals.
Source competition under mass transport-limited conditions
If Cb is further decreased below 1.6 mM, the situation is reversed in that HZnO is inversely proportional to DZnO (Fig. 1c,f). This phenomenon originated from an increased competition for the precursor among the neighbouring rods9,10. Thicker rods need more precursor consumption to grow at the same rate as thinner rods, but the limited precursor ions available from the surroundings lead to a decrease in growth rates. The competition is still active at a lower solute concentration of 1.25 mM or at a wider rod-to-rod spacing Lc–c of 3 μm (Fig. 1f). Another distinct feature is that the thick rods grown in this situation generally have a concave tip, which should be related to the transport of Zn2+ ions and/or their local distributions due to the electrostatic interaction near the top polar surface of ZnO rods that are more critical in the competition regime. There should be a localized increase in the Zn2+ ion concentration at the edge of the surface compared with the centre, since the surface polarity is stronger at the centre of tips32. In addition, Zn2+ ions existing in the surrounding diffuse along the nonpolar side surface or in the solution and mostly arrive at the edge of the tips earlier than at the centre25,27. As a consequence, precipitation occurs preferentially at the edge of the tips, which produces their unique morphology. A similar mechanism was introduced to explain the ZnO nanotube growth in solution32.
In our model, mutual interactions among growing rods might not only be determined by DZnO and synthesis parameters, but can also be affected by inter-distances and configurations of the neighbouring crystals. To clarify this issue and to investigate the change in growth velocities of ZnO rods depending on the configurations, we grew a series of square arrays (6 × 10) of ZnO rods using circular hole arrays with diameters that gradually increased from 100 nm (far left array) to 500 nm (far right array) (Fig. 2a,b) while being identical within the same array. At Cb of 2.5 mM (in which the GT effect dominates), the HZnO shows a gradual increase with DZnO, but it becomes saturated when thicker rods are closely adjacent and the gaps between the rods are smaller than DZnO (DZnO≥500 nm) (Fig. 2c, red squares). This can be attributed to the onset of material competition, counteracting the local concentration gradient originating from the GT effect. Along the same lines, for the case of Cb below 1.6 mM (in the competition control regime), the more severe competition among the thicker rods caused a further decrease in the growth rate. Consequently, HZnO became more sensitive to DZnO for the square arrays (green and blue squares in Fig. 2c), compared with those in Fig. 1f (see also Supplementary Fig. 8).
Synergetic effect
In the GT control regime (at Cb of 2.5 mM), the overall HZnO values decreased by ~0.2 μm with increasing Lc–c from 800 nm to 3 μm (see closed versus open triangles in Fig. 1e; Fig. 3a,b also directly compares the heights of rods with the same DZnO, but different values of Lc–c). This is contrary to the cases at lower Cb, where the contribution of source sharing results in higher growth rate at wider rod-to-rod spacings (Fig. 1f, see also Supplementary Figs 2 and 3). Similar behaviour was observed during vapour-phase growth of III–V compound nanowires and was attributed to the catalysed decomposition of metal-organic precursors to secondary species that diffused to neighbouring wires and synergistically contribute to wire growth33. As mentioned earlier, in our case, ZnO can be precipitated via the hydroxide, which illustrates the development of the Zn(OH)2 at the rod surfaces, especially at the tips. The intermediate specie is known to be stable in an aqueous solution at a relatively high ion concentration32,34, and can be desorbed or reabsorbed reversibly and contribute to the growth of neighbouring rods within their diffusion limit. The Zn(OH)2, however, dissolves easily in lower ion concentration, and thereby the synergetic effect is not significant in the competition regime.
On the basis of our hypothesis, the synergetic effect becomes significant when rods are located close enough without substantial overlap of the precursor collection volumes, and thus precursor competition is negligible. To examine the validity of the hypothesis, we grew linear arrays of small diameter rods (DZnO=230 nm) between thicker rods (DZnO=625 nm). When the rods are located at an Lc–c of 1 μm, thin rods right next to the thick rods grew faster than those in the middle of the array (Fig. 3c); this is a characteristic feature of the synergetic effect of crystal growth33,35. It is also noted that both thicker rods and neighbouring thinner rods accelerate each others’ growth rate, resulting in an overall increase in the HZnO (Fig. 3d). As expected, the synergetic effect decreases with increasing inter-rod spacing and, in this case, almost disappeared at an Lc–c of 2 μm or longer, whereas the GT effect is still strongly active.
Discussion
We attribute our finding on strong interactive growth to complex interplay of diffusing transport of precursor ions and Zn(OH)2 around the neighbouring rods. To justify our growth model, the contribution of local diffusion of Zn2+ ions between the neighbouring rods, Ji, relative to bulk diffusion through the boundary layer, Jb, is first considered numerically. Under quasi-steady-state conditions, the precursor ion concentration in the boundary layer decreases linearly and comes close to Csi=Cbi/(1+Φ) near the flat solid surface, where Cbi is the ion concentration in the bulk solution and the Thiele modulus (Φ) is the ratio of the surface reaction rate to the diffusion rate. If the size effect was taken into account, the local equilibrium concentration near the surface of the rod with a radius of curvature rZnO slightly increases to by the GT effect, where γ is the interfacial energy, Vm is the molar volume of the solid phase, R is the gas constant and T is the temperature28. In the case of Ф<1 (at higher Cbi), the overall growth is determined by consumption rate via surface reaction, Js, and thus the local concentration difference between the rod surfaces has no substantial influence. However, in the mass transport-limited regime (Ф>1), the interplay between bulk and local diffusion prevails over surface reaction, and their contributions are simply estimated as a function of Ф (see Supplementary Methods and Supplementary Fig. 10 for details). The ratio of Ji to Jb for the adjacent rods with DZnO of 800 and 140 nm, respectively, separated by 1–3 μm, is shown in Fig. 4, in which lateral growth is ignored. The boundary layer thickness δ was set to a typical diffusion length of Zn2+ ions (~300 μm). Importantly, the Ji/Jb becomes larger for smaller Ф and, as Ф approaches 1, Ji/Jb reaches 1.6 even at a wider Lc–c of 3 μm. We therefore conclude that the GT effect has a crucial influence to yield the strong diameter-dependent height profile observed in this study. Conversely, with reduced Cbi (Ф>>1), Ji becomes negligible compared with Jb, while competition for the precursor consumption increases. Accordingly, this leads to a complete reversal of the DZnO–HZnO relationship, as observed for Cb below 1.6 mM.
On the other hand, given that the Ji/Jb is inversely proportional to the Lc–c, a stronger GT effect is expected by reducing the Lc–c. This is, however, somewhat mismatched with our observation. For example, the height difference between different diameter rods is almost unaffected by Lc–c (in case of Fig. 1e) or slightly reduced at lower Lc–c (in case of Fig. 3d). To explain this, diffusive transport of the Zn(OH)2 also must be considered. According to the aforementioned synergetic effect, intermediate species are generated near the top (0001) surfaces of thicker rods and enhance the axial growth of nearby thinner rods, compensating for the height difference driven by the GT effect. It should be noted that the concentration of the intermediate species is higher at the rod surface than in the surroundings; thereby, they diffuse circumferentially (that is, the flux is inversely proportional to Lc–cn; n~3). This is different from the case of Zn2+ ions, whose concentration is lower at the rod surface (which acts as a sink) than the surroundings (see Supplementary Fig. 4); here, diffusion of Zn2+ ions caused by the GT effect occurs mainly between adjacent rods with different diameters (that is, Ji is inversely proportional to Lc–cn; n~1) under equilibrium conditions. This analysis also explains the rapid disappearance of the synergetic contribution, with an effective range of the Zn(OH)2 of <~2–3 μm; this is significantly lower than that of precursor Zn2+ ions. Although our simple analyses partly illustrate the complicated interaction among the growing crystals, further theoretical studies are needed to improve our fundamental understanding on these phenomena and to provide a generic model that will be applicable to various material systems.
Investigations on the ZnO crystal growth in solution have shown that the concentrations of reactant species would evolve with a prolonged growth time26,36, which could affect the growth kinetics. To address this issue, we have investigated the time dependence of HZnO on DZnO at various precursor concentrations (see Supplementary Figs 5–7). In all cases (Cb=25, 2.5 and 1.6 mM), the growth rate is relatively slow at the initial stage (t<1–2 h). This is attributed to the diffusion barrier created by the PMMA holes and/or nucleation barrier that exists even in homoepitaxial growth37. Following the initial stage, the growth rate becomes faster and stabilized. At Cb of 25 mM, HZnO is almost irrelevant to DZnO during the entire growth process (over up to 10 h) (Supplementary Fig. 5a). At Cb of 2.5 mM, there is no dependence of HZnO on DZnO in the beginning (t<2 h), but thereafter the HZnO significantly depends on DZnO because the GT effect becomes dominant (Supplementary Fig. 5b). More interestingly, at Cb of 1.6 mM, HZnO increases with increasing DZnO in the beginning (t<~6 h), but afterwards the situation is gradually reversed (Supplementary Figs 5c and 7); such a gradual change of the growth behaviour from the GT to the competition regimes is associated with the decreasing precursor concentration with time26. To further demonstrate the general applicability of our findings, we tested the growth of ZnO nanostructures with more complicated patterns, targeting specific 3D geometries. Growth in GT effect-dominating conditions allows thick rods to grow longer and produces castle-like 3D nanostructures. It is also possible to produce an inverted high profile in the competition regime (Fig. 5). Such 3D nanoarchitectures provide unique applications that would be difficult to be achieved by top-down fabrication approaches or that may require multiple-stage repetitive processing. As a proof of concept for practical applications, Si nanotube arrays were fabricated by employing a ZnO rod array as a sacrificial template, and they then served as an active constituent of highly sensitive strain gauges (or pressure sensors) (see Methods and Supplementary Fig. 9). This new type of electronic sensor can enable stepwise response to nanoscale deflection owing to the nanoscale height profile of the 3D Si nanotube array.
In summary, we demonstrated multiple types of growth mechanisms showing significant dependence of the diameter of the ZnO rod on the height, and elucidated the strong interactive growth behaviours observed in the anisotropic growth of these nanocrystal arrays. In this stage, our study is restricted to the case of ZnO crystals; however, this has its origin in general phenomena, including diffusion and the GT effect, which can be commonly applicable to a variety of materials, and thereby represents an opportunity for ab initio synthesis of diverse and functional 3D nanostructures in the solution phase.
Methods
Hydrothermal growth of ZnO rod arrays
For epitaxial growth of ZnO hexagonal rods, ZnO epilayers grown on GaN films on Al2O3 (0001) substrates were used as a seed layer. First, native oxide on a GaN surface was removed via chemical etching with aqua regia containing (3 HCl: 1 HNO3) for 5 min. Then, ZnO seed layers were deposited at 450 °C by metal-organic chemical vapour deposition (MOCVD), which produced c axis-oriented ZnO films with a typical thickness of ~200 nm. A detailed experimental description of the MOCVD process of ZnO films can be accessed elsewhere27.
To achieve position and diameter-controlled growth of ZnO rod arrays, ~120-nm-thick PMMA mask layers were spin-coated on the ZnO seed layers, and then arrays of circular holes were defined using an electron beam lithography technique. The geometries and parameters of hole arrays used in this study are schematically shown in Supplementary Fig. 1.
For the solution-phase synthesis of ZnO rods, aqueous solutions containing equimolar concentrations of zinc nitrate hexahydrate (ZNH) (Zn(NO3)2.6H2O, Sigma-Aldrich) and HMT (C6H12N4, Sigma-Aldrich) were used. The mixture solution of 25 mM ZNH and 25 mM HMT was diluted by adding appropriate volumes of deionized water to control the solute concentration in the range of 25–1.6 mM. Finally, the samples of ZnO seed layers coated with PMMA patterns were immersed into the prepared aqueous solutions, and they were then placed in an oven at 70 °C.
Fabrication of nano-strain gauge devices
Nano-strain gauge devices were fabricated using the following procedures: first, patterned ZnO rod arrays with different DZnO (from 200 to 600 nm) and HZnO (from 480 to 510 nm) were coated with a thin Si layer (typically 50 nm thick) by CVD. The thin Si layer, that is, a Si membrane with a 3D nanotube array at its centre, was then coated with a thin protecting layer of PMMA. By submerging the sample in HF solution (50 wt% diluted 1:20 v/v in deionized water), the core ZnO template was selectively etched, which separated the PMMA/Si membrane from the substrate. After rinsing with deionized water, the freestanding PMMA/Si membrane was mounted on the device substrate (plastic or Si/SiO2 substrate), in which the metal bottom electrode was pre-defined. Using an electron beam lithography technique, a trench was defined at the central region of PMMA where the Si nanotube array was located. Finally, a graphene-based top electrode on a polydimethylsiloxane (PDMS) structure was placed on the PMMA/Si membrane.
Additional information
How to cite this article: Lee, J. M. et al. Strong interactive growth behaviours in solution-phase synthesis of three-dimensional metal oxide nanostructures. Nat. Commun. 6:6325 doi: 10.1038/ncomms7325 (2015).
References
Ionescu, A. M. & Riel, H. Tunnel field-effect transistors as energy-efficient electronic switches. Nature 479, 329–337 (2011).
Chu, S. et al. Electrically pumped waveguide lasing from ZnO nanowires. Nat. Nanotechnol. 6, 506–510 (2011).
Robinson, J. T. et al. Vertical nanowire electrode arrays as a scalable platform for intracellular interfacing to neuronal circuits. Nat. Nanotechnol. 7, 180–184 (2012).
Xu, S. et al. Self-powered nanowire devices. Nat. Nanotechnol. 5, 366–373 (2010).
Goldberger, J., Hochbaum, A. I., Fan, R. & Yang, P. Silicon vertically integrated nanowire field effect transistors. Nano Lett. 6, 973–977 (2006).
Dayeh, S. A. & Picraux, S. T. Direct observation of nanoscale size effects in ge semiconductor nanowire growth. Nano Lett. 10, 4032–4039 (2010).
Givargizov, E. Fundamental aspects of VLS growth. J. Cryst. Growth 31, 20–30 (1975).
Dubrovskii, V. et al. Gibbs-Thomson and diffusion-induced contributions to the growth rate of Si, InP, and GaAs nanowires. Phys. Rev. B 79, 205316 (2009).
Dayeh, S. A., Yu, E. T. & Wang, D. Surface diffusion and substrate−nanowire adatom exchange in InAs nanowire growth. Nano Lett. 9, 1967–1972 (2009).
Jensen, L. E. et al. Role of surface diffusion in chemical beam epitaxy of InAs nanowires. Nano Lett. 4, 1961–1964 (2004).
Schubert, L. et al. Silicon nanowhiskers grown on <111>Si substrates by molecular-beam epitaxy. Appl. Phys. Lett. 84, 4968–4970 (2004).
Dubrovskii, V. G. et al. Diffusion-induced growth of GaAs nanowhiskers during molecular beam epitaxy: theory and experiment. Phys. Rev. B 71, 205325 (2005).
Schmidt, V., Senz, S. & Gösele, U. Diameter dependence of the growth velocity of silicon nanowires synthesized via the vapor-liquid-solid mechanism. Phys. Rev. B 75, 045335 (2007).
Bootsma, G. A. & Gassen, H. J. A quantitative study on the growth of silicon whiskers from silane and germanium whiskers from germane. J. Cryst. Growth 10, 223–234 (1971).
Murray, C. B., Norris, D. J. & Bawendi, M. G. Synthesis and characterization of nearly monodisperse CdE (E=sulfur, selenium, tellurium) semiconductor nanocrystallites. J. Am. Chem. Soc. 115, 8706–8715 (1993).
Kim, K. S., Jeong, H., Jeong, M. S. & Jung, G. Y. Polymer‐templated hydrothermal growth of vertically aligned single‐crystal ZnO nanorods and morphological transformations using structural polarity. Adv. Func. Mater. 20, 3055–3063 (2010).
Melrose, J. C. Applicability of the Kelvin equation to vapor/liquid systems in porous media. Langmuir 5, 290–293 (1989).
Boercker, J. E., Schmidt, J. B. & Aydil, E. S. Transport limited growth of zinc oxide nanowires. Cryst. Growth Des. 9, 2783–2789 (2009).
Trentler, T. J. et al. Solution-liquid-solidgrowth of crystalline Ill-V semiconductors: an analogy to vapor-liquid-solid growth. Science 270, 1791–1794 (1995).
Alivisatos, A. P. Perspectives on the physical chemistry of semiconductor nanocrystals. J. Phys. Chem. 100, 13226–13239 (1996).
Zeng, H. et al. Template deformation-tailored ZnO nanorod/nanowire arrays: full growth control and optimization of field-emission. Adv. Func. Mater. 19, 3165–3172 (2009).
Aizenberg, J., Black, A. J. & Whitesides, G. M. Control of crystal nucleation by patterned self-assembled monolayers. Nature 398, 495–498 (1999).
Lee, W. W. et al. Morphology-controlled three-dimensional nanoarchitectures produced by exploiting vertical and in-plane crystallographic orientations in hydrothermal ZnO Crystals. Cryst. Growth Des. 11, 4927–4932 (2011).
Xu, S. & Wang, Z. One-dimensional ZnO nanostructures: solution growth and functional properties. Nano Res. 4, 1013–1098 (2011).
Viswanatha, R., Santra, P. K., Dasgupta, C. & Sarma, D. Growth mechanism of nanocrystals in solution: ZnO, a case study. Phys. Rev. Lett. 98, 255501 (2007).
Ashfold, M. N. R., Doherty, R. P., Ndifor-Angwafor, N. G., Riley, D. J. & Sun, Y. The kinetics of the hydrothermal growth of ZnO nanostructures. Thin Solid Films 515, 8679–8683 (2007).
Lee, W. W., Kim, S. B., Yi, J., Nichols, W. T. & Park, W. I. Surface polarity-dependent cathodoluminescence in hydrothermally grown ZnO hexagonal rods. J. Phys. Chem. C 116, 456–460 (2011).
Wong, E. M., Bonevich, J. E. & Searson, P. C. Growth kinetics of nanocrystalline ZnO particles from colloidal suspensions. J. Phys. Chem. B 102, 7770–7775 (1998).
Wagner, C. Theorie der Alterung von Niederschlägen durch Umlösen (Ostwald‐Reifung). Z. Elecktrochem 65, 581–591 (1961).
Peng, X., Wickham, J. & Alivisatos, A. Kinetics of II-VI and III-V colloidal semiconductor nanocrystal growth:“focusing” of size distributions. J. Am. Chem. Soc. 120, 5343–5344 (1998).
Lifshitz, I. M. & Slyozov, V. V. The kinetics of precipitation from supersaturated solid solutions. J. Phys. Chem. Solids 19, 35–50 (1961).
Sun, Y., Riley, D. J. & Ashfold, M. N. R. Mechanism of ZnO nanotube growth by hydrothermal methods on ZnO film-coated Si substrates. J. Phys. Chem. B 110, 15186–15192 (2006).
Borgstrom, M. T., Immink, G., Ketelaars, B., Algra, R. & BakkersErik, P. A. M. Synergetic nanowire growth. Nat. Nanotechnol. 2, 541–544 (2007).
Polsongkram, D. et al. Effect of synthesis conditions on the growth of ZnO nanorods via hydrothermal method. Phys. B Condens. Matter. 403, 3713–3717 (2008).
Hocevar, M. et al. Growth and optical properties of axial hybrid III–V/silicon nanowires. Nat. Commun. 3, 1266 (2012).
Sun, Y., Fuge, G. M., Fox, N. A., Riley, D. J. & Ashfold, M. N. R. Synthesis of Aligned Arrays of Ultrathin ZnO Nanotubes on a Si Wafer Coated with a Thin ZnO Film. Adv. Mater. 17, 2477–2481 (2005).
Wen, C. Y., Tersoff, J., Reuter, M. C., Stach, E. A. & Ross, F. M. Step-flow kinetics in nanowire growth. Phys. Rev. Lett. 105, 195502 (2010).
Acknowledgements
This work was supported by the National Research Foundation of Korea (NRF) funded by the Ministry of Science, ICT and Future Planning (MSIP) of Korea (Basic Science Research Program: 2012R1A1B3001442, International Research & Development Program: 2013K1A3A1A32035393 and Future-based Technology Development Program Nano Fields: 2010-0029325). H.-G.P. acknowledges support for this work from the NRF grant funded by the Korea government (MSIP) (No. 2009-0081565).
Author information
Authors and Affiliations
Contributions
J.M.L., H.-G.P. and W.I.P. designed the experiments. J.M.L., Y.N. and S.K. performed experiments and analyses. J.M.L., H.-G.P. and W.I.P. wrote the paper. All authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-10, Supplementary Methods and Supplementary References (PDF 1117 kb)
Rights and permissions
About this article
Cite this article
Lee, J., No, YS., Kim, S. et al. Strong interactive growth behaviours in solution-phase synthesis of three-dimensional metal oxide nanostructures. Nat Commun 6, 6325 (2015). https://doi.org/10.1038/ncomms7325
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms7325
This article is cited by
-
Facet-selective morphology-controlled remote epitaxy of ZnO microcrystals via wet chemical synthesis
Scientific Reports (2021)
-
Investigation into effect of coupled resonance phenomenon towards sensitivity enhancement of SAW conductivity sensors integrated with ZnO nanorods
Microsystem Technologies (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.